By Toshia Ishii, Jun Kubota, Noriko Kubo

"For steel continuous castings, it is essential to control molten steel velocity at the meniscus, since the velocity is closely related to surface defects on the resultant products. Argon gas is supplied with molten steel into the mold through the submerged entry nozzle to prevent nozzle clogging. In this study, to investigate the influence of argon gas on molten steel flow, a numerical simulation was carried out by a two-phase model. Simulation results indicate that as argon gas bubbles ascend near the nozzle by their buoyancy, they induce the molten steel flow with them and resulted a meniscus molten steel flow from the nozzle to the narrow face of the mold. This flow direction is opposite to the case without argon gas. The calculated data are compared with the experimental data. The comparison shows generally good agreement between the measured and the calculated data. IntroductionIn a steelmaking process, molten steel carried by a ladle is first fed into a buffer vessel called tundish. From the tundish, it is then fed into a continuous casting mold. Molten steel solidifies gradually in the mold (the primary cooling zone) forming a solidified shell. As the solidified shell is just thick enough to support the molten steel at the mold exit, it is withdrawn through the mold by pinch rolls. It is progressively thicken as it is further cooled with water sprays in the secondary cooling zone. At the end of guide roll zone, completely solidified steel is cut into desirable lengths. Schematic view of a typical continuous casting is shown in Figure 1."

Jan 1, 1999

By L. Béjar-Gómez

The aim of this research work is to study and characterize precipitates in structural microalloyed steel by transmission electron microscopy and analysis by high resolution (HRTEM). Microalloyed steel with titanium was produced by casting in an electrical induction oven of 25 Kg. capacity. Carbon content in steel was less than 0.1 % and titanium content of 0.04%. Steel was processed thermomechanically; reheated to 1250ºC and hot rolled on a laboratory mill to a 13.0 mm thick plate with a finish rolling temperature of 900ºC and thickness reduction of 80%. Analysis by High Resolution Transmission Electron Microscopy (HRTEM) identified precipitates in the steel; type and morphology. Energy Dispersive Spectroscopy (EDS) analysis was applied to obtain the chemical composition of precipitates and the matrix. STEM-EDS analysis was also applied to obtain the element profile of precipitates. The results showed the presence of carbonitride precipitates of titanium, Ti (CN), with a circular morphology and size of 10 nm and less.

Jan 1, 2006

By Shaolong Chen, Carl-Gustav Berg, Hannu Mansikkaviita

Kumera Steam Dryer has been developed particularly for nonferrous metal concentrates with steam as heating source generated from waste heat boilers. Its unique structure enables the dryer to work at high capacity, up to 240 t/h, and high availability, over 95%. With half a century of engineering experience, and more than twenty industrial steam dryer installations worldwide during last 15 years, Kumera has demonstrated significant benefits of the steam drying technology in terms of energy efficiency and emission reduction to the end users. The dryer of this type can also be applied for other suitable mineral materials.

Jan 1, 2015

By Art Johnston

Gas handling at Magma Copper Company's, San Manuel smelter receives process gas from a flash smelting furnace and four copper converters. The major gas handling equipment consists of four electrostatic precipitators and a sulfuric acid plant. Process vessels in gas handling are typically confined spaces. Lethal gases., mechanical and chemical hazards, and the difficulty of rescue, should an accident occur, makes this area a must in the safety plan. The presence of hazardous chemicals and explosive gases in process vessels and piping are of major concern when repairs are required. Proper job procedures are critical to prevent injury during repairs. This includes plant employees and contractors who are likely to be unfamiliar with the hazards involved. The safe operation of a gas handling operation must include the functions of operations employees on a daily basis. This includes a safe working environment and involvement. of all employees in the safety program. If an injury does occur quick medical response is critical to prevent serious injury. Medical responders must be adeqliately trained and prepared to treat the injured person without becoming victims themselves.. The methods used at Magma copper Company to deal with these safety problems are the focus of this presentation.

Jan 1, 1992

By Moto Goto

Today, Pierce-Smith converters, coupled together with various types of smelting units, are used in most of the world's smelters. However, due to the "batch" processing nature, and problems associated with fugitive emissions during the transfer of melt and blowing stages, this arrangement will unlikely be adopted in future smelters. Modern day alternative processes include the Mitsubishi Process, Outokumpu Flash Smelting and Flash Converting Process, the Noranda Process, and the Ausmelt Process, but only the Mitsubishi Process is a "truly continuous" smelting and converting operation, producing a constant flow of blister without tapping, and is economically proven by long term commercial operations. This paper reviews recent advances in modern continuous converting technologies, with a special section devoted to operation of the "first standalone Mitsubishi C-furnace" coupled together with a Noranda Reactor, at Port Kembla Copper Pty. Ltd. in Australia.

Jan 1, 2003

By F. J. Tavera

The column flotation technology, at first developed for application in mineral dressing, has received special attention in processing of non-mineral dispersions as a result of its low cost, high efficiency and relatively simple operation. This paper presents the results from the operation of a laboratory flotation column for the separation of vegetable oil and soap from aqueous industrial effluents, The flotation system was operated under continuous countercurrent conditions without and with additions of a cationic collector. The experiments show that it is possible to separate about 80% of the organic phase in a rougher flotation stage. These results suggest that the recovery of the organic phase is highly dependant on the dispersion characteristics (i.e. bubble size, gas holdup and bubble surface area flux) and the existing an optimum bubble size from which either smaller or larger, the recovery of the organic decreases.

Jan 1, 2003

By Moto Goto

Today, Pierce-Smith converters, coupled together with various types of smelting units, are used in most of the world's smelters, However, due to the "batch" processing nature, and problems associated with fugitive emissions during the transfer of melt and blowing stages, this arrangement will unlikely be adopted in future smelters. Modern day alternative processes include the Mitsubishi Process, Outokumpu Flash Smelting and Flash Converting Process, the Noranda Process, and the Ausmelt Process, but only the Mitsubishi Process is a "truly continuous" smelting and converting operation, producing a constant flow of blister without tapping, and is economically proven by long term commercial operations. This paper reviews recent advances in modern continuous converting technologies, with a special section devoted to operation of the "first standalone Mitsubishi C-furnace" coupled together with a Noranda Reactor, at Port Kembla Copper Pty, Ltd. in Australia.

Jan 1, 2003

By Fumito Tanaka

The Mitsubishi process is the sole pyrometallurgical process for the continuous production of blister copper from copper concentrates and has been successfully operated around the world. The development of calcium ferrite slag (CaO-FeOx-Cu20), the so-called "C-slag", has enabled continuous converting from matte to blister copper in the commercial scale operations. Commercial interests in the slag led to many papers over the CaO-FeOx slag. However, CU2O- bearing slag has not been studied well due to experimental difficulties. The authors have quantified the thermodynamic properties ofthe CaO-FeOx-Cu2O system. The results have been utilized to analyze various issues related to the converting furnace, such as the magnetite precipitation from the slag or from blister copper and to develop better controlling criteria for the continuous converting operation.

Jan 1, 2003

By Keith M. Axler

This report addresses issues specific to the generation of hydrogen fluoride via reaction of calcium fluoride with sulfuric acid. This process has been established on a commercial scale and is under consideration for treatment of calcium fluoride residues from uranium processing. Magnesium fluoride slags are also available as a product of uranium processing. The technique of using sulfuric acid for the production of hydrogen fluoride from magnesium fluoride is also under consideration as a residue processing scheme. In the current study, thermodynamic modeling was used to investigate these chemical processing systems. The results presented herein reveal information relevant to the selection of processing temperatures and conditions. Details include predicted effects in system composition based on operating temperatures for both the calcium fluoride and the magnesium fluoride systems.

Jan 1, 1996

By Bogidar Mihaylov

A laboratory study was conducted on continuous precipitation of copper, cadmium, mercury and arsenic using thiourea, thioacetamide, sodium sulfide and ammonium sulfide as precipitating agents. Depending on the experimental conditions the metals precipitate with the sulfide donors at different orders and rates. These differences were employed as a basis of several techniques for continuous separation of copper and arsenic, cadmium and arsenic, mercury and copper, and copper, mercury and arsenic. The separation of the metals from industrial waste solutions was also studied. The precipitates obtained were inspected using x-ray diffraction, scanning electron microscope, atomic absorption spectrometer and plasma particle counter.

Jan 1, 1992

By S. Yin, A. Bogno, H. Henein, P. Natzke

Impulse Atomization (IA) (a single fluid atomization technique) was used to rapidly solidify Al- 4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc under argon atmosphere. In addition to the IA-generated droplets, the same technique was used to produce strips by Spray Deposition (SD) of the same alloys on a copper substrate with and without oil coating. The rapid solidification microstructures were analyzed using Scanning Electron Microscopy (SEM). From the SEM images, the amount of eutectic and the secondary dendrite arm spacing (SDAS) were measured. These SDAS results lead to the estimation of cooling rate. The eutectic fraction coupled with the metastable extension of the solidus and liquidus lines of Al-Cu (Sc) phase diagram lead to the estimation of primary and eutectic undercoolings. A comparison of the solidification path of the droplets and the strips was done as well as the analysis of the effects of scandium.

Jan 1, 2015

By Yongzhong Xiao, Tiejun Chun, Jian Pan, Deqing Zhu

"An innovative process of reverse floatation-direct reduction-low intensity magnetic separation was developed to effectively beneficiate the superfine run-of-mine (ROM) ore mined from Hunan Province, China. Mineralogy was measured that the ROM ore is of superfine low grade hematite ore type, assaying 27.2wt%Fetotal and with main valuable minerals of hematite occurring at size between 3 to 5µm. The upgrading results show that the final iron concentrate, assaying 88.3wt%Fe total and 94.5% metallization degree was obtained at an overall iron recovery of 69.9% under the following conditions: rough concentration by grinding of ROM up to 88.7% passing 0.074 mm and reverse flotation at pH=9.4, 100 g/t starch and 200 g/t dodecylamine (DDA), and coal reducing the rough concentrate pellets containing 12% calcium containing complex additive at 1200 oC for 120 min, and finally magnetic separation of the reduced pellets by grinding up to 89.2% passing 0.043 mm at 0.08 T field intensity.IntroductionWith the rapid development of iron and steel industry in China, there has been a soaring demand for iron ores in the past decade. The imports of iron ores have increased from 148 million ton in 2003 to 628 million ton in 2009 [1]. Iron making industries increasingly demand for high grade raw materials to improve product quality and reduce operation cost. However, availability of high grade natural ores is limited and enrichment of lower grade ores is necessary to meet the demand. Therefore, large quantities of superfine low grade iron resources are necessary to utilize in China at the moment."

Jan 1, 2011

By S. M. McDeavitt

Waste form alloys are being developed at Argonne National Laboratory for the disposal of remnant metallic wastes from an electrometallurgical process developed to treat spent nuclear fuel. This metal waste form consists of the fuel cladding (stainless steel or Zircaloy), noble metal fission products (e.g., Ru, Pd, Mo and Tc), and other metallic wastes. The main constituents of the metal waste stream are the cladding hulls (85 to 90 wt%); using the hulls as the dominant alloying component minimizes the overall waste volume as compared to vitrification or metal encapsulation. Two nominal compositions for the waste form are being developed: (1) stainless steel-IS wt% zirconium for stainless steel-clad fuels and (2) zirconium-8 wt% stainless steel for Zircaloy-clad fuels. The noble metal fission products are the primary source of radiation in the metal waste form. However, inclusion of actinides in the metal waste form is being investigated as an option for interim or ultimate storage. Simulated waste form alloys were prepared and analyzed to determine the baseline alloy microstructures and the microstructural distribution of noble metals and actinides. Corrosion tests of the metal waste form alloys indicate that they are highly resistant to corrosion.

Jan 1, 1996

By Jan Yaozhong

The composition and the possible utilization of Ti bearing blast furnace from a titanomagnetite blast furnace smelter were studied. The slag contained about 20% Ti02 and trace Sc. The mineralogical analysis indicated that Ti in the slag is mainly as perovskite. By means of magnetite separation, the Ti containing phase could not be enriched. An effective hydrometallurgical approach was proposed with sulphuric acid leaching. The method proposed for processing the studied slag renders product Ti02 and SC203. Besides the recovery ofTiO2 and SC2O3' the leaching process yields fine grained residues which can used as additives for making cement.

Jan 1, 1996

By G. Upadhya

Considerable success has been achieved recently in modeling microstructural evolution during solidification of castings bthrough the coupling of macroscopic heat transfer with microscopic solidification kinetics models. However, a complete model for simulation of solidification in complex shaped castings involves: (i) the description of fluid flow, during and after mold filling, coupled with (ii) heat transfer to the mold and surroundings by use of a macro model, followed by (iii) a description of subsequent solidification of liquid metal by use of a micro model for solidification of the alloy under consideration. This paper describes the coupling of solidification kinetics model to a 3D, transient, fully coupled fluid flow and heat transfer model. Coupling between the macremicro models is achieved by using the latent heat method. Micro models for the eutectics of gray, white and ductile iron are discussed. This coupled code has been used for predicting the thermal history and microstructural data for shaped castings. Various applications of the model, including prediction of shrinkage defects, grain density contours, and graylwhite transition region in the casting, are presented for a relatively complex casting geometry.

Jan 1, 1992

By Hui-Gai Li

The fine Ti oxide inclusions precipitated during solidification are favorable for intragranular ferrite nucleation. The oxygen content before solidification affects the composition and size of inclusions. The composition of precipitated inclusions in Mn-Ti alloyed steel was studied by means of thermodynamic calculation and experiment in this paper. The micro-segregation of Mn, Ti and O during solidification was considered in calculation and unidirectional solidification apparatus was employed in experiment to ensure that alloy elements diffused along solidification direction. The results showed that: inclusions are mainly Ti oxide when oxygen content is 10ppm; they are Ti oxide and Mn-Ti oxide when it is 20ppm; Mn-Ti oxide dominates when it is 30ppm. With the increase of oxygen content, the size of inclusions increases. The maximum oxides size is about 3µm from statistical results of experiment.

Jan 1, 2008

By Patricia Negrini Siqueira

Abstract. Polymers are susceptible to changes in their chemical structures that affect their mechanical properties under weather condition. Exposure of plastics to UV radiation causes a loss in their mechanical properties and/or change in appearance, including reduced ductility, color changes, yellowing and cracking. Today, there are several additive systems (light stabilizers) developed to work according to resin, final application, type of cultivation, and other characteristics. This study evaluates the different additive systems (Hindered Amine Light Stabilizer - HALS, nano calcium carbonate - NPCC, nZnO and nTiO2), applied 0.75% (in weight) in linear low density polyethylene (LLDPE). The samples were mixed by high rotation homogenizer and extrusion. Later, the samples were molded by injection and aged in QUV-B simulating 6 months of exposure to weather. Tests of FT-IR and tensile strength comparing to the non-aged samples were carried out in order to evaluate the performance of several additive systems.

Jan 1, 2015

By Zhiqian Zhang, Chao Wu, Chao Li, Hongxu Li, Chuanqi Jiao

"Many used electronic and optical products contain cerium of rare earth oxides, but it is difficult to recover such rare earth compounds by traditional metallurgy methods. The proposed supercritical water metallurgy is a novel way, perhaps it will be very helpful for rare element recycling, but the thermodynamic properties at such special systems is not clear. In the paper the H20-CeO-CeO2 and H2O-CeO2-Ce2O3 ternary system phase diagram were produced under the pressure of30MPa with different temperature of350°C, 375°C and 400°C. The stability existing area of possible cerium compounds and different ions like Ce2+,Ce3+,Ce4+,W,HO2-,0ff ,CeOH2+,CeO+ and CeO2· were determined.IntroductionCerium is an extensively used metal element playing an important role in the rare earth elements. CeO2 is an apparently simple binary oxide with cubic fluorite structure [l]. Ce0O gives rise to a range of important technological applications because of its oxygen storage capacity at moderate temperatures as below: CeO2=CeO2.x+ X/2O2 [2]. The oxygen storage phenomenon gives ceria important technological uses in different fields as automobile exhaust purification catalyst [3-4], fluorescent powder, ultraviolet absorption material [5], polishing powder, fuel cell materials [ 6], and gas sensors, etc. The excellent properties of CeO2 nano powder make its synthesis and preparation become one of the hot spots of world scientists study."

Jan 1, 2013

By Marcio Toshio Tanaka, Marcelo Breda Mourao, Cyro Takano, Cesar Yuji Narita

"The concerns in questions related to the environmental impact in the steelmaking industries caused mainly on the gas emissions such as the dioxide carbon are due to its raw material such as the coal, a fossil and non renewable resource. The purpose of this paper is to replace from 10% to 50% of the coal used in cokemaking by mixing it with a renewable source (wood charcoal). The powder (- 325 mesh) from both raw materials (coal and wood charcoal) were mixed in order to obtain a briquette that was then heat treated at 1100°C to obtain the biocoke. Results of usual analysis (coke reactivity index, coke strength after reaction and cold crushing strength test) were employed to compare to regular coke briquettes. It was found that biocoke with different amounts of wood charcoal present features enabling it to be used in some ore reductionprocesses.1. IntroductionThe iron and steelmaking industry is a heavy emitter of carbon dioxide; according to the World Steel Association, 6.5% of global emissions of this greenhouse gas is due to the production of ferrous materials [ 1]. This is due to the fact that the fuel and reductant employed in the blast furnace is metallurgical coke, obtained from fossil coal. There are some projects aiming to reduce or even eliminate the emission of fossil GHG in the iron and steelmaking process [2]. Most of them propose the capture and storage of the gas (CCS) [3], a technology not yet proven. Other studies point out that the coke consumption in the blast furnace could be reduced by using high reactivity coke; this could lead to lower temperatures in the thermal reserve zone of the blast furnace and consequently less fuel rate in the furnace.The use of biomass in the iron ore reduction process is known as an environmentally accepted solution, as biomass does not release already fossilized carbon."

Jan 1, 2013

By Yuzo Hiroshige, Masayuki Kyoi, Tomonori Saeki, Masahide Okamoto, Toru H. Okabe, Yu Miyamoto, Tomohiko Akahori, Takeshi Nemoto

We report Hitachi's approach to establish the recycling process for rare-earth metals in magnet. We have developed a process to disassemble the used electric products to collect the magnets, a process to remove the surface plating film of the magnet, and processes to separate rare-earth metals from the magnet. All processes are operated without chemical solutions in order to minimize the environmental impact due to the waste water emission. For the disassemble process, we have developed an equipment to generate continuous shock on the electric products to loosen screws. A sand blast technique is applied for the plating removal process. Rare earth metals in the magnets are extracted by immersion of the magnets in molten magnesium. The extracted rare-earth metals are separated from Mg by evaporation of Mg. The overall yield of recovery is 86.8 %. The purity of the final rare-earth metal is 98.8 %.

Jan 1, 2014