By Andriy Burbelko, Daniel Gurgul, Wojciech Kapturkiewicz, Marcin Gómy

"The mathematical model of the globular eutectic solidification in 2D was designed. The proposed model is based on the Cellular Automaton Finite Differences (CA-FD) calculation method. The model has been used for studies of the primary austenite and of globular eutectic grains growth during the ductile iron solidification in the thin wall casting. The model mentioned above takes into account, among other things, non-uniform temperature distribution in the casting wall cross-section, kinetics of the austenite and graphite grains nucleation, solute diffusion and non-equilibrium nature of the interphase boundary migration.Some aspects of stochastic nature of the solidification processes are taken into account. The results of the CA solidification modeling have been shown, that differences between cooling curves obtained in the same conditions of the casting solidification may be a result of the stochastic nature of the grain nucleation.The results of modeling were compared with the experimental microstructure. The model is well worked for thin walled ductile iron casting, for fast solidification process.IntroductionNodular graphite cast iron, also known as ductile iron (DI), has major applications in critical engineering parts due to its mechanical properties and castability. The mechanical and physical properties of this material depend on the shape and number of the graphite grains andmicrostructure of the metallic matrix.Solidification of DI was a subject of many computer modeling programs described in literature [ 1-5], in which the stationary conditions of carbon diffusion in austenite is pre-assumed. Recently, a tendency for production of thin-walled castings has been observed [ 6-8]. In this technology, the process of the fast solidification may be very far from equilibrium and steadystate conditions [9].The purpose of the present work is a two-dimension model development for simulation of the DI structure formation during the solidification in the condition of non steady-state temperature and diffusion fields in the thin-wall casting.Model of process The CA-FD is one of the known methods of the simulation ofmicrostructure formation during the solidification [ 10, 11]. In the CA microstructure modeling the outer grain shape is the result of the simulation and does not superimposed beforehand. The model development for a onephase microstructure evolution is a subject of the numerous researches [12 -23]. Model of the eutectic solidification of DI in the uniform temperature field and superimposed cooling rate is known [24]."

Jan 1, 2013

By S. C. Flood, J. D. Hunt

"The columnar-equiaxed transition (CET) has been studied numerically under unsteady-state conditions using mathematical models that: (i) include a non-equilibrium undercooling at the columnar front;and(ii) describe the simultaneous evolution of the columnar and equiaxed zones.The results are discussed and compared with those produced by a steady-state analysis.IntroductionThe majority of the previous work on the columnar-equiaxed transition (CET) has concentrated on the production of equiaxed nuclei, regarding this as being the critical step in the formation of an equiaxed zone. Recently, the growth of equiaxed grains has been considered and this is not unreasonable because, for an equiaxed zone to be present, the grains must grow as well as nucleate. Since the growth rate of the grains will be determined by the thermal environment at and ahead of the columnar tips, it was decided to model the liberation and flow of heat during solidification to discover whether the various trends in the columnar range might be explained by their effect on the temperature profile throughout the casting. The models presented here for the solidification of a casting are the first to include the latent heat liberated ahead of the columnar front. Burden and Hunt (1) consider its effect only qualitatively, and although Lipton et al (2) adopt a criterion for the CET which is based on the thermal interaction of the columnar and equiaxed grains, they do not actually include the latent heat in their calculations.It can be argued that the latent heat liberated by the equiaxed grains in the bulk will retard the columnar dendrites in a casting: once the equiaxed grains are sufficiently well-established, the latent heat that they evolve could slow down the columnar growth to such an extent that the equi axed would dominate. Alternatively, the latent heat produced by the equiaxed grains might suppress further equiaxed solidification by raising the bulk temperature. The nature of the thermal interaction between columnar and equiaxed growth is not obvious, and because it is dependent on the material parameters and the dimensions of the system, it cannot be considered effectively in a qualitative way but has to be studied quantitatively: hence the need for the mathematical models discussed in the following pages. The results of the models are discussed in the light of a steady state analysis."

Jan 1, 1986

By Andre Thess, Jurij Kolesnikov, Christian Karcher

"During the motion of molten metal under external non-homogeneous magnetic field the induced electric currents produce Lorentz body forces in the opposite direction to the flow, causing deformation of velocity profile, vortical structures, and adding a pressure drop across the magnetic field. The same Lorentz force acts on the magnet system. We analyse these phenomena in metallurgy, namely, at molten metal pumping, stirring, continuous casting, and in contactless Lorentz force flowmeter (LFF). Experiments with liquid metal alloy, including direct measurements of Lorentz forces, velocities, and flow structure visualization were conducted. Based on this study the industrial prototypes of LFF systems were designed, built, and tested in a secondary aluminium production. A molten metal flow at high temperature (700°C-850°C) can be effectively measured. The LFF technique method allows measuring precisely the volumetric and mass flow rates linked with Lorentz force, and the mass accumulated within production process.IntroductionThe present work demonstrates the development of a non-contact electromagnetic system for measurement of a liquid metal flow. Our approach embodies the Lorentz force velocimetry [1-6] technique which is physically based on a measurement of the force acting on an external magnet system the field of which interacts with the flow. This force is exactly equal to the braking Lorentz force induced in a flowing conducting fluid. In what follows a measurement system based on the Lorentz force velocimetry principle. For monitoring and controlling the production process it is desirable to measure continuously the mean velocity of the liquid metal in order to deduce the mass-flux and volume-flux from it. The form and dimensions of the magnet system are in agreement with geometry of the operating channel. We consider here a version of magnet systems in a composition of permanent magnets.The LFF possesses a number of advantages which make it attractive for the measurement of flows in hot and aggressive melts. The relation between the measured force and the desired volumetric flow rate is often linear (for closed channel or at a constant liquid metal level in open channel). For the converting of the measured force into volumetric and mass flow rate we should know the calibration factor. The calibration factor is independent of the viscosity and density of the liquid metal and depends only on the magnetic field magnitude, the electrical conductivity of the liquid metal and the geometry of the channel in which the liquid metal flows. In aluminium production, for instance, there exists a number of standard alloy compositions having welldefined conductivities for which the calibration factors can thus be tabulated. We consider below consistently effects in liquid metals arising under influencing magnetic field, construction principle of LFF and measurements of metal flows at industrial conditions."

Jan 1, 2011

By M. I. Kalashnikova

Gipronickel Institute has developed the technology of treatment of difficult to concentrate sulphide Pb-Zn concentrates (Zn-19,9%, Pb-8,4%, Cu-0,34%, Fe-8,8%, Ba-6,8%, S-18,7%, Ag-106 g/tonne). The technology consists of pressure leaching, impurity removal from leaching solution, electrowinning and Pb-Ag containing cake treatment. Despite low zinc content in initial concen-trate the technology allows production of solution which is suitable, after standard procedure of impurity removal, for electrowinning with production of zinc grade SHG. Comparing to the standard technologies the flowsheet developed provides the lesser expenses per zinc unit because of decreasing of liquid to solid ratio at pressure leaching stage. The initial concentrate is characterized along with low content of principal metals by high con-tent of barite, which makes flotation of pressure leaching residue more difficult. That is why in this case the hydrometallurgical treatment was chosen. At optimal parameters of chloride leach-ing found during laboratory experiments the principal components extraction was 99.5% for Pb and up to 92% for Ag.

Jan 1, 2006

By Simon Lekakh, Von Richards, C. Hank Rawlins, Kent Peaslee

"Batch aqueous leaching and carbonation tests were conducted using industrial steelmaking slags to determine the effect of carbonic anhydrase enzyme as a catalyst. Calcium leaching is a strong function of particle surface area, and the extent can be expressed as a function of time and particle size. Carbonic anhydrase did not affect the calcium-leaching rate, however, it did catalyze calcium carbonate formation to achieve a neutralization time near the theoretical rate. Additionally, carbonic anhydrase modified the precipitate morphology due to accelerated particle nucleation. Time controlled tests in which the pH dropped to ~6 decreased the amount of carbonate produced, and this effect was exaggerated by carbonic anhydrase, while pH controlled tests (>8.5) exhibited the highest rate of carbonation. Because the leaching rate was ~50% faster than the carbonation rate, a further increase in the amount of carbonation may be realized by using carbonic anhydrase however pH must be >10.3.IntroductionSteelmaking slag contains high fractions of alkaline earth oxide based phases (i.e., CaO and MgO) that exothermically form carbonates. Thus, it is being considered as a means of permanent carbon dioxide sequestration. At current U.S. steel production rates, approximately 13-17 million tons/year of slag are generated from basic oxygen furnace (BOF), electric arc furnace (EAF), and ladle metallurgy furnace (LMF) processes [1]. BOF and EAF slag is used as high quality mineral aggregate or cement clinker, while LMF slag, produced at ~15% the rate of BOF and EAF slags, has limited use as blast furnace flux or acid mine neutralization with the majority going to landfill [2]. Based on slag’s chemical nature and immediate availability as a co-product from steel production, the steel industry initiated a project to investigate hydrous carbonate formation in steelmaking slag as a method of sequestering carbon dioxide emitted in steelmaking offgas [3]. The goal of this project is to determine the reactor parameters suitable for the design of an industrial system for treating steelmaking offgas with raw or minimally processed slag."

Jan 1, 2009

By Wang Jia, Chai Li-yuan, Zhang Jin-Long, Peng Bing, Zhang Qiang

"Electrolytic manganese dioxide (EMD) residue was mixed with shale and fly ash as the main materials to make solidification/sintering brick for the utilization of the residue from EMD production. The effects of sintering temperature, sintering time, solid waste content and cooling process on its mechanical properties and toxic elements solidification were investigated according to compressive strength and leaching toxicity. The results showed that the calcined residue had capability of solidifying toxic metals and exhibited perfect strength after treated in the optimal parameters of EMD residue below 50%, temperature at 1000-1100°C, time3-5h, and semi-quenched at 600°C1 InstructionSolid clay-brick holds the leading position among building materials for a very long time in China. The traditional technique of making clay-brick has the drawbacks of backward process, simple facilities and single product. Since Chinese Reform and Opening-up, urban-rural construction and real estate have been booming with the rapidly development of national economy and science technology. The problems of ruining fertile land, environment contamination and high energy consumption in the traditional technique of clay-brick making have not been solved yet. On the other hand, more than 7 billion tons of industrial wastes are accumulated over years which occupies over 6.7 million hectares filed and causes serious environmental problems[1-31. Strategy present in ""The Chinese Agenda of the 21st Century"" required the production of wall materials less energy conservation, land saving and waste recycling.Coal gangue[4-9l, fly ash[I0- 13l, sludge from waste water treatment and tailings of gypsum, pyrite, copper mine, high silicon containing iron, asbestos and ects [l4-lSJ are the solid wastes used for brick making around the world. There are two kinds of process for brick making, high temperature sintering and low temperature steam curing[19•201. Although the technology of two brick making made great progress and got widely application in construction field, no precedent for preparing sintering-bricks with EMD residue as materials occurred in China because of its complicated processing technics and lack of sufficient practical experience to guarantee the bricks' quality.In this study, EMD residue was mixed with shale and fly ash as the main materials to make solidification/sintering brick. The effects of sintering temperature, sintering time, solid waste content and cooling process on its mechanical properties and toxic elements solidification were investigated according to compressive strength and leaching toxicity."

Jan 1, 2011

By B. Nebreda, I. Vegas, R. Vigil, O. Rodríguez, M. I. Sánchez de Rojas, M. Frías, R. García, J. Urreta

"This paper shows the possibility of reutilize paper sludge waste as supplementary cementing material for the cement manufacture. This industrial waste consists essentially of a mixture of organic matter (30%) and inorganic compound, such as calcite and clay minerals. The raw paper sludge does not present pozzolanic properties, but once calcined at 650ºC during 2 hours, exhibits high pozzolanic activity, similar to silica fume at 28 days, as a consequence of the transformation of kaolinite into metakaolinite. Calcined paper sludge was used as partial Portland cement replacements of 0, 5, 10 and 20%. Enhancement in compressive strength was appreciably obtained for 10 and 20% substitution levels from 7 days on. Furthermore, calcined paper sludge slightly reduces the initial and final setting times of cement paste. Introduction Natural pozzolanic materials have been ordinary used in different aspects of construction, mainly for their influence on the microstructure and durability of blended cement matrixes [1, 2]. Due to the regulations of environmental protection, many researches are focusing on the possibility of obtaining pozzolanic materials from industrial wastes and not from natural materials (ceramic wastes, silica fume (SF), activated clays) [3–5]. One of the most used pozzolanic products is the metakaolin (MK) obtained from the activation of natural clay (kaolinite). The positive effect that MK has on blended cement performances [6,7] and also the influence that curing temperature and matrix nature have on the reaction kinetics and stability of hydrated phases produced during the pozzolanic reaction, according to the studies carried out by Frías et al. [8,9] are well known. However, there is a worldwide trend towards the use of recycled products in cement industry. In this line, some authors have reported an alternative way of obtaining MK from waste paper sludge [10-14]. The raw paper sludge (PS), once calcined under controlled conditions (700-800ºC), produces a MK with pozzolanic properties [15-20]. The present research is part of an experimental study about alternative source for MK from the Spanish paper recycling industry and its use as supplementary cementing material. This contribution pays special attention to the option of reducing activation temperature below 700ºC. This fact has a positive effect in reducing the energy consumption, as well as in reducing environmental impacts associated with decarbonation of calcite. The chemical and mineralogical characteristics of raw paper sludge and derived calcined product are described. In addition, the influence and behavior on blended cement properties (setting times and mechanical properties) are also discussed."

Jan 1, 2008

By Jafar Safarian

A new kinetic modelling technique has been applied to study the rate of MnO reduction from slags by dissolved carbon in liquid iron. Based on a consideration of the fundamental reaction kinetics, a general differential equation for the slag reduction process has been formulated, which then is solved analytically for certain special cases. By re-writing the solutions in a dimensionless form the poorly known kinetic constants are eliminated, which makes the model both flexible and applicable to a wide range of experimental conditions. For example, changes in process parameters such as temperature, metal composition, slag composition, gas composition can readily be captured along with variations in the crucible geometry. Based on a comparison with a series of experimental reduction curves being reported in the literature, it is concluded that the predictive power of the model is surprisingly good, yielding outputs that are both reliable and physically reasonable. An attractive feature of the model is that it provides an alternative way of calculating the activation energies from experimental reductions curves. For example, it suggests that the activation energy for the reduction of MnO by dissolved carbon in liquid iron is about 90 kJ/mol, which is different from the previously reported activation energies. The model also suggests that the crucible geometry, which affects both slag the volume and the resulting slag/metal interfacial area, has a significant influence on the overall reduction kinetics. This design parameter is a key to further optimisation of the process on an industrial scale.

Jan 1, 2006

By Yotamu Stephen Rainford Hara

"The aim of our work is to investigate a low energy and clean route for the recovery of copper and cobalt from complex sulphide mineral concentrates. The mineral concentrates were roasted in air, in the presence of CaO (MS + CaO + 202 =MO+ CaS04) at temperatures below 973K. The roasted products containing CuO, CoO and Fe203 were carbothermically reduced at 1073K within an hour to preferentially reduce copper and cobalt. The kinetics of reactions were studied using the thermogravimetric technique and by characterisation ofreaction products using the XRDSEM-EDX techniques. The effects of MS:CaO ratio, roasting temperatures and physical nature of the mineral concentrates were analysed. The method for capturing S02 by forming CaS04 was analysed for reuse in the process. The energy balance for the above process is compared with that of conventional continuous smelting/converting process.1.0 IntroductionCopper sulphide mineral concentrates from Zambia contains substantial amouot of cobalt. The cobalt metal content in the concentrates ranges between 0.7 and 2 % weight, which corresponds to 3 and 9 % weight copper, based on the spot price of copper ($7 386/tone) and cobalt ($31 000/tone). Although the traditional approach using a combination of roasting-leaching-electrowining steps can be applied to recover copper and cobalt from sulphide mineral concentrates [1-4], there are two major draw backs of the traditional process: (i) the S02 emitted during roasting is too lean for economical conversion for sulphuric acid manufacture, which causes serious environmental pollution. (ii) silver and gold which are normally present in the sulphide concentrates are lost out [5] because they are not leachable by H2S04 or HCl which are the common leachants. The above two problems have been overcome by adopting flash smelting in which a rich S02 gas above 20% is produced [1, 5] and successfully converted into sulphuric acid. The precious metals tend to partition to blister copper and recovered during refming. However, nearly all cobalt is lost into the slag phase uoder oxidising condition which prevails during flash smelting. It is important to note that the cobalt content in the slag can be up to 2.6 % weight [6]. The recovery of cobalt from the slag is a process which requires huge amouot of energy since the slag is smelted above 1873K [6]. With a view of minimising the amouot of energy and S02 emission during metal recovery, our investigation involves roasting the sulphide concentrates in the presence of lime and reducing the roasted samples with carbon."

Jan 1, 2013

By Hong N. Vu, Jitka Jandova

"Gypsum and limestone methods were examined in this study to process zinnwaldite wastes originating from dressing Sn-W ores mined in the Czech Republic. These wastes containing 0.20-0.30% Li and 0.10-0.20% Rb were subjected to magnetic separation to obtain a zinnwaldite concentrate with 1.36% Li and 0.94% Rb. It was observed that processing of the zinnwaldite concentrate with gypsum resulted in almost 96% recovery of Li into aqueous liquors, whilst rubidium extraction was only 25%. At the same time, it is possible to extract almost 92% Li and Rb from the identical zinnwaldite concentrate if the concentrate is processed by limestone method. Lithium carbonate, a final product of both methods was recovered from the refined sulphate solution using K2CO3 as a precipitation agent and/or from unrefined hydroxide solution using gaseous CO2. In the continuation of this study, rubidium will be separated from carbonate solutions after Li2CO3 precipitation as RbAl(SO4)2, an intermediate for Rb2CO3 production. IntroductionLithium is used as an alloying constituent in lightweight alloys, as a heat transfer medium in nuclear reactors and as a component in primary and secondary batteries. With the development of a new generation of electric vehicles, the lithium demand will dramatically grow. Lithium chemicals find extensive application in many industrial branches such as metallurgical, glass, ceramic and pharmaceutical industries. Rubidium compounds are predominantly used in psychiatry and medicine, in magneto-optic modulators, solid-state lasers, phosphors and components of electrolytes for fuel cells. The four most important lithium minerals are amblygonite, spodumene, petalite, and lepidolite. Spodumene LiAlSi2O6 (6.0-7.5% Li2O) and petalite LiAlSi4O10 (3.5-4.5% Li2O) belong to aluminosilcate minerals. Lepidolite (Li.Al)3(Al.Si)4O10(F.OH)2 (3.30-7.74% Li2O), lithium mica, is the most important representative of the mica minerals, a subgroup of the aluminosilicates. It frequently contains 3–5% Rb2O and eventually caesium. Zinnwaldite, which has the general formula K(Li.Al.Fe)3(Al.Si)4O10(F.OH)2 (2-5% Li2O), is regarded as a variety of lepidolite with a high iron content. Commercial amblygonite is a complex phosphate (Li.Na)Al(F.OH)PO4 (up to 9.88% Li2O), however, its deposits have not been commercially exploited because of their small size. Natural brines with a high lithium chloride content are important in the industrial production of lithium [l]"

Jan 1, 2008

By A. Siegmund, R. D. Prengaman

Lead anodes used in zinc electrowinning generally contain 0.5 - 1.0 % silver to reduce the rate of corrosion over the service life. For good quality zinc, the cathodes must contain less than 10 ppm lead. In order to reduce the lead contamination of the cathode, the lead anode must become coated with a protective layer of Pb02/Mn02. The formation of this layer may take as long as 30 - 60 days, during which time zinc production is substantially reduced and the cathodes are contaminated with lead. To improve the mechanical properties of Pb-Ag-anodes alloying elements such as calcium, strontium, barium and others are added. The production of cast lead-silver or lead-silver-calcium anodes often results in the formation of numerous holes, voids or laps in the anode surface that can initiate localized internal corrosion. Based on the experience as the major supplier of rolled anodes for copper electrowinning, RSR Technologies has developed an improved anode for zinc electrowinning. The anode consists of a rolled Pb- Ag-Ca-alloy with a controlled surface grain structure. It forms an adherent protective oxide coating within 2 - 3 days when placed in an electrowinning cell. The preferred calcium and silver contents of the alloy are 0.03 - 0.08 % and 0.3 - 0.4%, respectively. Rolling sheets significantly reduces the presence of internal porosity or laps. The lack of defects results in long anode life. The rolling also produces a uniform grain structure to which the corrosion product readily adheres, thus significantly reducing the conditioning period.

Jan 1, 2000

By Nieves Iglesias

The removal of the refractoriness of a gold bearing pyrite- arsenopyrite ore is studied. Flotation concentrates were prepared and leached with a dilute acidic ferric sulfate solution. The elemental sulfur film which forms on arsenopyrite in the oxidation process is not responsible for the low rate of the arsenic dissolution observed. A positive effect on the leaching rate is observed when Ag' is added. This pretreatment eliminates the refractory nature of concentrates.

Jan 1, 1993

By Y. Moriya, Y. Sadayoshi, Y. Nonogaki, Y. Takeda

"Preparation and growth processes of CaF2 on Si(111) and of . InxGa1-x,As islands on CaF2 by molecular beam epitaxy (MBE) are described. It was found that first of all the Si(111) surface treatment process to obtain the 7x7 reconstructed structure was necessary to ensure the cleanness of the surface and to grow a flat and high quality CaF2 on it. Growth of InxGa11-x,As islands on CaF2 was tried by droplet heteroepitaxy using the same MBE reactor. In,GaxGa1-xAs islands were successfully grown epitaxially, and the size and density of the islands dependent on the In composition were investigated.IntroductionThough semiconductor/semiconductor heterostructures are widely used for many device applications, small band off-sets of the conduction bands and the valence bands restrict the utilization of the intra-subband transitions to far-infrared regions. With InAs as the quantum well and fluorides as the barrier layers, we can design three-electronic-level systems in the infrared region, which is the low loss transmission window of the silica optical fibers. To realize those structures, we have grown InxGa1-xAs islands on CaF2 thin films that were epitaxially formed on Si(111) substrates by molecular beam epitaxy. By the droplet heteroepitaxy that we invented, the InxGa1-xAs islands with height of -10 nm have been obtained successfully. Optimum processing to obtain atomically smooth surfaces of Si and CaF2 and high quality InxGa1-xAs islands is reported.ExperimentsMBEMachineCaF2 was grown on Si(111) and InxGa1-xAs islands were grown on CaF2 successively by MBE. The MBE machine consisted of a growth (or reactor) chamber and a loading chamber. The reactor chamber was equipped with Ga, In, As and Er metal source cells and CaF2 and BaF2 source cells. Cell materials were P-BN for Ga, In and As metals, and were graphite for CaF 2, BaF 2 and Er to avoid reaction with BN cells. The electron gun and screen were attached to the reactor to observe the RHEED pattern during the substrate surface treatment and the growth of CaF2 and InxGa1-xAs islands. The substrate manipulator was designed to heat up the Si substrate up to 1,200°C for the surface cleaning. The QMS was also equipped to analyze the residual gas species in the reactor chamber. The base pressure of the reactor chamber was 2-5x10-11 Torr, being pumped by ion pump and the liquid nitrogen shroud"

Jan 1, 2000

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By W. Kunda

A laboratory study was carried out on the treatment of sulphidic copper concentrates in aqueous chloride systems under elevated temperatures and oxygen overpressure. Exploratory tests showed that chalcopyriteoxidizes with various chloride salts to form, depending upon the pH of the system, soluble copper chloride or insoluble copper oxychloride salts; the copper can then readily be recovered from the solution or residues respectively. During the leaching, iron was oxidized to iron oxide and remained in the leach residue while the bulk of the sulphide sulphur was oxidized to the elemental form with a minor portion oxidized further to sulphate. The presence of metal chloride salts in the system increased the oxidation rates of chalcopyrite and depressed the solubilization of iron in the system. A systematic oxidation leach study carried out in (1) ammonium chloride and (2) sodium chloride systems showed that the former system required little or no HC1 addition while the latter required 2 mol of HC1 per mol of dissolved copper (plus zinc). The copper was recovered from the cuprous or cupric chloride leach solutions by cementation with iron. Extractions of 99% copper and zinc, 97% silver, and negligible iron were obtained. Sulphur was oxidized to the elemental or sulphate form; the relative proportions of the total sulphur were 60 and 30% for system (1) and 80 and 10% for system (2). A flowsheet for a conceptual process with minimal reagent requirements was proposed.

Jan 1, 1976

By C. L. Kusik

Environmental issues are having a significant impact on how automobiles are designed and ultimately disposed of at the end of their lives. On one hand, increasing concerns about landfill disposal have resulted in greater attention being focused on recycling materials and components from old junk autos. On the other hand, corporate average fuel economy (CAFE) requirements have led to downsizing, use of coatings, materials substitution and other measures that often make recycling more difficult. Automobile makers have responded to Corporate Average Fuel Economy (CAFE) Standards in a variety of ways such as: Downsizing; Designing of more fuel efficient engines; Reducing aerodynamic drag by sleeker body designs; Redesigning by using thinner gauges of coated steels; and Substituting material such as lightweight plastic or aluminum parts for steel. Other driving forces affecting production techniques, choice of materials and recycling issues include the Clean Air Act and its amendments, RCRA. and other environmental legislation. The variety of materials used in automobiles makes the recycling issue extremely complex. Not only does one have different materials used in different automobiles for making similar parts, but changing designs, evolving environmental issues, landfill closures affecting solid waste disposal, and increasing raw material quality standards have created a complex set of dependencies related to materials use and recycling.

Jan 1, 1994

By Daniel Chen, Jewel Andrew Gomes, Venkata Palla, Sadia Afrin Jame, David Cocke, Paul Bemazzani

"Textile industries use various kinds of chemicals including dyestuffs and pigments during dyeing and finishing processes. The effluent from these processes includes suspended particles, strong color, high pH and high chemical oxygen demand (COD) that are extremely toxic and make environmental hazard. Although physical, chemical, photochemical, and biological methods are available for treating such wastewater, the electrochemical technique, electrocoagulation (EC), has emerged as an efficient, simple, and cost-effective technology in the last few decades. In this study we present the applicability of EC technique for removing dye, such as direct red dye using iron electrodes, and the optimized conditions such as dye concentration, current density and pH. The degradation of dye molecules was investigated using UV-visible spectroscopy. The EC-floe was also characterized using SEM/EDS, XRD and FTIR.IntroductionWastewaters generated by textile industries contain large amounts of toxic aromatic compounds, especially azo dyes. Azo dyes and their degradation products, such as aromatic amines, are highly carcinogenic. These effluents are also responsible for causing high levels of color. The colored wastewater released into the environment is also a source for disruption of aquatic life and aesthetic pollution as well [1].In most textile industries, dyeing and finishing are the two important processes which are generally applied. These two common processes generate significant amount of wastewater, which may contain, suspended particles, high pH, strong color and high chemical oxygen demand (COD) concentration [2]. Low pH and high temperature are other polluting factors from the waste water. Textile industries make use of about 10,000 dyes and pigments [3]. Disposal of these colored wastewaters poses a major problem for the industries as well as a threat to the environment. In textile industries, because of the low efficiency (60-90%) of dye fixing on textile fibers, substantial amounts of unfixed dyes are released in waste waters. The conventional method for treatment of textile wastewater was a combination of biological, physical and chemical methods [2]."

Jan 1, 2011

By Yan Yuan

Stable Nitroxyl polymers, such as poly (2,2,6,6-tetramenthyl-1-piperidinyloxy-4-yl methacrylate) (PTMA), are known to be effective as cathode active materials for lithium rechargeable betteries.The nitroxide radicals displayed a reversible and very rapid redox performances.We present a new synthesized method to get PTMA powder, then a doctor-blading method was used to prepare the PTMA composite electrodes, enabling successful production of homogeneous electrodes. It was characterized through FT-IR and SEM methods.The organic radical battery consists of lithium metal anode and PTMA cathode with an active material content of 65wt%.The best performance is achieved with a thin cathode that shows nearly 100% utilization of the active material (111mAh/g) at 0.1C.Through the electrochemical tests, it was found that there was a stable plateau at 3.5V while discharging. Besides, the cycling stability and rate capability were measured in detail. Although they showed a certain quantity of irreversible capacity on the first cycle, the capacity stabilized after the second cycle.

Jan 1, 2009

By Alana Pereira Ramos, Walman Benicio de Castro

Amorphization and martensitic transformation (Ms) characteristics of Ti–Ni-Cu alloy ribbons prepared by melt spinning were investigated by means of differential scanning calorimetry and X-ray diffraction. In these experiments particular attention has been paid to change the wheel linear velocity from 21 to 63 m/s. Then the cooling rates of ribbons were controlled. The effect of this cooling rate and alloy composition on martensitic transformation behavior is discussed.

Jan 1, 2015