Search Documents

TULSA, the host of the Petroleum Division this year, is the oil metropolis of the Mid- Continent and gateway of the Southwest. It has risen in less than three decades from a dusty cattle town of less than 1000 population to its present-day status of a modern, wide-awake and prosperous city of close to 150,000, with an assessed realty valuation of approximately $100,000,000. Oil was discovered near Tulsa in 1901, and with it came th.2 development of the Mid-Continent field, one of the richest in the world. Tulsa from the start has been the center of operations, and its location on foul- and aggressive application of the airplane to oil-field requirements tends to fix this status as production is developed farther and farther afield. That Tulsa is far more than an ephemeral oil town is punched into the newcomer's- especially the Easterner's-mind, as he is whisked by taxi from the railroad station to the Hotel Mayo. The cicadalike pounding of the riveters on the steel skeletons of many skyscrapers, mounting upward to fill the gaps in an already well-developed skyline, dispels the feeling of a new atmosphere and puts him back on Forty-second Street, Michigan Boulevard or whatever his own particular "Main Street" may be along which an American city is being remade. Practically every company of any importance operating in the Mid-Con-

Jan 1, 1928

By P. H. G., Durville

ANY metal which contains even a small percentage of aluminum possesses certain peculiarities of appearance and properties which are exhibited both when the metal is melted and after it solidifies. Pure aluminum, or an alloy containing a small proportion of aluminum, can be melted without flux-except for a layer of charcoal-because a film of aluminum oxide and metal forms at the surface of melted aluminum. Although very thin, this film is air-proof, and it prevents the metal underneath from oxidizing. This oxidized film does not move easily on account of its toughness and high surface tension. One very important point in connection with this process of still casting has not been strongly enough stressed, namely, that the same kind of surface film with the same peculiarities forms over the surface of all melted alloys that contain even a small proportion of aluminum. Experienced foundrymen know how desirable it is to cast aluminum under its "skin" or under the surface of the film which tends to remain still. In the case of red copper, when in fusion, the surface shows pure copper only. This' is due to the fact that liquid copper constantly absorbs the copper oxide which forms on the surface. By closely examining melting copper the oxide can be seen dissolving in the bath, and going into solution just as pulverized sugar dissolves in water. When copper is cast in the open, either in wire bars or cakes, the surface of metal exposed to the air is covered by a film of black oxide that cannot be absorbed by the metal.

Jan 1, 1927

By JAMES A. VEASEY

SINCE the World War, excepting for a few brief periods of relief, the American petroleum industry has been obliged to meet its important economic responsibility to this nation hampered by the maladjustment that inevitably follows a marked and unwholesome over-production of its raw material, crude oil. Despite the warnings of the Federal Oil Conservation Board and the endeavors of many of the leaders in the business to stem the flow of oil from the wells of the country, the evil ,not only persists but, at the moment, seems more malignant than ever before. Unless the local and temporary restraints on drilling and production now in effect in California, Wyoming, Texas, and Oklahoma are continued, and, indeed, unless stricter and more comprehensive measures of the same sort are imposed and adhered to by the industry in those States, over-production in the enterprise during the current year will be more pronounced than in any other period in history.

Jan 1, 1929

By Lysle E. Shaffer

TEACHING engineering students how to write and speak effectively -is one of the greatest problems facing the technical schools today. No phase of engineering education has received more criticism, and rightly so, for the criticism is justified. Year after year we continue to graduate men that are indifferent to the use of a tool they will need every day of their lives. Our young engineers cannot write a clear, concise report, and their business letters are a disgrace to the profession that takes pride in precision. The problem is not new. The remark ascribed to Sir James Barrie, that "The man of science appears to be the only man who has something to say, just now-and the only man who does not know how to say it" is as uncomfortably true today as it was thirty years ago. The records of meetings of engineering educators and the transactions of the engineering societies show that the inability of the engineer to communicate his ideas has been discussed for years. Engineering educators, prodded by industry, have recognized that the problem exists, but they have not solved it. Instead they continue to expose the student to composition and rhetoric, hustle him through English and American literature, and then blame his high school because he does not know enough English grammar to write a clear sentence. We must face the fact that the graduate is not going to reflect on the high school, but on his college. If the high school has shirked the job, the responsibility for correction rests on the faculty of the professional school.

Jan 1, 1948

By WM. HUFF WAGNER

Computations and allowances for mine depletion for Federal income tax purposes depend upon the meaning of certain terms in the pertinent provisions of section 114(b) 4 of the Internal Revenue Code. Unfortunately, but one of these terms is defined in the Code. Congress left it to the Commissioner to define the other terms in the Regulations. Even though the Commissioner, through his staff, labored long and earnestly to draft these definitions they have not been satisfactory to the mining industry, because the definitions in the Regulations and the interpretation placed thereon by the Commissioner do not state what the industry believes to be the clear and obvious intent of Congress. Consequently serious and prolonged disputes, unduly delaying the settlement of Federal tax returns involving percentage depletion deductions are continually arising between taxpayers and the Commissioner.

Jan 1, 1949

By Barton, Donald C.

THE elastic, earthwaves produced naturally by earthquakes -have been used for a long time as evidence from' which to draw conclusions in regard to the constitution of the interior and crust of the earth. The elastic earthwaves produced artificially by occasional explosions and recorded by seismological .observatories were used to draw conclusions regarding the-geology of the intervening area. Intentionally produced elastic earthwaves in the past five years have come to be used extensively in the investigation of very local geologic structure. The seismic method of working geologic structure, which makes use of artificially controlled explosions and the resulting earthwaves, has developed almost `clairvoyant power in handling certain geologic situations, and in the discovery of salt domes in the Gulf Coastal: Plain region of Texas and Louisiana has 'scored the, most brilliant success.

Sep 1, 1928

By WILLIAM BOWIE

THE development of the isostatic idea during the last century would make an interesting paper in itself. But the various steps in the development have been covered in a number of papers and books which are readily available. Therefore this short paper should not give space to. the historical phases of the subject. Isostasy is really an old idea, but it is only in the last few decades that it has taken on any great prominence or importance in the study of earth phenomena. It is really remarkable how closely Dutton' sensed the isostatic principle 40 years or more ago. His general principles of isostasy as outlined by him have stood the test of time and fit in closely with the general ideas held today. It would seem, however, that some of his views with regard to the application of isostasy to geological processes must be modified or abandoned.

Jan 1, 1930

By Robert Keeney

THE electric smelting of manganese ore and the production of ferro- manganese did not exist as an industry, in the United States or elsewhere, previous to the outbreak of war in 1914. Ferromanganese had been produced, electrically, during times of high prices by two companies at Niagara Falls and by several European companies, but the production. was spasmodic, and none was electrically produced when ferromanganese sold at from $35 to $40 per ton. Thus the electric smelting of manganese ore must be considered as a development caused by the high prices prevailing during the years 1916, 1917 and 1918, and the necessity of smelting domestic ore in order to fill the ferromanganese requirements of the steel industry of the United States, which increased from 189,088 tons in 1914 to 356,356 tons in 1918. The electric furnace is well adapted to smelting domestic-ore because it can be located in small units near the source of ore supply. In 1918, the ferromanganese production of the United States was 333,027 tons, of which about 7 per cent., or 23,000 tons, was produced in the electric furnace. The electric furnace not only assisted materially in the development of a domestic-ore supply but made a considerable saving of coke, as it requires about 1,4 tons of bituminous or lignite coal per ton of ferromanganese compared with a blast-furnace consumption of 2.9 tons of coke per ton of ferromanganese. Some of the plants in the United States that smelted manganese ore in the electric furnace during the war and in 1920 are listed in Tabled. From early in 1919 to about February, 1920, little ferromanganese was produced in the electric furnace. During this period the price of ferro-manganese (78 to 82 per cent. manganese) was about $100 per ton. During the first half of 1920, several plants resumed operation when the, price of. ferromanganese (76 to 80 per cent. grade) gradually increased to $200 per ton, delivered.

Jan 2, 1921

By Peter T. Luckie, Harold L. Lovell, E. R. Palowitch, A. W. Deurbrouck, James K. Kindig

PART 1: DENSE MEDIUM SEPARATION by E. R. PALOWITCH and A. W. DEURBROUK INTRODUCTION During 1965, 64.9 percent of the 512 million tons of bituminous coal and lignite produced was cleaned mechanically, of which 95 million tons was cleaned by dense medium processes.l The percentage of bituminous coal and lignite cleaned mechanically by dense medium processes rose from 7.0 to 28.5 percent from 1938 to 1965. Dense medium separations include those coal preparation processes which clean raw coal by immersing it in a fluid having a density intermediate between clean coal and reject. As there is a general correlation between ash content and specific gravity, it is possible to achieve the required degree of removal of ash-forming impurities from a raw coal by regulating the specific gravity of the separating fluid. Dense medium processes offer the following advantages over other coal cleaning processes : 1. Ability to make sharp separations at any specific gravity within the range normally required even in the presence of high percentages of the feed in the range of e 0.1 specific gravity units. 2. Ability to maintain a separating gravity that can be controlled with ±0.005 specific gravity units. 3. Ability to handle a wide range of sizes (up to 14 inches). 4. Relatively low capital and operating costs when considered in terms of high capacity and small space requirements. 5. Ability to change specific gravity of separation to meet varying market requirements. 6. Ability to handle fluctuations in feed both in terms of quantity and quality. HISTORY Sir Henry Bessemer patented the first dense medium process in 1858. Solutions of the chlorides of iron, manganese, barium and calcium were proposed as separating liquids; the separation was made in a cone-shaped separator. One large-scale plant using calcium chloride was erected in Germany but soon was abandoned. The Chance process, using a mixture of sand and water, was first

Jan 1, 1968

By Charles Barrett

SINCE 1925, when the preferred orientations in compressed aluminum were first determined1, 2 the orientations have been described as a fiber texture in which a face diagonal, [110], of the face-centered cubic lattice is parallel to the compression axis. Subsequent experiments have seemed to confirm this texture,3-5 and a number of theories (recently summarized in references 6 and 7) have been proposed to explain it and to relate it to the behavior of single crystals during compression. 3,8-11 The experiments reported in this paper prove that the orientations are not adequately described as quoted above-i.e., as a [110] fiber texture-although this is a first approximation to the actual texture. They also show that the texture cannot be thought of as a stable orienta-tion that is reached and maintained after a sufficient amount of deforma-tion. The actual texture, when studied in detail at successive stages of compression, indicates that a hitherto unsuspected range of orientations is present, both in the polycrystalline metal as a whole and in various individual grains in its interior, and that a state of dynamic equilibrium exists within this range. The reasons for the failure of previous theories to predict the actual texture become obvious when the heterogeneous nature of the flow is considered. In addition to the deformation texture, the manner of its develop-ment, and its theory, this paper presents data on the following related subjects: the identity of strain markings in aluminum; the orientation changes in aluminum single crystals during compression and a com-parison of these with the conditions in individual grains of a polycrystal-line specimen; the origin of asterism in deformed single crystals, which heretofore has been regarded as a distortion localized at the surfaces of slip planes; and the relation of plastic strain in individual grains in an aggregate to the strain of the whole.

Jan 1, 1939

By Robert E. Hoffman, John B. Hudson

The self-diffusion coefficient of pure lead has been measured at five pressures between atmospheric and 40 kb. over a temperature range of about 150°C near the melting point at each pressure. Measurements were made using a radiotracer technique, samples being sectioned electrochemically after the diffusion anneal to determine the diffusion penetration curve. Pressure was applied in a "belt" type pressure device similar to that used by Hall et al., in the diamond synthesis. The self-diffusion coefficient, D, can be represented by an equation of the form at constant pressure, and an equation of the format constant temperature. An apparent correlation between the effects of pressure on self-diffusion and on the melting point of the material observed by Nachtrieb et al., at pressures below 10 kb. was found to be only approximate as measurements are carried to higher pressures. OVER the course of the past 30 years a large number of studies1-' of the rate of atom movements in solid metals have been carried out. These studies have in general been aimed at increasing the understanding of the detailed atomic process by which atom movements in metals can take place. The largest portion of these studies consisted of measurements of the self-diffusion coefficient, D, as a function of temperature. From such studies con- siderable information regarding the energetics of the motive process has been deduced. Recently such measurements have been extended to the pressure dimension. However, the existing work in this area is scanty and has in the past been limited to the pressures attainable in oil or gas bombs—i.e., up to about 10 kilobars (kb). In the present work, the self-diffusion behavior of pure lead has been investigated using the "belt" type high-pressure apparatus designed by Hall7 over a pressure range from atmospheric to 40 kb at temperatures extending over about a 150°C range close to the melting point at each pressure.

Jan 1, 1962

By J. E. Burke, C. S. Barrett

The fine lines shown in Fig I are typical of markings that ma): be detected after polishing and etching deformed specimens of alpha brass and other alloys. Although they have long been the subject of discussion by metallurgists their nature is still uncertain and the names that have been applied: to them, such as deformation line4 or strain markinas, indicate this uncertainky. In this paper which repotts the results of a furthcr investigatinn of their nature, they will be called strain mxrkings. Introduction Mathewson and Phillips1 described strain markinps in 1 916 and concluded that they appear only after 20 pet deformation. They objected to the markings being called slip tines believing this term should be sewrved for surface markings protluced by plastic deformntion. In 1921. vogel² described similar striations which appeared after polishing and etching the roughly ground surface of numerous alloys. He reported that the markings were crystallo-graphic in nature, and since they resemble Seumann hands in iron, at least superficially, he assumed them to be mechanical twins. In 1928, Matherwson reported work by Phillips which indicated that the lines were more readily produced by impact than by slow deformation and that in many cases the twins inside recrystallized grains were parallel to strain markings in the original deformed grains. This was taken as cvirlence that the markings coalesce into anncaling twins. and hence that they themselves are mechanical twins. Many attempts have been made to demonstrate directly that the markings are mechanical twins. In 1934, Samans described the results of X ray studies of two defomed crystals of alpha brass. Evidence was obtained which could be interpreted to indicate that the strain markings arc mechanical twins, and this remains the only direct evidence to this effect. Several other attempts to obtain similar evidence by X ray diffraction have failed5.8.7 although in no Ease was the original method of Samans employed. An

Jan 1, 1949

By C. S. Barrett, J. E. Burke

The fine lines shown in Fig I are typical of markings that ma): be detected after polishing and etching deformed specimens of alpha brass and other alloys. Although they have long been the subject of discussion by metallurgists their nature is still uncertain and the names that have been applied: to them, such as deformation line4 or strain markinas, indicate this uncertainky. In this paper which repotts the results of a furthcr investigatinn of their nature, they will be called strain mxrkings. Introduction Mathewson and Phillips1 described strain markinps in 1 916 and concluded that they appear only after 20 pet deformation. They objected to the markings being called slip tines believing this term should be sewrved for surface markings protluced by plastic deformntion. In 1921. vogel² described similar striations which appeared after polishing and etching the roughly ground surface of numerous alloys. He reported that the markings were crystallo-graphic in nature, and since they resemble Seumann hands in iron, at least superficially, he assumed them to be mechanical twins. In 1928, Matherwson reported work by Phillips which indicated that the lines were more readily produced by impact than by slow deformation and that in many cases the twins inside recrystallized grains were parallel to strain markings in the original deformed grains. This was taken as cvirlence that the markings coalesce into anncaling twins. and hence that they themselves are mechanical twins. Many attempts have been made to demonstrate directly that the markings are mechanical twins. In 1934, Samans described the results of X ray studies of two defomed crystals of alpha brass. Evidence was obtained which could be interpreted to indicate that the strain markings arc mechanical twins, and this remains the only direct evidence to this effect. Several other attempts to obtain similar evidence by X ray diffraction have failed5.8.7 although in no Ease was the original method of Samans employed. An

Jan 1, 1949

By Josef Intrater

A dilatometric determination of the a + ß region temperature limits was performed on vacuum melted Zircaloy-2. The temperature of transformation for a-a+ß and a+ß — ß on heating and cooling as a function of rate of heating and heat treating history was studied. The limits were found to be 815° to 830°C to 975° to 995°C on heating and from 960° to 930°C to 785° to 770°C on cooling. A 5° to 15°C increase was observed for a- a + ß with increased rate of heating and a 20° to 30°C decrease for ß - a + ß with increased rate of cooling. 1 HE transformation temperature for pure zirconium has been determined by many investigators1-5 using metallography, electrical resistivity measurements, and dilatometry. The effect of the rate of cooling on the transformation temperature of zirconium has been studied by Hayes and Kaufmann6 and Duwez,7 and the effect of alloying elements by pfei18 and McGeary.13 Since the development of Zircaloy-2, the limits of the a + ß region for that alloy have been also determined. The first reported temperature for the a — a + a transformation in Zircaloy-2 was 900°C and for a + ß - ß 1000C Subsequent studies by Picklesimer and damson" indicated the beginning of the transformation at 810°C, and the metallographic study by the Technology Group of the Special Materials Section at the Westinghouse Bettis plant1' suggested that 820°to 830°C is the temperature of transformation. The dilatometric investigation by the latter group yielded 830°C for the beginning of the transformation. Thomas and Forscher12 set the beginning of the transformation at 900 °C on heating and the end of the transformation at 870°C on cooling. The above investigators stated in their paper that the dilatometric curve exhibits features caused by a eutectoid reac-

Jan 1, 1962

By W. A. Wood, W. H. Reimann

A study is made of the creep that can be induced in armco iron at room temperature by superposing small amplitudes of alternating torsion on a tensile creep load. It is shown that the creep differs from that in comparable tests on copper in being trmsient only. At the same time, though transient, the creep can produce extensions of some 10 pct under creep loads less than the tensile yield stress of the material. The creep can be largely suppressed b$ applying cyclic strain of suitable amplitude before applying the creep load and the metal thereby stabilized. At room temperature, plastic flow in a metal under steady load is normally limited by strain-hardening processes. However, if a small cyclic stress is superposed on the steady load these processes may be more or less neutralized and, as shown in recent investigations,'-4 plastic flow may continue. In this way annealed copper, for example, can be induced to creep continuously to fracture under loads as small as 1 tsi. Dislocation mechanisms possibly responsible for this room-temperature creep have been usefully reviewed by Feltner.But discussion so far has been based mainly on creep as it is found in close-packed metals initially in the annealed state, and their behavior may not be general. In fact, recent work shows that the form of creep in annealed copper is different from that even in cold-worked copper;7 the creep thus depends on the dislocation pattern already in a metal as well as on the metal itself. This paper describes the creep in annealed armco iron, tested in the same way as the above-mentioned copper. One object was to see how creep in a typical bcc metal compared with that in the annealed close-packed metals. Another object was to utilize the fact that a bcc metal like iron has a more pronounced elastic range than close-packed metals like copper and to find to what extent the creep load or superposed cyclic stress had to exceed their re-

Jan 1, 1964

THE refining period of an open-hearth heat blends imperceptibly into the finishing period, during which final adjustments are made in slag composition, in bath action and temperature, and in composition of the steel, in order to prepare it for casting into ingots. Operations must be governed by the consideration that alterations in the character of the heat during the finishing period must be held to a minimum. In a broad sense, the finishing and deoxidation period of a heat may be said to begin when the action of the last ore addition has ceased, and to end when the teeming of the ingots is completed. INGOT STRUCTURES A survey of the relative advantages and disadvantages of different types of ingot structure is required because deoxidation treatments during the finishing period control the amount of gas evolved during solidification and consequently determine the type of ingot structure. Four classes of ingots are recognized, depending upon the degree of deoxidation to which the steel has been subjected. These types are killed, semikilled, capped, and rimmed; typical examples of their structures are represented by ingots 1, 2, 5, and 7, respectively, of Fig 9-1. The actual ingots from which these cross sections were sketched were all poured to the same height (indicated by the dotted lines) in the same type and size of bottle-top molds. The eight drawings of the figure represent selected types of ingot structure in a continuous series from "dead killed" to "wild," resulting from variations in the total quantity of gas evolved, from none at all to copious amounts, during solidification of the steel in the mold. Killed and semikilled steels are adjacent at the "quiescent" end of the ingot structure series where only small amounts of gas are evolved. The term "quiescent" describes the action of the molten metal during and subsequent to the teeming of killed and semikilled steels. Capped and rimmed steels are adjacent at the

Jan 1, 1951

THE refining period of an open-hearth heat blends imperceptibly into the finishing period, during which final adjustments are made in slag composition, in bath action and temperature, and in composition of the steel, in order to prepare it for casting into ingots. Operations must be governed by the consideration that alterations in the character of the heat during the finishing period must be held to a minimum. In a broad sense, the finishing and deoxidation period of a heat may be said to be- gin when the action of the last ore addition has ceased, and to end when the teeming of the ingots is completed. INGOT STRUCTLIRES A survey of the relative advantages and disadvantages of different types of ingot structure is required because deoxidation treatments during the finishing period control the amount of gas evolved during solidification and consequently determine the type of ingot structure. Four classes of ingots are recognized, de- pending upon the degree of deoxidation to which the steel has been subjected. These types are killed, semikilled, capped, and rimmed; typical examples of their structures are represented by ingots 1, 2, 5, and 7, respectively, of Fig 9-1. The actual ingots from which these cross sections were sketched were all poured to the same height (indicated by the dotted lines) in the same type and size of bottle-top molds. The eight drawings of the figure represent selected types of ingot structure in a continuous series from "dead killed" to "wild," resulting from variations in the total quantity of gas evolved, from none at all to copious amounts, during solidification of the steel in the mold. Killed and semikilled steels are adjacent at the "quiescent" end of the ingot structure series where only small amounts of gas are evolved. The term "quiescent" describes the action of the molten metal during and subsequent to the teeming of killed and semikilled steels. Capped and rimmed steels are adjacent at the

Jan 1, 1964

By Stuart Croasdale

Not long ago I was called upon to conduct some experiments on the treatment of ores from the New Cornelia copper mine, Ajo mountains, Arizona, for the Calumet & Arizona Copper Co. The problem was a very interesting one and contained some unusual features. Incidental with this problem was the utilization of a large amount of low-grade pyrite in the Bisbee mines of the company, provided this could be accomplished by any feasible method. The New Cornelia mine is situated 45 miles south of Gila Bend, the nearest railroad point, on the Southern Pacific Railroad. It is about 160 miles, almost due west, from Tucson. This section is one of the most arid in the United States. The normal annual precipitation, as given by the United States Weather Bureau covering a period from 1870 to 1901, is 3 to 5 in. During June and July, 1913, the records kept by the company gave the following results. These are all I have available, but they show the enormous evaporation that can be expected, which may be a factor in leaching operations on a large scale. Temperature, Degrees F. High Low Average June...................... 112 62 84.0 ' July...................... 115 71 87.8 Evaporation June July Concrete tank, inches............ 11.7 10.72 Iron tank, inches.............. 14.8 13.07 Rainfall, inches................ None 0.77 Cloudy days................... None 10.00 Aside from several springs about 10 miles from the property, the nearest known water in quantity at the time these experiments were made was the Gila river at Gila Bend, 45 miles distant. Part of the developinent of the property of course included drilling for water in the valley, which was in progress at the conclusion of my experiments. The ore deposit itself is unusual. It consists of of intrusive plug of monzonite or granite porphyry. Chalcopyrite, bornite, and magnetite are finely disseminated throughout the magma in sufficient quantities to make the greater part of the mass commercial ore to a certain depth.

Jan 1, 1915

By H. C. van Elst

Ultrahigh-speedphotographic and electronic meth-ods were applied to an investigation of details of brittle-fracture propagation in steel. The brittle fractures studied were obtained in steel plate with the aid of a Robertson apparatus. It was found that a brittle fracture proceeds by discrete steps ranging from 30 mm near the stop temperature to less than 2 mm at lower temperatures. The halting FROM prior metallographic observations of brittle fracture in steel' it could be concluded that the distribution of mechanical twins along a brittle fracture was similar to the distribution of mechanical twins induced by explosive deformation. It was therefore assumed that a running brittle fracture created stress waves, cf. Refs. 2-7. An emission of stress waves by a brittle fracture, however, seems only conceivable if the fracture propagates by discrete steps. For this reason a study of the details of times between successive steps drop in this tem-perature region from 20 usec to about 1 psec. The stepwise propagation mechanism is accompanied by an intermittent emission of stress waves of the order of 100 to 200 kg per sq mm. These stress waves seen1 to play an important role in the mechanism of brittle fracture as will be discussed. brittle-fracture propagation was undertaken to investigate the possible determination of the fracture steps and the emitted stress waves associated with the assumed mechanism. The more practical object of this work is the development of a test method for the determination of the ductile-brittle transition in small specimens. This has special advantages for the study of irradiation damage in steel. In this test method, which will be published in a following paper, the stress waves emitted by an actual brittle fracture are reproduced with explosive or electrical means and are then transmitted through small specimens at various temperatures. In the present paper only the results of the brittle-fracture study will be reported.

Jan 1, 1964

By Lewis A. Smith

Chromium is one of the new metals, but considerable research has been required to determine an approximate record of its production from 1827 until the present. Its use in the form of pure metal is not extensive; of the chromite mined, about one-half is required for making ferrochro-mium, about two-fifths goes directly into refractories and the remainder is absorbed chiefly by the chemical trades. The industries that demand chromite for such uses are mainly in countries that produce little chromite, while the important chromite-producing countries are not generally consumers. The international flow of chromite is therefore of interest, as well as the political and commercial control of resources of the metal. World Production The first mining of chromite is said to have occurred as early as 1820, at the Roros deposit in Norway, but the first well-established output came from the Reed mine, in Maryland, about 1827. Thereafter the United States led the world in chromite production until 1860, when Turkey took the lead. Russia in turn became the chief producer from 1897 to 1902, inclusive. From 1903 to 1909, New Caledonia held first place, but alternated with Southern Rhodesia from 1910 to 1917, inclusive. In 1918, 1919 and 1920-1921, the United States, India and New Caledonia led, respectively. In 1922 Southern Rhodesia assumed first place and has since continued to be the world's foremost producer by a large margin. Fig. 1 illustrates the production of the leading countries from 1890 to 1929, inclusive. Fig. 2 shows the world production of chromite from 1890 to 1929, inclusive, in long tons and Table 2 gives the production by countries for the same period. The total world production for the 103 years, 1827 to 1929, ipclusive, is estimated at about 7,100,000 long tons, distributed as shown in Table 1. World Trade in 1928 In reviewing the figures for the flow of chromite in 1928, it is evident that the six countries that produce most consume little chromite and

Jan 1, 1931