Search Documents

By Takeshi Azakami

By combining the iron reduction process with the usual rotary kiln process, the direct production of metallic zinc from EAF dust is proposed. After thermodynamic estimation and desk-top experiments it is confirmed that the process is hopeful under suitable conditions. In order to get some practical test data the enlargement of the process scale was planned and the bench scale tests were carried on successfully. In these experiments a zinc ingot of PW grade was produced from EAF dust.

Jan 1, 2003

By Mingchun Lu, Zhijia Liu, Xueqi Zhang, Jianliang Zhang

"In order to solve the problem of shortage of scrap, especially high quality scrap, a new substitute for scrap or DRI has been developed. The decarbonization mechanism of granular pig iron has been analyzed and the technical process and decarbonized granular pig iron have been evaluated in this paper. The research result shows that this new process is superior to direct reduction process in product quality, construction investment, operation flexibility, production efficiency etc. Decarbonized granular pig iron (DGPI) not only can be used as conventional scrap but also can be charged into EAF as high purity .burden equivalent to heavy scrap:IntroductionIn the past years, with the universal application of continuos casting technique in China, the amount of scrap generated inside steelworks has been reducing continually. On the other hand, the EAF steel proportion is increasing and this gives to the obvious change in structure of steel product. At present, the requirement on both scrap quantity and scrap quality is being paid more and more attention. Because China is a country which is devoid of scrap and poor in resource (nature gas and high grade iron ore) for developing direct reduction iron (DRI) so that sponge iron can not be produced cosmically in China and has to be mainly imported. Instead of part of scrap, some cold pig iron in cold state has been charged into EAF in China. However the high carbon content in pig iron has limited its proportion in EAF metal burden. Because the price of pig iron is lower than that of imported DRI in China, the technique of granular pig iron decarboniztion is hopeful to become effective way to produce substitute for scrap or DRI."

Jan 1, 2000

By Viktor. P. Popov, Oleksandr. V. Derev'yanko, Oleksandr. I. Raychenko

"This paper is devoted to scrutiny problem of obtaining electro-contacts by electro-discharge sintering technology. A new unconventional method of electro contacts production (on Aggraphite base) can yield essential optimization resource.Review of three electro-technological methods of processing contacts materials is presented:- using graphite powder cladded by Ag;- mixture of graphite powder(which is a non-cladded powder) with Ag powder and addition of Fe powder particles;- method of infiltration of melted Ag into graphite piece without deformation and rupture of object.This technological approach can give the possibility to increase of compression strength of electro-contacts materials up to 340 MPa and more under conditions of additional reinforcing components (for example, by Fe).IntroductionThe electric current can be an active ""participator"" of the powder metallurgy technology [l]. At the passage of electric current through powders or some powder mixtures the phenomena including phase transformations arise. Here such effects, which are observed in the Ag-graphite and Ag-Fe-graphite powder mixtures and in the pair Ag-porous graphite, are described.The Ag-graphite composition materials (CM) are used, for example, as electric contacts [2, 3]. Since a material being produced is destined for the contacts it is necessary to take into account the following aspects: commutating current, its character and voltage, active or reactive character of working load, geometrical dimensions of contacts, quantity and frequency of switching on and switching off, pressure on contacts, distance between contacts, method of arc control, surrounding medium, its content, pressure and temperature. Thus, these and, maybe, choice of some other circumstances influence design, materials and production technology of contacts. The range of problems concerned dictates such steps as alloying of contact materials, optimization of structure, selection of kind of graphite, its connection with metal [4-10]. It is expedient to recall the main procedures of the first stage of the conventional technology: dosage of the initial graphite powder and binder-phenolic resin plastic varnish (for example, Bakelite), mixing, densification, thermal treatment, crushing, grinding, sieving, drying, dosage of grained graphite, dosage of the initial silver powder, obtaining of the silver salt solution, settling of salt, filtration, washing, drying of the cladded graphite powder, thermal treatment, obtaining of the graphite powder of particles cladded by silver. The second stage of the convectional technology starts by obtaining of the cladded graphite powder and finishes by annealing of the pressed blanks (Fig. 1)."

Jan 1, 2004

By Alex Probst

With low metal prices and increasing value placed on plant water and tailings disposal areas, it is becoming essential to maximize the efficiency of solid-liquid separation processes. Since its inception over 25 years ago, the use of flocculants has grown exponentially. While flocculants play a crucial role in the sedimentation process, they are also a major operating cost. Recent innovations are revolutionizing the industry once again. New thickener designs are doubling thickener-loading rates while reducing flocculant consumption. The feedwell, as the heart of the thickener, is undergoing many significant metamorphoses. With CFD and other advanced computational analysis, feedwell technology is being examined more thoroughly than ever before, The result is that the thickener previously thought of, as a "Black Box" is now being mapped and controlled with state-of-the-art technology. This paper will examine recent design improvements in all aspects of thickeners in order to project the look of the thickener of tomorrow.

Jan 1, 1999

By Kimio Itagaki

Thermodynamics and rate process fundamentals are two of the important principles involved in nonferrous production processes. The process configuration establishes whether thermodynamics or rate process behavior is most relevant in a particular application. In this paper, thermodynamic theory and rate process fundamentals are used to analyze the main characteristics of smelting and converting processes. The effect of increased oxygen potential .is examined with emphasis in view of the increased use of highly oxygen-enriched gas in modem smelting processes. Phase equilibrium and the distribution of minor elements between copper or nickel matte and FeOx-SO2- or FeOx-CaO-based slag are reviewed. The use of oxygen-rich gas has no serious effects on 'the recovery of valuable copper and silver in the matte phase, while the recovery of nickel and cobalt is adversely affected. The oxygen content in the gas also strongly affects the distribution behavior of arsenic, antimony and bismuth. Analysis of the rate processes occurring in the shaft of flash smelting, and converting furnaces by a 3-D computational fluid-dynamics model is also discussed. After being validated with experimental data collected in a large laboratory furnace, the computer model has been used to simulate the main features of an industrial flash converting operation. The results present quantitative features of the improved mixing of the particle-gas suspension and increased oxygen efficiency obtained with a distributor-cone burner compared with those with a single axial entry burner. The role of basic principles in the engineering analysis of high-intensity matte smelting processes is also discussed.

Jan 1, 2002

By Zviad Kovziridze

Structure of celsian ceramics in BaO-Al2O3-SiO2system is studied with electron microscope in the entire temperature region of baking interval. The process of the pores filling and the full consolidation of material growth at comparatively high temperatures of baking intervals are described.

Jan 1, 2006

By James D. O, DeLa&apos

Multicomponent materials are common in nearly all areas of materials science and technology, yet the use of phase diagrams to represent these complex systems is hampered by the requirement of three or more dimensions for explicit graphical representation. In the present work, the "solid-modeling" capabilities of a computer aided design (CAD) system have been applied to the representation of three-dimensional phase diagrams. Relevant phase diagrams for a hypothetical quaternary eutectic system were constructed and used to demonstrate the capabilities of the technique. These capabilities lead to relative ease of phase diagram construction and improved access to qualitative and quantitative information. Results of this work are contrasted and compared to previous efforts toward computer ,representation of phase diagrams. It is concluded that solid-modeling of three-dimensional phase diagrams can be used to advantage in both education and research.

Jan 1, 1991

By Sharon L. Eyer

"FTIR spectroscopy is employed to define mineable ore deposits based on exploration samples. The RAMBO (Robotic Assessment of Mineable Bauxite Ore) technology is operating successfully at an alumina refinery in K winana, Australia, for assessment of a number of critical ore attributes including available alumina, extractable organic carbon and total iron. Classical methods of analyses for these properties require laboratory-scale digestion of alumina ore (bauxite) or XRF analyses.Multivariate calibration is used in the RAMBO system to generate robust mathematical models that are able to estimate classical data from FTIR spectral data. Furthermore the models can highlight regions of ore that are relatively unusual. Unusual ore may be investigated for potential impacts on refinery processes well in advance of mining.The components of the technology are described and some results for an example application (bauxite) are presented. Challenges and difficulties are discussed. The potential to apply the technique to process control is introduced."

Jan 1, 1999

By Carlos Maurício. F. Vieira, Lázaro A. Rohen, Sérgio N. Monteiro, Rafael G. de Castro, Gustavo X. Borges, Maycon A. Gomes, Frederico M. Margem, Anna C. C. Neves

Economic and environmental benefits are motivating studies on natural fibers, especially lignocellulosic extracted from plants, have been studied to substitute synthetic fibers, such as glass fiber as reinforcement in polymer matrices. By contrast to synthetic fibers, natural fibers have the disadvantage of being heterogeneous in their dimensions specially the diameter. About the hemp fiber, little is known of their dimensional characteristics. The aim of the present work was to statistically characterize the distribution of the diameter of hemp fibers. Based on this characterization, diameter intervals were set and the dependence of the tensile strength of theses fibers with a corresponding diameter was analyzed by the Weibull method. The diameter was measured with precision using a profile projector. Tensile tests were conducted on each fiber obtain mechanical strength. The results interpreted by Weibull statistical showed a correlation between the resistances of the fiber to its diameter.

Jan 1, 2015

By Ma Ying

The continuous directional solidification technique of five kinds of special ZA alloys with eutectic, peritectic and eutectoid transformation under the condition of continuous casting by heated mold was studied. The mechanism of surface defects appearing in ZA alloy line was discussed and the structure of some defects were analyzed by SEM. The results show that only when the fitting of various technique factors, pressure head, outlet temperature, pulling speed and cooling condition are reasonable under a certain range, can the ZA alloy smooth line be continuously pulled out. Unreasonable techniques will result in hot tear, rough surface, mush outlet, leaking and other defects. The shape and location of solid-liquid zone have an important influence on the formation of the above defects. When the solid-liquid zone is located in the mould outlet or inner mould, the surface of solidification will protrude into the inner mould. If the remaining liquid cannot counteract the solidification contraction, a rough surface will appear. If the solidification surface further into the mould, the ingot in the mould will have a great friction force when pulling and will form a hot tear. When the solid-liquid zone is moved out of mould, the solidification surface will turn into a plane, which easily results in leaking. A vibration or unstable operation will cause an ingot winding during pulling

Jan 1, 2003

By Donna Post Guillen

"Cyclopentane, a flammable hydrocarbon, is being considered as a working fluid for waste heat recovery applications using Organic Rankine Cycles with Direct Evaporators. A postulated failure mode consisting of a pinhole leak in a heat exchanger tube raises safety concerns due to autoignition of the working fluid. Experiments were conducted to determine the ignition delay time (IDT) of cyclopentane using an Ignition Quality Test™ (IQT™) device. Two sets of experiments were conducted per ASTM D6890 (with exception to charge pressure and temperature) to determine ignition delay of the fuel at atmospheric pressure for standard air (-20.95% oxygen) and vitiated air (13.3% oxygen) at a temperature of 803 K. Operation of the IQT device at a much lower pressure (1 bar) than normal operation (21.4 bar) with a standard injector led to very rich conditions and wetting of the stainless steel chamber walls. Catalytic effects are postulated to produce the small IDTs observed. Experiments were repeated with a modified injector to prevent wall wetting, resulting in average IDTs that are substantially longer.IntroductionCyclopentane is being considered for use as a working fluid in a Direct Evaporator of an Organic Rankine Cycle (ORC). In this configuration, the heat exchanger is placed directly in the flow of the hot exhaust gas, rather than using a secondary heat transfer loop to isolate the flammable working fluid from the heat source. This configuration offers the advantages of approximately 15% lower cost and improved efficiency over a standard ORC. However, placing a heat exchanger operating with a flammable hydrocarbon in the hot exhaust gas stream presents potential safety risks. If a pinhole leak were to occur in the heat exchanger, working fluid could leak into the hot exhaust stream. Gas turbine exhaust is provided to the Direct Evaporator at a temperature of approximately 803 K, whereas the autoignition temperature of cyclopentane is 634 K (Gallant and Yaws, 1993). Autoignition of the working fluid has been identified as the key risk for this type of system.Autoignition occurs when sufficient self-heating by chemical reactions takes place to accelerate reaction rates to produce full-scale combustion. This is in contrast to forced ignition, in which an external source (e.g., spark) is employed to initiate the combustion process. For combustion to occur, the fuel to oxidizer concentration must be between the lower (lean) and upper (rich) flammable limits. The reaction rate depends on the species concentration of the fuel and oxidant, the local temperature and pressure. Ignition processes are comprised of steps that take a fmite amount of time. This latent period prior to the start of combustion is referred to as ignition delay time (IDT)."

Jan 1, 2012

By Tangstadm Merete, Eli Ringdalen

"This paper presents an overview of results from The Norwegian Research Institution SINTEF and the Norwegian University of Science and Technology, NTNU regarding new and ongoing research in silicon production. The main studies are related to condensation of SiO gas and cavity formation. If SiO gas condensation is increased at the top of the furnace resulting in SiO content in the off-gas closer to equilibrium, the Si yield will be increased significantly. Experimental work, simulating a cavity under industrial conditions, has shown that the cavity grows downwards from one layer. Physical appearance of zones in industrial furnaces, and selected reactions in these, are discussed based on results from excavation of industrial furnaces and results from laboratory experiments. Experimental studies of reaction rates for the formation of SiO are presented. Quartz properties are demonstrated to vary between differing quartz types and the effect of this is discussed.Introduction Both the theoretical and industrial issues associated with the production of silicon are described in detail in the textbook written by Schei et al [1]. This book covers the knowledge of silicon production process up to 1998. Together with the work by Myrhaug [1] and by Aasly[2], this is the main basis for this paper. Recent and ongoing research at SINTEF and NTNU focusing on production of Si and SiO in the high temperature zone, dissociation of SiO and condensate and cavity formation will be discussed."

Jan 1, 2012

By J. Shibata

The recovery process of valuable metals, such as Ll, Mn, Ni and Cr from a waste lithium battery was developed n this study. Lithium and Mn are selectively leached from the battery by using dilute mineral acid. Main part of the battery comprises stainless steel, and Fe, Ni and Cr are easily leached by the mixture of dilute HCl and HNO3 Lithium and Mn are precipitated as metal carbonates from the? individual leached solution with sodium carbonate solution. The solution containing Fe,Ni and Cr Is treated by solvent extraction to separate NI and Cr from the leached solution. The experiments are carried out for leaching and separation steps. According to the experimental results, the flow. sheet for a recovery process of valuable metals from a waste lithium battery has been established.

Jan 1, 1995

By P. M. Swash

This paper reviews the application of some mineralogical techniques in the evaluation of the Uitkomst Ni-Cu deposit, South Africa. The low grade of the ore necessitates detailed and representative characterisation in order to establish the prospects viability. The relevant mineralogical information is generated by using optical microscopy, magnetic and heavy liquid . separations, XRD. SEM and EMPA. Methods used are briefly reviewed. The cost savings and metallurgical understanding that is provided by the mineralogical work is described especially with regard to milling, flotation and the presence of by-products (PGMs and chromite).

Jan 1, 1991

By Xiao Long, Ting Wu, Lilong Zhu, Qian Wang, Shengping He

"During the continuous casting of peritectic steel slabs, mould fluxes with high crystallization capacity are usually chosen for improving slab surface quality. However, the lubrication condition of casting shell also could be deteriorated. Since precipitation of crystals within liquid slag film can change the composition and property of liquid slag over solid-liquid slag film interface region, its impacts on continuous casting process also are not clear. In order to clear this phenomenon, an experiment method was put forward, and mould fluxes for peritectic steel slabs continuous casting were selected and examined. The results reveal that after crystals have been separated, the crystallization capacity of leftover liquid slag increased with different levels, which could deteriorate the lubrication condition of casting shell and cause a series of problems. Thereby, mould fluxes with high crystallization capacity at beginning for heat transfer control and then weaker after crystallization should be considered in the future.IntroductionIn the continuous casting of peritectic steel slabs, contradiction between heat transfer control and slab shell lubrication by mould fluxes has been treated as a key problem for maintaining a smooth manufacturing process [ 1]. Strong and uneven horizontal heat flux over the meniscus region will cause uneven solidification of casting shell, especially for peritectic steel slab with enormous volume change caused by phase transition. All of those could cause surface defects like longitudinal crack [2-4]."

Jan 1, 2013

By F. Shen

Qualitative and quantitative results obtained during the physical modeling of the molten aluminum flow in a tundish using an aqueous system are presented. Surface tuft, free-surface powder and laser sheet visualization techniques were utilized for qualitative studies, whereas laser Doppler velocimetry was used to elucidate the 3-D flow regimes quantitatively. The results of the study are used for validation of the CFD codes, and to explore the effect of the alterations below the nozzle in order to: (1) decrease turbulence levels, and (2) collect the inclusions. Near the nozzle, the interaction of the impinging jet and the inclined walls gives rise to vortex structures. Downstream of the nozzle, two counter-rotating secondary cells diminish in strength. As flow turns through the bend, a separation region is created. The flow heading into the closed duct is seen to be nonsymmetric. A video tape highlighting the major findings is presented.

Jan 1, 1993

By J. Dille

Metallic cobalt exist in two allotropic forms : the hexagonal compact a which is stable at low temperature ( ( 420') and the cubic form 0 stable at higher temperature. This latest form is the only one which is ductile. During the electrode position of Co, in moderate acidic conditions, we noticed a code position of both a and B forms. The influence of several parameters on the B/a ratio in the deposit was investigated. High acidity and the presence of Fe increased its ratio; on the opposite, high temperature promote the a phase. No significant influence on the material were noticed. The differentiation of a and B forms of Co is rather difficult and the method of J. Scoyer was improved quite successfully.

Jan 1, 1988

By Larry F. McHugh

Current sulfide ore processing methods involving mechanical sizing of ores, froth flotation, electro-winning, solvent extraction, smelting and roasting are quite effective but typically represent a significant energy and environmental cost. This paper is the subject of a recent patent application and development program involving major improvements in sulfide ore processing. This two-step ?looping oxidation? process effectively removes sulfur while producing materials of adequate purity in an energy proficient and environmentally friendly manner. The first step results in a metal sub-oxide and a highly concentrated sulfur oxide off-gas stream. This gas stream can be processed for recovery in a more effective manner regarding both energy and capital equipment costs. In the second step, this metal sub-oxide is further oxidized to efficiently generate energy that can be recovered and utilized without the typical complications of an ?acid gas? stream process. Additionally, a portion of the final fully oxidized product can be looped back to the first step as the oxidizing agent. This process will be described in detail and compared to existing technologies in the area of energy efficiency, and off-gas environment treatment energy requirements.

Jan 1, 2008

By Yong Hack Lee

Nonferrous smelting processes have been through a rapid transformation since the beginning of 1980. The copper smelting technology has changed from the conventional Blast Furnace process to the Flash Smelting and MIB process. In the field of lead smelting, the technology has changed from the Blast Furnace Smelting to the Direct Smelting such as QSL and KIVCET. In 1992, Onsan Refinery successfully commissioned Direct Smelting QSL technology for lead. The QSL could produce more than 160,000 ton per year of lead bullion from lead concentrate and various residues. Moreover, since the year 2000, the TSL (Top Submerged Lance) Technology utilizing the same Direct Smelting process has been successfully commissioned to treat lead concentrate as well as lead sulfate residue produced from a hydrometallurgical zinc plant. This paper presents and compares the energy flows of lead smelting processes such as a conventional process and the Direct Smelting Processes plotted on the Pb-O-S phase diagram. The oxygen potential diagram suggests how to control the oxygen potential in the furnace. Also, it describes the recent operational experience in the TSL plant of Onsan Refinery with necessary mass balance of key elements.

Jan 1, 2003

By B. Sereda

As it is known the creation and development of new titanic alloys has been problematic up to now. They can be used in aircraft and vehicle construction, shipbuilding and as materials for keeping static loadings in high-temperature environments. In this work the synthesis of various titan aluminides is investigated. Mathematical model of structurization process was done. On the base of retrieved model the mechanisms of structurization in systems Ti + Al and Ti + 3Al was determined. Experimental researches were done at two different modes: burning and thermal spontaneous ignition. The method of retrieving compacted products combusted in SHS conditions (SHS-compacting) was used to gain these intermetallic compounds. The physical and thermal characteristics of technological process and their influence on structurization, homogeneity of structure and porosity of titan aluminides have been simulated and researched. It is established that the SHS-compactizing technology is fully capable of supervising the process of structurizations with the whole complex of advantages and can be applied for receiving qualitative titan aluminides with the set of chemical-physical properties.

Jan 1, 2010