By Sijun Li, Bingyu Zhang, Haitao Zhou, Zhendong Zhang, Guofei Si, Xianghua Liu

"Hot compression test of Nb microalloyed coiled tubing steel is performed on Gleeble3500 at 1123K—1373K and strain rate from 0.001 to 5s-1. It is found that flow softening occurs and the flow curves exhibit a peak with a characteristic of dynamic recrystallization (DRX) and change with temperature and strain rate significantly. The peak stress and peak strain are dependent on the Zener-Hollomon relationship with activation energy of 390 KJ/mol. On the basis of Avrami equation and the Zener-Hollomon parameter, it is obtained that the dynamic recrystallization kinetics equation with which the calculated and measured recrystallization fraction is very close. On the results of hot compression test, the Nb microalloyed coiled tubing steel is rolled by Thermo-Mechanical-Control-Processing (TMCP), and it is obtained that the yield strength and tensile strength of Nb microalloyed coiled tubing steel are 565MPa and 685MPa respectively, and the elongation percentage is 30.1%.IntroductionCoiled tubing is widely used in oil field for well logging, well completion, drilling, work over and other operation in various fields to solve a number of conventional operating techniques problem which are difficult resolved, and it plays a more and more important part in exploration and production at oil field. [1] It will improve the efficiency of exploration and exploitation, studying, developing and using coiled tubing technology. Therefore, the development of domestic coiled tubing materials and manufacturing technology are great significance. It is well known that Coiled tubing has relatively poor working conditions and complex force state. So, the coiled tubing needs satisfier a kind of high strength, high plasticity, and corrosion resistant under complex oil gas condition. As the coiled tubing technology developed, the level of the coiled tubing steel is from CT55 originally to CT90 and CT100, and the corresponding tensile strength is 483MPa-758MPa. [2, 3]"

Jan 1, 2012

By C. Carreno, A. D. Gonzalez Escarcega, M. A. Neri, A. Martinez –Villafane, O. Cobarrubias-Alvarado

"Waspaloy is a superalloy used to manufacture some aeronautical parts subjected to high temperatures and stresses. During thermo-mechanical processing cracks are generated, causing some parts to be rejected. In order to determine the causes of these cracks, this alloy was characterized using techniques such as chemical analysis, optical microscopy, scanning electron microscopy, and EDX analysis. Heterogeneous grain sizes in the microstructure cause a non-uniform strain distribution in these parts, creating cracks in zones with different grain sizes.IntroductionNickel-base superalloys are important materials for high-temperature service applications. The manufacture of components from these materials is typically based on solidification or powder-metallurgy processes [1]. Solidification techniques comprise either the direct casting of parts or the casting of ingots which subsequently undergo a series of thermo-mechanical-processing steps to refine the microstructure. During solidification, microsegregation is usually unavoidable. The primary solidification product is a disordered nickel solid solution with an fee crystal structure (?). In many alloys, the material which solidifies last is a mixture of ã and an ordered fee phase (? '). In prototypical nickel-base superalloys, the ?'-phase is Ni3(Al,Ti) [2-3].Waspaloy is a superalloy that is used in demanding high-temperature environments in which good creep and fatigue resistance are required. One of the most common applications of Waspaloy is for turbine engine rings. To ensure the required mechanical properties, the rings are usually forged and heat treated (Figure 1). Two distinct types of microstructures are usually found to be attractive for such applications: a) A microstructure with a grain size of ASTM 10 to 14 for tensile strength, ductility, and resistance to crack nucleation in low-cycle fatigue; or b) A microstructure with a grain size of ASTM 4 to 8 required for creep strength and resistance to crack propagation [4]. Because it is impossible to refine the grain size through heat treatment, a skillfully designed forging process is crucial for the control of the grain size and, hence the properties of the forged ring [5-6]."

Jan 1, 2012

By Xi-Shan Li, Qian Li, Yong-bin Yang, Li-na Cui, Tao Jiang, Jie Ge

"With regard to control environment pollution in the roasting pretreatment of sulfur & arsenic-bearing gold concentrate, roasting of double-layered pellet was proposed. In the paper, the characteristics of double-layered pellet roasting were studied. Removal and solidification rates of sulfur and arsenic were investigated as primary factors. The result indicated that the removal and solidification rates of arsenic reached up to 95.91 % and 98.95% while the sulfur was 97.19% and 97.90% respectively on the premise of adopting slaked lime as solidified agent at temperature of 6000, the package proportion of 2.14 and roasting time of 3h. However, pyrite and arsenopyrite were transformed to hematite and magnetite and product of solidification mainly consisted of calcium sulfate, calcium arsenate and calcium sulfite within optimum roasting parameters.IntroductionUtilization of refractory gold resources has been gradually concentrated on with the depletion of the gold resources which are easy to deal with in the world [1]. Sulfur and arsenic-bearing gold ore is a typical refractory gold one, in which ultrafme gold is encapsulated in the structure of metal sulfide minerals [2,3], so it gives poor recovery through direct cyanide leaching. These refractory ores need pretreatment before the process of cyanide leaching to undermine lattice structure of pyrite and arsenopyrite containing gold [4] so that the gold could touch with cyanide solution [5]. Among various methods of pretreatment, conventional roasting method is most effective, but this process generates gases such as S02 and As203 harmful to environment. Therefore solidification roasting was proposed to solve this problem occurring in the conventional roasting at the end of last century."

Jan 1, 2013

By Ulrich E. Klotz, Gemot Pottlacher, Shahid Mehmood

"Platinum alloys are frequently used in technical applications and in jewellery. Their thermophysical properties such as density, heat capacity, thermal conductivity and surface tension play an important role in casting processes and are required as input data for casting simulation. Scope of this work was to investigate these properties by different methods. Platinum and four alloys namely, Pt96Cu4, Pt68Cu32, Pt50Cu50 and Pt25Cu75 were investigated. Melting range and thermal expansion was measured at fem by DSC and dilatometry, respectively.At TU Graz wire shaped samples were investigated by an ohmic pulse heating technique. This technique allows the calculation of specific heat capacity and the temperature dependencies of electrical resistivity, enthalpy, and density of these alloys in the solid and liquid phase. Experimental results were compared with available literature and data from thermodynamic calculation using the SNOBl database and ThermoCalc.IntroductionPlatinum is a precious element and its alloys are commonly used in jewellery. But Platinum is much more difficult to cast then other jewellery elements like silver or gold, because of its high melting temperature, large shrinkage during freezing, low thermal conductivity, high surface tension, and high viscosity. As a result there arise problems during casting. Hence to resolve these difficulties a detailed study of thermophysical properties of solid and liquid platinum and its alloys is necessary for simulation and casting. The Platinum alloy samples were prepared by vacuum induction melting and casting into copper molds. Rods of 3 mm in diameter and a length of 80 mm were prepared and drawn to wires of 0.5 mm in diameter."

Jan 1, 2011

By Nozomu Uchida, Uematsu Keizo, Daisuke Shouji

"Grain orientated microstructure was developed for the improvement of ceramic characteristics. Novel polarized light microscopy was developed to examine the grain orientation quantitatively. The degree of grain orientation was estimated from the retardation determined with a Berek compensator. The method was essential to determine a minor grain orientation, which could not be analyzed by means of conventional X-ray measurements. The data were favorably related to ceramics characteristics. The comparis of the ceramics with various degree of orientation was very important to explain the change of ceramic characteristics with processing.IntroductionMicrostructure with grain orientation has a high potential for greatly improving characteristics of ceramic. However, there has been strong restriction on processing and material for developing this structure. It has been crucial to apply forming methods involving high shear such as injection molding1). Grains must have an elongated shape.In recent years, much attention has been paid on the effect of high magnetic field on diamagnetic materials2)3)4), Many ceramic materials are known to be diamagnetic. High magnetic field has a high potential to orient grains. The principal driving force for grain orientation is the magnetic anisotropy of material, which is generated by non-cubic crystal symmetr5). This method of grain orientation is not restricted by grain shape, and can be applied to all materials having non-cubic crystal structure.This study uses alumina as raw materials, and produces alumina ceramics with orientated grain in high magnetic field (10T). Alumina has a magnetic anisotropy due to hexagonal crystal structure. The degree of grain orientation in the green and sintered bodies will be examined and their relevance to magnetic field will be discussed."

Jan 1, 2000

By Yanxia Lu

Porous silicon carbide (SiC) has been the top selection for diesel particular filters (DPFs) since 2000 because of its high thermal diffusivity and strong body, which help it to survive in the harsh environment of a diesel exhaust system. However, the process to produce SiC DPFs is a costly one. The work presented herein describes more cost effective composite materials for this application, namely Si-SiC and Si₃N₄-SiC. Both composites have shown excellent filtration efficiency, low back pressure and outstanding survivability of regeneration at high soot loadings. Since the composites are batched from silicon metal, they can be prepared by a low temperature process that is impossible in the production of pure SiC PDFs. In fact, fabrication of SiC composites simply involves reactions between nitrogen gas and silicon metal, or silicon metal bonded with SiC, and as such uses a much less costly process when compared to the one employed to make SiC. In addition, the pore structure of the composites can easily be tuned by selecting raw materials and changing the ratio of two components. A typical pore structure consists of well connected pores with a median pore size of 5-20 µm and a porosity of 40-55%. This talk will describe the exothermic behavior as well as the mechanical and thermal properties of SiC composites in comparison to those of SiC filters. It will also show the superior thermal shock resistance of Si₃N₄ bonded SiC which is due to the unique combination of these phases that lowers the thermal expansion and elastic modulus relative to pure SiC.

Jan 1, 2006

By Baicheng Liu, Houfa Shen, Wensheng Li

"In order to understand the formation of macrosegregation in steel ingots, a mixture model has been developed which accounts for coupled mass, momentum, species, and energy transport to describe the sedimentation of free equiaxed grains during solidification. In this model, the mushy zone is divided into the slurry and porous regimes according to a solid packing fraction. Settling velocity of equiaxed grains in the slurry regime is given by an explicit expression. The solidification of a binary steel ingot (Fe-0.36wt.%C) with a two-dimensional geometry is numerically simulated. It is demonstrated that the predicted macrosegregation patterns agree to some extent with classical experimental results. Further refinement of this model is still necessary for realistically simulating steel ingot solidification.IntroductionModeling macrosegregation in steel ingots is still a challenging study, mainly due to the length scale of the products and the complexity of global multiphase transport phenomena coupled with microscopic solidification kinetics [l]. The thermal-solutal convection and the motion of equiaxed grains are the two main mechanisms responsible for macrosegregation. But there are few models that deal with the motion of equiaxed grains, which is confirmed as the main phenomenon that explains the negative macrosegregation along the centerline of large steel ingots [2]. A model which takes into account melt convection and grain sedimentation was first proposed by Beckermann and co-workers ([3], and references therein). More recently, similar multiphase solidification models with advanced nature have been presented by Wu and Ludwig [1,4] and Combeau and co-workers [5,6]. It is known that the application of these sophisticated models to steel ingot casting is at its beginning.In this paper, a solidification model based on continuum mixture approach, using much less sophisticated relations to obtain the settling velocity of free equiaxed grains, has been proposed in order to predict the macrosegregation in steel ingots. The model is applied to simulate the solidification of a binary steel ingot with a two-dimensional geometry, and preliminary modeling results are presented."

Jan 1, 2011

By Ragnhild Aune

In fire refining of copper, the affinities of various impurity elements on dissolved oxygen is of great significance. Further, in the design of oxygen probes in liquid copper, the influence of solute interactions on the activity of oxygen need to be considered in order to evaluate the oxygen concentration in molten copper. The present paper presents a series of measurements of the activities of oxygen in liquid Cu-M-o alloys (where M stands for Mn, Zn, As, Se or Te) carried out by the present group employing the solid electrolyte galvanic cell technique. Extreme care was taken to control the oxygen potentials in the inert gas atmosphere, and to keep the oxygen levels very low in the molten metal. The oxygen content was determined by analysis of the samples taken out from the melt. The results obtained showed that Mn has a strong negative influence on the activity coefficient of oxygen in liquid copper. A similar, but less prominent effect was observed in the case of Zn. Arsenic had no influence on the activity of oxygen in Cu (liq.). Se and Te had slight negative effect on oxygen activities in copper at XO > 10-5, while at lower oxygen levels the interaction coefficients were found to be positive. The results obtained were compared with empirical models for the calculation of interaction coefficients available in literature.

Jan 1, 2003

By Ragnhild Aune

In fire refining of copper, the affinities of various impurity elements on dissolved oxygen is of great significance. Further, in the design of oxygen probes in liquid copper, the influence of solute interactions on the activity of oxygen need to be considered in order to evaluate the oxygen concentration in molten copper. The present paper presents a series of measurements of the activities of oxygen in liquid Cu-M-o alloys (where M stands for Mn, Zn, As, Se or Te) carned out by the present group employing the solid electrolyte galvanic cell technique. Extreme care was taken to control the oxygen potentials in the inert gas atmosphere, and to keep the oxygen levels very low in the molten metal. The oxygen content was determined by analysis of the samples taken out from the melt. The results obtained showed that Mn has a strong negative influence on the activity coefficient of oxygen in liquid copper. A similar, but less prominent effect was observed in the case of Zn. Arsenic had no influence on the activity of oxygen in Cu (liq.). Se and Te had slight negative effect on oxygen activities in copper at XQ >10-5, while at lower oxygen levels the interaction coefficients were found to be positive. The results obtained were compared with empirical models for the calculation of interaction coefficients available in literature.

Jan 1, 2003

By R. Padilla

In most of the Chilean copper and gold concentrates, arsenic is present mainly as enargite, Cu3AsS4, which at the conventional roasting or smelting temperatures decomposes liberating arsenic as gaseous compounds. The objective of this investigation was to study the decomposition reaction of enargite in an inert atmosphere in the range of 500 °C - 750°C. The results obtained indicated that the decomposition begins at about 525 °C. Two distinct regions in the temperature dependence of the decomposition rate were observed: a low temperature region between 525 °C to 650°C and a high temperature region between 650 °C to 725 °C. The X-ray diffraction analysis suggests that the decomposition of enargite occurs through the formation of intermediate tenantite, according to the following sequential reactions: 4Cu3AsS4(s) ? Cu12 As4S13(s)+ 3/2S2(g) Cu12 AS4S13(s) ? 6Cu2S(s) + 2As2S3(g) + 1/2S2(g) The decomposition kinetics was analyzed by using the model for a topochemical reaction of spherical particles: 1-(1-X) 1/3 = kt, which represented well the data. Apparent activation energies of 113 kJ/mol and 60.5 kJ/mol were found for the low and high temperature regions, respectively.

Jan 1, 1999

By Dan Wang, Qian Li, Yong-bin Yang, Tao Jiang

"Thiosulfate is one of the most promising non-cyanide lixiviants for gold leaching. However, the undesirable reaction between thiosulfate and copper (II) gives rise to increased reagent consumption, which results in high cost and huge limit to its development. This paper presents study on the effect of ammonia, copper (II) and Cu(NH3)l+ ions on the oxidative decomposition of thioulfate. It shows that the presence of copper (II) and Cu(NH3)l+ can significantly increase the thiosulfate oxidation, while ammonia is relatively unaffected. The oxidation of thiosulfate by copper(II) in the absence of ammonia is fast at first and then decreases as time increased within a certain time, which can postulate that an intermediate product is responsible for the decreased consumption. The effect of ammonia is depended on the interaction with copper (II), which was found to significantly affect the consumption of thiosulfate.IntroductionFor over one century cyanidation is widely used in industrial production of gold, due to its simplity of process and low cost of production. However, cyanide is a highly toxic chemical reagent used dangerously and brings serious environmental pollution. What's more, cyanidation has slow speed of leaching gold and poorly leaching effective for refractory ores. With the exhausting of free-milling gold ores and promoted environmental protection requests, the disadvantage of cyanidation becomes a growing problem. In recent years, more and more research activities have been focused on alternative processes using non-cyanide lixiviants. Among the non-cyanide lixiviants, thiosulfate is considered as the most promising one[l-5].Compared to cyanide, thiosulfate is an inexpensive, nontoxic and less-pollution reagent, which can form complexes with many metal ions. Thiosulfate leaching of gold has an acceptable leaching rate and is insensitivity to impurities. Moreover it presents advantage on the treatment of refractory gold ores such as carbonaceous gold ores, copper gold ores, complex arsenic and sulfur gold ores, and so on[6]."

Jan 1, 2013

By Jitka Jandová

In this study, hydrometallurgical processing of waste ZnO flue dust arising during zinc removal from galvanized low-alloy steel sheets was investigated on a laboratory-scale to obtain electrolytic zinc. The flue dust was separated from flue gases, generated during heating waste galvanized steel sheets in an electric furnace under air atmosphere at temperatures of about 1000oC. The dust, comprising tetragonal ZnO and insignificant amounts of SiO2, was contaminated by Fe, Mn, Pb, Al, Mg, Pb, Cu and Ca. The dust was leached in 0.5 and 1.0M H2SO4 and/or in 20 and 30% NaOH at different temperatures and different liquid-to-solid ratios to determine the optimum conditions leading to the highest possible selectivity of leaching and efficiency of Zn extraction in minimum time. The subsequent electrowinning process was performed with refined zinc sulphate leach liquors and/or with untreated zinc caustic solutions. Zinc sulphate leach liquors were purified using a combination of a hydrolytic pH-controlled precipitation, cementation and carbon refining. Effects of operational variables on Zn electrowinning have been studied for both sulphate and caustic electrolytes. The conventional plate-plate electrowinning cell has been explored in this study. Comparison of results obtained for both zinc electrowinning from acid sulphate and alkaline solutions is presented contribution.

Jan 1, 2003

By K. C. Mills, P. N. Quested, A. P. Day, R. F. Brooks

"Methods have been developed to measure the physical properties of molten materials relevant to the fluid flow in high temperature processes. Data for the densities, viscosities and surface tensions of Al-, Ni- and Fe-based alloys are compared with (i) values for the pure metals and (ii) estimated values obtained from models making use of chemical composition of the alloy. Experimental values for metallurgical slags are also given and compared with estimated values.1 IntroductionPhysical property data has proved very useful in improving process control and product quality. For instance, in the continuous casting of steel the viscosity (TJ) of the mould flux is important since it determines (i) the optimum casting conditions, nVc = 2.5±1 dPas (m min-1) where V c is the casting speed and (ii) the level of slag entrapment (which leads to inclusions) in the metal. Thus data for properties like viscosity are exceedingly useful in understanding the process and the problems encountered and the causes of defects and problems.Another interesting development which has helped to increase our knowledge of processes and improve process control and product quality is the development of mathematical models of the fluid and heat flow in the process. These models have been developed to the stage where one of the prime requirements is for good physical property data for the industrial materials involved. Recently, Oxley [1] has shown that the use of reliable, experimental, property values for the commercial alloy in a commercial software package produced a significant improvement in the prediction of casting defects. Thus reliable property data are required for liquid metals but also for (i) liquid slags since many processes involve the use of a slag to refine and protect the metal or to lubricate the mould and (ii) refractories, sand and investment moulds."

Jan 1, 1999

By Ivanildo Hespanhol

"DALYs are a measure of the health of a population or burden of disease due to a specific disease or risk factor. It evaluates the time lost because of disability or death from diseases compared with a long life free of disability in the absence of disease. DALYs are calculated as the sum of years of life lost by premature mortality (YLL) and years of healthy life lost in states of less than fully health, i.e., years lived with a disability (YDL), which are standardized by means of severity weights, thus: DALY=YLL+YLD.WHO has established for wastewater use in irrigation (1) the same reference level of health protection as established for drinking water quality (2), i.e., the additional burden of disease from consuming water irrigated food should not exceed 10-6 DALY(Disability-Adjusted Life Years) loss per person per year (pppy). This level of risk means that a single additional case of disease may occur in a population of 1 million, during a life time (70 years). In a individual basis is equivalent to the occurrence of a mild disease during about 31,5 seconds.Such a restrictive risk is almost impossible to be attained in most developing countries which may not be able to afford the cost of wastewater treatment and of other protective measures, even for restrict irrigation.This paper presents proposals to adapt the reference level of risk to local technical, cultural, economical and social conditions of developing countries on the basis of a risk benefit approach."

Jan 1, 2008

By Shenghui Guo, Dongbo Li, Lijun Liu, Chengdong He, Jinhui Peng, Libo Zhang

In present study, partially stabilized zirconia (PSZ) was prepared by CaO doped fused zirconia heated by microwave furnace at the temperature of 1450 oC and holding time of 120 min. The XRD results showed that untreated fused zirconia mainly consists of crystalline compounds of cubic ZrO2 phase; while the roasted one mainly is composed of crystalline compounds of cubic ZrO2 phase and monoclinic ZrO2 phase. It is shown through the optimization of structures of two phases that structure of cubic ZrO2 and monoclinic ZrO2 reject each other, revealing its difficulty in forming coinciding interface and linkage of two phases being of Ca atom. Introduction Due to advantages of zirconia, such as high melting point, chemistry inertia, low heat transmission and so on. Zirconia is always taken as megathermal refractory material[1]. However, in the heating and cooling processes of pure zirconium oxide, martensitic transformation will take place associated with greater shear force and volume change, which severely limits the industrial application of pure zirconia in some areas. Such as: Refractory materials, grinding materials and high temperature insulation materials[2]. Through adding a certain amount of MgO, CaO, or Y2O3 stabilizer, etc.[3,4], the zirconia can change into fully stabilized zirconia, which exists in cubic phase. But this high purity fully stabilized zirconia cracks easily because of thermal stress. Therefore, the thermal shock resistance variation is one of the most important quality indicators of zirconia-based materials. According to the heat treatment, the fully stabilized zirconia can be changed into the partially stabilized zirconia (PSZ)[5], which exists in cubic phase and monoclinic phase and has superior mechanical properties, such as anti-heat, low thermal conductivity, large coefficient of thermal expansion and stability, as well as good wear resistance[6].

Jan 1, 2011

By T. V. Jayaraman, Kranti Kumar, Paul Praveen J., Dibakar Das, A. R. James

"Lead free piezoelectric ceramics with high piezoelectric coefficients are in great demand for sensor and actuator applications. Synthesis and characterization study of one such lead free system, barium zirconate titanate - barium calcium titanate [xBZT-(1-x)BCT] (x = 0.5), via solgel method have been carried out. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the formation of single phase BZT-BCT nanoparticles (<50 nm). The as-synthesized powders were calcined at 1000°C and the powders were pressed into cylindrical pellets. Solid-state sintering of the green pellets at 1550°C for 2 hrs resulted in single phase perovskite structure. Hysteresis loops were obtained which indicates the ferroelectric nature ofBZT-BCT. The bulk ceramic samples with the highest sintered density (~93%) were subjected to electrical poling and the piezoelectric properties ( d33, kp, & i:,) were measured. The structure and piezoelectric properties were investigated and correlated for the given composition of the BZT-BCT system.IntroductionPiezoelectric ceramics are widely used in various sensors and actuators and most of the piezoelectric ceramics, which are presently used, are lead based, which contains at least 60% lead (Pb) by weight. The critical disadvantage of these lead based piezoelectric ceramics is their hazardous effect related to the toxicity of lead, which poses a serious environmental concern starting from their processing to the disposal stage[l]. It is well known that a material to be a good piezoelectric it requires a morphotropic phase boundary (MPB) i.e. the composition induced phase transition between any two ferroelectric phases."

Jan 1, 2013

By Esperidiana A. B. Moura, Michelle Gomes, Cordelia M. F. Escanhoela, Francisco R. V. Diaz, Angel Ortiz, Rene R. Oliveira

"This work evaluates changes in morphological, mechanical and thermo-mechanical properties of electron-beam irradiated HDPE/nanoclay and HDPE/Piassava fiber/nanoclay. Material samples irradiated with 100 and 200 kGy using a 1.5 Me V electron beam accelerator (room temperature, presence of air) were submitted to tensile, flexural, and HDT tests. MFI, SEM and XRD analyses were carried out. Correlation between properties was discussed. Results showed that incorporation of piassava (Attalea funifera Mart) fiber and nanoclay, followed by irradiation represented significant gain in thermo-mechanical properties. Changes in surface morphology and reduction in MFI were observed. In conclusion, it may be claimed that the incorporation of piassava fiber in small size particles and nanoclay in the HDPE followed by electron-beam irradiation effectively improved the polymer properties and led to materials with superior properties suitable for several industrial applications.1. IntroductionIn recent years, the preference for using natural fibers instead of synthetic ones in polymer composites has been growing significantly. In Brazil, due to the great diversity of woody and fibrous plants of our forests, a vast potential of natural fibers is found, presenting good mechanical strength properties, chemical and biological stability, fire resistance, abrasion resistance, shear strength and lightness, among other which may contribute to the development of new materials for different applications such as automotive, aerospace, construction, food segment, cosmetics and others [ 1]."

Jan 1, 2013

By Jian Pan, Zhen He, Deqing Zhu, Shouyan Yue

"The differences of raw material characteristic among six kind of iron concentrates and the influences on ballability were studied from the aspect of the size distribution, specific surface area and particles morphology. The results show that the specific surface area of iron concentrates has crucial influence on ballability, and the effective method of improving ballability for weak ballability iron concentrate has been found. It is of important guidance for Chinese steel mills to import and use iron concentrate from the whole world.IntroductionChina's steel industry has developed rapidly in recent years, crude steel production in 2011 is an unprecedented 683 million tons, which is almost half of the world crude steel production, and it is equivalent to the total sum production of the nations which rank at 2,3,4,5 and 6 in the world [1]. In order to match the development of steel industry, the blast furnaces are becoming larger and more modernization, therefore charging burden of higher quality is requested, and the reasonable blast furnace burden structure is more and more important, at the same time, for iron ore powder sintering process's continuous improvement and development, another method providing ""concentrate"" for blast fumace-pelletizing is also taken seriously. The grate-kiln method of pelletizing has achieved great development for its unique advantage, and in just a few years, there are over 60 rotary kiln production lines have built or being built in China, the sum of pellets has reached to more than 140 million [2, 3]. The rapidly growth of pelletizing yield demands diverse source of pellet, which include not only domestic magnetite concentrate, but also imported hematite which is high in iron and low in silicon. Usually the ratio of imported hematite concentrate increased gradually. The imported hematite concentrate has high grade and fine particle size (the content of -0.074 mm mostly higher than 90%), but the ballability of part of the concentrates is poor."

Jan 1, 2013

By Ragnhild E. Aune, Shahid Akhtar, Reza Beheshti

"The potential use of Black Dross (BD) as a raw material for the production of refractories, fluxing agents and glasses is the main motivation of the present study. Heat treatment experiments were carried out in Ar, and under reduced pressure (20 Pa), to evaluate the salt removal efficiency. The chemical composition of the BD after heat treatment was investigated by SEM-EDS and XRD analyses. Based on the present results, it is established that the salt starts to evaporate at ˜1273 K in Ar, and under reduced pressure. The salt removal efficiency in a 20 g sample was found to increase in both cases as a function of time and temperature. Moreover, in Ar the chlorine concentration was lowered to 0.3 wt% after heat treatment at 1523 K for 10 hours. Under reduced pressure, however, 0.2 wt% residual chlorine was obtained after 8 hours at 1473 K.IntroductionIt is believed that aluminum recycling in the near future will become the main route of aluminum production [1]. Black dross (BD) that is produced during this process contains, among other things, high amount of salts like NaCl and KCl [2, 3]. Almost 800,000 tons of BD is annually land filled in United States and this number continues to grow with the increase in aluminum recycling [2]. The BD should be dumped in controlled land field and it is costly procedure [4, 5].The water-soluble compounds in BD react with water or environmental humidity and release chlorides into the water and/or generate toxic gases such as H2, CH4, NH3 and H2 S [6-8]. In the Europe, BD is considered as toxic waste and its disposal as landfill is forbidden [8, 9]. After salt removal, the BD is considered to be non-hazardous and can be buried under ground [10].On the other hand, BD do also contains many relatively valuable compounds that may be changed in to useful materials as a result of further treatment [11, 12]"

Jan 1, 2012

By Donghai Li, Cheng Pan, Xuyang Liu, Xuewei Lv, Chenguang Bai

"Fine chromite ore is the common raw material to produce ferrochrome alloy through the submerged electric furnace process. The electric resistivity of fine chromite ore plays an important role in the operation efficiency because it determines the current distribution. The effect of particle size and the contact area of the particles on electric resistivity for several of chromite were investigated at room temperature, and the relationship between the electric resistivity of mixed particles and the volume fraction of lump ore to fine ore was also studied. The results shown that the electric resistivity increases with the increase of particle size, and the electric resistivity of mixture decreases with the increase of volume ratio of fine ore.IntroductionChromium is one of the most important alloying elements in manufacturing of stainless steel that used at high temperature and corrosive environment applications [I, 2]. As the raw materials to be charged into the steel, ferrochromium alloys and charge chromium are produced directly by smelting of chromite ore with the reducing agent in submerged electric arc furnace (SAF). During the process, the oxides of chromium and iron were reduced by carbon and meanwhile the electrical energy were consumed [3,4]. The ideal industrial process is to achieve high recovery level of Cr and Fe with minimal power consumption. In SAF process, the electric resistivity of charge stock has significant effect on the current distribution, which determines the heat distribution, molten bath structure and chemical reactions in the furnace. High resistance of the charge is desired to reduce the current distribution through the charge stock, thus the electrodes may insert into the charge stock with proper depth to form a high temperature arc heat source, and proper smelting can be realized[5]."

Jan 1, 2012