Search Documents

By Henry Rawdon

THE following note describing the behavior of copper under rather unusual conditions is offered here for its suggestiveness rather than as a complete study of the question. The examinations described were made because of a request for information concerning the embrittlement of copper when heated in a molten salt bath (sodium chloride) for the purpose of cleaning it, as well as for softening it. It is well known that metals may be rendered very brittle by electrolytic action, in aqueous solutions, in all probability by the action of nascent hydrogen, and it was suspected that perhaps the embrittlement of the copper by means of the molten salt was produced in a somewhat similar manner. It was found that the copper was in contact with iron (or steel) while immersed in the molten salt, through the occasional use of an iron stirring rod, iron forceps for handling the pieces, and an iron pot for containing the fused salt. In the electrochemical potential series iron and copper stand some distance apart, copper being electronegative to the iron. Assuming that the two metals bear a similar relation to each other, when immersed in a bath of molten salt, as they do in an aqueous solution, they would be expected to form a galvanic couple, the copper being the cathode. By this means the copper might be embrittled, as often happens in aqueous solutions, by the action of the liberated hydrogen. In this case, however, the embrittlement must be attributed to some other agent than hydrogen. To demonstrate how copper may be embrittled under these conditions, two small rods, one of copper and the other of mild steel, approximately 3/8 in. (9.5 mm.) in diameter, were immersed in a bath of sodium chloride that had been heated somewhat above its fusion point (melting point of sodium chloride is 819° C.) and an electromotive force of approximately 6 volts from a storage battery was impressed upon the system. The copper was made the cathode and the action was continued for

Jan 2, 1920

By Pradeep K. Rohatgi, Clyde M. Adams

Structures produced upon solidification of the eu-tectic composition (33 wt pct Cu) aluminum copper alloy have been examined as a function of freezing rate dfs /d? , the rate of change of fraction solid (fs) with time (8). Slow (dfs/d? = 0.0016 sec-1), intermediate (dfs/d? = 0.02 sec-1) and rapid (dfs/d? = 0.4 to 7.30 sec-1) freezing rates were used. The lamellar Al-Cual2 eutectic is arranged in the form of rod-shaped colonies at rapid freezing rates. The colonies are aligned parallel to the direction of heat flow, whereas the lamellae within the colonies are aligned at various angles, as high as 90 deg, to the direction of heat flow. The colony spacing (C) is proportional to the square root of inverse freezihg rate. The relationship is C = 15.5(dfs/d?)-1/2 where C is in µ and 8 is in sec. The ratio of colony spacing to lamellar spacing is greater than 20.0 and increases with a decrease in the freezing rate. A duplex dendritic structure is produced at intermediate freezing rates. A fine lamellar eutectic is arranged within the dendrites (exhibiting side branches at an angle close to 60 deg from the main stem) and a coarse irregular eutectic appears in the interdendritic regions. The duplex eutectic structure is also produced at slow freezing rates. However, at slow freezing rates there is a Platelat of CuAl2, along the center of the main stem of each dendrite and the other lamellae are arranged perpendicular to the central platelet. THE eutectic between CuA12 and a! aluminum has been reported to freeze in a lamellar form by several workers.'-3 chadwick4 has measured the interlamel-lar spacing as a function of growth rate. Kraft and Albright2 have reported on irregularities in the lamellar structures, and have proposed growth models which account for the formation of faults during solidification. In certain instances the lamellar eutectic has been found to exist in colonies. The colony formation315 has been attributed to the breakdown of a planar liquid-solid interface due to rejection of impurities. The aim of the present work is to study the structures produced from the eutectic aluminum-copper alloy under relatively fast solidification rates, such as encountered in casting and welding operations. The solid-liquid interface presumably remains planar under conditions of slow unidirectional freezing which produce lamellae aligned parallel to the direction of heat flow. The local growth velocities are the same over the entire interface and are equal to the rate of growth of the all-solid region. The spacing between the eutectic lamellae is inversely proportional to the square root of the growth rate of the all-solid region. Under the freezing conditions used in the present study, the solid-liquid interface is cellular or dendritic and the local growth velocities are different in the different regions of the interface. The relationship between the growth rate of the all solid region and the local growth velocities varies with the location and the shape of the interface. The growth rate of the all-solid region is, therefore, an inadequate parameter to describe the eutectic micro-structures which depend upon the local growth velocities. For this reason the structures have been examined as a function of freezing rate, dfs/d?, where fs is the fraction solidified at time 0. The freezing rate was varied by a factor of 4000. The relationship between the freezing rate, dfs/d?, and the growth velocit of the all solid region depends upon the specimen geometry and the shape of the interface. EXPERIMENTAL PROCEDURES The A1-33 pct Cu alloy used throughout this study was made in an induction furnace, using electrolytic copper and aluminum of commercial purity (99.7 pct), the primary impurities being silicon (0.12 pct), iron (0.14 pct), and zinc (0.02 pct). Three ranges of freezing rates were investigated: 1) A spectrum of rapid freezing rates (ranging from 0.40 to 7.30 sec-1) was obtained in arc deposits made on 2-in. thick cast plates of the eutectic alloy. The arc was operated at constant power and was made to travel at constant velocity on the surface of the plate that was in contact with the chill surface during solidification. The pool of liquid metal formed under the moving tungsten arc solidified rapidly by heat extraction through the unmelted plate. Conditions of unidirectional heat flow were achieved near the fusion zone interface, especially in the center of the arc deposits. The great advantage of the arc technique is that rapid cooling and freezing rates can be varied in a qualitative way. The correlation between the arc parameters and the solidification rate is given by the following relationship:6-8

Jan 1, 1970

A shrinkage stope is an overhand stope in which the broken ore accumulates until the stope is completed to, or near, the level above. As broken ore generally occupies at least 60 per cent. more space than ore in place, about a third of this must be drawn out as the stope advances to leave a working space under the back. The ore remaining supports the miners and gives temporary support to walls, and is all withdrawn when the stope is finished. The shrinkage-stope method is applicable to steep-dipping deposits of strong ore with strong walls. It may be applied to narrow or wide veins, and is simple and cheap. Five examples, which include important and varied types of deposits, are given: namely, Kennecott, Homestake, Jarbidge district, Mogollon district, and Cripple Creek district.

Jan 1, 1925

By R. A. Hadfield

It seems a specially fitting opportunity to present a paper on the alloys of iron and aluminum at the New York meeting of this Institute, owing to the fact that America has, more than any other country, originated and developed the manufacture of cheap aluminum. The Cowles, Castner, and Hall systems have all originated in the ever-busy brain of our cousin across the water. The problem of cheaply producing this valuable metal has been a difficult one, but to the writer it seems that the more arduous the task the greater the delight with which our American friend attempts to overcome the difficulties surrounding it, and the more vim he throws into the work. Another and equally striking proof of this is to be found in the recent appearance of the already wellknown remarkable work, The Mefallurgy of Steel, by Mr. H. M. Howe, of the Institute of Technology, Boston, Mass. It is to be hopel that this Institute will not be slow to recognize by some special mark its appreciation of this signally valuable and original work. The writer has been led to describe the following experiments, believing that so far no full and exact report has yet been presented to this Institute as to the effect of aluminum alloyed or combined with the metal iron. It has been a special object to make the material as far as possible a true alloy or combination of aluminum and iron, with as small quantities as possible of other disturbing ingredients, such as silicon, manganese, etc. In the material described in these experiments, the total amounts of other elements present (sulphur and phosphorus being disregarded as present in such small quantities) do not exceed about 0.5 per cent. Such material may therefore be probably taken as fairly illustrative of the effect of the metal aluminum upon iron. Since completing the experiments the writer

Jan 1, 1891

By J. E. House, J. L. Drobnick, R. R. Swanson, D. W. Agers

The paper describes an improved process for the recovery, purification, and concentration of copper values from acidic dump leach liquors. The process employs a new liquid ion exchange material (LIX® 64 reagent) capable of separating copper values from iron and other impurities common to dump leach liquors in the typical pH range of 1.4-3.0. Properties and performance of the reagent are discussed. Design scale-up information for both pilot plants and commercial installations, including preliminary economics, are presented. Economic considerations include the production of electrolytic copper from the purified copper aqueous concentrate. INTRODUCTION Since the commercial acceptance of the liquid ion exchange process in the mineral processing industry, it has been predicted that a wide selection of chemical reagents to efficiently and economically separate many metals in solution under a wide range of conditions would be commercially available. Several years ago, General Mills began a basic research and development program to determine if it were possible to develop a reagent to extract economically metallic ion from existing process streams. Progress toward reaching this objective was reported in late 1963, when development of quantities of LIX -63 reagent, a highly selective reagent for the extraction of copper, was introduced. The properties of this reagent are described in a previous paper.' The development work with this reagent indicated that perhaps the largest potential application for a copper extractant, the treatment of acidic dump leach liquors, would not be economically possible with LIX-63 because of limitations of the reagent to extract copper below a pH of 3.0. The relatively small pH adjustment required with LIX-63 would result in a significant processing cost and the undesirable precipitation of ferric hydroxide from the liquor. This pointed to the need for another copper extractant which would extract copper from dump leach liquors without pH adjustment. General Mills was successful in synthesizing a molecule which does not have the pH limitation of the LIX-63, yet possesses the selectivity-solubility properties required of a metallic extractant. The resulting LIX-64 reagent broadens the pH range from which copper can be effectively extracted and separated from other metallic impurities. Of special significance is the fact that the reagent, LIX-64 was developed by combining the technical requirements of a specific problem in hydro-metallurgy with theoretical organic and physical chemical principles.

Jan 1, 1967

By Thomas Varley

IN THE congressional act establishing the Bureau of Mines one of the functions outlined was "to assist I the industry in the prevention of mineral waste." This had not only to do with the waste in mining but in milling and metallurgical practices, including smelting. The organization of the Bureau of 'Mines includes many divisions, each working in a particular field and charged with certain investigative work. The metallurgical division has the above duties under its immediate supervision, and the station located at Salt Lake City is directed by the chief of this division: There are ten experiment stations of the Bureau of Mines, located in various parts of the country, most of them being housed at state universities under cooperative agreements. Considerable care was exercised in locating the stations and in choosing the particular type of work to be investigated at each place. Inasmuch as the Bureau was designed to serve and cooperate with the industry it is only natural that the investigative work be of interest and importance to the territory immediately adjacent to the respective stations.

Jan 1, 1925

By Henry F. Herley

The New Orient mine, owned and operated by the Chicago, Wilmington & Franklin Coal Co., has caused a great deal of comment and interest because of its unusual features and huge daily production. It is in Franklin County, Illinois, adjacent to the town of West Frankfort. The seam being mined is the Illinois No. 6 which in this locality is 9 to 12 ft. thick and lies approximately 500 ft. below the surface. Without fear of contradiction, it can be said that this is one of the largest coal mines in the world from a daily production standpoint. During 1928, New Orient produced 2,400,000 tons, which amounts to over 10,000 tons each day the mine operated that year. The mine is built for a capacity of 12,000 tons but has actually hoisted over 15,000 tons in one 8-hr, shift. This enormous production can perhaps be better visualized if it is realized that each day's operation depletes over two acres of coal. The general features of this mine have already been fully covered in a paper by George B. Harrington,' President of the Chicago, Wilmington & Franklin Coal Co. In a paper of the nature of Mr. Harrington's, it was unnecessary to stress any particular phase of mining conditions, consequently the ventilation problems were touched upon but lightly. In this paper an attempt has been made to describe some of the problems which have been encountered in providing adequate ventilation for the mine. Ventilating Conditions The acreage allotted to New Orient mine has a length, north and south, of approximately 6 miles, and a width, east and west, of 2 to 4 miles. A number of important considerations caused the hoist shaft, air shaft and surface plant to be located near the southeast corner of the property, instead of near the center, as is usual. During the initial phase of the mine development, the mine was ventilated through these shafts, although there was a full realization that at some future date other shafts would be required.

Jan 1, 1930

By G. E. Johnson

LEAD SMELTERS AND REFINERS in 1932 were confronted with the problem of adjusting operations and costs to curtailed production and consumption at reduced prices, a problem which has been partially solved at least by improvements in operating technique and increased efficiency. At the Mount Isa properties in Australia, a third blast furnace and additional Dwight-Lloyd sintering machines were installed during the year, designed to increase the production to 6,000 tons of bullion per month. The large proportion of lead carbonate in the ores to be treated has presented metallurgical problems. Of the total lead contained in the concentrates to be smelted, two-thirds is Dresent as carbonates and one-third as sulfides. In the iiitial operations, the resulting Dwight-Lloyd sinter was soft, contained an excessive amount of fines, and was easily fusible. When charged to the blast furnaces it developed accretions in the upper part of the furnace owing to the easily fusible lead carbonates softening and fusing at the top of the charge column. This was remedied by the addition to the sinter feed of diluents of higher melting point, granulated slag and crushed limestone. The sinter feed consists of concentrates, Cottrell dust and wind-box cleanings, totalling 57 per cent of the charge; return sinter fines 15 per cent; granulated slag 23 per cent; and crushed limestone 5 per cent. The sinter produced contains 34 per cent lead and 0.5 per cent sulfur. Experiments indicated that double sintering under these conditions was of no advantage, so the original plan of single sinter treatment was retained.

Jan 1, 1933

By H. C. Schultz, F. K. Middleton Hunter

Certain local conditions were known to govern in large measure the successful adaptation of liquid-oxygen explosives to the large-scale blasting at Chuquicamata. The wide variation in hardness of the rock at this mine makes necessary the use of several types of explosives. A locally manufactured, relatively cheap black powder is used in blasting the softer waste and capping material, where a thorough displacement breaks the ground sufficiently. Before the introduction of L. 0. X., an ammonia dynamite of about 65 per cent. strength was being used exclusively in the harder underlying orebody, where a strong disruptive as well as a displacement effect is required for breaking the ore. The L. 0. X., as developed for quarry work in the United States, has a practically pure carbon cartridge material, and the explosive has an extremely high rate of detonation, which should therefore cause it to develop usefully its full disruptive effect in hard ground. The individual blasts at Chuquicamata arc large, black-powder shots which dislodge masses of rock averaging 250,000 tons each, and dynamite shots which dislodge masses averaging 80,000 tons each. It was desirable, therefore, to attempt to displace with L. 0. X. the faster, higher-cost ammonia dynamite used in the smaller blasts. It was not considered practical to attempt to displace the low-cost black powder with 1,. 0. X., as estimated costs showed no probable saving if this were accomplished. Since it was desirable to continue shooting relatively large blasts for effective operation, it was recognized that larger storage facilities than had been in use would be needed for the liquid oxygen. Because of the difficulty of transporting and discharging large storage containers of efficient design, the better plan appeared to be storage and discharge of the liquid at the place of manufacture, and transportation of the filled soaking boxes to the blast. Present Liquid-oxygen Plant An experimental unit with a rated capacity of 75 liters per hour was erected during the latter part of the year 1926 to prove the effectiveness of L. 0. X. at this mine, its cost, and possible efficiency of large-scale storage of the liquid. With this experimental unit 200,000 tons of ore

Jan 1, 1928

By I. M. Roberts

The war emergency has affected every phase of industry. The gas and coke-oven companies have sought faithfully to discharge their responsibility in this critical period and have willingly modified their operations where possible to meet the ever increasing demands made upon them. Our company made commitments for blast-%urnace coke for war purposes which necessitated a reduction in coking time in order to produce the amount required to meet the new demands. At the same time there were certain customers of long standing, who had been supplied with foundry and egg-sized coke produced on fairly long coking periods, who also were engaged in war work and whose patronage we desired to retain. Coke produced on short coking rates from the coal mixture we were then using would not have been satisfactory for these customers. The average width of our ovens is 19¾ in., which is a little wider than the more modern ovens of the present day. They were originally designed to give somewhat cool tops in order to produce a rich gas. This necessitates carrying the heats a little on the warm side so that the tops will be fully carbonized. A reduction in coking time, as is generally known, is accompanied by a reduction in the average size of the coke produced. This is due to the greater shrinkage that takes place at the higher temperatures required to carbonize the charges in a shorter time. The net result is that the coke is more cross fractured and longitudinally fractured and breaks up into small sizes on handling. The cokes produced from the better coking coals seem to be more susceptible to fracture at high temperatures than those from poorer coking coals. A coal mixture that produces a beautiful foundry-sized coke at 30 to 36 hr. may yield a product at 18 hr. that would be so badly fractured as to be unsatisfactory for foundry practice. Coking Characteristics OF Coals Our problem was to find some economical innovation and develop a method that would enable us to reduce the coking time and still produce a coke satisfactory to our foundry trade. However, before discussing the results of our present operations, it might be well to present a few observations on the coking characteristics of coals in general. Most coke-oven operators carbonize a blended mixture of coals. It may consist of a single high-volatile coal with a single low-volatile coal, or of a combination of several high-volatile and low-volatile coals. Medium-volatile coals of the Eagle seam are used for the production of high-grade foundry coke. Medium and high-volatile coals are often blended with one or more low-volatile coals. The possibilities are almost infinite, but the combinations are limited by such factors as cost and facilities for handling multicoal mixtures, and by other practical considerations. Every coal has characteristics that make it blend better with a particular coal or coals in preference to others. This property has

Jan 1, 1944

By I. M. Roberts

The war emergency has affected every phase of industry. The gas and coke-oven companies have sought faithfully to discharge their responsibility in this critical period and have willingly modified their operations where possible to meet the ever increasing demands made upon them. Our company made commitments for blast-%urnace coke for war purposes which necessitated a reduction in coking time in order to produce the amount required to meet the new demands. At the same time there were certain customers of long standing, who had been supplied with foundry and egg-sized coke produced on fairly long coking periods, who also were engaged in war work and whose patronage we desired to retain. Coke produced on short coking rates from the coal mixture we were then using would not have been satisfactory for these customers. The average width of our ovens is 19¾ in., which is a little wider than the more modern ovens of the present day. They were originally designed to give somewhat cool tops in order to produce a rich gas. This necessitates carrying the heats a little on the warm side so that the tops will be fully carbonized. A reduction in coking time, as is generally known, is accompanied by a reduction in the average size of the coke produced. This is due to the greater shrinkage that takes place at the higher temperatures required to carbonize the charges in a shorter time. The net result is that the coke is more cross fractured and longitudinally fractured and breaks up into small sizes on handling. The cokes produced from the better coking coals seem to be more susceptible to fracture at high temperatures than those from poorer coking coals. A coal mixture that produces a beautiful foundry-sized coke at 30 to 36 hr. may yield a product at 18 hr. that would be so badly fractured as to be unsatisfactory for foundry practice. Coking Characteristics OF Coals Our problem was to find some economical innovation and develop a method that would enable us to reduce the coking time and still produce a coke satisfactory to our foundry trade. However, before discussing the results of our present operations, it might be well to present a few observations on the coking characteristics of coals in general. Most coke-oven operators carbonize a blended mixture of coals. It may consist of a single high-volatile coal with a single low-volatile coal, or of a combination of several high-volatile and low-volatile coals. Medium-volatile coals of the Eagle seam are used for the production of high-grade foundry coke. Medium and high-volatile coals are often blended with one or more low-volatile coals. The possibilities are almost infinite, but the combinations are limited by such factors as cost and facilities for handling multicoal mixtures, and by other practical considerations. Every coal has characteristics that make it blend better with a particular coal or coals in preference to others. This property has

Jan 1, 1944

By W. H. Bassett, C. H. Davis

In the commercial annealing of cartridge brass there are four points regarding which definite data are essential. They have to do with the correct interpretation of grain count in its relation to annealing temperature and, incidentally, to Brinell hardness. These points are: 1. The comparison of the grain sizes of two cartridge-brass mixtures: 69 copper, 31 zinc, 0.376-in. (9.5-mm.) gage; and 68 copper, 32 zinc, 0.130-in. (3.3-mm.) gage 2. The comparison of the grain sizes of annealed metal that had previously been reduced by rolling varying amounts; for instance, 20.0, 36.6, 50.9, and 59.1 per cent. 3. The determination of standards for grain sizes on annealed brass of the composition 68 per cent. copper, 32 per cent. zinc and 69 copper, 31 zinc. 4. The comparison of grain size with Brinell hardness on identical samples of annealed metal. In their comprehensive and thorough investigation of the recrystal-lization of cold-worked alpha brass on annealing,l Mathewson and Phillips have discussed the relations between temperature of anneal, degree of deformation, and structural alteration in alpha brass. They have also shown certain comparisons between the ordinary physical properties and the grain size of annealed brass. The purpose of the present investigation is mainly concerned with the grain size of cartridge brass, its relation to Brinell hardness, and the publication of sufficient data to enable those engaged in the inspection of such material to have a correct foundation upon which to work. The first alloy was taken from regular mill stock that had been rolled from 0.580 in. to 0.376 in. (14.7 mm. to 9.5 mm.) gage, a reduction of 35.1 per cent. This bar (No. 1) had the following composition: Copper, 69.20 per cent.; zinc, 30.76 per cent.; lead, 0.02 per cent.; iron, 0.02 per cent. The second alloy was also taken from mill stock of 0.325 in. (8.25 mm.) gage and was rolled as shown in Table 1, in order to get four bars reduced two, four, six, and eight B. & 5. numbers respectively. This second alloy

Jan 1, 1919

By H. W. Becker, C. C. Frye, A. V. Degau, A. Masuda

Natural gas containing 25.65 per cent hydrogen sulfide and 4.75 per cent carbon dioxicle is gathered frorn eight \veih arid tratzsporrcd 26 miles at a flow rate of 160 MMcf/D and at operating pressures of frotrl 1,200 to 1,800 psig. Dry desiccant dehydrators at each wellsite tnaintaitz the dew point of the gas below 17F. Telemetering facililies permit control of field operations from a central instrunlent console. Corrosion control ineasures, design coilsiderations and material specifications pertainitz to these specia1 conditions are cliscussed. INTRODUCTION Natural gas containing 25.65 per cent H2S and 4.75 pcr cent CO, is produced from the Pine Creek field, Alta. It is dehydrated at wellheads, gathered at 2.200 psig and transported 26 miles to the Windfall field where it is delivered to the inlet of injection compressors at 1,800 psig. The daily average volume of gas transported is 160 MMcf. The project is believed to be unique in its combination of percentage of hydrogen sulfide, operating pressure and transportation distance. This paper describes the project and presents details of some of the design features, corrosion control program and centralized automatic operational control. The Pine Creek field project is one phase of a joint operation of two fields—thc other being the Windfall field. The two fields lie about 30 miles north of Edson, Alta. and 20 miles west of Whitecourt, Alta., respectively, as shown on the map (Fig. 1). They are owned by the same interests and operated according to a plan for maximum economic recovery of products. The Windfall Leduc D-3 reservoir contains a rich condensate-bearing gas containing 15.5 per cent HIS. The gas from the Pine Creek field contains only very small quantities of butane and heavier products. The Windfall reservoir is being cycled to obtain maximum condensate recovery using gas from the Pine Creek field as the displacing fluid, while producing the residue sales gas for both fields from the Windfall field. The Pine Creek field development and gas-gathering facilities are shown on the map (Fig. 2). The producing formation is the Leduc D-3 reef at a depth of 11,300 ft. The original reservoir pressure was 4,590 psia at 7,400 ft subsea and the temperature is 245F. Eight wells are equippcd with dry desiccant dehydrators with the following capacity ratings: three at 35 MMcf/D; three at 20 MMcf/D; and two at 10 MMcf/D. WELLHEAD EQUIPMENT Dry desiccant dehydrators were designed to reduce the water content of the saturated wellhead stream to 2.5 lb of water/MMcf at 2,000 psig. This specification was necessary to prevent hydrates and corrosion forming in the pipeline which will operate at temperatures as low as 20F. A typical flow diagram is shown in Fig. 3, and Fig. 4 is a photograph of one of the wellhead installations. Some of the design details given below are subject to modification in the field. The well-stream flowing temperatures range from 135 to 170F. Wellhead flowing pressures up to 3,200 psig are reduced to the dehydrator-operating pressure of about 2,100 psig by throttling through a pressure control valve. The gas is then passed through an aerial cooler where its temperature is reduced to 105F. thus removing over half

By F. A. Forward, A. H. Ross, J. Halpern

Application of the carbonate leaching process to carno-tite ores has often been limited by the difficulty of obtaining simultaneous high recoveries of uranium and vanadium. The chemical aspects of this problem are discussed and the effect of prior roasting procedures on this discovery is described. IN treating carnotite ores by carbonate leaching it is often necessary to subject the ore to a prior roast. Among the advantages that may result from roasting are: 1) improvement in settling and filtering characteristics of the ore; 2) destruction of carbonaceous impurities that would otherwise contaminate the leach solution and consume carbonate reagent; and 3) substantial increase in extraction of vanadium, which is usually low when the un-roasted ore is leached. Recovery of vanadium may be an important factor in processing carnotite ores, and the fact that vanadium is usually recovered in good yield by acid leaching has often been an economic advantage over results obtained with carbonate leaching. It has been found that response of an ore to carbonate leaching, following roasting, depends primarily on its composition and on the conditions of the prior roast treatment, particularly with regard to the roasting temperature, the atmosphere maintained above the charge during roasting and cooling, and the presence of certain reagents. These factors, especially the last, virtually determine the extractions of uranium and vanadium attainable by carbonate leaching, as well as the reagent consumption on leaching, whereas adjustment of the leaching conditions has only a limited influence. These variables were examined systematically to elucidate roasting and carbonate leaching of carnotite ores and to establish a treatment yielding high recoveries of both uranium and vanadium. Tests were conducted on samples of four different Colorado Plateau ores, described in Table I. Roasting Procedure: The roasting tests were conducted in an electrically heated furnace in which the temperature was controlled to ±15°C. The ore (usually a 500-g charge) was ground to —100 mesh, mixed with the desired reagent, and spread in a silica tray to a bed depth of about 1/2 in. During the roast the charge was rabbled at intervals of 15 min. To provide free access of air the furnace was usually ventilated; however, in a few experiments a controlled atmosphere such as carbon dioxide or hydrogen was maintained above the charge. Leaching Procedure: The pulp, generally comprising 500 g of ore and a 2000-cc solution containing 80 g per liter of Na2CO8 and 20 g per liter of NaHCO3, was agitated in an autoclave at 120°C, under 30 psi 02. Samples were withdrawn periodically, and the solution and ore residue were analyzed. Under the conditions employed, maximum attainable extractions were generally achieved in 4

Jan 1, 1959

By Edward W. Parker

IF one is to place any credence at all in the reports published in the daily press, the subject of conservation has been a very lively topic of conversation during the past 60 days, and it does not appear that the temperature of the summer months has been in any way moderated by the discussion. It is a subject in which we are all vitally interested and to which, so far as our mineral resources are concerned, both the Institute and the Geological Survey have liberally contributed. The report of the National Conservation Commission, appointed by President Roosevelt, contains a series of papers on the conservation of mineral resources, all of which were prepared by members of the Geological Survey and were compiled largely from information previously collected by that Federal bureau in the performance of its regular duties. It is not the purpose of this paper to reiterate in extenso any of the material already published. The contributions of the Survey officials to the Commission's report have been published in a separate document as Bulletin No. 394. This docunient is for free distribution and may be obtained upon application to the Director of the Survey. In the preparation of this paper I desire merely to make a few suggestions regarding the possible necessity of some restraint upon or control of one branch of the mining industry with which I have been somewhat closely associated for the past 20 years-that of coal. Most of the members of the Institute are cognizant of the suits brought by the government against the anthracite-operators in Pennsylvania, or the combination of interests commonly known as the ? hard-coal trust." No defense of any illegal combination in restraint of trade is intended, but there are some facts which should not be lost sight of, and unfortu-\

Nov 1, 1909

[Note.—The paper of Mr. Hoffman on " Practical Results in the Magnetic Concentration of Iron-Ore " (page 602); that of Mr. Langdon on "The Use of Magnetic Concentrates in the Port Henry Blast-Furnaaces" (page 599); and those of Mr. Landis on "The Determination of Iron in the Tails from Magnetic Concentration " (page 609) and "Note on Sampling Iron-Ore" (page 611), were all prepared as contributions to this discussion.] The papers of Mr. Langdon and Mr. Hoffman were presented. W. H. Hoffman, Croton Mines, N. Y.: I will add a few remarks, by way of answer to inquiries for further details. The Croton Mines are particularly well located for cheap mining. The ore-bed is very large, and so lies in relation to the railway tracks of the Harlem and other railroads that a very large proportion of our mining for several years to come can be done above these tracks. The concentrating-mill is now 400 feet from where we are working in the quarry. In blasting we never remove less than 2500 tons at a blast,

Jan 1, 1892

By ROBERT H. BOOTH

THE happy intra-plant relationships of the Bridgeport Brass Co. are largely attributable to the interest of the management in this important business factor. In furtherance of this development Carl F. Dietz, President of the Company and a member of the Institute, has contributed the novel plan for the objective presentation of business economics, described herein. All of the officers of the corporation are active in its management and they together with many other workers filling both executive and subordinate positions have a substantial financial interest in the enterprise. The viewpoint of this organization is fairly reflected by the following quotation from Roosevelt's "The Foes of Our Own Household."

Jan 1, 1924

By Edward W. Parker

THE agreement of September, 1922, between the anthracite operators and the United Mine Workers of America, which followed the 54.5 months strike during the summer of that year, contained the following provision : The parties unite in a recommendation to Congress that legislation be forthwith enacted creating a separate anthracite coal commission with authority to investigate and report promptly on every phase of the industry and the parties hereby ask the President to request the enactment by Congress of the recommended legislation. The continuance of production after Aug. 31, 1923, shall be upon such terms as the parties may agree-upon in the light of the report of the Commission.

Jan 1, 1924

By A Guinier

RECIPITATION in alloys is undoubtedly one of the most essential phase transformations in metallurgy and, besides, it is a phenomenon of great interest to physicists. It seems then that it can be chosen as a topic for an Annual IMD Lecture. Of course, the subject is a very wide one and I shall discuss here only a very restricted part of it. I should like to show why it is now considered that there is, at the beginning of the process, a stage distinct from the real precipitation, which is the pre-precipitation. We shall be chiefly interested in the atomic structure of the metal in this preprecipi-tation stage. Numerous reviews on this subject have been published recently.', ' The latest was given by H. K. Hardyh t the last meeting of the Institute of Metals in London. One of the most complete articles has been written by the late Dr. Geisler." I should like, at the beginning of this lecture, to pay a tribute to the memory of our friend Arthur Geisler. Some of the ideas which will be developed here are different from those advocated by him. But everybody knows the considerable progress in experiment and in theory which we owe to him and, personally, I deeply feel how fruitful have been the long discussions which we have had during many years. Experimental Basis of the Precipitation Problems Let us recall the essential facts pertaining to the problem of the precipitation. The starting point and the final one are well known. The initial stage is the supersaturated solid solution before quenching. The dissolved atoms replace some of the atoms of the solvent at the points of a definite lattice. It is generally considered that the distribution of the atoms is completely random, and that the lattice distortions are relatively weak. These assumptions are only an approximation. It has now beenproven", that, in some cases, the dissolved atoms have a tendency to segregate to form very small nuclei. These fluctuations of composition are greater than the normal statistical fluctuations in a purely random alloy. We shall see the role played by these nuclei later. The final state is obtained by a very long annealing at such a temperature that an equilibrium is reached in a reasonable time. The alloy is then composed of a matrix which is a saturated solid solution, much poorer than the initial one. Imbedded

Jan 1, 1957

By T. Lane Carter

Before describing the experience with the Chinese on the Rand and the work they have accomplished, it will be necessary, first, to give a brief account of labor-conditions in the Transvaal since the war, and then to show how the necessity of importation of labor arose. As is well known, the Transvaal mines are run on the dual system of labor—that is, the rough work is done by colored laborers under the superintendence of white men. From the start of mining operations in South Africa there has been the cry of shortness of native labor, due in great measure to the failure of Kaffirs to work continuously in the mines. While he works, the Kaffir is a satisfactory laborer, but his period of service is short, averaging about nine months. People unacquainted with the Kaffir have maintained that, by offering a higher wage and better accommodation, better results would be obtained from the native workers, but an increased wage simply aggravates the trouble. The Kaffir's wants are few. While at work Be spends little of his money, and before long has sufficient capital with which to buy wives and become a gentleman of leisure. Doubling the wage of the Kaffir means that he acquires a competency in half the time, so that his period of service is correspondingly reduced. In 1899, before the war, there was always a cry about the scarcity of Kaffir labor. The highest number of natives at work was in July and August, 1899, when nearly 100,000 were employed. At the outbreak of hostilities the Kaffirs were scattered far and near, many doing well during the war by working for the military authorities. On the resumption of mining operations on the Rand a serious mistake was made. Based on past experience, it was argued that if the whole industry decided to start anew with

Jan 1, 1909