Francis Drake, Bulawayo, Rhodesia, So. Africa (communication to the Secretary *):—I should like to place on record some data in addition to those given by Mr. Canby in his paper. I regret that my notes have been destroyed so that I can give no accurate measurements of the water jacket that I am about to describe. This furnace mas erected in Cerro Gordo, Inyo county, Cal., early in 1875, and I think it quite possible that it was the first applied in lead smelting. It was made of plate iron and elliptic in shape, the inner dimensions being about 54 by 42 in. by 48 in. high. The distance between the inner and outer plates was about 6 in. Tuyere holes, one at the back and two on each side, about 12 in. in diameter, were made in this, and in these were placed cast-iron water tuyeres about 16 in. long, the diameter of the blast orifice at the point being about 3 in. The height from tuyeres to feed door was about 9 ft., but the top of the charge was kept about 5 ft. above the tuyeres. There was a space of about 12 in. between the jacket and the top brick-work. This brick-work was supported by a cast-iron plate resting on four cast-iron columns. At the beginning, the jacket was lined with air-dried radial bricks, made of crushed quartz and fire-clay, as it was thought that the jacket would not stand the heat on its bare plates. After a short time the practice was altered and no lining mas put in. The jacket was closed at the top and had a steam drum connected by two pipes at the back. This steam drum was connected to the boiler in which the steam was made for driving the Baker blower, the rock breaker and the pumps. The bottom of the jacket mas also connected to the boiler. The jacket was run under boiler pressure (80 Ib.) for some time, but eventually cracks developed in the inner plate between the tuyere holes,

Jan 1, 1913

By T. L. Chu, G. A. Gruber

Silica films hare been rleposited 011 silicon substmtes at 400° to 600°C by a chemical-transport technique using hydrogen fluoride as the transport agent ill a closed system. This transport takes place from a source materia1 1071: temperature to substrates at higher temperatures, as indicated by the thermochemistry of the transport reaction. The experimental variables of- the transport process, such as the substrate temperature, the pressure pi the transport agent, and so forth, have been studied. The rate -determining step of the transport process appears to he the ),ale of chemical reaction in the source region. The transported films are similar to thermally grown silica films in physical proper-ties with the exception of 'some what higher dissolrrtion rates. SILICA films deposited on suitable substrates serve many purposes in electronic devices. They are used for the fabrication of tunneling devices, the surface passivation of devices, and the shielding of devices from nuclear radiation: and as selective masks against the diffusion of specific impurities into semiconductors. Doped silica films can also be used as sources for the diffusion of impurities into semiconductors. Several oxidation and deposition techniques for the preparation of silica films have been developed to meet the requirements of these applications. The therma1 oxidation of silicon by oxygen or steam at temperatures above 900 C is commonly used in silicon technology. The deposition techniques are perhaps more advantageous since they usually require lower temperatures and are not limited to silicon substrates. Silica films have been deposited on silicon and other substrates by reactive sputtering and chemical reactions. The sputtering of silicon in an oxygen atmosphere is capable of depositing good-quality silica films on silicon' and gallium arenide. Many chemical reactions are known to yield silica at room temperature or higher. These reactions may involve intermediate steps. However, the final step yielding silica should take place predominately on the substrate surface in order to produce adherent films. When silica is formed in the gas phase by volume reactions, no adherent deposit can be obtained. Generally, the experimental conditions of a reaction can be varied so that the surface reaction predominates over the volume reaction. The chemical reactions which have been used successfully for the deposition of silica films are briefly as follows. The pyrolysis of alkoxysilanes in an inert atmosphere or under reduced pressure has been employed to deposit silica films on germanium3 and silicon4 at 650" to 750°C in a flow system. The deposition of silica films from alkoxysilanes has also been achieved at nearly room temperature by a low-pressure plasma. Device quality silica films have been deposited on germanium and gallium arsenide by the deposition of an amorphous thin silicon film followed by oxidation at 600" to 700" . Silica films for high-temperature capacitors have been produced by the hydrolysis of silicon tetrabromide at 950°C in argon and hydrogen atmospheres.7 We have developed a chemical-transport technique for the deposition of silica films on semiconductor substrates at relatively low temperatures. The thermochemistry of the transport reaction, the experimental variables of the transport process, and the properties of the transported silica films are described in this paper. THERMOCHEMICAL CONSDERATIONS The transport of solid substances by chemical reactions in the presence of a temperature gradient has been used for the preparation of films and crystals of many electronic materials. In this technique, a gaseous reagent is chosen so that it reacts reversibly with the solid substance under consideration to form volatile products. Since the equilibrium constants of most reactions are temperature-dependent, the transport of these products to regions of suitable temperature in the reaction system would cause the reverse reaction to take place. depositing the original solid. When the equilibrium is shifted toward the formation of the solid as the temperature is decreased, the solid is transported from a high-temperature zone to a lower-temperature region, and vice versa. This chemical-transport technique can be carried out in a closed or gas-flow system. In a closed system, chemical equilibrium is presumably established in the different temperature regions of the system, and the transport agent regenerated in the deposition region repeats the transport process in a cyclic manner. The local chemical equilibrium may not be approached in a flow system: however, this system offers a greater degree of flexibility. Silica reacts reversibly with hydrogen fluoride and this reaction was chosen for the transport process. The over-all reaction between silica and hydrogen fluoride may be written as: SiO2(s) + 4HF(g-) = SiF4Ur) + 2H2O(^)

Jan 1, 1965

By Christine Alexander

Twenty years ago, the northern Oquirrh Mountains overlooking Salt Lake City were bare. Heavy logging and overgrazing combined with erosion and uncontrolled forest fires had severely denuded the mountains by the turn of the century. As a final coup de grace, a copper smelter was built there in 1906, and for the next 50 years its sulfurous fumes killed off what little vegetation remained. In 1956, Paul Rokich, a biology student at the Univer¬sity of Utah, started to surreptitiously restore the mountains. For the next 17 years, Rokich devoted his spare time and money to replanting the Oquirrhs, with the result that several thousand acres of the mountains are green again, and animals have returned: deer, elk, and rabbits thrive among olive, maple, and fruit trees, wheat grass, and sunflowers.

Jan 10, 1975

By William P. Blake

Postscript to the paper read by Prof. William P. Blake at the Lake Superior meeting, September, 1904. POSTSCRIPT.*-Since the publication of my paper upon the blackening of the surface of rocks in desert regions, I have noted that similar views of the origin of superficial discoloration in the case of certain rocks from the Salt Lake basin of Utah have been expressed by Prof. George P. Merrill. In the pamphlet, he described the brown-coated weathered boulders from Tooele county, reaching the conclusion that the discoloration was due to the solution of the manganese and iron compounds 'in the interior of the boulder, while they were in the water, and the gradual bringing of this material to the surface through capillarity and its oxidation when exposed.

Mar 1, 1905

By R. W. Regehr, R. A. Burmeister

Epitaxial growth of GaAs 1-xPx on germanium substrates was achieved using an open tube vapor transport system. The compositional range of 0.3 < x < 0.4 was examined. The best results were obtained with (311) orientation of the germanium substrate. The physical and chemical properties of the resulting layers were investigated using several techniques. Spectrographic analyses of the layers indicate substantial incorporation of germanium into the GaAs t-X Px layer. Evidence is presented which indicates that this incorporation occurs via a vapor phase transport process rather than by solid phase dijfu-sion. Electrical measurements suggest that the germanium thus incorporated behaves predominantly as a deep donor in the compositional range of 0.33 < x * 0.40 and has a deleterious effect upon the luminescent properties of GaAs1-x Px. The increasing technological importance of GaAs1-xPx for use in light-emitting devices has led to an evaluation of several aspects of existing growth processes. The method most commonly used to prepare GaAs1-xPx for electroluminescent device applications is vapor phase epitaxial growth on GaAs substrates.&apos;-4 In a typical electroluminescent diode structure the active region of the diode is entirely within the epitaxial layer and thus the electrical properties of the substrate are relatively unimportant since it is effectively a simple series resistance (assuming hetero-junction effects to be negligible). The use of germanium rather than GaAs as the substrate material is of interest for several reasons. First, GaAs of reasonable structural quality has been epitaxially grown on germanium4-2 and it is reasonable to expect that GaAs1-xPx could subsequently be deposited on the GaAs layer. Second, germanium substrates are readily available with both lower dislocation densities and larger areas than GaAs. Finally, single crystals of germanium are more economical than GaAs single crystals. The principal objective of the present investigation was to test the feasibility of growing GaAs1-xPx epi-taxially on germanium substrates, and to evaluate the properties of such layers with regard to electroluminescent device requirements. The approach used was to a) demonstrate epitaxial growth of GaAs1-xPx on germanium, and b) characterize the relevant structural, electrical, and optical properties of the GaAs1-xPx layers. The possibility of germanium incorporation into the grown layers was of special interest since there was some indication of this in previous studies of GaAs growth on germanium.5&apos;11,12 Although a study of the electrical properties of germanium in GaAs1-xPx was not an intent of this investigation, several features of the electrical properties of the layers grown in the present study which appear to be due to germanium are described. EXPERIMENTAL PROCEDURE The open-tube vapor transport system used for the epitaxial growth of GaAs1-xPx is illustrated in Fig. 1. This system utilizes the GaC1-GaC13 transport reaction and is similar in most respects to the larger system described elsewhere.&apos; The germanium substrates were n-type, with a resistivity of 40 ohm-cm (Eagle-Picher Co.). These were cut to the orientations of {100), {111), and (3111, and were mechanically polished and chemically etched in CP-4 (5 min at 0°C) prior to growth. In some cases, a GaAs substrate was employed in addition to the germanium. The orientation of the latter was {loo}, and they were also mechanically polished and chemically etched prior to growth. The initial composition of the deposited layer was pure GaAs. After approximately 10 microns of GaAs was deposited on the germanium substrate, the phosphorus content of the layer was gradually increased over a distance of approximately 15 microns to the desired concentration and maintained at this value throughout the remainder of the growth. Typical operating parameters used during growth are given in Table I. Selenium was used as a n-type dopant in several runs to facilitate comparison of the electrical properties of the layers grown on germanium with those of layers grown on GaAs substrates, which are usually doped with selenium. The concentration of H2Se in the gas phase was adjusted to a value which would normally yield a carrier density of 1 to 5 x 101 7 at room temperature in layers grown on GaAs substrates. The terminal surfaces of the epitaxial layers were examined by optical microscopy for structural characteristics. Laue back-reflection photographs (Cu radi-ation) were also made on the terminal surface to verify the epitaxial nature of the deposit. After these steps

Jan 1, 1970

By John F. Abel

In the debate between miners and ecologists, our industry has at last begun to get some of its story told. I have been told many times that it is hopeless to even try to get our side across. Some are sure that no one will believe us even when our cause is just. My reply would be that we have to tell the truth; again, again, and again. We will never convert a fanatic, but we must try to reach the reasonable and thinking people. I am encouraged because more of us are trying. Various mining companies here in Arizona have bought newspaper space to set forth some of the facts around our local environmental problems. The Arizona Mining Association co-sponsored a symposium in March: Mining and Ecology in the Arid Environment. The symposium program included tours arranged with local mining companies. The participants saw an acid plant, an acid leaching operation, an alluvial tailings dike, a tailings pond, a smelter, and a couple of open pit mines. This wouldn&apos;t phase you until you realized that half the visitors were ecologists, watershed and wild- life managers, and other assorted conservationists. It took a lot of guts. I am proud that we had that much confidence. As Pogo said, "We have met the enemy and they is us!" Actually, we met the enemy and they were just like us-concerned.

Jan 1, 1970

By N. S. Stoloff, R. G. Davies

A study has been made of the efject oj different dislocation-precipitate interactions upon the temperature dependence of the flow stress of aged Ni-14 at. pct A1 alloy. It is observed that when the dislocations bow between widely spaced (-20004 coherent Ni3Al particles the flow stress decreases with increasing temperature in the normal way. However, when the dislocations cut closely spaced (-5004 particles the flow stress is independent of temperature from -100 to 600°C, due to a balance between softening of the matrix and an increase in strength of the particles with increasing temperature. The retention of strength at high tempera-tures of commercial nickel-base alloys, which are strengthened by the precipitation of a phase based upon Ni3Al, is thought to be due to the unusual strength properties of Ni3Al. The flow stress of Ni3Al increases continuous1y from -196"C to a maximum at -600"C. It is concluded from a series of thermal-mechanical tests that the sevenfold increase in flow stress over this temperature interval is due to a lattice effect and is not diffusion-controlled. The flow stress of precipitation- or dispersion-hardened materials depends on the resistance to dislocation motion within the matrix and the extra energy required for dislocations to bow between or to cut particles. If the dislocations bow between the particles or if the strength of the cut particles is constant with temperature, then the flow stress of the precipitation-hardened alloy must decrease with increasing temperature due at least to the decrease in elastic modulus of the material. There will be softening also from thermally activated cross-slip or climb, offering an additional degree of freedom for dislocations to avoid particles. For example, in the case of nickel containing a dispersion of thoria,&apos; which most probably deforms by dislocations bowing between particles, the flow stress decreases by about 50 pct between 25" and 650°C. In A1-Cu alloys2 aged to produce the 8" precipitate, dislocations cut the particles, and the flow stress decreases by about 20 pct between -269" and 25°C. However, many commercial high-temperature nickel-base alloys, for example Inconel-X and Udimet-700, exhibit little or no decrease in flow stress with increasing temperature up to about 700°C. A characteristic feature of these alloys is that they are strengthened by the precipitation of a phase based upon Ni3A1. Guard and westbrook4 and flinn&apos; have shown that Ni3Al (and alloys in which a third element such as molybdenum or iron is substituted for part of the aluminum) is unusual in that the hardness and flow stress increase with temperature to a maximum at about 600°C. For the flow stress of a precipitation-hardened alloy to be independent of temperature we propose that the particles must be cut by dislocations moving through the matrix and that the strength of the particle must increase with increasing temperature. Theories of precipitation hardening do not take into account the flow stress of the dispersed particles that are cut during deformation; the only dissipative process usually considered7 is the creation of interface within the particle and between the precipitate and matrix. The purpose of the present investigation has been to study in detail the temperature dependence of the flow stress of a nickel-base alloy strengthened by the precipitation of Ni3Al in two structural conditions such that when deformation occurs it does so by dislocations a) bowing between the particles and b) cutting the particles, respectively. A simple binary Ni-14 at. pct A1 alloy was chosen because considerable information is already available for this system concerning phase equilibria and precipitation reactions and rates.&apos; Dislocation-precipitate interactions in the binary alloy should be similar to those in the more complex commercial alloys. In addition, the mechanical and physical properties of NisAl were studied in detail in the hope of elucidating the mechanism by which the strength increases with increasing temperature up to 600°C. EXPERIMENTAL PROCEDURE For the study of the effect of precipitation of Ni3A1 upon the temperature dependence of the flow stress, an alloy containing 14 at. pct A1 was utilized; a Ni-8 at. pct A1 solid-solution alloy was employed as a comparison material. Vacuum-cast ingots were hot-rolled at 1000°C and cylindrical compression samples, 0.20 in. diam by 0.40 in. high, were prepared from the 1/4-in.-diam rod. Specimens were recrystallized and solution-treated at 1000°C for 1/2 hr and then water-quenched. A preliminary study revealed that, when the Ni-14 at. pct A1 alloy was aged for 1 hr at 700°C, significant precipitation hardening was obtained, and that the structure was free from grain boundary discontinuous precipitation; an overaged condition was produced by annealing the aged specimens at 850°C for 1 hr. To circumvent the difficulties involved in the hot rolling and swaging of Ni3A1, compression samples,

Jan 1, 1965

BECAUSE it is necessary that the powders made for casting have a magistery of salt water, I wish now to teach you to prepare the salt that must form this magistery, for without it these powders would not have the toughness to hold themselves together when they are dry. In short, you take the quantity [119v] of salt that you need to prepare and put it in a rough pot, either baked or, if it suits you better, raw but well dried. This is completely covered with a lid or is luted with well- made moulding clay. Then it is encircled with brick ends at a distance of three dita, like a drying furnace. This space is filled with good charcoal; fire is applied and it is left to stand until all the charcoal is consumed by itself* Then you take that quantity of this burned or rather melted salt which you wish to use for moistening the clay and which you think can be dissolved in the water so that it wd remain very salty. It is boiled in a pot with water and then left to stand. After it has settled, your powder is moistened with it and used for moulding. When you see by testing it that the powder stands up as you wish, it is good. If not, give it some more of this water again and continue until you see that it holds enough. For without this magistery it would return to the dryness that it had before as a powder, and you could not use it without fear that it would fall from the Games. In this way this earth, either natural or artificial, is prepared and made ready, and it is used as the need occurs.

Jan 1, 1942

By H. J. McQueen, G. C. Kuczynski

ThE useful properties of k6-Alfenol and the thermenol alloys (summarized by J. E. Nachman and W. J. Buehler&apos;) have encouraged research into those alloys which, having compositions near 25 at. pct Al, 75 at. pct Fe, undergo an ordering transformation between 500° and 550°C. The equilibrium diagram of the iron-rich iron-aluminum alloys was first determined by Bradley and Jay.2,3 They distinguished three structures: the disordered, which is bcc; FeAl, which is simple cubic with one Fe atom and one Al atom per lattice site; and Fe3Al, which is fcc with three Fe atoms and one Al atom per lattice site. This last structure may be conceived as eight body-centered cubes with Al atoms at the centers of alternate ones, so that Al atoms have only Fe as first and second nearest neighbors. Later, Osawa and Murata4 determined the boundaries of the different superlattice regions in the iron-rich Fe-Al solid solution by dilatometric and X-ray methods. Two of the six phases, which they found between 0 and 50 at. pct Al, were never identified by other workers. A. Taylor and R. M. ones,&apos; concurrently with and independently of this research, redetermined this diagram by measuring lattice parameters at temperature. Further reference will be made to their results. EQUILIBRIUM DIAGRAM A) Experimental Procedure—The alloys were prepared from NRC gas-free iron (99.9 pct Fe) and 99.99 pct Al. They were melted in alumina&apos; crucubles under vacuum in an induction furnace. If the ingots were unsound or showed more than a 3 pct weight loss, they were rejected. The ingots were homogenized at 1100°C for 24 hr before hot-rolling at 700" to 900°C from 1 in. to 0.25 in. thick. It is interesting to note that alloys containing more than 28 at. pct Al were able to take an 80 pct reduction of area in the ordered FeAl region. The dilatometer specimens and specimens for chemical analysis were cut from these plates. A Leitz dilatometer was used to measure the coefficient of linear expansion as a function of temperature. The specimens were slowly cooled from 900" to 300°C where they were annealed for 10 hr before slowly cooling to room temperature. The expansion was recorded photographically as the alloys were heated and cooled at 1.5oC per min between 100" and 1000°C. The magnetic measurements determining the Curie points were performed on the dilatometer specimens in the dilatometer, by using direct current in the furnace windings both to heat the specimen at 1.5°C per min and to serve as the primary coil. The regular specimen holder was replaced by a thin alundum tube on which was wound, as a secondary, a closely spaced coil of fine copper wire. A reversal of current in the furnace windings produced, in the secondary, an emf which was proportional to the induction in the specimen, and which could be detected on a galvanometer. In this way, it was possible to determine the Curie points of alloys to within * 5°C. B) Results and Discussion—The coefficients of linear expansion, as obtained from the dilatometer curves, are plotted as a function of temperature and composition in Fig. 1. Since in many cases the heating and cooling curves were superimposed, it was decided to measure slopes of heating curves only. Definite high peaks, due to the transformations, were observed on each curve between 400" and 520°C, and, for alloys containing more than 23 at. pct Al, a second set of smaller peaks at temperatures above 660°C. The sharpness of the peaks indicates that ordering to Fe3Al is a first-order reaction. The compositions and the temperatures of these peaks are listed in Table I. When these temperatures are plotted as a function of the composition, the result is the constitution diagram presented in

Jan 1, 1960

By R. A. Davidson, L. Silverman

RESIDENTS of many urban centers are becoming increasingly aware of the obscuring effect of fume and smoke discharge from power, metallurgical, chemical, and other industries; and they, as well as the legislatures of these affected cities, are agitating for cleaner air. Management&apos;s most pressing problem is to find an economical way to reduce process effluents in response to the growing pressure from population and legislative demands. The removal must be done, if possible, without handicap to the current operation, since the costs of relocating are often excessive or prohibitive. In fume recovery or disposal, an important item to consider is whether or not the material being discharged has any value. If it has commercial value, the cost of its recovery may offset or aid amortization. For this reason, in making a study of the specific problem in hand, a major factor was the nature of the material emanating from the stack: in particular, its particle size, size range, and its chemical and physical composition, as well as its potential value and utility when recovered (in either a wet or dry state). Should the product have no commercial value, it must be disposed of at minimum cost in a way to prevent recontamination. Initial studies were therefore made to determine stack concentrations and volumes of material evolved from the operations. The next phase of the study concerned the physical and chemical nature of the collected fume. The third portion of this paper describes the wet and dry collector studies undertaken to recover the fume. Cleaning Requirements for Ferroalloy Furnace Operation The basic need for any effluent collection equipment is the highest possible efficiency and the lowest tolerable resistance when the power consumption involved is considered. Since the electric furnace effluent is largely composed of fume of small size (less than 0.5u), it has high light obscuring properties, and even low concentrations will cause some loss of visibility and be evident to nearby residents. The permissible limit for fly ash emission in many cities is based on a weight value (viz, approximately 0.4 grains per cu ft), but the smoke density values are dependent upon a shade of color. In the case of the Los Angeles County code, emission is restricted to pounds per pound of material processed per hour basis (but not exceeding 40 lb per hr for any one given plant operation). If an average particle size of the fume from ferro-silicon alloy electric furnaces is assumed to be 0.4u (as shown later, this is the approximate mean size) and an average loading of 1 grain per cu ft (stp), each cubic foot of stack gas will contain approximately 75x10 10 particles (based on assumed, and confirmed, spherical shape and a standard deviation of unity). When it is realized that the air in metropolitan areas, which are also general industrial areas, contains approximately 5x108 particles, the tremendous light scattering effect of this concentration becomes apparent. Consequently, nearly 100 pct collection would be necessary to equal the average concentration. Fortunately, however, discharge from a high point above ground (50 to 100 ft) will result in at least a thousandfold dilution, or the stack concentration reaching the ground in the foregoing case might result in a ground concentration of &apos; particles. If the concentration at the source could be reduced by a factor of 100 (99 pct efficiency of collection), then a concentration of 75x10" particles would be diluted to 7.5x10&apos; which would be very satisfactory. An efficiency of 90 pct (factor of 10 decontamination) at the source would result in a discharge of 75x109 articles which upon dilution yields 75x10 which is still 15 times the general air value. Another approach to this consideration is to use the value of concentration of 0.005 grains per cu ft for the value of a visible effluent as cited by Kayse.1 To attain this value with an average loading of 1 grain per cu ft would require an efficiency of 99.5 pct. Since the foregoing value is not based on any reported size of fume particles, it is felt that the numbers&apos; approach given previously is more reliable. These calculations serve to indicate the desirability of thorough cleaning, preferably at the source, and with efficiencies well above 90 pct, preferably above 95 pct (dilution 1:20). One of the most important items in any control program is to reduce the concentrations as close to their sources as possible. The use of better furnace design, deeper coverage over the electrodes, and the prevention of blows or breaks in the surface all help to reduce dissemination; consequently, all of these improvements should be made, if possible, to cut down the effluent load. In addition, in order to minimize the volume of contaminated air that has to be cleaned, the furnace should be enclosed as much as possible. Test Arrangements Before fundamental studies with collectors were made, a furnace stack selected for the test program was sampled to determine the gas temperatures and

Jan 1, 1956

By C. A. Hartnagel

The production of petroleum in New York in 1940, totaling 4,999,000 bbl., was only slightly under the amount produced in each of the previous three years. The year 1940 started auspiciously with a posted price on Jan. I of $2.75 a barrel. Four price reductions, beginning in May, resulted in August in a low of $1.85 a barrel, after which two increases brought the year&apos;s closing price to $2.15 a barrel. The favorable crude price at the beginning of the year stimulated an increased drilling program, especially in the water-flooding districts. In the Allegany County region, which accounts for about two-thirds of the state&apos;s oil production, 886 wells, including water-intake wells, were drilled; 200 more than in the preceding Year. During the closing months of the Year there was a marked decline in the number of wells drilled. The unfavorable position in which the industry found itself before midsummer was due largely to the loss of export markets for its high-grade lubricants, constituting approximately 25 per cent of its business. As a result of this situation, runs to refineries were curtailed as much as 30 Per cent at the middle of the Year. Improvement in market conditions toward the end of the Year found the stocks of available crude at an almost record low. Deep DRILLING with the gradual exhaustion of some of the important natural and flood-oil-produc-ing areas of the Allegany and Bradford pools, overproduction will not be a serious problem in the future. The possibility of finding new territory or deeper producing sands has been further lessened by the drilling of additional deep wells for gas in and about the present oil fields. Many of these wells drilled to the Oriskany sand-stone were over 4000 ft. deep and have tested the entire thickness of the Devonian formation, the upper 2000 ft. of which contain all the important oil-producing strata in the state. Water-flooding It is thus evident that the problem of the New york oil producers is not one of find-ing new supplies but of obtaining as much 6 oil as possible from the old developed fields that during the 60 years of their life have 1 produced I 3o,ooo,ooo bbl. of oil. Although a few floods were in operation before I9I9, when the production of oil by flooding was 1 made legal, the output for that year amounted to only 85I,000 bbl. From 1919 I on there has been an almost constant increase, which during the past four years has averaged well above 5,000,000 bbl. annually. During the last 22 years, which constitutes the period of important flooding operations, 651337,000 bbl. of oil have been produced in the state. Careful estimates indicate that between one-third and one-half of the oil fields are being flooded or are already watered out. Some of the flooded and watered-out areas include territory with unusually thick sands, which were highly productive during the early history of the fields. From a recent study of operations in the New York oil fields, it is estimated that about 65,ooo,oo bbl. of oil

Jan 1, 1941

By C. A. Hartnagel

The production of petroleum in New York in 1940, totaling 4,999,000 bbl., was only slightly under the amount produced in each of the previous three years. The year 1940 started auspiciously with a posted price on Jan. I of $2.75 a barrel. Four price reductions, beginning in May, resulted in August in a low of $1.85 a barrel, after which two increases brought the year&apos;s closing price to $2.15 a barrel. The favorable crude price at the beginning of the year stimulated an increased drilling program, especially in the water-flooding districts. In the Allegany County region, which accounts for about two-thirds of the state&apos;s oil production, 886 wells, including water-intake wells, were drilled; 200 more than in the preceding Year. During the closing months of the Year there was a marked decline in the number of wells drilled. The unfavorable position in which the industry found itself before midsummer was due largely to the loss of export markets for its high-grade lubricants, constituting approximately 25 per cent of its business. As a result of this situation, runs to refineries were curtailed as much as 30 Per cent at the middle of the Year. Improvement in market conditions toward the end of the Year found the stocks of available crude at an almost record low. Deep DRILLING with the gradual exhaustion of some of the important natural and flood-oil-produc-ing areas of the Allegany and Bradford pools, overproduction will not be a serious problem in the future. The possibility of finding new territory or deeper producing sands has been further lessened by the drilling of additional deep wells for gas in and about the present oil fields. Many of these wells drilled to the Oriskany sand-stone were over 4000 ft. deep and have tested the entire thickness of the Devonian formation, the upper 2000 ft. of which contain all the important oil-producing strata in the state. Water-flooding It is thus evident that the problem of the New york oil producers is not one of find-ing new supplies but of obtaining as much 6 oil as possible from the old developed fields that during the 60 years of their life have 1 produced I 3o,ooo,ooo bbl. of oil. Although a few floods were in operation before I9I9, when the production of oil by flooding was 1 made legal, the output for that year amounted to only 85I,000 bbl. From 1919 I on there has been an almost constant increase, which during the past four years has averaged well above 5,000,000 bbl. annually. During the last 22 years, which constitutes the period of important flooding operations, 651337,000 bbl. of oil have been produced in the state. Careful estimates indicate that between one-third and one-half of the oil fields are being flooded or are already watered out. Some of the flooded and watered-out areas include territory with unusually thick sands, which were highly productive during the early history of the fields. From a recent study of operations in the New York oil fields, it is estimated that about 65,ooo,oo bbl. of oil

Jan 1, 1941

By D. Turnbull, R. E. Cech

FISHER, Hollomon, and Turnbull have developed a theory for the nucleation of martensite. They first tested the theory on Fe-C alloys and low alloy steels. The major factor influencing nucleation of martensite was considered to be statistical composition fluctuations occurring in small regions at high temperature and frozen-in on quenching. These local regions of varying size and composition serve as nucleation centers. They become supercritical, one by one, as temperature is progressively lowered, resulting in temperature-dependent or athermal transformation. Fisher next applied nucleation theory to substi-tutional solid solution alloys. Detailed predictions were made for Fe-Ni alloys because of the availability of free energy data on this system. It was shown that composition fluctuations that were significant energy-wise did not occur, and nucleation frequencies could be calculated from average properties of the system. Nucleation was predicted to occur as time-dependent and having the functional relationship to give a C curve of nucleation frequency vs temperature. The analysis further predicted that the nucleation frequency was extremely sensitive to composition. Experimentally, it would be found that the transformation in some compositions is so slow that measurable amounts will not form in a reasonable length of time. With other compositions, only slightly different, the nucleation frequency becomes so great that the material becomes transformed while still distant in temperature from the maximum nucleation frequency. On quenching an alloy of such composition, the observed transformation kinetics would be similar to those found in Fe-C alloys. Cech and Hollomon repeated experiments of Kurdjumov n which the kinetics of transformation were similar to those predicted by Fisher for Fe-Ni alloys. The alloy studied in this investigation contained 73.3 pct Fe, 23.0 pct Ni, and 3.7 pct Mn. Fisher,&apos; using an idealized model for the extent of transformation as a function of the number of martensite crystals per grain of parent phase, derived nucleation frequencies from the transformation curves of Cech and Hollomon. Complicating influences such as coupling effects between grains in the polycrystalline specimens were neglected. Nevertheless, excellent agreement was found between the theoretically and experimentally derived nucleation frequencies. These experiments, however, could not provide a critical test of the theory. Experimental nucleation frequencies could vary widely from those calculated, depending upon the extent of deviation from ideal partitioning and the extent of coupling effects. Further, since the compositions of material theoretically analyzed and experimentally determined were different, the free energy changes involved in the experimental work could only be estimated. Also, the effect of heterogeneities on the transformation kinetics was not considered. For these reasons, it was decided that experiments designed to test the validity of the Fisher analysis must be conducted on binary Fe-Ni alloys, which were the ones considered theoretically by Fisher. The martensite transformation in Fe-Ni alloys has been the subject of considerable study. Machlin and Cohen have shown that transformation proceeds in a manner quite unlike that in any other ferrous alloy system. They found that single crystals would transform to a large extent in a single burst. In large grain polycrystalline specimens, frequently more than one grain and sometimes the whole specimen would transform at the same instant in this manner. Results on filings indicated that different particles would undergo the burst transformation at widely different temperatures. These results support the conclusion that the transformation behavior could not be described by a single nucleation frequency as would be the case if the nucleation were homogeneous. It appeared that further work was necessary to define the factors responsible for burst-type transformation, so that the conditions could be altered to favor homogeneous nucleation of martensite if such could be accomplished. This report summarizes the results of some experiments conducted with powdered Fe-Ni alloys for this purpose and the re-

Jan 1, 1957

By N. H. Jensen, B. L. Sackett, Carlos Bardwell, Simon Jacobson

Lead smelting has been an important industry in Utah for many years. The first lead smelting was done, over 60 years ago, at the Rollins mine in Beaver County, by burning heaps consisting of alternate layers of wood and high-grade carbonate ore. The lead thus obtained was molded into bullets. With the development of the mines, the problem of cheaper handling of the ore became important. The only outlet for this ore was Swansea or the Atlantic Coast but to ship to either cost $150 per ton or more for treatment and handling. From 1864 to 1871, experimenting was done with blast, Scotch hearth, and reverberatory furnaces, with the blast furnace surviving as the standard plant. The first crude furnaces were circular or hexagonal in shape, and were made of adobe and stone, which quickly burned out. They were small, about 21/2 ft. in diameter, and smelted from 3 to 10 tons in 24 hr. The metal had to be tapped from the bottom of the crucible, necessitating a shut down of the furnace during this process. This procedure caused salamanders to form around the tap hole when the furnace was started again, which frequently resulted in freezing. The campaign lasted until a tap of bullion was made. The first successful plant of the crude stone type was operated in 1870. From 1870 to 1872, there was a smelter building craze in the state. During that period, about 20 furnaces were built, chiefly near the mines, and their operation was limited and sporadic. The work was then placed in the hands of trained metallurgists, who standardized on the rectangular form of furnace. In 1871, Daggett, at the Winnamuck mine in Bingham, installed water-jackets around the smelting zone of the furnaces. These furnaces were circular; the diameter at the tuyere line was 3 ft. 6 in. and at the charge floor 5 ft. 3 in. The height from tuyere line to charge floor was 14 ft., height of tuyere line above top of crucible was 3 ft. 8 in. Furnace capacity was about 14 tons per day, with a campaign of about 16 days. Cost of smelting was about $44 per ton. The ores making the

Jan 1, 1926

By G. W. Gross

A commercial deposit of white kaolinite clay contained in the sandy overburden of the Cambrian Gatesburg formation in Central Pennsylvania was successfully mapped by combined SP and resistivity methods and results were checked by drilling. Resistivity minima in the range between roughly 2000 and 3500 ohm-meters coupled with second-order SP maxima of 50-60 mV contrast were found to characterize commercial white kaolinite clay beneath not more than 30-40 ft. of sandy overburden in the area stdied. This investigation supports the hypothesis, established previously, that certain SP phenomena may reasonably be ascribed to diffusion and membrane potentials produced by interaction of clay lenses, sandy matrix, and ground waters. The success of this test proves that this prospecting technique can assist in locating clay deposits in sandy overburden derived from the weathering of sandstones and carbonate rocks such as the Cambrian formations of Central Pennsylvania. In a recent paper, Gross and Moore (1959) described broad self-potential minima above the outcrops of the Cambrian Gatesburg formation. These "first-order" SP anomalies, of 220-350 mV contrast (Figure 7), are related to the peculiar sandy residual soil covering the Gatesburg formation. Small positive ("second-order") peaks of 50-60 mV contrast are superposed on the bottom or flanks of the first-order troughs. They appear to be related to lenses and layers of kaolinite clays within the sandy Gatesburg overburden. Both first-order and second-order anomalies show a characteristic inverse relationship with apparent resistivity profiles in most cases. An explanation in terns of liquid-junction and shale potentials was advanced. According to this working hypothesis, shale potentials are generated: 1) at the contact of the sandy Gatesburg overburden with the more argillaceous soils of surrounding formations; 2) at the boundary of clay lenses contained in the sandy matrix of that overburden. Concentration gradients between interstitial infiltration waters and perched water tables within the Gatesburg overburden are believed to give rise to the liquid-junction potentials. In order to test this hypothesis further, a detailed study was carried out of a second-order positive anomaly on the property of the Woodbury Clay Co. at Mines (Blair County, Pa., Hollidaysburg folio of the U.S. Geological Survey). A second aim was to establish if combined SP and resistivity surveys are suitable as a practical method for delimiting favorable areas in which commercial kaolinite clay de~osits may be found by drilling. Drilling control was provided by the Woodbury Clay Co. PROCEDURES Instrumentation used for SP measurements was the same as described in the paper mentioned. For resistivity surveys, a direct-current voltmeter-ammeter device built by Georator Gorp. of Manassas (Va.) was used in combination with non-polarizing electrodes from the same manufacturer. Power was supplied by one to six 45-volt, heavy-duty B-batteries

Jan 1, 1961

By R. J. Teitel

The Pb-U system has been investigated by X-ray, thermal, and microscopic analyses. Two pyrophoric intermetallic compounds were found; UPb3 and UPb. The crystallographic structure of UPb3 is reported. A phase diagram was drawn for the system showing three eutectic and one syntectic reaction. AS a result of the interest in uranium metallurgy, the Pb-U system has been investigated. Practically no quantitative data appears in the literature concerning this system. Chips were machined from bars of high-purity uranium obtained from Ames Laboratory and the lead was 99.9 pct high-purity grade from Bel-mont Smelting & Refining Co. The chips were pickled in a dilute solution of nitric acid, washed in water and then alcohol, and dried prior to use for alloy preparation. The lead was simply sheared from the pig with no chemical treatment. Lead and uranium were placed in graphite crucibles and loaded into an induction furnace. In order to insure good alloy formation, the lead was loaded above the uranium to wash the uranium chips into the melt. After the charge was held at the desired preparation temperature for 15 to 30 min, it was allowed to cool in the crucible. The entire melting operation was accomplished in an atmosphere of helium (double charcoal refined grade with no further treatment). The procedure was to outgas the furnace by first evacuating it to 10-% m Hg, admitting helium to 8 psi gage and sealing the furnace off. An optical pyrometer focused on the charge through a hole in the crucible cover was employed for thermal measurements. Usually a 50° to 70°C correction had to be added to the instrument value. The most suitable alloy preparation temperature range was found between 1220° and 1280°C. The reason for this is explained by the phase diagram, Fig. 7. Above this temperature range two liquids separate preventing alloy formation upon cooling at a reasonable rate. On the other hand, below this range the uranium was coated with a layer of both compounds and the rate of reaction was diminished by diffusion processes. The fastest reaction rate occurred in this narrow range of temperature because only UPb coats the uranium and it evidently does not protect the uranium as well as UPb,. Apparatus and Procedures The development of apparatus and techniques was determined by the peculiar properties of the alloys. All the alloys were pyrophoric, and, consequently, the alloys had to be protected from oxidation by handling them in a dry box or inert atmosphere furnaces. Other operations performed outside of this equipment had to be done as quickly as possible. Thermal analyses were conducted in a furnace and arrangement similar to that described by the author.&apos; Graphite crucibles having a thermocouple well in the bottom were used to contain the prepared alloy, while a helium atmosphere protected the melt from oxidation. The furnace was outgassed by pumping a 10-3 mm Hg vacuum until the furnace had been heated to 400°C. Then helium was admitted and the furnace sealed under 8 psi gage pressure. Chromel-alumel thermocouples were used for thermal analysis and the accuracy of thermal measurements was judged to be k 5°C. At first, an attempt was made to use platinum-platinum-rhodium thermocouples, but evidently lead vapors attack it at high temperatures forming low melting alloys. These lead vapors had direct access to the thermocouple because the graphite crucible was porous. A differential temperature control was used to regulate thermal analyses. The thermal gradient across an alundum tube placed between the windings and the crucible was maintained constant by a controller.

Jan 1, 1953

By J. Allen Veatch

THERE exists in., the territory embraced between the summit of the Sierra Nevada and the coast a great dike and vein system that appears never to have been recognized in its entirety, nad many facts concerning it have never been published. This is important, not only in affording numerous clues bearing on the origin, nature, and age of the mercury deposits, and eliminating many controverted questions, but it. incidentally affords numerous facts bearing on the genesis of gold, copper, chromite, magnesite, dolomite, a type of calcite deposit, and numerous associated minerals. The mineral springs of the State almost without exception emanate from these dikes. A great range of the hydrocarbons also exists throughout the entire system of these dikes. Seepages from their, walls have frequently been mistaken as emanating from the inclosing sandstone and shale, resulting in heavy expenditures in the futile development of these Cretaceous beds, which contain no petroleum within the territory. The theory of mountain making by lateral or tangential pressure is inconsistent with some of the following recorded facts. The limitations of this paper do not admit of a description of each of the hundred or more mercury deposits embraced in the area, and therefore only typical examples will be described. The accompanying map, Fig. 1, is not submitted as complete, or as entirely accurate, but it is as nearly so as the notes at hand will admit. The field is too extensive to be completely covered by a single individual. The heavy continuous lines represent sections actually surveyed! The sections and extensions- in. dotted line are assumed, and are either unsurveyed, or -buried under younger beds. There are numerous branches connecting the great parallels that the small-scale map does not admit of plotting, even if the survey had been complete. Likewise, the conclusions in some instances may be faulty, but it is to be hoped that as a whole they may serve as a foundation on which a more complete structure may be built in the future.

Jan 2, 1914

By D. A. Stevenson, R. A. Burmeister

Single-phase silver antimony telluride has been prepared by zone-melting techniques using initial compositions of A new phase appears upon prolonged annealing of this material, but the reaction does not appear to be a simple eutectoid decomposition. A complete analysis of the phase equilibria is complicated by the slow kinetics involved. The Hall coefficient, magneto -resistance, electrical resistivity, and Seebeck coefficient are all sensitive to the presence of second phases. The low Hall mobilities measured for single-phase material indicate that the usual band theory is inadequate to explain the observed transport properties in the system. Density anomalies of up to 2.5 pet between measured and theoretical density were observed but are not conclusive evidence for a defect structure. COMPOSITIONS in the Ag-Sb-Te system have been studied previously by several investigators.1"18 The interest in this system arises from potential thermoelectric applications of alloys on the Ag2Te-Sb2Tes vertical section. Although the composition corresponding to the formula AgSbTe, has received most attention, it has been found to consist of more than one phase.7&apos;8 A thorough understanding of the properties of this heterogeneous material has been impeded by both lack of knowledge of the properties of the homogeneous phases comprising it and the problem of analysis of transport properties in an inhomogeneous system. The present work describes the preparation of the homogeneous ternary phase and the corresponding electrical properties of both homogeneous and heterogeneous material. MATERIAL PREPARATION Most specimens for this investigation were prepared by encapsulating the elements in evacuated quartz tubes after which they were melted and homogenized in the liquid state. The ambient temperature was then dropped to 500°C and the resulting ingot zone melted. The growth rate, width of zone, stoichiometry, and number of passes have an effect on the resultant microstructure. Grains several centimeters in length were easily produced by this method. Other solidification techniques were also used, including uniform slow cooling of the entire specimen and rapid freezing. The microstructures of specimens produced by these techniques frequently differed appreciably from similar compositions prepared by zoning. A variety of nonequilibrium microstructures characterized by long needlelike particles resulted from the rapid-freeze method. PHASE EQUILIBRIA The lack of information on phase equilibria is a major difficulty associated with a comprehensive study of the Ag-Sb-Te system. Considerable confusion has resulted from the use of the formula AgSbTe, to identify the cubic ternary intermediate phase even though it has been established that material of this stoichiometry normally contains AgzTe as a second phase.798 In this paper, silver antimony telluride will denote the cubic ternary intermediate phase comprising the major portion of AgSbTe,. The term "single phase" will denote material which consists of only the cubic phase (as evidenced by metallographic examination and X-ray diffraction) and the term heterogeneous will describe multiphase material containing AgzTe, SbzTe3, or other phases in addition to the cubic phase. The single-phase material may actually contain a variety of inhomogeneities—gradual changes in composition on a macroscopic scale, localized fluctuations in composition, clusters or other products of early stages of the precipitation process, and a variety of point and line defects—all of which will not be detected by the present techniques for determining homogeneity. Single-phase material has been prepared from compositions close to 59 mole pct SbzTe3 21 (this notation refers to the location on the Ag,Te-Sb2TeS vertical section). Zone widths of =2 cm and growth rates 51.2 cm per hr were used. The single-phase region at elevated temperatures extends off the vertical section to a composition which can be expressed approximately as Ag,,SbzgTes,.9 The latter two compositions as well as AgSbTe, are represented in the conventional Gibbs triangle in Fig. 1. It is not presently possible to ascribe exact values to the limits of the single-phase region on a given isotherm or vertical section due to the extremely

Jan 1, 1964

By J. J. Gilman

The data presented indicate that the critical shear stress and strain-hardening Thedatapresentedrate of a zinc monocrystal depend on the orientation of its slip direction with respect to its external boundaries. The tendency of a crystal to form deformation bands also depends on its shape. THE plastic behavior of pairs of zinc monocrystals in which both members of the respective pairs had the same orientation with respect to the longitudinal axis, but each had different orientations with respect to their rectangular external shapes, were compared in this investigation. The purpose of the investigation was to see what influence the shape or surface of a zinc crystal has on its mechanical properties. In a previous investigation of triangular zinc monocrystals,1 anomalous axial twisting was observed which seemed to be related to the triangular shape of the crystals. Wolff,&apos; in 400°C tensile tests of rectangular rock-salt crystals bounded by cubic cleavage planes, found that, of the four equivalent slip systems, the two with the "shorter" slip directions yielded and produced slip lines at lower stresses than the other two. This observation and the work of Dommerich³ as formulated by Smekal4 as a "new slip condition" for rock-salt: "among two or more slip systems permitted by the shear stress law, with reference to the formation of visible slip lines by large individual glides, that slip system is preferred which has the shortest effective slip direction." More recently, Wu and Smoluchowski5 reported essentially the same effect for ribbon-like (20x2x0.2 mm) aluminum crystals at room temperature. Experimental Chemically pure zinc (99.999 pct Zn), purchased from the New Jersey Zinc Co., was the raw material. Glass envelopes, containing graphite molds and zinc, were evacuated while hot enough to outgas the graphite but not melt the zinc. At a vacuum of about 0.2 micron the envelopes were sealed off and then lowered through a furnace at 1 in. per hr so as to melt and resolidify the zinc and produce mono-crystals. One-half of one of the molds is shown in Fig. la. Each mold consisted of four pieces from a cylindrical graphite rod that was split longitudinally and transversely at its midpoints. Rectangular milled grooves 0.050 in. deep and % in. wide formed the mold cavity when the split halves were assembled with twisted wires. Fig. lb shows the specimen shape obtained when the top and bottom mold-halves were rotated 90" with respect to each other. Good fits prevented leakage and excess zinc was necessary to provide enough liquid head to fill the mold completely. In removing soft crystals from the molds it was impossible to avoid small amounts of bending. However, manipulations were carried out whenever possible with the crystals protected by grooved brass blocks. All specimens were annealed prior to testing. From the top and bottom sections of each crystal, X-ray specimens and tensile specimens 7 to 8 cm long were sawed. The tensile specimens were annealed inside evacuated tubes for 1 hr at 375°C. Next the crystals were cleaned and polished by 2-min dips in a solution of 22 pct chromic acid, 74 pct water, 2.5 pct sulphuric acid, and 1.5 pct glacial acetic acid.&apos; Cleaning was followed by a 10-sec dip in a 10 pct caustic solution, then washed in water and alcohol, and dried. This treatment results in a bright surface covered by an invisible oxide film. The testing grips were a slotted type with set screws and were supported in a V-block during the mounting operations in order to avoid bending the crystals. A schematic diagram of the recording tensile-testing machine is shown in Fig. 2. The machine has been described elsewhere.&apos; The head speed was 0.3 mm per sec for all tests. The crystal orientations were determined by the Greninger X-ray back-reflection method with an estimated accuracy of 1. Description of Crystal Geometry A schematic picture of a rectangular zinc mono-crystal is shown in Fig. 3. ABD designates the front edge of a basal plane (0001) of the crystal, the only active slip plane for zinc at room temperature. Of the three possible (2110) slip directions, the active one is indicated by an arrow. Cartesian coordinates are taken parallel to the specimen edges. The normal, n, to the basal plane (n is parallel to the hexagonal axis) has the direction cosines a, ß and ?. X0 = 90 — y is the angle between the longitudinal axis and

Jan 1, 1954

The use of the verb in this mood is not as common as formerly: at the time, for example, when the Bible was translated and the plays of Shakespeare were written. Nevertheless it is an essential part of literary English. In editing the &apos;Mining and Scientific Press&apos; I do not insist upon the use of the subjunctive in articles that are contributed from the outside, but it is deemed proper in all our editorial writing. To speak plainly, the subjunctive is a mark of scholarship; it is ignored by those that are not particular in such matters, and unfortunately it is a source of perplexity to many that are entirely unfamiliar with the use of it. Therefore, as an editor, I think it well to allow the indicative mood to be used by contributors in sentences in which, to be strictly correct, the verbs should be in the subjunctive mood. The fact that most subjunctives are indistinguishable in form from indicatives is another cause of trouble to the uninitiated.* For example, the verbs in such phrases as "Suffice it to say", &apos;(So help me God ", and "God save the King" are in the subjunctive. One reason why the subjunctive is becoming uncommon is the growing habit of expressing the subjunctive meaning by aid of auxiliary verbs that are coupled with the infinitive; thus: "It will sate to say" and "May God save the King". The subjunctive is common in subordinate clauses, and that is how it obtained its name, &apos;subjunctive&apos;, meaning

Jan 1, 1931