By E. A. Smith, E. R. Parker

METALLURGISTS and engineers have always been interested in the mechanism of high-speed deformation because metals are rapidly deformed in various applications and manufacturing processes. The deformation of metals by impact loads has recently engaged the attention of a number of investigators. Many of their results have not been disclosed but some of the published investigations1-8 have shown that the tensile strength, yield strength and elongation generally increase with increasing strain rate. The investigation reported herein is an attempt to determine the reason for this increase in strength and elongation. Single-crystal copper specimens were broken in tension at impact velocities up to 100 ft. per sec. The distribution of slip bands in the fractured crystals was found to depend upon the strain rate. In the bars broken at high speeds, the slip bands appear to be more numerous. This might account for the higher strength as well as the greater elongation. EXPERIMENTAL PROCEDURE Single crystals of copper (approximately 99.98 per cent) were made in graphite molds by the conventional method of lowering the mold out of the hot zone of a hydrogen furnace at a rate of one inch per hour. Solidification progressed from the bottom upward, forming a single crystal. The crystals were about 0.30 in. in diameter and 4 in. long. They were made into test bars by sliding threaded steel bushings over each end of a crystal and then flowing silver solder between the crystal and the bushing. The inside diameter of the bushings was slightly greater than the diameter of the crystals, to allow space for the silver solder. The bushings were placed so that the gauge length of the crystals was one inch. The assembly is shown in Fig. I, with two views of a fractured crystal. Annealed polycrystalline copper bars of similar shape were machined from solid stock. X-ray measurements were made on all single crystals to determine their orienta¬tions. The results are shown in Fig. 2, where the location of the axis of each specimen is indicated on a standard projection. The bars were broken in a commercial variable-velocity tension im¬pact machine, which has been described in detail elsewhere.7,8 The stress and strain were recorded by means of wire strain gauges and a special commercial oscillo-raph, also described in detail elsewhere.9,10 The equipment and method can be briefly described as follows. The impact machine consists of a motor-driven flywheel containing a two-pronged hammer. This hammer is held retracted in the flywheel

Jan 1, 1944

JOHN W. BELL (communication to the Secretary*).-I have to thank Mr. Merrill not only for his very kind remarks, but for the weight of his implied opinion that the work accomplished probably has an important practical aspect. I think there is a distinct although unuttered impression among engineers, that it will be time enough for them to begin to take an interest in the law of crushing when it emerges from the cloud of violent and even vituperative controversy that has hovered over it during the last 6 or 7 years. I have a very confident feeling that as the result of the work done by Mr. Gates, by me and by Messrs. Mitchell, Baily and Cockfield, who so loyally helped me to obtain the necessary data, at least the practical law of crushing has emerged; that it is ready and available for use by our fellow engineers, and that it will help them to unravel a number of the many practical problems they are con¬stantly confronted with. In regard to Mr. Gates' discussion, I would indeed like to believe that McGill could claim, as a minor achievement, the credit which Mr. Gates so generously bestows of having established the "law" of crushing. I think that more work would be required to establish this claim in the, strict sense of the word, as there is a fairly large gap between the coarse and fine crushing results. I am not worried about that gap, because the reason for it is quite clear to me; at the same time I-think it will be well to bridge it by a series of tests, and I am bound to admit that the testing machine is the most promising machine right at hand to work with, although whether the minute amounts of power required to crush small quantities of rock can be so accurately integrated as to insure high accuracy in the final result is still a question in my mind. If we had an Amsler-Laffon machine I would certainly try it. Mr. Gates' remarks about choke crushing are extremely interesting. He compels me to wonder, too. It is a new and probably a very important factor to be considered in this connection. I am in perfect accord with Mr. Gates about the desirability of the determination of crushing constants, because when this is accomplished the efficiencies (not relative mechanical, but real efficiencies) of different types of rock-crushing plants in any part of the world will then be comparable. For this reason it would, seem desirable that the American Institute Committee should not only consider ways and means for accom-

Jan 6, 1917

By A. R. Elsea, E. E. Fletcher

Cast X-40 alloy with the lowest nitrogen content studied had a 100-hr rupture stress at 1500°F about equal to the reported value for the commercial alloy. Increases in nitrogen content progressively decreased the rupture strength, and with about 0.1 to 0.2 pct N a minimum strength was reached, but there was no accompanying change in microstructure. Further increases in nitrogen resulted in the fomzation of progressively increasing amounts of a lamellar, pearlitic-type structure at the grain boundaries, with accompanying increases in rupture strength, and above about 0.25 to 0.33 pct N, the rupture strength exceeded the normally reported values. Two series of melts representing different melting stocks exhibited minimum rupture strengths at different nitrogen contents. This suggests that some unidentwed trace element not removed by vacuum melting has a strong influence on the response of this alloy to variations in nitrogen content. In a series of melts with manganese contents ranging from 0.6 to 3.2 pct, the material with the lowest manganese content had the highest 100-hr rupture strength at 1500°F. The manganese variations had no appreciable effect on the microstructure. CAST cobalt-base alloys such as X-40* exhibit high strengths at elevated temperatures (1500°F and above), but they also show considerable scatter in high-temperature properties. Since the design of parts for critical applications must be based on the minimum expected properties, this broad scatter appreciably lowers the design strength of the alloy. If the relatively poor properties exhibited by a few test parts from any given group could be improved, the spread in properties would be narrowed, and the design stress could more closely approach the average expected properties. The purpose of this research investigation was to learn what were the causes of these erratic properties and, if possible, to find methods for eliminating them. Earlier unpublished work showed that vacuum melting markedly influenced the high-temperature strength of cast X-40 alloy. There were indications that this behavior may have been the result of changes in the nitrogen or manganese content of the castings. Consequently, in the current investigation, the influence of variations in nitrogen and manganese content on the structure and high-temperature properties of cast X-40 alloy was studied. In this program, X-40 melting stock was vacuum melted to produce a base material that was very low in nitrogen content and in volatile trace elements. Additions were then made to this base material to produce alloys of the desired composition. The metal was cast into investment molds producing coupons which were machined into stress-rupture bars. These bars were subjected to stress-rupture tests and me-tallographic study to determine the influence of changes in analyses (nitrogen and manganese content) on the structure and properties. Material—The melting stock used for these experi-ments was in the form of shot from two master heats of commercial X-40 alloy. Only one master heat was used in a given series of melts. Thus, any differences in structure or properties that showed up in the specimens from a given series would be the result only of the intended variations in composition. The certified analyses of the master heats were as follows: C Mn Si Cr Ni Lot No. 2 0.50 0.71 0.66 25.44 10.53 Lot No. 3 0.54 0.73 0.70 25.95 10.00 W Fe Co P S Lot No. 2 7.45 1.34 Bal. 0.011 0.013 Lot No. 3 7.58 1.53 Bal. 0.005 0.016

Jan 1, 1960

By K. A. Jackson, J. D. Hunt

A new classification of eutectics is proposed, based on tlze entvopies of wzelting of the tuio eutectic phases. The clnssification was used to predict suitable tvansparent analogs of the metallic systems. Experimental confir?nation loas obtained for the theovetical shape of the lamellar solid-liquid interface, fov the fault mechanisms of lanzellar spacing changes, and for the development of low-energy solid-solid boundaries between the lamellae. An explanation is presented to account jov the irvegular and coinplex regular structures zrhich are found in some eritectic systems. FrOM experimental observations, single-phase materials can be divided into two groups according to their solidification characteristics, those that grow as faceted crystals and those that do not. acksonl' showed from thermodynamic reasoning that the type of growth depended on a factor a which was almost thg entropy of melting. Most nonmetals have high entropies of melting (a greater than 2) and grow with crystalline facets. Most metals have low entropies of melting (CY less than 2) and grow almost isotropically with no facets. The authors propose that eutectics may be classified in a similar manner. There are three groups of eutectics, those in which both phases have low entropies of melting, those in which one phase has a high and the other phase has a low entropy of melting, and those in which both phases have high entropies of melting. Lamellar or rodlike structures are formed in systems in which both phases have low entropies of melting. In these alloys dendrites of either phase may be formed, when the alloy is rich in the relevant component. Examples are Pb-Sn, Sn-Cd, Pb-Cd, Sn-Zn, Al-Zn. Irregular, Fig. 14((), or complex regular, Fig. 14(b), structures are formed in alloys in which one phase has a high entropy of melting and the other has a low entropy of melting. Examples are A1-Si, Zn-MgzZnll, Pb-Bi, Sn-Bi. When the alloys are rich in the low entropy of melting phase, dendrites are formed; when the alloys are rich in the high entropy of melting phase, faceted primary crystals are produced. These crystals are sometimes called hoppers or pseudodendrites. In this work the term dendrite will only be used to describe nonfaceted primary crystals. Dendrites are not formed during solidification in high entropy of melting single-phase materials. The third group of eutectics includes alloys in which both phases have high entropies of melting. Each phase grows with a faceted solid-liquid interface. Since most metals do not have high entropies of melting, metallic examples in this eutectic group are rare. However they may occur between some intermetallics and semiconductors or semimetals such as silicon, germanium, and bismuth. Attempts have been made to study eutectic solidification visually by watching the growth process.374 Since metals are not transparent, the observations had to be made on external surfaces. This difficulty can be overcome by using transparent analogs of the metallic systems. As was mentioned earlier, most single-phase compounds have entropies of melting greater than 2 and so grow as faceted crystals. Recently organic materials with entropies of melting less than 2 were investigated.' These materials grow in exactly the same way as the low entropy of melting metals. When the materials are pure, they grow with a solid-liquid interface parallel to an isotherm; when they are impure, cells or dendrites are formed. Since these materials are transparent, have low melting points, and even have cubic structures, they should be ideal for making up transparent analogs of the metallic eutectics. The purpose of the present work was to investigate these organic eutectics and to see whether this quite different series of eutectics could be classified in the same way as the metallic systems. The observations made on the organic alloys are also discussed with reference to the current theories of lamellar growth. Explanations are proposed to account for the structures formed in the other eutectic groups. EXPERIMENTAL Thin cells containing the organic alloys were uni-direction ally solidified on a specially constructed microscope stage.' Uniform growth rates were obtained by moving the cells, with a motor drive, through a fixed temperature gradient, so that the solid-liquid interface remained stationary with respect to the microscope objective lens. The cells were made by fusing two microscope cover slides 7/8 by 7/8 by 1/100 in. together on three sides, leaving a gap of 1 to 3 mils between the slides, and these were filled by surface tension. A preliminary investigation of the phase diagram between two components could be made very rapidly. One side of the cell was filled with component A and the other side with component B. Since only a small amount of mixing could occur every composition from pure A to pure B was present in the cell. When the cell was placed in the temperature gradient a pictorial representation of the phase diagram was obtained. Eutectics, peritectics, "interorganics", and solid -solid transformations could be readily detected. Fig. 1 shows part of a eutectic phase diagram. The Sample was first grown slowly then stopped. The two

Jan 1, 1967

By Karl J. Benecke

Though the first patent on a bucket wheel excavator (BWE) was granted in 1881 in the US, this technology was developed in Germany to the high standards of today. However, this development was only possible in parallel with development of shiftable belt conveyors and boom stackers. The combination of these three types of equipment in the open pits of the Federal Republic of Germany has made lignite the cheapest energy source for power generation, despite the low heating value of German lignite on the order of 8500 kJ/kg (3600 Btu/lb) only. Comparing the costs for fuels used in power generating on the basis of their heating value, the relation between lignite, high quality black coal, and imported crude oil is on the order of 1 to 1.5 to 2.5, hence highly in favour of lignite. These cost advantages for lignite in Germany are due mainly to the concentration of lignite mining in a few high-output mines. The largest one, Fortuna mine in the Cologne district, produced a total of 45 million tons of lignite in 1976. That equals the annual fuel need of a 5750 MW power plant running 7000 hours per year at full capacity. Altogether 95.2 million bank m3 equal to 200 million tons of overburden had to be removed to accomplish this lignite output. The largest BWE ever built is working in the Fortuna mine [(Fig. 1)]. At a digging height of 51 m above crawler level, the total vertical reach in relation to the face conveyor level is 98 m by means of its conveying bridge and loading unit. The hourly output is 10 400 bank m3. Its weight in operation is 13 000 tons and its wheel diameter 21.6 m, as high as a seven-story building. Major reasons for the development of BWE technology in Germany were: ? Lignite deposits with moderately consolidated, alluvial-type overburden (gravel, sand, loam, marl, clay, etc.) ? Great overall depth of the deposits, ranging far beyond 100 m, requiring a wide opening of the mine, hence not permitting direct overcasting of overburden. ? Multiple-seam deposits of poor-quality coal divided by reject partings, which demand a perfectly selective digging tool for clean separation. In general, these conditions are almost identical to those prevailing in the lignite deposits of Texas and neighbouring states: The type of overburden suitable for BWE digging, the overall deposit depth ranges down to around 100 m, and finally, the multi-seam occurrence with partings between seams, the latter ranging from just 1 m to a few meters in thickness. Technique As the Texas-type lignite deposits come into focus more and more as a possible fuel source in power plants to replace natural gas and crude oil, the following will deal with the BWE technology for mining a typical Texas lignite deposit under the aspect of producing enough fuel for a 500-MW power plant located at the mine mouth.

Jan 1, 1980

By Ernest N. Patty, Sherwin F. Kelly

The present case history deals with the examination of an almost forgotten nickel prospect, near Winesap, Chelan County, Washington. Although the final results yielded no ore body of commercial importance, the integration of surface and underground exploration, geophysical survey and diamond drilling endow the story with interest. The program is significant because it is illustrative of how the most disappointing expenditures in mining exploration, the "not-finding" costs, could have been reduced had geophysical methods been applied at an appropriate stage in the prospecting work. The Chelan nickel deposit was discovered about 1900, on a sage-brush-covered hillside with a southerly slope, adjacent to Winesap Canyon; the paved highway now extending from Wenatchee northward, up the Columbia River and into Okanogan Valley, is only a mile away. After the deposit was found, three short prospect tunnels were driven into it, and the prospect then remained dormant for 40 years. No. x tunnel was 80 ft. long, running north into the hillside. For the first 35 ft. this adit exposed a typical, iron-stained gossan with streaks and stains of malachite, and small seams of water-soluble nickel sulphate. Beyond this, it encountered a relatively fresh peridotite, well mineralized with blebs of pentlandite. Systematic sampling yielded an average assay of 1.5 per cent nickel and 0.3 per cent copper. Down the hillside to the south and 35 ft. lower in elevation, No. 2 tunnel was driven under No. I and in the same direction, traversing 50 ft. of gneiss before it reached the peridotite. At this point the latter formation showed only scattered blebs of sulphides, not of commercial grade. To the west, on the same contour line as No. I tunnel, and 800 ft. around the hillside from it, No. 3 tunnel was driven 50 ft. into the hill to explore a strong gossan outcrop that assayed 0.5 per cent nickel (Fig. I). From the geological exposures on the hillside and in the tunnels, it appears that the main mass of the hill is formed of an ancient and altered gneiss complex. Into this, a sill-like injection of amphibolite (altered peridotite) was intruded, which, at least in some places, contains commercial quantities of nickel sulphide. Its structure is obscure, but it appears to dip into the hill at an angle of about 15°. In the vicinity of No. 3 tunnel a large dike of quartz diorite cuts the peridotite or amphibolite; about 140 ft. north of the portal of the tunnel, a dike of andesite 00 ft. wide cuts boldly up the hillside to break the continuity of the peridotite in that direction. The geological evidence available was not adequate to decide whether the peridotite forms a continuous sill, or occurs as isolated bodies in the gneiss. Not all of this peridotite carries commercial amounts of pentlandite, but if the mineral-

Jan 1, 1946

By Ernest N. Patty, Sherwin F. Kelly

The present case history deals with the examination of an almost forgotten nickel prospect, near Winesap, Chelan County, Washington. Although the final results yielded no ore body of commercial importance, the integration of surface and underground exploration, geophysical survey and diamond drilling endow the story with interest. The program is significant because it is illustrative of how the most disappointing expenditures in mining exploration, the "not-finding" costs, could have been reduced had geophysical methods been applied at an appropriate stage in the prospecting work. The Chelan nickel deposit was discovered about 1900, on a sage-brush-covered hillside with a southerly slope, adjacent to Winesap Canyon; the paved highway now extending from Wenatchee northward, up the Columbia River and into Okanogan Valley, is only a mile away. After the deposit was found, three short prospect tunnels were driven into it, and the prospect then remained dormant for 40 years. No. x tunnel was 80 ft. long, running north into the hillside. For the first 35 ft. this adit exposed a typical, iron-stained gossan with streaks and stains of malachite, and small seams of water-soluble nickel sulphate. Beyond this, it encountered a relatively fresh peridotite, well mineralized with blebs of pentlandite. Systematic sampling yielded an average assay of 1.5 per cent nickel and 0.3 per cent copper. Down the hillside to the south and 35 ft. lower in elevation, No. 2 tunnel was driven under No. I and in the same direction, traversing 50 ft. of gneiss before it reached the peridotite. At this point the latter formation showed only scattered blebs of sulphides, not of commercial grade. To the west, on the same contour line as No. I tunnel, and 800 ft. around the hillside from it, No. 3 tunnel was driven 50 ft. into the hill to explore a strong gossan outcrop that assayed 0.5 per cent nickel (Fig. I). From the geological exposures on the hillside and in the tunnels, it appears that the main mass of the hill is formed of an ancient and altered gneiss complex. Into this, a sill-like injection of amphibolite (altered peridotite) was intruded, which, at least in some places, contains commercial quantities of nickel sulphide. Its structure is obscure, but it appears to dip into the hill at an angle of about 15°. In the vicinity of No. 3 tunnel a large dike of quartz diorite cuts the peridotite or amphibolite; about 140 ft. north of the portal of the tunnel, a dike of andesite 00 ft. wide cuts boldly up the hillside to break the continuity of the peridotite in that direction. The geological evidence available was not adequate to decide whether the peridotite forms a continuous sill, or occurs as isolated bodies in the gneiss. Not all of this peridotite carries commercial amounts of pentlandite, but if the mineral-

Jan 1, 1946

By G. D. Gemmell

Effects of solid-sdutidn alloying with titanium, molybdenum, and tungsten at concentrations up to 10 pct on the strength of pure columbium at elevated temperatures (mainly 2000°F) have been investigated by means of creep-rupture, hot-tensile, and hot-hardness testing and recrystallization studies. ThIS paper presents some results from the initial part of a study of the effects of alloying on the high-temperature strength properties of columbium. The elevated-temperature strength characteristics of pure columbium were first studied. Binary alloys of columbium with titanium, molybdenum, and tungsten containing 1, 5, and 10 pct of the solute elements were chosen on the basis of their high melting points, their known solid solubility in columbium, and results of separate oxidation-resistance studies of columbium alloys. EXPERIMENTAL PROCEDURE All the materials used were of highest purity. A typical analysis of the columbium is shown in Table I. Compositions of the alloys are also given in Table I. To evaluate the strength properties of pure co-lumbium and the alloys at elevated temperatures, creep-rupture, hot-tensile, and hot-hardness testing was done on recrystallized material. To prepare the pure metal and the alloys for these tests, 1- 1b buttons were made in a water-cooled copper crucible, inert atmosphere, tungsten arc furnace. Tapered ingots, 3 in. long, were made from these buttons by a skull-casting technique and these were machined to 1/2 in. diam, swaged to 50 pct reduction (pure columbium at room temperature, alloys at lowest temperature possible without cracking, generally in range 1100" to 1800°F) and heated in vacuum (lo-' mm Hg) for 16 hr at 2550°F for re-crystallization and homogenization. The resulting grain diameter was 0.1 to 0.3 mm. The 10 pct Mo alloy casting was not successfully swaged at temperatures up to 1800°F without cracking and was not included in the test program. Creep-rupture testing was done at constant load in vacuum on cylindrical specimens of 0.16 in. diam, using Instron capsules. The pressure at test temperatures was less than 10-1 mm Hg. Hardneas readings taken on the test specimen before and after testing were used as a check on possible gaseous contamination. Hot tensile tests in vacuum on cylindrical specimens of 0.125 in. diam were also made with Instron equipment at a strain rate of 0.067 min.-l. Hot-hardness measurements were taken with a unit constructed at the Du Pont Experimental Station. The test piece, supported on an alumina anvil, and the molybdenum indenter shaft with sapphire tip is heated in a platinum-wound furnace. The load applied to the pyramid indenter is measured by strain gages attached to a proving ring located outside the hot zone. In the measurements reported here the load was I kg. The tester operates in a vacuum of about 10"5 mm Hg and is capable of temperatures up to 1400°C.

Jan 1, 1960

By K. O. Stamm, B. A. Rogers

Because it is the basis of the economically important operation of hardening steel by quenching, the A3 transformation in iron has been the subject of numerous investigations. Although the contributions to this subject are interesting, no general review will be given here. Readers who care to follow the matter further are referred to the comprehensive summary by Cleaves and Thompson,l which covers the literature to about 1935. Their references to 53 papers on the subject suggest that further investigation is hardly justifiable. However, considerable interest has devel oped recently concerning the reversibility of the transformation. From thermo-dynamic considerations, the transition ought to occur at the same point on heating or cooling, if the change of temperature is sufficiently slow. Yet all of the earlier investigators found a difference of several degrees. Burgess and Crowe,2 who used thermal methods, obtained average temperatures of 912" for Ac3 and 900°C. for Ar3 on electrolytic iron. Their data indicate a considerable range of temperature over which the change occurs, both on heating and on cooling. Terry3 measured the susceptibility in the critical range and estimated from the steepest parts of his curves that Ac3 came at 9I8° and Ar3 at 903°C. Ishiwara4 was one of the first investigators to report a shorter interval between the temperature of the change in the two directions. He measured the change of susceptibility of kaolin-coated samples of steel, in a hydrogen atmosphere, at rater of heating and cooling so low that about 3 or 4 hr. were required for the transformation to complete itself. His results show some variability between samples, but indicate that the difference between Ac3 and Ar3 is in the vicinity of 6°C. Roberts and Davey5 measured the space lattice in pure iron in the vicinity of 900°C. and concluded that a change occurs reversibly between 907' 3" and 910" 3°C., probably between 907" and 910°C. Wells, Ackley, and Meh16 made dilatometric determinations of the Ac3 and Ar3 points in samples of hydrogen-treated carbonyl iron maintained under a vacuum. They used three rates of heating and cooling: 2°, ½°, and .?°C. per min. and found the spread between the two points decreased with low rates. At the slowest rate, the Ac3 transition occurred at 909° to 909. 5°C. and the Ar3 change at 907°C. in three of the samples believed to contain the lowest percentages of alien elements. They concluded that if the rate of temperature change and the content of alien eiements were low enough, the A3 transformation would be completely reversible at 909.50 + 1°C. The question of reversibility is an interesting one and when some iron with especially small percentages of alien elements became available the opportunity to conduct an investigation was welcomed. This iron was prepared by the Division of

Jan 1, 1942

By B. A. Rogers, K. O. Stamm

Because it is the basis of the economically important operation of hardening steel by quenching, the A3 transformation in iron has been the subject of numerous investigations. Although the contributions to this subject are interesting, no general review will be given here. Readers who care to follow the matter further are referred to the comprehensive summary by Cleaves and Thompson,l which covers the literature to about 1935. Their references to 53 papers on the subject suggest that further investigation is hardly justifiable. However, considerable interest has devel oped recently concerning the reversibility of the transformation. From thermo-dynamic considerations, the transition ought to occur at the same point on heating or cooling, if the change of temperature is sufficiently slow. Yet all of the earlier investigators found a difference of several degrees. Burgess and Crowe,2 who used thermal methods, obtained average temperatures of 912" for Ac3 and 900°C. for Ar3 on electrolytic iron. Their data indicate a considerable range of temperature over which the change occurs, both on heating and on cooling. Terry3 measured the susceptibility in the critical range and estimated from the steepest parts of his curves that Ac3 came at 9I8° and Ar3 at 903°C. Ishiwara4 was one of the first investigators to report a shorter interval between the temperature of the change in the two directions. He measured the change of susceptibility of kaolin-coated samples of steel, in a hydrogen atmosphere, at rater of heating and cooling so low that about 3 or 4 hr. were required for the transformation to complete itself. His results show some variability between samples, but indicate that the difference between Ac3 and Ar3 is in the vicinity of 6°C. Roberts and Davey5 measured the space lattice in pure iron in the vicinity of 900°C. and concluded that a change occurs reversibly between 907' 3" and 910" 3°C., probably between 907" and 910°C. Wells, Ackley, and Meh16 made dilatometric determinations of the Ac3 and Ar3 points in samples of hydrogen-treated carbonyl iron maintained under a vacuum. They used three rates of heating and cooling: 2°, ½°, and .?°C. per min. and found the spread between the two points decreased with low rates. At the slowest rate, the Ac3 transition occurred at 909° to 909. 5°C. and the Ar3 change at 907°C. in three of the samples believed to contain the lowest percentages of alien elements. They concluded that if the rate of temperature change and the content of alien eiements were low enough, the A3 transformation would be completely reversible at 909.50 + 1°C. The question of reversibility is an interesting one and when some iron with especially small percentages of alien elements became available the opportunity to conduct an investigation was welcomed. This iron was prepared by the Division of

Jan 1, 1942

By Theron Wasson

The oil and gas fields of Michigan that have been under development since 1925 are in an area that extends across the middle of the lower peninsula from northeast to southwest, a distance of about 200 miles, and with a width of about 80 miles. In 19 years 70 fields have been discovered. Most of these are relatively small when compared with other oil-producing areas. This is borne out by the fact that since the first wells were drilled these fields have produced a total of only 204,000,000 bbl. However, Michigan is still maintaining its production, for during the past five years the annual production has remained fairly constant at approximately 20,000,000 bbl. Production for 1943, as reported by the Bureau of Mines, was 20,682,000 barrels. Roughly, one third oi Michigan's production in 1943 came from the Reed City field, which was discovered in 1941. During the year, 237 oil wells were completed in Michigan in 1943. The decrease of 56 from the 1942 total is probably due to the continuance of Government regulations requiring a 40-acre spacing pattern over most of the state. Fig. I shows the principal oil and gas fields of Michigan, and the columnar section, Fig. 2, shows the principal producing horizons in relation to the section drilled. The data of Table I and Table 2 have been carefully checked with previous reports to eliminate errors. Six new producing areas were discovered during 1943 and five areas discovered in 1942 were developed during the year. Both the new discoveries and the 1942 discoveries that were developed appear to be small and relatively unimportant. Goodwell Field.—The best discovery of the year is the Goodwell field, T. 14 N., R. 11 W., Goodwell township, Newaygo County. This small structure was located by core testing done by The Pure Oil Co. in 1942 and early 1943. The first producing well, C. R. Harris No. I, was completed on July 5, 1943, ill the Traverse limestone at a total depth of 2742 ft., with ail estimated potential of 1100 bbl. per day. By the end of the year, 18 wells had been completed in this field and approximately 281,000 bbl. of oil produced. The field operated under proration of 262 bbl. per day per well from Oct. I to Dec. I; 150 bbl. per day per well after that date. Woodville Field.—The small Woodville pool, T. 15 N., R. 11 W., 3 miles north of the Goodwell field, was discovered by core testing by the Ohio Oil Co. The discovery well was completed on May 5, 1943, flowing 650 bbl. of fluid, including 18 per cent salt water the first 18 hr., from the Traverse limestone at a depth of 2810 to 2815 ft. Seven wells had been completed by the end of the year and 67,000 bbl. of oil had been produced. Development is now practically at a standstill because further drilling does not aDDear economically iustified.

Jan 1, 1944

By Theron Wasson

The oil and gas fields of Michigan that have been under development since 1925 are in an area that extends across the middle of the lower peninsula from northeast to southwest, a distance of about 200 miles, and with a width of about 80 miles. In 19 years 70 fields have been discovered. Most of these are relatively small when compared with other oil-producing areas. This is borne out by the fact that since the first wells were drilled these fields have produced a total of only 204,000,000 bbl. However, Michigan is still maintaining its production, for during the past five years the annual production has remained fairly constant at approximately 20,000,000 bbl. Production for 1943, as reported by the Bureau of Mines, was 20,682,000 barrels. Roughly, one third oi Michigan's production in 1943 came from the Reed City field, which was discovered in 1941. During the year, 237 oil wells were completed in Michigan in 1943. The decrease of 56 from the 1942 total is probably due to the continuance of Government regulations requiring a 40-acre spacing pattern over most of the state. Fig. I shows the principal oil and gas fields of Michigan, and the columnar section, Fig. 2, shows the principal producing horizons in relation to the section drilled. The data of Table I and Table 2 have been carefully checked with previous reports to eliminate errors. Six new producing areas were discovered during 1943 and five areas discovered in 1942 were developed during the year. Both the new discoveries and the 1942 discoveries that were developed appear to be small and relatively unimportant. Goodwell Field.—The best discovery of the year is the Goodwell field, T. 14 N., R. 11 W., Goodwell township, Newaygo County. This small structure was located by core testing done by The Pure Oil Co. in 1942 and early 1943. The first producing well, C. R. Harris No. I, was completed on July 5, 1943, ill the Traverse limestone at a total depth of 2742 ft., with ail estimated potential of 1100 bbl. per day. By the end of the year, 18 wells had been completed in this field and approximately 281,000 bbl. of oil produced. The field operated under proration of 262 bbl. per day per well from Oct. I to Dec. I; 150 bbl. per day per well after that date. Woodville Field.—The small Woodville pool, T. 15 N., R. 11 W., 3 miles north of the Goodwell field, was discovered by core testing by the Ohio Oil Co. The discovery well was completed on May 5, 1943, flowing 650 bbl. of fluid, including 18 per cent salt water the first 18 hr., from the Traverse limestone at a depth of 2810 to 2815 ft. Seven wells had been completed by the end of the year and 67,000 bbl. of oil had been produced. Development is now practically at a standstill because further drilling does not aDDear economically iustified.

Jan 1, 1944

By H. W. Hitzrot, R. H. Limons, L. V. Fegan

The testing of a new method for measuring pellet-bed temperatures in the traveling-grate or shaft furnace is presented in this paper. This method, using silver-palladium alloy wires as indicators, overcomes disadvantages existing in the methods based on the use of thermocouples which are costly and time-consuming. The authors have developed and tested a new method for measuring pellet-bed temperatures in the traveling-grate or shaft turnace through the use of silver-palladium alloy wires as indicators. This method overcomes the disadvantages of existing methods, which, based on the use of thermocouples, are generally costly and time-consuming. For example, in the case of the traveling-grate furnace, the installation of an instrumented pellet, together with its attached thermocouples, requires stopping the furnace, with resulting loss of production time. As for temperature measurement in the shaft furnace by the existing method, the movement of the shuttle-car feeder seriously interferes with both the actual insertion and the resulting distribution of continuously fed thermocouples. The authors have overcome these difficulties by using, as temperature indicators, a range of silver-palladium alloy wires that can be easily recovered, after firing at any desired location in a pellet furnace. Silver-palladium wires having specific melting points from 2000°F to 2500°F are enclosed in ceramic capsules. Each capsule is placed in a ni-chrome wire basket filled with a sample of green pellets, the baskets being the means for recovering the capsule after firing. After the encapsulated wires have been exposed to the firing cycle, the alloy wires are examined to determine the maximum temperatures attained by the pellet sample. This method gives accurate, rapid determinations of maximum temperatures attained during pellet induration in either the traveling-grate or shaft furnace The new method has the following advantages over existing methods: 1) it is less expensive; 2) no furnace downtime is required; 3) the testing units can, be made in quantity in advance; 4) measurements can be made in rapid succession at all desired locations; 5) measurements of maximum firing temperatures are more accurate; 6) on the basis of points 4 and 5, the new method gives a more reliable picture of the correlation of pellet quality, petrographic textures and maximum temperatures, thus providing a more effective quality-control tool. A disadvantage of the method is, of course, that the measurements are not continuous and only maximum temperatures are determined. TEST PROGRAM Preparation of Materials: CALIBRATION OF ALLOYS - In the following discussion the term "bead point" (see Fig. 1) refers to the temperature at which each alloy begins to melt and form a bead. Fig. 2 gives the bead point curve for silver-palladium alloys. Before the alloys are used in plant tests, the bead point of each alloy should be determined in the laboratory to verify the alloy compositions. Once a given alloy has been calibrated, it can be

Jan 1, 1965

By J. D. Forrester, Erich Sarapuu, T. C. Cheasley

John G. Tripp-—The concept of converting fuel deposits in-situ to useful forms of energy and chemical raw materials has important possibilities as a means of stretching out our fuel resources. The authors have worked in this field for years and in fact are among the pioneers in developing in-situ techniques based on underground electrocarbonization. Their efforts have aroused great interest in this subject and their contributions will undoubtedly gain even more significance as time goes on. The 4 to 5 billion tons of petroleum are proved reserves, that is, they are completely defined and could be produced economically with present methods of recovery. Reserves of coal, tar sands, and oil shale shown in Table I are not equivalent to proved reserves as the term is used in the oil industry. Incidentally, the 4.3 billion tons of oil shown in the tabulation is equal to about 28 billion barrels of oil and, therefore, presumably does not include reserves of natural gas liquids estimated at about 5 billion barrels. The relative comparisons would be more complete if these liquids together with the reserves of natural gas were included in the tabulation. It is stated in the report that production costs of the order of 10c per million Btu's could be expected from a large industrial electrocarbonization installation. The authors state that the operation probably could be operated successfully and at a profit. I would like to express my view that for the operation to be profitable extremely favorable conditions would have to prevail. For example, the coal seam would have to be thick and close to the surface in order to minimize drilling costs; the deposit should be dry and so situated that there would be little, if any, inflow of ground water; and the seam would have to be relatively gas tight to avoid excessive gas leakage. Notwithstanding the tremendous strides that have already been made, it is my hope that the authors plan to continue their development work. Experiments on underground electrolinking and initial carbonization at Gorgas, Ala., indicate a need for improved control over the operation. Subsequent examination of the underground system at Gorgas has shown that the gasification zone did not always follow a direct path between the electrodes. Undoubtedly the control of the in-situ thermal processes can be improved by further development work. With respect to the electrocarbonization of oil shale it may be well to point out that the cost of mining oil shale is estimated to be 50c to 60c per ton. These are low mining costs as compared to coal. Thus it would appear that there is less economic incentive for applying in-situ thermal methods to oil shale than there is for applying these methods to coal. As is the case with in-situ methods for petroleum, the product from the shale having the most economic interest would be liquid oil rather than gas. The authors point out that for distances up to several hundred miles it is cheaper to transmit energy as electricity than it is to ship energy as coal. This is a very important point, and with coal shipping rates rising periodically, it could prove increasingly important in the future. I believe that the authors deserve great credit for their outstanding work on underground electrocarbonization. The knowledge resulting from their efforts is of great value to our fuels technology. James L. Elder—The experimental work conducted by the authors on the electrolinking-carbonization of carbonaceous materials in situ is of great interest. The method is of great importance in the development

Jan 1, 1955

By D. A. Dukelow, G. Derge

THE Fe0-Mn0-Si0, system has many properties of fundamental interest besides its occurrence in steel-making. The system is the simplest ternary complication of the FeO-SiO, binary whose electrochemical properties have been explored. Therefore, knowledge of the conformance of Fe0-MnO-SiO, melts to Faraday&apos;s laws, as investigated by current efficiency measurements, would be of particular value in interpreting the observed variations of electrical conductivity, while at the same time furthering understanding of this type of molten oxides. Pertinent to the present study are conductivity data of FeO-SiO, and Fe0-Mn0-SiO2, and current efficiency data of FeO-SiO,. Concerning conductivity measurements, Inouye, Tomlinson, and chipman&apos; studied the specific conductivity, a, of molten wüstite as a function of temperature and oxide addition. Liquid FeO in equilibrium with an iron crucible was found to have a o whose magnitude and positive temperature coefficient were undeniably semiconductor in nature (o1400°C = 269 ohm-1cm-&apos;). Additions at 1400°C of 5 mole pct MnO decreased o to 227 while a similar addition of SiO2, dropped o to 125. Additional SiO2 produced an exponential decline of o. It was reasoned that because wüstite is known to be oxygen excess and since there is no pronounced change in oFeO upon melting, that UFeO(L)is p-type semiconduction. Björling2 gives o data for the ternary FeO-MnO-SiO, using fayalite, 2 FeO-SiO,, as the base substance. Upon addition of tephroite, 2 MnO-SiO, he noted a small decrease in o. Taking his data for 1400°C with one-half of the fayalite replaced by tephroite, o shows a decrease of some 40 pct relative to o for fayalite, i.e., 5 ohm-&apos; cm-&apos; to 3. In line with this observation, Mori and Matsushita3 reported that substituting MnO for FeO in the silicate de- creased o slightly except at high SiO, contents where the decrease was somewhat larger. Investigating the ionic nature of FeO-SiO2 melts, Simnad, Derge, and George4, found the anode current efficiency, C,, as calculated from iron anode weight loss, was temperature invariant and in general increased with SiO2 concentration. The authors suggested the possible presence of electronic conduction to explain why C+ < 100 pct. Fig. 4 includes their results as curve (b). EXPERIMENTAL METHOD Apparatus—Fig. 1 is a schematic section of the electrolysis cell used in all the current efficiency runs. The melt was contained in an iron crucible that rested on an alundum ring. A centered silica tube came within 1 in. of the surface of the melt and initially served as a thermocouple well and then as the guide for the anode.

Jan 1, 1961

By G. R. Frank, R. E. Willett, E. H. Hollingsworth

The most generally accepted equilibrium diagram for A1-Fe alloys has a eutectic system on the aluminum side with an essentially insoluble constituent of the formula, FeAl,, as the second phase. In 1938, Bradley and Taylor1 did report a phase change of FeAl,, but this change has never been confirmed. According to them, FeA1, is the stable phase only at higher temperatures; at lower temperatures, it is converted into Fe2Al7 and aluminum. It has now been found that there is, in fact, a phase change of the Al-Fe constituent on the aluminum side of the equilibrium diagram. This change, however, is not the one reported by Bradley and Taylor. The alloys used were cast by continuous processes and had these analyses: Fe - 1.98 to 2.02 pct, Cu-0.01 pct, Si - 0.01 pct, Mn - 0.01 pct, Mg - 0.00 pct, Zn - 0.00 to 0.01 pct, Cr - 0.00 pet, Ti - 0.00 to 0.04 pct. The constituent in these alloys was identified by X-ray analysis with a Guinier camera and by chemical and X-ray powder diffraction analyses. Two procedures were used to separate constituent for the last two analyses. In one procedure, it was separated by treating a sample with a solution of methanol saturated with iodine. And in the other procedure, it was separated by first applying, at 12 amp per sq ft in 15 pct sulfuric acid at 70°F, an oxide coating to a sample, and then dissolving this coating in a solution of 35 ml of 85 pct H3PO4 and 20 g of CrO3 per liter. Several observations directed attention to a phase change of the A1-Fe constituent. Differences that appeared too great to be accounted for by micro-structure alone were found in the voltages required to apply the same thickness of an oxide coating to products from rapidly and slowly chilled ingot. Even more striking was the difference in appearance of the coatings themselves. One applied to a product from a rapidly chilled ingot was dark gray in appearance, in fact, almost black, while one applied to a product from a slowly chilled ingot was essentially white. Also, even a short period of thermal treatment at an elevated temperature of products from rapidly chilled ingot led to the same anodizing behavior as that of products from slowly chilled in-

Jan 1, 1962

By William D. Manly, John Towers, Paul A. Beck

RECENT work on grain growth in high purity aluminum and in a solid solution type alloy of aluminum and magnesium&apos; showed that the isothermal increase of the average grain diameter D with time follows the equation [D = K(to + A)-Eq I] Here [to] is that portion of the total annealing time [t], which is available for grain growth, i.e. the annealing time less the time necessary for complete recrystallization. The parameters A and n depend only on the temperature. A has the dimension of time, and is usually of the same order of magnitude as the time for recrystallization: R. In some instances R may be substituted for A in Eq I. This is the case for example at long periods of annealing or at high temperatures, where both A and R become small in comparison with t. In such instances Eq I is simplified to [D-K-tnEq2] For high purity aluminum the exponent n increases in the ratio of about 1 to 5 in the temperature range of 350° to 600°C. 70-30 brass has been long known to exhibit grain growth of the continuous type, such as occurs in pure metals. For this reason, it was of interest to determine whether grain growth in brass also follows Eq I and 2 as it does in aluminum. Isothermal grain growth data for 70-30 brass were published in recent years by R. S. French2 and by H. L. Walker3 Fig I shows a log D vs. log t plot of French&apos;s data, together with the 500, 600 and 100°C data by Walker for 42.8 pct reduction by rolling. In such a log D vs. log t plot Eq 2 corresponds to a straight line with a slope of n. As seen in Fig I, the data of French and the 600°C data of Walker can be represented by straight lines. However, the 500 and 700°C data of Walker give curved lines and the average slope of his 500°C line is very different from the slope of the line representing French&apos;s data for the same temperature. Furthermore the curvature of the 700°C line suggests a tendency for grain growth to stop after 8 hr. If confirmed, this would constitute a definite deviation from Eq 2, not explainable on the basis of the specimen thickness effect found in high purity aluminum.1 Walker&apos;s specimens were 0.125 in., i.e. 3.18 mm thick, while the deviation occurs at a grain size of approximately 0.4 mm. A further point of divergence arose recently, when J. E. Burke suggested4 on the basis of Walker&apos;s data, that, instead of Eq 2, grain growth in 70-30 brass follows the equation [D-D. =K• t,Eq3] Here D, is the grain size as recrystallized at the temperature in question. Although it was possible to show5 that, for pure aluminum, for which isothermal grain growth has been carefully investigated, Eq 3 is incompatible with the experimental facts, the situation remained somewhat obscure with respect to 70-30 brass. In view of the discrepancies between the

Jan 1, 1948

By Philip R. Strand, O. F. Stewart

Vermiculite is the name generally applied to the group of hydrated ferromagnesian aluminum silicates that are characterized by the ability to expand when heated. This process, called exfoliation, results in a lightweight product of commercial value. Most uses of vermiculite are for the expanded material. The chief markets are in construction, agriculture, and horticulture, with lesser uses in general industry. Composition and Properties Vermiculite, in its natural state, has the characteristic micaceous habit, a perfect basal cleavage which causes splitting into thin laminae that are soft, pliable, and inelastic. The structure of vermiculite is basically that of a talc. The prominent monoclinic crystal faces are often marked by lines at 60° and 120°. Hardness varies from 1.5 to 2 or more; specific gravities are between 2.1 and 2.8; color varies from almost clear to amber, bronze, brown, green, or black. Vermiculite feels like talc, especially when wet. Although much research has been performed on the chemical and structural composition, there is not yet complete agreement on the exact formula. This is to be expected when different workers have examined the many different varieties. Vermiculite is not considered to be a single mineral species but a family of related minerals. The structural formula for a trioctahedral vermiculite may be written: (H20)-(Mg,Ca,K)-(A12,Fe,Mg)-(Si,A1,Fe)4O10 (OH) 2 Hydrobiotite also occurs with vermiculite and is usually considered a vermiculite for commercial uses. When heated quickly to elevated temperatures, vermiculite expands by exfoliating at right angles to the cleavage into wormlike particles. The name vermiculite is derived from the Latin vermiculare, to breed worms. This characteristic of expansion is the result of the mechanical separation of the layers by the rapid conversion of contained water to steam. The decrease in bulk density of commercial grades is usually approximately 10 times, from 50 to 5 lb/ft3, but varies depending on the quality, size, and furnace efficiency. Individual flakes may expand up to 30 times. Vermiculite may also be expanded by soaking in chemicals such as hydrogen peroxide, weak acids, and other electrolytes. Color change during expansion is dependent upon the type of vermiculite and furnace conditions. Heating in an oxidizing atmosphere produces a dull gray or tan color, whereas a reducing atmosphere can produce a bronze or gold color. The expansion of the vermiculite crystal results in large pores being formed between the platelets. Thus, exfoliation makes available a large increase in void volume which is important in the application of vermiculite as a chemical carrier. Mathieson and Walker (1954) state vermiculite must be regarded as a true clay mineral. The characteristic properties of the mineral, such as high cation exchange capacity, organic complexing ability, and variable interlamellar distance are very similar to those of montmorillonite. The cation exchange capacity of vermiculite is one of the highest of all the clay minerals. The interplatelet space is accessible to penetration by some electrostatically neutral molecules. Water and glycerine are two common substances whose molecules may be so imbibed. In the natural state and under normal atmospheric conditions, water occupies the spaces between the silicate layers. The crystal d-spacing is near 14.2A. By differential thermal analysis, it has been determined that the water

Jan 1, 1983

By P. D. S. St. Pierre

IN recent years the use of high sulphur fuels and charges in steelmaking has necessitated rapid methods of slag control in order to insure the production of high quality steel. Several systems of control have been discussed in the literature, and of these the method described by Philbrook, Jolly, and Henry&apos; has received the most attention recently. In their process the hydrogen ion concentration of an aqueous slag suspension is determined under controlled, but arbitrary conditions. The basicity of the slag may then be derived from a previously established pH-V ratio curve. Thus, by measuring the pH, some indication of the V ratio is gained, from which significant properties of the slag may be deduced. Philbrook et al. made no claims as to the theoretical justification of their treatment, but simply offered it as a rapid means of slag control. Encouraging results caused others to study the method and publish their findings.2-5 Although there was fair agreement on the efficacy of the method, no common parameter was evolved against which pH readings could be plotted. The results of the various determinations were related to such V ratios as CaO/SiO2 and CaO/ SiO2 + P2O5 by some,&apos;-3 while others" plotted against "excess lime." Rivet,&apos; however, found a simple proportionality between the hydrogen ion concentration and the sulphur content of the molten steel beneath the slag. Since slag control in North American practice is largely directed toward the efficient removal of sulphur from steel, Rivet&apos;s approach to the problem had the advantage of connecting directly a property of the slag with the impurity being removed. In view of the diversity of parameters used it seemed probable that some fundamental point was being overlooked in seeking a relationship. Examination of the literature revealed that much emphasis had been laid on experimental detail but scant attention paid to the fundamental aspects of the hydrolysis of the aqueous slag suspension. Consequently the present investigation was undertaken with the object of rectifying this deficiency and deriving, if possible, a parameter of general application. Petrographic studies on several matured Canadian open-hearth steel slags have shown that their major constituents are dicalcium and tricalcium silicates set in a complex matrix of iron oxides and ferrites. These phases are shown in Figs. 1 and 2. Free lime is frequently encountered in slags, but is not an equilibrium phase since on continued heating it dissolves forming silicates or ferrites. Thus, it appeared that a study of the hydrolysis of the major phases in steel slags would be profitable. The experimental technique used in the present work was a modification of that described by the other workers.&apos;- Electrical conductivity measurements were also made on the suspensions, since Smith et al." had claimed advantages for this method in their paper on slag control. Experimental Procedure The compounds studied in this investigation were prepared in the laboratory by heating purified oxides

Jan 1, 1954

By M. G. F. Söhnlein

IN THE metallurgical treatment of sulfide silver-tin ores mined at Oruro, Potosi, and Chocaya, the most important and difficult step is chloridizing-roasting. The ores are chiefly mined from veins in rhyolite, a detailed description of which can be found in most textbooks on ore deposits. The chief gangue minerals are Pyrite and quartz, and the silver content is derived from tetrahedrite, jamesonite, stibnite, and cylindrite. Most of the tin is present in the form of a rather impure cassiterite, which forms microcrystalline aggregates of varying richness with quartz and pyrite; occasionally, some tin is found as stannite, cylindrite, and other complex sulfantimonates. The silver content of the minerals that compose the ore is approximately as follows: Pyrite, 3 to 5 oz. per ton; jamesonite, 30 to 50 oz. per ton; stibnite, 30 to 150 oz. per ton; cylindrite, 200 to 300 oz. per-Jon; tetrahedrite, 500 to 3000 oz. per ton. Occasionally, some ruby silver ore is found, but it is very rare. In the mines of Oruro, which are the deepest in the sulfide zone, tetrahedrite has nearly disappeared, stibnite, jamesonite, and, in the deepest levels, cylindrite taking its place. At present, there are six mills treating this ore, two at Potosi, two at Chocaya, one at Poopo, and one at Machacamarca. The ore is crushed dry, given a chloridizing roast, leached with water and hyposulfite solution (or with brine) to extract gold, silver and copper, and concentrated for tin with or&apos; without regrinding.

Jan 8, 1920