By Victor J. Miller

The Northeast Tripp Slide is one of the larger slope failures that can be attributed to open pit mining. It is a 11.7 million cubic meter (15.3 x l0 6 yd3) wedge failure created by two thick gouge-filled fault zones whose intersection plunges into the Tripp pit at 13°. One unique aspect of this failure is that the slide is now stable despite having moved an estimated 8.5m (28 ft.) towards the pit and having reached a maximum overall velocity of 2lmmlday (0.07 ft/day). The slide started to fail in 1968, accelerated until mining in the slide's toe area was halted in April 1970, then began to decelerate. With the cessation of mining in the toe area, rubblized rock sloughed into the pit bottom which added weight to the failures toe constraints and began the stabilization process. Measurements from a network of survey stations revealed a correlation between the slide's velocity and heavy precipitation. Runoff water accumulating in the tension cracks is believed responsible for this correlation. Moreover, the survey net measurements showed that during the failure's last stage the vertical component of the slide's movement greatly increased. It is proposed that this settling was caused by plastic-like flowage of the clay gouge underlying the failure The fault zone's effective shear strength was estimated by a back- analysis on the wedge's geometry and by performing direct shear tests. The tests, performed on cores taken from samples that were collected on the failure, yielded a residual shear strength of: cohesion 0.61 kg/cm2 (8.7 lb/in2), and a friction angle of 9.6°. This residual shear strength was near1y equal to the back-calculated strength indicating that the controlling fault's effective strength was essentially the same as the residual shear strength of the gouge filling

Jan 1, 1983

By J. Ostachowicz, B. Holynska, M. Lankosz

The paper presents an analyzer and the method for the continuous determination of weight percentage of ore grains with diameter smaller than 75 µm in mineral slurries. The method is based upon the measurement of characteristic x-rays of copper excited by primary radiation of two different energies 16.5 keV and 60 keV from Pu238 and Am241 sources respectively. Additionally the backscattered primary radiation is measured in order to correct the variations of the solids content in the slurry. Since the particle size distribution of slurry can be described by the Rosin-Rammler formula, some calculations have been carried out in order to evaluate the influence of distribution parameters upon the results of the measurements of weight percentage U75 of particles smaller than 75 µm. The influence of solids content and of the copper concentration variation on the results has been also evaluated.1 It resulted from the calculations that the ratio rl/rz, where rl and r2 are the relative intensities of copper characteristic x-rays excited with 16.5 keV and 60 keV photons respectively does not depend on the copper content within the range 1 % to 4% of copper and is slightly dependent on the solids weight fraction and its chemical composition. The change of the dispersion parameter of the Rosin- Rammler distribution from 0.5 to 0.9 results in a change of value of U75 of approximately 3.0%. The results of calculations have been confirmed by the results of laboratory experiments. Therefore, a prototype of industrial analyzer for continuous determination of weight percentage of particles smaller than 75 µm has been designed and made. Its schematic drawing is shown in [Fig. 1]. Slurry is flowing down through steel flow-cell of the length equal to approx. 2 m. In the center, two XRF measuring heads (1) and (2) are located. Each of the heads comprises a rigid waterproof cover (3) with the mylar window (4), in which a proportional counter of resolution 15% for 6.4 keV is mounted with a preamplifier (5). The low- energy isotope source (6) is centrally located above the detector

Jan 1, 1980

By J. R. Long, R. S. Dean, F. S. Wartman, E. T. Hayes

The production of titanium in I5-lb. lots and with a purity sufficient to be consolidated into ductile metal, as described in a previous paper,' has provided adequate material for a study of the physical properties of titanium and a more thorough examination of its working qualities. Data on the physical properties reported in that paper were obtained on metal fabricated by a fixed procedure, standardized for the purpose of control of the reduction, and are representative only of material fabricated under those conditions. There are many possible variables in the working schedule, which will have significant effects on the properties of the finished material; and since the previous working methods were not necessarily the best, an investigation of the fabrication of titanium by other methods was undertaken. In this work the consolidation of the powder by pressing and sintering was conducted essentially as outlined in the report cited' and all efforts were centered on fabrication methods for those powders and the proper- ties produced by them. Hardness, density, microstructure, and tensile properties were determined at various stages in the working and annealing; and resistivity measurements were made on a few bars and drawn wire. Consolidation of the PowdeR The screen analysis of the available titanium powder is given in Table I. No attempt was made to alter the size distribution from that noted because this powder, although coarse by normal powder-metallurgy standards, produced acceptable compacts suitable for the present work. Because of their large specific surface, finer powders are more contaminated by oxygen and produce harder compacts, which are difficult to work. The powder as produced is soft, compresses in a normal fashion, and exhibits very little tendency to adhere to the die surfaces. Unlike aluminum and magnesium powders, it can be readily pressed without the use of die lubricants. When compacted at 50 tons per

Jan 1, 1946

By W. P. Sykes

THIS investigation was undertaken primarily to establish the relations existing between temperature and mechanical properties in molybdenum, nickel, and an aluminum-copper alloy. Molybdenum (m.p. 2500° C.) was chosen because it is partly similar to tungsten and partly similar to the common ductile metals. Also it is known to furnish, by proper treatment, a desirable material to use in studying relation of grain size and physical properties. The molybdenum used was of the quality that is drawn into wire 0.003 in. in diameter for use as filament supports in incandescent lamps; chemical analysis shows less than 0.1 per cent. of impurities. Nickel belongs to the same class as iron. Its melting point is 1450° C. and an allotropic change at about 370° C. results in a loss of magnetism above that temperature. This feature made nickel doubly valuable for the purposes of these tests. The nickel used was obtained from the Driver-Harris Co. as 0.090 in. (2.3-mm.) wire, annealed; analysis showed 99.8 per cent. nickel and 0.150 per cent. iron. Aluminum is one of the low melting-point metals. Some tensile tests at elevated temperatures have been reported by Bengough but the possibility of learning more with the low temperature and sensitive apparatus available recommended this metal. The samples marked Al are an aluminum-copper alloy; they contained 3 per cent. copper, 0.42 per cent. iron, and 0.21 per cent. silicon. The presence of the copper somewhat complicates the analysis of the results; but the action of copper in aluminum has been studied so that its influence might have been foretold, in part at least. The material and analyses were furnished by the Aluminum Castings Co. The nickel wire, which was deformed at 400° C., was drawn under a bath of molten lead and through a die, which also was immersed in the bath. A thermocouple was suspended in the molten metal to indicate

Jan 1, 1921

By J. R. Long, E. T. Hayes, R. S. Dean, F. S. Wartman

The production of titanium in I5-lb. lots and with a purity sufficient to be consolidated into ductile metal, as described in a previous paper,' has provided adequate material for a study of the physical properties of titanium and a more thorough examination of its working qualities. Data on the physical properties reported in that paper were obtained on metal fabricated by a fixed procedure, standardized for the purpose of control of the reduction, and are representative only of material fabricated under those conditions. There are many possible variables in the working schedule, which will have significant effects on the properties of the finished material; and since the previous working methods were not necessarily the best, an investigation of the fabrication of titanium by other methods was undertaken. In this work the consolidation of the powder by pressing and sintering was conducted essentially as outlined in the report cited' and all efforts were centered on fabrication methods for those powders and the proper- ties produced by them. Hardness, density, microstructure, and tensile properties were determined at various stages in the working and annealing; and resistivity measurements were made on a few bars and drawn wire. Consolidation of the PowdeR The screen analysis of the available titanium powder is given in Table I. No attempt was made to alter the size distribution from that noted because this powder, although coarse by normal powder-metallurgy standards, produced acceptable compacts suitable for the present work. Because of their large specific surface, finer powders are more contaminated by oxygen and produce harder compacts, which are difficult to work. The powder as produced is soft, compresses in a normal fashion, and exhibits very little tendency to adhere to the die surfaces. Unlike aluminum and magnesium powders, it can be readily pressed without the use of die lubricants. When compacted at 50 tons per

Jan 1, 1946

By P. Pietrokowsky

RECENTLY a comprehensive investigation of the various sigma binary alloys was published by Duwez and Baen.1 It was shown that the following conditions are necessary for the formation of the sigma phase: (1) the difference in atomic diameters of the two alloying metals must not be more than about 8 pct; (2) of the two elements which form sigma, one must exhibit a body-centered cubic structure while the second metal must be face-centered cubic, at least in one of its allotropic forms. In addition, a tetragonal unit cell was proposed and powder patterns of six sigma phases were indexed for d spacings greater than 1.640 kx. Since the indexing, based on tetragonal symmetry, led to only fair agreement, the possibility of sigma being orthorhombic was investigated. Various methods for indexing orthorhombic powder patterns are de- scribed in the literature.' The method used in this investigation was a graphical examination of the differences in values of sin' 9 for the adjacent lines of the powder diffraction pattern. This method led to a complete indexing of the Cr-Co (60-40) pattern. Because of the strong similarity between the various sigma alloys, it was then possible to assign indexes to the patterns of Fe-Cr (50-50), Fe-Cr-Mo (30-30-40), Fe-V (50-50), Co-V (50-50), and Ni-V (50-50). The values of sin' 9 and indexes of the six sigma alloys, together with visually estimated intensities, are presented in table 1. In general, the similitude between the six patterns is quite good. For spacings greater than 1.75 kx a few differences are noticeable. In the Ni-V pattern, no (320) exists and the two strong lines (030) and (031) are separated by only two lines of lower intensity, unlike any of the other sigma patterns. However, very little is known about the Ni-V phase diagram and it is possible that the equal atomic percentage composition in this system lies in a two-phase region. At lower spacings there is a close analogy between the patterns. The planes

Jan 1, 1951

By Paul A. Farrar, Felix Ermains, Harold Margolin

The systems Ti-Crand Ti-Vhave been reinvesti-gated in the region up to 40 wt pct alloying addition using both conventional and rapid quenching techniques. The Ti-Cr eutectoid temperature was determined to be at 667° & 10° C and 14.5 wt pct Cr. The solubility of the Cr in a Ti was found to be less than 1 pctat 700"C. The P transus of the Ti-V system was found to be depressed to 510°C at 40 wt pct V and the solubility of V in a Ti was found to be less than 2 wt pct at 700°C. Investigation by a. d. McQuillan1-3and m. k. McQuillan4 on the systems Ti-Co, Ti-Cr, Ti-Cu, Ti-Fe, Ti-Mn, Ti-Ni, and Ti-V has cast doubt as to the position of the ß/a + ß boundaries in many of these systems. Their investigations were carried out using hydrogen pressure and/or rapid quenching experiments, as opposed to the conventional quartz capsule techniques employed by most other investigator.'" By these methods, the ß/a + ß boundary was found to be lower than that obtained by conventional techniques in all except the Ti-Fe system. In the latter, the ß/a + ß boundary was essentially the same as the boundary obtained by conventional technique.7' On the basis of rapid quenching results in the Ti-Cr system, M. K. McQuillan4 placed the eutectoid temperature below 550°C whereas other investigations using conventional techniques had placed the eutectoid variously as between 650' and 700°C,5 between 675' and 700°C,6 between 650" and 675°C,7 at 670°C,8 and above 625"C.la9l3 In order to check these results, a reinvestigation of four of the systems was undertaken using both conventional and rapid-quenching techniques. The Ti-Fe and Ti-Mn systems will be dealt with in anoth er paper, with only the Ti-Cr and Ti-V systems being discussed here. EXPERIMENTAL TECHNIQUES Alloys employed for the delineation of the systems under investigation were prepared from iodide titanium sheet capsules containing the alloying materials,

Jan 1, 1962

By J. H. Bucher

The effect oj strengthening by the precipitation of CbC on the toughness offerrilic steel (0.11 pct C, 0.74 pct Mn, 0.02 pct Cb) was stlrdierl. A g-veater degree of pvecij~itatiotz strengthning is ohtaznable by aging the so11ution-treated steel rtt velaticely Low temperature was (1050" to 1l0O3F) than at higher temperatures (I150" to 1200°F). Tlzis ),eslrlts because a finer dispersion of CbC is obtained. However, the ductile-brittle transition te~ripertltlo.e is raised approximately tlzjeee tirues as IFLIIC~ perv a given yield stress increase) by aging in the lower tempareture range, as opposer1 to the Irigher temperaturee range. This is proposed to result pl-iir~avily because different precipitation distributions ar-e associated with the different aging -treaments. For tile steel aged at 1050" and 1100 F, heavy: precipitation on disloccctions occurs resulting in a high degree of rlislocution pinningh tl~us lowevirzg- the toilguiess. in tll c(.rise of the steel aged at 1150 'a?zd 1300"F, Pvecipitatiol~ is irzove g-enerally distributed throughout the matrix rather limn preferentially on dislocations.; and Ike detlsitj, oj mobile dislocations is not sttyong-ly affected. THE most effective means of strengthening hot-rolled ferritic steels are grain refinement and precipitation hardening. It is well-known that grain refinement increases both the strength and the toughness. However, the upper limit of yield strength obtainable by grain refinement alone is about 60,000 psi,'12 i.e., without the formation of acicular structures of lower toughness. The most economical means of obtaining higher strengths is the addition of small amounts of elements such as columbium, vanadium, and titanium which form carbonitrides. These precipitates are very effective in increasing the strength, but the ductile-brittle transition temperature is is Although it is agreed upon that precipitation decreases the toughness, there has been little effort to isolate the causative aspects of embrittlement. The purposes of this research are to assess quantitatively the embrittlement associated with different precipitate distributions and morphologies, and to correlate the degree of the embrittlement with the microstruc-ture. In this manner, a more fundamental insight into the mechanism of embrittlement may be gained. The steel selected for this purpose was a low-carbon, columbium-bearing steel which, after solution treatment, was aged in various time-temperature cycles while attempting to hold all other microstructural variables constant. MATERIALS AND PROCEDURE The composition of the steel used in this investigation is given in Table I. Starting with commercially hot-rolled material 0.074 and 0.280 in. thick, tensile blanks were cut from the thinner material and sub-size Charpy blanks from the thicker stock. The steel had been rolled using a low finishing temperature and rapid cooling after hot rolling to produce grain refinement. Also, chemical-extraction analysis and electron-microscopic examination revealed that the cooling was rapid enough to suppress any significant precipitation of CbC. Therefore, the as-rolled steel is essentially in the solution-treated condition in terms of the precipitation reaction, and it was used as the base material in this investigation. The room-temperature tensile properties of the as-rolled steel aged at 1100", 1150", and 1200°F for various time intervals were determined, see Table 11. The ductile-brittle transition behavior was studied for smooth and notched tensile specimens, and longitudinal half-size (0.200 in. thick) Charpy V notch specimens aged at 1100" and 1150°F for various times, also Table 11. In addition, tensile specimens aged for single times at 1050" and 1200°F were evaluated with respect to their ductile-brittle transition. Only one 1050°F treatment was used because of the extremely slow kinetics of precipitation at this temperature and because no significant difference between 1100°F aging was observed. Only one treatment at 1200°F was used because aging at this temperature alters the shape of the grain boundary cementite particles present in this steel and complicates analysis. The design of the tensile specimens is given in Fig.1.

Jan 1, 1968

By R. Schuhmann

Available thermodynamic data applicable to copper smelting systems are collected and tabulated, and the important gaps are pointed out. A few examples are given of estimations which can be made from the available data. An experimental research program is proposed to supply the thermodynamic data that appear most essential to better quantitative understanding of the chemistry of copper smelting. The proposed program is designed also to shed specific light on the practical problems of slag losses and magnetite behavior. OPPER smelting, from flotation concentrates to V-/ blister copper, is conspicuous among the large scale chemical processes which are conducted with only relatively incomplete knowledge of the physical chemistry involved. For example, no common metallurgy text explains adequately why copper enters the matte phase while iron enters only to the extent that sulphur is left over after satisfying the copper. Explaining this important phenomenon as a manifestation of the greater affinity of sulphur for copper than for iron is unsound because the affinities of copper and iron for sulphur are about the same at smelting temperatures. As will be shown, other affinities are really decisive in the relatively clear-cut separation of copper in the matte. In contrast, thermodynamic studies have contributed much to our understanding of copper refining, zinc oxide reduction, magnesium production, steelmaking, etc. For each of these processes, the important reactions are clearly recognized, and fair to good quantitative values of the free-energy changes and equilibrium constants are available. Such data have proved to be of constantly increasing practical value in process development and improvement. Work in other fields has furnished much thermodynamic data applicable to copper smelting systems. In fact, several promising starts have been made in applying such data to specific smelting problems. Kelleyl made an appraisal of the possibilities of recovering elementary sulphur from low grade matte. His calculations and compilations of thermodynamic data have represented the starting point for much of the work in this field, including the present survey. Huang and Hayward2 nd Aksoy3 used thermodynamic methods in the study of copper losses in reverberatory slags. Peretti4 used thermodynamic data in explaining the chemistry of converting. The recent publications of Darken and Gurry"." and of Darken,' dealing with the iron-oxygen and iron-silicon-oxygen systems, respectively, present equilibrium data that are applicable to copper smelting systems. Also additional data were reported recently on the affinity of sulphur for copper, manganese, and iron8 and on the sulphur pressures of iron-sulphur melts." The survey presented in this paper was made as the basis for planning an experimental program on the thermodynamics of copper smelting. Few researches on the chemistry of copper smelting have been reported in recent years, so that a reappraisal and coordination of old and new data are essential if further work is to take the directions of maximum value. The experimental program is now in progress, and the plan of attack is outlined at the end of this paper. Progressive Oxidation and Desulphurization of Copper-bearing Liquid Phases: The chemical activities of sulphur and oxygen are two of the most important thermodynamic yardsticks to be applied to copper smelting processes. Virtually the entire smelting and refining sequence involves a series of systems characterized by decreasing sulphur activity and increasing oxygen activity. In this section, therefore, an attempt is made to define and explain these activities in terms of equilibrium partial pressures of SO2, s2, and O,. Also, estimates of these quantities are presented, the estimates being based largely on calculations presented in a later section of this paper. The sequence of steps from raw flotation concentrate to fully oxidized copper ready for poling involves progressive and controlled oxidation. Iron is oxidized and enters the slag. Sulphur is oxidized and leaves in the gas. Table I summarizes several important features of this oxidation and desulphurization sequence, starting at the beginning of the matte blow in the converter. The top line gives in order the principal smelting and refining stages up to fully oxidized copper, plus the additional step, not used commercially, of oxidizing all the way to Cu,O. In the second line are shown the principal copper-bearing liquid phases which characterize the process. Through most of the sequence the copper

Jan 1, 1951

By W. D. Forgeng, D. Beregekoff

In the routine examinatlion of a wide variety of metal specimens it is sometimes necessary to have special methods of polishing in order to retain and reveal certain details in each specimen. Among such special cases is the retention of graphite in malleable and gray cast irons, the preservation of all types of non metallic inclusions in both hard and soft steels, obtaining a scratch-frec surface with soft metals, and avoiding the usual relief effects with very hard specimen. such as tool metals c3o1ltaining various carbide and nitride phases. It, is the purpose of this paper to give an account of some of these special polishing methods in use at the Union Carbide and Carbon Research Laboratories. The polishing procedures outlined have been found to give uniform results. It is obvious that only general rules and the most important working details can be given here. Following these rules, the polisher can obtain satisfactory results if he possesses the necessary patience and has a sincere desire to give as nearly perfect a finish as possible to his work. Procedure The specimen is flattened with considerablecare on a file or sharp cutting sanding belt, since the initial production of a flat surfacc greatly facilitatcs subscqucnt polishing. The polishing motors have two speed., 600 and 1200 r.p.111. ,It higher speeds specimens arc likely to he over-Ileated, therefore the high speed is used only when a saving of time is important. The following abrasive papers are used consecutively: Yo. 2, So. 1, No. 0, No. 00 and No. 000. The final wet polishing is done oil a cloth-covercd metal disk. Woolen broadcloth of the best quality and capable of resisting severe pressure is most commonly used on the last lap. . polishing felt of the type used for polishing optical glass has been found equally satisfactory and is much stronger than broadcloth. For retaining inclusions and graphite, a hard cloth with very little residence, such as

Jan 1, 1939

By C. G. Dunn

Many investigations have been made concerning the nature of plastic deformation and recrystallization of metals either in the form of polycrystalline materials or in the form of single crystals. However, similar work on strip materials composed of large grains as thick as the strip and having a high degree of preferred crystal oricntation has not been carried out extensively. Such materials are ideal not only for studying changes in single crystals under conditions where neighboring grains exert their influences but also for obtaining the complete change in orientation of a grain or group of grains during the course of plastic deformation and subsequent recrystallization. It is well known that first-order twins in the form of Neumann bands may be produced during the plastic deformation of ferrite crystals, particularly silicon ferrite crystals.l--3 Furthermore, it is believed that high-stress regions exist in the vicinity of these bands4. and it has been said that these banded regions would be active in recrystallization processes.5 Evidence to that effect in silicon ferrite had already been presented with photomicrographs showing recrystallization among Neumann bands during the early stages of recrystallizati~n.5,6 Similar evidence has been published for nonferrous metals5 Merging of fine parallel deformation bands during annealing to form twin bands of ordinary appearance in alpha brass has been offered not only as evidence of an active role being played by mechanical twins but also as evidence that such twins cxisted prior to recrystalli~ation.5 Proof that such new structures are actually first-order twins, or even twins at all, must be considered inadequate except for those cases where X-ray or optical data have been obtained to confirm the necessary oricntation relationship.7,8 A. B. Greninger has obtained excellent iliustrations of annealing twins in alpha iron.9 Since his material was previously deformed by sharp hammering, a process that generally induces Neumann bands, the existence of twins following annealing might suggest that they grew from mechanical twins. In connection with transformation twins in alpha iron, Greninger reported that grains containing three twin orientations occurred rarely and none occurred with three sets of well-developed bands.9 The work at the Pittsfield Works Laboratory on silicon ferrite in the form of large-grained strip steel deformed a small amount and annealed to partially recrystallize the grains indicates that the deformation and recrystallization processes that lead to annealing twins involvc more complex processes than the formation of Neumann bands and the growth of such bands. Some groups of annealing twins are obtained which contain not only three well-developed twin structures, but also contain more than one order of twins. It is also shown, in one case, that an interrelated group of twins did not arise within one single parent grain and, furthermore, orientations of grains in the group

Jan 1, 1944

By Paul T. Allsman, E. W. Newman

Trenching, sampling, and core drilling in Stillwater and Sweetgrass Counties, Mont., by the Bureau of Mines have delimited over 5,000,000 tons of chromite ore containing more than 20 per cent chromic oxide. The Benbow and Mouat-Sampson mines have been developed and are fully equipped for mining and milling 500 tons and 2000 tons a day, respectively. Introduction The Montana chromite deposits were the first to be explored under the Strategic Minerals Act of 1939. In June of that year, the Bureau of Mines started exploration by trenching, test pitting, sampling and diamond drilling, and completed the project in March 1943. The U. S. Geological Survey cooperated by mapping the geology and logging the cores. The project was to determine the extent and grade of the chromite ore and to indicate sufficient reserves to justify development and exploitation of the deposits for the national emergency. Exploration has indicated that the district contains the largest and most important reserve of chromite ore in the United States. The Benbow and Mouat-Sampson mines have been developed and a 500-ton concentrating mill has been constructed on the Benhow property and a 2000-ton mill on the Mouat-Sampson property. Concentrates were produced from the Benbow mill three months after the attack on Pearl Harbor, when the nation's major chromite supplies from foreign sources were cut off. History It has been known for 50 to 60 years that some chromite deposits existed in an east-west belt along the north escarpment of the Beartooth Mountains about 25 miles north of Yellowstone Park, but nothing was known of their size and extent until the war demand of 1917 and 1918 stimulated the search. In those years two properties in the Stillwater region were actively developed, but no shipments were made. The Benbow property was located in 1918 by a local group. The property comprised seven claims along the strike at the east end of the belt. An adit was driven several hundred feet on the Eclipse claim. The seven claims were sold to the Chromium Products Corporation of Livingston, Mont., and were subsequently patented. In 1929, an eastern group obtained an option, installed some equipment, and erected several log cabins. The "crash" in the market in 1929 caused the operators to drop their lease, and the property remained inactive until 1939, when the Bureau of Mines began its exploration. Fourteen claims were located on the Boulder River in 1918 and subsequently patented by the U. S. Chrome Corporation.

Jan 1, 1949

By Bernhard Blumenthal

A melting process was developed by which high purity electrolytic uranium crystals can be converted into sound ingots without serious contamination. Careful preparation of the crystals, melting in a high vacuum, and directional solidification led to a metal of better than 99.993 wt pct purity. The metallographic examination showed a substantially clean metal with only residual amounts of a second phase which responded to heat treatment. The density of high purity uranium is 19.05 g per cu cm. FOR the study of the fundamental properties of uranium and its alloys, a base metal of high purity is needed, and an investigation was started at Argonne several years ago to examine various methods of preparing high purity uranium. Early success was achieved by the fused salt electrolysis process in preparing high purity metal in crystal form,' and the problem became that of melting the crystals into ingots without contamination. The electrolytic crystals contained a few ppm of heavy metals, less than 15 ppm C, and large quantities of potassium and lithium in the form of trapped fused salt electrolyte. On melting in vacuo in magnesia or urania crucibles, the metal picked up considerable quantities of carbon and some iron, copper, and silicon but lost most of the potassium and lithium. It was not metallographically clean, and much research work was necessary to determine the optimum melting conditions for minimum contamination. This work has resulted in the development of a melting procedure by which sound ingots can be prepared with only a limited contamination by carbon. In the section entitled "Melting of the Electrolytic Metal," the equipment and processes that have been developed for melting the electrolytic crystals are described in detail. The "Metallography" section is devoted to the metallography of high purity uranium, and the section "Density of High Purity Uranium" contains the first property measurement on high purity uranium—a density determination. Melting of the Electrolytic Metal Apparatus—Melting and Vacuum Equipment: Uranium may be melted in either resistance or induction-type electric furnaces. Resistance heating was found to be preferable to induction heating for melting down the electrolytic crystals, for several reasons: Although induction heating permits fast heating, this advantage cannot be utilized when crucibles with limited thermal shock resistance are used. Temperature control of induction-heated melts is poor, and the stirring effect increases the rate of contamination of the melt from the crucible, slag, or the furnace atmosphere; liquation and controlled solidification are difficult to carry out. Because of these objections, resistance heating was chosen. A 10 kw Globar resistance furnace of low heat capacity permitted uniform heating of a uranium charge to its melting point in 45 min. The furnace was insulated with a removable aluminum shield so that, after melting and removal of the shield, the furnace could be quickly cooled to room temperature. The furnace was equipped with an apparatus for directional solidification; see Fig. la. The crucible was suspended in the center of the furnace; and when the melting was complete, the crucible was slowly lowered into the cold end of the furnace tube. Solidification took place upward from the bottom; and when the rate of lowering was small, a sound ingot free from sink holes and shrinkage cavities was produced. To remove the large quantities of gas contained in the electrolytic crystals, melting in a high vacuum is mandatory. While, from the standpoint of contamination, melting in a highly purified argon atmosphere appeared feasible, lithium and potassium removal proved less efficient under such conditions. Also, a vacuum-melted ingot has a cleaner surface than one melted in an inert atmosphere. The vacuum system must be of very high pumping speed and leak tight so that a vacuum of less than 2x10-7 mm Hg is attainable when the system is pumped down cold. The system must have a high pumping speed, so that the pressure maximum which may rise to 1x10-4 mm during heating can be quickly reduced

Jan 1, 1956

By D. Beregekoff, W. D. Forgeng

In the routine examinatlion of a wide variety of metal specimens it is sometimes necessary to have special methods of polishing in order to retain and reveal certain details in each specimen. Among such special cases is the retention of graphite in malleable and gray cast irons, the preservation of all types of non metallic inclusions in both hard and soft steels, obtaining a scratch-frec surface with soft metals, and avoiding the usual relief effects with very hard specimen. such as tool metals c3o1ltaining various carbide and nitride phases. It, is the purpose of this paper to give an account of some of these special polishing methods in use at the Union Carbide and Carbon Research Laboratories. The polishing procedures outlined have been found to give uniform results. It is obvious that only general rules and the most important working details can be given here. Following these rules, the polisher can obtain satisfactory results if he possesses the necessary patience and has a sincere desire to give as nearly perfect a finish as possible to his work. Procedure The specimen is flattened with considerablecare on a file or sharp cutting sanding belt, since the initial production of a flat surfacc greatly facilitatcs subscqucnt polishing. The polishing motors have two speed., 600 and 1200 r.p.111. ,It higher speeds specimens arc likely to he over-Ileated, therefore the high speed is used only when a saving of time is important. The following abrasive papers are used consecutively: Yo. 2, So. 1, No. 0, No. 00 and No. 000. The final wet polishing is done oil a cloth-covercd metal disk. Woolen broadcloth of the best quality and capable of resisting severe pressure is most commonly used on the last lap. . polishing felt of the type used for polishing optical glass has been found equally satisfactory and is much stronger than broadcloth. For retaining inclusions and graphite, a hard cloth with very little residence, such as

Jan 1, 1939

By J. A. Norden

MUCH has been written concerning the hoisting equipment of various mines -throughout the country, but most of the literature on the subject, if not all, describes equipment of extraordinary capacity and the small and medium-sized outfits have been neglected. The hoisting equipment here described is capable 'of handling about 1200 tons per day. It has not been worked, to capacity, but 600 to 700 tons, together with men and materials, have been handled in two shifts without any great effort. Only one shaft extends from the surface to the lowest levels of the mine; see Fig. 1. It is composed of three compartments, two of which are used for hoisting and the third for water, air, and electrical lines, and for sinking purposes. In 1909, this shaft was raised from the 1000-ft. (304-m.) level to the 700-ft. There a station was cut and an air hoist installed. At this time all mining operations were confined to the upper levels of the mine; that is; above the 700-ft. The. ore was-dropped to this level through chutes from the 300-, 400-, 500-, and 600-ft. levels and then lowered in cars on cages to the 1000-ft., which is the main haulage adit, the mill and railroad bins being about 3000 ft. from the shaft. Orebodies were, in due time, developed on the 1000-ft. level and below. Therefore, in 1913, the shaft was sunk to the 1150-ft. level and thereafter sinking was continued at regular intervals until the 1500-ft. level was reached. But, hoisting from the 1300-ft. level was a difficult, and slow process with the antiquated air hoist, so, in 1916, it was derided to raise the shaft to the surface and install a modern, electrically operated hoist. This was completed early in 1917 and the hoist was in operation in March of that year.

Jan 8, 1920

By R. B. Hoy, Stanley J. LeFond, K. Reckling

World production of natural diamonds prob¬ably exceeds 50,000,000 carats a year. The Republic of Zaire is the leading producer, with an output which is primarily industrial rather than gem grade. The USSR ranks second, and the Republic of South Africa third. Diamonds are also mined in South-West Africa, Angola, Ghana, Sierra Leone, and other African coun¬tries. In the western hemisphere, Brazil and Venezuela are the principal producers (Fig. 1). A very small output of diamonds is mined today in India, which was the first source of commercial production. In the U.S., efforts at commercial diamond mining have been con¬fined to a small area near Murfreesboro, Ark. The first diamond was found in a kimberlite pipe there in 1906. Small-scale trial mining has not, however, proved economical. Since diamonds were first discovered over 2000 years ago, only about 130 tons have been mined. In order to obtain 1 g (5 carats) of diamonds, it is necessary to remove and process approximately 25 tons of rock. Recovering this small percentage involves a combination of highly developed techniques in mining, quarrying, and earth-moving, and extremely sophisticated recovery processes. End Uses Diamonds are used for two unrelated end uses; gem diamonds are jewels of great beauty while industrial diamonds are essential ma¬terials of modern industry. Although imitation stones are substituted for the gem diamond, none of these matches its properties sufficiently well to offer real competition. Synthetic indus¬trial diamonds are now of a quality that per¬mits wide substitution in the fine-grained sizes. Gem Diamonds A diamond is a natural prism. It has the ability to bounce light rays (reflection), to bend them (refraction), and to break them into all colors of the rainbow (dispersion). This ability to "modify" light gives the diamond three characteristics for providing beauty. First is brilliance, the reflection of light back to the eye. Second is fire, dispersion of light into the colors of the spectrum. Third is scintillation, the "twinkling" that occurs when the diamond is moved (Bauer, 1969). The skill of the diamond cutter is required to unlock the brilliant, fiery beauty of a gem dia¬mond (Fisher, 1966). Diamond-cutting skills have gradually developed over the centuries. The first cutters, in India, learned how to grind one rough diamond against another to remove their "skins" and to give them various shapes. This revealed some fire and beauty, but little compared to that of the diamonds that are cut today. About 1475, a Flemish cutter named Van Gerquem discovered that diamond dust on an iron wheel would polish facets on a diamond to provide more brilliance and fire. Cutters continued to experiment with facets, and shortly before 1700 a Venetian cutter named Peruzzi developed the 58-facet brilliant cut. With the development of the science of optics, cutters have learned more about the behavior of light within the diamond. Early in the 20th century, they learned how to angle Peruzzi's

Jan 1, 1975

By Frederick C. Hull, Robert F. Mehl, Robert A. Colton

IT is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth 12 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in 1939 3 Two types of process were described (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures, and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth Both cases are met in the formation of pearlite from austenite (Fig 1),2,3 the former, occurring near the knee of the S-curve has been named "grain-boundary transformation," and the latter, occurring at temperatures near AeI, has been named "group-nodule transformation " In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important''' to obtain data on the rate of nucleation and the rate of growth of pearlite Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the actors that affect hardenability, when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite 2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature,, and the degree of homogeneity of the parent austenite The studies are restricted chiefly to plain carbon commercial steels PREVIOUS DATA ON RAID OF NUCLEATION AND RATE OF GROWTH Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Mehl,1 and by Dorn, De Garmo and Flanigan22 It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc ), austenite grain size, and mode of formation of pearlite at the temperatures given

Jan 1, 1942

By C. W. Gennet

Announcement was made in the spring of 1926 that the Boston & Maine R. R. Co. had contracted with the well-known German steelmakers, Messrs. Fried Krupp, for the manufacture of 15,000 tons of basic open-hearth steel rails at the Rheinhausen Works, for delivery to Boston, Mass. The manufacture of rails in the United States has for many years been almost a national pride, and as this feeling is chiefly the result of a long-time liberal and consistent patronage of American rails by American railroads, it is not strange that this somewhat unusual announcement should arouse more than ordinary interest. Since the end of the World War, the importation of foreign rail has been fairly large, principally because the newly created economic conditions have rendered some American competition more difficult, but the tonnage imported, for the most part, has been made up of small orders for miscellaneous use; and the contract referred to constitutes the largest single importation of foreign rail in over ten years. In 1915, the Algoma Steel Co. of Sault Ste. Marie, Canada, supplied the Illinois Central R. R. with 30,000 tons of rails,' and various other American roads with smaller amounts. In 1902, 1903 and 1904, large tonnages of rail from abroad were purchased, the Louisville & Nashville R. R. alone obtaining 30,000 tons from German mills. It is the object of this paper to present, in what is believed to be a new and concise form, figures showing the production and consumption of rails in the United States, and to record some of the testing and inspection results of the recent Krupp rails; also, to direct attention to two quite unique departures from American practice that were regular features of the Krupp process and which are worthy, it is thought, of careful study. Production and Consumption of Rails in the United States Table 1 shows the tonnage of rail produced in the United States and the amount imported, exported, and consumed by years since 1849. That, evidently, was the first year of record, for the statistics of the American Iron and Steel Institute and its predecessor, the American Iron and

By John D. Sullivan, Edwin J. Rogers, Chester R. Austin

THE problem of making a building unit combining the necessary physical and mechanical properties and good thermal insulation has been foremost in the minds of architects and ceramic and construction engineers for many years. This paper presents the results of studies on thermally expanding shales or clays to produce light-weight cellular products suitable for making building units. An expanded clay block suitable for building purposes should be large enough so that substantial savings may be effected in labor costs in laying the wall. The permeability should be low and it should have sufficiently good "dry-wall" characteristics to permit exposing the exterior surface to the elements, and to permit plastering directly the inside wall surface. The thermal conductivity should be low and the mechanical properties should be adequate. Obviously, a unit possessing satisfactory qualities for constructing an outside wall would be satisfactory for interior walls and for back-up purposes. The results of studies on bloating various shales or clays† and the properties of the expanded products are reported. In another paper1 basic factors involved in bloating of clays are discussed. Manufacturers of ceramic products, particularly structural clay, may encounter bloating of the ware during burning, and precautions must be followed to avoid this phenomenon. About 1927 the C. F. Burgess Laboratories, Madison, Wis., while carrying on an investigation for the American Face Brick Research Corporation, conceived the idea of intentionally bloating clay while holding it in a restrained condition, with the hope of producing a unitary cellular mass. Work was carried on until about 1931, when studies were terminated because of business conditions. These studies were continued later by The Western Brick Co., Danville, Ill., which developed a process of "inwardly expansive bloating." The major purpose of the latter investigation was to produce back-up tile to compete with concrete blocks made from Haydite or cinder aggregate. Haydite is a light-weight aggregate formed by heating certain clays or shales rapidly in a rotary kiln. While the investigations at the C. F. Burgess Laboratories or at Western Brick Co. were not carried far enough to lead to the commercial production of material for the construction of walls, particularly outside walls, they showed that certain clays could be thermally expanded and that it was possible to produce a material of low permeability with a large percentage of the total voids or cells closed. Commencing in 1939, the Ozark Chemical Co. sponsored a research program at Battelle Memorial Institute for the purpose of determining whether it is technically feasible to make thermally expanded building units, and specifically to get answers to the following questions:

Jan 1, 1942

By R. F. Mehl, G. V. Smith

THE decomposition of austenite in steels, because of its immense practical importance, has been subjected to extensive study in recent years from the point of view of the mechanism of the process.1-3 Although much information has been acquired a number of questions, principally of theoretical interest, remain. One is that of the atomic-crystallographic mechanism by which each of the various reaction products forms. The isothermal reaction products of the eutectoid decomposition in plain carbon steels (to which this study is restricted) have conveniently been classified in three general groupings-pearlite, bainite, and martensite. Of these several products, pearlite and martensite have been studied extensively, but bainite has received only scant attention. As a result, the mechanism of the formation of pearlite and that of martensite are now fairly well understood while a great deal of uncertainty exists regarding bainite. PEARLITE Pearlite forms from austenite by the precipitation of alternate platelets of cementite and ferrite, which grow into the austenite matrix.2-5 The rate of reaction may be described in terms of a rate of nucleation and a rate of growth 2 3 Mehl and Smiths have attempted to determine the lattice relationships existing between the ferrite in pearlite and the parent austenite. Using a pole-figure method of analysis, it was found that a limited number of ferrite orientations resulted from the decomposition of a single grain of austenite; it was not possible,[ ]decide between two assumed ideal relationships, both of which appeared to account for the experimentally determined pole figure. It was definitely shown, however, that the relationship obtaining was quite different from that determined for the proeutectoid separation of ferrite.7 No attempt was made to determine the habit plane (matrix plane to which the precipitate lies parallel) of the pearlite lamellae. Belaiew8 earlier had stated that the number of directions assumed by the pearlite lamellae in a single grain of austenite was 12 (no details were given) and concluded wrongly, as Mehl and Smith' have pointed out, that the lamellae delineate the {210} planes of ferrite.* MARTENSITE It is known that martensite is a transitional constituent of body-centered tetrag-

Jan 1, 1942