By Jorge Alberto Soares Tenório, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Franco Alves Lavacchini Ramunno

"The traditional process for recovery of metals from waste electric and electronic equipment (WEEE) usually involves pyrometallurgical processing. However, the application of this technology to processing waste printed circuit boards (WPCBs) might lead to the formation of dioxins and furans, due to thermal degradation of flame-retardants and polymeric resins present in the board substrate. Therefore, this paper proposes a hydrometallurgical route for the recovery of copper. The acid leaching behavior of copper has been investigated at three different temperatures (25°C, 50°C and 75°C) with and without the addition of an oxidizing agent (hydrogen peroxide - H202). The dissolution kinetics for acid copper leaching was calculated based on chemical analysis by ICP-OES (Inductively Coupled Plasma - Optical Emission Spectroscopy). At 50°C with 1 mol/L H2S04 added 10 mL H202 (30%) each half hour under pulp density of 1 g I 10 mL, 100% of copper was extracted after 3 hours. The dissolution kinetics of copper with H2SO4-H2O 2 followed 1 - (1 - X)113 =Ket, i.e. chemically controlled reaction model.IntroductionThe information regarding the generation of waste electric and electronic equipment (WEEE) are still difficult to obtain because the estimates should take into consideration the historical production and sale of various products and the rate at which they reach the end of their life cycle, whose duration depends on the behavior of consumers [1]. Thus, the estimated overall WEEE generation varies between 25 and 50 million tons each year, which corresponds to more than 5% of all municipal waste generated [2], and this amount will increase at a rate of 3 to 5% per year, approximately three times faster than other individual types of waste [3].Printed circuit boards (PCBs) are essential parts of electric and electronic equipment (EEE), being found in virtually all electronic products, as well as in weapons systems [4]. A PCB is a basic component, which consists of a board where copper tracks are deposited. While the board behaves as an electrical insulator, the tracks connect electrically the various components attached to the board [ 5]. In addition to glass fibers, paper and resins, the PCBs contain significant amounts of metals, such as copper, iron, nickel, lead, stain, silver, gold and palladium [6]. In general, the weight fraction of metal is around 28% and the remainder of the boards is composed of plastic (19%), bromine (as flame retardant - 4%) and ceramic material (49%) [7]."

Jan 1, 2014

By Masayuki Kudoh, Kiyotaka Matsuura

"Molten aluminum and nickel cast onto a steel block exothermically react and produce molten nickel monoaluminide, NiAI, which is simultaneously joined to the steel. The heat of the exothermic reaction is transferred to the steel block, and steel near the surface of the block is melted. The depth of the melted steel increases with both the initial temperature of the steel block and the thickness of the produced NiAI. Iron from the melted steel dissolves in the molten NiAI, and an intermetallic compound of NiAI-Fe pseudo-binary system is produced. During solidification of the intermetallic compound, it is strongly joined to the steel. The Ni.Al-Fe intermetallic compound has an excellent resistance to oxidation and corrosion.IntroductionAn intermetallic compound of nickel monoaluminide, NiAl, offers many advantages over conventional superalloys, such as higher melting temperature, lower density, greater specific modulus and higher thermal conductivity [1]. NiAl also exhibits excellent high-temperature oxidation resistance when doped with zirconium or hafnium, and excellent high-temperature corrosion resistance when doped with chromium or yttrium, that are superior to existing high temperature alloys or coating materials [1-4]. On the other hand, NiAI is significantly brittle at temperatures below 600 K [5-7], which is the most sigriificant disadvantage of NiAI. A possible way to overcome the disadvantage and to utilize NiAl as an environmental-resisting high-temperature structural material may be joining of NiAl to a ductile material."

Jan 1, 2000

By Shen Shen, Paul R. Ohodnicki, Samuel J. Kemion, Vladimir Keylin, Alex Leary, Joseph F. Huth, Michael E. McHenry

"Recent DOE workshops highlight the need for advanced soft magnetic materials leveraged in novel designs of power electronic components and systems for power conditioning and grid integration. Dramatic weight and size reductions are possible in these applications through operating at increased frequencies. This manuscript discusses processing and composition design approaches for optimizing FeCo-based nanocomposites for higher frequency operation at 100 kHz and above. The proposed strategy involves starting with prior compositions known to exhibit high inductions, optimal field crystallization induced anisotropy, and excellent mechanical and high temperature magnetic properties. Proposed alloy modifications for the applications of interest would include increased amorphous phase resistance, optimum induced anisotropy, and minimized or carefully engineered magnetostriction. Relevant process developments would target reduction of ribbon thickness by optimizing the casting process or post-processing treatments such as chemical thinning or rolling. Three archetypes FeCo-based nanocomposites are described including near equiatomic FeCo-based, Fe-rich and Co-rich alloys.MotivationSilicon steels are widely applied for 60Hz utility-scale transformers [1]. For applications at high frequencies, however, Si-steels exhibit unacceptable losses and ferrites are typically used due to their high electrical resistivity and good soft magnetic properties [2]. However, the low inductions offerrites have limited their applications in power electronics. Developments in rapid solidification have led to amorphous metal alloys and controlled nanocrystallization processing has resulted in state-of-the-art amorphous/nanocrystalline nanocomposite soft magnets [3-5]. Commercial utility-scale transformers made with Fe-based amorphous materials have been demonstrated to result in significant energy savings with an associated reduction in greenhouse gas emissions [6]. DOE workshops held in 2010 emphasized a need for advanced soft magnetic materials for the next generation of power electronics. For advanced power conditioning and grid integration applications, frequencies of 20 kHz up to -1 MHz are of interest depending on the power level [7]. Here, we review previous work and discuss the approaches to optimize FeCo-based nanocomposite materials for high frequency applications."

Jan 1, 2012

By Gervais Soucy, François Quesnel, Pierre Hovington, Wen Zhu, Karim Zaghib, Jocelyn Veilleux

The properties of lithium titanates anodes in Li-ion batteries are highly dependent on their secondary constituents. While their main phase is usually constituted of Li4Ti5O12, significant quantity of lithium titanates compounds of various stoichiometry are often present, due to either the processing, usage or aging of the material. These may go underreported, as many of these spectrums overlap or display low signal in X-ray diffraction (XRD). Samples of nanosized lithium titanates synthetized by inductive plasma were characterized by XRD and scanning electron microscopy (SEM), as they provide a regular yet typical crystallite size and shape including multiple phases. A Rietveld refinement was developed to extract the composition of these samples. Mass balance through further annealing and differential scanning calorimetry (DSC) enthalpy measurements from phase transformations were also used as identification and validation techniques.

Jan 1, 2015

By Tianzu Yang, Weifeng Liu, Shu Bin, Lin Chen, Wanda Bin

"Vanyukov Process has been mainly applied for processing copper and nickel sulfide ore for more than 30 years. Based on the understanding of the Vanyukov Process, researchers from China introduced the technology into the areas of lead, antimony and bismuth extraction by changing the furnace structure and technical flow, which greatly extended the application area and raised the processing efficiency, thus developed the oxygen-rich side-blow bath smelting (OSBS) technology in 2000. This contribution reviews the history of OSBS technology from four respects: the quantity, the furnace structure, the process flow and the application area. Its potential research direction and industrial application are also summarized.IntroductionVanyukov bath smelting furnace and related bath smelting technology were developed by researchers from Soviet Union who devoted comprehensive research on fundamental theory as well as engineering technology [1,5]. Vanyukov process has been applied for large industrial production since the 1970s and it is still one of the major methods in modem pyrometallurgy process. The appearance ofVanyukov double district furnace and joint double furnace in the past ten years, which are applied for copper smelting, is the most valuable advances of the Vanyukov process [7,8,9]. However, the application ofVanyukov process was limited in copper and nickel sulfide ore smelting, and few countries adopted this process except Soviet Union."

Jan 1, 2013

By Takashi Ikeda, Masafumi Maeda

"Demand for solar cells is increasing linearly throughout the world. Last year production totaled 3000 tons worldwide. The market size of solar silicon is expected to increase further because of international ""political"" demand to reduce carbonaceous emission from energy consumed. Most elemental silicon is produced by the carbon reduction of Silica in an electric arc furnace. Purity of silicon at this stage is 90-99%. Major impurities are Fe, Ti, Ca· and Al, and minor ones are P, B and carbon. The oxidizing metallurgical process is no longer effective to remove transitfon metals because those are less noble to silicon. Nonmetallic impurities such as phosphorus and boron must be reduced to 0.001ppm for semiconductor use. The most common process for high purity silicon is the Siemens C process, which is basically distillation of hydro-chlorinated silicon followed by CVD of SiHCl3. The cost of such silicon is expensive to allow its popular use in solar cells. Currently scrap silicon -of semiconductors is used for this; however, the supply-of that scrap is limited to just a portion of semiconductor production.In this paper world demand for silicon will be reviewed and some of the processes proposed summarized.IntroductionSilicon is element 14 in atomic number and has an atomic weight of 28.0855. Little elemental silicon is found in the earth, and it is mostly found as oxides or silicate. The Clark number of silicon is very large and the second in its number. If we were discussing the volatility of silicon element on the globe, we would never worry about it. However, it is very difficult to obtain pure elemental silicon because a high purity silicon compound is very rare. In most cases these are silica (silicon oxide SiO2). As shown in Table 1, there are many grades of silica ore classified mainly by their content of iron and alumina."

Jan 1, 2000

By Clemens Schmetterer, Patrick J. Masset

"The surface tension represents an important property for the modelling of high temperature processes. In this study the surface tension of two Al2O3 – CaO – SiO2 model slags and the influence of the admixture of 5 up to 30 wt.% FeO were studied. The surface tension measurements were carried out using the sessile drop technique on BN substrates under Ar atmosphere (10-6 atm O2) up to 1500 °C.IntroductionThe aim of VIRTUHCON1 is the virtualization of high temperature conversion processes, a task that requires thorough understanding of these processes. In many of these conversion processes slag plays an important role to control the properties of the product, to protect the reactor lining or simply as waste. Slag surface tension is one of the materials properties that is needed for the description of such processes, since it influences the interactions between the components in the reactor, e.g. at the slag – Fe interface in the blast furnace.Surface and interfacial tensions have thus received considerable attention in research, but the number of investigations in this particular pseudo-quaternary system is surprisingly low. Furthermore, the literature data are subject to different measurement conditions and techniques which complicates the data analysis and comparison.The slag atlas [1] offers a compilation of the available literature until 1986 (shown in Table I), but literature search has not revealed more recent studies of this system until now. For example, Elliott and Mounier [2] determined the surface tension of ACSF slags using the double tube maximum bubble pressure technique at 1200 °C. They kept their slags in contact with Cu-S-F mattes, and the slag therefore contained a certain amount of sulphur which acts as a surfactant and lowers the surface tension. The compositions of their slags were scattered over a wide composition range and they did not use a common ACS base mixture for their tests, either. The surface tension values vary between 417 and 446 mN/m, but due to the reasons just mentioned no trend in the measurements can be observed and the influence of FeO admixture on the surface tension cannot be deduced. Further information including the temperature dependence is available from Pavlov et al. [3], Ishchanov and Shushkov [4] and Murav’eva and Kaplun [5]; the diagram on page 446 in Ref. [1] has been drawn from these sources. Both positive and negative temperature coefficients are reported in these works. SiO2 is the only pure constituent that has a positive temperature coefficient [6], but a correlation of the temperature coefficient with the SiO2 content was not found to be conclusive."

Jan 1, 2011

By Malti Goel

"Ferrous and non-ferrous metals industries are source of both direct and indirect greenhouse gas (GHG) emissions. Metal industry accounted for 29.7% of the total GHG emitted from the Indian industry sector in 2007. Aluminum is second largest contributor after steel. Indian Aluminum industry has been growing and is adopting several effective measures for better efficiencies through process change and waste utilization. Improvement in the energy efficiency can form the basis of monitoring reduction in emissions. Under the National Action Plan on Climate Change 2008, National Mission for Enhanced Energy Efficiency (NMEEE) aims to upscale the efforts to unlock the market for energy efficiency improvement on a public private partnership (PPP) basis. For a transition to low carbon economy industry is undertaking voluntary measures through scientific and technological innovations both in upstream and downstream sectors. In this paper an attempt is made to overview recent developments in Indian Aluminum industry as well as summarize scientific & technological challenges and prospects.IntroductionAluminum plays a vital role in industrial development. It is a substitute for different type of materials ranging from wood to copper and steel. The aluminum industry has high energy consumption and high contribution to greenhouse gases from carbon dioxide and perfluorocarbons (PFCs) emissions. It is estimated that CO2 equivalent burden of aluminum industry is about 1% of total anthropogenic emissions. The anticipated world growth rate is 3.5% for aluminum demand. Through measures to reduce both direct and indirect CO2 emissions, electricity consumption was reduced from 25 kWh / kg of Aluminum in 1998 to 15 kWh / kg of Aluminum produced in 2008. It is targeted to further reduce it to 10.8 kWh. Aluminum industry is also responsible to about 60% of all PFC emissions. The PFC emissions are harmful to environment, accumulate in surrounding vegetation and contaminate. Efforts to reduce PFC emissions from aluminum industry started early and reduced to 0.5-1 kg / tonne in 1990 [1] from 12-15 kg / tonne in 1940. Since 1990s to 2000 it further reduced to 0.2 -0.4 kg / tonne as seen in Fig. 1. The Global Aluminum Sustainable Development Initiative (GADSI), targets perfluorocarbon (PFC) specific emissions reduction of 80% for 2010 relative to 1990."

Jan 1, 2011

By S. Niyomwas, T. Chanadee

The influence of flux CaO2–Al ratio on the Self propagating high temperature synthesis (SHS)-casting reaction products in WO3–Si–Al system has been investigated in this study. Incorporation of CaO2–Al amounting to 1–5 wt% of total charge has been found to be adequate to form WSi2 intermetallic with a maximum hard-W5Si3 secondary phase. The micro-hardness of tungsten silicides intermetallic product increased significantly with CaO2–Al ratio. The as-SHS-casting products were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM) with energy dispersive x-ray (EDX) technique.

Mar 1, 2017

By M. J. Adam

As part of its research program, the U.S. Bureau of Mines is investigating the partitioning of complex minerals to simpler phases using sulfidation reactions for selective extraction of mineral constituents of value from extraneous elements early in processing schemes. This report describes research in which thermal processing of the complex Ti -bearing mineral ilmenite (FeTiO, ) resulted in partitioning of the valuable Ti metal to the simpler compound rutile (Ti0 ). Samples of ilmenite were blended with elemental S for thermal treatment a2 various temperatures under controlled atmospheres in an effort to dissociate the Fe from the ilmenite complex. Product characterization revealed that the Fe was partitioned from the ilmenite, forming a rim of pyrrhotite/pyri te (FeS/FeS,) on a rutile core. The products were agate milled and then subjected to cursory magnetic and flotation techniques in an attempt to physically separate the partitioned phases. Partitioning results and phase concentration data are reported relative to thermal treatment variables and physical separation techniques.

Jan 1, 1993

By Shenghui Guo, Ying Lei, Hao Niu, Huilong Luo, Jinhui Peng, Libo Zhang, Yu Li

"In this work, the combination of microwave drying (MWD) and heat pump drying (HPD) drying experiments were designed by response surface methodology (RSM) based on central composite design (CCD) using design expert software (Version 7.15), and the process parameters were optimized. The conditions given by software are: the MWD time is 4.6 or 4.4 min; the HPD time is 9.0 or 8.6 min; and the sample mass is 620 or 600 g. Under those conditions the moisture content is 1.0 10-2kg water/kg wet basis, and the effectiveness ratio is 0.70 kg water/kwh. The results of confirmatory experiments conducted under the optimized conditions show the combined drying have superiority of decrease of energy consumption and increase of handling capacity over the single MWD or HPD.1 IntroductionSilica sand is one of a silicate mineral with properties as hard, anti-friction and less reactive, commonly used as raw material for foundry and construction. The silica sand obtained from mineral dressing processes such as scrubbing, magnetic separation and flotation. Its moisture content is approximately 0.08~0.12 kg water/kg wet basis. The most common methods used for drying are solar drying and hot air drying. But these methods have some shortcomings: for example, the solar drying has longer process time due to low energy yield, [1] hot air drying has low-energy efficiency and a lengthy drying time. [2]Microwave is electromagnetic waves with frequency are 300MHz to 300GHz. The outstanding features of microwave heating are rapidity and selectivity. The water specific inductive capacity of 60~78 is much bigger than common materials, the moisture always quickly absorb electromagnetic wave and rapidly transfer to vapors. So, it can significant reduce the drying time. [3] Heat pumps (HPs) are devices for raising the temperature of low grade heat energy to a more useful level using a relatively small amount of high grade energy."

Jan 1, 2011

By Z. Yang, R. W. Smith, Jr. Wharton

"Microorganisms have the ability to remarkably adsorb and/or absorb heavy metal ions. Hence they are being studied widely as a means of removing metal ions from aqueous solutions both in order to clean up toxic streams and to recover valuable metals from these and other streams. It is often difficult to harvest organisms such as bacteria and unicellular algae since they are usually too small to be readily screened out. Froth flotation may prove to be a feasible method to harvest such organisms subsequent to the ad/absortion of the metal Ions. The present paper discusses the surface/electrokinetic properties of microorganisms and the modifier-collect conditions under which they should float. The zeta potential of the green alga Chlorella vulgaris was measured in the presence of AI(III) and Pb(II) ions and in the presence of dodecylammonium chloride and sodium dodecylsulfate. Present and past data suggest that the organisms should behave similarly to other finely divided, charged (polar) solids with their behavior sometimes modified by the non-polar surface regions present.IntroductionThe overall field of bioengineering is growing at a remarkably accelerating rate. Hydrometallurgy and mineral processing are included among those disciplines where there has been actual or proposed commercial use of bioorganisms. Further, the actual or proposed use includes bacterial enhancement of leaching of a number of different types of ores (1-5), modification of the flotation or oil agglomeration separation of minerals by bacteria (6,7) and microorganism (algae, bacteria or fungi) concentration of metal ions present in effluent or other mineral processing or hydrometallurgy aqueous streams (8-23)."

Jan 1, 1988

By N. Kanari

Kinetics of the carbochlorination of Cr2O3 has been studied with C12+CO gas mixtures between 500 °C to 900 °C using thermogravimetric analysis. The apparent activation energy is about 100 kJ/mol. Mathematical fitting of the experimental data suggests that the shrinking sphere model is the most adequate to describe the carbochlorination mechanism of chromium oxide and that is controlled by the chemical reaction. In the temperature range of 550 "C to 800 OC, the reaction order is about 1.34 and is independent of temperature. Changing the C12+CO content from 15 pct to 100 pct increases the reaction rate and does not affect the reaction mechanism. Similarly, changing the ratio of C12/(Cl2+CO) from 0.125 to 0.857 do not modify the carbochlorination mechanism of Cr203. In these conditions, the reaction rate passes through a maximum when using a chlorinating gas mixture having a Cl2/(C12+CO) ratio of about 0.5.

Jan 1, 1998

By Jorge Alberto Soares Tenório, Denise Crocce Romano Espinosa, Luciana Harue Yamane

"The present work investigated the effect of inoculums volume on bioleaching to recover metals from printed circuit boards using Acidithiobacillus ferrooxidans-LR. Printed circuit boards from obsolete computers were mechanically processed by comminution followed by magnetic separation, and the obtained non-magnetic fraction was used in the bioleaching experiments. A shake-flask study was carried out on the non-magnetic fraction samples using a rotary shaker at 30°C, 170 rpm and different volumes of oxidized culture solution as inoculums (%v/v): 5, 10, 20, 30, 40, 50 e 60. The oxidized culture solution was prepared inoculating pre-adapted bacteria Acidithiobacillus ferrooxidans-LR (5%v/v) in 200mL T&K medium. Leaching in acidic ferric sulphate was also performerd. The analyzed parameters were pH, ferrous iron concentration and metals analysis (AAS). The results showed that using 10%v/v of inoculums were extracted 99,2% of copper and 60% of aluminum by bioleaching. Zinc, lead and tin extraction were not influenced by bacterial leaching and extractions rate were obtained by chemical leaching promoted by acid medium. Ferric iron leaching extracted less copper (35%) than bioleaching. SEM analysis shown surface difference between samples of non-magnetic fraction before treatment and after bioleaching, showing corrosion pits formed by the bacteria contact.IntroductionWaste of electrical and electronic equipments (WEEE) has been target of discussion due to environmental, political and economical issues involved. Around 17 million of computers are discarded annually in the world due to malfunctioning equipment or because technologies become obsolete [1,2]. In contrast, only the central processing unit (CPU) of computers weights around 3kg. From this data, it can be calculated that 51 million kilograms of CPU waste are discarded yearly. This calculation was performed considering only the CPUs, disregarding the cathode ray tubes and liquid crystal displays of monitors [3,4]. Because of the amount that has been accumulated, e-waste has become a global problem but also can be an alternative source to recover valuable materials [5,6]."

Jan 1, 2012

By Shadia J. Ikhmayies

"Nanocrystalline fluorine doped tin oxide (Sn02:F) thin films were produced by the spray pyrolysis technique (SP) on glass substrates at a substrate temperature T, = 450 ° C. The hydrated stannous chloride (SnClz.2H20) was used as a precursor and ammonium fluoride (NH4F) and hydrofluoric acid (HF) were used as the doping compounds. A comparison between the compositional, morphological and optical properties of the films obtained by using the two doping compounds was performed by using scanning electron microscope (SEM) observations, energy dispersive spectroscopy by X-rays (EDAX) and transmittance measurements. It is found that the films prepared by using HF have larger grain size, and higher fluorine content than the films prepared by using ~- In addition these films have higher transmittance and higher direct optical bandgap energy. These results are interesting for the use of Sn02:F as a forecontact in CdS/CdTe solar cells.IntroductionTin dioxide is an n-type, wide bandgap semiconductor (about 3.5 eV) and in the form of thin films, it is a transparent conducting material, characterized by high optical transmission (80- 90%) [l]. Sn02:F is the most widely used transparent-conducting oxide material. The transparent-conducting thin films of this oxide are used as electrodes in a variety of optoelectronic devices, as heat mirror coatings in 'smart windows' for buildings, in automobile and airplane windshields, in incandescent light bulbs, in flat-plate and concentrating solar collectors. Tin oxide and zinc oxide, in thin film configuration are technologically important materials because of their applications in photovoltaic cells [2].Among various dopants for Sn02, fluorine is often preferred, because fluorine doping results in films with high transparency and good conductivity [3]. By exploring the literatures, it was found that different sources of fluorine were used to produce Sn02:F thin fihns, among which are ammonium fluoride (NH4F) and hydrofluoric acid (HF) are the most used. Some researchers used~ [2, 4-7] and others used HF [3, 6-8] for doping Sn02 films. Gordillo et al.[7] used both of NH4F and HF and showed that the resistivity of thin films obtained by using HF was lower than that of similar films obtained by using NH4F by a factor of 2.2. They also found that the films obtained by using HF have more random orientations."

Jan 1, 2013

By Jingwei Lou, Bing Li, Suzhen Li, Miao Shen, Jianguo Yu

"As a main impurity in primary lithium metal, magnesium is difficult to remove because of the very close relative volatility of the two metals. Electrochemical refining provides a possibility to completely remove Mg in the LiCl-KCl melt prior to Li reduction. MgCl2 reduction processes in LiCl-KCl- MgCl2 melt were investigated by cyclic voltammetry (CV), square wave voltammetry (SWV), chronoamperometry and chronopotentiometry. Then potentiostatic electrolysis was carried out and Mg (II) ion was reduced onto a liquid lead cathode from the LiCl-KCl-MgCl2 melt at the Mg deposition potential. The results show that Mg ( II ) is reduced in one step with two-electron transfer. The reduction potential of Mg ( II ) was well defined. The reduction of Mg( II) results in Li ( I ) underpotential deposition at 0.2V more negative potential than that of Mg( II) reduction. Therefore, in order to prevent Li ( I ) from codeposition with Mg, accurately controlling Mg ( II) reduction potential during the potentiostatic electrolysis was necessary. Ninety three to 99 % removal rate of MgCl2 was achieved after 8-12 h electrolysis when liquid lead was used as cathode.IntroductionMetallic Li has been widely used in batteries, light weight alloys and in fusion reactors because of its excellent properties. Currently, the only way in industry to produce metallic Li is by electrowinning from molten LiCl-KCl at about 450 °C [l-5]. LiCl-KCl is the only electrolyte used, because they presents a lower eutectic temperature and KCl shows a slightly higher theoretical decomposition voltage than LiCl, as shown in Table l .The produced metallic Li generally contains 1-2 wt% impurities including Na, K, Al, Ca, Mg, Si, etc. [6l, which are derived from the corresponding metal chloride compounds or metal oxide compounds existing in the LiCl and/or KCl raw materials. These impurities have to be removed by subsequent vacuum distillation at high temperatures to meet the requirements for metal Li purity in the final products. Separation of Mg from Li by vacuum distillation is difficult because their relative volatilities are very close, as shown in Table 2."

Jan 1, 2011

By Robert Vidal

The performance of a laboratory-scale cell for the electrolysis of an aqueous chrome alum solution was studied. Electrode potentials, pH, and Eh were recorded. An optimum catholyte pH of about 2.5, consistent with information from the literature was observed. Values exceeding this range resulted in a precipitate formation and are detected by wavering cathode potentials. The role of anodically produced dichromate ions was investigated by chemical analysis. It was found that the steady state concentration of dichromate ions varies inversely with fluid flow from catholyte to anolyte. This concentration was also reduced with the use of precious metal coated titanium anodes.

Jan 1, 1994

By Adolfo Pillihuaman Zambrano

Fe-Cr-C production is a very high electrical energy consuming process. Decrease up to 10% of this electrical energy is expected when self-reducing agglomerates are used. This research aims to understand how the synergetic effects are when stronger reductant, like Fe-Si, is substituted for coke in self reducing pellets. Brazilian chromites containing 41.2%Cr2O3 were mixed with petroleum coke and agglomerated with cement as the binder. Small amounts of 1%, 2% and 4% of Fe-75%Si were substituted for the equivalent petroleum coke, and pure silica plus hydrated lime were added for adjusting the slag composition. The mixture was pelletized, dried and submitted at 1773K up to complete the reactions. The results showed that the reduction reactions were 1.4 and 2 times faster with 1% and 2%Fe-Si addition, respectively, than with no addition. The microscopic analysis showed that it was formed a liquid phase, but the pellet did not collapse what indicates that the coalescence of the metallic phase depends on the dissolution of the pre-reduced particles of the chromites into slag.

Jan 1, 2008

By P. Henry

A novel electrochemical cell has been developed for the recovery of MnO2 from residue of pyrolusite ore leading loaded with Fe, Al Ni, Co and Si impurities, This new process can be considered as an alternative to the traditional methods : S02, H2O2 or bioleaching. It has been observed to proceed fairly rapidly and could prove to be a more economically viable process, as well as being more environmentally acceptable. Electrochemical characterization and kinetic studies have shown that MnO2 is effectively leached by electrogenerated ferrous ions at high current density from a pulp containing less than 5 g8 Fe. The chemical reactions are : Cathode (inox) : 2F23+ + 2e ? 2 Fe2+ Bulk: MnO2 + 2 fe2+ 4H+ ? Mn2+ + 2 Fe3+ + 2 H2O Anode (Pb-Ag) : H2O ? ½ O2 + 2H+ + 2e Global: MnO2 +2H+ Fe2+ = Mn2+ + H2O + 1/2 O2 The catholyte (MnO2 pulp) circulates upward in the expanded mesh cathode separated from the sulfuric acid solution anolyte by a separator which shows high mechanical resistance, low porosity, low potential drop, and reasonable cost. Laboratory and mini-pilot tests have led to the construction of an OT crating pilot plant (100 kg/hr) able to leach more than 95% of Mn, Ni, Co at 1000-1200 A/m2, 50°C with high faradic yield (> 95 %) and low power consumption (3.2 kWh/kg kWh/kg &4D). New applications like the treatment of spent Zn-Mn batteries, polluted soils, spent catalysts and oxide ore (cobalt, nickel) with electrogenerated redox species are now investigated at a laboratory and mini-pilot scale.

Jan 1, 2000

The U.S. Bureau of Mines investigated CaF2-assisted H2SO4 leaching to extract Mn from domestic silicate manganese resources. A pyroxmangite ((Mn,Fe)Sio3) ore containing, in pct, 34 Mn, 23 Si, 3 Ca, and 1 Fe was leached at 90° C for 3 h in a solution containing, in g/L, 12 Mn, 140 H2SO4, 130 (NH4)2SO4, and 5 CaFz. Manganese extraction of 92 pct was achieved. Manganese of greater than 99 pct purity was prepared by electrolyzing the purified pregnant solution at a current density of 50 mA/cm2. The current efficiency was 65 pct.

Jan 1, 1991