Search Documents

By C. G. Dunn

It is well known that plastic deformation alters many of the properties of a metal and subsequent heat-treatment partially or completely restores these properties.l In the deformed or strained state, the metal is unstable and tends to change toward a condition called a "strain-free state." The transformation occurs through recovery, recrystallization, and grain growth—processes that may take place singly or in combination. The distortion of the lattice of an individual grain of a metal in a state of strain may be rather complex in nature, because plastic deformation produces: (I) dislocations within mosaic blocks; (2) elastic variations of the lattice spacings; and (3) gross alterations throughout the lattice, especially along slip planes, along composition planes between a grain and its mechanical twins, and along boundaries of deformation bands. These gross alterations are of the nature of bent planes or rotated regions of the crystal lattice and are revealed by a spread in the orientation of the grain. Although we cannot describe these strains and their formation accurately because of insuffcient knowledge, we can, nevertheless, use the information as well as possible to obtain a better understanding of recovery processes. In recovery, the lattice of a grain is not made anew as it is in recrystallization, but is improved or mended in such a way that the basic structure remains unaltered: Until recatly observations were .that recovery produced no marked changes in the shapes of spots in Laue diffraction patterns, whereas recrystallization did, but now it is known for silicon ferrite2 that Laue spots may become quite sharp entirely through recovery. Consequently, the shape of Laue spots alone would not be a suitable test to distinguish between recovery and recrystallization. There is considerable evidence that the micro-structure usually does not change visibly during recovery. Absence of a visible change in the microstructure, therefore, provides a sufficient test of recovery in many cases. However, including this observation in a definition of recovery as a necessary condition (this is usually done) is unfortunate, because recovery may, as will become evident later, produce new grain boundaries that are visible not only in the microstructure but also in the macrostructure. For the present, therefore, let us say that a necessary condition for a process to be one of recovery is that the principal orientation or orientations of a deformed grain be essentially unchanged throughout the transformation toward the strain-free state. Several transformations may occur that fulfill this condition, and the nature of the distortion in a grain indicates what these must be if the lattice is to be mended in part or fully. Consequently, it will be convenient as well as

Jan 1, 1947

By Robert E. Bush, E. S. Mardock

The objective of this paper is to present practical methods of applying radioactivity logs to problems of interest both to those engaged in evaluating fundamental reservoir data as well as to those engaged in subsurface structural work. The basic theories underlying the operation of radioactivity logging methods are briefly discussed along with some of the problems arising in the interpretation of the log. Relative methods of quantitative interpretation are described, with a discussion of relative reference lines and specific examples are given showing the application of these relative quantitative interpretation methods. To show the variation of the methods described, specimen wells penetrating formations widely divergent in point of geologic age were selected to demonstrate the application. A relative reference line is determined for the Neutron Curve and by comparison to known petrophysical data such as porosities from diamond cores, a direct quantitative relationship is developed. The application of this relative calibration curve to logs of unknown wells will permit a reasonably accurate determination of porosity in limestone and dolomite formations. Specific examples are given showing the application of these relative methods of interpretation to logs of the Smackover limestone in Louisiana, the Edwards limestone and dolomites of South Texas, and Permian dolomites of West Texas. Radioactivity logs have been used extensively by the petroleum industry for a number of years and recognition of their value has grown steadily, not only as tools to aid in the solution of specific stratigraphic problems, but also as potential sources of the basic data necessary for the estimation of net pay and reserves. The value of radioactivity logs for stratigraphic work has been pointed out in the literature,1,2,4,5,6 and now has long been recognized by the industry, but the quantitative application of the logs has advanced but little beyond the stage of a strong conviction that radioactivity logging curves will some day provide the information on such important quantities as the porosity and the liquid saturation of the formations. During the past few years the staffs of the Lane-Wells Company and Well Surveys, Incorporated, have devoted a great deal of time, thought, and experimentation to the relationships existing between radioactivity curves and the lithologic conditions encountered, and this paper is, in a manner of' speaking, intended as a progress report of this work and includes suggestions which the authors have found useful in the interpretation of radioactivity logs. The section on theory is not intended as a complete exposition of the physical processes involved, but rather as a brief introduction to the reader of these processes so that he may acquire a better understanding of the behavior of the radioactivity curves under the varied conditions encountered in normal well logging. Three relative methods for using neutron logs for the quantitative estimation of porosity in limestone or dolomite are presented. These methods are based on the comparison of logs and porosity data from wells in Louisiana, South Texas, West Texas, and New Mexico. These areas were selected because not only were there more core data available from these areas but also the majority of these data were from limestone or dolomitic zones. The correlation between core data and logs is simpler for limestones and dolomites than it is for sandstones due to the fact that sandstones are more complex than limestones and differ more widely among themselves as to composition of cementing materials, siltiness, etc. When data applicable to the various types of sandstones are available, the authors hope to present a discussion similar to this paper covering sandstones or possibly a more general discussion covering all types of reservoir rocks. The relative methods for estimating porosity which are presented in this paper fall short of the absolute method sought. However, these methods possess the advantage that they can be applied to almost any neutron log as long as the range of application is held within the limits imposed by the local lithologic conditions which prevailed during calibration, i.e., these methods are for short range application only. THE THEORETICAL BASIS FOR RADIOACTIVITY LOGGING The two redioactivity logging curves commercially available today are the

Jan 1, 1950

By M. H. Forester, John D. Cooner

ALTHOUGH the unmined anthracite will last for approximately A 150 years, most of the thicker and cleaner coal beds have been almost entirely first-mined and pretty well robbed, leaving much of the present and future production to come from thin and dirtier beds. Herewith is a section of one of the dirty beds being mined in the Wyoming region This section shows that 45.8 per cent of the bed is made up of impurities and that the 45 in. of coal in the bed is in five benches, the thickest of which is 19 inches. In some localities of the anthracite region there are 14 beds of minable coal. Orderly and proper mining of the coal makes it necessary to rob or second-mine-almost all beds have already been first-mined-in sequence from the top downward. Therefore the robbing of the few remaining portions of the thicker and cleaner beds is in many instances being held up by the mining of the overlying thin and dirtier coal beds. Impurities Impurities consist of fire clay, slate, rock, and bone. The latter, which is black, contains 40 to 60 per cent carbon and often resembles good coal. In some beds there are also bands of "blue" coal, which, as the name implies, is of a bluish slaty color. Although much of this "blue" coal has a carban content almost as high as the good anthracite, it is not

Jan 1, 1943

By Edwin H. Olson, Morton Smutz, Charles J. Baroch

IN 1949 an orebody containing some 10 billion lb of recoverable rare earth metals was discovered in the Mountain Pass district of San Bernardino County, California.1 The following year Molybdenum Corp. of America purchased a number of claims at the deposit and a mill on the property which had been constructed to process the district's gold ores. Average composition of ore from the San Bernardino deposit is less than 0.1 pct ThO2, 25 to 35 pet calcite, 10 pet rare earth oxides, 15 to 20 pet silica, and 30 to 40 pet barite.2 Rare earth content of the ore analyzes 50.7 pet CeO2, 4.2 pet Pr6O11, 11.7 pet Nd2O3, 1.3 pet Sm2O3, and 34.3 pet La2O3, and others.2

Jan 3, 1959

By R. H. Landshof, Reynold Q. Shotts, James A. Redding

GENERAL INTRODUCTION by R. Q. Shotts The sizing of coal particles is one of the most important beneficiation operations performed from the time coal is broken at the face until it is delivered to the customer. Indeed, in many cases it may be virtually the only such operation performed in that interval, although it is most often accompanied by some comminution. Sizing, as the term implies, is a separation of the broken coal particles into arbitrary groups, each group containing particles within restricted mass, volume or size limits. Size itself is not a rigidly defined property, but is actually determined more by the operating principles of the sizing device than by unique properties of the particles themselves. Particle size cannot be uniquely defined independently of particle shape. Taggart l says, "In fact, it is not possible to state the size of a single irregular body by means of a single dimension; such possibility exists only for regular polyhedra and their limit, the sphere." In view of the scarcity of regular polyhedra among coal particles, even though most appear to approximate a cube, we actually define size in terms of a surface opening through which the particle barely will or will not pass, or of two openings, the smaller of which retains all particles of the group under study and the larger of which passes all of them. Alternatively, size is expressed in terms of rate of settling of particles in a fluid under closely controlled conditions. Historical Sketch2-Taken from Coal Preparation, 2nd Ed. "Sizing is the process of separating mixed particles into groups of particles all of the same size or into groups in which all particles range between certain definite maximum and minimum sizes. In coal preparation, sizing is generally accomplished by passing the coal over screens. Separation by differential settling in air or water currents has been adapted to the special field of separating very fine sizes, and these processes are in commercial use to a relatively small extent in the coal industry. Separation with screens is a very old industrial practice. Agricola described the use of screens for ore treatment in the middle ages. In the literature of the British coal industry references were made to the screening of coal as early as 1589, but the practice of extensive sizing for the market did not become general until the last half of the nineteenth century. "In America, the practice of sizing developed first in the Pennsylvania anthracite region, beginning with the use of rakes in the mine working places to recover coarse coal. The mining procedure left the fines in the mine.

Jan 1, 1968

By Alan Probert

IN his inaugural address in 1949, President Truman made a policy declaration which launched the foreign technical assistance program known to the world as Point Four. Congress passed Public Law 535 defining the scope of the program and holding activities to certain limitations. It also provided $34.5 million for the first fiscal year. The Technical Cooperation Administration was established within the Department of State to coordinate and direct a program to include "economic, engineering, medical, educational, agricultural, fishery, mineral and fiscal surveys, demonstration, training and similar projects." The mineral programs of Point Four have been staffed and managed by two agencies of the Department of Interior, the Geological Survey and the Bureau of Mines. The Geological Survey is concerned primarily with water-supply problems, the discovery of mineral deposits, and the determination of habit, shape, and grade of mineral deposits. The Bureau of Mines is concerned with determining the commercial potentialities of mineral deposits, mineral technology, and the production and distribution of mineral commodities. Mineral projects comprised only 1 pet of the first year's budget. In spite of the relatively insignificant expenditure compared to those for food, agriculture, and health, a commendable record has been achieved.

Jan 1, 1952

By J. Szekely, J. W. Evans

A formulation is given for radiant heat loss from the surface of molten steel held in a ladle and numerical solutions are presented for the resultant integrodif-ferential equations. The results are shown on plots of the net rate of heat loss against time, with the geometlry, emissivities, thermal properties of the walls, and Preheat as parameters. It was found that the rate of the vadiant heat loss from the exposed metal surface was comparable to the conductive losses from the Portion of the metal in direct contact with the walls. The radiant heat loss was markedly affected by the geometry and by the thermal properties of the walls the net radiant heat loss from the steel could be drastically reduced by providing a top cover and also by the provision of preheat. The results of this work are thought to be relevant to heat loss calculatious concerned with vacuum degassing and with operatzons in which molten metals are held in ladles. WhEN molten steel is held or transferred in ladles heat losses inevitably occur. The accurate assessment of these heat losses is of importance in process design considerations, as the temperature of the metal may have to meet rigid specifications in certain stages of the processing sequence. As shown in Fig. 1, the principal mechanisms responsible for heat loss are: i) Conduction into the walls and ii) Thermal radation from the top metal surface (possibly augmented by natural convection) The conductive heat loss may be readily calculated as much information is available in the literature on both the general theory1'' and on its particular applications to ladle heat loss calculations. Evaluation of the radiant component of the heat loss is less straight-forward. In two recent papers it has been shown that the presence of a slag layer 2 to 3 in. thick would prevent any significant heat loss for periods up to an hour,5'" however, should bare metal be exposed, constituting the radiant surface, substantial heat losses could occur. This latter case is of considerable practical interest in various degassing operations and in the vacuum processing of certain specialty steels, where the top surface of the metal is not covered by a protective slag layer. Under these conditions a substantial radiant flux is emitted by the top metal surface; part of this flux leaves the system, part of it falls in the ladle walls. The radiant flux incident on the ladle walls is in part absorbed and conducted away, and in part reflected and re radiated. The purpose of the paper is to present a general formulation of the problem, the resultant solution of which should enable computation of the net radiant heat loss from the metal surface. The principal variables, the effect of which will be investigated, include initial metal temperature, geometry, thermal and radiative properties of the wall, and various modes of preheat. FORMULATION Consider a cylindrical enclosure, shown in Fig. 2, with a diameter D, height H, and wall thickness W, the cover at the top of the cylinder having a wall thickness L. If the temperature of the base (representing the top surface of the metal) is kept constant, say, Tb, the problem is to calculate the net rate of heat loss from the base as a function of time, geometry, the initial temperature distribution, and the thermal properties of the system. As customary, the formulation will consist of the mathematical statement of the conservation of thermal energy within the system.

Jan 1, 1970

By William G. Kegel

Apart from a usable product and good mining conditions, the greatest asset for a profitable coal mining organization is an effective mine maintenance program. The first step in achieving this is to have good mechanics-or men who want to be mechanics and are interested in knowing, more about the design and control of the machines in their charge. A good mechanic's knowledge and ability result from ambition, curiosity, and determination. Starting with these qualities, the aspiring mechanic can launch his career by learning all he can about mechanics, electricity, and hydraulics. Though the path is rough, the end result is rewarding. Mining machinery probably receives as much, if not more, abuse as any other heavy equipment in use today. Considering the conditions under which much of the repair work must be done, it is essential that the mine operator has the best men and tools to perform the work. Mining machines, from their inception, have utilized the electric motor; and down through the years of mechanization, this power source has undergone many changes to better adapt it to the job. The first motors used were direct-current (d-c) motors since d-c power was the most economical power source for mining at the time of early mechanization. These motors were large open-type machines which are seldom used in modern mining. Because of the mine environment, the d-c motor has been reduced in size to better suit the application in mining machines and is now manufactured with dust-tight or explosion-proof enclosures. The d-c motor is constructed with either (or both) series and shunt fields located on the stationary part of the motor (stator) and an armature coil wound on the rotating part of the motor (rotor). Power is supplied to the armature by brushes which are held stationary and make sliding contact with the armature. The brushes requires regular and careful maintenance because worn or defective brushes will cause heat or arcing which can destroy the motor. D-c motors can be used as d-c generators when mechanical power is supplied to them by the rotating

Jan 1, 1981

By R. E. Zimmerman

The separation of fine sizes of coal from its impurities by means of various flotation methods has become of increasing importance in the coal industry. This, no doubt, will be even more so in the future as the quantity of high grade coal is depleted, particularly that used for metallurgical purposes. The purpose of this paper is to describe and report the results of research work done under the auspices of the Pittsburgh Coal Co. to determine the amenability of their bituminous fine sizes of coal to flotation, to investigate the value of various reagents and factors affecting their use, and compare the results between froth flotation and bulk oil flotation. Compared with the preferential flotation of complex minerals, or ores, the flotation of coal is comparatively easy. However, this statement should not lull one into the feeling that there are no special problems involved. For instance, the separation of coal from pyrite in high sulphur coals is still far from being 100 pet successful. Size consist has considerable effect on reagent consumption and recovery. Other factors will be described and finally it must be remembered that in the flotation of coal a low priced material is being treated and thus economic considerations govern more closely its application than is generally the case in treating other minerals. As a result of the research work done by the Pittsburgh Coal Co. on the flotation of coal, it was concluded that it was practical to clean the —48-mesh coal commercially by froth flotation and after several different types of flotation units and circuits were investigated by means of pilot plants, large scale units were installed at their Champion Nos. 1, 4 and 5 Preparation Plants for the cleaning of —48-mesh slurries. These large scale operations have been recently described by D. H. Davis.' C. P. Proctor and C. B. Carlson2 in their chapter on Froth Flotation of Coal in the AIME Seeley W. Mudd series book on Coal Preparation describe some of the practical applications of our Pittsburgh Coal Co. laboratory work in actual plant practice as well as summarizing part of the investiga-tional work. The author presents this paper, however, as a supplement to their reports, and records the basic research accomplished in the laboratory investiga-tional work as well as the results of experiments using bulk oil flotation. In presenting this work the author wishes to state much more work must be done in applying the principles of flotation to cleaning coal, especially in view of recent studies and practices in other mineral beneficiation fields. Methods of Conducting Laboratory Tests The bulk of the research work was conducted in the laboratory of the Champion No. I Preparation Plant. This plant has elaborate facilities for sampling and analyzing coal and proved to be an admirable location for the investigational work. Four types of laboratory flotation ma-

Jan 1, 1949

By C. G. Dunn, P. K. Koh

THE primary recrystallization texture in cold-rolled silicon iron, which is the matrix texture for developing the Goss texture or the cube-on-edge texture by secondary recrystallization at temperatures near 900°C,1-5,21 has not been adequately described. Thus from the present available information, it is not possible to explain satisfactorily both the grain-growth selectivity of the matrix and the often observed magnetic torque curve, which itself provides some information on the texture. Also lacking is information on the special annealing texture that develops in this material when the annealing temperature is 1200°C or higher and the rate of rise to temperature is extremely rapid. From the work of May and Turnbull5 and from unpublished work, it was known that isothermal annealing near 1200°C tends to reduce the extent of secondary recrystallization and that a much weaker cube-on-edge texture results if appreciable normal grain growth replaces secondary recrystallization. Koh and Dunn6,7 have obtained additional information on complex primary recrystallization textures from further studies made after normal grain growth. In these instances the initial textures were retained during normal grain growth. A similar result reasonably could be expected in the present study except for the presence of a grain growth ihibitor1-5,8,9.21 and its tendency to allow only a few grains to grow. However, any information on the orientations of grains in the special annealing texture, even if far from representative of the initial matrix texture, would provide useful information on the nature of the matrix texture. In the present texture study the method of Newkirk and Bruce,10 which is based on the methods of Geisler" and Schwartz, 12 is used to obtain a complete (110) pole figure of the primary recrystallization texture. The high-temperature annealing texture is determined simply from the orientations of a large number of selected grains. The kinetic nature of the process that produces the annealing texture is treated elsewhere13 and it is shown that a form of secondary recrystallization with a very high rate of nucleation occurs during rapid annealing at high temperatures. EXPERIMENTAL PROCEDURE Commercial 0.014-in. cold-rolled silicon iron strip (3.16 wt pct Si), prepared by two stages of cold rolling with an intermediate short anneal, was given a decarburizing 3-min anneal at 800°C. Me-tallographic studies indicated complete recrystallization. Short-time anneals at 900° C and at higher temperatures proved that secondary recrystallization had not begun at 800°C, in fact, the short additional anneals were still in the induction period of secondary recrystallization. A rapid rise to an annealing temperature of 1260°C (2300°F) was obtained in a BaC12and NaCl fused salt bath. The structures that resulted from anneals in the range 12- to 1000-sec duration were relatively finegrained, even though the growth was a form of exaggerated grain growth13 or secondary recrystallization with a high nucleation frequency.= Many of the grains were large enough for an X-ray study using a 5-mil X-ray beam. A transmission Laue Camera and an optical-mechanical stage for moving the grains into the X-ray beam were used. A total of 325 grains were X-rayed in this manner and the grain orientations determined. Complete (110) pole figures were obtained for the primary recrystallization texture using CoKa radiation at 30 kv in the back-reflection range, such as (220) for (110) poles, as described recently by Newkirk and Bruce.10 The low voltage serves to reduce the spurious white radiation to a minimum. A filter of 0.001-inch iron foil was located in front of the detector slit for transmission and in front of the beam slit for back reflection. A new and improved specimen holder extended the useful tilting angle range for transmission to 70 deg instead of 60 deg as previously reported.' A torque magnetometer was used to obtain the magnetic torque curves for a number of l-in. diam disk specimens. RESULTS The (110) pole figure of the material after recrystallization at 800°C is shown in Fig. 1. The positions of the pole concentrations are found to be

Jan 1, 1961

By S. K. Asunmaa, W. D. English, N. A. Tiner, W. A. Cannon

This paper discusses the reaction of metal surfaces with fluorine. Fluorination reactions result in the formation of metal fluoride films which are "passive" toward further reaction of the metal with fluorine. These films are very adherent, and do not easily detach from the substrate metal by mechanical flexing or thermal shock. Exposure of passive films to a humid atmosphere produces hydrated metal fluorides which cause secondary fluorination reactions upon reexpo-sure of the metal surface to fluorine. The surface films formed range from 10 to 30A in thickness and they pow at the expense of surface oxide films. The apparent film formation is completed rapidly in 15 to 30 min on stainless steel and nickel surfaces. On copper and on Monel surfaces, the film at first grows rapidly, then increases slowly over an extended period of time. Passive films are formed at all fluorine pressures in the range from 0.1 to 1.4 atm at room temperature. ALL metals react when exposed to fluorine. These reactions generally produce surface films which consist of metal fluorides. The rate of reaction is largely determined by the extent to which these films are protective. Although there is an extensive literature concerning reactions of oxygen with metals, there are very few investigations reported concerning fluorine-metal reactions. Brown, Crabtree, and ~uncan' investigated the kinetics of the reaction of gaseous fluorine with copper metal which had been freshly reduced in hydrogen. The reaction rate was independent of pressure over the range from 6 to 60 torr. A logarithmic rate law was obeyed in the temperature range from 25" to 300" ~. There was some deviation at higher temperatures which could have been the onset of a parabolic law. The calculated film thicknesses ranged from about two molecular layers, 10A, for 5 hr exposure at room temperature to thirty-five molecular layers for 5 hr exposure at 200" . The authors concluded that no single mechanism could explain all the observations. O7Donnell and spatkowski2 studied the reaction of fluorine with copper at 450°C at pressures from lo to 133 torr. The reaction was found to be pressure -dependent and followed a logarithmic rate law. It was not entirely diffusion-controlled, and fluorine was thought to be the migrating species in the reaction. Miscellaneous metal-fluorine reactions were investigated by Haendler et ~1.~ Reaction products were identified but no rate data were determined. Air Prod- ucts and Chemicals, Inc., have conducted an investigation of reactions between fluorine and various metal powders at room temperature and 85° C. Fluoride film thickness as a function of time of exposure was reported on the assumption that the reaction takes place between fluorine and metal to form the normal metal fluoride. Surface areas of the powders were only estimated so the relative film thicknesses may not be exact. The data showed reaction rates which were generally logarithmic in character, the rate of film growth virtually ceasing after a few hours exposure time for some alloy powders. The effect of moisture on fluoride films was also investigated by measuring additional reaction with fluorine after exposure of passivated powders to atmosperic moisture. The fluorination of iron was studied by 0'~onnell~ at temperatures from 225" to 525" ~ and at pressures ranging from 20 to 200 torr. In all ranges, the reaction followed a logarithmic rate law and was dependent on the square root of the gas pressure. The author concluded that fluorine gas passes through pores in the film. As the film grows, the blocking of pores leads to a rapid decrease in reaction rate; hence a logarithmic rate law is observed. Jarry, Fischer, and Gunther' investigated the mechanism of the reaction of fluorine with nickel at about 600" to 700°C. On the basis of the metallographic examination of fluoride scales growing on the nickel and from separate radioautographic data, it was claimed that fluorine is the migrating species in the reaction. This is in sharp contrast to the growth of oxide films on nickel where it has been shown that nickel ions migrate through the scale to the gas-solid interface to react with oxygen. Few investigations have been reported of the reaction of fluorine with metal oxides. Such investigations should be of great significance for a better understanding of passivation in view of the ubiquitous oxide films on technical alloys. Haendler et al.3 studied the reaction of fluorine with oxides of copper, tin, titanium, zirconium, and vanadium. Copper (I) oxide reacted as follows in the temperature range 150" to 300"~: temperature above 300" ~ was required for the CuO to react to form additional copper fluoride. Ritter and smith7 also investigated the reaction of fluorine with copper (11) oxide. An oxide powder comprised of spherical particles with a fairly high surface area was reacted with fluorine, starting at room temperature and increasing to 100° C over a period of 3 or 4 hr. The initial reaction was slow until the fluoride film thickness reached about to or 15R at which time the reaction rate accelerated, then decreased again. Most of the kinetic data was obtained during this final phase of reaction. The authors conclude that the film grows slowly at first until the stresses developed in the distorted lattice are sufficient to rupture the initial

Jan 1, 1969

By Carl Altstetter, Emmanuel deLamotte

The influence of an external stress and plastic deformation on the allotropic transformation of single crystals of a Co-30.5 pct Ni alloy was investigated. Experimental results were obtained from dilatometry, X-ray diffraction, and optical and electron microscopy. The effects of stresses could be conveniently divided into three stress ranges. In range I, from 0 to about 400 g per sq mm, the specimens exhibited a multi-variant phase change on cooling and a considerable amount of retained cubic phase. In range II, from 400 g per sq mm to the elastic limit, hexagonal regions of a given orientation grew in size and the cubic phase disappeared with increasing stress level. In range III, just above the elastic limit, specimens transformed into hexagonal single crystals. It was found that plastic deformation, not applied stress, was the factor which determined whether a single-crystal product was formed. The observed macroscopic shear directions were mainly (112) on cooling, but the behavior was more complicated on heating under stress. To explain these properties of the phase change, a model based on the nucleation of partial dislocations is proposed. IT is well-known1 that, on heating, hcp cobalt transforms into an fcc arrangement by shearing on close-packed planes. The crystallographic orientation relationship of the phases is as follows: the habit plane is (OOO1)hcp ?{lll}fcc and a (1010)hcp direction is parallel to a (112)fcc direction. The temperature at which the transformation occurs in pure cobalt is around 420.C 1,2This temperature decreases with increasing nickel concentration: and at about 30 pct Ni it reaches room temperature. However, many of the transformation characteristics remain essentially the same, particularly the crystallographic features.495 A convenient way of studying the transformation is to alloy cobalt with nickel, thus avoiding the difficulties of doing experiments at the high temperatures needed to transform pure cobalt. Due to the hysteresis of the transformation it is possible to choose a Co-Ni alloy with an Ms temperature below room temperature and an A, temperature above room temperature. Either structure of such an alloy could then be studied at room temperature, depending on whether it had just been heated or cooled to room temperature. The choice of nickel is further favored by the small difference in lattice parameters between cubic cobalt and nickel and the similarity of their physical, chemical, and electronic properties. Co-Ni alloys are reported to have neither long- nor short-range order.6 The main purpose of this work was to investigate the influence of an external stress on the transformation characteristics of Co-Ni single crystals. It may be expected that slip, twinning, and transformation should have many features in common in cobalt, because the (111) planes of the cubic phase operate as slip planes when plastic deformation by slip occurs, they are the twinning planes, and they are the habit planes for the transformation. Many previous investigators7-&apos;6 have concluded that dislocations must play an important role in the nucleation and propagation of the transformation, just as they do for slip and twinning propagation. An external stress will affect their motion, and a study of its influence should yield further information about the atomic mechanism of transformation. The present work extends that of Gaunt and christian17 and Nelson and Altstette18 in both qualitative and quantitative effects of stress. The basic concept underlying all the present theories of the transformation of cobalt and Co-Ni alloys is the motion of a/6<112> partial dislocations over {1ll} planes of the cubic lattice. The ABCABC... stacking of the close-packed planes of the cubic phase can be changed into the hexagonal ABABAB... stacking by the sweeping of an a/6 <112> partial on every second plane. Twinning, on the other hand, requires a shear of a/6 <112> on each close-packed plane. The reverse transformation can be effected in a similar way by a/3 (1010) dislocations moving over every other basal plane of the hexagonal phase. Transformation theories2, 7- 12,14 differ in the details of the nucleation of the transformation and the propagation of the partial dislocations from plane to plane. EXPERIMENTAL PROCEDURE Nickel and cobalt rods supplied as 99.999 pct pure were induct ion-melted together under a vacuum of about 10-5 torr in a 97 pct alumina crucible. An alloy containing 30.5 pct Ni was found to have the desired transformation range, with an Ms near -10°C and an j4s in the vicinity of +10O°C. The ingots were swaged to &--in. rod and electron beam zone-leveled in a 10-6 torr vacuum. This procedure resulted in 12-in.-long single fcc crystal rods (designated I to VII) from each of which several tensile specimens of identical orientation were made. Chemical analysis of the bar ends indicated no contamination or gross segregation and no micro segregation was seen in electron micro-probe scans. Tensile specimens with a 9/32-in.-sq by 1-in.-long gage section were spark-machined from the rods and then electropolished or chemically polished to remove the machining damage and to provide a flat surface

Jan 1, 1970

By G. R. Fitterer

NONMETALLIC inclusions in steel have received much attention by metallurgists during the past few years. Many investigators have been emphatic in stating their belief that these impurities are the chief causes of steel failures, while others think that their effects are negligible. One of the main reasons that definite information on the effects of these impurities is lacking is that no reliable method has been developed for the exact determination of the amounts of these different impurities in steel. Some valuable new information has been brought out by a reliable method for nonmetallic inclusions which has been developed at the Pittsburgh Experiment Station of the U. S. Bureau of Mines, in cooperation with the Carnegie Institute of Technology and the Metallurgical Advisory Board. This procedure satisfactorily extracts some of the more common inclusions from steels, thus enabling the investigator to correlate steel failures with inclusion content. Although the data given herein are the first to be published on the subject of the electrolytic extraction method, the interest in the subject is evidenced by the fact that it is already being used by some 20 to 30 steel companies for their various purposes. Some of the comments received from these laboratories indicate that the method is highly satisfactory: the unfavorable comments, when traced to their sources, have been found to be based on some small mistake made in either installation or operation. The chief discrepancy seems to have occurred in attempts to apply the method to the extraction of inclusions from alloy steels. The procedure can be used only for the plain carbon steels and for such low alloy steels as those containing the usual amount of copper (0.2 to 0.3 per cent). Steels containing the carbide-forming alloys such as chromium, tungsten, etc., present far too many difficulties for the accurate determination of inclusions. Luckily, the iron and manganese carbides do not offer any difficulties and no contamination of the oxide-sulfide residue results. It is highly probable that some modification of the following

Jan 1, 1931

By R. F. Domagala, M. Hansen, D. J. McPherson

Iodide zirconium was combined with calculated amounts of nitrided zirconium sponge and arc melted to prepare alloys in the 0 to 6 wt pct N region. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat-treated specimens permitted construction of the binary phase diagram from 0 to 6 pct N. Features of the diagram include the peritectic formation of both a and ß solid solutions. The maximum solubility of nitrogen is 0.8 pct in 8 zirconium and 4.8 pct in a zirconium. An X-ray study of nitrided materials was made in the range 6 to 13 wt pct N region because serious nitrogen losses were experienced when attempts were made to arc melt these high nitrogen alloys. PHASE relationships in the Zr-N system have been determined. Due to the inability to retain nitrogen in nitrogen-rich alloys subjected to arc melting, definitive work was possible only in the range 0 to 6 wt pct (0 to 30 atomic pct) N. Sufficient complementary X-ray work was done to permit construction of the binary phase diagram up to 13.3 wt pct (50 atomic pct) N (ZrN). Small ingots were prepared by arc melting master alloys with enough zirconium to produce an alloy of the desired composition. Following pretreatment, alloys were annealed at temperature levels between 600" and 2020°C. Determination of the phase boundaries was then accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to corroborate solidus curves, and X-ray diffraction was employed to study the nitrogen-rich region of the a + ZrN phase field. Materials Westinghouse Grade 1 iodide zirconium crystal bar served as the base material for this investigation. The as-received bars were lightly sandblasted, pickled in a 20 pct HN0-5 pct HF aqueous solution, rinsed in water and acetone, and dried. They were rolled to about 1/32 in. strip and acid-pickled, followed by water and then acetone rinses. The material was sheared to approximately 1/4 in. squares, cleaned with acetone, and stored for use. Pure zirconium nitride is not commercially available, according to correspondence with possible suppliers. A literature survey indicated that nitrogen may be introduced into zirconium metal by passing nitrogen or ammonia gas over zirconium at an elevated temperature. After considerable experimentation, a train was devised whereby high quality nitrogen was passed through a series of bubblers to remove the last traces of oxygen, through an H,SO, bubbler and a cold trap to remove moisture, and finally over zirconium within a resistance furnace. Hand-picked Bureau of Mines magnesium-reduced zirconium sponge proved more amenable to nitriding than the crystal bar. The nitrogen used was extra pure gas purchased from Linde Air Products Co. The first two bubblers through which the gas was passed contained a solution suggested by L. F. Fieser" as being ideal for removing the last traces of oxygen from nitrogen. The solution contains 20 g KOH, 2 g sodium-anthraquinone ,9-sulphonate, and 15 g NaHSO, dissolved in 100 ml water. It is blood-red and turns brown when contaminated with oxygen. A saturated lead acetate solution, next in the series of bubblers, removed any H2S which might have formed in the 0, removal stage. An H,SO, bubbler and cold trap removed moisture before the nitrogen was passed over the zirconium. The zirconium was contained in a stainless steel screen within a Vycor or quartz tube in a resistance furnace. Unreacted nitrogen passed out of the system through a mercury bubbler. A nitriding run was performed in the following manner: Zirconium was placed in the screen within the furnace tube. The unit was assembled, suitably clamped off, and evacuated to remove the air and moisture within the tube and that trapped by the zirconium sponge. The unit was flushed with nitrogen and evacuated twice. After nitrogen was allowed to pass over the zirconium for about 30 min, the furnace was turned on; several hours were required to reach temperature. The reaction was allowed to continue at temperature for about 4 hr and the screen was then withdrawn from the hot zone of the furnace by means of a Nichrome or Kanthal rod. The screen and its contents were allowed to cool at the end of the tube and were then removed. At 800°C no more than about 5 pct N could be introduced into the sponge zirconium. This material was designated M-1 (master alloy No. 1) and reserved for the preparation of alloys in the dilute nitrogen region. A second set of experiments was conducted at 1000°C; no more than 7.2 pct N could be introduced into the zirconium at this temperature. Enough material (M-2) of this nitrogen content was prepared to produce a second set of alloys to complement the first and to provide alloys in the 0 to 6 wt pct N range. It was hoped that a diffusion anneal plus a re-nitriding might yield a material of higher nitrogen content. The material containing about 7 pct N was therefore given a homogenization treatment at 1000°C for 6 hr under an argon atmosphere. It was

Jan 1, 1957

By R. V. Higgins

This paper presents a computer method to obtain the shape factors and equal cell volumes of the channels for any well spacing pattern from a potentiometric model. By using this program the authors have processed the data for the seven-spot, direct line-drive and the staggered line-drive patterns. The data for the five-spot pattern had been previously processed by a noncomputer method and are included for completeness. The shape factors and volumes for the channels are presented in tables for those who want to use them to process data using their own permeability relationships and viscosities of their reservoir oils. The authors have used the data and sets of representative permeability curves to process sample calculationr of waterflood performances. The comparison of the calculated results shows that the influence of well spacing is small. The permeabilities of the reservoir rock to oil and water had a greater influence on oil recovery for a given pore-volume throughput of water than the well spacing pattern. The more water-wet the reservoir rock, the better the possibility of permeabilities which are conducive to good recovery. The viscosity of the reservoir oil also influences the recovery more than the well spacing pattern. The reduction in the percentage recovery of oil with increase in viscosity of the reservoir oils is small when oil viscosities are in the range of 0.1 to 3. Above this range the reductions in recoveries are extensive. Sample comparisons of the time required for different patterns to recover the oil are presented. Results of an example calculation are given to show the effect of the permeability profile on recovery. INTRODUCTION The effect of well spacing pattern on the recovery of oil when flooding with either gas or water has been studied by many investigators. Muskat et al.1 presented an analysis using conductivity, sweep efficiency and unit mobility to the time of breakthrough. Dyes et al.2 used experimental techniques (X-ray shadowgraphs) and different mobility ratios. They presented quantitatively the relationship between mobility and sweep efficiency at and after breakthrough. Hauber3 presented a method to predict waterflood performance for arbitrary well spacing patterns and mobility ratios. Craig et al.,4 using techniques similar to Dyes et al. to determine sweep efficiency for a five-spot pattern, added the use of relative permeability curves at breakthrough and thereafter. Douglas et al.5 sed rela- tive permeabilities and continuously changing saturations throughout the entire five-spot flood pattern. In obtaining their solutions they used finite-difierence equations. Hig-gins and Leighton6,7 also used relative permeabilities and continuously changing saturations throughout the pattern before and after breakthrough. They employed techniques that process a flood-pattern calculation on the computer in about one minute. The methods of Douglas et al. and Higgins and Leighton both checked closely the laboratory results for a wide range of mobility ratios. This paper presents some sample performances calculated by the Higgins and Leighton method that show the effect on recovery of different permeabilities and viscosities using the seven-spot, the line-drive and the staggered line-drive, as well as the fivespot flood pattern. No previous paper has presented these data using different permeability curves and continuously changing saturations throughout the flood patterns. The paper also presents (1) the results and analyses of the flood-pattern prediction, (2) the computer techniques for determining the shape factors and volumes from the potentiometric models for the foregoing flood patterns, and (3) the shape factors and volumes of the channels of the flood pattern in the event reservoir engineers may like to process waterflood calculations using their own permeability curves and reservoir oils. DESCRIPTION OF METHOD VOLUMES AND SHAPE FACTORS The use of channels taken from a potentiometric model (see Fig. 1) to aid in calculating the performances of water floods of nonlinear patterns has been thoroughly explained in the literature.0,7 Therefore, very little theory, discussion, or proof regarding this phase will be repeated in this paper. The computer method presented in this paper to calculate the volumes and the shape factors of the channels of potentiometric models employs the trapezoidal rule for the volumes and the Pythagorean theorem (the hypotenuse equals the square root of the sum of the squares of the two sides of a right triangle) for the shape factors. In calculating the volume of a channel, the area of each cell in the channel is determined and then multiplied by the thickness to obtain the volume. In determining the areas of the cells, trapezoids are constructed whose vertical sides are spaced Ax apart, as shown in Fig. 2. The length of the sides is the difference between an ordinate cut off by the top and bottom of the cell — usually equipo-tentials. The coordinates of the points along an equipo-tential or streamline are obtained by Lagrange&apos;s8 equation of interpolation for which the constants are coordinate points at the intersections. Three intersections for con-

Jan 1, 1965

By Paul Foote

MOST of the treatises on metallurgy intimate that simultaneously with the development by the atomic physicist of a really satisfactory theory of the atom will be inaugurated a new epoch in the science of metals. Metallurgically and metaphorically, we shall dwell in the Utopia of Sir Thomas More. It is my privilege this afternoon to demonstrate that this state has not arrived. An atom is a miniature planetary system consisting of a positively charged nuclear sun about which revolve electrons each carrying the negative charge e. The charge on the nucleus is + Ze where Z is the atomic number and the number of planetary electrons in a neutral atom is equal to Z. These electrons are arranged in several groups having different binding energies. Ordinary x-ray phenomena relate to processes occurring deep within the atom, usually with electrons in the so-called K or L shells. Such electrons in the heavier atoms are so closely bound to the nucleus that the forces exerted by neighboring atoms in a solid are relatively inappreciable. For most practical x-ray investigation, the atom may, be considered as in the gaseous phase completely isolated from its neighbors. The K radiation from an element in the gaseous state, in the solid or liquid phase, or even in combination with other elements in all its possible valences, is almost identical. ? Visual and ultraviolet spectroscopy is concerned with disturbances of the most loosely, bound outer or valence electrons of the atom, always in the vapor state. The remarkable progress of the last year in both theo-

Jan 2, 1926

By L. F. Mondolfo

An investigation of the relationship between properties of the elements and type of binary diagram formed was conducted. It was found that, for each type of equilibrium diagram, the factors for the size, valence, electronegativity, period, melting point, entropies of fusion, and sublimation calculated for each pair of elements cover a range of values. However, these factors show sufficient relationship to the equilibrium diagram so that the correlation of several of them can be used to predict the type of diagram formed, or at least limit the choice to only a few types. ThE goal of the metallurgist concerned with alloy development has always been to find a method that predicts the properties that can be obtained when a certain metal is added to another one. In most cases a qualitative predictiton of properties can be made if the equilibrium diagram is known. However, this means that for new metals the alloy development has to start with the experimental determination of the equilibrium diagrams. Because this determination is at least as complicated and time-consuming as the determination of the properties themselves, most alloy development has taken place by trial and error, and the study of the equilibrium diagrams has followed rather than preceded the creation of new alloys. Alloy structures and properties depend on the interaction between electrons and a complete knowledge of these interactions would permit prediction of structure and properties of alloys. Unfortunately direct measurement of these interactions is extremely difficult and somewhat doubtful and only properties that depend on them can be measured easily and with certainty. Study of the relationship between properties of the elements and equilibrium diagrams is not new. Besides the well known Hume-Rothery rule of the necessity of an atomic diameter fit within 15 pct for extensive miscibility in the solid, and the wide knowledge of the effect of such factors as size, electronegativity, electron-atom ratio on solid state features,"&apos; work relating to liquid state and liquid-solid reactions can be found in the literature. Of particular interest is the work by Axon,3 who investigated the effect of size and melting point on a selected number of eutectic and monotectic dia-

Jan 1, 1962

By M. Bevis, E. O. Fearon, P. C. Rowlands

Fe-Ni and Fe-Ni-C martensite specimens have been deformed in compression at room temperature and the habit planes of operative deformation twins determined by two-surface optical trace analysis. The full orientations of the martensite crystals were determined from divergent X-ray beam diffraction patterns. The experimental results are in excelled agreement with predicted twinning modes. In particular, the habit planes of some deformation twins in bcc martensites are consistent with a "Type XI compound&apos;&apos; twinning mode with Kl, Kz, 71, 77~ elements given by {5, 8, 11) {ioi}, (33) (ill) Tetragonal derivatives of this mode are operative in bct martensites. UnUSUAL deformation twinning modes have been reported by Richman&apos; to occur in Fe-Ni-C martensites with bcc and bct structures. The twin habit planes were determined by single-surface trace analysis (pole locus method) and the remaining twinning elements were determined from the geometry of twin-twin intersections. The indices assigned to the observed habit planes are (3 101, "(089)" and "{0, 1,13)" or "{1,2,7} ", and only in the first case do the twinning elements correspond to a predicted twinning mode. This is mode 1.4 in the paper by Bevis et al. The results presented in Ref. 2 indicate that previously unpublished bcc and bct modes should be operative in preference to the (130) mode and anomalous modes reported by Richman. In view of these results and the uncertainties involved in determining habit planes from single-surface trace analysis and twinning elements from twin-twin intersections5 a two-surface trace analysis of deformation twins in Fe-Ni and Fe-Ni-C martensites has been carried out. EXPERIMENTAL PROCEDURES Two alloys with compositions Fe-23 pct Ni-0.6 pct C and Fe-30.4 pct Ni were prepared from 4N pure materials by induction melting under a vacuum of 10"5 mm Hg. The alloys were homogenized at 1350&apos;~ for 5 days. Both of these alloys are austenitic at room temperature with M, temperature - — 50"C. The aus-tenite grain size of the Fe-Ni-C alloy was approximately 300 to 400 p. The Fe-Ni alloy was remelted in a vertical tube furnace and the melt lowered slowly from the hot zone of the furnace to produce s ingle -crystal austenite specimens. Specimens approximately 10 by 5 by 5 mm were cut from the ingots and quenched to various temperatures below the Ms temperature. The specimens were elec-tropolished in a 10 pct perchloric acetic electrolyte before being deformed in compression at room temperature. Martensite plates which exhibited profuse deformation twinning were selected for analysis and the specimen polished on a second surface such that the two surfaces which contained the martensite plate enclosed an obtuse angle of approximately 145 deg. The specimens were then electropolished to reveal the traces of the deformation twins on both surfaces. The full orientations of the martensite crystals were determined using a divergent X-ray beam technique (Kossel line technique) employing an AEI SEM2 electron probe microanalyzer. Details of this technique which include a detailed description of the Kossel camera attachment to the microanalyzer used in the present experiments have been discussed elsewhere.3 Only additional details relevant to this investigation are discussed here. The specimens were mounted with one surface normal to the incident electron beam as illustrated schematically in Fig. 1. The martensite plates to be analyzed were located using the normal scanning equipment of the microanalyzer. The position of the electron beam and hence the position of the source of divergent X-rays generated within the crystal could be located to within 1 p. Exposure times of approximately 8 to 10 min were required for back-reflection Kossel patterns and it was found that useful diffraction patterns could be obtained consistently from heavily deformed martensite plates. A reference line (carbon contamination mark) produced on the two surfaces of the specimen by scanning the electron beam in a direction having a known relationship with the reference !ine in the X-ray camera enabled the full orientation of the crystals to be determined. Martensite plates with widths as small as 8 p could be oriented using this procedure. The Kossel line patterns were interpreted using the charts developed by Rowlands and ~evis~ as generally

Jan 1, 1969

By D. A. Belforti, M. P. Lepie

Spectroscopically pure copper was melted on sapphire plaques in a zydrogen atmosphere. The surface tension of the liquid metal was determined using the sessile drop technique. Measurements were made by direct observation with the aid of a specially const,mcted telescope. The value obtained, 1268 dynes per cm, is compared to that found in the literature. THERE is at this time considerable interest in the use of ceramics for vacuum tubes. The crystalline material is superior to the more conventional glass in mechanical strength, chemical inertness, dielectric properties, ability to withstand high temperatures, and so forth. However, ceramics are much more difficult to seal hermetically with metals than are the glasses. For this reason an investigation was undertaken to determine the wetting and adhesion of metals to ceramics. The sessile drop technique offers a convenient means at elevated temperatures for measuring liquid surface tension, wetting angle, density, spread- ing coefficient, and work of adhesion. Thus, from the contour of a drop of liquid at rest on a solid surface one can obtain a quantitative evaluation of the degree to which the two substances will bond. To this end a special apparatus was constructed so that various molten metals could be observed. Standardization of the apparatus was done initially by measuring the surface tension of copper since this is well documented in the metallurgy literature. Although there are many methods available for the measurement of surface energy,&apos;+ the sessile drop technique has been used most extensively for molten metals and ceramics.5"&apos; Fig. 1 illustrates the dimensions to be measured. From these values, the surface tension of the liquid can be obtained using the Bashforth and bdams&apos; equation and tables.

Jan 1, 1963

By Alan Morris

BRASS rod for use in automatic screw machines is one of the major products of the brass mills. A large tonnage is consumed each year in the manufacture of an endless variety of finished articles and parts for assembly into other products. The machines that do this work have been developed to a high degree of efficiency, and their manufacturers are still striving for higher production speeds. This development has brought with it a demand for brass rod to meet the increasingly difficult machining conditions. This paper is a report of the results of tests undertaken in an effort to obtain a measure of the effects of such variables as lead content, microstructure and cold work on the machinability of brass rod. It is realized that the term "machinability" has never been well defined. Power, finish and tool life all should have a place in such a. definition. In practice it is sometimes found necessary to sacrifice some of these in order to obtain a rod that will not tend to throw up a burr, or will give a burr which is easily tumbled off. Again a specially stiff rod may be necessary because of long overhang from the chuck or a rod of special characteristics is needed to take a given broaching operation without chattering. It is only through an understanding of the effect of basic mill operations on the machinability of the rod that such problems as these may be solved most economically. It is hoped that this paper, together with the discussion it may evoke, will prove to be a basis for such an understanding.

Jan 1, 1932