By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, ' AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.' The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By G. G. Hancock, H. H. Johnson

Hydrogen gas at atmospheric pressure is shown to cause substantial embrittlement in a martettsitic high-stretzgth steel. Subcritical crack growth is observed at very lom stresses and with high growth rates. It is suggested that an adsorbed layer of hydrogen atoms at the crack-tip surface provides the damaging hydrogen. Oxygen in small quantity, as little as O.7 pct by volume, is shown to eliminate subcritical crack growth in gas environments caused by hydrogen or water vapor. However, dissolved oxygen in water has little or no influence upon crack-growth rates. Oxygen-stopped cracks may be restarted by water, or by hydvogen or water vapor if oxygen is removed from the environment. These observations are interpreted in terms of preferential adsorption of oxygen at the crack tip and the formation of an oxide barrier. RECENT investigations1-3 have demonstrated that environmental factors are frequently responsible for delayed failure in martensitic high-strength steels. The environment causes crack initiation from preexisting cracklike flaws at unexpectedly low stresses, often far below the uniaxial yield strength. The crack then propagates at a rate controlled by the environment and the crack-tip stress-field intensity; during this period crack propagation will cease if either the stress or the aggressive environment is removed, and this may be considered a definition of subcritical crack growth. Fracture occurs when the crack has grown to a critical length, such that the fracture toughness of the steel is exceeded. Several liquids are known to cause delayed failure, but water and water vapor are the most severely damaging of the environments investigated to date.'-3 It has been suggested that hydrogen produced during corrosion reactions may be the actual embrittling agent2 The severe embrittlement caused by water vapor inevitably raises the question as to whether other gas environments are damaging. Previous work4'5 has demonstrated that high-pressure hydrogen (2250 psi or greater) is an effective embrittling medium, as measured by such criteria as reduction in area, notch tensile strength, and time to failure. Moreover, the embrittlement was eliminated by the addition of small quantities of air or oxygen to the high-pressure hydrogen, but it was not influenced by additions of nitrogen or argon.4 In the present study attention is focused upon gas environments at atmospheric pressure, in particular hydrogen and oxygen. The influence of these constituents upon the initiation and growth of a crack from a pre-existing cracklike flaw in a high-strength steel was determined directly by the electric-potential method of monitoring crack growth. MATERIALS AND PROCEDURE The H-11 steel was supplied by the U.S. Naval Research Laboratory as 3 by 12 by 0.065 in. sheet specimens with 1-in. transverse center slots. The slot tips were finished by Elox machining to a radius of 0.001 in. or less. The yield strength was 230,000 psi; chemical composition and heat-treatment schedule are given in Table I. The experimental apparatus, precracking procedure, and incremental loading sequence have been described previously.3 In the only significant change, precracking was sometimes carried out by a hydrogen embrittlement and baking technique. All experiments were conducted at room temperature; the hydrogen gas environment was purified by a commercial palladium purifier. Crack initiation and propagation were followed by the electric-potential method,'-3 using a calibration that has been recently dicussed. Stress-field intensities at the crack tip were computed by the conventional Irwin frmula; the plasticity correction was negligible and therefore not included. EXPERIMENTAL RESULTS A striking brittleness associated with molecular hydrogen at atmospheric pressure is demonstrated by the data in Table I1 and Fig. 1, which indicate that subcritical cracks in hydrogen initiate at lower stress-field intensities and propagate more rapidly than in fully humid argon. Ki and Kf are the crack-tip stress-field intensities at initiation and termination of subcritical crack growth, respectively. Termination, of course, corresponds to fracture. In both hydrogen and humid argon Ki is less than Kf

Jan 1, 1967

By A. V. Bradshaw, R. I. L. Guthrie

The behavior of large bubbles in the size range 4 to 25 cm3, rising through molten silver, has been studied. It was found that rising velocities were equivalent to those in aqueous systems of low viscosity. Mass transfer coefficients for oxygen bubbles dissolving in silver were found to be 0.036 ± 0.007 cm sec-1, being close to those predicted for transfer through the front surface of the spherical cap bubble only. It is suggested that the surface active nature of oxygen in silver could account for the relatively low coefficients obtained. MANY metallurgical processes involve interactions between gas bubbles and liquids. Examples include the removal of carbon monoxide in Open Hearth Steelmak-ing, the removal of sulfur by blowing air through copper matte during converting, and the removal of hydrogen from steel during vacuum degassing or inert gas flushing. The steps involved in such refining processes include; transport of the dissolved species to the bubble interface, adsorption and chemical reaction of the species at the interface, desorption of product molecules from the interface, and transport of product gas into the bulk gas phase of the bubble. It has been concluded1 that all the interfacial steps involved proceed so rapidly at steelmaking temperatures that transport of the solutes, present in the metal, become the important rate controlling factors provided nucleation phenomena are not restrictive. The O-Ag system was chosen for the investigation into gas bubble-molten metal interactions due to the relatively high solubility of oxygen that enables rates of oxygen transfer to be measured from changes in bubble volume. Other advantages of this system include the absence of a stable oxide phase at an oxygen pressure of 1 atm and the relatively low melting point of the metal which permits the use of a metallic container, providing that it is resistant to oxidation. In those metallurgical processes where bubbles have an important influence, bubble volumes are usually greater than 5 cm3. For this reason the present study relates specifically to single large bubbles of oxygen rising in silver. These bubbles adopt the characteristic spherical cap shape similar to that shown in Fig. 1 for a 30 cc bubble rising in water. After an initial investigation to determine the velocities of inert (nitrogen) bubbles rising in molten silver, experiments were carried out with oxygen and the rates of mass transfer between the oxygen bubbles and the silver were measured. EXPERIMENTAL Apparatus. The apparatus, Fig. 2, for containing molten silver, was constructed from "Nimonic 75" Alloy (75 pet Ni, 20 pet Cr, 5 pet Fe, Mn) and provided for the release of single bubbles from an hemispherical cup, situated at the bottom of the column. The cup was turned by translating the rotation of the drive shaft through 90 deg. This was accomplished by the use of a bevelled gear system, and a smooth drive was provided by the lubricating action of the silver on the gears. Since reliable high temperature seals at 1000°C were found to be impracticable, the filling and drive shaft tubes were extended outside the 3.5 kw resistance wire tube furnace, where connections were made using easily accessible O-ring seals. The apparatus remained gas tight to the atmosphere at pressure differentials far in excess of those used. The filling tube was connected via a small bore tube to the differential pressure transducer. Gas could be bubbled into the inverted cup from two i-in. tubes which passed down the inside of the column to preheat the gas. The temperature of the silver was maintained at 1020°C during all experiments. Measurement of Bubble Volume. In order to calculate mass transfer rates, it was necessary to obtain a continuous record of the bubble's volume during its passage through the column of molten silver. The method adopted for measuring the bubble volume involved closing off the top gas space to the atmosphere prior to each experiment, and recording the variation in gage pressure of this space during the formation and rise of the bubble. Since any change in bubble volume results in an equal change in top space volume, Boyles Gas Law may be applied (for isothermal con-

Jan 1, 1970

By L. D. Lash, J. R. Ross

Discovery of scandium in the Vitro solvent extraction plant for uranium led to commercial recovery of the byproduct. Micro amounts of scandium were extracted with uranium by dodecyl phosphoric acid, but failed to follow ura-niuminto the hydrochloric acid strip solution and were eventually concentrated in the organic extractant. A fluoride strip system was developed to recover scandium from the solvent in concentrated form. High purity scandium oxide was then prepared in multi-pound lots by chemical separation techniques. The plant recovery operation, final product purification, and analytical procedures are described. Scandium is a pseudo-rare earth which is truly rare and expensive. It has special properties which may make it desirable even at the present price of $2750 per lb. Recently the price was lowered from $5000 per Ib which had prevailed since 1952, and it is anticipated that usage will be stimulated because of the lowered price. This metallic element is distributed widely in trace amounts in the rocks of the earth's crust. In addition to micro-amounts found in most uranium ores, concentrations of 50 to 100 ppm have been found in Colorado ferberite ore, lateritic nickel ore, heavy sandstone from Utah, Wyoming, and New Mexico, and various zircon sands and monazites from the western part of the U. S. Scandium has been found as an essential constituent of very few minerals, the most important being thortveitite, a scandium silicate. At the present time, this mineral commands a price more than twice that of gold. Chemically, scandium is in group 3A of the periodic table. It is closely associated with yttrium and the rare earths which it strongly resembles in its reactions. It has a valence of three and will form an insoluble hydroxide, fluoride, or oxalate under proper conditions, similar to the rare earths. Eight years before its discovery, scandium was predicted by Mendeleef who ascribed his eka-boron with properties nearly identical to the actual properties of scandium. Its position as the element with Atomic No. 21 and Atomic Weight 44.96 places it between calcium and titanium in Period 4 of the chart. The successful commercial application of scandium must depend on unique properties to justify use of this high cost substance. Greater consumption would allow additional price reductions, but scan- dium will remain a relatively high-priced commodity because of its inherent scarcity. Research reportedly has been oriented toward use of scandium as an agent to achieve high-temperature, low-density alloys with magnesium and tantalum.' Also, the U.S. Air Force sponsored a project for production of research amounts of pure scandium metal.' The oxide has been used experimentally in electronics, ceramics, and metallurgy. The various aspects of scandium are well covered in recent publications.s-5 CONCENTRATE RECOVERY Small amounts of scandium exist in uranium ores and are dissolved during an acid leach yielding up to 0.001 gpl Sc2O9. When Vitro converted their uranium plant from phosphate precipitation to solvent extraction: scandium was found to follow the uranium into the dodecyl phosphoric acid solvent (DDPA). However, scandium did not strip with uranium from the DDPA in hydrochloric acid, but remained in the solvent. Therefore, a concentration of scandium built up in the organic phase. Residues from the solvent were spectrographed by the U.S. Bureau of Mines and found to contain scandium. As a result of this discovery, provisions were made in the plant for recovery of scandium-bearing concentrates. Solvent extraction of uranium was added to a conventional acid leach process in a typical installation? The ore was crushed and ground, and then leached with dilute sulfuric acid. Addition of an oxidant such as sodium chlorate insured conversion of uranium minerals to a soluble form. At this point, the slurry was chemically reduced by a sulfide, such as sodium hydrosulfide, to remove substances such as ferric iron and molybdenum which were partially extracted by the solvent. The solids-liquid separation was accomplished by a four-stage counter cur rent decantation (CCD) thickener circuit. The uranium was extracted from pregnant liquor with 0.1M DDPA in kerosene and stripped with ION

Jan 1, 1961

By I. B. Cadoff, J. C. Bilello, R. Rosenberg

Diffiusion of magnesium into the surface of LiF crystals to controlled depths and subsequent heat treatments provided a wide range of surface zone harahesses and structure, The bend strength of the LiF crystals was increased by as much as an or-dev of magnitude. Ductility was achieved when dislocation generation occurred in the diffusion zone or when dislocations penetrated to the surface from the intevior. A critical surface hardness of 130 to 140 kg per sq mm was found helozu which generation could take place in the diffusion zone and ahoue which the zone was impenetrable, This hardness was obtainable by several methods, among them the aging of quenched MgF2 -LiF solutions to produce MgF, precipitation. Maximum hardness was ohtained in quenched specimens with no visihle evidence of MgF,. Diffusion-zone formation followed a parabolic rate law and an activation energy of 20.9 kcal per mole was obtained for the process. RECENTLY, the properties of ionic crystals as related to surface condition have been receiving much attention, specifically the transitions between ductile and brittle behavior. Originally Joffe 1 showed that NaCl crystals could be made ductile by immersion in water and related this to the elimination of surface microcracks. Aerts and DeKeyser 2 and Gorur 3' have subsequently shown that ionic crystals are inherently ductile and are embrittled through contact with air. Machlin and Murray4 hypothesized that a layer of NaCIO3 produced by contact of ozone with NaCl induced embrittlement by acting as a barrier to outward dislocation flow. westwood,' Rosenberg and Cadoff,9 and Bilello and cadoff' have reported surface strengthening of LiF crystals by coating with a magnesium compound and then heat treating for adherence. The major effect of the coat was to inhibit dislocation-slip lines from reaching the specimen surface. westwoods showed microcrack formation and fracture to be caused by slip-band interactions at the surface. The material presented in this paper is an extension of the work reported earlier by Bilello, Rosenberg, and cadoff'6,7 and illustrates the wide range of surface properties and bulk behavior obtainable by use of heat-treated magnesium-diffused surface regions in LiF crystals. EXPERIMENTAL PROCEDURE The LiF single crystals were obtained from the Harshaw Chemical Co. Some batch to batch variation was observed; therefore all specimens for a given test series were cleaved from the same crystal. The typical dimension used was 1 by 0.1 by 0.40 in. Surface damage resulting from cleavage was removed by chemically polishing in a 2 pct NH4OH solution. Each group of specimens was given a vacuum anneal at 700°C for 4 hr to provide a base standard for measuring comparative effects of various surface treatments. To produce the reacted surface zone, the annealed specimens were immersed in a boiling suspension of MgF, in doubly distilled HzO, agitated slbwly for 30 sec, removed, and dried at room temperature. Uniform coatings of MgF, were deposited with a thickness of approximately 5 mils. It should be noted that this technique can be modified for use with crystals which are soluble in water by using boiling absolute alcohol as the dissolving medium. This was found effective for the coating of NaCl with MgF2. The diffused surface zone was obtained by annealing the coated samples at elevated temperatures in a vacuum of lob4 mm Hg. Penetration depth was controlled by varying the annealing time from 1/2 to 28 hr. After heat treatment, the samples were tested for bend strength and hardness. Load was applied by four-point bending in a hard-beam testing jig. Four-point rather than three-point bending was used to provide a wide area of constant stress and to minimize the effect of localized inhomogenities in the specimen. The deflection rate was 8 x min-' and the distance between knife edges was 1/4 in. Load-time curves were obtained from a chart recorder coupled to the machine and converted to resolved shear stress on the shear plane vs deflection, as plotted in the figures. The unstressed portions of the sample outside of the two outer knife edges were used for the microhardness studies. Microhardness measurements were made with a Bergsman tester attached to a Reichert metallograph. All hardness impres-

Jan 1, 1964

By M. M. Mebta, G. W. Dean, W. H. Somerton

With the advent of underground heating operations, interest has developed in the alteration of rock properties by high-temperature treatment. In the present work a number of sandstones were heated to temperatures in the range of 400°C to 800°C under both atmospheric and simulated reservoir pressures. Pertneabilities increased by at least 50 per cent and sonic velocities and breaking strerlgths decreased by an equivalent amount. Differential thermal expansion and other reactions of constituent min-era1 grains are the causes of these alterations. INTRODUCTION In the underground combustion of petroleum reservoirs, temperatures of the order of 600C are reported to have been reached in the combustion zone.' At this temperature rocks are subject to extensive thermal alteration. Temperatures of this magnitude and higher may also occur in subsurface formations when subjected to bottom-hole heating, thermal drilling operations, and underground nuclear explosions. Temperatures of this magnitude might also be generated by conventional rock drilling methods at points of bit-tooth contact. In earlier work, the permanent deformation of rocks resulting from heating was reported. Major structural damage of rocks occurs due to differential thermal expansion of mineral constituents. A number of mineral alterations including crystal inversions, loss of water of crystallization and dissociation, may also contribute to changes in physical structure and properties of rock. In the present work, samples of three typical sandstones were heated to several temperatures up to a maximum of 800C and then allowed to cool to room temperature. Heating was done under both atmospheric pressure and simulated reservoir pressure conditions. Physical properties of the samples were measured before and after heating and comparisons made. Measured properties included permeability, sonic velocity, breaking strength and fracture index. Changes in physical properties were compared to changes in mineralogical characteristics as determined by thin-section. X-ray diffraction and chemical tests. EQUIPMENT AND PROCEDURE Two outcrop sandstones (Bandera and Berea) and one sub-surface sandstone (St. Peter) were selected for the tests. These samples have a wide ranee in composition and physical properties as shown in Table 1. The first series of tests was made on 2-in. diameter by 5-in. long test specimens. Test specimens used in all later work were 3/4-in. diameter by 1 1/8-in. long, this being the specimen size required for heating at simulated reservoir pressures. After careful washing, the cores were oven dried at 100 ± 5C for a minimum of 24 hours before the tests were run. Test specimens were heated in an electric furnace at a constant rate of temperature increase of 3C per minute. When maximum temperature of the run was reached, the sample was allowed to soak for one hour. The furnace was then cooled to room temperature at the same rate of 3C per minute. The entire heating operation was designed for reproducibility without subjecting the test specimens to excessive thermal shock. For samples heated under simulated reservoir pressures, a pressure cell designed by Dean was used (Fig. 1).3 The core sample was inserted into a thin-walled (0.006 to 0.01-in.) copper cup which was then mounted in a high-pressure cell. Provisions were made for the application of internal pore pressure as well as confining pressure. Tests showed that the thin-walled copper cup closed tightly around the core and satisfactorily transmitted confining pressure to the core. The core was heated by placing the entire cell into the electric furnace. The heating program was the same as that used in the atmospheric pressure runs: tempera-ture rise of 3C per minute to maximum temperature of the test, soaking at maximum temperature for one hour, and cooling at a rate of approximately 3C per minute. The cell was designed to withstand 5,000 psi at 1,000C. However, since it was considered likely that repeated heating and cooling would in time weaken the steel, 2,000 psi at 850C was set as a working limit. In the present series of tests, the pore pressure was held constant at 750 psi and the confining pressure at 1.500 psi. The pressure source was a high-pressure nitrogen tank. The two pressures were controlled manually but are accurate well within ± 50 psi.

Jan 1, 1966

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

Solid-solubility limits at 1500°, l000q and 500°C for carbon, nitrogen, and oxygen in high-purity tantalum were determined by X-ray lattice-parameter methods. For carbon, the solubility was found to be 0.17 at. pct at 1500°C, and less than 0.07 at. pct at 1000°C. A nitrogen solubility of 3.70 at. pct at 1500° C decreases linearly with temperature to 2.75 at. pct at 1000°C, and 1.8 at. pct at 500°C. In the case of oxygen, the solubility was found to be 3.65 at. pct at 1500°C, 2.95 at. pct at 1000°C, and 2.5 at. pct at 500°C. The phases Ta2C, the low-temperature modification of Ta205, and Ta,N of unknown composition but which has a superlattice structure based upon the original bcc tantalum lattice have been identified as the initial precipitates in the respective systems. Metallographic methods were employed to verify the X-ray analyses. The etching behavior of Ta is discussed in terms of lattice i?rzperfections and precipitate phases. The excellent fabricability, high melting point, and nuclear properties of tantalum are responsible for interest in this refractory metal. Data on the solid solubility of the interstitial elements (oxygen, nitrogen, and carbon) in tantalum and on the precipitate phases are somewhat limited. The significant contributions are discussed below. Because the purity of electron-beam melted tantalum (only recently available) is considerably higher than that used in previous studies, the present investigation was initiated. Gebhardt et all-3 have investigated the tantalum-oxygen and tantalum-nitrogen systems with particular reference to the changes in physical properties and to the rates of reaction between these gases and the metal. The solubility of oxygen in tantalum was reported2 to be 3.7 at. pet at 1500°, 2.3 at. pet at 100O°C, and 1.4 at. pct at 750°C. Schonberg4 reported that several oxide phases (Ta40, Ta,O, TaO and Ta,05) exist while X-ray studies by Gebhardtl showed only two oxides, Ta,05 and an unidentified phase which was associated with a platelet-type precipitate. La-gergren and Magneli,' however, questioned the existence of compounds other than the two allotropic modifications of Ta,05 for the tantalum-oxygen system. In the case of nitrogen, the solubility was estab- lished by Gebhardt3 to be of the order of 7 at. pct at 1800°c. The solubility was reported to decrease rapidly with temperature, and, although no limits were established, a precipitate phase was observed by Gebhardt except when the high-nitrogen specimens were cooled very rapidly from the reaction temperature of 1800c. He reported the initial precipitate phase to be a tetragonal distortion of the bcc tantalum lattice while Schonberg6 reported the phase lowest in nitrogen Jo be a cubic super-lattice with a cell size of 10.11 A. Two other nitride phases, Ta,N and TaN, were reported; these appear to be isomor-phous with the carbides of tantalum. The tantalum-carbon system was investigated by Ellinger7 and by Lesser and Braurer. Two compounds, Ta,C and TaC, were reported to exist, each with a range of composition. The solubility of carbon in tantalum was found to be practically nil at all temperatures. Thus, of the interstitial elements which are present in small amounts in high-purity tantalum, carbon might be expected to form precipitates. The present investigation was initiated to obtain additional data on the solid-solubility limits of these interstitials at 1500°, 1000°, and 500' with particular emphasis on the distribution and the identification of the precipitate phases. EXPERIMENTAL WORK AND RESULTS In the present investigations of the solid solubility and of the precipitate phases in the systems tantalum-nitrogen, -oxygen, and -carbon, high-purity tantalum was reacted with high-purity gases, homogenized at 1800°c, and annealed at and quenched from 1500°, 1000,

Jan 1, 1962

By B. C. H. Steele, C. B. Alcock

In choosing solid oxide electrolytes for use in the measurement of thermodynamic quantities at high temperatures, the two most important criteria are the values of the partial ionic and electronic conduc tizities. Measurements of these conducticities have been made for some Group IVA oxides and solid solutions of these oxides with CaO, Y2O3, and La2O3. The total conductivities as a function of temperature. oxygen partial pressure, and composition were determined, as well as the electromotive forces of cells in which the oxygen partial Pressures of the electrodes were between 10-7 and 10-29 atm at 1000°C. Additional factors that influence the experimental arrangements, such as the operating temperature, the appropviate cell atmosphere, and electrode kinetics, are also discussed. IT has long been recognized that galvanic cells incorporating solid electrolytes can possess many advantages for the measurement of high-temperature thermodynamic data. Unfortunately, the electrical-transport properties have only been established for a few solid electrolytes, although attempts have been made, and are still being made, to use such materials as porcelain' and magnesia.' Kuikkola and Wagner have discussed3 and demonstrated4 various applications of solid electrolytes, and, in particular, their work stimulated the electrochemical measurement of oxygen activities using cells incorporating the solid oxide electrolyte, Zr0.85Ca0.15O1.85 The excellent characteristics of this oxide electrolyte have been confirmed by the investigations of Kingery et al.5 (oxygen ion diffusion), Carter and Rhodes6 (zirconium and calcium ion diffusion), and Weissbart and Ruka7 (electronic transference number). However the observations of Peters and Mobius,8 later confirmed by Schmalzried,9 indicated that the electronic component of zirconia-based electrolytes could become significant at low oxygen chemical potentials. Under these conditions, thoria-based electrolytes have obvious advantages arising from their superior thermodynamic stability. It was known that certain thoria solid solutions possessed defect fluorite structures containing anionic vacancies (cf. Zro.85Cao.l50O1. 85), although data on their electrical properties were conflicting. Kiukkola and wagner4 concluded that thoria-based electrolytes exhibited appreciable electronic conductivity, whereas Peters and Mobius8 mentioned that the electronic conductivity only became important at high oxygen partial pressures, but gave no further details. In addition, both Kiukkola and wagner4 and Peters and Mann'" had determined the oxygen chemical potentials associated with the Fe-FeO, Co-COO, Ni-NiO, and Cu-Cu2O equilibria, and it was not known whether discrepancies in their results could be attributed to the different cell design, or the thoria-based electrolyte used by Peters and Mann. These uncertainties have been resolved during the present investigation into the measurement of low oxygen chemical potentials, and transport properties of the relevant oxide electrolytes are presented and discussed. Other experimental difficulties associated with low oxygen chemical potential measurements are also described, with particular reference to the Nb-O system. 1. THEORETICAL CONSIDERATIONS Oxide systems of potential use as solid electrolytes possess a large energy gap between the valence and conduction bands. Little is known about the defects present in these wide-gap metal oxides as a function of impurity content and deviations from stoichiom-etry, or the mechanisms by which electronic charges move in these solids. For these materials it is convenient to represent the measured conductivity as the the sum of three terms: where a, is the conductivity due to positive hole conduction (p type), and oe is the electronic conductivity due to electron conduction (n type). U there is a large concentration of ionic vacancies fixed by composition then the ionic contribution will not be a function of oxygen pressure. Although the possibility of a pressure-independent electronic component also cannot be ignored, it is likely that such a term would only become significant at very high temperatures, and in general the positive hole conduction will increase with increasing oxygen pressure, and the electron conduction will increase with decreasing oxygen pressure. It follows that the total conductivity is related to oxygen partial pressure as follows:

Jan 1, 1965

By D. G. Oss, S. E. Erickson

An automatic control method for the ferrosilicon heavy media process maintains media density within 0.01 specific gravity points. Continued demands for higher grade, competitive products from the Mesabi Range have resulted in experimental work such as that detailed for one concentrator. Various methods, step by step procedures and instruments used at an iron ore beneficiation plant in the development of an automatic control system are described. Work continues and it is hoped that further applications of control instrumentation can be made in the next operating season. The need for instrumentation and automatic control of the various parameters in the heavy media process of iron ore beneficiation has been apparent for some time. Continued demands for higher grade, competitive products from the Mesabi Range have made it necessary to increase the efficiency of the process in every possible way. In a typical heavy media flow scheme for iron ore beneficiation (Fig. 1) a sized, prepared feed (generally about —1% in. to +% in.) is fed to a heavy media separatory vessel, along with a ferrosilicon slurry. A separation of the feed is made on the basis of specific gravity. Low density particles overflow a tailings discharge weir, while high density ore particles sink to the bottom of the high density pool and are moved away to the concentrate discharge chute. Both products are passed over drainage screens and then are cleaned thoroughly of attached ferrosilicon on wash screens. Float material is generally stockpiled, while the sink product is shipped as a final concentrate. Undersize from the drain screens is returned directly to the circulating media sump. Wash screen undersize is cleaned of contaminating ore particles and slimes by passing through magnetic separators. Provision is also made for splitting a portion of the tailings drain undersize into the cleaning circuit if necessary for control of depth of tailings overflow, or for additional cleaning as required. Cleaned ferrosilicon is stored in a densifier and returned to the Circulating media sump as make-up material. Dilution water is also added to this sump to maintain a desired specific gravity of the circulating media. As in any process, operational intelligence is secured only by keeping records of the process variables. Generally apeaking, plant operators have neither the inclination nor the time to keep complete and detailed records of these variables over the course of their shift. Before instrumentation was added to aid the operator, specific gravity was measured by weighing a given volume of pulp at intervals of from 30 to 60 min. Scale readings were made at the beginning and end of each shift. No records were kept of operating conditions, such as rpm of the separatory ves-sel, media level in the machine, tons per hour of the products, and so forth. These items were recorded only when spot checks were made by the metallurgical staff. CONTlNlJOUS DENSITY RECORDING The first process instrument used, other than the usual ammeter on the drive motor of the separatory vessel, was a nuclear density gauge and its associated circular chart recorder. These instruments were used to indicate and record specific gravity of the circulating media. This was a tremendous aid to the operator in that tie was able to observe and correct the specific gravity at any time. There was also added incentive to make frequent corrections because of the permanent record made by the recorder of the densities. The addition of the nuclear density gauge was influential in securing optimum quality and recovery of the heavy media product. Manual control was improved, and it became possible for a good operator to main control within f.05 specific gravity units. This compares with an unknown quantity, estimated at f0.15 gravity units, when manual measurement and control was used. An example of the improvement in manual control over the course of one season's operations is shown in Fig. 2. Chart A is typical of the records made shortly after the gauge was installed. Needless to say, it was difficult for operators and foremen alike

Jan 1, 1962

By D. C. Seidel, E. F. Fitzhugh

The cementation of nickel from acidic solutions by metallic iron is discussed. The cementation is carried out in pressure vessels at temperatures above 100°C. The results from bench scale studies on variables such as retention time, temperature, and solution pH are presented. A continuous processing flowsheet is proposed. Cementation is one of the oldest known hydrometal-lurgical reactions. The cementation of copper on iron was recorded by 'Paracelsus the Great' in about 1500,1 and by 1600 the technique was being used to recover copper at the Rio Tinto operations in Spain.2 At least one early author felt that cementation may have been one of the primary reasons for the alchemists' belief in the transmutation of metals.' The early writings state that when iron was placed in the clear waters from some mountain springs, the iron disappears and copper is found in its place. To the alchemists this may well have been one of the most convincing proofs that transmutation could and did occur. Since these early times the recovery of copper from acidic solutions by cementation has been practiced in plants throughout the world. Probably the cementation technique in some form has been common to more copper mining and milling operations than any other single recovery process. During current hydrometallurgical extraction studies, which were sponsored by the Republic Steel Corp. at the Colorado School of Mines Research Foundation, Inc., it was found that under the proper conditions, metallic nickel could be cemented from acidic solutions by powdered iron. The reactions are apparently similar to those that occur during the cementation of copper, but the nickel cementation had not been anticipated because iron and nickel are nearly adjacent in the electromotive series. The potential difference between iron and copper is approximately 0.78 v, while the potential difference between iron and nickel is less than 0.21 v. The cementation of nickel with iron at room temperature is almost negligible, but when the reaction is carried out in a closed vessel at temperatures in excess of 100°C, the nickel can be cemented almost quantitatively. The part played by this discovery in a practical method of nickel recovery is set forth in a separate paper.3 The following paragraphs are a discussion of experimental studies that were made to investigate this cementation reaction. The technique has been designated the HTC or High Temperature Cementation procedure. The cementation work was part of a study on hydrometallurgical techniques for the extraction of nickel from the garnierite or silicate type nickel ores. A hydrothermal extraction procedure had been developed, and this technique produced an acidic pulp or solution that contained both nickel and appreciable amounts of magnesium.3 Small quantities of ferric and ferrous iron were also present along with cobalt, manganese, and chromium. The potential for recovering the nickel from these acidic solutions by ion exchange or solvent extraction did not appear to be promising because of the relatively high magnesium content. The Ni ++ and Mg++ have nearly identical ionic dimensions and tend to be co-absorbed or extracted during ion exchange or solvent extraction treatments. Preliminary tests indicated that the nickel could be precipitated as a sulfide when using the high pressure H2S precipitation technique developed for the Moa Bay operations of the Freeport Nickel CO.4 This technique gave good recoveries, but the nickel sulfide product requires considerable additional processing before a marketable form of nickel is realized. The process also requires clarified feed solutions, and the solids-liquid separations on the garnierite residues are difficult. A program was initiated to investigate alternate procedures that might shorten the route to a marketable nickel product, and hopefully also permit bypassing the difficult solids-liquid separation steps required for the H2S precipitation technique. It was during these studies that the nickel cementation reaction with iron was encountered. EXPERIMENTAL EQUIPMENT AND PROCEDURES The bench scale precipitation tests which were conducted during this experimental program were made in 2-liter stirred autoclaves.* A photograph showing the form and arrangement of the autoclave

Jan 1, 1968

By W. A. Backofen, D. H. Avery, G. A. Miller

An evaluation has been made of the relative importance of yield strength (?) and stacking-fault energy (y) to the rate of fatigue-crack growth in materials of fcc structure. Pure copper and its solid-solution al-loys with aluminum and nickel were chosen for the study because they provided sufficient range in both quantities of interest that either could be varied independently of the other. Experiments involved alternating tension and compression of flat specimens which were prepared with sharpened internal notches so that most, if not all, of the crack-nucleation interval could be eliminated. Growth rate (dC/dN) was concluded to be proportional to the square of the plastic-strain amplitude (€,,) over a strain range of approximately 6x 10-4 to 6 x 10-3. The factor, k, linking dC/dN and ep in dC/dN = kEp2 increased and decreased with corresponding variations in y, but it did not respond syste?>/atically to change in ay, indicating that y is the significant variable in crack growth at constant plastic-strain amplitude. In polycrystalline material, k varied by a factor of 5 over the available range of y. In a few single-crystal experiments on Cu-A1 alloys the growth rate responded less strongly to change in y. It has been suggested that single crystals behave somewhat differently than poly crystalline material because there is more extetnsive substructure near the grain boundaries in the latter, and this facilitates crack advance by separation along subgrain boundaries. A point of some controversy in current work on fatigue relates to the effects of strength and stacking-fault energy on crack growth. In recent experiments a separation was made between the cycling intervals for crack nucleation and the subsequent growth that eventually ends a specimen's fatigue life.' The study was carried out on Cu-A1 alloys primarily, fatigued in alternating four-point bending to constant deflection. A nucleation interval of about 10' cycles (at a total strain amplitude = 0.2 pct) was found to be insensitive to aluminum content in the range 0 to 7.5 wt pct, while the growth period was increased approximately forty fold over the same compositional range. The increase was not in any sense linear, however. Rather, most of the change occurred below 4 pct A1 or a stacking-fault energy, ?, of about 15 ergs per sq cm. It was argued that the plastic-strain amplitude was approximately constant, and therefore the effect of composition must have grown out of the reduction in stacking-fault energy. Several studies have shown that, with high ?, cross slip is encouraged, subgrain structure is introduced during fatigue, and cracking is aided through propagation along subgrain boundaries.1-5 Therefore, lowering ? sufficiently to interfere with substructure formation would be expected to retard growth rate. On the other hand, it is a general rule that resistance to fatigue cracking increases as strength is raised. Accordingly, there might still have been some doubt that Y was the controlling variable, since strength would be increased as y was lowered by the aluminum additions. To help in dispelling that doubt, an experiment was made on a polycrystalline Cu-Ni alloy similar in strength to the Cu-A1 alloys but of higher ?; the crack-growth interval was found to be essentially that of pure copper.' Further support for this position on stacking-fault energy as it relates to crack growth is derived from work by Boettner and McEvily,6 in which the actual crack-growth rate was measured on samples previously notched so as to minimize the nucleation period. Unfortunately, it was necessary in isolating strength level to compare different alloy systems and grain sizes. Recognizing the complication, it was still concluded that growth may be retarded by a reduction in y, per se. A related study has also been made by Roberson and Grosskreutz.7 The zinc content of a brass was systematically changed to alter strength and stack-ing-fault energy, although not below the 15 ergs per sq cm at which pronounced change in growth interval was found in the earlier work. The results were limited to more or less conventional S-N diagrams so that nucleation and growth events could not be separated. No definite conclusions were drawn, but

Jan 1, 1967

By L. E. Tanner

A study was made of the transformation kinetics of the commercial titanium-base alloys, Ti-2.5Al-16V and Ti-4A1-3Mo-1V, using two different heat treatment cycles: 1) step-quenching to aging temperatures from a ß solution anneal and 2) water-quenching from an a+ß solution anneal followed by reheating to aging temperatures. Metallographic examination and hardness testing provided the major portion of the data, while electrical resistivity, dynamic elastic modulus, and X-ray diffraction techniques were also used to obtain critical or confirnzatory data. TTT diagrams were constructed from these results. The sheet alloys, Ti-2.5Al-16V and Ti-4Al-3Mo-lV, are of current interest to the Department of Defense. As an aid to the planning of their respective heat treatments, a program was carried out to determine the transformation kinetics of these alloys using ß and a + ß reference states. This paper presents the TTT diagrams constructed from data obtained by metallographic examination and hardness testing, as well as by X-ray diffraction, electrical resistivity, and dynamic elastic modulus determinations. EXPERIMENTAL PROCEDURE Materials—Sheets of the alloys were obtained from the producers in the "mill anneal'' condition and were tested prior to shipment to assure their meeting mill specifications. Chemical analyses were also supplied and are presented in Table I. Heat Treatment—The majority of the data presented in this study were obtained from hardness testing and metallographic examination. Sample coupons were cut from the alloy sheets and heat treated on a mass scale. The annealing cycles were operated in the following manner: 1) The ß solution anneals were carried out in a horizontal tube furnace with the bare samples protected by a dynamic helium atmosphere. Following this treatment, the samples were quickly transferred to lead, solder, or oil-bath furnaces for aging. After prescribed times at the various reaction temperatures they were water-quenched. 2) The second cycle simulated commercial practice, which requires the alloys be quenched to room temperature following the a + ß sotution anneal. This anneal was carried out in a muffle furnace with a dynamic helium atmosphere. The specimens were then reheated from room temperature to the reaction temperatures in lead, solder, or oil-bath furnaces, followed by water-quenching after prescribed times at these temperatures. Information concerning the critical temperatures of the alloys was obtained from the literature and solution treatments were based on these values. A summary of the solution annealing treatments is found in Tables II and 111. The aging temperatures for the (a - ß alloys ranged in 50°C intervals from 200°C (392oF) to approximately 50°C below the ß/a + ß transus in the first cycle and approximately 50°C below the a + ß solution temperature in the second. The transformations in these alloys were known to be rather rapid, and thus aging times started at 0.5 min and went to a maximum of 7000 min. Hardness Testing and Metallographic Preparation— Heat-treated samples were sheared and mounted in Bakelite with their cut edges exposed. After a flat surface was ground, the hardness was determined in Vpn on an Armstrong-Vickers machine utilizing a 20-kg load. Three to four impressions were made on each specimen. After this procedure, the hardness impressions were removed and the edge surfaces of the specimens were prepared for metallographic examination in the usual manner. The etchant was 20 pct HF and 20 pct HNO3 in glycerine. Electrical Resistivity—It has been shown that the isothermal reactions in titanium-base alloys can be followed by measuring the changes in e1etrical resistivity attending these transformations. As mentioned earlier, the reaction kinetics of a-ß alloys are rather rapid; thus, it would be expected that resistivity data obtained from these alloys would be more significant if measurements were made continuously at the respective aging temperatures. To accomplish this end a special apparatus, based on the current-potential principle, was assembled. Its design was derived from earlier devices constructed by Colner and zmeska1 4 and Levinson.5 The set-up provided for the heat treatment zof machined specimens (approximately 2 x l0-4in. in cross section by 3 in. in length) and the determination of their relative

Jan 1, 1962

By J. W. Sandelin, L. S. Birks

The group five metals, vanadium, niobium, and tantalum all show cold-rolled textures of {100)(011) and {112)(0ll) with a preference for the (100) in vanadium and niobium and for the {112) in tantalum. Recrys-tallization texture of (100) and (111) was reported1 for vanadium after annealing (no temperature stated). For tantal~m ,~ annealing below 1200°C strengthened the (112) texture but the (111) texture increased and was predominant as the annealing temperature was raised to 2500°C. Annealing niobium up to 1100°C strengthened the ( 100) texture and developed a weak (111) texture.' In the present work niobium has been annealed up to 2000°C. Nearly 70 pct of the grains showed {111) texture with only a weak (112) component and an insignificant (100) component remaining. In addition, double-crystal rocking curves were used to follow the increase in crystal perfection of the grains with increased annealing time. Material and Treatment. Samples i by 4 in. were sawed from & -in.-thick cold-rolled niobium sheet obtained from Wah Chang. Chemical analysis of the material showed it to be 99.4 pct pure with tantalum as the major impurity. Individual pieces were annealed for 2, 15, 30, and 60 rnin in a vacuum of 10'* Torr using an rf generator. They were etched until the grain boundaries were well-defined, Fig. 1. Average grain size varied from 1 mm for 2 min annealing to 2 mm for 60 rnin annealing. Experimental Results. Preferred Orientation. The orientations of 97 of the 117 grains in the specimens of Fig. 1 were determined by back-reflect ion Laue patterns. A General Electric 10-cm-diam cylindrical camera was used rather than the conventional flat camera in order to record more of the low-index spots. The method proposed by Forest, Barton, and schieltz4 was used to transform the cylindrical film patterns to standard stereographic projections. Table I gives the compilation of data. Even 2 rnin anneal at 2000°C is sufficient to yield a strong (111) preferred orientation, and the percentage of grains with this orientation increases steadily with annealing time at the expense of all other orientations. Crystal Perfection. X-ray topographs were taken of each specimen in both the (111) and (112) orientation using the method described by Birks and Grant.' As the anneal time increases, the grains become larger and the individual reflections become slightly more uniform in intensity, indicating an increase in crystal perfection. For a more quantitative measure of crystal perfection, it was necessary to measure the double-crystal rocking curve. The spectrometer employed was a Gaertner instrument of Compton design. LiF was chosen for the first crystal because the (400) reflection with d spacing of 1.05 AU is a good match to the (222) niobium reflection with d spacing of 0.95 AU. CuKp radiation was used in order to further reduce the d spacing mixmatch correction.' A variable aperture was placed between the LiF and the niobium specimen so that a single grain or even a small portion of a grain could be examined. Fig. 2 shows typical rocking curves for the four annealing times. For the 2-min specimen, a single peak is observed with 10' of arc full-breadth at half maximum. As the annealing time is increased to 15 or 30 min, several sharper peaks of 40 to 80" breadth can be seen within a single grain. After 60 rnin anneal only a single peak of about 30" is observed. Table I1 shows the corrected rocking curve breadths and the dislocation densities, ND. The latter were calculated from the equation7 where W is the corrected rocking curve breadth at half maximum in radians and b is the effective Burger's vector. For (110)(111) slip in niobium, b is 2.86 AU. Discussion. The annealing of cold-rolled niobium at 2000°C causes rapid preferential growth of grains with {ill} orientation. After only 2 rnin annealing time, 35 pct of the grains have the (111) orientation, and after

Jan 1, 1968

By W. A. Nagel, R. P. Alger, H. Sherman, J. Tittmann

A sidewall epithermal neutron tool has been developed to substantially reduce environmental effects that have previously complicated neutron log interpretation. Designed for operation in uncased wells, the device provides increased accuracy in both liquid-filled and empty holes. A brief discussion of neutron moderation, diffusion and capture shows that logs using epithermal neutron detection depend on a smaller number of formation-characterizing parameters than those using thermal neutron or capture gamma ray detection. Thus, they come closer to providing an unambiguorls determination of hydrogen content. In this new device a directionally sensitive epithertnal neutron detection system has been incorporated in a side-wall source-detector skid to minimize borehole effects. The effects of variations in borehole size and shape, mud type, temperature and salinity are greatly reduced. Small residual borehole effects are then computationally accounted for in the surface control panel to provide a borehole-corrected neutron log. The log presents a direct recording of neutron-derived porosity on a linear scale. With corrections for borehole effects already applied, this direct recording of porosity simplifies log interpretation. Furthermore, comparison with a linear porosity presentation of a formation density log permits sandstones, limestones and dolomites to be readily identified. Thus, in complex or variable lithology, porosity is determined with greater accuracy and reliability than heretofore. Laboratory data and field results demonstrate the improvements in neutron logging afforded by this new side-wall epithermal neutron logging device. INTRODUCTION The new Sidewall Neutron Porosity (SNP) logging system, designed for use in uncased wells, provides reliability and accuracy never before achieved with neutron logs. The effects of variations in borehole diameter and shape, fluid salinity, mud weight and temperature—parameters that have long complicated neutron log interpretation— are suppressed or corrected for by this sidewall epithermal neutron detection system. Furthermore, to simplify interpretation the SNP log presents a direct recording of computed porosity on a linear scale. The performance improvements achieved by this new system arise primarily from the combination of two im- portant design features. First. though not unique to this new tool, an epithermal neutron detection system is used,',' Epithermal neutron detection substantially reduces the perturbing influences of the thermal neutron absorption properties of rock matrices and water salinity. Second, the neutron detection system is mounted in a directionally sensitive sidewall skid to greatly minimize borehole effects. The purpose of this paper is to explain briefy the advantages offered by the detection of epithermal neutrons, to describe the SNP equipment and the log, to present calibration and correction data and to give examples of interpretation methods made especially convenient by this new system. ADVANTAGES OF EPITHERMAL NEUTRON DETECTION Epithermal neutron detection, of all the neutron methods in current commercial use, provides the simplest determination of formation hydrogen content. Advantages of epithermal neutron detectors, as compared with thermal neutron and gamma ray detectors, are probably best explained by a brief review of the life of a source-emitted neutron. A fast neutron from the source will eventually be cap-tured by the nucleus of an atom. However. before capture is likely to occur, the fast neutron (energy of 100,000 electron volts (ev) or more) will be slowed down until it is in thermal equilibrium with its surroundings. The neutron is then considered to be a "thermal" neutron (average energy of 0.025 ev at 25C). The overwhelming majority of the slowing down thus occurs in reaching epithermal energies (energies just above thermal—0.5 to several ev). After reaching thermal energy. the neutron will "diffuse" through the formation with, on the average, no further energy change until capture. Upon the capture of the thermal neutron, relatively high energy gamma rays arc usually emitted. Hydrogen plays a very important role in the process of slowing down fast neutrons. On the other hand, the absorption effects of water salinity and low concentrations of other strong thermal neutron absorbers—relatively unimportant in the moderation process-—are very important in thermal diffusion, capture and the production of gamma rays. Thus, by detecting only epithermal neutrons with the SNP, spurious effects due to these thermal neutron absorbers are greatly minimized as compared to the effects on tools using thermal neutron or gamma ray detectors. The epithermal neutron detection system affords another important advantage. Log response in various litho-

Jan 1, 1967

By J. E. Burke, A. M. Turkalo

IN 1923 Desch¹ pointed out that the grains in a metal which is anisotropic with respect to its thermal coefficient of expansion would contract differently upon cooling, and that the stresses developed might approximate the plastic strength of the metal. More recently Boas and Honeycombe2-5 studied the behavior of several metals upon thermal cycling and observed that the stresses developed in arlisotropic metals are great enough to produce slip lines in individual grains and a roughening of the specimen surface. This phenomenon they have named "thermal fatigue." The mechanism they propose involves essentially a kneading of the grains, the deformation being alternately in compression and tension in a given grain as the temperature is changed in one direction and then the other. The present work was undertaken to investigate the possibility that an additional mechanism might operate to produce plastic deformation during thermal cycling—a "thermal ratchet" that depends upon a combination of grain boundary flow to relax the stress that develops between differently oriented grains upon raising the temperature and transcrys-talline slip to relax the oppositely directed stress which develops on lowering the temperature. Thus, thermal cycling should produce a nonreversible distortion such that certain grains will change shape differently from their neighbors with a simultaneous displacement being produced at the grain boundary. Temperature Dependence of Grain Boundary and Grain Strength The critical resolved stress for the initiation of slip in metal grains is only mildly affected by temperature." For example, in cadmium it decreases from 0.15 to about 0.05 kg per sq mm when the temperature is increased from 20° to 458°K and further temperature increase causes little further decrease. On the other hand, the work of KG1 indicates that the grain boundaries behave in a viscous fashion that can be described8 by the expression: t = BVexp(Q/RT) [1] t is the shearing stress on the boundary; B, a constant; V, the flow rate at the boundary; Q, the activation energy for grain boundary flow; R, the gas law's constant; and T, the absolute temperature. Eq 1 indicates that the stress necessary to cause a given grain boundary flow rate, V, decreases rapidly with increasing temperature. The value of the constant B is such that at sufficiently low temperature and ordinary strain rates deformation will occur preferentially by slip rather than by grain boundary flow. There is considerable evidence to indicate Consider the bicrystal shown in Fig. 1. In grain 1 the slip plane lies 45 " to the boundary while in grain 2 the slip plane is 90" to the boundary. The coefficients of expansion of the grains in a direction parallel to the length of the crystal are a1 and a, with a, > a2 for the orientations shown. The sequence of events that can occur upon heating and cooling this specimen is illustrated schematically in Fig. 2. Initially there is assumed to be no stress in the specimen (A). Upon heating, grain 1 attempts to become longer than grain 2, but is constrained by grain 2. Thus grain 1 is loaded in compression and grain 2 is loaded in tension, and a shearing stress is present across the boundary (B). As the temperature is increased, the stress will build up, and finally grain 1 will be plastically deformed by slip, since the greater stress is resolved on its slip planes. Any further heating will result in more slip and the stress will remain constant until some temperature T* is reached where the stress can be relaxed by grain boundary flow.† At this relaxation temperature (C) a step will appear between grain 1 and grain 2. Further heating above T* will cause grain 1 to become relatively longer, but no stress will appear because the grain boundary is too weak to support the stress (D). Upon cooling again, at T* (E), the grain boundary will again be able to support a shearing stress, and upon cooling further, grain 1 will be loaded in tension and grain 2 in compression (F). When the decrease in temperature below T* is sufficient to impose the critical shear stress upon the slip plane of grain 1, it will be stretched by slip.

Jan 1, 1953

By R. T. DeHoff, F. N. Rhines

The problem of determining the number of particles of a phase distributed randomly in unit volume c an opaque matrix from measurements made on random plane sections is closely investigated. A formalized derivation for the general case is presented. Applications of this formal result are made to specific types of aggregates dispersed in a matrix; circles, particles with flat circular ends, cylinders, and constant shape aggregates of ellipsoids of revolution. Quantitative measurements of the average geometric properties of these aggregates are developed. In 1953 R L. ullman' developed a technique for determining, from measurements made on random plane sections, the number per unit volume, Nv, of particles imbedded in an opaque matrix. Using meas urements previously developed for volume fraction, vV,' and surface area per unit volume, .SV,= he was able to determine average volume, average surface area, and average dimensions of particles, independent of size distribution, for spheres and circular disks,' as well as for uniformly sized cylinders of any axial ratio.4 The technique is mathematically rigorous for the cases studied. Recent studies of this problem have yielded rigorous solutions for the general case of cylinders, permitting evaluation of NV independent of size distribution and with all axial ratios intermixed. Generalization to shapes having flat, circular ends has been deduced. A solution has also been obtained for the ellipsoid of revolution, independent of size distribution, but requiring a constant axial ratio in the generating ellipses. In the following derivations, as in Fullman's work, it is assumed that the problem is purely a combination of geometry and probability theory,that is,eithe the particles to be measured are imbedded randomly in the matrix, or a sufficient number of random plane sections are taken to make the sample representative. A relationship exists between the number of par- ticles of a given size and shape that may be situated in unit volume (Ny) and the number of intersections a random plane can be expected to make with these particles (Na). It is the purpose of the following section to derive this relationship. The probability of Intersecting Convex Bodies. Consider a convex, closed surface, that is, one for which no two surface normals point in the same direction, situated at some arbitrary position and orientation in a cube of material that is one unit long at each edge. It is not necessary to assume that this surface is symmetrical. Let planes be constructed in the cube parallel to the top face and at random distances from it. Those planes which lie between the two planes which are just tangent to the top and bottom of the surface will intersect it. The probability that a plane will intersect the body may be defined as the limit of the fraction of planes that lie between the two tangent planes as the total number of planes constructed becomes infinite. This fraction, in the limit, is equal to the distance between the two tangent planes, DV, divided by the total length over which planes are constructed, which has been taken as unity. If the body is now rotated to a new orientation, applying the same argument, the probability of intersection is again numerically equal to the distance between tangent planes. Let DV ($, 0) be defined as the distance between tangent planes of a convex body as a function of orientation, Fig. 1. The probability, Pr, of intersecting the body with a randomly oriented and randomly positioned plane, is then equal to the average value of DV (0, $) over all possible orientations. It may be easily shown that for a system of spherical coordinates the probability of finding an orientation between Q and Q + de, $ and $ + d$ is (1/4n) sin $ dB d$, so that This relationship may be applied to each body in an aggregate of convex bodies. In particular, if the bodies in an aggregate are classified according to size and shape, and the ithsuch class is considered, Eq. 111 may be applied to this entire class, the probability of intersecting any body in this class being

Jan 1, 1962

By B. L. Averbach

Recovery and primary recrystalliza-tion in cold worked metals are usually considered as two competing processes. Some of the effects which usually accompany recovery are: alleviation of stress corrosion tendencies, changes in thermal emf,1 damping capacity,2 electrical resistivity,2 and magnetic properties,3 and only minor changes in hardness or the related strength properties. During primary recrystalliza-tion new unstrained grains are formed at the expense of the strained matrix. These new grains eventually become visible metallographically, and nucle-ation and growth kinetics have been indicated for this process.4,5 Frequent attempts have been made to study the cold-working phenomenon by observations on the line broadening by X ray diffraction patterns. Relatively few measurements of line intensities have been made, although Brind-ley and his collaborators, 6,7,8 by means of film techniques, compared the intensities of cold worked Cu, Ni, and Rh patterns with those from chemically precipitated powders. These precipitated powders were presumed to be strain free, and it was found that the intensities for the cold-worked materials progressively decreased as the Bragg angle increased except for the first line, where there was an increase due to reduction in extinction. This was interpreted as a randomness in atomic position induced by cold work. Such randomness is similar to that caused by thermal agitation and has been described as "frozen heat" displacement of 0.08-0.10 A from the mean atomic position. In a recent study9 on the effect of cold work in metals on their powder pattern intensities, the changes in integrated intensity for heavily cold worked alpha brass were observed as a function of the annealing temperature. These measurements were made with a manually operated Geiger-counter spectrometer using CuKa radiation monochromated with a rock salt crystal. Intensity measurements were made with a scaling meter over small intervals of angle, and the equipment was so arranged that the diffracted and incident beams made equal angles with the specimen. Intensities could be compared directly by simply interchanging specimens, and comparisons from day to day were made with a standard whose line intensities did not change on aging. It was shown that a cold worked alpha brass standard was stable for at least a year. Table 1 indicates the results of the integrated intensity measurements on a 70 Cu-30 Zn brass. In the sample preparation, a brass plate was first cold rolled 50 pct and then filed, screened to —325 mesh, compacted into briquettes at a pressure of 60,000 psi and finally annealed for one hour at various temperatures up to 400°C. The briquetting pressure did not seem to influence the integrated intensities, and most of the cold work was introduced by the filing. Although this method of cold work is not quantitative, it was used to obtain random orientation (and thus uniform diffraction lines) in order to make accurate measurements of integrated intensity. Back reflection patterns were taken in each case to check the uniformity of the lines, and from the observed line broadening it was apparent that this type of plastic deformation was quite severe. Care was taken to traverse the entire background of the pattern and to assign to each peak the total intensity above this background. The bases of the diffraction lines were quite broad and spread out over several degrees, even for the narrow peaks. The theoretical intensities were calculated to include a temperature correction, a dispersion correction, and a Lorenz- polarization factor corrected for the crystal monochromated beam. In Table 1 it was necessary to match the calculated and observed values at only one point, and the rest of the experimental values were converted directly to this arbitrary scale. The integrated intensities in Table 1 are listed in arbitrary units, and the accuracy was sufficient to reproduce any of the measured line intensities to within + 1.5 units. It is evident that the percentage error on the strongest line (111) was quite low. The calculated values and the observed intensities for the cold worked material matched reasonably well. As the annealing temperature was raised, however, the intensity of the strongest reflections, particularly the (lll), decreased measurably. Since the background intensities of all of these patterns were identical, such behavior could be interpreted as a primary

Jan 1, 1950

By Jean-Jacques Prompsy, J. S. Rinehart

Some time ago a study was initiated at the Colorado School of Mines in an effort to arrive at a better understanding of the stress fields developed within drill bits under dynamic loading and the influence that these stress fields could have on the failure of the bits. Particular emphasis has been given to the influence that bit shape has on the establishment of highly localized, potentially destructive stress inhomogeneities within the bit. The study has been divided into three phases involving three velocity regimes: impacts at very low velocities, 0 to 20 ft/sec, a velocity range in which dynamic effects are just beginning to be found; impacts at velocities ranging from 20 to several hundred ft/sec, a range commonly encountered in practical drilling operations; and impulsive loading through the detonation of explosives, a region in which the dynamic effects are greatly exaggerated and made more identifiable. The ultimate objective is to provide basic data which will enable the mitigation through judicious design of the frequency and severity of these transient concentrations of intense stress, thereby prolonging and increasing drill efficiency. This paper presents results of the third phase of this study — the development of a better understanding of the dynamics and mechanics of failures caused by transient stress-wave interactions. The impulsive loading or transient waves in these experiments were generated by detonating small explosive charges placed on the ends of Plexiglas cylindrical rods terminating in truncated cones. Under such intense loading, dynamic effects are greatly exaggerated and, hence, made more identifiable. The explosion generates a high-intensity transient stress disturbance which moves through the rod, reflects from surfaces which lie in its path, and establishes momentarily narrow regions of high concentrations of stress where failure of fracture may occur. The peregrinations of these waves, their interactions and their effects have already been described in the literature (see, for example, Refs. 1 and 2). The locations and extent of the regions quite apparently are strongly dependent on specimen shape, making it possible through judicious shaping of specimens to relocate the highly stressed regions, minimize their extent, or eliminate them entirely. These experiments were designed, first, to identify more clearly the vulnerable regions in geometries relevant to drill-bit design and, then, to modify these regions in a predictable way by changing specimen shape. Through this latter process, it is anticipated that better bit design might evolve. The specimens used in the experiments were cylindrical rods, 1 1/2 and 1 1/8 in. in diameter, ended by a truncated cone, with the cone angles ranging from 45° to 130°. Upper cone face diameters were 1/2, 3/4, or 1 in. A small plastic-covered electric blasting cap detonated on the axis of the specimen produced the spherical shock wave. The detonators used were Olin Mathieson No. 6, which induced into the rod a transient saw-toothed stress disturbance of about 3-microseconds duration, corresponding to a wave length of 0.3 in. in the Plexiglas. Five distinct systems of fracture were observed: (1) along the axis of the rod, a lower system of fractures, the cracks focusing around one point for specimens having cone angles of 80° and 90° and, as the cone angle was increased, spreading downward; (2) just above these fractures, an upper system of fractures composed of horizontal cracks observable in some specimens but not of any appreciable extent; (3) a third system of axial cracks still above the latter, observable in the small cone-angle specimens; (4) in the upper part of the specimen, a system of radial fractures extending from the blasting point; and (5) circular spalling due to reflection of the wave on the boundary of the cylinder. Only the first three systems, the axial fractures, are examined here. LOWER TENSILE FRACTURE SYSTEM The first, lower system of tensile fractures, shown in the photograph of Fig. 1, was observed in almost all of the specimens. It was due to the reflected tensile wave coming in from the boundary of the cylinder as shown in Fig. 2. The reflected wave was cylindrically convergent and focused

By R. F. Stewart, A. W. Hall

A method has been developed for continuously measuring the moisture content of coal. The method is based on the thermalization of fast neutrons by hydrogen in the coal. Neutrons from a small radio-isotope source penetrate the coal, are scattered by hydrogen, and measured by a thermal neutron detector. The number of thermal neutrons counted can be directly correlated with the moisture content of coal. In a pilot-scale system, moisture was measured continuously within 0.2% in coal moving at rates up to 20 tph. The method is adaptable in industry for continuously measuring the moisture content of coal at high tonnage flow rates. Such an application would permit continuous recording of moisture in coal without sampling and facilitate quality control. An automatic and continuous method of measuring the moisture content of coal is needed by the coal industry. Automatic control of the coal quality would reduce the cost of coal preparation, improve the product, and thus indirectly increase the use of coal. Moisture in coal can be determined by several methods, but the time required to obtain samples and analyze them by existing methods makes it difficult, if not impossible, to control the quality of the product. Both producers and consumers need a method for continuous and instantaneous measurement of moisture content without sampling in order to regulate process equipment and keep the moisture content of coal within specifications. At the Morgantown, W. Va., Coal Research Center we are developing a nuclear method for continuous measurement of moisture in coal. This method is based on the thermalization of fast neutrons by hydrogen in the water and organic matter of coal. Neutrons from a small radioisotope source penetrate the coal, are scattered by hydrogen, and are measured by a thermal neutron detector. The number of thermal neutrons counted can be directly correlated with the moisture content of coal. Design of a moisture meter based on neutron thermalization depends on many variables, any or all of which can affect the sensitivity of the meter. These factors include those related to the nuclear aspect; type and size of neutron flux and source, type of detecting device, and background count; and those related to the coal being tested: rank, particle size, and ash content. A survey was initiated to eliminate the relatively insignificant factors and to ascertain the magnitude of the major effects. Such information was necessary to fully evaluate the technique and to establish design criteria. Coal contains a relatively large amount of hydrogen in the organic coal substance and the water of hy-dration of the shaly material as well as in the moisture. To apply this concept of moisture measurement to coal requires that the organic substance in coal from any one seam of a particular mine be uniform in hydrogen content. The difference in total hydrogen content of wet and dry coal is relatively small, so that a moisture measurement based on this concept requires a measurement between two large numbers to a high degree of precision. Thus, it was necessary to develop a highly precise instrumentation system for continuous measurement and to obtain a physical arrangement permitting measurement of moving coal with a minimum effect from density variation. EXPERIMENT WITH TRAYS OF COAL Tests were conducted with metal trays containing SO to 100 lbs of coal to develop an instrument system of high precision. A scaling system with a maximum instrument error of 0.2% was used to test different types of thermal neutron detectors. The most suitable type of detector was a boron-10-lined proportional counter tube. While this type of detector showed satisfactory stability, extensive testing disclosed a long-term count reduction probably due to some type of deterioration in the detector. However, development of an electronic system using dual detectors eliminated this deterioration as a serious problem. (The second detector would be used to measure a reference drum of dry coal — the difference in count rate between the wet coal and dry reference coal being a direct measure of moisture content.) Table I, column 1, shows typical results with a 1-curie plutonium-beryllium neutron source and a thermal neutron detector beneath a tray of coal and illustrates the precision of measurement. Consecutive measurements (indicated in Table 1, columns 2-5) of thermal neutrons at various times and positions be-

Jan 1, 1968

By Michael Hoch, Walter C. Wyder

The isothermul section of the Nb-Ti-Zr-O system at 1500°C was investigated using X-ray dzffraction and metallographic techniques. UP to 66.7 at. pct 0, the system contains nine four-phase regions. Tsopleths at 10, 20, 30, 40, 50, and 55 at. pct 0 weye constructed. The purpose of this investigation was to determine the general shape of the quaternary equilibrium phase diagram of niobium, titanium, zirconium, and oxygen at 1500°C. The system was truncated at 66.7 at. pct. O., PREVIOUS INVESTIGATIONS The Ti-Zr-O system was investigated in this laboratory.' The binary systems of interest have been compiled and discussed by anssen2 and Levin, McMurdie, and Ha11. Elliott4 has determined the Nb-O system by metallographic and X-ray diffraction techniques. He shows the existence of three oxides, namely NbO, NbO2, and Nb2O5. At 1500°C the solubility of oxygen in niobium is about 4 at. pct. No solid solubility region is shown for either NbO or NbO2. EQUIPMENT The same equipment as that for the study of the Ti-Zr-O system was used. The X-ray diffraction patterns were analyzed with the help of the ASTM card set5 and NBS circulars.6 MATERIALS The niobium powder (99 pct pure), the titanium powder (99.6 pct pure), the niobium pentoxide, and the zirconium dioxide used in this study were purchased from the Fairmount Chemical Co., Newark, N.J. The zirconium powder (99.4 pct pure) was obtained from the Charles Hardy Co., Inc., N.Y. Reagent-grade titanium dioxide was purchased from the Matheson Co., Inc., Norwood, Ohio. The oxides were dried in air at 700°C for 24 hr before use. Though the materials used were not "hyper-pure," the impurities present do not affect the results (lattice parameters, phase boundaries), within the experimental accuracy. PROCEDURE Samples of the desired compositions were made up, in mole pct, from the materials listed above. In some cases the intermediate binary compounds, such as NbO and TiZrO4 were prepared beforehand and used in the preparation of the samples. This technique enabled equilibrium to be reached from two sides. The components of each sample were mechanically mixed in a mortar and pestle and pressed into 3/16-in. diam pellets. The pressures used in compacting were of the order of 50 to 100 x 103 psi. Sintering was accomplished by heating the samples in a tungsten crucible (3/4-in. high, %-in. diam, 1/8-in. wall, lid with XB-in. hole). The pellets were separated from each other and from the crucible by means of small spiral coils of tungsten wire placed between the stacked pellets and on the bottom of the crucible. The sintering time was from 4 to 12 hr at 1500°C under a vacuum of 6 x 101-5 to 1 x 10-6 mm of Hg. All samples were reground after the first or second heating repressed, and reheated. In most cases: equilibrium was obtained after the first heating, as the X-ray diffraction pictures after each heating remained unchanged. Quenching of the samples from 1500°C was at first only possible by allowing the crucible and its contents to lose heat by radiation. The temperature dropped from 1500° to 900°c in approximately 1 1/2 min, which was considered adequate when compared to the times used by other investigators to reach equilibrium in the temperature range of 1000°c and lower. Later, a new technique for faster quenching of the samples was cleveloped. This technique involved the removal of the samples from the crucible, whereupon they were quenched by coming in contact with the water-cooled copper base of the furnace. This manipulation was performed without breaking the vacuum. The sample pellets were placed on a tungsten wire rack inside the crucible. The wire rack passed through the hole in the crucible lid, where it was connected to a small nonmagnetic chain. The chain was fed to the side of the furnace by means of a brass rack which fitted between the body and lid of the furnace. Suspended at the end of the chain, near the furnace wall, were three magnetic washers. With the use of a strong

Jan 1, 1962