Search Documents

By L.L. Wyman

The exact nature of the changes that take place in the iron-nickel alloys, giving rise to the interesting and useful expansion alloys in the Invar range, has yet to be fully understood. Similarly, the ternary iron-nickel-cobalt alloys, which also possess such commercially useful expansion characteristics,1,2 are concerned with transformations that appear to be identical with those found in the parent iron-nickel alloys. The investigations on iron-nickel alloys in the range 26 to 29 per cent Ni have been reported by several authors3-9 wherein it is shown that there are factors other than temperature, such as stress and grain size, which play an important part in determining the temperature at which the low-temperature transformation takes place. It will be shown in this paper that the ternary iron-nickcl-cobalt alloys having nickel contents comparable to the alloys mentioned above behave in a parallel manner. The alloys in the range of 26 to 31 per cent Ni and 16 to 21 per cent Co have a coefficient of expansion of about 4.0 X 10-6 per degree Centigrade, and the alloys in this range of composition find considerable application in making glass-to-metal seals, because these expansion properties so well match commercial glasses. The behavior of these alloys is not a simple matter, for it has been observed in alloys of 28.5 per cent Ni and 18.5 Co that severe working ran cause the appearance of a second phase having a needlelike structure similar to the martensite structure in carhon steels. Fig. 1 shows the change brought about in an alloy of this composition when a strip of this material was cut with tin shears. This second phase has been identified as the body-centered cubic alpha phase, and it is the purpose of this paper to describe the results of some of the preliminary investigations in the study of the changes involved in these alloys. Materials The past work on these alloys has concerned itself primarily with materials made by the usual casting procedure and involving the use

Jan 1, 1939

By T. F. McCormick

THIS year, 1950, is the golden anniversary of the construction and operation in this country of a tube mill for the sole purpose of fabricating aluminum alloy tubing. For a short period prior to the beginning of this mill, aluminum alloy tubing was obtained from foreign sources or produced in mills fabricating other metals. Indeed, it was a very short period because aluminum itself was a newcomer in the field of metals. The first sheet rolling mill had been in operation just eight years and a rod rolling mill for the production of wire and cable had been functioning one year. The first tube mill for aluminum was built by the Aluminum Co. of America in May 1900 and started production with four draw benches and five men, including the mill superintendent. The building itself was a lean-to attached to a sheet-rolling mill at New Kensington, Pa. The cost of equipment, including the draw benches, dies, mandrels, and other tools, was about $5000. This figure seems absurd in the present day but nevertheless it was questioned at that time whether or not such a large sum should be spent to embark on a new and uncertain venture. The initial production system for the new mill consisted of casting round hollow ingots in a tilting-type iron mold, reducing the ingots to bloom size outside the plant, and finally drawing to size on the draw benches. This method of producing aluminum alloy tubing survived just two years, as blooms of satisfactory quality were not obtained consistently. It was superseded by the cupping method in which a 24-in. diam circle cut from a rolled plate was formed into a tube bloom using first a small cupping press and then a push bench. It was stated that tubing so produced was limited to a maximum diameter of 2 3/4 in. and to wall thicknesses varying from 12 to 24 gage. However, for the first time all the operations were performed at one plant and the result was a quality product. Later larger cupping presses and push benches were obtained and the method continued to be the principal one for aluminum alloy tubing for almost a quarter of a century. During the interim the use of a Alan Mannesmann -type billet piercer was explored and it was used to some extent, but failed to produce consistently a smooth inside surface suitable for drawing with aluminum alloys. Experiments started during the latter stages of World War I in the production of tube blooms with a hydraulic extrusion press, led to the use of this type of equipment to make tube blooms for further drawing during a change-over period extending from 1925 until 1930. At this time the cupping method was discarded completely. From these humble beginnings, the aluminum alloy tubing business expanded until well over six million pounds were produced in a single month in the United States during World War II. The major portion of this production was in strong alloys which did not appear in the tubing picture until 1022, when 17S alloy tubing was introduced for aircraft construction.

Jan 1, 1951

By L. L. Wyman

The exact nature of the changes that take place in the iron-nickel alloys, giving rise to the interesting and useful expansion alloys in the Invar range, has yet to be fully understood. Similarly, the ternary iron-nickel-cobalt alloys, which also possess such commercially useful expansion characteristics,1,2 are concerned with transformations that appear to be identical with those found in the parent iron-nickel alloys. The investigations on iron-nickel alloys in the range 26 to 29 per cent Ni have been reported by several authors3-9 wherein it is shown that there are factors other than temperature, such as stress and grain size, which play an important part in determining the temperature at which the low-temperature transformation takes place. It will be shown in this paper that the ternary iron-nickcl-cobalt alloys having nickel contents comparable to the alloys mentioned above behave in a parallel manner. The alloys in the range of 26 to 31 per cent Ni and 16 to 21 per cent Co have a coefficient of expansion of about 4.0 X 10-6 per degree Centigrade, and the alloys in this range of composition find considerable application in making glass-to-metal seals, because these expansion properties so well match commercial glasses. The behavior of these alloys is not a simple matter, for it has been observed in alloys of 28.5 per cent Ni and 18.5 Co that severe working ran cause the appearance of a second phase having a needlelike structure similar to the martensite structure in carhon steels. Fig. 1 shows the change brought about in an alloy of this composition when a strip of this material was cut with tin shears. This second phase has been identified as the body-centered cubic alpha phase, and it is the purpose of this paper to describe the results of some of the preliminary investigations in the study of the changes involved in these alloys. Materials The past work on these alloys has concerned itself primarily with materials made by the usual casting procedure and involving the use

Jan 1, 1939

By C. W. MacGregor

The observation of the flow layers, or Luders' lines, produced in mild steel when it is stressed into the plastic range often provides considerable useful information for the study of the fundamental mechanism of the plastic flow of metals. It is a commonly observed fact that as soon as the upper yield point in a mild-st'eel tensile-test bar is passed, an unstable condition develops in the equilibrium, the load on the testing machine drops and if the surface of the bar contains a thin mill scale, the latter begins to flake off rapidly along certain "lines." These "lines" are ill reality traces of wedge-shaped flow layers and are formed by the inter-section of the surface of slip and the surface of the bar. The average plane of the flow layer itself has been found by various experimenters to be inclined at an angle of approximately 45" to the axis of the test bar. In a body of more complicated shape stressed in possibly a different man-ncr, the tangent planes to the flow layers at each point seem in many cases to be inclined at an angle of about 45" to the principal stress direct-tions at the point. As examples of the latter may be mentionecl the logarithmic spirals obtained when a rivet hole is punched in a thin plate, or when a tube is subject,ed to internal pressure only, etc. IIencc if the flow layers are observed from an experiment, the shear-st'ress trajectories —the curves indicating the direct,ions of the maximum shearing stresses in the body—may then be approximately determined. Since the latter curves form an orthogonal family inclined at 45" to the principal stress directions, the family of principal stress trajectories, or the curves irldicating the directions of the principal stresses, may be thus obtained Although the discontinuous type of stress-strain curve at the yield point is commonly observed with test bars of mild steel, more recent experiments have shown that this is by no means the only material exhibiting this interesting phenomenon. A similar effect has been observed in zinc and cadmium crystals, by Becker and Orowai~; in duralumin and other aluminum alloys, by Dawidenkow,~Elam,~ Fell4 an(l others; in copper and copper-alloy crystals, by Elam;~ in brass by Elam;3 in brass wires by deForest;" in higher carbon steels, tungsten steel, and

Jan 1, 1939

By D. L., Hayes

THE concentration of zinc ore in Wisconsin is a comparatively simple process, although it presents problems that must be overcome in an efficient manner in such a way that installation and operating costs are low. As the ore deposits are small, the first cost of the concentrating plant must be low; while the low margin of profit makes it necessary to have the minimum operating costs. The original mills were copied from those of the Joplin district, as most of them were built and operated by Joplin millmen. These served the purpose well; they made a clean concentrate, which was the chief requirement at that time, as most 'of the mines were' considerably 'richer than the average at the present time, and wages and supplies were also considerably lower. ' The apparatus used at present has changed very little in principle. . The grizzly opening has gradually been increased to 12 in. and sometimes no grizzly 'is used. The crusher, gradually grew in size, the largest crusher has -an opening of about 24 by 13 in. and a 7/8-in. throw on the. eccentric shaft.

Jan 1, 1921

By E. J. Ripling

TUBES may be produced by a large number of forming processes, the most common of which will be discussed analytically in this paper. In no case will the stress analysis for any given tube producing process be derived formally for where such analyses are available, they may be referred to readily. Rather, emphasis will be placed on the interpretation of the theory of the different processes, few of which are developed to a state that will allow rigorous mathematical analyses, in an attempt to give a rational description of the effects of the different variables involved in each method. Tube producing methods can be divided into two groups: Those used to form shells, and those used to further work these shells into a shape more suitable for their final use. Among the first group are included roll piercing, extrusion and cupping for seamless shells, and bending with welding for welded tubes. The re-forming processes include sinking, drawing with a plug, and drawing with a rod. Only the plastic forming operations will be discussed here; other forming processes such as casting shells will not be considered. PRODUCTION OF SHELLS Shells for Seamless Tubing Piercing: The extremely important process of forming an axial hole in a billet by oblique rolling never has been analyzed satisfactorily, although a certain amount of experimental work relating to this process has been conducted. There are a number of factors that make piercing difficult to analyze; one of these is the fact that piercing is not a problem in plasticity, but one in fracturing, and the laws of fracturing are even less well understood than those of plasticity. If, however, it is assumed that fracturing occurs on a surface as a result of tensile stresses acting normal to this surface, piercing can be analyzed qualitatively by examining the stresses established in the oblique rolling process. To determine the origin of the tensile stresses that are thought to effect piercing, it will be necessary to know the angular relationships between the maximum stresses that are established in piercing. These angles quite frequently can be determined in a plastic deformation process by an examination of the deformed product. For example, consider the stresses established when a tensile test is conducted on a rectangular cross-sectional specimen of pearlitic steel. When stretched, this material first flows plastically, exhibiting the well-known yield jog on a stress-strain curve. The formation of the slip areas that give rise to the yield jog can be detected during the straining, since these flowed areas cause depressions on the specimen surfaces which can be seen if the surfaces are polished highly. The plastically strained areas also can be found after the specimen has been stretched to a strain not exceeding the yield jog, by sectioning the test piece and. etching these sections with Fry's etch. With this etchant, it is possible to dis-

Jan 1, 1951

By H. M. St. John

MAINTAINING a satisfactory structure in brass and bronze castings has always been a foundry problem of great practical importance. While metallurgists and scientific investigators have not entirely ignored this matter, it has received less of their attention than has been given to iron, steel and the wrought copper and aluminum alloys. Investigation in this field has probably been discouraged to some extent by the complicated nature of the alloys involved. Hundreds of alloys are in more or less common use, most of them containing copper, zinc, lead and tin in-widely varying proportions. They also contain appreciable percentages of iron and antimony as impurities, and often phosphorus, which has been added as a deoxidizer and fluidifier. Small amounts of sulfur are usually present. It is not uncommon to find nickel, sometimes in rather substantial quantities. Traces of other metals are frequently present. So complicated and variable a mixture obviously offers difficulties in. any investigation of the various factors that influence the structure and other properties of the casting.

Jan 1, 1930

By Clair Upthegrove, Elbert S. Rowland

THE widespread interest in the alloys of beryllium with copper is due principally to the fact that certain compositions show very favorable precipitation-hardening characteristics and are, in fact, the strongest nonferrous alloys known at the present time. Investigations have been conducted by Masing and Dahl and others on the physical characteristics of ternary beryllium alloys, in an attempt to produce precipitation-hardening effects with a smaller amount of beryllium than that required in the binary copper-beryllium alloys (2.0 to 2.5 per cent Be). The results of these investigations show that ternary alloys of beryllium with Cu-Sn, Cu-Al and Cu-Zn, among others, exhibit promising improvements in physical properties after precipitation-hardening treatment and, while the increases in properties obtained are not as high as those realized from the binary copper-beryllium alloys, excellent properties are: obtained with beryllium contents averaging about one-half the amount required in the binary alloys. This paper presents the results of an investigation of the equilibrium relations of certain alloys containing copper, tin and beryllium. The alpha-phase boundary of the ternary system is given for alloys containing from. 0 to 1 per cent beryllium. The equilibrium conditions beyond the alpha-phase boundary are presented for alloys containing up to 32 per cent tin and 1 per cent beryllium. The data were collected by means of

Jan 1, 1935

By T. S. Spicer

The relationship of coal characteristics to the principal types of firing equipment has been known to the coal combustion engineer, but is not as familiar a subject for purchasing agents, salesmen, consumers, and executives of coal-producing and consuming companies. This general survey of characteristics determined by standard laboratory tests, of major types of combustion techniques, and of the relationships between the two is directed toward the latter audience. It will also serve as a review for those actively engaged in the combustion of coal. Although the relationship of coal characteristics to the principal types of firing equipment is well known to the experienced coal combustion engineer, apparently there is need for a summary article on this subject. The author has received numerous requests for such a paper from purchasing agents, coal salesmen, coal customers and executives of coal-producing and consuming companies. Consequently, the scope of this paper will be directed to this audience, with the hope that it may serve also as a review to others actively engaged in the combustion of coal. The magnitude of this subject is so great that only a brief general treatise is possible. The author realizes that because there are so many special cases and exceptions to the generalities which follow, he is in jeopardy of contradicting himself. It is the hope, however, that the many references cited will prove valuable to those who wish to study the details excluded by necessity, due to space and time limitations. Hence, the characteristics of coals as determined by standard laboratory tests will be discussed; the major types of combustion techniques reviewed; and then the characteristics and firing will be related. CHARACTERISTICS OF UNITED STATES COALS The coals of the United States range from lignite to anthracite and each has its own general characteristics. The extensive coal fields of the U. S. are shown in Fig. 1 and the estimated reserve according to rank for each state is illustrated in Fig. 2. Coals may be classified according to rank as shown by Table I from the ASTM Standards on Coal and Coke, D-338-38.1 The basis of this classification is ac- cording to fixed carbon and heating value (Btu per pound) calculated to a mineral-matter-free basis. The high-rank coals are classified according to fixed carbon on the dry basis; and the low-rank coals according to Btu on the moist basis. Agglomerating and slacking (weathering) indices are used to differentiate between certain adjacent groups. While rank is not itself a characteristic it does signify certain characteristics that accompany a class of fuel. Anthracite, for example, immediately implies a hard, free-burning, smokeless coal of low volatile matter, usually having an ash of high fusibility. Coals may also be classified according to grade as described by ASTM Designation D-398-37.1 This quality classification is determined by size, calorific value, ash, ash-softening temperature, and sulfur. This type of classification is not used as extensively by the industry as the rank classification. Fig. 3 shows the heat value of different ranks compared to proximate analyses. Coals may also be classified by sizes, as shown in Tables IIA and IIB, and sizes can be on both top and bottom limits. If this is done, then the coal is called double screened; otherwise, either top or bottom sizes can be specified as a limit. Bituminous coal sizing varies from field to field and depends upon the market demand. The common sizes and their main uses are outlined in Table IIA. Anthracite is usually available in many sizes at the colliery, and Table IIB summarizes standard sizes and names. Although rank, grade, and size designations help identify and describe a coal in question, there still remain other characteristics such as indicated by moisture, free swelling index, grindability tests, etc. A bituminous coal information chart Table III) suggested for use in studying the available coals in a region, lists origin and chemical and physical characteristics. Even this more comprehensive list does not completely spell out all the characteristics of a heterogenous material like coal. For example,

Jan 1, 1961

By C. E. Birchenall, J. R. Stubbles

ThE equilibrium between lead, lead sulfide (PbS), and atmospheres of H2 and H2S has been determined previously by Jellinek and Deubel,' and SudO.' Blbem and Kroger3,4 used Jellinek's data to calculate the sulfur dissociation pressures of PbS crystals (of

Jan 1, 1960

By John T. Awald

The Bradshaw Mountains of west-central Arizona cover an area of 1600 square miles and contain numerous old mines and prospects. The area has been geochemically sampled on a reconnaissance basis to relate mineralized areas to regional structure and rock types. Copper analyses of stream sediments have been classified and contoured to show the distribution of low and high backgrounds and low, intermediate, and highly anomalous areas. Contoured results are compared to geology and known mines. Several prospecting areas are indicated.

Jan 1, 1972

By Nelson Severinghaus

THIS Rock Chapel plant of Consolidated Quarries Corporation (Fig. 1) is three miles northeast of Lithonia, DeKalb County, Georgia. It was opened about eight years ago for crushed stone aggregate. This paper reviews a number of experiments that have been tried in drilling and blasting, and gives the practice in use today. It also present, several theories on the action of explosives in this type of blasting. [ ] The rock worked is a bare dome of granite gneiss about 3000 ft. in diameter, rising 150 ft. above the surrounding ground (Fig. 2). It is uniform in composition and quality, without seams, and extends downward to unknown depth below the quarry floor. A water well drilled 600 ft. remained in the same rock. The principal difficulty encountered in blasting is an easy split, which tends to break clown the rock in large blocks.

Jan 1, 1938

By L. H. Levenson, Charles S. Barrett

Plastic flow in metal crystals and the changes in orientation resulting from it are generally understood to take place by the following fundamental mechanisms: (1) slip on crystallographic planes, (2) homogeneous crystal rotation resulting from the slip, (3) bending of the 1attice between the planes of slip, and, under certain circumstances, (4) twinning. This paper and a preceding one on iron subjected to uniaxial compression1 concern two additional processes that must now be added to this list: (5) the formation of deformation bands, and (6) the bending and rotation of these bands. The present investigation yields a new understanding and definiteness to the common terms so loosely used when speaking of cold-worked metals —('grain fragmentation," "elongated grains," and "deformation twins," "deformation bands," "etch bands," or "X-bands." Bands have been noted on the polished and etched surfaces of cold-worked metals by various investigators for more than 25 years, ‡ yet their nature and their significance have been so little understood that they are not treated in the most comprehensive modern texts on the deformation of crystals. The experiments in this series show that they are one of the fundamental processes in the deformation of metals, of importance in the development of preferred orientations, in work-hardening (since they have the effect of reducing the effective grain size and interfering with slip), and in the recrystallization process. The present experiments were performed on the same stock of material that was used in the earlier compression experiments1—hydrogen-purified mild steel in which the carbon content had been reduced to the limit detectable under the microscope and in which single crystals could be grown by a strain-anneal treatment.2

Jan 1, 1939

By L. Russell, van Wert

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By van Wert, L. Russell

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By Charles S. Barrett, L. H. Levenson

Plastic flow in metal crystals and the changes in orientation resulting from it are generally understood to take place by the following fundamental mechanisms: (1) slip on crystallographic planes, (2) homogeneous crystal rotation resulting from the slip, (3) bending of the 1attice between the planes of slip, and, under certain circumstances, (4) twinning. This paper and a preceding one on iron subjected to uniaxial compression1 concern two additional processes that must now be added to this list: (5) the formation of deformation bands, and (6) the bending and rotation of these bands. The present investigation yields a new understanding and definiteness to the common terms so loosely used when speaking of cold-worked metals —('grain fragmentation," "elongated grains," and "deformation twins," "deformation bands," "etch bands," or "X-bands." Bands have been noted on the polished and etched surfaces of cold-worked metals by various investigators for more than 25 years, ‡ yet their nature and their significance have been so little understood that they are not treated in the most comprehensive modern texts on the deformation of crystals. The experiments in this series show that they are one of the fundamental processes in the deformation of metals, of importance in the development of preferred orientations, in work-hardening (since they have the effect of reducing the effective grain size and interfering with slip), and in the recrystallization process. The present experiments were performed on the same stock of material that was used in the earlier compression experiments1—hydrogen-purified mild steel in which the carbon content had been reduced to the limit detectable under the microscope and in which single crystals could be grown by a strain-anneal treatment.2

Jan 1, 1939

By Norman Pilling

The micrographic analysis of silicon steels is possible if a dilute solution of nitric acid and methyl alcohol in nitrobenzol is used. The action of this reagent differs from that of sodium picrate in that there is no persistent deep-seated staining and the solution is used cold. THE technical difficulties hampering the metallographic analysis of silicon steels are chiefly the result of the extreme corrodibility of these alloys. The addition of silicon to iron in increasing quantities, up to about 6 per cent., rapidly increases the susceptibility of the alloy to chemical attack, not only in acid solution, but in water. This renders the preparation of metallographic sections very difficult, because of a non-selective attack upon the finely polished surface by the water used as a lubricant in polishing. This water attack masks the true structural details revealed by suitable etching reagents. It is thus necessary to use alcohol as a polishing lubricant in the last stages of preparation and to avoid all etching reagents having an aqueous base. A specific reagent for the identification of iron carbide in ferrous alloys, and the one hitherto used almost exclusively by metallurgists, is an alkaline aqueous solution of sodium picrate, which stains this constituent selectively. Its application to silicon steels has not proved successful, as its distinctive selective action is more or less completely hidden by the general attack of the aqueous solvent on the silico-ferrite, greatly accentuated by the fact that this reagent must be used at its boiling temperature (105° C.). Thus, a powerful metallographic aid to the study of the higher silicon alloys, such as transformer steels, is lost. A new reagent has been developed for the purpose of overcoming this difficulty. It is with some hesitation that the list of etching reagents, already overburdened, is increased, but the properties of this new reagent are advantageous in several ways and a definite field for it may be found in the metallography of ferrous alloys.

Jan 1, 1924

By Alan Morris

Brass rod for use in automatic screw machines is one of the major products of the brass mills. A large tonnage is consumed each year in the manufacture of an endless variety of finished articles and parts for assembly into other products. The machines that do this work have been developed to a high degree of efficiency, and their manufacturers are still striving for higher production speeds. This development has brought with it a demand for brass rod to meet the increasingly difficult machining conditions. This paper is a report of the results of tests undertaken in an effort to obtain a measure of the effects of such variables as lead content, microstructure and cold work on the machinability of brass rod. It is realized that the term "machinability" has never been well defined. Power, finish and tool life all should have a place in such a definition. In practice it is sometimes found necessary to sacrifice some of these in order to obtain a rod that will not tend to throw up a burr, or will give a burr which is easily tumbled off. Again a specially stiff rod may be necessary because of long overhang from the chuck or a rod of special characteristics is needed to take a given broaching operation without chattering. It is only through an understanding of the effect of basic mill operations on the machinability of the rod that such problems as these may be solved most economically. It is hoped that this paper, together with the discussion it may evoke, will prove to be a basis for such an understanding. Testing Apparatus The testing apparatus used was of the single-tooth milling cutter type, in all respects sirnilar to that first used and described by Airey and Oxford1 and again by Boston. The machine used in the present test is shown in Fig. 1. It is an ordinary milling machine in which a heavy pendulum has been substituted for the pulley on the arbor. If the pendulum is raised

Jan 1, 1932

By O. H. Eschholz

THE electrostatic process of fume precipitation is an excellent example of the successful application of scientific knowledge to an industrial operation. Originally proposed for the precipitation of sulphuric acid mists, it has been extended until at present there is practically no fume carrying gas to which the method cannot be applied. Among the more common applications are: the recovery of non-ferrous smelter flue-dust, iron blast-furnace dust, cement dust, and potash fume. It should be borne in mind that the process is restricted to the precipitation of suspended particles, either liquid or solid, and does not separate gaseous constituents. However, -by proper temperature control, mixtures of vapors having different temperatures of condensation to either solids or liquids may he selectively precipitated. The process consists essentially of subjecting suspended particles, including those too minute to be effectively acted upon by centrifugal or gravitational forces, to such an electrical force that they are driven from the gas stream, acting as a conveyer, and deposited upon a suitable receiving surface. This directional impulse is obtained front the interaction of charged particles and an electrostatic field of definite intensity gradient existing between two dissimilar electrodes, known as discharge and receiving electrodes. In principle, the equipment is equally simple. As shown diagrammatically in Fig. 1, it consists of: (1) A source of high-potential direct current, requiring: (a.) Source of alternating-current energy. (b) Means of transforming from tow voltage to high voltage. (c) Means of converting alternating to direct current. (2) Precipitation chamber having: (a) Transmission tubes for fume-laden gases. (b) Suitably designed and disposed electrodes. (c) Means for affecting removal of deposited solids.

Jan 8, 1918

By M. G. Corson

INFORMATION regarding the use of manganese alloys has hitherto been incomplete and available only from widely scattered sources. This paper attempts a systematic description of properties and uses of alloys other than manganese bronze, manganin and duralumin, which are probably the only non-ferrous alloys associated with manganese in the minds of most metallurgists.1 PROPERTIES OF MANGANESE Manganese can react either acid or basic; it is hard to obtain in the pure state; it has two different crystalline lattice structures, both of the cubic system, one stable above 850° C. and the other below 650° C., both coexisting in the intermediate range. Although the commercial product is hard and brittle, the pure metal seems to be ductile. In fact Zhemchuzhny, in Russia, was able to obtain ductile manganese and draw it to fine wires by the simple expedient of adding about 3 per cent. copper to the alumino-thermic product. Copper most probably brings the silicides, aluminides, nitrides and carbides present in the commercial product into a much less harmful form of distribution. One industrial use that can be foreseen for wrought manganese articles is as anodes for electrolytic processes in sulfate and nitrate solutions, particularly with high voltages. A practically insoluble skin of manganese peroxide is likely to form in such cases and an insoluble and strong anode material will be available. MANGANESE AS A SCAVENGER Because of its activity manganese might become the most efficient scavenger and refiner of copper, were it not for the fact that 0.01 per cent.

Jan 1, 1928