Search Documents

By Jayagopal Ucbil, M. Krishna, V. T. Vijayalakshmi

"The pitting susceptibility of aluminium metal matrix composites reinforced with garnet particles has been examined using static weight loss method by exposing the metal matrix composites (MMC) specimens to the action of IN HCI acid at laboratory temperature for different time intervals. It was found that the corrosion rate decreased with increase in weight percentage of reinforcement while the corrosion rate was a function of the matrix alloy but not of the reinforcement material. Further, it was found that the rate of corrosion was dependent on the interface region formed between the reinforcement and the matrix. A comparison of the base matrix with the corresponding composite when subjected to heat treatment for varying periods of 4, 8, and 12 hours respectively was made. The comparison revealed that corrosion resistance of the composite increased with the duration of heat treatment and this has established a considerable improvement in corrosion resistance of the composite when compared with the base matrix.IntroductionMetal matrix composites (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and light weight [1-5]. The trend is towards safe usage of the MMC parts in the automobile engine, which work particularly at high temperature and pressure environments [6-7]. Particles reinforced MMCs have been most popular over the last two decades. Among the MMCs, the most popular families are represented by aluminium reinforced with ceramic particles. Although the incorporation of the second phase into a matrix material can enhance the physical and mechanical properties of the base metal, it could also significantly change the corrosion behavior."

Jan 1, 2000

By Noriaki Kurita, Norihiko Fulcatsu, Teruo Ohashi

"An electrochemical sensing device for hydrogen in molten metal has now been available owing to the development of the proton conducting solid electrolyte made of ceramics of metal oxide. The structure of the sensor and the theoretical limitations of its applications are discussed based on the electrochemical properties of the electrolyte used. The practical performance of the sensor is reviewed from the results of test measurements at the plants of aluminum and copper melting industries. The effectiveness of the sensor to the process control of continuous casting of copper is also discussed.IntroductionSince the in-line monitoring of the amount of oxygen dissolved in molten metal was realized by using the oxygen concentration cell based on zirconia solid electrolyte a similar method has been expected to be developed for sensing of hydrogen, which is a very important element of gas species in liquid metals, especially, in aluminum and copper. In 1981; Iwahara and coworkers found the dominant proton conduction at a high temperature in some perovskite-type oxide (1). Since then, the effort has been made to apply this proton conducting material as the electrolyte of the hydrogen concentration cell for high temperature use. The hydrogen sensor for liquid aluminum of this kind was first produced in 1991 (2) and released commercially from TYK Co., Ltd. Recently, we have developed the mother one usable at higher temperature such as copper and silver melting processes (3). In this note we discuss their structure, design and applicable limitations based on the electrochemical properties of this new type electrolyte. The performance of the sensor and benefit to use it to control the melting process is also discussed"

Jan 1, 2000

By S. W. White

Plasma arc technology is increasingly being used to process a number of waste materials. In present research, plasma technology is being investigated to treat waste magnesium baghouse dust, which is a waste material from the Magnetherm process. This dust contains mostly MgO, but also contains NazO, CaO, and KzO. Plasma energy is to be used along with a reducing agent to produce pure gaseous magnesium while keeping the other materials in a slag. The magnesium will then be collected by rapid quenching. A non-transferred arc plasma torch is ideal for this reaction because of its high enthalpy and improved energy efficiency over conventional methods. Another advantage of plasma is that it allows for the pre-heating or pre-reacting of fine particles before contact with the melt. Thermodynamic calculations using the Gibb energy minimization method were used to determine the most stable compositions of the materials at various temperatures. Energy balances have also been calculated. These results conclude that we can recover approximately 98% of the magnesium with a proper quenching technique. The calculated results are compared with the experimental data, and good agreement between them was observed.

Jan 1, 1999

By Chen Zhang

Polycrystalline Ti-rich NiTi thin films have been deposited from a single NiTi target using a DC magnetron sputtering system. Free standing film was obtained by using a single crystal silicon substrate. Thickness ofthe thin films is controlled at around 12 pm. In this investigation, the effect of deposition temperature on the microstructure and transformation temperatures of the thin films is studied. Influence of post heat treatment temperatures on the properties of the thin films is also investigated. Transformation temperatures of the thin films are determined by differential scanning calorimetry (DSC). The surface microstructure of the thin films is studied using a scanning electron microscope (SEM), and the crystallinity is determined using x-ray diffractometry. It is found that the thin film deposited on a hot substrate is crystalline even when the substrate temperature is as low as 300°C, while the normal crystallization temperature for an amorphous thin film is around 500°C. The microstructure of the film deposited on a hot substrate shows a very fine grain size. The grain size increases with increasing substrate temperature during deposition. The effect of post deposition heat treatment on grain size is minimal.

Jan 1, 1999

By Phillip B. Messersmith, Emmanuel P. Giannelis

"A versatile in-situ polymerization approach is described for the synthesis of polymerceramic nanocomposites consisting of two-dimensional layers of mica-type silicate (MTS) within polymer matrices. Functionalized, organically modified mica-type silicates (OMTS) were used to promote delamination/dispersion of the host layers and initiate polymerization of organic rrionomer. Epoxy nanocomposites prepared in this manner exhibit substantial modulus reinforcement at low silicate loadings. The water vapor permeability of the poly(?-caprolactone) nanocomposite containing 4.8% silicate by volume was reduced by nearly an order of magnitude compared to pure poly (?-caprolactone).IntroductionPolymer matrix nanocomposites are a relatively new class of materials with dimensions typically in the range of 1-100 nm.1 In general, because of the ultrafine phase dimensions involved, nanocomposites exhibit new and improved properties when compared to their micro- or macrocomposite counterparts. We as well as others are currently investigating the design, synthesis and characterization of polymer-ceramic nanocomposites. Our effort, in particular, has focused on the use of mica-type silicates (MTS) with various thermoplastic and thermosetting matrices.2-5MTS's belong to the general family of 2: 1 layered silicates. Their crystal structure consists of layers of two silica tetrahedral sheets fused to an edge-shared octahedral sheet of either aluminum or magnesium hydroxide. Stacking of the layers leads to a regular van der Waals gap or interlayer.6 Isomorphic substitution within the layers generates negative charges that are counterbalanced by cations residing in the interlayers. Although the natural forms of MTS's usually contain hydrated Na+ or K+ ions, ion exchange reactions with organic cations (e.g. alkylammonium ions) can render the normally hydrophilic MTS's organophilic."

Jan 1, 1994

By Vadim J. Jabotinski

Electron beam processing is potentially very attractive for the high temperature treatment of hazardous materials. The very high power efficiency of the electron beam energy source (80- 90% of the power from the electric power line is converted to useable energy) is one of the positive features of this technique. This paper will consider advanced electron beam concepts for solid, liquid, and gaseous waste treatment such as stabilization of radioactive solid and liquid hazardous streams. Fundamental aspects and applications including an analysis of the economic potential of electron beam processing of waste treatment will be presented.

Jan 1, 2000

By Suguru Kohno, Yoshihiro Momose, Masakazu Honma, Tokirou Kamosawa

Copper metal surfaces have been examined by an extremely sensitive surface analysis technique called temperature programmed photoelectron emission (TPPE). The surfaces were ultrasonically cleaned and subsequently abraded by a screw in organic solvents and water. The TPPE apparatus is composed of a Geiger counter with Q gas (He+ iso-C4H10). The curve of photoelectron emission (PE) intensity vs. wavelength from 300 to 170 nm, termed PE spectrum, was repeatedly measured at different temperatures in the temperature- increase process from 25 to 350°C. The number of emitted electrons in a PE spectrum (PE total count) increased, reached a maximum at-250°C, and decreased with increasing temperature. With the surfaces cleaned alone in the liquids the maximum PE total count decreased in the order C3H70H > (CH3) 2CHOH > C2HpH > CHPH > H2O. With the mechanically abraded surfaces in the liquids the maximum PE total count changed as a function of the abrasion period and the maximum tended to appear at higher temperature with increasing abrasion period; the maximum value at 10-min abrasion decreased in the order H2O > CHpH > C2HPH > (CH3) 2CHOH > n-C3HpH. It was suggested that the TPPE behavior can be related to the acid-base interaction between the alcohols and the abraded metal surfaces and the presence of a contaminant over layer on the surface. From the XPS analysis of the 01 s spectra it was suggested that the chemical change of the adsorbed oxygen to oxide oxygen with temperature plays a substantial role in the appearance of the maximum PE total count.

Jan 1, 2000

By H. Ipek

In this study the effects of interstitial ratios on k-feldspar samples were investigated. The k-feldspar samples were taken from Egypt using dry batch grinding conditions and a kinetic model. Three different mono size fractions (-3350+2360, -850+600 and -300+212 µm) were ground separately for 0.5, 1, 4, and 8 minutes and at four different interstitial ratios (125%, 100%, 75% and 50%) using a Bond mill with a mixture of five ball sizes. The mill used was at a size of 30.5 cm diameters, with 30.5 cm length, providing a total mill volume of 22272 cm3. The mill has a total mass consisting of 22648 g. steel ball mixtures of 38.10, 31.75, 25.40, 19.05 and 12.70mm diameters, occupying 22% of mill volume. The mill rotates at a speed of 70 rpm. The weights of the feed charges were 3000, 2000, 1000, and 500 g for 125%, 100%, 75% and 50% filling of the interstices of the balls respectively. The specific rate of breakage (Si) was determined from the top size fractions at different grinding times that were mentioned above and the model parameters were compared for the four different powder filling ratios (U). In many investigations, it has been found that an interstitial filling ratio of U = 0.6-1.1 is a good powder ball loading ratio to give an efficient breakage in a ball mill. In this study, it was found that U=1.25 is a good ratio for K-Feldspar.

Jan 1, 2006

By Pan Gu, Zhen Zhang, Jiang Diao, Bing Xie, Hongyi Li

Viscosities of FeO-SiO2-V2O3-CaO-P2O5 slags have been measured at the temperature range of 1673 K to 1773 K (1400°C to 1500°C). This investigated system represents the major components of basic vanadium slag that is an important intermediate product of a novel vanadium extracting process, in which removal of phosphorus and extraction of vanadium can be achieved from the vanadium-containing hot metal simultaneously. It was found that higher CaO/SiO2 ratio resulted in lower viscosity in the composition range of interest. Also, the viscosities increase with the increasing P2O5 concentration. The varying viscosities can be attributed to the modification in complexity and polymerization of the slag network. The variation of apparent activation energies are in tune with the viscosity measurements. The results of this work revealed the effect of CaO/SiO2 and P2O5 on the viscous properties of FeO-SiO2- V2O3-CaO-P2O5 slags and therefore provide the theoretical foundation for the control of the coupling de-P and V-extraction process.

Jan 1, 2016

By Naiyang Ma

"High oil concentration is one of the major barriers for recycling of mill scale of steel hot rolling mills. It is of vital importance to find cost-effective technologies of reducing oil concentration in mill scale in order to recycle the mill scale without causing detrimental effects on production and environment. This paper discusses in-process separation of mill scale from oil at steel hot rolling mills. Formation of mill scale and status of oily wastewater at hot rolling mills are reviewed in the first place. A mathematical model is then formulated to relate oil concentration in mill scale to physical properties of mill scale, chemical and physical properties of wastewater and interacting parameters between mill scale particles and wastewater. From this model, three approaches of in-process separation of mill scale from oil are derived: (1) avoiding contacts between mill scale particles and oily wastewater, and (2) maintaining low oil concentration in wastewater, and (3) collecting mill scale in upper streams of wastewater flows. In-process separation of mill scale from oil might have advantages of lower capital cost, lower operating cost and less additional environmental concerns, compared to other strategies of separating mill scale from oil.IntroductionHot rolling is an inevitable step in producing finished steel products. Figure 1 schematically shows a steel hot rolling process. Semi-finished steel products, slabs here, are reheated first, and then the reheated slabs are discharged from the furnaces and transported on hot rolling trains to descaling units for removing scale with pressurized water. After being descaled, the slabs are rolled by roughing mills. After treated with cropping and the second descaling, the slabs are finally rolled into finished products, coils here, by finishing mills."

Jan 1, 2012

By M. Misra, J. Nanor

The precipitation and removal of arsenic from process waters can be accomplished with addition of lanthanum chloride alone or in conjunction with ferric sulfate. The long term stability of these corresponding precipitated compounds is critical from the disposal stand-point. In this paper the characterization of ferric, lanthanum and lanthanum-ferric arsenate compounds formed at room temperature in acidic and alkaline pH is presented. The characterization techniques used included zeta potential, XRD and SEM. Zeta potential measurements of ferric and lanthanum hydroxides in the presence of arsenate indicate that oxyanions of arsenate are chemically adsorbed onto the positively charged surfaces of these hydroxides. In alkaline pH there is desorption of arsenate species from the ferric hydroxide surface, hence the product is thought to be unstable. On the contrary, lanthanum arsenate is stable in alkaline pH. XRD patterns show that the ferric arsenate formed in acidic and alkaline pH is amorphous, whereas lanthanum arsenate and lanthanum-ferric arsenate formed in acidic and alkaline pH are crystalline.

Jan 1, 1999

By Wei Yu, Tiejun Chun, Jian Pan, Deqing Zhu

In this paper, the technology of producing fluxed pellets by using hydrated lime as binder instead of bentonite was carried out. Green balls with 0.8% bentonite and others with 2% hydrated lime were obtained under the same conditions of 1.5% coke, 1.45 basicity and balling at 8.5% moisture for 13 min in disc pelletizer. The properties of two types green balls were as follows: drop numbers of 4.8 to 5.0 times/0.5m, compressive strength of 19.7 to 24.2 N/pellet and thermal shock temperature of 280 to 385?, respectively. Comparing with bentonite as binder, the compressive strength of fired pellets with hydrated lime is elevated by 13.8% and climbs up to 3113 N/pellet under the following conditions: preheating at 1050? for 10 min and firing at 1300? for 15 min. The hydrated lime also improves the metallurgical performance of fired pellets. The reduction index was enhanced from 68.6% to 70.6%, RDI+3.15 increased from 90.1% to 98.8% and reduction swelling index dropped from 22.4% to 7.4%, respectively. Therefore, hydrated lime can not only replace bentonite as binder to enhance the firing behaviors of green balls, but also effectively improve the metallurgical performance of fluxed pellets which can be used as high quality feed for blast furnace.

Jan 1, 2011

By Animesh Jha

Univariant diagrams are constructed for the reduction of nickel and cobalt oxide and sulphide minerals. The results from the carbothermic and hydrogen reduction of sulphide minerals are compared. The importance role of lime and calcium sulphate in controlling the emission of sulphurous- gases during reduction reaction is also explained. The mechanism of carbothermic reduction of nickel sulphide is explained by examining the sulphur exchange and reduction reactions. The phase equilibrium relationships that determine the formation of multicomponent liquid are characterised. Also the governing equilibria for inert atmosphere calcination- roasting of nickel and cobalt sulphide minerals are also described for the metallization of nickel and cobalt.

Jan 1, 1993

By Yeliz Demiraya, Onuralp Yucelb

"Production of strontium metal from its oxide was studied under the pressure of 1-5 mbar by methalothermic process. SrO with 99 % purity was used in the experiments. Effects of Al powder addition (100, 200, 300 % of stoichiometric ratio) and time were investigated on recovering of metallic strontium. Effects of BaO addition (100 %, 200 %, 300 %) was also investigated. The final residues were examined for their chemical composition. XRD, AAS and Flame Photometer were used for chemical analysis. More than 96 % of strontium metal recovery can be obtained.IntroductionStrontium is an element which is used in many advanced technology applications. Barium strontium titanat, strontium bismuth titanat, and strontium bismuth tantalat thin films are promising materials in ferroelectric and Schottky-based microelectronics technologies, especially for memory applications. Physical vapor deposition (PVD) techniques as magnetron sputtering, thermal evaporation and molecular beam epitaxy (MBE) are the most widely used methods for growth of these thin films [1-3]. In these techniques high-purity of Sr metal is used as evaporation sources and sputtering targets. Furthermore, metallic strontium is used as a ""getter"" in electron tubes, and as an alloying elements in aluminum alloys [4].The most used Sr compound is SrCO3 and widespread process used in production of SrCO3 is the hydrometallurgical carbonation of celestite. Although there are considerable amount of Selestite reserves, SrCO3 and strontinum metal are not being produced in Turkey, yet [5].Concentrated celestite (SrSO4) is conversed to SrCO3 in carbonate media. Black ash and direct conversion processes are currently used methods. There are many satisfactory studies about hydrometallurgical carbonation of celestite and decomposition of SrCO3 [6, 7]. Since strontium metal is produced from it’s oxide (SrO), SrCO3 needs to be decomposed to SrO."

Jan 1, 2011

By Nan Wang

Based on the commercial computational fluid dynamics software, Fluent, a three dimensional finite-volume model has been established, and the fluid flow and heat transfer in the super-wide slab mold (cross section 3250mm×150mm) of Nanjing Iron and Steel Company has been simulated. The basic feature of flow and temperature field in a super-wide mold has been analyzed, and the effects of mold width, the submergence depth of SEN, outlet angle of SEN, casting speed, superheat and cooling rate on the flow and temperature field have been investigated. The results by comparing several simulated calculations for 3250mm×150mm slab show that a more proper fluid flow and temperature field in the super-wide mold can be obtained with 15°outlet angle, 120~150mm submergence depth of SEN and 1.2~1.4m/min casting speed. The results through numerical simulation provide a theoretical basis for optimizing the configuration design of SEN and choosing reasonable processing parameters for the continuous casting mold of super-wide slab.

Jan 1, 2009

By Jayagopal Uchil, M. Krishna, Shanta Sastcy

"Damping behaviour of aluminite particulate reinforced ZA-27 alloy metal matrix composites processed by compocasting method is studied. The weight percentage of particulate reinforcement is 0,1,2,3, and 4%. A dynamic mechanical· analyzer is used ·to measure the damping capacity and dynamic modulus at the natural frequency of the specimen over a temperature range of 30°C to 300 °C both in the heating and cooling cycle. The damping capacity of the material is found to increase with increase in temperature and weight percentage of aluminite reinforcement although this is accompanied by a decrease in dyliamic modulus.The damping capacity and dynamic young's modulus exhibit a sharp decrease in their values around 300 °C a8 ZA-27 alloy undergoes a first order phase transition in this region which is confirmed by Differential scanning calorimetric studies. Several damping mechanisms have been evaluated theoretically for the material under study. The damping capacity at low temperatures is attributed primarily to coefficient of thermal expansion mismatch induced dislocations and high intrinsic damping of the matrix. At higher temperatures the damping capacity is attributed to ZA-27/aluminite interface, phase transformations and thermoelastic damping.IntroductionMetal matrix composites. (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and lightweight [1-5]. At present, the usage of ceramic particles as reinforcement in MMCs has attracted considerable interest from scientists and engineers. The MMCs show substantially improved elastic modulus, strength, stiffiless, and tribological properties with low coefficient of thermal expansion compared with the unreinforced matrix material."

Jan 1, 2000

By Y. Shigeno

The reactivity of a porous solid is a strong function of its pore structure (porosity, pore surface area and pore size distribution). It follows that reactivity could be altered by altering pore structure; one way to achieve this is by chemical vapor infiltration whereby a gaseous species is reacted in the porous solid to produce a solid. Experiments were carried out in which the pore structures of various carbons were modified by cracking methane within the pores; oxidation rates of the carbons were then measured for both infiltrated and original samples. For coke it was found that two indices of coke performance used in the steel industry (CRI and CSR) can be greatly improved following a small amount of infiltration. Infiltration/oxidation results are interpreted in terms of measured pore structure changes.

Jan 1, 1993

By Cyro Takano

An alternative use for recycling of waste from bag house of iron ore sinter plant was tested by producing and evaluating" at laboratory scale, the self reducing cold bonded pellets. This waste was characterized and the self-reducing pellets were produced using anthracite coal fines as reductant and Portland cement or hydrated lime/Blast Furnace slag as binder. It was used the molar ratio of Fe2O3/C (fix) equal to 3. Evolution of cold strength with curing time, for different contents of binder, was evaluated. Cold strength of 200N/pellet was obtained, for sinter dust, after 10 days of curing. Suitable hot strength was also presented and no decrepitation and swelling were observed. Good fractional reduction was obtained at 950°C and 1137°C. These results show that this material may be used by the Self-Reducing Processes for hot metal production, as an alternative route for this dust destination.

Jan 1, 1996

By Huanyu Zhang, Zhancheng Guo, Liqiang Fan, Huiqing Tang

"In this study, a simple process has been developed for zinc oxide recovery from RHF (rotary hearth furnace) secondary dust. The results have shown that a high dissolution efficiency of soluble zinc was achieved with water leach at ambient temperature with a liquid/solid ratio of 10/1 in 30min while 20% of the dust was left as solid residue. The rate of dissolution increased slowly after the dissolution efficiency reached 90%. The leaching process was found to be controlled by external diffusion. After separation, zinc was precipitated in leached liquor by introducing a precipitation agent of potassium hydroxide. The resulting solid was purified and dried at 393K. Zinc powder in the form of ZnO with purity of 98.5 mass% was obtained with an average size of 12.4µm.IntroductionThe RHF (rotary hearth furnace) direct reduction process is widely used in many iron and steel enterprises to deal with various metallurgical dusts [l]. The basic principle of this process is that first various metallurgical dusts (BF dust, EAF dust and so on) are pelletized with a coal reductant, and they are then subjected to a fast reduction using RHF after being dried. Highly metallic pellets are produced and at the same time, nonferrous elements such as Zn, Pb, K and Na are evaporated into the RHF flu gas as secondary dust. Zinc is listed by the Enviromnental Protection Agency as one of the 129 priority pollutants. Therefore, recovering zinc from the industrial wastes is important in terms of enviromnental protection [2-3]. On the other hand, nowadays China is in shortage of zinc resource and the annual output from metal recycle only accounts for some 13% of the total zinc resource. There are many ways proposed to recover zinc from various wastes [ 4-7]. The aim of this paper is to recover zinc oxide from RHF secondary dust by a method with water leach followed by caustic precipitation. This work investigated the influence of the leaching temperature and leaching liquid/solid ratio on the zinc recovery efficiency. The process consisted of three stages: (1) leaching with water; (2) liquor/residue separation; and (3) zinc precipitation in caustic milieu."

Jan 1, 2014

By Edgar E. Vidal, Keith Smith, James A. Yurko

Beryllium, like many other reactive metals, is extracted from a halide (generally BeF2) using magnesiothermic reduction, also known as the Kroll process. The beryllium is produced in a molten state, which when solidified resemble "pebbles". Although beryllium is used in limited quantities compared to other metals (< 100 Mt/annual), it is a critical material for the nuclear, defense/aerospace, and large science markets because of its unique nuclear and mechanical properties. Beryllium processing has unique environmental, health, and safety concerns which must be handled appropriately in the 21st century from a worker and environmental safety perspective, and must be designed with this first in mind. In 2011, Materion began operations of its new Kroll plant – informally known as the “Pebbles Plant” - in Elmore, Ohio. The plant was majority funded by a U.S. Department of Defense Production Act (DPA) Title III grant, which is a unique government/industry partnership program to, "create assured, affordable, and commercially viable production capabilities and capacities for items essential for national defense." After a twelve year hiatus from primary beryllium production, Materion has reentered its extraction business and has relearned how to make pebbles. The purpose of this presentation is to give an overview on beryllium extraction and discuss some of the unique aspects of building and operating a safe beryllium facility during the production scale-up phase.

Jan 1, 2015