By H. L. Talbot, A. J. Hall, R. S. Young

A METHOD for the chemical differentiation of oxidized cobalt from sulphide cobalt in complex mine and concentrator products is of considerable interest to a number of mining companies throughout the world. At Rhokana Corporation, in Northern Rhodesia, for instance, cobalt is found chiefly in the sulphide form, as carrollite, but a cobalt oxide mineral also occurs irregularly underground, and relatively small quantities in the mill feed from time to time are difficult to detect it visually at the concentrator. The oxide cobalt is not amenable to the sulphide flotation process used at Rhokana and nearly all of it passes into the tailing. The occasional. period when high tailing losses occur with no appreciable change in the cobalt content of the mill feed has naturally been disturbing to the concentrator staff, who had no means of determining whether an influx of cobalt oxide ore or laxity on the part of the mill flotation operators were responsible for these results. A procedure for determining oxidized copper minerals, based on their solubility in dilute sulphuric acid saturated with SO2, has been used for many years in the copper industry. In the presence of cuprite the procedure fails, but otherwise it gives results quite satisfactory for control purposes. Empirical methods for determining oxidized forms of zinc and lead have been proposed, but they are generally unsatisfactory except in isolated cases of a very simple ore. No published procedure for determining oxidized forms of cobalt or similar elements has come to the authors' notice. EXPERIMENTAL PROCEDURE There are obviously two alternatives in attacking a problem of this nature. One is to employ a solvent for oxide cobalt that will not dissolve cobalt sulphide. The other is, to find a substance capable of oxidizing the cobalt sulphide to sulphate, which of course is water-soluble and can then be leached from the water-insoluble oxide cobalt. A representative sample of Rhokana cobalt oxide ore was secured, ground to minus 200-mesh, and carefully rolled to furnish a standard sample for this work. The analysis of this material gave the following percentages: Co, 0.55; Cu, 1.64; Fe, 2.98; S, 0.08; SiO2, 41.42; A1203, 11.20; CaO, 13.82; MgO, 3.80. As a source of cobalt sulphide a similar large sample of carrollite was prepared, analyzing Co, 23.36 per cent; Cu, 27.32; and S, 31.13. This sample of course was not pure carrollite, but was the best obtainable in quantities sufficient for a standard intended for considerable work. It was a pure sulphide sample, microscopic examination showing only carrollite, a little bornite, and gangue, with no visible sign of oxidized ore present. A wide variety of reagents were used in an effort to selectively dissolve oxide cobalt or to oxidize sulphide cobalt to

Jan 1, 1946

By William Klement

THIS note reports the results of some attempts to metastably extend the primary solid solubilities of tin, antimony, and silicon in silver by rapidly quenching these binary alloys from the melt. The procedures employed for alloy preparation, quenching, and Debye-Scherrer X-ray diffraction measurements have been described elsewhere. The lattice parameters obtained for the fcc structures in Ag-Sn and Ag-Sb alloys are presented in Fig. 1, together with the results of Owen and Roberts.4 Alloy compositions are believed to be within ± 0.2 at. pct on the basis of negligible weight losses during preparation and reproducibility of the lattice spacings. Diffraction lines from hcp phases were also detected: the relative visual intensities of the fcc (200) and hcp (10.2) lines were estimated as shown in Table I. The intensities were m for the (200) and w for the (10.2) in a quenched 13.6 at. pct Sn alloy: a lattice spacing for the fcc structure could not be reliably obtained, however. As seen from Fig. 1, the lattice parameters vary linearly with composition up to 8., at. pct Sb and 13." at. pct Sn, respectively, which may be compared with the maximum equilibrium solid solubilities5 of 7.2 at. pct Sb and 11.5 at. pct Sn, respectively. The presence of the hcp phases, which were found together with the fcc phases, is a consequence of the competition1,3 in the nucleation and growth processes during solidification. Both the fcc and hcp phases must be of the same composition for those alloys in the range where lattice parameters increase linearly with solute concentration. Despite much effort with quenched alloys of several silicon concentrations, it has not been possible to obtain lattice spacings of sufficient precision to establish the variation of lattice parameter with composition or the maximum metastable solid solubility: the equilibrium data5 suggest little primary solid solubility of silicon in silver. For alloys containing less than 16 at. pct Si, the Si (111) diffraction line was not observed. For alloys containing 10 to 25 at. pct Si, faint low-angle lines were detected and these could be indexed as the (10.0), (00.2). and (10.1) reflections of an hcp structure with a = 2.87 + 3A. c = 4.52 ± 3A, and c/a = 1.57 ± 2. The 16 at. pct Si alloy was quenched to, and examined at. liquid nitrogen temperatures without any change observed in the proportion of the hcp phase. These experiments were jointly supported by the Atomic Energy Commission and Office of Naval Research under a program directed by Professor P. Duwez. The assistance of H.-L. Luo and A. Abu-Shumays is acknowledged. as is the support afforded

Jan 1, 1965

By L. Grånäs, B. Aronsson

In a recent study of Fe-Si alloys Walter and Koch' observed pairs of dislocations in Fe-6.25 pct Si crystals rolled to reductions of 10 pct and subsequently annealed for 1 hr at 650°C. They interpreted these pairs as being due to stacking faults. From the spacing of the dislocations a stacking-fault energy of 15 to 19 ergs per sq cm was calculated. These authors did not pay any attention to the order -disorder phenomena in Fe-Si alloys. It is the purpose of this communication to report some preliminary results from a study of ordering and its influence on the plastic deformation of Fe-6.0 pct Si alloys. Our results suggest that the dislocation pairs observed by Walter and Koch may have been due to long-range order rather than to stacking faults. The alloys used in this investigation were prepared from pure electrolytic iron and silicon and were melted in argon. After hot working, strip tensile specimens were machined to a gage length of 70 mm and a thickness of 1 mm. The specimens were heat- treated for 2 hr at 1000°C, furnace-cooled, and subsequently deformed 2 pct in tension at 400°C. The strain rate was 5.6 X lo-' sec-'. Thin foils of the deformed specimens were prepared by means of the Bollman technique and examined in a Siemens Elmis-kop I at an accelerating voltage of 100 kv. In the Fe-Si system long-range ordering occurs at a silicon content of about 6 pct Si. In our alloys evidence for ordering is given by selected-area diffraction patterns which show extra reflections consistent with a super lattice of the D0 9 type. In addition, the dislocation arrangement in deformed specimens indicates that long-range order is present. A typical mi-crophotograph of a thin foil is shown in Fig. l. The dislocations are usually straight and parallel and laying in distinct directions. In the commonly observed (111) zone the projections of the dislocations are close to (113) and (oil). Observation of the image position indicates that the two dislocations in a pair have the same Burgers vector and hence constitute a superlattice dislocation.~ According to theory3 a superlattice dislocation in the DO3 structure consists of four ordinary dislocations connected by two types of antiphase boundaries as shown in Fig. 2. In our specimens only two dislocations in each pair have been observed, Fig. 1. The problem is to decide whether the area between these is a NN or a NNN antiphase boundary. Dark-field images using the (200) reflexion (the indices are defined with respect to the DO3-type superlattice) can

Jan 1, 1968

By Eric Kula, Åke Josefsson

L. J. Dijkstra and R. Sladek, (Ontario Research Foundation, Toronto, and Institute for the Study of Metals, Chicago, respectively)—This interesting paper confirms some results obtained some years ago in collaboration with Fast: namely the broadening of the nitrogen peak by the presence of small amounts of manganese. Later on a more extensive study of this effect was made at the Institute for the Study of Metals at Chicago. As the work has not yet been submitted for publication we wish to mention here briefly some of the results. The effect of about 0.5 atomic pct manganese, chromium, molybdenum, or vanadium on the nitrogen-peak in iron was examined. The broadening found previously in the case of manganese was even found to be more pronounced for chromium. In the case of molybdenum and vanadium a double peak was observed which seemed to justify the idea that in all cases mainly two relaxation times were involved: namely, the normal relaxation time as found in pure iron and a second relaxation time related to the existence of abnormal interstitial lattice sites introduced by the foreign metallic element. The analysis showed that for the normal nitrogen-peak as a reference at 22°C the abnormal peak was found at about 32°, 47°, 75°, and 87°C in the case of manganese, chromium, molybdenum, and vanadium, respestively. In the manganese alloy the free energy difference for a nitrogen-atom at an abnormal and a normal lattice site was estimated at 2800 cal per mol. This means that for temperatures above 100°C the solid solubility and overall diffusion rate of nitrogen is not much affected by additions of 0.5 pct Mn. We believe that the difference in rate of precipitation of nitrogen in pure iron and the manganese alloy is mainly a question of the number of potential nuclei available in the different steels. In studying the effect of these alloying elements on precipitation of nitrogen, a distinction must be made between the para reaction and ortho reaction, using terminology introduced by Hultgren.7 The ortho reaction in which the alloying metallic element participates in the diffusion under formation of nitrides occurs at high temperatures such as 600°C. The para reaction in which the alloying metallic element does not diffuse and in which the nitride inherits its alloy content from the matrix occurs at lower temperatures. To prevent the ortho reaction the alloys have to be quenched rapidly from the phase. It is not surprising that the authors find that the height of the peak indicates a lower nitrogen content than chemical analysis. In the first place the peak is not a single relaxation peak and secondly, the steels were not quenched from the phase after the nitrogen was introduced at 580 °C.

Jan 1, 1953

By R. Schuhmann

PROBLEMS in expressing, interpreting, and using size-distribution data recur in many phases of mineral dressing; therefore it is desirable that size analyses be expressed in such a form, either numerically or graphically, that comparisons can be made readily. The size distribution of comminuted material is a result of a specific physical operation on the material and therefore should be governed by some definite physical principle, or cause-effect relation. Although this principle has not been discovered, it has been found that the size distribution of comminuted, homogeneous solids may be expressed by relatively simple mathematical equations. Two equations in particular, proposed by Gaudin1 and by Rosin and Rammler,2 respectively, have stood out, both having wide demonstrated ranges of application. The form and the method of application of the two appear almost irreconcilably different on the surface, but, as will be shown, they are asymptotic in the fine sizes when expressed in the same units. This paper gives the results of a further study of the Gaudin and Rosin-Rammler relations, made with the object of developing a form of size-distribution equation that will be more usable and more significant-particularly in comminution studies, both for interpreting the nature of size distribution and for evaluating surface. The work is summarized in the following: I. An equation relating cumulative per cent finer to particle size in the fine sizes is derived from Gaudin's original equation. That equation relates weight per cent retained on one size and through the next larger size in a geometric series of sizes to size (of the retaining screen, for example). 2. Comparisons with Gaudin's equation and with the Rosin-Rammler equation show that the cumulative equation applies to the fine sizes of all size distributions that fit either of these earlier relations, and, furthermore, has some advantages over each. 3. A simple graphical method of surface calculation based on the cumulative-equation plot is evolved and illustrated. 4. Additional confirmation of the cumulative equation was obtained in the more severe test of sizing down to the limit of a sedimentation balance a sample of jaw-crushed quartz. The equation was closely followed over a 20o-fold range in size, from approximately 0.4 mm. (35 mesh) down to 0.0023 mm. (2.3 microns), the lower limit of the size analysis made. There is no indication that the equation will not hold further to well below 2.3 microns. 5. Calculations of the surface produced in the jaw-crushing test mentioned above showed that at least 8o per cent of the total new surface was on particles finer than 35 mesh (about ½ 5 of the crusher setting). The minus 35-mesh portion was only

Jan 1, 1940

By C. H. Li, R. J. Stokes, T. L. Johnston

The phenomenon of solid-solution strengthening has previously been studied in a number of binary alloy systems.1-8 There has been, however, very little information published concerning the strengthening effects of specific solutes in magnesium alloys. Schmid and his coworkers9,10 investigated the behavior of aluminum and zinc in binary and ternary magnesium-alloy single crystals, but this work was done before high-purity materials were readily available. Workers at the Dow Chemical companyH reported increases in the critical resolved shear stress upon alloying magnesium single crystals with zinc and indium. Recently, Hardie and parkins* investigated the extent of hardening produced by the addition of various solutes to poly crystalline magnesium. The present work was undertaken to provide data on the strengthening effects of a number of solutes in high-purity magnesium, for the purpose of supplying further experimental information which might be useful in describing a general mechanism for solid-solution strengthening. To simplify interpretation of the results, the mode of deformation was limited to basal slip, through the use of single crystals. EXPERIMENTAL PROCEDURE Magnesium and magnesium binary-alloy single crystals containing indium, cadmium, thallium, aluminum, and zinc were prepared in the form of l/2-in.-diam rods, approximately 8 in. long, using a modified Bridgman technique in which the crystals were slowly cooled from the melt in a steep temperature gradient, in an atmosphere of helium. It was found that a solid-liquid interface travel speed of about 0.7 in. per hr consistently produced single crystals. The poly crystalline starting materials for the preparation of single crystals consisted of 1/2-in.-diam extruded rods, prealloyed to the desired composition. The unalloyed magnesium and magnesium-indium extrusions were furnished by the Dow Chemical Co. The other alloys were prepared at the Rensselaer Polytechnic Institute Metallurgical Laboratories. Some preliminary studies of the strengthening effect of indium were conducted at room temperature using a constant rate of tensile loading of 1040 g per min. Stress was applied to the crystals by means of a simple 5:l lever arm. The lever was loaded by a constant rate of flow of shot into a receptacle suspended from the long arm of the lever. Plastic flow was detected by an electrical resistance strain gage cemented to the surface of the crystal normal to the minor axis of the predicted glide ellipse. The crystals were acid machined to produce tensile specimens with a reduced section between the grip ends, with an additional step in the center of the reduced section to compensate approximately for the slip-retarding effect of the strain gage. The balance of the single crystals were extended in an Instron tensile tester. This machine employs a synchronously driven screw and automatically records applied load as a function of cross-head separation. It became unnecessary therefore, to employ a strain gage to detect deformation or to acid machine a reduced section. Preparation for testing reduced merely to chemical cleaning of the surface, thus minimizing the amount of handling and probability of accidental damage to the crystals. The rate of elongation employed in all the tests was 0.002 in. per min, corresponding to a strain rate of approximately 0.0004 per min. EXPERIMENTAL RESULTS The investigation confirmed the finding of many workers that the yield strength of hexagonal metal crystals is strongly orientation-dependent. This is illustrated in Fig. 1, in which o, the tensile stress required to produce gross plastic flow in eleven unalloyed magnesium crystals stressed at a constant rate of loading is plotted as a function of sin X, cos Ao where X, is the angle between the

Jan 1, 1960

By J. N. Butler, R. J. Morris

A series of organic collectors has been developed which successfully float synthetic secondary uranium minerals, such as autunite, carnotite, and torbernite. Recoveries up to 97 pct have been obtained. With cleaning of rougher concentrates, ratios of concentration as high as 15:1 are possible on head assays of 0.10 to 0.50 pct U 3 O 8. Additions of certain base metal salts aid in recovery and materially increase the rate of flotation and selectivity of the collectors for the synthetic minerals. Flotation tests on natural uranium minerals have not yet equaled results obtained on the synthetics, although these collectors do give better results than conventional collectors for nonsulfide minerals. RAPID increase in mining and milling uranium ores during the past seven years and the discovery of large tonnages of uranium-bearing material too low in grade to stand the cost of leaching have developed considerable interest in possible methods for beneficiating these marginal ores. Such ores are generally classed as those containing less than 0.10 pct U3O8. Development of a beneficiation method that would give both high recovery and high ratio of concentration would also make possible the beneficiation of higher grade ores and would provide higher grades of feed to existing leaching plants. Although considerable research and testing on physical or physico-chemical beneficiation of domestic uranium ores has been done in the past, to the best knowledge of the authors only a single application of physical beneficiation is now in operation on a commercial scale. Flotation has been attempted on the basis of mineral association rather than by direct concentration of the contained uranium minerals. Flotation studies conducted on this project on certain ores gave recoveries of 60 to 70 pct of the uranium by the use of conventional flotation agents such as oleic acid, but ratios of concentration were in the order of 1.5:1 to 2.5:1. Subsequent cleaning to upgrade the concentrates rapidly increased losses in the cleaner tailings, which were not later refloated in the rougher flotation. Selection of Collector: In selecting desirable organic collectors for these oxide systems, a thorough study was made of the relationship between structural characteristics and collector activity by an examination of the behavior of a number of different functional arrangements present in a variety of organic molecules, (see Fig. 1). It is generally accepted that a collector must have a relatively long-chain hydrocarbon radical and a chemically reactive elec-trophilic center. Such a requirement could be met by a large number of compounds, but steric effects at the uranium mineral surface, solubility, compat-ability with aqueous systems, air avidity, bond strength at the mineral surface, interfacial concentration of the collector, and diffusion rate of the formed complex from the air-water interface eliminated many as unsuitable for this purpose. Preliminary investigations were completed of possible collector designs consisting of aliphatic and aromatic hydrocarbon radicals attached to stable combinations of nitrogen, oxygen, sulfur, and halogen electrophilic centers, Fig. 1.Tests were made to determine melting point spans, solubility of mineral-collector combinations in various solvents, reactions with soluble uranium salts, contact angles, and floatability by semi-quantitative beaker methods.' Contact angle determinations were not too useful because of the fine particle sizes of available mineral samples. From the foregoing study it appeared that nitrogen-sulfur electrophilic centers coupled with straight-chain saturated alkyl hydrocarbon radicals would hold the most promise for floating secondary uranium minerals. As the dithiocarbamate compounds can be made to combine these attributes they were selected for further study. The dithiocarbamates form a parallel structure to the xanthates, with the fortuitous exchange of

Jan 1, 1957

By R. I. Jaffee, C. M. Craighead, G. A. Lenning

Hydrogen forms a beta-stabilized system with titanium, with a beta eutectoid at about 300°C and 44 atomic pct H2. 'The solid solubility of hydrogen in alpha decreases from about 8 to about 0.1 atomic pct from 300°C to room temperature. Hydrogen has little effect on tensile properties, but decreases notch-bar toughness to a large degree. This latter effect appears to be the result of increased notch sensitivity. PRIOR to this investigation, only a small amount of information was available on the effect of hydrogen on the mechanical properties of titanium. The effects of the other interstitially soluble elements, carbon, oxygen, and nitrogen, had received detailed study. Jaffee and Campbell1 indicated that hydrogen up to 1 atomic pct did not affect tensile properties deleteriously. Pitler' indicated that 1 atomic pct H, in titanium reduced the impact strength appreciably, but his alloys contained appreciable amounts of oxygen, and it was difficult to attribute the embrittlement entirely to hydrogen. The high temperature portion of the equilibrium diagram for the Ti-H system was established by McQuillan," and his data generally corresponded with the results of Kirschfeld and Sieverts," Gibb and Kruschwitz," Bevington, Martin, and Mathews," and other investigators. The lower concentration limit of the hydride phase varied considerably among investigators, and Gibb and Kruschwitz9 ad shown that small amounts of contaminants in either titanium or hydrogen caused considerable variation in this lower limit. In view of this pronounced effect of contaminants, the extrapolated value of McQuillan's, about 48 atomic pct at the 325°C eutectoid, appeared the most reasonable. McQuillan's lowest experimental value was 54 atomic pct at a temperature of 450 °C. The density of titanium had been shown to decrease with increasing hydrogen content, but discrepancies were noted among the various investigations. The best values indicated that the density was decreased from 4.56 grams per cc at 0.27 atomic pctl to 3.84 grams per cc at 61.3 atomic pct? This investigation was conducted to determine the effects of hydrogen on a titanium, both in high purity and commercially pure metals, and on high purity a titanium alloys. Material and Fabrication The literature indicated that impurities in either the hydrogen or the titanium must be kept to a minimum. For this reason, the initial studies were made with high purity iodide-refined titanium. The vendor's analysis of the iodide titanium and the hydrogen content of the as-fabricated Y4 in. diameter rods are shown in Table I. Two 1 lb ingots were prepared by arc melting under argon in a water-cooled crucible, using a water,cooled tungsten electrode. This equipment has been described.' As-cast Brine11 hardness numbers of 88 and 58 for these ingots were low enough to insure that the high purity of the metal was maintained during arc melting. The ingots were hot forged to % in. diameter rods at 800°C, cleaned by grit blasting, and then cold swaged to Yz in. diameter rods. The rod was then air annealed at 725 "C, ground to remove scale, and cold swaged to Y4 in. diameter (75 pct reduction in area). The material was then annealed for 1 hr in argon at 800°C to develop an equiaxed a grain size of about 0.05 mm. Micro tensile specimens and microimpact specimens were machined from this rod prior to treatment in the Sieverts-type absorption apparatus. Two lots of commercially pure RC-55 titanium were also used in this investigation to determine the effects of hydrogen and the normal impurities on mechanical properties. The commercially pure RC-55 alloy was obtained in the form of % in. diameter rod. The analysis of this material is also given in Table I. The % in. diameter rods were hot swaged

Jan 1, 1955

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid cobalt and a number of dilute cobalt alloys Was measured in the temperature range 1550" to 1700°C at nitrogen pressures to 1 atm. At 1600°C and 1 atm nitrogen pressure, the solubility in pure cobalt is 0.0047 wt pct [3.8 cu cm (stp) per 100 g Co]. The standard free- energy change for the solution reaction 1/2 N,(g) = gout pct in Co) is iF - 10,000 + 5.24 T cal per g atom N. The alloying elements Cv, Cu, Mo, Nb, Tu, W, and V increase the nitrogen solubility, while Al, Fe, Ni, and Si decrease the nitrogen solubility. THE solubility of nitrogen in cobalt was studied previously by Sieverts, Busch and Dodd,2 and Schenck, Frohberg, and Graf.3 Sieverts investigated the solution below the melting point of cobalt, and Busch and Dodd worked with the liquid metal; however, neither study found any solubility for nitrogen in cobalt. Schenck et al, reported a solubility of 0.005 wt pct N in cobalt at 1600°C. Seagle et al. 4 reported residual nitrogen in cobalt after electron-beam melting, although no reasons were ventured for the presence of this interstitial impurity. This investigation was undertaken to clarify these inconsistencies, and to provide additional data on atomic interactions in dilute metallic solution. EXPERIMENTAL PROCEDURE This study was well-suited to the Sieverts' method, which has not changed significantly since its introduction by Sieverts. 5 The apparatus was of the same design as that described by Humbert and Elliott, 6 with a reaction bulb similar to that reported by Weinstein and Elliott. 7 The buret was not water-jacketed, but the measured gas volumes were corrected for small changes in room temperature. The melt temperature was measured by a disappear ing-filament optical pyrometer sighted through a prism onto the melt surface. Temperature calibration was made based on a measurement of the melting point of pure cobalt taken as 1495°C. The difference between the reciprocal of the observed and the true temperatures was assumed to be a constant, neglecting the changes in emissivity with small additions of alloying elements. The total error in gas-volume measurement caused by accuracy limitations in reading the mercury level in the buret, variation in ambient temperature, and variation in melt temperature was about 0.5 cu cm. This represents approximately 10 pct of the total solubility, and is a larger relative error than in previous studies6-' because of the small nitrogen solubilities encountered in the present investigation. The source and purity of the materials used are listed in Table IA. Recrystallized alumina crucibles were used throughout the investigation. Examination of the crucibles after solidification of the melts showed no reaction or penetration. Alloying of the cobalt melt was accomplished with the dropping technique described by Humbert. 6 The investigation was started using cobalt from African Metals Corp. in shot form, but this material was not of sufficient purity and did not yield consistent solubility results. Sherritt Gordon Mines Ltd. cobalt was then used throughout the investigation. In experiments involving alloying elements which could react with oxygen dissolved in the melt, the cobalt was further refined by annealing at 1400°C in a dry-hydrogen atmosphere. This treatment, described by Woolley and Pehlke, 8 markedly reduced the oxygen content. The oxygen and nitrogen analyses of the cobalt used in this study are presented in Table IB. RESULTS Hot Volume. The hot volume was measured prior to each run and was 50 to 55 cu cm (stp) at 1600°C. It increased linearly with increasing pressure and decreasing melt temperature. Pure Cobalt. Measurements of the solubility of nitrogen in pure cobalt and the temperature coefficient of solubility are summarized in Table 11. At 1600°C and 1 atm nitrogen pressure, the solubility was found

Jan 1, 1967

By J. M. Smith, G. P. Willhite, J. S. Dranoff

Heat transfer rates were measured in sandstones with flow of gases perpendicular to the direction of energy transfer. Effective thermal conductivities ker ranged from 0.7 to 1.7 Btu/(br)(ft)(°F). The contribution of the solid phase appeared to be the most important in these consolidated materials, although the thermal conductivity of the gas had some effect. The velocity of the gas through the pores of the sandstones had no influence upon ker up to values of 168 lb/(br) (sq ft) in agreement with data obtained for unconsolidated beds of glass beads. The present results indicated that gas mixing, and hence heat transfer by convection in the pores, is less for perpendicular transfer of energy than when fluid flow and energy transfer are in the same direction. HEAT TRANSFER PERPENDICULAR TO FLUID FLOW IN POROUS ROCKS Heat transfer in porous media with pore sizes in the micron range depends upon the fluid in the pores and the geometry of the solid phase. The best characterized system is a bed of solid spherical particles. Heat transfer in this system has been studied extensive1y (Ref. 8 summarizes the literature up to 1959) when the pores contain stagnant fluid. When the fluid is in motion the directions of flow and energy transfer have an effect on the heat transfer rates, as demonstrated by comparing the work of Willhite, et al l3 for perpendicular flow and that of Kunii and Smith9 for parallel flow of energy and fluid. For perpendicular flow, no increase in effective thermal conductivity ke was noted up to mass velocities G of 77 lb/(hr) (sq ft). In contrast, for parallel flow ke, increased with G in the same range of flow rates. These higher values of ke in the direction of flow also have been observed3,4,10 in beds of larger particles, 0.1- to 0.5-in. diameter. For beds of consolidated materials, such as porous rocks, data are not available for these compar- isons, although Adivarahan1 reported results for the parallel case. Hence the primary objective of this work was to measure ke values for perpendicular flow of fluid and energy in porous rocks. Of interest also was the variation in effective conductivity with fluid velocity. APPARATUS AND PROCEDURE In the experimental method, a constant heat flux was applied to the inner surface of an annular section of the porous rock. By cooling the outer wall, a temperature gradient through the annular sample was established and measured with thermocouples placed within the sample at various radial positions, and at three elevations (A,B.C). The location of the 2-in. O.D., 3.75-in. long sample in the apparatus is shown in Fig. 1. Fluid entered the bottom (1) of the 3-in. I.D. (approximate) steel shell, flowed upwards through the sample and out at the top (3). pressure taps (2,4) were used to check the permeability of the sample. The energy flowed radially from the centrally-located electric heater through the sample and was absorbed in the water-cooled jacket. The samples studied were naturally occurring sandstones from different locations with the properties given in Table 1. These materials are identical with those used by Adivarahan 1 for the parallel flow of energy and fluid. Prior to use they were refluxed with toluene to remove hydrocarbons and leached with distilled water to remove soluble salts. Each sample was visually examined and discarded if large nonhomogeneities, such as cracks or stone particles, were noted. Eight copper-constantan thermocouples were inserted in holes drilled radially into the sample with

By R. S. Rickard, M. C. Fuerstenau

Anodic polarization curves for iron dissolution and cathodic polarization curves for copper deposition and ferric and hydrogen ion reduction were studied. These results were used to predict the relative rates of the reactions: The rates of the first two reactions were found to be first order with respect to the reacting ion, and the rale-controlling step was diffusion of the ions to the callzode surface. The rate of hydrogen ion reduction in an oxygen-free solution is dependent on the reciprocal of the square root of the hydrogen ion activity. In solutions containing oxygen, the rate of hydrogen reduction becomes dependent on the square root of the partial pressure of oxygen. At equal concentrations copper precipitation occurs about twice as fast as ferric ion reduction. In an air-saturated solution containing 0.01 M cupric ion at pH 2, the rate of hydrogen ion reduction zs about 10 times slower than that of copper precipitation. At pH values below 3, the rate of hydrogen reduction in oxygen-free solutions is very slozu. COPPER cementation has been utilized industrially for many years as a means of recovering copper from aqueous solutions. There are many different types of cementation plants, but all simply provide a means of contacting iron with relatively dilute copper solutions. In the past little or no attention has been paid to rates or mechanisms of the reactions involved. As a result, this and other studies'-3 have been undertaken recently to establish the important parameters in this system. The reactions involved in copper cementation by iron are: Since transfer of charge is involved in every case, these reactions should be considered from an electrochemical point of view. In any electrochemical system involving electrolytic conduction, passage of electrons necessitates ion transfer to the respective electrodes according to Faraday's law. The current in the system will be proportional to the rate of ion transfer, and, therefore, when the current in the galvanic cell is known, the rates of the reactions involved can be determined. Galvanostatic electrode measurements5" are applicable for these electrochemical studies, in that with this technique polarization curves (current density vs electrode potential) are established by impressing a constant current through an electrode and measuring the electrode potential. Once the current density, electrode potential, and reacting area are known for each reaction in this cementation system, the rates of the iron-consuming reactions can be determined. EXPERIMENTAL MATERIALS Several metal electrodes were used in this investigation; they are shown in Table I. Solutions were made with reagent-grade salts and conductivity water. Air, nitrogen, and oxygen were employed. All of these gases were saturated with water and degreased prior to use. EXPERIMENTAL PROCEDURE The experimental work was divided into two general areas. The first area involved galvanostatic measurements, which were used to determine the rates of reactions as a function of various parameters. The second area comprised actual cementation experiments to check the rates predicted from the electrode measurements. Galvanostatic Electrode Experiments. Polarization curves were obtained using a standard galvanostatic technique5'= with the apparatus shown in Fig. 1. The various electrode polarization experiments were run the same way except for changes in solution composition, polarity, and type of measured electrode. The general procedure involved the following steps: 1) a solution was made 0.5 M in sulfate ion and to the desired cation concentrations; this solution was placed in a constant-temperature bath and saturated with the desired gas; 2) the electrodes were cleaned and placed in the electrode holder; 3) the previously cleaned apparatus was assembled and immersed in a constant-temperature water bath (temperature controlled to ± 0.05"C); 4) the electrode was then positioned; the solutions were introduced, and the polarization meas-

Jan 1, 1969

By G. L. F. Powell, L. M. Hogan

Large degrees of undercooling have been produced in bulk samples, 400 g, of copper and Cu-O alloys by melting in a slag of commercial soda-lime glass. The maximum degrees of undercooling obtained for copper, hypoeutectic and hypereutectic Cu-O alloy samples were 208°, 218°, and 97°C, respectively. No grain refinement as a function of undercooling was observed for the pure copper samples although in Cu-O alloys there was a marked decrease in grain size at degrees of undercooling greater than 150°C. The grain size change is the result of recrystallization during or immediately following the freezing process. THE first report of a large degree of undercooling in a bulk sample of metal was that by Bardenheuer and Bleckmann1 who produced 258°C undercooling in a 150-g sample of iron by melting in a glass slag. Garbeck2 extended this technique to nickel, cobalt, and copper and reported maximum undercoolings of 220°, 230°, and 60°C, respectively, while Fehling and schei13 undercooled a large number of metals as 2 to 20-g samples slagged in glass. Subsequently, one of the authors4 applied the glass slag technique to bulk samples, -500 g, of silver and obtained a maximum undercooling of 250°C. It was concluded that impurities which normally catalyze nucleation at small degrees of undercooling could be removed by oxidation and solution in a glass slag. Large undercooling of bulk samples of iron, nickel, cobalt, and their alloys has also been reported by other authors.8'10'11 Of the five metals mentioned above, copper was the only one which had not been undercooled by at least 200°C in the form of a large bulk sample. Since copper exhibits high liquid solubility for oxygen, as do iron, nickel, cobalt, and silver, it was considered that a much larger degree of undercooling than that observed by Garbeck for copper should be possible. This was obtained by modification of the technique applied previously to silver and the results of undercooling experiments with 400-g samples of copper form part of this paper. The undercooling behavior of Cu-O alloys was also studied, and the influence of a small oxygen content on the grain structure of undercooled copper was observed metallographically. 1) EXPERIMENTAL The copper was obtained as oxygen-free high-conductivity copper, the major impurities of which were Fe 0.01 pct, Zn 0.015 pct, and Si 0.02 pct. Melting was carried out in an open-ended vertical cylindrical fur- nace wound with Kanthal wire. A schematic diagram of the experimental setup is shown in Fig. 1. The undercooling technique previously used for silver4 involved preoxidation of the samples by melting the silver in contact with the atmosphere. The oxygen content was subsequently reduced by freezing the samples under a glass slag, whereby the oxygen was evolved as gas and the continuous glass cover over the surface prevented re-solution of oxygen when the sample was remelted. Since oxygen is not released as gas when a Cu-O alloy is frozen. the technique had to be modified for use with copper. Also, copper is oxidized during fire refining so that an in situ preoxidation treatment of the samples was not considered to be a prerequisite to large undercooling. Experimentation proved that this supposition was correct. Instead, it was found that care was necessary during melting of the copper under glass to minimize oxygen pickup. Samples of copper weighing 400 g were prepared by adding 50-g pieces of copper to a vitreous silica crucible partly filled with soda lime glass at a temperature of approximately 1000°C. Each piece was quickly immersed in the glass slag and held at this temperature until the oxide coating on the surface decomposed. This change was easily observed and coincided with the formation of gas bubbles in the glass

Jan 1, 1969

By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.' There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.'j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

By J. F. Butler

Boron nitride, BN, has been identified in boron low-carbon steels by means of light microscopy, electron microscopy and diffraction, and chemical analysis. This boron nitride is responsible for strain aging suppression in these steels through the removal of nitrogen from solution; however, small oxidizing potentials which result in deboronization In the austenitic temperature range also result in boron nitride decomposition and the subsequent occurrence of nitrogen strain aging. THE addition of boron to low-carbon steels is an effective means of eliminating the detrimental effects of strain aging;',' however, the mechanism by which boron suppresses strain aging has not been established. In studying the effect of heat treatment on the strain aging of boron low-carbon steels, Butler3 found that no detectable nitrogen was present in the ferrite solid solution after various heat treatments even though the total nitrogen analyses of the steels were 0.003 pct N. Apparently the function of boron in suppressing strain aging is the removal of nitrogen from solution to form a relatively stable second phase. A clue to the identity of this phase was found by Speight4 who extracted from an aluminum-killed boron steel an acid insoluble residue which contained boron and nitrogen in proportions corresponding to the compound, BN. Shyne and Morgan5 found that the addition of nitrogen to a hardenable boron steel lowered its hardenability in a manner which suggest-d the presence of nucleating particles (presumably BN) even at high austenitizing temperatures. Although this indirect evidence for the presence of boron nitride in boron steels has been found, the compound was not identified metallographically as a separate phase in these steels. Because boron has an affinity for oxygen comparable to that of silicon,5 boron steels must be thoroughly killed with aluminum in order to prevent the reaction of boron with oxygen.7 The affinity of boron for oxygen also is demonstrated through the ease of deboronization of a boron steel in an oxidizing atmosphere. Digges, Irish, and Carwile8 found that a mixture of wet natural gas and air caused both deboronixation and decarburization of a boron steel at 1900°F. The boron content rose at the surface of the steel due to the formation of boron oxide. Shyne and Morgan9 encountered deboronization at much lower oxygen potentials; loss of boron occurred in steels treated at 1750o F under argon purified to 0.0014 pct 0, even though decarburization did not occur. Boron oxide, B2O3, is much more stable than the nitride, BN, as is indicated by the standard free energies of formation at 980oC: -235 kcal per mol of B2O3 (liquid) and -28 kcal per mol of BN (crystal). It is evident that the oxygen potential must be kept low in the presence of BN in order to prevent its decomposition and the subsequent formation of B2O3' The purpose of the work described in this paper was to identify the nitride phase responsible for the removal of nitrogen from solution and to study its stability under oxidizing conditions. IDENTIFICATION OF BN In order to identify the phase containing boron and nitrogen, several alloys high in boron and nitrogen were made up in a small vacuum furnace. In alloys 3 and 4, Table I, electrolytic iron was used as a charge material. Boron additions were made in the form of 18 pct B ferro-boron after the iron was molten. In the case of alloy 3, the charge was solidified at this point; for alloy 4, nitrogen at 1 atm pressure was admitted over the melt before it was

Jan 1, 1962

By T. S. Lundy, R. A. Padgett

The fact that cobalt diffuses in silver at a much slower rate in a region near a free surface than in bulk material has been demonstrated in a variety of experiments. Various possible mechanisms of this near-surface effect (NSE) are examined in light of experimental evidences. The tendency for surface segregation of some solute atoms appears to be a likely mechanism to explain the effect. UNIDIRECTIONAL and isothermal diffusion from a plane source of radioactive tracer into an isotropic, homogeneous medium follows the Gaussian solution to Fick's second law, or: where A(x,t) is the position and time-dependent concentration of the diffusing species, M is the quantity of diffusant per unit area initially at x = 0, and D is the diffusion coefficient. For a given time, say t = tl, one can easily see that: d In Aixji)_____1_ r2] d(x2) 4Dti Thus, if diffusion data obtained by serial sectioning are plotted as In A(x,tl) vs x2, the diffusion coefficient is obtained from Eq. [2]. The ideal behavior seldom is observed in real systems. Deviations from ideality generally occur either at small or large values of penetration distance. The overall picture is shown schematically in Fig. 1 where Regions I, 11, and 111 are due, respectively, to some near-surface effect or effects (NSE), volume diffusion, and short-circuiting effects. For different systems and conditions of specimen preparation and analysis, the relative importance of Regions I, 11, and I11 may be drastically different. Region I is completely absent in many systems and there is no NSE. In others, however, there may be considerable difficulty in determination of volume diffusion coefficients due to the overshadowing influences of Region I. Such is particularly true when indirect techniques such as the surface concentration decrease or the Gruzin method' are used to find D. In this paper several experiments which had as their goal a better understanding of near-surface effects are reported. Specifically, it is well-known that unusual penetration behavior results for the diffusion of several impurities in ilver- and that considerable controversy exists with regard to interpretation of the published diffusion data. We chose to examine those unusual results which occur for cobalt diffusion in monocrystalline silver395 primarily because knowledge of experimental procedures and materials were readily available. Both radioactive co60 and co5' could be utilized to offer a wide range of available concentration of the diffusing species. Experiments were also performed on the diffusion of AgnO in silver. They gave base-line data for the system—both for technique evaluation and for examination of the vacancy distribution near the surface. I) PROCEDURES Cylindrical-shaped specimens 1.25 cm diam and 1 to 1.25 cm long were cut from 99.999 pct Ag single crystals obtained from Monocrystals Co., Cleveland. One end surface of each specimen was polished flat and etched with a mixture of 20 ml saturated Cr03 solu-tion-20 ml H20-3 ml concentrated HC1. Radioactive tracer (co60 or co5' or Ag'lO, each having a radio-chemical purity of greater than 99 pct) was deposited onto the prepared surface either dropwise with evaporation to dryness of the solution containing the tracer (0.5 N HC1 solution for the co60 and co5' and 0.6 N HNO3 solution for the A"'), by electroplating, or by evaporation from a tantalum or tungsten filament in an evacuated bell jar. The amount of deposited cobalt was varied from many atomic layers of cobalt containing the co60 to approximately one co5' atom per lo6 surface atoms of silver. This large variation in amount of deposited cobalt yielded information about both the influence of a thick-source layer of tracer and solubility effects on the NSE. Such variations were possible because of the large differences in half-lives,

Jan 1, 1969

By W. V. Green

The creep-rupture behavior of commercial powder-metallurgy tungsten rod is reported for temperatures of 2250°, 2500°, 2700°, and 2800°C, stresses up to 7000 psi, and times up to 4 hr. The temperature dependence and the stress dependence of creep rates are evaluated. Rupture time is fitted to the Larson-Miller parameter and compared to lower-temperature and higher stress results reported by pugh.4 THE tensile strength of single-crystal wire1 and of polycrystalline wire2 have been measured by Goucher. More recently Bechtold3 and pugh4 have studied the mechanical properties of tungsten rod between room temperature and 1200°C. Since tungsten has the highest melting point of all metals, it should retain useful strength to very high temperatures, and should find many applications in missiles, rockets, and so forth. Therefore, the mechanical usefulness of polycrystalline tungsten rod was investigated in the 2250" to 2800°C temperature range by short-time creep-rupture tests. MATERIALS TESTED Creep specimens were machined from 1/2-in. round commercial tungsten rod which was manufactured from powder by cold pressing, sintering, and hot swaging. Purity reported by the vendor was 99.95 pct W. Spectrochemical analyses showed "traces" (less than 0.01 pct) of silicon, iron, and titanium, and "faint traces" (less than 0.001 pct) of calcium and manganese. Carbon content was 30 ppm and nitrogen content was 70 to 110 ppm. No oxygen analysis was obtained. Room-temperature stress-strain tests on the as-received tungsten gave badly scattered results. Threaded end specimens broke at the threads. When these specimens were retested using shoulder grips, the specimens broke at the shoulders. No fractures occurred in the gage lengths. The fracture stresses were: 127,000; 137,000; and 154,000 psi for three specimens which fractured at the shoulders. The microstructure of the as-received tungsten rod is shown in Fig. 1. SPECIMENS USED Fig. 2 shows the two types of creep specimens tested. The threaded-end type specimen, which was used in most tests, had a 3/4-in. gage length and 1/4-in. gage diam. The cone-end specimen, which was used primarily to investigate the effects of a smaller gage diameter and the practicability of the modified grips and specimen, had a 3/4-in. gage length and a 1/8-in. gage diam. In both cases, the gage length terminated at 0.005-in. high shoulders which served as fiducial marks for optical strain measurements. Surface finish on the gage length was 16 µ-in. rms. Creep rates and rupture times were not significantly different for the two types of specimens and were not affected by electropolishing the specimens before testing. TESTING PROCEDURE The constant-load creep-testing machine used has been described by Smith, Olson, and Brown.5 In it the specimen is held vertically by grips of similar material and on the axis of a cylindrical tungsten or tantalum heater-tube. The specimen is loaded by means of the specimen grips, a pull rod (which is sealed to the chamber lid by a vacuum-tight bellows), a mechanical lever system, and hanging dead weights. Both specimen and grips are heated by radiation from the heater-tube, which is heated by its own electrical resistance. An optical system views the incandescent specimen through slits in the radiation shielding and heater-tube. The optical system projects an enlarged image of the specimen gage length on a ground-glass screen. Periodic gage-length measurements are made on this image with two cathetometers. Thorium oxide coatings on the specimen threads or conical end surfaces completely prevented diffusion-welding of specimens to grips, and were used

Jan 1, 1960

By S. Weinig, E. S. Machlin

IN a previous study of the grain boundary stress relaxation phenomenon,' the authors had arrived at the conclusion that two successive steps were involved in the complete relaxation of stress at a grain boundary. These two steps were grain boundary migration and grain boundary slip. It was further suggested that the slower of these two processes is rate controlling. In an attempt to ascertain the validity of the above, a study of grain growth kinetics on the same alloys used for the previous study was undertaken. Separate wire specimens, 0.030 in. diam, in the same as-deformed state (99 pct reduction in area) as in the previous investigation were heated to the various temperatures for a sequence of times. The compositions used and the temperatures of testing are summarized in Table I. A statistical determination of grain size was then made on each specimen, using the average length of traverse between boundaries as a measure of the grain size. Examples of typical results obtained are shown in Figs. '1 and 2. The grain growth law D = ktn was found to fit most of the data. Using this relation, values of the grain growth exponent n were calculated and the inter -esting dependence of n on solute content shown in Figs. 3 and 4 was then obtained. Also, it was found that the constant K which was obtained from extrapolation is roughly independent of solute content. (K is uncertain to within ±25 pct.) An estimate of the activation energy for grain growth was made using the technique of Burke? This method utilizes the plot of the reciprocal of time necessary for the grain size to increase from a definite starting size Do, to a final size D, for each isothermal heat treatment. The slope of this curve corresponds to the heat of activation for the process. In Fig. 5 the rate of grain growth is plotted against the reciprocal of absolute temperature. The activation energies were obtained from these curves and are summarized in Fig. 6. Discussion It is interesting to note that the same saturation in the variability with concentration has been found for the grain growth exponent n in this research as was found in the previous researches on both grain boundary stress relaxationa and internal friction of dislocation origin." The significant feature is that saturation in the variation of these properties has been found to occur at about the same level of solute concentration, namely, between 0.1 and 0.5 atomic pct. The only characteristic common to these different quantities is that solute adsorption at grain boundaries and dislocation can take place and affect these values in a similar fashion. Thus, it is concluded that the grain growth exponent n depends upon solute adsorption at the grain boundaries. It appears, therefore, that theoretical considerations leading to the contrary conclusions5,6 have not treated the real process by which solute atoms exert their effect on grain growth. Prior to the analysis of the observed activation energies, certain of the aspects of the aforementioned grain boundary stress relaxation investigation will be briefly reviewed. It was found that with the addition of solute atoms the grain boundary stress relaxation peak (internal friction vs temperature) decreased in intensity. Simultaneously a second peak was observed which increased with increasing solute atoms. Both of these peaks were shown to be the result of grain boundary stress relaxation. They have been termed, respectively, poire peak and solute peak. It was suggested that the solute peak was dependent upon grain boundary migration, whereas the pure peak was a manifestation of grain boundry slip. Activation energies for both peaks were obtained as a function of Solute content. The value of the activation energy in the temperature range corresponding to the solute peak was

Jan 1, 1958

By H. N. Lawrie

Introduction. THIS study was undertaken on account of the lack of definite knowledge concerning the influence of bismuth on wire-bar copper, and the small elimination of bismuth from copper-matte during the smelting-operations. The early workers who studied the influence of bismuth on copper confined their investigations to malleability and ductility-two physical properties which are related to the others so intimately that their determination is of primary importance. Karsten ' and Levol,2 using bending- and mealleability-tests, seem to have been the first to take up the subject, and while their results are incomplete, they agree in the main with the later work of Hampe.3 The bending-tests used by the first investigators consisted in bending the specimen until it failed. The malleabilitytests were made by beating the material to a knife-edge with a hammer. Hampe not only determined the percentage of bismuth which would cause red-shortness and cold-shortness of the alloy, together with other influences of bismuth on the malleability and ductility of copper, but also took up the influence of the bismuth protoxide, BiO, on copper, and of bismuth sesquioxide, Bi2O3, on the copper protoxide, CuO. Hampe's conclusions of the influences of these two latter compounds of bismuth on copper are as follows "If the protoxide of bismuth be alloyed with metallic copper, it is not changed to metallic bismuth, but remains mechanically distributed throughout the copper.

Sep 1, 1909

By Kefton H. Teague

Attempts to locate domestic supplies of sillimanite have been unsuccessful until recently. This paper describes recent discoveries of sillimanite-bearing schists in the Southeastern States, with emphasis on geology of the deposits, mineral composition, origin, and reserves. Statements concerning possible methods of mining, milling, and utilization of sillimanite are given. Results from refractory tests on a laboratory scale are summarized.

Jan 1, 1950

By Francis M. Walters

IN spite of the war and the preoccupation of many physical metallurgists with work on secret or confidential problems, definite progress was made during 1944 in our understanding of the behavior of steel and of the effect of alloying elements. During the first two years of the war there was much concern over the possible unavailability of certain alloying elements; this period saw the development of the N.E. (National Emergency) steels. However, the measures taken eased the alloy situation and currently, highly practical problems under study are the graphitization of low-carbon steel and weld-cracking, while investigations of more theoretical interest have concerned hardenability, isothermal reactions, the effect of hydrogen and the interpretation of the notched-bar impact test.

Jan 1, 1945