Search Documents

By W. D. Donnelly, M. L. Rudee

THE crystallography and morphology of ?-Al3Fe precipitates in an A1 + 0.5 wt pct Fe alloy have been studied by transmission electron microscopy. The alloy was cast in cylindrical ingots, 15 cm in diameter and 60 cm in length, and cooled slowly. The measured composition was 0.527 wt pct Fe, 0.001 wt pct Mg, and 0.003 wt pct Cu. Spectrographic analysis revealed no additional trace impurities. Thin slices were cut from the ingot and reduced by more than 95 pct by rolling to a thickness of 0.1 mm with no intermediate annealing treatments. These thin sheets were then vacuum-annealed for 1 hr at 612°C and air-cooled in their capsules. Thin foils for examination in the electron microscope were prepared by electropolishing. The precipitate is found in the form of oval platelets on the (110) planes of the matrix. The major axes of the platelets are parallel to the (110) directions of the matrix, and vary in length from 1/2 to 2 p. The thickness is about 1/10 µ. Examples of platelets, both in the plane of the foil and normal to the foil, are shown in Figs. l(a) and l(b), respectively. lack' found that ?-A13Fe (more correctly Al13Fe4) belongs to the monoclinic system. Using Black's structural data and simultaneous electron-diffraction patterns from the matrix and precipitates, the habit planes and directions were determined to be: (001)? 1 (110)Al [100]?|| H [001]Al The orthogonal crystallographic axes of the precipitates are accurately in the habit plane, while the measured coincidences of the directions are only within 10 deg. The major axis of the platelet is parallel to [010] in the 0. This orientation corresponds to the direction of nearest registry of the lattices.

Jan 1, 1964

By I. G. Grettum, Eugene A. Stephenson

The flooding process was originally the result of accidents to casing and tubing, but it has gradually passed from an accidental condition to a definite engineering procedure. In spite of the general sheetlike char-acter of the major sand body, the position of shale bands, their thickness, the size of the grain and variations in effective porosity all give the sand different characteristics in different layers and in different places in the same layer. This condition has an important influence on the movement of flood oil and water, and on the yield per acre, as well as a bearing on what shall be considered the best method of handling flood wells. . A valuation takes into consideration six factors: (1) Flooding methods, of which four have been in common use, as follows, in order of effective recovery, (a) circular flood, (b) line flood, (c) five-spot and (d) five-spot with delayed drilling; (2) recovery per acre, which is definitely related to the oil content, the porosity, the method of flooding, the spacing program, and the continuity of the water supply; (3) the rate of production per well per day, which is definitely related to the mcthod of flooding, the oil content and the porosity of the sands; (4) the operating cost of the well, including royalty, overhead, taxes, etc. (Operating costs are usually expressed as unit cost per barrel.); (5) the expected price per barrel. It is safer to use the average price over a number of years than to attempt to forecast future price fluctuations. The discount factor (the sixth factor) used in appraisal of Bradford flood properties should be less than that commonly applied to other properties, because the hazards of operations have been reduced almost to those of a manufacturing industry.

Jan 1, 1930

By E. E. Malouf

With the continued development of low-grade porphyry copper deposits by open pit mining, substantial amounts of copper-bearing strip material have been accumulated in waste dumps adjacent to the many large mines. Since the end of World War II, the production of copper from leaching these copper-bearing wastes increased from approximately 4% of the total copper production to 10% by the early 1960's. Projected increases will probably raise this figure to 20 to 30% by the early 1970's. Furthermore, a gradual recognition of the economic feasibility of leaching mined-out areas is evident and will undoubtedly contribute additional production. Waste dumps in canyons and gulches on the periphery of open pit mines, mine stopes, caved areas, and abandoned open pits often contain substantial quantities of leachable rock ranging in concentration from 0.1 to 0.4% copper. Recent developments in the leaching of copper, mainly the recognition of bacterial oxidation of sulfide minerals combined with better under- standing of the control of the salt content of the leach solutions, both by adjusting the pH and/or by hydrolysis, are resulting in a greatly expanded recovery of copper from these hitherto uneconomic mine rejects. 11.5-1. Mechanism of Leaching. Leaching processes for the extraction of metal values from mine ore or waste may be classified for convenience as either chemical leaching or bacterial leaching. Chemical leaching is considered to be the extraction of soluble salts by metathesis in acidic, basic, or neutral water solutions. The reactions involved may be evaluated by chemical thermodynamics. Bacterial leaching, although a chemical process, is dependent on biological catalysis and this is generally a much more complex process. This justifies its separate treatment in the application to leaching. Acid ferric sulfate solutions are commonly employed in the mining industry to leach valuable metals from metal sulfide ores. The leaching mechanism is a reduction-oxidation reaction in which minerals are oxidized at the expense of ferric sulfate. Such chemical leaching is profitable when

Jan 1, 1968

By C. M. Nickerson

The possibility of deeper production in the Buena Vista Hills was first considered in 1933. At that time, however, the heavy state curtailment program served to deter any operator from drilling test wells, which, if successful, might upset the proration schedules. Because most of the acreage was held by several major operators and the remainder by substantial independents, the adoption of a plan of cooperative development was considered desirable. Such a plan was formulated for the development of any deeper oil and gas horizons that may be found to exist. This plan, which was signed by the Secretaries of the Navy and of the Interior on behalf of the United States on July 9,1936, is now effective for the development of lands within the area shown on Fig. 1. Unlike most unit plans, the present cooperative development plan permits each operator to drill and produce his own wells. For the purpose of this plan the Buena Vista Hills field is divided into two pools. The present production is classed as the " old pool,"' while any future production below a certain marker which roughly coincides with the bottom of the Santa Margarita formation is included in the "pool" to which the provisions particularly apply. Naval Petroleum Reserve No. 2 lies within the area and constitutes the major portion of the Federal leases subject to the plan. There are 39,040 acres and 27 operators within the area. Twenty-six operators controlling 99.5 per cent of the acreage have signed the agreement. Geology oF the Buena Vista Hills The Buena Vista Hills consist of a low range in the southern portion of the San Joaquin Valley, and are roughly parallel to the adjacent Temblor range to the south. The Elk Hills oil field parallels the Buena Vista Hills a few miles to the north. The subsurface structure is a re-entrant anticline upon the major Midway-Sunset monocline. This anticline is divided into two minor

Jan 1, 1937

By Warden A. Moller

The Fushun coal-field, now being opened up by the South Manchurian Railway Co., is connected with the main line by a branch, 30 miles long, from Sui Chia Tun, 10 miles south of hlukden, the oapital of Manchuria. The coal-field, which lies on the southern bank of the Hun river, 25 miles east of Xiukden, consists of a long narrow valley, running east and west between hills composed of granitic and volcanic rocks. At the foot of the northern hills, the Hun river flows westward towards the Liao river, which drains the greater part of South Manchuria. At the foot of the southern hills, resting immediately upon volcanic rocks, and overlain by 30 ft. of alluvium, is a thick layer of Tertiary shales, carrying near the base two coal-seams. In many places the lower of these two seams is in immediate contact with volcanic lavas and basalts, the flows of which were evidently both prior and subsequent to the formation of the coal-seams. This contact has practically destroyed the lower seam for commercial purposes. The value of the field lies in the upper seam, which, for a length of nearly 8 miles, varies from 100 to 130 ft. thick. Of this seam, 85 per cent. is good coal. The seam dips to the north conformably with the shales, at angles of from 25 to 30°, and appears to have an uninterrupted dip for about 1.5 miles before being possibly cut oft' by the northern hills. The coal-bearing shales extend east and west for a length of about SO miles, but towards the east the continuity of the seams is broken by intrusive rocks. The coal is of the sub-bituminous variety, low in ash, bright in appearance, and breaks with a conchoidal fracture. It has the usual qualities of Tertiary coal—quick steam-raising and poor stacking qualities. Pieces of resin, varging in size from

Jan 1, 1911

By E. A. Stephenson

In spite of tremendous handicaps notable advances in production engineering have been achieved during 1932. The technique of deep well drilling has continued to progress, notably in California and at Big Lake, Texas. In the latter field a method has been devised by which two grades of oil in contact with each other are produced without intermingling. In rig design many improvements have been made whose objective is to facilitate deep drilling with reduced power losses and increased life of the equipment. Flush joint casing and drill pipe have been improved further, careful tests indicating that the drilling time can be reduced by from 5 to 20 per cent where flush-joint pipe is used. Slow-speed pumping has come into wider use, with further increases in over-all efficiencies. A number of improved well pumps also have been developed and are being tested. One of the most important of these is a positive displacement pump of the rotary type, directly connected to an electric motor placed in the bottom of the hole, and adaptable to various sizes of tubing and casing. In some localities the trend is towards the replacement of electric motors and large-cylinder engines by multiple-cylinder gas engines. Experiments have been conducted and critical analyses made of flow conditions in wells equipped with various styles of tubing which give promise that tubing may be designed to fit individual well conditions. In those wells producing at less than maximum capacity, the gas-oil ratio has been shown to depend on the rate rather than on the method of production, or the design of equipment. Important factors in the design of screened pipe have been carefully analyzed and made the basis of a method for determining the required mesh. Remarkable progress has been made in the use of subsurface pressure data. In East Texas particularly, use of such data is providing a means for the control and equalization of water encroachment and is also pointing the way to a sound means of allocating to individual tracts an

Jan 1, 1933

By D. R. Uhlmann, T. P. Seward, O. Chalmers

A magnetic field has been used to damp out liquid convection during the solidification of castings. Ingots of Al-2 pct Cu were poured from various sperheats (10" to 65°C) into a room-temperature graphite mold located between the poles of an electromagnet. The effect on ingot structure of varying the strength and time of application of the magnetic field was investigated, and the results are interpreted in light 01- current theories of ingot structure. In the solidification of alloy systems, thermal gradients in the melt and differences in density of the constituents are expected to produce convective motion in the liquid. The thermal convection caused by temperature gradients should be present during the freezing of both alloys and pure materials, while the solute convection caused by density differences should be of concern only for alloys. The possible influence of this natural convection on the structure of castings has been discussed by Ruddle,' Chalmers, and Tiller. More recently, an experimental investigation of such effects was carried out by Cole and Bolling. These workers took stationary molds containing lead- and tin-based alloys and. using a brine solution. quenched them from various superheats above their respective liquidus temperatures. When grids were placed across the mold diameter to suppress convection, the grid region was later observed to contain a larger percentage of columnar grains than other parts of the casting or than similar castings poured without the grids present. From thermocouple measurements, they found the temperature in the grid region to be higher than that in the region outside the grids throughout the freezing process, and concluded that convection should be an important mode of heat transfer in normal castings. In addition to such convection arising from thermal gradients or differences in density of the constituents, a further source of convective motion, which we shall call "momentum convection", may be particularly important in small (laboratory-size) castings. By this term we refer to the convective motion produced in the initial pouring process, a motion which is damped out as the linear momentum and angular momentum of the liquid are dissipated. Besides these sources of convection, which are present to some extent in all castings. external influences may also be effective in producing convective motion. Examples of such "forced" convection which have been discussed in the literature include stirring the melt, shaking the mold, rotating the mold, and so forth The purpose of the present study was to examine the effect of convection on the structure of castings poured into a cold mold. In this work, a magnetic field was employed to damp out the convective motions within the liquid, and hence control the extent of con- The effect of a magnetic field on convective currents in a conducting liquid is to induce eddy currents which oppose and damp out the convective motion. vection. The technique of magnetic damping was previously used by Utech and F1emings" in their study of convective effects on impurity banding and other substructure in alloy crystals grown unidirectionally from the melt. In their investigation, fields as small as 200 gauss were found to be effective in damping the convection currents which influence the banding. I) EXPERIMENTAL TECHNIQUE In the present study, alloys of A1-2 wt pct Cu were poured into a room-temperature graphite mold. The mold, in the shape of a circular cylinder, 2 in. ID, 2-3/4 in. OD, 5 in. inside height, and 5-1/2 in. outside

Jan 1, 1967

By K. T. Aust

It is proposed that the intergranular corrosion of austenitic stainless steels is associated with the presence of continuous grain houndary paths of either second phase, or solute segregate resulting from solute-vacancy interactions. Experimental observations of structural changes and crrosion behavior of different types of austenitic stainless steel provide support for this poposal. On the basis of this model, it is shown that the intergranular -corrosion susceptibility of austenitic stainless steels in nitric-dic hromate solution may be substantially reduced either by suitable heat treatments or by impurity control. AUSTENITIC stainless steels, such as Type 304, generally have excellent corrosion resistant properties when properly solution heat-treated and used at temperatures where carbide precipitation is slow. However, several corrosion environments have been found which produce intergranular corrosion of solu-tion-treated stainless steels, that is, those steels with no detectable carbide precipitation.''2 Of the various corrosion environments, the most widely used test solution has been the boiling nitric-dichromate solution. In these acid solutions, stainless steels have been found to be susceptible to intergranular attack despite the addition of carbide-forming elements such as titanium or columbium, or despite lowering of the carbon content or use of high-temperature solution treatments. Studies of the electrochemical mechanism of corrosion attack have been made by several worke1s3'4 who found that oxidizing ions such as crt6 depolarize the cathodic reactions and consequently raise the open-circuit potential of stainless steel immersed in nitric acids. As a result of this, the anodic reaction is accelerated. The reason for the localization of anodic activity at the grain boundaries, and resulting intergranular corrosion, has not been conclusively determined. Several workers, e.g., Streicher,3 and Coriou et al.,4 have suggested that the strain energy associated with grain boundaries provides the driving force for the accelerated intergranular corrosion. This argument would predict that alloys of high purity would still be susceptible to intergranular attack. However, work by chaudron5 and by ArmijO,6 has shown that high-purity alloys are immune to attack, in disagreement with this argument. An alternative suggestion is that chemical concentration differences exist between grains and grain boundaries, that is, impurity segregation at boundaries, and that these chemical differences provide the driving force for localized attack. It is this impurity segregation which can lead to accelerated dissolution of grain boundaries when the alloy is exposed to a suitable corrodant. This mechanism would predict the immunity of high-purity alloys to inter-granular attack, which is in agreement with experi-mental observations. In the present paper, some recent studies on inter-granular corrosion of austenitic stainless steels which were conducted by coworkers and myself will be re-tibility A simple model will be described in which it is proposed that the intergranular corrosion of aus-tenitic stainless steel is associated with the presence of continuous grain boundary paths of either second phase or solute-segregated regions.* On the basis of this model, it is suggested that the intergranular corrosion rate can be markedly reduced by the formation of a discontinuous second phase at the grain boundaries if the discontinuous second phase incorporates the major part of the segregating solute, drained from the grain boundary region. Results are presented of corrosion tests and electron microscopic studies of different types of austenitic stainless steel after various heat treatments which provide experimental support for this model. Finally, a solute clustering mechanism, based on a solute-vacancy interaction, is shown to be consistent with the results obtained for inter-granular corrosion of solution-treated austenitic stainless steels. EXPERIMENTAL Corrosion tests using weight loss measurements were made on sheet specimens, which were lightly electropolished, washed, and immersed in boiling (115°C) 5 N HN03 containing 4 g crt+6 per liter added as potassium dichromate. Studies in which the inter-granular penetration depth was measured both by electrical resistance and metallographic methods have shown an empirical correlation between the rate of intergranular penetration and the weight loss per unit time for identically treated specimens of stainless steel." As a result, although all the corrosion data reported here are in terms of simple weight loss measurements, these data are considered to reflect primarily the rate of intergranular dissolution. Fig. 1 shows a typical result of intergranular attack of a solution-treated Type 304 stainless steel after 4 hr in a boiling nitric-dichromate solution. The wide grain boundary grooving at the surface, and the attack at incoherent twin boundaries, are evident; very little corrosion attack is seen at the coherent twin boundaries. INTERGRANULAR CORROSION MODEL

Jan 1, 1970

By N. J. Grant, B. C. Giessen, R. Koch

The system Nh-Ir was investigated over the complete concentration range by metallography and X-my techniques, using forty one alloys. The solubility limits of terminal and intermediate phases and the solidus temperatures were determined. Five intermediate phases were found: a Nb3Ir, cubic, Cr3O type; tetragonal, ofecr thorhomhic, isostruc-turn1 with (ta-Rh); and a Nhlr3. cubic, AuCu, type. a Nb3lr and a Nbfr3 melt congruently; three eutectic and three pentectic reactions occur. The phase diagram of the Nb-Ir system had not been fully treated in the literature; only surveys of intermediate phases were found.1"5 In this study, the details of the phase boundaries were investigated as well as the crystallography of the intermediate phases. EXPERIMENTAL METHODS The experimental procedures such as arc melting of powder compacts, heat treatments, solidus measurements, X-ray, and metallographic observation were identical with those used in the work on the Nb-Rh phase diagram.&apos; They will therefore not be repeated here except where the conditions differed. The purity of the niobium powder was as stated in Ref. 6; the iridium powder of 99.9+ pct purity from J. Bishop and Co., Malvern, Penn., did not contain impurities exceeding 100 ppm, except rhodium (200 ppm). The melting points and vapor pressures of both elements are very similar. This fact contributed to a very small weight loss on melting and facilitated preparation of homogeneous alloys. As shown in Ref. 6 for Nb-Rh, no oxygen pick-up exceeding 200 ppm had to be considered; this was regarded as valid also for Nb-Ir. A total of forty one alloys were used in the determination of the phase diagram; their concentrations are shown in Fig. l, which presents the phase diagram. The concentration limits as determined by the weight-loss method averaged <0.2 at. pct, and never exceeded 0.5 at. pct. Heat treatments were carried out as described in Ref. 6. Depending on the concentration, only tantalum, tungsten, or iridium containers were employed, avoiding oxide crucibles altogether. Alloys from 0 to 25 and from 65 to 100 at. pct Ir were homogenized at 2095°C for 15 hr, intermediate compositions from 25 to 65 at. pct Ir for 65 hr at 1780°C. A typical annealing-time schedule is presented in Table I. Solidus points were measured as described in Ref. 6 with the modification that samples rich in niobium were held between pieces of tantalum foil and samples of high iridium concentrations were held between rhenium platelets or in iridium wire. After each run it was ascertained metallographically that no reaction with the holder had occurred. Rhenium was selected as holder material after it had been shown in separate tests that the melting points of Re-Ir alloys rise continuously from 2440°C. Metallographic examination was carried out as described in Ref. 6, and the same procedure and etchants were used successfully. While metallographic discrimination between a Nb3lr and o was easily possible, X-ray diffraction was necessary to separate al and ct2. X-ray powder patterns were taken and evaluated as for Nb-Rh6 yielding the error limits indicated in Table 111, to be introduced later. For the determination of the invariant reactions and phase boundaries, the same techniques as for Nb-Rh6 applied. The general accuracy of invariant concentrations is regarded as somewhat higher than for Nb-Rh due to the small slope of most solvus lines.

Jan 1, 1964

By D. C. Hilty

It has long been known that in melting high-chromium steels, some of the carbon might be oxidized out of the melt without excessive simultaneous oxidation of chromium, and that higher temperatures favor retention of chromium. The advent of oxygen injection as a tool for rapid decarburization of a steel bath permits significantly higher bath temperatures, and it was quickly recognized that the use of oxygen injection facilitated the oxidation of carbon to low levels in the presence of relatively high residual chromium contents. Up to the present time, however, specific data pertaining to the chro-mium-carbon-temperature relations in chromium steel refining have not been available. Individual steelmakers have evolved practices more or less empirically, but there has been very little real basis for predicting how effective any given practice can be in permitting maximum oxidation of carbon with minimum loss of chromium. The current investigation, therefore, was undertaken in an effort to establish the fundamental carbon-chromium relationship in molten iron under oxidizing conditions. As reported below, the equilibrium constant and the influence of temperature on that constant have been derived for the iron-chromium-carbon-oxygen reaction in the range of chromium steel compositions with what appears to be a fair degree of precision. The practical application of the result will be obvious. Experimental Procedure The laboratory investigation was carried out on chromium steel heats melted in a magnesia crucible in a 100-lb capacity induction furnace at the Union Carbide and Carbon Re- search Laboratories. The charges for the heats consisted of Armco iron, low-carbon chromium metal, and high-carbon chromium metal, the relative proportions of which were calculated so that the various heats would contain from approximately 0.06 pct carbon and 8 pct chromium to 0.40 pct carbon and 30 pct chromium at melt-down. When the charges were melted, the bath temperatures were raised to the desired level, and the heats were then decarburized by successive injections of oxygen at the slag-metal interface through a ½-in. diam silica tube at a pressure of 30 psi. The duration of the oxygen injections was from 30 sec to 2 min. at intervals of approximately 5 to 30 min. It did not appear that length or frequency of the injection periods had any significant effect on the results; cansequently, no effort was made to hold them constant and they were controlled only as was expedient to the general working of the heats. Between successive injections, the heats were sampled by means of a copper suction-tube sampler that yields a sound, rapidly-solidified sample representative of the composition of the molten metal at the temperature of sampling. This sampling device is a modification of the one described by Taylor and Chipman.1 An attempt was made to vary bath temperatures between samples, but it quickly became evident that, unless the variations were small or unless the new temperature was maintained for a minimum of 15 min. during which an injection of oxygen was made in order to accelerate the reactions, a very wide departure from equilibrium resulted. For most of the runs, therefore, temperature was maintained relatively constant at approximately 1750 or 1820°C. A few reliable observations at other temperatures, however, were obtained. Temperature Measurement The high temperatures involved in this investigation were measured by the radiation method, utilizing a Ray-O-Tube focused on the closed end of a refractory tube immersed in the metal bath. The immersion tubes employed were high-purity alumina tubes specially prepared by the Tona-wanda Laboratory of The Linde Air Products Co. These tubes were quite sturdy under reasonable mechanical stress at high temperature. They were unusually resistant to thermal shock, and chemical attack on them by the melts was slow. With care, it was found possible to keep these tubes continuously immersed in a heat for as long as 5 hr at temperatures up to 1850°C, before failure by fluxing occurred. The Ray-O-Tube—alumina tube assemblage was similar to those supplied commercially for lower temperature applications. In operation, the alumina tube was slowly immersed in the molten metal to a depth of approximately 5 in., and the device was then clamped solidly to a supporting jig where it remained for the duration of the run. A photograph of the equipment, in operation with Ray-O-Tube in place and oxygen injection in progress, is shown in Fig 1. When in position in a heat, the instrument was calibrated by means of an immersion thermocouple and an optical pyrometer. For calibration through the range of temperatures from 1500 to 1650°C, a platinum -platinum + 10 pct rhodium thermocouple in a silica tube was immersed alongside the alumina tube. Output of the Ray-O-Tube in millivolts and the

Jan 1, 1950

By F. W. Glaser

Metal-carbon-boron powder mixtures were hot pressed and the resulting specimens were studied by X-ray diffraction. It was found that regardless of the starting combination of the metal, carbon, or boron powders, a metal boride phase was always the major component in these samples. In the absence of carbon the boride phase formed on hot pressing depended only on the amount of boron present. Two new phases of the system Ti-B were found. They are Ti2B and Ti2B5. The existence of a controversial face-centered cubic phase of formula TiB was confirmed. Electrical resistivities were measured for various boride phases. It was found that the diborides are generally better conductors than the monoborides of the same metal. THE carbides and borides of the transition elements have very high melting points, in the range 2500° to 4000°C, and are therefore of interest as high temperature materials. The literature on the stability or chemical reactivity of these carbides and borides is very scarce. Various investigators&apos;-" have demonstrated a relative instability of certain carbide phases in the presence of boron or boron-containing substances. In a recent publication, Glaserl demonstrated the stability of zirconium-boride (ZrB,) in the presence of carbon at temperatures in excess of approximately 2900°C, while during a preliminary investigation of boride phases, Steinitz&apos; concluded that the diborides are stable in the presence of carbon while the monoborides of the fourth and fifth group are not, forming diborides plus carbides instead. Nelson, Willmore, and Womeldorph" have elaborated on the reaction B,C + 2TiC = 2TiB, + 3C, which was known to occur because of a relative instability of B,C and the great tendency towards TiB, formation at relatively low temperatures (approximately 1200°C). A similar study, involving as starting materials TiO, and B,C and resulting in TiB,, was recently described by Honak4, who observed the beginning of an exothermic reaction of a Ti0,-B,C powder mixture, which, when preheated in a hydrogen atmosphere to approximately 950°C, was carried to about 1600 °C by the heat of reaction. To shed more light on reactions of this type (Metal-C-B), the final product apparently always resulting in a boride phase at the expense of a carbide phase," a systematic investigation was started * Boride phases of various metals, as reported to date, are listed in Table I. and the following is an account of some of the results that were obtained. Materials, Preparation of Samples, Testing Methods The raw materials employed for this work consisted of various carbide, boride, and metal powders. as well as of boron and graphite powders. In cases where commercial grades of carbides were considered unsuitable because of low purity or excessive amounts of graphitic carbon, such carbide powders were prepared by this laboratory. The procedure for the preparation of carbide powders (zirconium carbide, titanium carbide, tantalum carbide, and niobium carbide) consisted of mixing graphite and the respective metal hydride powders in stoichio-metric proportions and subsequent heating of such mixtures in a hydrogen atmosphere in carbon crucibles. The heating was by high frequency to temperatures ranging between 1700" and 2100°C. The resulting carbide was then comminuted and screened to the desired particle size. ZrB, and TiB, powders were produced by the electrolysis of fused salt baths, according to the method described by Andriex.. The borides of niobium, vanadium, tantalum, molybdenum, chro-ium, and iron were obtained by mixing the respective metal and boron powders in the desired proportions. Such metal-boron mixtures were heated in a high frequency furnace to form boride powders. For each metal-carbon-boron group (Tables I1 through XI) a metal, its hydride, carbide or boride were mixed with carbon, boron or boron carbide powders. The additions of carbon, boron or boron carbide powders to any of these metals or metal compounds were calculated to satisfy a particular carbide or boride phase that according to the literature (Table I) had definitely been established by X-ray diffraction work. Samples of powder mixtures were hot pressed in graphite molds that were heated by direct conduction. The specimen dimensions were approximately 2.5X1X1 cm. Hot pressing temperatures were measured optically and maintained for approximately 30 sec under a constant pressure of about 1.3 ton per sq in. Wherever possible, an attempt to obtain maximum specimen density was made by temperature variation. Electrical resistivity testing was done by measuring potentiometrically the voltage drop over a length of 1.5 cm for a current of 10 amp, at room temperature. To obtain electrical resistivities for specific carbide or boride phases, values were plotted as a function of the respective sample densities

Jan 1, 1953

By Robin O. Williams

Robin 0. Williams (Oak Ridge National Laboratory)— The authors have questioned the degree to which the coherency strains between the iron-rich and chromium-rich phases are isotropic as proposed in Ref. 5 on the basis of the difference between the elastic properties of the two phases. The relative magnitude of the stresses is determined by the moduli as shown by Eqs. [2], [3], and [4] of Ref. 34. However, the moduli of the two phases have no direct bearing on the uniformity of either the stress or strain within either phase. The idea that the strains are isotropic within each phase (but normally of different magnitude and always of different sign) is based entirely upon the experimental observation that X-ray line broadening has not been detected even when the particles become rather large. It has not proven possible to grow the particles sufficiently large that they lose coherency. Based upon this lack of line broadening one can estimate an upper limit for the nonuniformity of the strains within each phase as follows. It is considered possible to detect line broadening if it is as great as 10 pct of the separation of the K, doublet for the (211) line using chromium radiation. The doublet separation would correspond to a total strain of 0.0017 such that the total variation of lattice parameter relative to the average lattice is now k0.05x0.0017 or something less than ± * For the present case the strain in each phase is roughly 0.002 such that the variation of strain within a phase will not exceed 5 pct. It is stated that the expression derived for strengthening for the hydrostatic straining as observed in this system would substantially overestimate the magnitude due to dislocation flexure. This is contrary to the conclusion reached in the original paper34 for the present range of particle sizes. What is the lowest temperature at which a has been observed to form in this alloy? M. J. Marcinkowski, R. M. Fisher, and A. Szirmae (nutlzors&apos; reply)— -Williams&apos; arguments based on X-ray findings for a chromium-rich precipitate and an iron-rich matrix strained to a common lattice parameter are certainly convincing. This being the case, there are no shear components of strain associated with the precipitate-matrix aggregate to interact with the shear components of the dislocation stress fields, contrary to the opinion expressed by the present authors. On the other hand, the present authors, in spite of this error, did not expect the shear interactions to be significant. The chief objection to Williams&apos; model in the present case is that the various segments of the dislocation line are assumed to pass from one potential valley to the next independently of neighboring segments. This is only true for a highly flexible dislocation line, i.e., one whose radius of curvature is something less than the center to center distance between precipitate particles which amounts to about 90A in the present alloy. In order to maintain this curvature, an externally applied shear stress of at least 230,000 lb per sq in. would be required or about four times the observed stress. It is therefore concluded that the dislocation lines move rather rigidly through the lattice. This being the case, the forces on the dislocation resulting from the hydrostatic interaction between the stress fields of the edge-dislocation components and the precipitate particles should average out to zero; that is particles above the below the slip plane produce forces on the dislocation of opposite sign and therefore will cancel when averaged over the entire length of the dislocation. On the other hand, since the dislocation is not perfectly rigid, Williams&apos; model may lead to some strengthening, but far less than that predicted. A second and equally serious objective to using Williams&apos; strengthening model for the present alloys is that profuse wavy slip due to the motion of screw dislocations played a predominant role not only in the unaged alloys but in the fully aged ones as well. Since the screw dislocation has associated with it only shear components of stress the hydrostatic strengthening model no longer applies. In view of these arguments the present authors must reject Williams&apos; model of strengthening as being pertinent to the present alloy system. The present authors have made no detailed study of the lowest temperature at which a forms in the quenched ferritic alloys. None was ever observed n the alloys aged at 500°C so that forma-tion must occur at temperatures higher than this and was therefore not a factor in the present study.

Jan 1, 1965

By Dr. O’Neil Thomas J., Donald W. Gentry

Money is like an arm or leg-use it or lose it." -Henry Ford INTRODUCTION If it were not for the existence of interest, the analysis of investment opportunities would be greatly simplified. In the absence of interest, investors would be indifferent as to when cash outlays are made or cash benefits are received. It would, in fact, be irrelevant whether the outlays preceded or followed inflows as long as both amounts are known with certainty. Of course, it does make a considerable difference whether, for example, a firm receives $1 million now or five years from now. The reason is that money does, indeed, have a value which is a function of time. Interest is how this time value is measured. Interest is generally defined as money paid for the use of borrowed money. In other words, interest is the rental charge for using an asset over some specific time period. The rate of interest is the ratio of the interest chargeable at the end of a specific period of time to the money owed, or borrowed, at the beginning of that period. In order to understand why interest exists, it is necessary to take the lender&apos;s viewpoint. The lender can justify charging interest for several reasons: 1) Risk: The lender is faced with the possibility that the borrower will be unable to repay the loan. 2) Inflation: Money repaid in the future will be in units of lower value due to inflation. 3) Transactions Cost: There will be expense incurred in preparing the loan agreement, recording payments, collecting the loan, and other administrative tasks. 4) Opportunity Cost: By committing limited funds to one borrower, a lender is unable to take advantage of other available opportunities. 5) Postponement of Pleasure: By lending money, an individual (or organization) is postponing the pleasure which that money could purchase. Each of these is a valid reason for a lender demanding interest from a borrower. The level of interest is, like the price of other assets, determined by supply and demand. Nonetheless, from time to time various analysts have taken a then current average interest rate and broken it down into the components described previously.

Jan 1, 1984

By G. S. Rice

IT is evident from Professor Louis&apos; remarks that he holds a different opinion on certain phenomena connected with a specific type of surface subsidence from mining than is held by many engineers in the United States. The question which appears to be at issue is whether or not the line or plane of "draw" produced in ground movement resulting from extraction of pillars may, under certain conditions, be vertical or even inclined toward the workings rather than inclined for- ward over the unworked mineral, as it is universally agreed occurs in mining by the longwall advancing method. In discussing this case it is well to take the simplest condition, such as specified by Professor Louis, of a flat bed, whether it be coal, iron or other mineral, where the overburden is stratified rock and where there is no overlying quicksand. Professor Louis says in effect that his experience is that the ultimate angle of draw is always positive and inclined 5" to 15" from the perpendicular over the unwrought mineral. My experience under Illinois coal-mining conditions is that .&apos;where longwall advancing is used the draw is always positive as Professor Louis describes it, but that in extracting of panels by withdrawal of pillars, the ground movement is manifested, after the first roof&apos; beam break, by the forming of an unstable dome over the goave. Then subsequently, by the falling of individual slabs from the under side, the dome gets larger and higher until it breaks through to the surface of the rock., Up to this time, arch stresses buttress the rocks above the solid coal or mineral. When, however, after. the dome breaks through and the central hole - #enlarges so the arch is no longer sufficiently supported -the stratified rocks cantilever out .from over the solid unworked mineral and tend to break off in masses triangular in vertical cross-section, until the broken loose material, sliding down against the solid rock, .has such a thrust that it balances the tendency ,for the solid stratified rock to break away and slide toward the excavation.

Jan 1, 1929

By L. R. Jackson

THE idea presented in this paper is that the capacity of a metal for plastic flow before rupture is dependent on the type of stress system applied-that is, the absolute magnitude of the stresses are unimportant provided that they are large enough to produce continued flow; the important factor is the "type" of stress system. A term called the "triaxial stress ratio" is defined in such a way that this ratio can be used to characterize the "type" of system. The paper is divided into three sections. The first section discusses means of representing the effect of complex stresses on plastic flow and defines "triaxial stress ratio"; the second section discusses various methods of&apos; obtaining complex stress distribution. The third section gives some experimental results showing the effect of types of complex stress on the capacity of various metals for flow. An appendix discusses some details on methods of obtaining complex stresses. I. REPRESENTATION OF COMPLEX STRESS SYSTEMS AND THEIR EFFECT ON PLASTIC FLOW Representation of Stresses It is convenient to have a consistent system of notation that will allow the representation of the entire range of complex stresses from hydrostatic compression to hydrostatic tension on plastic flow in a single diagram. Such a system is provided by making use of the fact that any complex stress system can be resolved into a hydrostatic tension or compression and a pure shear. Consider a stress system having the principal stresses [S1 S2 5 S3]. This system can be resolved into a new system consisting of the three components [ ] and three pure shears. If Sm is positive, the net stress effect is hydrostatic tension; if it is negative, the effect is hydrostatic compression. In order to produce a systematic notation, a quantity that will be referred to as the "triaxial ratio" will be defined by the equation [ ] Sm is given by Eq. I and S1 is the absolute magnitude of the largest principal stress without regard to sign. Table I lists the triaxial ratios for various common systems. [ ] Representation of Strains Strains will be plotted as "true" strains according to the system proposed by Ludwik.1

Jan 1, 1944

By Charles Pack

Die castings may be defined as metal castings made by forcing molten metal, under pressure, into a metallic mold or die. It is necessary to keep this definition in mind to avoid confusing this process with other permanent-mold casting processes. The fundamental principles of the process have been known and practised many years. The simplest application is embodied in the modern linotype machine in which molten metal (usually tin-lead alloy) is forced under pressure into a metallic mold. The pressure is derived from a piston and cylinder immersed in the molten metal. Progress in the art of die casting may conveniently be divided into three groups: Machine for imparting pressure to the metal, material for the die or mold, casting alloys. The problem of delivering molten metal under pressure into a die is comparatively simple, when dealing with low-fusing-point alloys, as the alloys of lead and tin, but it is much more complicated when dealing with metals of higher fusing points, such as the alloys of zinc, aluminum, and copper. Although the art of die casting is comparatively new and, to a large extent, unknown, the records of the patent office are replete with patents on the subject. Fig. 1 shows the Underwood machine patented in 1902; this is probably one of the first machines designed for the production of commercial die castings. The relation of this machine to the linotype casting machine is clearly apparent. A cylinder and piston are immersed in the molten metal, the application of power to this piston forcing the molten metal, under pressure, into the mold or die. The Doehler machine, Fig. 2, patented in 1907, is based on the same general principles. This machine is used to a large extent at the present time, throughout the United States, for the production of zinc, tin, and lead alloy die castings. In the machine shown in Fig. 3, patented by Doehler in 1910, compressed air is used for forcing the metal into the die. In Fig. 4 is shown another of this type of machine. Here compressed air is applied to the surface of the molten metal to force it into the die. In a machine patented by Chandler in 1914, shown in Fig. 5, the

Jan 1, 1919

By L. Valentik

Many attempts have been made during the last 40 years to evaluate the performance of gravity separation equipement, that is, the effectiveness with which light and heavy particles are separated. The most comprehensive treatment of the subject was made by Cerchar at the 1st International Conference on Coal Preparation held in Paris in 1950. The methods suggested by the Conference were accepted and very widely used in the last two decades. This paper discusses an improved method of evaluation in the light of the now-accepted standard presentation. The float-and-sink analysis of the product is presented on a Gaussian distribution curve, resulting in an easier visualization of the inherent difficulties of separation. The ogives of the distribution curve me then plotted, giving a quantitative measure of the deviation from perfect separation as an error distance instead of an error area. Illustrations of the new method are given both for gravel and for coal preparation, but the content is valid and applicable to other types of minerals which are separated by gravity methods. Many attempts had been made during the last forty years to evaluate the performance of heavy-media separation (HMS) equipment, that is, the effectiveness with which floats and sinks are separated.&apos;-&apos; The most comprehensive treatment of the subject was made by Cerchar at the 1st International Conference on Coal Preparation held in Paris. 6 The primary aim was the thorough understanding of the mechanism of separation and the unified presentation of data on gravity separation so that the evaluation and comparison of washery performance could be made from all over the world. No strict overall standardization has been achieved, but after the conference a more or less uniform presentation of performance was accepted, which, during the last two decades, has been very widely used. In this paper, illustration of the old methods and an improved method of evaluation will be given. HEAVY-MEDIA SEPARATION (HMS) PERFORMANCE CRITERIA In the ideal HMS process, all material lower in density than the specific gravity of separation (SGS) would be recovered as floats and all material of higher density would appear as sinks. In order to evaluate the misplaced material, the washery products are tested at the density at which the washing unit is operated. The original type of plot1,7, 8 is shown in Fig 1; this was developed primarily for coal cleaning units. The curve for raw coal represents the cumulative percentages of sink material. The refuse curve is also plotted as a cumulative sink, the percentages being expressed in terms of raw coal. This diagrammatic representation of the results of washing units has the merit of easy visual observance of the degree of separation obtained. The error areas (cross-hatched) are a measure of the amount of misplaced material and therefore they can be used to characterize the quality of separation. The ideal and actual separating performance between floats and sinks can be best seen from the partition curve developed by Tromp,2 where the ordinate is the percentage recovery of the sinks, and the abscissa is the specific gravity (Fig. 2). It can be seen from the shape of the curve that as the SGS is approached, the proportion of material reporting to the improper product increases rapidly. In fact, the SGS can be defined as the density of the material in the feed that is distributed equally between float-and-sink products. When the upper half of the curve is inverted, a shape similar to that of a Gaussian error distribution curve is obtained and therefore the analysis of gravity separation may be carried out by using the law of probability. The shape of the curve in Fig. 2 is determined partly by the density composition of the feed, and partly by the sharpness with which the unit separates floats from the sinks.9, l0

Jan 1, 1970

By G. T. Murray

The aging behavior of a Cu-Ti (3.2 at. pct Ti) alloy has been followed by electrical resistivity, hardness, and metallographic changes. The resistivity data indicate two principal processes, the first causing a sharp decrease in resistivity, and the second, which occurs over a long period of time, a much smaller rate of decrease. Lamellar nodules, Widmanstätten platelets, and homogeneous continuous precipitation was observed. The Widmanstätten platelets grow at the expense of the latter. When this study was initiated, little information was available on the aging behavior of copper-base titanium alloys. Several articles&apos;-3 that appeared in the early 1930&apos;s showed that these alloys could be strengthened by precipitation, but a detailed study was not made. Within the past year, however, two other more comprehensive studies4&apos;5 have been reported in the literature, one consisting primarily of an investigation of mechanical properties, the other

Jan 1, 1961

By P. J. Root, J. E. Warren

An idealized model has been developed for the purpose of studying the characteristic behavior of a permeable medium which contains regions which contribute significantly to the pore volume of the system but contribute negligibly to the flow capacity; e.g., a naturally fractured or vugular reservoir. Unsteady-state flow in this model reservoir has been investigated analytically. The pressure build-up performance has been examined in some detail; and, a technique for analyzing the build-up data to evaluate the desired parameters has been suggested. The use of this approach in the interpretation of field data has been discussed. As a result of this study, the following general conclusions can be drawn: 1. Two parameters are sufficient to characterize the deviation of the behavior of a medium with "double porositym from that of a homogeneously porous medium. 2. These parameters can be evaluated by the proper analysis of pressure build-up data obtained from adequately designed tests. 3. Since the build-up curve associated with this type of porous system is similar to that obtained from a stratified reservoir, an unambiguous interpretation is not possible without additional information. 4. Differencing methods which utilize pressure data from the final stages of a build-up test should be used with extreme caution. INTRODUCTION In order to plan a sound exploitation program or a successful secondary-recovery project, sufficient reliable information concerning the nature of the reservoir-fluid system must be available. Since it is evident that an adequate description of the reservoir rock is necessary if this condition is to be fulfilled, the present investigation was undertaken for the purpose of improving the fluid-flow characterization, based on normally available data, of a particular porous medium. DISCUSSION OF THE PROBLEM For many years it was widely assumed that, for the purpose of making engineering studies, two param- eters were sufficient to describe the single-phase flow properties of a producing formation, i.e., the absolute permeability and the effective porosity. It later became evident that the concept of directional permeability was of more than academic interest; consequently, the degree of permeability anisotropy and the orientation of the principal axes of permeability were accepted as basic parameters governing reservoir performance. 1,2 More recently, 3-6 it was recognized that at least one additional parameter was required to depict the behavior of a porous system containing regions which contributed significantly to the pore volume but contributed negligibly to the flow capacity. Microscopically, these regions could be "dead-end" or "storage" pores or, macroscopi-cally, they could be discrete volumes of low-permeability matrix rock combined with natural fissures in a reservoir. It is obvious that some provision for the inclusion of all the indicated parameters, as well as their spatial variations, must be made if a truly useful, conceptual model of a reservoir is to be developed. A dichotomy of the internal voids of reservoir rocks has been suggested.7,8 These two classes of porosity can be described as follows: a. Primary porosity is intergranular and controlled by deposition and lithification. It is highly interconnected and usually can be correlated with permeability since it is largely dependent on the geometry, size distribution and spatial distribution of the grains. The void systems of sands, sandstones and oolitic limestones are typical of this type. b. Secondary porosity is foramenular and is controlled by fracturing, jointing and/or solution in circulating water although it may be modified by infilling as a result of precipitation. It is not highly interconnected and usually cannot be correlated with permeability. Solution channels or vugular voids developed during weathering or burial in sedimentary basins are indigenous to carbonate rocks such as limestones or dolomites. Joints or fissures which occur in massive, extensive formations composed of shale, siltstone, schist, limestone or dolomite are generally vertical, and they are ascribed to tensional failure during mechanical deformation (the permeability associated with this type of void system is often anisotropic). Shrinkage cracks are the result

By H. W. McCue

In 1944, in the Texas Panhandle, 245 oil wells were drilled with a total daily initial production of 32,886 bbl., representing an average initial production of 134 bbl, per well. This was an increase over 1943 of 121 wells drilled, and an increased initial production of 13,861 barrels. On Dec. 31, 1944, the field was operating on an allowable of 113,567 bbl. per day, but actually was producing 85,539 bbl. per day from the 5901 oil wells. The tota1 production for the year was 33,439,436 bbl., bringing the cumulative total to 5.04,537,048 barrels. Gas Sixty-three gas wells with a combined open flow of 992 million cu. ft., were drilled during 1944. This was an increase of seven wells over 1943, but a drop of 216 million cu. ft. in initial open flow. The

Jan 1, 1945