By E. A. Gulbransen, J. W. Hickman

The physical and chemical structure of the oxide films formed on metals and alloys is of interest in our understanding of their protective properties. According to Pilling and Bedworth,¹ if the specific volume of the oxide is equal to or greater than that of the metal, a compact or continuous structure results; if the volume of the oxide is less, a cellular or porous structure forms. With the cellular type of coating the surface layer of oxide offers no impedance to oxidation; at a given temperature the rate of oxidation is quite constant. On the other hand, the compact type of coating acts as an effective barrier to oxygen and the rate of oxidation will follow a parabolic law. The recent work of Gulbransen2 and of Leontis and Rhines3 on the oxidation of magnesium indicates that it is not necessary for the volume of the oxide to be greater than that of the metal in order that the oxidation may follow a parabolic rate law. One exception to the rule of Pilling and Bedworth¹ is noted by Scheil;4 namely, tungsten. At 500° and 700°C long-time oxidations indicate a linear rate law with time. However, Dunn's6 0xidation measurements from 700°to 1000°C indicate that a parabolic rate law is followed. The oxide is mainly yellow WO a with a thin layer of the blue oxide. Preliminary results on the oxidation of tungsten6 in the temperature range 400° to 500°C indicate that the oxidation does proceed according to a parabolic rate law. Irrespective of the actual rate law that tungsten may obey, it is of interest to compare the results obtained on the oxidation of tungsten in the thin film region with those found when the metal is scaling. A time-temperature study of the oxides formed on both molybdenum and tungsten may indicate whether there exist any peculiarities in the oxide structures of the thin film region compared with those of the scaling region of oxidation. In a recent paper the authors7 presented an investigation of the structures of the oxide films formed on the metals iron, cobalt, nickel, chromium and copper. The results of these studies are presented in graphical form as existence diagrams of the oxides on a time-temperature scale. The existence diagrams of the oxides occurring on some of the metals are simple and show few chemical transitions, but there are many cases in which the physical state of the oxide surface changes as a function of time and temperature, as evidenced by the appearance or disappearance of orientation effects and sharpness of patterns. In general an increase in temperature results in an increase in

Jan 1, 1947

By George Sachs

I deeply appreciate the honor of being selected to deliver the twentieth Annual Lecture of the Institute of Metals Division. The subject of my paper is extremely involved and voluminous, therefore I shall discuss only some more recent experimental material and speculate somewhat on the physical and mechanical fundamentals of these changes. The flow and the rupture of a solid material are rather different phenomena. It is therefore surprising that up to a rather advanced stage in metallurgical science these two fundamental phenomena have been simultaneously treated and forced into the general conception of the "failure " of solid material. Only in this century, and particularly during the last 20 years, have the very different physical meanings of flow and rupture been clearly recognized. Several hundred of the more recent publications deal with these subjects.l Law of Similarity The basic values commonly considered responsible for the mechanical behavior of any material are the stresses. From this standpoint both a large and a small article made from the same homogeneous metal and of geometrically similar shapes should behave identically, i.e., they should deform geometrically in a similar manner, if subjected to the same stress values at corresponding points. This "law of similarity" was introduced about 60 years ago simul- taneously by Barba2 and Kick3 and was derived from the classical theory of elasticity. As far as the plastic behavior of a metal is concerned, this rule appears to be valid. The conventional properties of large and small tension or compression test bars, machined from larger sections, are identical; while the force required to deform a section is proportional to its cross-sectional area and the work consumed in deforming geometrically similar articles in a geometrically similar manner is proportional to its volume. The general trend of the stress-strain diagram of a metal is independent of the section size (Fig. I). No exceptions from this rule are known. However, if the deformation of a metal is continued until rupture occurs, and the breaking stress or the work consumed is measured, a test bar of large cross section appears to fail before or at lower stresses than does one having a small cross section. Thus, the specific impact energy has been often found to decrease with increasing size of the test specimen, particularly for materials with a limited ductility.4 Another exception from the rule of similarity is offered by fatigue-strength values, which usually decrease with increasing section size.6'6 The conclusion must be drawn from these experimental facts that the ductility of a homogeneous metal decreases with increasing section size (Fig. I). This effect has been actually confirmed by Docherty,7 who observed that in static notch bending tests large specimens failed earlier and in a more brittle fashion than small specimens ma-

Jan 1, 1941

By J. W. Hickman, E. A. Gulbransen

In a previous paper' the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300' to 7o0°C. except for copper, wherc the range selected was 100' to 500°C. The results of these studies were presented in graphical form as existence diagrams of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviatiois in lattice Darameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: 1. The existence diagrams of various alloys. 2. The effect of the structure of the alloying metal on the existence diagram of iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body-centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K4²B, Nichrome V, Hipernik, Inconel, Stellite "²I," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1947

By George Sachs

I deeply appreciate the honor of being selected to deliver the twentieth Annual Lecture of the Institute of Metals Division. The subject of my paper is extremely involved and voluminous, therefore I shall discuss only some more recent experimental material and speculate somewhat on the physical and mechanical fundamentals of these changes. The flow and the rupture of a solid material are rather different phenomena. It is therefore surprising that up to a rather advanced stage in metallurgical science these two fundamental phenomena have been simultaneously treated and forced into the general conception of the "failure " of solid material. Only in this century, and particularly during the last 20 years, have the very different physical meanings of flow and rupture been clearly recognized. Several hundred of the more recent publications deal with these subjects.l Law of Similarity The basic values commonly considered responsible for the mechanical behavior of any material are the stresses. From this standpoint both a large and a small article made from the same homogeneous metal and of geometrically similar shapes should behave identically, i.e., they should deform geometrically in a similar manner, if subjected to the same stress values at corresponding points. This "law of similarity" was introduced about 60 years ago simul- taneously by Barba2 and Kick3 and was derived from the classical theory of elasticity. As far as the plastic behavior of a metal is concerned, this rule appears to be valid. The conventional properties of large and small tension or compression test bars, machined from larger sections, are identical; while the force required to deform a section is proportional to its cross-sectional area and the work consumed in deforming geometrically similar articles in a geometrically similar manner is proportional to its volume. The general trend of the stress-strain diagram of a metal is independent of the section size (Fig. I). No exceptions from this rule are known. However, if the deformation of a metal is continued until rupture occurs, and the breaking stress or the work consumed is measured, a test bar of large cross section appears to fail before or at lower stresses than does one having a small cross section. Thus, the specific impact energy has been often found to decrease with increasing size of the test specimen, particularly for materials with a limited ductility.4 Another exception from the rule of similarity is offered by fatigue-strength values, which usually decrease with increasing section size.6'6 The conclusion must be drawn from these experimental facts that the ductility of a homogeneous metal decreases with increasing section size (Fig. I). This effect has been actually confirmed by Docherty,7 who observed that in static notch bending tests large specimens failed earlier and in a more brittle fashion than small specimens ma-

Jan 1, 1941

By E. A. Gulbransen, J. W. Hickman

In a previous paper' the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300' to 7o0°C. except for copper, wherc the range selected was 100' to 500°C. The results of these studies were presented in graphical form as existence diagrams of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviatiois in lattice Darameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: 1. The existence diagrams of various alloys. 2. The effect of the structure of the alloying metal on the existence diagram of iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body-centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K4²B, Nichrome V, Hipernik, Inconel, Stellite "²I," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1947

By B. M. Larsen, L. S. Darken

SOME years ago we collated all laboratory data then available to us on the distribution at equilibrium of manganese and of sulphur between metal and simple slags, and used the results in setting up an equation, which proved to be in accord with determinations of the distribution ratio of manganese and of sulphur between liquid steel and open-hearth slag, over a wide range of operating conditions. We now present an outline of our calculations and inferences on these two closely related questions, which are of especial importance because of the advisability of conserving manganese wherever possible. In general. our results show that in the open-hearth furnace equilibrium between metal and slag, with respect to both manganese and sulphur, is substantially attained during the finishing period of the heat, or in about a half hour to an hour after any additions were made. This implies that the end result will be identical whether manganese is added as alloy or metal to the liquid steel or as oxide to the slag. The proportion of total manganese retained by the steel is favored: (I) by use of the minimum amount of lime, consistent with other operating limitations, required to give a lime-silica ratio of about 2.4, which usually corresponds to a minimum practical slag volume; (2) by a high concentration in the slag of MnO relative to FeO; (3) by high operating temperature. Absorption of sulphur by the slag from the liquid metal is favored: (I) by large slag volume; (2-by a high concentration of active (or "free") lime and of manganese oxide dis) solved in the slag; (3) by low concentration of silica, iron oxide, and phosphate dissolved in the slag. DISTRIBUTION OF MANGANESE BETWEEN SLAG AND METAL AT EQUILIBRIUM On the basis that the distribution of manganese between liquid steel and slag is controlled by the reaction [FeO + Mn ;7± MnO + Fe [A] slag metal slag metal] the distribution at equilibrium, at a given temperature, is expressed by the equilibrium constant for this reaction, which is defined as [K" aFPI OFeO ? aMn] where a is the activity of the molecular species denoted by the subscript. The activity of each of the several components, although it is not known precisely, is approximately equal to the concentration of each component expressed as its mol fraction; that is, as the ratio of the number of mols of the given component to the total number of mols of all the molecular species present in the metal or slag, as the case may be. Moreover, since the activity, or concentration, of iron in the liquid metal is in fact substantially constant, the term aFe may he combined with K" to give a new constant K'. Making these changes.

Jan 1, 1942

By Arthur Smith

THE Verde mining district is in Yavapai County, in north-central Arizona. Jerome, the principal town, has a population of 6000 and the two important mines of the district-the United Verde and the United Verde Extension-lie almost within its limits. Perched high on the southwest side of the Verde valley, at elevations of 4800 and 5500 ft. (1463 and 1676 m.) respectively, both mines have long tunnels from their lower levels through which the ore is hauled to the smelters. Clarkdale, the smelter town for the United Verde mines, lies in the Verde valley 4.1 miles (6.5 km.) distant in an air line from Jerome and at an elevation of 3560 ft. The two towns are connected by the standard-gage railroad of the Verde Tunnel and Smelter R. R., a subsidiary of the United Verde Copper Co. This road is 11 miles long and has a compensated grade of 4 per cent. At Clarkdale it connects with the Verde valley branch of the Santa Fe railroad. Clemenceau, the smelter town for the United Verde Extension mine, lies 3.5 miles (5.8 km.) in a southeasterly direction from Clarkdale, at an elevation of 3420 ft. It is connected to the Verde Valley branch of the Santa Fe railroad at Clarkdale by the Arizona Extension R. R., . a subsidiary of the United Verde Extension Mining Co. The portal of the haulage tunnel, at an elevation of 3757.5 ft., is also connected with the smelter town by 4 miles of standard-gage track belonging to? the same company. In the vicinity of Jerome, the great southern escarpment of the Arizona plateau forms the northeast side of the Verde valley. The general level of this escarpment, or "rim" as it is called, is about 4000 ft. above the Verde River. A corresponding elevation is reached only by the highest peaks of the Black Hills, which bound the valley to the southwest. Two lava-capped mesas, known as "Mingus" and "Wood chute mountains," form the culmination of the Black Hills. That part of the Old Black Hills mining district which lies between their crests and the Verde River is now known as the Jerome, or Verde, mining district. If the . smelter towns are not included, a strip about 7 miles long by 3 miles (11 by 5 km.) wide, embraces practically all of the properties belonging to the Jerome district. This strip lies parallel to and along the side of the Verde valley from First View, 2 miles northwest from Jerome, to the vicinity of Allen Springs, at the south end of Mingus mountain and all within the boundaries of the Prescott national forest reserve.

Jan 3, 1924

By W. C. Ellis, M. E. Fine

INTRODUCTION IN the iron-cobalt system there are several property-composition relationships of theoretical importance. The alloys are ferromagnetic exhibiting a maximum saturation at approximately 33 at. pct cobalt;1 the interatomic distances at room temperature show large positive deviations from Vegard's rule;2 and in the region of 50 at. pct cobalt there is an order-disorder transition which has a large effect on other properties. The thermal expansion data for the system have been reported3,4.5,6 only from room temperature to 100°C, and for this temperature range a minimum in coefficient in the region of 50 at. pct cobalt is well established. 3,4,6 This paper reports the expansion properties in the iron-cobalt system for temperatures from 30 to 850°C, shows the correlation with other physical properties, and proposes an explanation for the interrelation. EXPERIMENTAL PROCEDURE The thermal expansivities of iron-cobalt alloys in 10 pct steps in composition were determined from 30 to about 850°C. The major series of alloys was prepared by induction melting from Armco iron and cobalt rondelles with the addition of about 0.6 wt pct manganese. This series was supplemented by three compositions: high purity electrolytic iron, high purity electrolytic cobalt, and an alloy of 52.1 wt pct cobalt prepared from the high purity electrolytic iron and electrolytic cobalt by vacuum-melting. The compositions of both series of alloys are given in Table I. The specimens for measurement were prepared from the cast ingots by first hot-swaging followed in most instances by cold-swaging to 0.180-in. diam rod. Some alloys in the region of 50 pct cobalt, because of inherent cold-brittleness, were swaged hot to the final diameter. The expansion specimens were approximately 2 ½ in. long with flat-ground and polished ends. Before measurement they were annealed in hydrogen for r hr at 900°C. In the apparatus used for the thermal expansivity measurements (Fig I), a modification of that designed by Hidnert and Sweeney,7 the differential expansion between the specimen and vitreous silica was measured by a dial micrometer reading to 0.001 mm. An invar fixture supported the dial gauge, and this fixture, in turn, was connected to a split invar collar which supported the outer silica tube. A pyrex "T" was placed over the outer silica tube and was sealed to the invar collar by Apiezon Q sealing compound. A movable hollow vitreous silica rod which rested on top of the test specimen slid through a flexible rubber diaphragm cemented to the top of the pyrex "T." The specimen rested on a vitreous silica pedestal fused into the outer tube and was kept centered by a silica sleeve. A non-oxidizing atmosphere was obtained by admitting hydrogen into the

Jan 1, 1948

By E. F. Sturcken, J. W. Croach

A grain orientation distribution function, P(u,F), was developed for use in predicting physical properties in oriented metals. Examples are given of the use of the function to predict thermal expansion coefficients in rolled uranium rods and plate. The P(u,F) function was synthesized from X-ray difpaction intensity measurements, Ii, norrnally used to plot inverse pole figures. The symbols u and F specify the angles that the crystallographic axes of the grain make with the normal to the sample surface and P(u, F) gives the number of grains oriented in each direction, (u,F). P(u,F) is obtained from a least squares fit of the Ii to an orthonormal set of spherical harmonic functions. The P(u, F) function was also used to define a quantity, J, which is a measure of the departure of the orientation distribution from unifomzity (or "randomness"). The J parameter may be used to follow, quantitatively, the amount of preferred orientation induced as a function of mechanical working or heat treatment. An example is given of the application of the J parameter to prefevred orientation studies of hot- and cold-rolled uranium rods and hot-rolled uranium plate. Because P(u,F) is derived from relative intensity measurements by the powder diffraction technique, it is applicable to material with large absorption coefficients and/or grain size and is particularly suitable for characterizing the preferred orientation of large numbers of samples such as fuel elenzents for a nuclear reactor. IN general the physical properties of an oriented metal depend on the direction in which the properties are measured. Hence to predict physical properties the grain orientation must be known as a function of the direction of the specimen. The conventional methods of expressing preferred orientation measurements are the pole figure1 and the inverse pole figure.2-8 Both methods are difficult to use for predicting physical propertiess because they are graphical and because they are stereographic projections and hence are not "area-true." In the present report a quantitative orientation distribution function, P(u,F), is synthesized from pole density measurements normally used to plot inverse pole figures. For inverse pole figure plots the pole densities, pi, are obtained by powder dif-fractometer intensity measurements of their reflections from a flat surface of the sample, normal to the direction of interest. Each pole density, pi, represents a single orientation, i, and is proportional to the volume of material with orientation, i; hence a set of pi gives an approximation for the general orientation for the sample direction measured. The expression8'7 for calculating the pole densities, pi, from the diffraction measurements was previously

Jan 1, 1963

By Herman Garlichs

THE development of the extensive Southeast Missouri deposits greatly preceded that of the Iowa and Wisconsin deposits. It began about 1720 at Mine La Motte and other localities, and has continued uninterruptedly to the present time. It is estimated that this district produced about 184,000 tons of lead in the year 1916, having a value of approximately, $25,000,000. This is a new high record. The Southwest Missouri orebodies were hardly known before 1845 and were not extensively developed until 1870: Lead production in South-west Missouri for 1916 was 38,788 tons. Oklahoma produced 14,399 ,tons and Kansas 2,345 tons, making a total for Southwest Missouri, and the adjoining districts in Oklahoma and Kansas, of 55,532 tons of lead. The first metallurgists in Missouri were the Indian and the hunter. The early settler learned to procure his bullets either by melting ore in his camp fire or by throwing pieces of galena on an old stump and depending on the usual roasting and reaction method to obtain the metal. A little more refined method was to arrange two flat stones in the form of a V. Wood and galena were placed in the furnace and ignited. As heat developed, some of the metal was extracted and molded into bullets. The next step in utilizing the lead ores was the log hearth. All lead in Missouri was smelted in this crude affair before 1820. It was built on sloping ground, and consisted of a hearth of stone, surrounded on the front and two sides by a stone wall. The wall was 7 ft. high in front. The top and rear end were left open and in front an arch or opening was made, forming the eye of the furnace. In front of this a pit was dug in the ground, to receive the molten metal. Large logs were rolled in at the back and made to rest upon ledges formed inside, to raise them from the hearth and to give a draft. These logs filled the entire width of the furnace. Small split logs were then set up around the two sides and the front, and the ore was piled on until the furnace was full. Finally, the mass was covered with logs and fuel until the ore was completely surrounded. A gentle heat was started, which was raised very gradually. After 12 hr. the heat was increased and continued for 12 hr. more, 24 hr. being required, for each smelting. The furnace treated about 5,000 lb. per 24 hr. and the ore yielded about 50 per cent. of its metallic lead. A considerable quantity of the ore was not desulphurized, and fell between

Jan 7, 1917

By John E. Conley

The slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. Use of Waste Slates for Making Aggregates The lightweight-aggregate industry has been discussed elsewhere4,5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. Requirements for Raw Materials As pointed out by Hughes,4 the lightweight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of ally low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig, I illustratcs the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By John E. Conley

The slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. Use of Waste Slates for Making Aggregates The lightweight-aggregate industry has been discussed elsewhere4,5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. Requirements for Raw Materials As pointed out by Hughes,4 the lightweight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of ally low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig, I illustratcs the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By H. l. Burghoff, C. H. Mathewson

THE study of the creep of metals under conditions of prolonged loading has received the attention of many investigators for several years and almost innumerable papers have been published on the various aspects of the subject. As it appeared that much could still be learned from a study of single crystals, the present work was carried out to study the effects of temperature and conditions of loading upon the properties and deformation in tension of single crystals of alpha brass containing about 70 per cent copper and 30 per cent zinc. In particular, it was hoped to obtain information from tests below and above the recrystallization temperature of the material, so that properties such as elastic limit, yield point or critical stress, and manner of deformation might be compared for tensile tests at an ordinary loading rate and for prolonged. loading. Accordingly, short-time tensile tests and creep tests were made at room temperature, 300º, 500° and 700°F. The two latter temperatures are above the lowest possible recrystallization temperature of polycrystalline 70-30 brass. PREVIOUS WORK Clarke and White1 have made creep tests of some copper-zinc alloys, including 70-30 brass, and copper-zinc-tin alloys at temperatures both below and above the recrystallization temperature of the materials considered. Hanson and Wheeler have studied the flow and fracture of single crystals of aluminum for short-time and prolonged tensile loading over a range of temperature extending from room temperature to 400°F., their experiments being made without consideration of the orientations of the test specimens. Extensive creep and fracture tests on single crystals of lead at room temperature have been made by Betty3 and by Baker, Betty & Moore.4 Results of the last-named investigation were published while the present work was in progress. Millers examined the elastic limit of zinc single crystals at and above room temperature by means of creep tests, while Miller and Milligan6 reported the results of tests designed to show the influence of temperature on elastic limit of single crystals of aluminum, silver and zinc. The behavior, of iron crystals under static tensile loading at room temperature was reported by Gensamer and Mehl7 while the present investigation was in progress. Their specimens exhibited a well-defined yield point, below which no appreciable creep could be detected. The manner of yielding proved interesting, as the shape of the creep-time curve for the iron crystals differed from the common type of creep curves. Elongation did not begin immediately, or at least was initially very slow. The rate of elongation then increased continuously and finally decreased to zero. This S-shaped type of elongation-time

Jan 1, 1941

By E. C. Bohlen, H. l. Burghoff

THE work reported in this paper was carried out to supplement the existing information concerning directional properties and recrystallization textures of annealed brass sheet and strip. These characteristics are of direct interest when the forming and drawing properties of such material are being considered. Among those who have made contributions in this field are Bass and Glocker;1 Bauer, Göler and Sachs;2 Phillips and Samans;3 Pratt;4 Price;5 Cook;6 Richards;7 Brick;8 and Brick and Williamson.9 These investigators have found, in general, that in brass strip that shows directional variations in properties, tensile strength has a minimum value and elongation has a maximum value at 45° to the rolling direction. The most pronounced directional properties have been found in material given the greatest reductions in rolling followed by high annealing temperatures. Recrystallization texture of brass has been variously reported as (113)[112], (001)[100], and a combination of (110)[115] and traces of the primary rolling texture, (110)[112]. The directional studies have been very informative, but actual tests appear to have been confined to material in its final condition. Tests at intermediate stages have received little attention although previous history of some materials has been partly considered. Perhaps the most comprehensive investigation was made by Cook,6 who studied the directional properties of 70-30 brass strip for which the final and penultimate, or next to the last, anneals and the final reductions were varied. He found that, for any given combination of penultimate anneal and final reduction, the tendency toward the development of directional properties was reduced as the temperature of the final anneal was decreased. In addition to drawing cups and making tensile tests of the finished material at various angles to the rolling direction, he measured the frequency and the angles of twins in grains for several specimens. Plots of his twin counts showed directionality for the materials that produced eared cups. TEST MATERIALS AND EQUIPMENT For this investigation, one commercial heat of 68-32 brass was cast in the form of bars for cold-rolling, 13 ½ in. wide and 1 ½ in. thick. The analysis was as follows: 68.83 per cent copper, 0.04 per cent lead, 0.01 per cent iron, 31.12 per cent zinc (by difference). The bars were so processed to the final thickness, 0.020 in., as to obtain on this thickness all possible combinations of the variables listed below except those involving the sequence of 84 per cent penultimate reduction and 84 per cent final reduction: I. Penultimate reductions of 37 per cent, 50 per cent and 84 per cent; 2. Penultimate anneals at 800°, 900°, 1050° and 1200°F.; 3. Final reductions of 37 per cent, 50 per cent, 69 per cent and 84 per cent;

Jan 1, 1942

By Jack A. Crichton, Henry J. Gruy

This paper discusses methods used in the estimation of natural gas reserves and the general conditions under which the various methods are applicable. The factors used in estimating natural gas reserves are reviewed. Errors which have been found to occur frequently are listed. Introduction The estimation of natural gas reserves has become of paramount interest because of the increasing importance of gas in the nation's economy. Gas is a most desirable fuel, a fact substantiated by the continued rise in the market demand. In addition, new uses for gas are being developed by the chemical, plastic, and associated industries, and plants are being built to make gasoline from natural gas. These are a few of the factors contributing to the importance of the nation's natural gas reserves. With the increased importance of gas there is an increase in the need for reliable estimates of the magnitude and availability of natural gas reserves. These estimates are being used currently: (I) to determine which fields contain sufficient available reserves to justify the construction of pipe-line outlets to serve particular markets; (2) to design pipe lines necessary to serve those fields adequately;] (3) to determine the location of industrial and chemical plants; (4) to finance the development of gas properties, and the construction of gas pipe lines; (5) to determine fair and adequate depletion allowances and depreciation rates; (6) to justify applications for gas pipe lines before various regulatory bodies; (7) to determine the number of wells required to exploit the reserves most economically; (8) to aid in establishing values for the purchase or sale of gas properties, and for purposes of inheritance taxes; (9) to determine equities under unitized operations; (10) to provide a basis for calculating the economics of gas-cycling operations. History or Estimation of Natural Gas Reserves The natural gas industry in the United States had its beginning during 1826 when natural gas was used for lighting the city of Fredonia, N. Y. The first natural gas pipe line was a 25-mi]le wooden line constructed from hollowed logs, connecting West Bloomfield and Rochester, N. Y. There is no record of an attempt to estimate the gas reserve at West Bloomfield but an attempt was made to determine the capacity of the well by measuring the time required to 611 a large balloon. One of the earlier publications concerning estimation of natural gas reserves is the "Manual for the Oil and Gas Industry," published by the Treasury Department, United States Internal Revenue, in i9i9. The following methods of computing "gas depletion" are listed: (I) production decline of the gas well or property; (2) decline in open-flow capacity; (3) comparison with the life history of similar wells or properties, particularly those exhausted Art

Jan 1, 1949

By George Sachs

I deeply appreciate the honor of being selected to deliver the twentieth Annual Lecture of the Institute of Metals Division. The subject of my paper is extremely involved and voluminous, therefore I shall discuss only some more recent experimental material and speculate somewhat on the physical and mechanical fundamentals of these changes. The flow and the rupture of a solid material are rather different phenomena. It is therefore surprising that up to a rather advanced stage in metallurgical science these two fundamental phenomena have been simultaneously treated and forced into the general conception of the "failure" of solid material. Only in this century, and particularly during the last 20 years, have the very different physical meanings of flow and rupture been clearly recognized. Several hundred of the more recent publications deal with these subjects.1 LAW OF SIMILARITY The basic values commonly considered responsible for the mechanical behavior of any material are the stresses. From this standpoint both a large and a small article made from the same homogeneous metal and of geometrically similar shapes should behave identically, i.e., they should deform geometrically in a similar manner, if subjected to the same stress values at corresponding points. This "law of similarity" was introduced about 60 years ago simultaneously by Barba2 and Kick3 and was derived from the classical theory of elasticity. As far as the plastic behavior of a metal is concerned, this rule appears to be valid. The conventional properties of large and small tension or compression test bars, machined from larger sections, are identical; while the force required to deform a section is proportional to its cross-sectional area and the work consumed in deforming geometrically similar articles in a geometrically similar manner is proportional to its volume. The general trend of the stress-strain diagram of a metal is independent of the section size (Fig. I). No exceptions from this rule are known. However, if the deformation of a metal is continued until rupture occurs, and the breaking stress or the work consumed is measured, a test bar of large cross section appears to fail before or at lower stresses than does one having a small cross section. Thus, the specific impact energy has been often found to decrease with increasing size of the test specimen, particularly for materials with a limited ductility.4 Another exception from the rule of similarity is offered by fatigue-strength values, which usually decrease with increasing section size. 5,6 The conclusion must be drawn from these experimental facts that the ductility of a homogeneous metal decreases with increas¬ing section size (Fig. x). This effect has been actually confirmed by Docherty,7 who observed that in static notch bending tests large specimens failed earlier and in a more brittle fashion than small specimens ma-

Jan 1, 1941

By H. A. Sawin, C.M. Romanowitz

Placer dredging as we know it today, especially gold dredging, is an industry about 40 years old, dating from the beginning of this century, when a few mining men in California saw the possibilities in adapting earlier dredging methods to California placer fields in and immediately adjacent to streams. At first it was thought that dredges must be operated in existing stream beds, but experience soon pointed the way to dredging alluvial deposits of old stream beds, operating on landlocked dredging ponds. Within the first five or six years of modern dredging, experience was gained so rapidly that dredges to dig 60 ft. below water level were *designed and built. This depth was believed by many operators to be the maximum at which successful dredging could be carried on. Alluvial deposits of gold, suitable for dredging, were readily handled by equipment available and developed early in the industry's history. Much of the gravel was easily dug and if deposits were cemented, contained large boulders, or for some other reason could not be handled by a dredge, the ground was abandoned in favor of other deposits that could be handled easily. Many failures, adversely affecting the dredging industry, resulted from attempts at that time to extend the scope of placer dredging with equipment not suited to the formation being dredged. Dredging ground suited to early equipment was exhausted eventually, but many supposedly undredgeable alluvial fields containing gold in commercial quantities were found and became known to dredgemen. Improved equipment was needed to work deposits known to exist at great depths or associated with unusual obstructions. Operating companies looked to dredge manufacturers and metallurgists, particularly manganese-steel foundries, for improved designs and materials. Experience developed in California has spread throughout the world, and dredges of improved types have been adapted to the mining of platinum and tin as well as gold. Space will not permit a description of all the improvements in dredging since the early days, but a few of the recent developments are worthy of note, because they make possible the dredging of placer deposits of great depth, those having hard, irregular bedrock or containing large boulders in great quantities, and compacted or cemented gravel deposits. Deep Dredging At Hammonton, calif., yuba consolidated Gold Fields has, within= the past two years, built its dredge No. 20. The company has operated continuously in that field since 1904, digging successively at maximum depths of 60 ft., 80 ft., 112 ft., and now 124 ft. below water level. The first dredges were equipped with buckets of 6 and 7½-cu. ft. capacity; six dredges operating in the field today have 18-cu. ft. buckets, digging now 65 to 124 ft. below water level. Some ground near Hammonton has been dug for the third time, owing to the devel-

Jan 1, 1943

By A. G. H. Anderson, A. W. Kingsbury

Silicon bronzes containing ken are used to a considerable extent in industry, under the trade name of P.M.G. alloys. Various classes of wrought alloys fall in the composition range 1.5 to 3.5 per cent silicon, and 0.5 to 2.5 per cent iron. Castings may contain as much as 6 per cent silicon and 3 per cent iron at present. The constitutional diagrams of these alloys are thus of considerable practical importance. Copper-silicon-binary alloys have been thoroughly investigated by a number of workers, the latest reports being those of C. S. Smith1 and of A. G. H. Andersen.2 Although much work has been done on iron-copper alloys,3 recorded investigations on the copper-rich copper-iron binary constitutional diagram are not numerous. Tammann and Oelsen4 etermined the solubility limits of iron in copper by means of magnetic measurements, and found that the solubility of iron in copper amounts to a fraction of one per cent at 400°C., increasing slowly to one per cent at 800°C. From 800°C., the solubility increases rapidly and attains 4 per cent at iioo°C. Hanson and Ford,5 using electrical resistivity measurements and the microscope, determined a somewhat different solubility limit. of earlier X-ray works on the copper-iron system, very little has been published. The work by Bradley and Goldschmidt6 on copper-iron-aluminum alloys includes some information on the copper-iron binary. These investigators conclude that substitution of iron in the copper lattice decreases the spacings, which is contrary to the evidence of the present work. Hanson and West? have investigated the ternary alloys of copper with iron and silicon. Although their diagrams are valuable contributions to the understanding of these alloys, they did not recognize the kappa phase,l,2,7,8 and their diagrams do not everywhere conform to the phase rule. The present work contains a check by means of X-rays of the solid solubility limit of iron in copper, and an X-ray investigation of the ternary-phase diagram, which, owing to present conditions, it became necessary to curtail considerably. Preparation of Samples Castings weighing about 75 grams were melted under vacuum. The charges were made up of ingot iron, copper cathodes from Laurel Hill, and refined silicon supplied by the Electrometallurgical Co. Alundum crucibles were generally used. The exceptions were alloys 77 and 78, which were melted in graphite crucibles. The ingots were annealed at 800°C. for one week, then samples were cut for chemical analysis. Longitudinal sections of the binary alloy ingots were hammered into plates 1/8 in. thick. Wherever possible, these plates were homogenized at temperatures ensuring

Jan 1, 1943

By A. W. Schlechten, A. H. Larson

Equilibrium H2S/H2 ratios were determined as functions of temperature (500o to 900°C) and composition in a hydrogen-circulation apparatus. Within the composition range studied there exists a two-phase region of "Zr3S4" and "ZrS2". The upper composition limit of this two-phase region is hounded by a disulfide phase and is practically constant over the temperature range investigated. The lower composition limit of this two-phase region is bounded a "Zr3S4 " phase and varies appreciably with tem- perature. The upper composition limit of the homogeneous region of the disulfide phase is not definitely determined, but it appears to he bounded by the stoichiometric composition of ZrS2. The lower composition limit of the homogeneous region of the Zr3S4 phase could not he determined due to the extremely low values of the equilibrium H2S/H2 ratios. Various thermodynamic quantities are evaluated from the data. PUBLISHED free-energy data for the Zr-S system are practically nonexistent. Strotzer, Biltz, and Meisel1 measured the sulfur pressures for the reaction 2ZrS2(s) + S2(g) = ZrS3(s) in the temperature range 783" to 874°C. The average heat of reaction calculated from the temperature dependence of the sulfur pressure is -47 keal. It should be noted, however, that according to these investigators, the two-phase region as determined by sulfur pressure constancy under isothermal conditions extended from approximately ZrS2, 3 to ZrS2.7. From consideration of X-ray data they concluded that the homogeneous regions of the disulfide and trisulfide phases are ZrS1.8-2.0 and ZrS2.8-3.2, respectively. Hahn and coworkers2 have made a structure study of the zirconium sulfide phases. They summarized the zirconium sulfide phases as follows: the compounds ZrS3 and ZrS2 with narrow homogeneous regions, a "Zr3S4" phase with a homogeneous region roughly within the limits of ZrSl.5 and ZrSo.9, the compounds ZrS and Zr4S3, and a "Zr3S2" phase with a homogeneous region within the limits ZrSo.8 and ZrSo.5. It is noted that the compounds ZrS and Zr4S3 are only formed in the gaseous state through sublimation of a phase which has the approximate composition of the compound. This paper describes the determination of the stability of the zirconium sulfide phases by a hydrogen-reduction method in which hydrogen is circulated over the heated sulfide until equilibrium is attained. The resulting H2S-H2 mixture is then analyzed. Partial molar free energies, enthalpies,

Jan 1, 1964

By A. G. H. Anderson, A. W. Kingsbury

Silicon bronzes containing ken are used to a considerable extent in industry, under the trade name of P.M.G. alloys. Various classes of wrought alloys fall in the composition range 1.5 to 3.5 per cent silicon, and 0.5 to 2.5 per cent iron. Castings may contain as much as 6 per cent silicon and 3 per cent iron at present. The constitutional diagrams of these alloys are thus of considerable practical importance. Copper-silicon-binary alloys have been thoroughly investigated by a number of workers, the latest reports being those of C. S. Smith1 and of A. G. H. Andersen.2 Although much work has been done on iron-copper alloys,3 recorded investigations on the copper-rich copper-iron binary constitutional diagram are not numerous. Tammann and Oelsen4 etermined the solubility limits of iron in copper by means of magnetic measurements, and found that the solubility of iron in copper amounts to a fraction of one per cent at 400°C., increasing slowly to one per cent at 800°C. From 800°C., the solubility increases rapidly and attains 4 per cent at iioo°C. Hanson and Ford,5 using electrical resistivity measurements and the microscope, determined a somewhat different solubility limit. of earlier X-ray works on the copper-iron system, very little has been published. The work by Bradley and Goldschmidt6 on copper-iron-aluminum alloys includes some information on the copper-iron binary. These investigators conclude that substitution of iron in the copper lattice decreases the spacings, which is contrary to the evidence of the present work. Hanson and West? have investigated the ternary alloys of copper with iron and silicon. Although their diagrams are valuable contributions to the understanding of these alloys, they did not recognize the kappa phase,l,2,7,8 and their diagrams do not everywhere conform to the phase rule. The present work contains a check by means of X-rays of the solid solubility limit of iron in copper, and an X-ray investigation of the ternary-phase diagram, which, owing to present conditions, it became necessary to curtail considerably. Preparation of Samples Castings weighing about 75 grams were melted under vacuum. The charges were made up of ingot iron, copper cathodes from Laurel Hill, and refined silicon supplied by the Electrometallurgical Co. Alundum crucibles were generally used. The exceptions were alloys 77 and 78, which were melted in graphite crucibles. The ingots were annealed at 800°C. for one week, then samples were cut for chemical analysis. Longitudinal sections of the binary alloy ingots were hammered into plates 1/8 in. thick. Wherever possible, these plates were homogenized at temperatures ensuring

Jan 1, 1943