By A. Siegmund, Gerhard Martin

The recycling of metal containing scrap is a common practice in the industry and has a long tradition. . In rec~nt years, this philosophy has been transferred to organic materials, in particular to thermoplastic polymers. BSB . Recycling GmbH, a company with a long experience in the treatment and recovery of lead from battery scrap,· had recognized this exploitation at an early stage and challenged it by a consequent continuation of the idea to recycle materials other than metals without degradation and maintaining the quality. These efforts resulted in an economic and environmentally acceptable solution producing high quality polypropylene compounds at BSB beside lead and lead alloys from battery scrap. The raw material fair the production of polypropylene compounds is shredded plastics from the separated casings of spent lead-acid batteries. The production of polypropylene with specific physical and mechanical properties is carried out by the accurate dosing of organic as well as inorganic additives. The result of the procedure is a novel product group "Seculene PP", a registered trademark of BSB Recycling GrnbH.

Jan 1, 2000

By Hande Cavus, Ibrahim Yusufoglu, Cem Kahruman

"In this study, ammonium tetramolybdate (ATM) was obtained as the intermediate product of ammonium heptamolybdate tetrahydrate (AHM). The thermal decomposition mechanism of ATM was investigated under nonisothermal and isothermal conditions in air and inert gas atmospheres. Nonisothermal experiments were carried out by TGA/DTA/MS while TG was used for isothermal conditions. Characterization of the decomposition products were carried out by XRD and FT-IR. The thermal decomposition of ATM in air proceeds in a single step and forms M0O3 while [(ÍÇ4)2è]ïïï83Ìïè3 and molybdenum suboxide (Ìïè3.÷, ÷=0.025) were obtained in the first and the second steps of thermal decomposition in He, respectively. Activation energies, frequency factors and kinetic model equations were determined for thermal decomposition reactions. Fractional conversion-time diagrams were compared with diagrams drawn according to kinetic model equation.IntroductionM0O3 is usually used as catalyst in industry [1]. AHM is the basic source to produce molybdenum containing catalysts used in petrochemistry [2]. The oxides of Li, V, W, Te, Bi and Sn are doped in M0O3 to produce catalysts, which find commercial applications in the industry. The properties of M0O3 are affected by dissolution, settling, calcination, drying and thermal decomposition processes [1]. There are several studies in the literature about the thermal decomposition of AHM and the characterization of the decomposition products in different gas atmospheres and at various heating rates [3-19]."

Jan 1, 2012

By Ben Q. Li

An efficient numerical algorithm for solving steady state heat transfer and solidification problems is described. The algorithm is of boundary integral type and is based on the formulation of the field variables along the boundary of the domain of interest. Compared with the familiar domain-based methods, such as the finite element and finite difference (or finite volume) methods, this boundary-based method has an advantage of solving fewer unknowns and hence has a potential for reducing computational time significantly. Another and yet more important advantage of the present algorithm is that it is a stable scheme and is not prone to numerical oscillations resulting from convective effects, as often encountered in the domain-based methods. Therefore, no numerical or artificial diffusion (such as streamline upwinding) is necessary. Numerical examples are presented that are drawn from processing systems for producing aluminum-based materials.

Jan 1, 1994

By Osarnu Inoue

In Mitsubishi Continuous Copper Smelting and Converting Process, smelting, slag-matte separation and matte converting are continuously carried out in series in three furnaces connected by launders. As a result of this operational configuration of the furnaces, influence of the change in operating condition in upper stream, such as variation of feeds in the smelting furnace, propagates to down stream with some delay. In order to achieve stabler operation, process control algorithm based on the dynamic characteristics of each furnace would be very effective. In this study, the dynamic process simulation model was developed for the smelting furnace. The model consists of two mathematical modules, i.e. the thermodynamic module and the mixing module. The calculation results using operating data obtained at Naoshima Smelter showed good agreement with the actually observed change in temperature, composition and flow rate of matte and slag at the outlet of the furnace. In addition, operation parameters such as reaction efficiency of oxygen and coal, dead volume of melts were estimated.

Jan 1, 1999

By Alicia Esther Ares, Alex Iván Kociubczyk, Verónica Liliana Scheiber, Roberto Rozicki

In the present research the horizontal solidification of Sn-Zn eutectic alloys (Sn-8.9wt.%Zn) is performed, with two opposite senses of heat extraction. From the process of solidification, the thermal parameters (local solidification time, cooling rates and interphases velocities) and grain sizes from macrostructures obtained were determined. The presence of defects in the solidified samples was analyzed, observing that they occur largely in the collision zones of solidification fronts advancing in opposite directions in the samples.

Jan 1, 2016

By C. M. Acuña

Copper losses in slags are of great concern, specially in smelting and slag cleaning processes. It is widely accepted that the suspension of metallic copper and matte droplets is strongly affected by the viscosity of the slag. The Chuquicamata Division of Codelco- Chile produces concentrates high in zinc, an element which reports mainly to the slag phase. The ZnO may affect the viscosity and therefore the copper losses. This work aimed to investigate the effect of lime to control the viscosity of slags, and in turn to control the copper losses. By using the experimental viscosity data and the Stoke's law, the settling rate of matte prills in various slags was estimated. The results indicate the possibility of increasing the recovery of copper and/or decrease the process time.

Jan 1, 1999

By T. A. Larssen

The efficiency in production of manganese ferroalloys is dependent on the gaseous reduction of the higher manganese oxides in the ores used as raw materials. The materials, descending in the furnace, will meet the furnace gas that contains significant amounts of CO(g) and reduce in subsequent steps, the last step being reduction of Mn3O4 to MnO. This step may to varying extent occur at temperatures exceeding 800 °C, i.e. in the active region of the Boudouard reaction. The gas reduction of Assmang and Comilog manganese ores were investigated in CO-CO2-atmosphere at temperatures up to 1000 °C. It was seen that decreasing ore size correlates to a lower reduction temperature and increasing reduction rate. Similar effect was observed with increasing CO-content in the gas atmosphere. Further, it was found that Comilog ore obtained a complete prereduction at 600 °C, whereas reduction of Assmang ore was not complete at 800 °C for the majority of the experiments.

By Richard Jack De Klerk

The standard industrial method of arsenic removal from acidic aqueous processing effluents involves coprecipitation of arsenic with ferric iron (Fe/As>3) by lime neutralization in continuous circuits. To better understand current industrial practice, continuous circuit coprecipitation experiments were performed to identify industrially relevant process parameters and co-ion solutes that contribute to improved arsenic removal and retention. The coprecipitated solids were subjected to accelerated ageing at 20°, 40° & 70°C and arsenic behavior was monitored and modeled. Staging and the presence of calcium ions were found to have the most significant impact on arsenic retention. In this paper the techniques used and major results obtained are discussed.

Jan 1, 2008

By Hai-Peng Guo, Lu Jiang, Xiao-Man Yan, Bing Xie, Hong-Yi Li

Traditional, calcium compounds cannot be used in vanadium extraction processing due to the limitation of sodium roasting technology, which results in unsatisfied dephosphorization for vanadium-containing hot metal in converter and thus increasing the dephosphorization burden for subsequent steelmaking. The calcium roasting technology is an alternative for vanadium extraction and allows adding lime into vanadium slag in converter. In the present study, vanadium was leached by soda from roasted vanadium slag with high calcium content. Effects of roasting temperature and time, leaching temperature, Na2CO3 concentration andliquid to solid ratio on vanadium leaching rate were studied. The results show that 94% of vanadium was extracted by roasting the vanadium slag at 950℃ for 2.5h and then leaching in 160g/L Na2CO3 liquid at 95℃ for 1h with liquid to solid ratio of 10:1 ml/g. Impurities of Si and P reacted with calcium and formed insoluble Ca2SiO4 and Ca3(PO4)2 respectively.

Jan 1, 2015

By Victor Bredykhin

The report is devoted to the investigation and improvement of processes taking place at contact of large quantities of water insoluble liquid and particles of solid phase in a pulp. Theoretical analysis and simulation of acting conditions have allowed to determine that after attaching of oleophilic particles on the «water-reagent» separation surface the break of a formed complex is taking place according to the reagent volume and for oleophobic minerals along the «solid-reagent» separation surface. As a result particles are selectively treated if the magnitude of the reagent adhesion to the surface of solid phase in water is great. The results of dispersion are influenced significantly by availability of sharp edges on the surface of real particles. They keep tree phase perimeter of moistening. It is possible to fix reagent in the form of lens whose contact angle is significantly smaller in comparison to the thermodynamic angle. In adhesion dispersion the reduction of reagent volume, covering the equal area of particles surface is possible when the reagent is in a pulp in the form of thin films on the «water-gas» separation border. The process is tested in laboratory conditions as well as at pilot concentrating mills in flotation of sulfide ores, non-ferrous metals (copper-molybdenum ore), native sulfur and coal.

Jan 1, 2006

By Dai Xi

In the present work, the viscosities of molten FenO-MgO-Si02 and FenO-MgO-CaO-Si02 semi-synthetic slags for nickel flash smelting were measured in the temperature range from 1473 to 1723K by a rotational viscometer. The ratio of Fe to Si02 was fixed at 1.2, calcium and magnesium oxide contents varied in the range from 2 to 8 mass% and 9 to 12 mass%, respectively. The results showed that silicate anions became smaller by increasing CaO content, which results in a decrease of the viscosity of the slag. In the case of MgO addition the viscosity behavior was complicated. At MgO content below 11 mass%, the viscosity increased with the increase of MgO at all temperatures tested. However, when the MgO content was above II mass%, the viscosity decreased slightly for FenO-MgO-CaO-Si02 system. At higher MgO contents, low-viscosity slags can be obtained by adding CaO. At a given composition, the viscosity decreased with increasing temperature. The higher the temperature, the more MgO can be added before saturation. The effect of Fe304 on the viscosity was quite significant. The viscosity of slag increased by 300mPa's at l573K when Fe304 content varied from 3 to 9 mass%. The viscosity values are presented as the functions of temperature and composition. A comparison between FenO-MgO-Si02 and FenO-MgO-CaO-Si02 systems is given in this study.

Jan 1, 2003

By N. Kanari

The kinetics of oxychlorination of MgO by C12+02 was studied in the temperature range of 850 °C - 1025 °C, using thermogravimetric analysis. The effects of C12/02 ratio, gas velocity, temperature and partial pressure of reactive gases on the reaction rate were investigated. The oxychlorination process was characterized by an apparent activation energy of about 214 kJ/mol. The reaction orders with respect to C12+02, C12 and 02 at 950 °C were about 0.65, 0.98, and -0.37, respectively. Some data about oxychlorination kinetics of MgO, Cr2O3, and MgCr2O4 contained in chromite were compared. Efficiency of using oxychlorination for the removal of iron oxides contained in magnesia was demonstrated.

Jan 1, 1999

By Wei Yin, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Copper anode slime is an increasingly significant resource for precious metals such as Au, Ag and Pd. The extraction of Au, Ag and Pd from decopperized anode slime by different pretreatments and different lixiviants including cyanide, chloride, thiourea and thiosulfate have been investigated. When oxidizing roasting pretreatment was carried out under the conditions of roasting time 120min and temperature 625 ℃, the removal ratios of S and Sb could reach 82.18% and 98.52%, respectively. And the following alkaline leaching of calcine could result in the dissolution of 46.40% Cu and 98.48% Pb. The optima leaching ratios of Au, Ag and Pd reached 99.48%, 97.69%, 94.79% by cyanide leaching, and 95.01%, 79.84%, 96.59% by chloride leaching, and about 95.21%, 95.66%, 48.79% by thiourea/thiosulfate leaching.

Jan 1, 2015

By D. Quattrini

The aim of the present work is to present the gas chromatography (GC) as an alternative method of analysis in the thermal decomposition of calcium carbonate. Therefore, a furnace/GC on-line system was employed to study the kinetics of the reaction, measuring the CO2 produced in the decomposition. One of the advantages of the GC method is the possibility to perform an in-situ characterization and quantification of the gaseous products to obtain kinetic parameters, besides the method is simple and shows a good reproducibility. The decomposition of calcium carbonate was carried out in isothermal conditions at temperatures from 655 to 715°C with nitrogen as purge gas. Several gas velocities were used to determine the adequate flow that minimizes the effect of external mass diffusion as rate controlling step. It was made a preliminary analysis of the sample size influence on the reaction rate. The activation energy of the reaction was determined by Flynn method. The value obtained was in a good agreement with other authors. On the other hand, gravimetric measurements were employed for compare GC results.

Jan 1, 2006

By Y. Ide, K. Kishitake

It is expected that an Al-Cr-N composite nitride film may have a higher resistance to oxidation at elevated temperatures than the well-known Ti-Al-N films. The formation conditions of Al-Cr-N films by a de reactive sputtering method and their properties were studied in this study. The films characterized with respect to their high temperature properties such as chemical composition, crystal structure, microhardness, wear and· friction. The crystal structure of the Al-Cr-N films changed from hexagonal phase to cubic phase with an increase in Cr content in the films. The resistivity to thermal oxidation of the Al-Cr-N films is superior to that of usual TI-Al-N films. A half of the friction coefficient in the Al-Cr-N film was obtained comparing with that in the ordinary TI-Al-N film at room temperature and the wear rate of Al-Cr-N film was 2 order smaller than that of TI-Al-N film. The Al-Cr-N films show a small friction coefficient at 500°C and then they are recognized to have good tribological characteristics.

Jan 1, 2000

By J. L. Liow

Studies have been carried out on the causes and effects of slopping in an annular cylindrical geometry such as the top submerged combustion reactor. Properties of standing waves formed such as the wave profile, period, pressure distribution and velocity have been derived analytically. The wear profile due to wave erosion was calculated based on the assumption of linear motion and that the wear is a dissolution process. The use of the j, factor showed that the wear was proportional to the square root of the wave velocity at any point. Using the dimensions of the lsasmelt reactor given by Errington et al. (1987)[11, the wear profile due to wave erosion was calculated using the analytical solution. The wear profile calculated was shown to have a maximum just below the initial bath surface. The wear was found to be concentrated in the region where the first asymmetric standing wave was most active. The results showed that the refractory near the bath surface will be affected by wave erosion, more so than any other parts of the reactor. The contribution of wave erosion on wear must be accounted for in assessing the total refractory wear of a vessel in which slopping exists.

Jan 1, 1991

By Noboru Masuko, Sachiko Ono

"The structure and composition of anodic films formed on aluminum in a borate solution have been investigated by using TEM and SIMS with respect to the effect of current density and electrolyte temperature. The film is composed of a boron-containing outer layer and a boron-free inner layer with disc-like crystals present at the interface. The thickness of the film formed at constant current density up to an identical voltage, decreases with increasing current density. The thickness increases remarkably with elevated temperature. The transport number of Al3+ estimated from the thickness ratio .of the cuter to the inner layers is 0.4 when the film is formed at the current density of 20 Am-2 at 60°C. It increases slightly with increasing current density and decreases significantly with increasing temperature. Content of boron in the outer layer increases 1.5 times when current density .increases 10 times. These changes in film structure and composition with electrolysis conditions must have a significant role in the determination of electric properties of anodic alumina films as a capacitor material.IntroductionThe growth of anodic alumina film in ·a neutral electrolyte proceeds at both film/electrolyte and film/substrate interfaces giving a duplex structure. The oxide layer formed at the former interface includes electrolyte anions while a-pure alumina layer is formed at the latter interface. The thickness ratios of each layer respectively represent transport numbers of Al3+ and 0 2 - (1). The film thickness and the incorporated anion content as well as transport numbers of both ions must affect the dielectric properties of the film as a capacitor material. However, the correlation between film structure and electrolytic conditions is not fully understood (2). For the further clarification of anodic film growth mechanism, more detailed characterization of anodic films in relation to electrolytic conditions is advantageous. In the present paper, therefore, the effect of current density and electrolyte temperature on the microstructure and composition of anodic barrier films formed in a neutral borate solution was studied. The films were characterized by direct observation using transmission electron microscopy (TEM) and depth profiles of constituent elements obtained by secondary ion mass spectroscopy (SIMS)."

Jan 1, 2000

By Hiroyuki. Fukuyama

The pseudo-binary phase diagram of the cuspidine (3CaO2?SiO2?CaF2) - CaF2 system has been studied by electron probe microanalysis (EPMA) and X-ray diffractometry (XRD). To prevent fluorine loss in the form of a HF gas by a reaction of CaF2 with water vapor at elevated temperatures, the equilibrium experiments were conducted with the sample hermetically sealed in a platinum tube. By employing this technique, it was successfully revealed that cuspidine exists as a stable phase and congruently melts at 1684 ± 1 K, and the cuspidine - CaF2 system presents a simple eutectic type of phase diagram, of which eutectic temperature has been estimated to be around 1540 K, corresponding to the composition of 40 mass% 3CaO?2SiO2 - 60 mass% CaF2?

Jan 1, 1999

By Saskia Duyvesteyn

For many applications in hydrometallurgy and water treatment it would be advantageous to use ion-exchange resins in stirred reactors. However, attrition of the resin may lead to significant losses of both resin and metal values and prevent water quality goals from being reached. We have studied the recovery of fine resin particles by froth flotation, using the model copper - Dow XFS4195 chelating resin system. As the functional group on the resin is a bis-picolylamine, the resin should be amenable to flotation by anionic collectors, such as sodium dodecylsulfate and sodium dodecylsulfonate. The kinetics of copper loading from dilute aqueous solutions in an agitated vessel were studied as a function of copper concentration, pH and resin bead size. The flotation of unloaded resin was investigated for different types of collector, collector concentration, conditioning time, and resin bead size. Potential applications are discussed.

Jan 1, 1995

By Huaming Yang

Infrared materials are a special kind of material widely used in military, biological engineering and chemical industry. However, the problems associated with them such as unstable properties, high cost and a high thermal expansion coefficient seriously restrict the development and the wide application of the traditional infrared materials with the SiC or ZrSiO4 matrix. The ultrafine quartz powder is normally used to prepare the infrared materials by hot-pressing technology. The aim of the paper is to investigate the thermal expansivity, the effect of the SiO2 size and the addition of Al2O3 or Fe2O3 on the infrared emissivity of the quartz matrix of the infrared material (QMIM) in a 8-25um wavelength range. The results indicate that 89% of infrared emissivity and 0.4x 10-5/°C of thermal expansion coefficient of QMIM can be obtained. The affecting mechanism of A1203 and Fe2O3 on the infrared emissivity of QMIM were also discussed.

Jan 1, 2003