Search Documents

By D. S. Flett, D. W. West

The solvent extraction of chromium 111 has been studied for the system Cr 111, H,SO., H,O/RNH/RNH., xylene, where the primary amine used was Primene JMT. Rate studies have shown that extremely long equilibrium times are required, ranging from 1 hr at 80°C to 20 days at room temperature. Heating the solution prior to extraction increases the rate of extraction. The variation in the amount of Cr 111 extracted is an inverse function of the acidity of the aqueous phase. Thus, the slow rates of extraction appear to be connected with the hydrolysis of the Cr I11 species. Extraction isotherms for the extraction of Cr 111 have been obtained for two sets of experimental conditions, namely at 60°C and for a heat-treated solution cooled to room temperature. The separation of Fe 111 from Cr 111 and Cr 111 from Cu 11 in sulfate solution by extraction with Primene JMT has been studied and shown to be feasible. A survey of the literature relating to the solvent extraction of chromium showed that, although many systems exist for extraction of Cr VI, only a very few reagents have been found to extract Cr 111. The extraction of Cr III by di-(2-ethyl hexyl) phosphoric acid has been reported by Kimura.' A straight-line dependence of slope —2 was observed between log D,, and the log mineral acid concentration at constant extractant concentration. Since the slope of this plot reflects the charge on the ion extracted, it must be concluded that a hydrolyzed species of Cr III is being extracted. Carboxylic acids generally do not form extractable complexes with Cr III but di-isopropyl salicylic acie does extract Cr 111. Simple acid backwashing of the organic phase, however, failed to remove the chromium. Similar difficulty in backwashing was found by Hellwege and Schweitzer8 in the extraction of Cr I11 with acetyl-acetone in chloroform. The extraction of Cr 111 from chloride solutions by alkyl amines has been reported4-' but the maximum amount of extraction achieved in these studies did not exceed 10%: From sulfate solutions, however, Ishimori" has shown that appreciable amounts of Cr I11 were extracted by amines. The amines used were tri-iso-octyl amine, Amberlite LA-1 (a secondary amine, Rohm & Haas) and Primene JMT (primary amine, Rohm & Haas). The efficiency of extraction with regard to amine type was primary>secondary> tertiary. Appreciable extraction of Cr I11 was recorded for Primene JMT as the aqueous phase acidity tended to zero. The major difficulty with Cr I11 in solvent extraction systems stems from the nonlabile nature of the ion in complex formation. This accounts for the slow rate of extraction generally experienced and the difficulty encountered in backwashing the Cr I11 from the organic phase in the case of liquid cation exchangers. Consequently, the possibility of extraction of Cr I11 as a complex anion is attractive since the backwashing problems should be minimized in this way. From published data, it appeared that the extraction of chromium from sulfate solutions of low acidity by primary amines afforded the best chance of success for a useful solvent extraction system for Cr iii This paper presents the results of a study of the extraction of Cr I11 from sulfate solution by Primene JMT and examines the application of such an extraction procedure for the recovery of chromium from liquors containing iron and copper. Experimental Chromium solutions were prepared from chrome alum in sulfuric acid and sodium sulfate so as to maintain a constant concentration of sulfate ion of 1.5 molar. Solutions of Primene JMT were prepared in xylene and the amine equilibrated with sulfuric acid/sodium sul-fate solutions, of the same acidity as the chromium solution, until there was no change in acidity between the initial and final aqueous phases. The solutions of Primene JMT conditioned in this way were then used for the equilibration experiments. Equilibrations at 25°C were carried out in stoppered conical flasks shaken in a thermostat; equilibrations at all other temperatures were carried out in stirred flasks in a thermostat. After equilibration, the phases were separated and analyzed for chromium. In the tests on the rate of extraction, small samples of equal volume of both phases were withdrawn from time to time and the chromium distribution determined. The chromium analyses were carried out either coloi-imetrically using diphenyl carbazide, or volu-metrically using addition of excess standard ferrous ammonium sulfate and back titration of the excess iron with potassium dichromate. The oxidation of Cr 111 to Cr VI in the case of the raffinate solution was effected by boiling with potassium persulfate in the presence of silver nitrate and, for the backwash solution, by boiling with sodium hydroxide and hydrogen peroxide. Results Preliminary experiments indicated that extraction results were effected by the age of the chromium solution, higher distribution coefficients being obtained with solutions which had been allowed to stand for some time. Consequently a stock solution of chrome alum, 10 m moles per 1 Cr I11 in 1.4 M Na,SO,/O.l M &SO,,

Jan 1, 1971

By D. F. Hewett

[In an increasing degree in recent years, especially since the war, men in many parts of the world are turning their attention to the problems of the future, attempting to appraise the basis and extent of man's progress and interpret the problem that he faces in the near future. The war made clear to ma persons the degree to which modern industry depends upon t continuous flow of enormous quantities of raw materials, a especially of the minerals. In many circles throughout t world, the question of adequate supplies of the mine especially the fuels and metals, for near as well as more remo needs is receiving serious consideration. As a result, persons representing the state as well as industry are looking to geologists and engineers for all the data that throw light on the distribution, extent and availability of the minerals that must serve coming generations.] Obviously, in a brief research I have been able to consider only a few sources of the metals in Europe, perhaps fifty out of a total of many hundreds. In order that the conclusions may have value, however, I have chosen districts which have been important sources during some epoch of the last three hundred years or more.

Jan 1, 1932

By D. R. Walker, M. C. Shaw

THE laws of comminution of Kick and Rittinger have been debated for many years. Certain data obtained from ball mill and drop tests are found to be in approximate agreement with Rittinger's law while other data would seem to support Kick's law. In all these tests the energy required to produce a wide variety of particle sizes has been studied. Surface area has also been measured with considerable difficulty, at first because it was thought that the energy associated with crushing was that required to create new surface, later because of precedent and because a more fundamental variable was unknown. Tests made with the machine shop type of grinding process show that normally brittle materials that are usually crushed can behave like the more ductile metals. Brittleness is then a relative property largely dependent on specimen size and stress state. The machine grinding operation offers a convenient means for studying the comminution of materials in which the important size variable retains its identity. The energy required to grind a certain volume of material is shown to be strongly de- pendent on size. Kick's law is found to hold very well for particles below 1 micron in size, while Rittinger's law holds approximately in the comminution of larger particles. While a physical origin of Kick's law is established in terms of the theoretical strength of materials having a perfect lattice structure, there is found to be no physical basis for Rittinger's law.

Jan 3, 1954

By A. A. Scheil, S. I. Hoyt

In technological studies on steel considerable emphasis has been placed on the identification of the foreign inclusions, testimony of which is adequately given in the metallographic literature covering methods for their identification. The outstanding accomplishment in this field is the scheme devised by Campbell, Comstock and Wohrman for identifying various oxides, sulfides, silicates and other constituents by systematic etching tests and microscopic examination.' The time involved in carrying out this procedure has led to attempts to secure quicker methods, or at least to shorten the time required to secure essential information. An example of this is the use of dark field illuminatin,2 but when this was tried out by the authors it was found that cavities and pits on the polished surface appeared bright on a dark field and could not be distinguished from small glassy inclusions. Still another means is the Leitz Ultropak, an instrument equipped with optical units for the illumination of the specimen by reflected light to secure an effect similar to dark field illumination. The structures are made visible in exceedingly sharp details by utilizing the inherent properties of the samples, such as refractive index, absorption coefficients and reflection powers. We have had no experience with the Ultropak, but a recent paper by Benedicks and Löfquist3 describes methods for determining the refractive index of (Fe, Mn) O and MnS by the use of this equipment. Presumably this method would be subject to about the same limitations as dark field illumination, though the, feature added by Benedicks and Löfquist appears to offer great promise in inclusion identification.

Jan 1, 1935

By R. K. Hopkins

For a great many years fusion welding has been used in and around petroleum refineries, but it is only within six or seven years that the more important pressure vessels have been constructed by this process, because before that time the properties of fusion welds would not with-stand such rigorous service. Since the adoption of fusion welding for the construction of this equipment, the refiner has required pressure vessels suitable for operation over a very wide range of conditions. On the one hand, vessels must operate at extremely high temperatures, in the range of 950° to 1000° F., and on the other vessels must be suitable for operation at sub-zero temperatures down as low as -75° F. Also, vessels are required suitable for operation at pressures upwards of 1000 lb. per sq. in., and as low as a 29-in. vacuum. In addition, vessels are required to withstand the attack of very corrosive mediums. It has been a rather difficult task for the fabricator to meet all of these require-ments, but as a result of the extensive research carried on by steel manu-facturers and several fabricators of class I vessels, practically all of these demands have been met. In order to meet the refiners' requirements for this wide range of conditions, the fabricator has worked closely with the metallurgist. This has enabled him to choose the proper base metal for each service condition, but it has been the fabricator's problem to develop a welding rod and welding technique, as well as a heat-treatment, that would produce in the welded vessel characteristics in and around the weld comparable to those in the base metal. Where corrosion is not a serious problem, and where the operating temperatures are not too high, ordinary carbon steel has served very well. But when corrosion is serious, and/or when the temperatures are either very high or very low, it is necessary to use some form of alloy steel to give satisfactory service.

Jan 1, 1935

By J. H. Yang, K. E. Gray

Results of single-blow bit-tooth impact tests on saturated rocks under elevated confining pressures and zero pore pressure were reported in a previous publication.1 This paper presents an extension of the earlier work to include a study of crater formation during tooth impact on both gas- and liquid-saturated Berea and Bandera sandstones at elevated confining and pore pressures. The basic data obtained were force-time, displacement-time, velocity-time and force-displacement curves during crater formation. Crater volume was also measured and the mode of crater formation determined. Bit tooth geometry, depth of penetration and velocity of impact were held constant. Results indicate that, with pore fluid present in the rock, failure trends from brittle to ductile as pore pressure is increased at constant confining pressure (pore pressure and borehole pressure were equal) For a given rock type, the mode of crater formation was dependent not only upon the nominal effective stress, but also upon the fluid which saturated the rock pore space. When confining pressure and pore pressure were equal (zero nominal effective stress), bit-tooth impact resulted in brittle failure for nitrogen-saturated Berea, and brittle to transitional failure for nitrogen-saturated Bandera; when saturated with liquid both rocks failed in a ductile manner at zero nominal effective stress. INTRODUCTION Dynamic wedge penetration tests have been conducted by investigators in several fields, but the failure mechanism of rock under dynamic stresses is not understood completely. The complex action of drilling bits, even considering the action of a single tooth, may be considered as a combination of drag bit and rolling cutter action. Thus, as a first step in understanding rock breakage in oil well drilling, single chisel impact and rock planing are of fundamental importance. For example, Gray 2 and Crisp3 studied drag bit cutting action at brittle stress states. Simon4 and Hartman5 studied the reaction of rocks to vertical impact by means of drop tests. The depth of penetration, crater volume and force-vs-time curves during crater formation were observed. The significance of indexing single-bit impacts has been noted.4,6-8 Gamer et al,9 reported impact tests on impermeable Leuders limestone at atmospheric and elevated confining pressures. In all cases the tests were accomplished on dry rock and pore pressure was considered to be zero. The importance of both confining pressure and pore pressure on the failure characteristics of rock was described. 10-12 It was found that the yield strength and ductility of porous rock depend on the state of stress under which the sample is tested. The importance of pore pressure on drilling rate in microbit experiments was noted by Cumingham and Eenink. l3 Robinson 12 also pointed out that in drilling the most important parameter in rock failure is the effective stress, where effective suess is defined as confining pressure pc minus pore pressure pp. The effect of pore pressure and confining pressure on rock strength was also noted by Serdengecti and Boozer 14 in strain rate tests, and by Gardner, Wyllie and Droschackl5 in elastic wave studies. Until recently all reported wedge impact studies under simulated wellbore stress states have been conducted on dry rock. Maurer 16 reported impact tests on samples saturated with deaerated water. Borehole and formation fluid pressures were equal in these tests except when mud was used in the borehole. With mud in the borehole and a high borehole-to-formation fluid pressure differential. Maurer observed "pseudoplastic" crater formation. Podio and Grayl reported impact tests on Berea and Bandera sandstone saturated with pore fluids having wide ranges in viscosities. In Podio and Gray's tests, confining pressure was elevated, but pore pressure and borehole pressure were held fixed at atmospheric pressure. The presence of

By Walter V. Knopp, Laurence Delisle

The aim of this work was the preparation of nickel-steels from elemental metal powders by powder metallurgy techniques. It was known that plain carbon steels could be made from a mixtufe of iron powder and graphite and that the effect of carbon on iron in powder form was of the same nature as that produced in fusion metallurgy. The problem in making nickel steels from elemental powders consisted therefore in finding out whether sufficient diffusion of the nickel and other incidental metals . normally present in such steels could be induced in the solid state to modify the properties of plain carbon steels made from powders and produce the beneficial effect of alloying. The composition selected originally was that of an S.A.E. 2330 steel. Metal powders, in the proportion correspending to that composition, were mixed with graphite, pressed, and heated at different temperatures for different periods of time, to produce bonding of the metal particles and mutual diffusion of the various elements without melting. Temperatures up to 1325°C and sintering periods as long as 6 hr were first investigated because it was expected.that such conditions would produce maximum diffusion with an accompanying improvement in the properties of the alloy. It was found that, although diffusion proceeded to a large extent under the conditions investigated, it would not be complete unless sintering were carried out at a high temperature for much longer than 6 hr. Relatively high temperatures and long sintering times are objectionable from a practical point of view, particularly when a low COSt material is to be produced, because they necessitate the use of special, costly equipment. Work could be done to improve the diffusion of iron and nickel by changing conditions other than the sintering temperature and time, that is, finer primary or alloy powders could be used. However, a marked change in the properties of the steel had been observed even with only partial diffusion. It was thought, therefore, that instead of trying to improve the diffusion, advantage might be taken of its incompleteness to produce a special structure consisting, in the unquenched condition, of a hard constituent, rich in nickel, dispersed in a tough pearlitic matrix. Steels with such a structure, not readily obtainable by fusion, should have desirable mechanical properties. Besides, it should be possible to prepare them from elemelltal powders under economical conditions. This latter alternative was therefore adopted for the second phase of this work. This report is divided into four parts: I. General Procedure. 2. Effect of Sintering Temperature. 3. Effect of Varying the Nickel Content. 4. Effect of Alloying Elements. General Procedure The general technique of cold pressing as used in powder metallurgy was applied.

Jan 1, 1949

By A. A. Scheil, S. I. Hoyt

In technological studies on steel considerable emphasis has been placed on the identification of the foreign inclusions, testimony of which is adequately given in the metallographic literature covering methods for their identification. The outstanding accomplishment in this field is the scheme devised by Campbell, Comstock and Wohrman for identifying various oxides, sulfides, silicates and other constituents by systematic etching tests and microscopic examination.' The time involved in carrying out this procedure has led to attempts to secure quicker methods, or at least to shorten the time required to secure essential information. An example of this is the use of dark field illuminatin,2 but when this was tried out by the authors it was found that cavities and pits on the polished surface appeared bright on a dark field and could not be distinguished from small glassy inclusions. Still another means is the Leitz Ultropak, an instrument equipped with optical units for the illumination of the specimen by reflected light to secure an effect similar to dark field illumination. The structures are made visible in exceedingly sharp details by utilizing the inherent properties of the samples, such as refractive index, absorption coefficients and reflection powers. We have had no experience with the Ultropak, but a recent paper by Benedicks and Löfquist3 describes methods for determining the refractive index of (Fe, Mn) O and MnS by the use of this equipment. Presumably this method would be subject to about the same limitations as dark field illumination, though the, feature added by Benedicks and Löfquist appears to offer great promise in inclusion identification.

Jan 1, 1935

By C. Gatlin, N. E. Garner, A. Podio

Experimental data from single chisel blows on Leuders limestone are presented. A pressure chamber, similar in design to well known microbit drilling chambers, was utilized to impose variorcs stress states on the sample. Confining pressure of zero to 10,000 psi and borehole pressures from zero to 5,000 psi have been used in the studies. Pore pressure was zero and the rock samples dry in all instances. Force-displacement records and visual examination of the craters indicate that the mode of failure depends on both confining and borehole pressure in certain ranges, ranging from brittle, through a transition, to near plastic. The mode of failure is reflected in the observed blow force and energy data, as well as the shape of force-penetration curves. INTRODUCTION A previous paper' presented initial data from the project on which this paper is the second report. While the first paper dealt with impact studies on synthetic rocks, the literature cited there is also pertinent to this paper, but will not be listed again in order to avoid needless repetition. This paper presents experimental data from single chisel impacts on limestone at certain simulated wellbore stress states. Specific variables investigated were combinations of borehole and confining pressure, crater geometry, a narrow range of impact velocity and the forces required to drive the chisel into the specimens under the varying conditions. EXPERIMENTAL PROCEDURE The same basic apparatus described in our earlier paper, except for the pressure vessel, was used in this study. Fig. 1 shows the complete experimental system. Fig. 2 shows details of the pressure cell, which is quite similar to the well known microbit drilling chamber. The confining (overburden) pressure system provides independent pressure control over the sample except for two, 21/4 in. diameter areas located on the sample ends. These two areas provide a pore pressure entrance on the bottom and a striking surface on the top where borehole pressure can be controlled. The ends are isolated from the confining pressure by O-ring seals. The borehole and pore pressures are related through the striking surface; they will be the same unless a seal is deposited on the borehole surface, either a mud cake or some other impermeable membrane. In these studies pore pressure control was not used, as the rocks were dry and unsaturated in all cases. Rock samples were prepared from 4-in. cubes as illustrated by Fig. 3. The circular disks of adhesive vinyl plastic protected the impact surface from the resin coating (Scotchcast No. 2) and were removed just prior to each test. This procedure insured a fresh uncontaminated surface for the impact. Fig. 4 shows the dimensions and loading of the sample, including the concentrations around the "borehole" periphery (O-ring seal). The rock used in this study was Leuders limestone, of Permian age (Leonard), quarried near Leuders, Tex. Geologically, Leuders limestone is a light gray, fossili-ferous limestone (oolitic foraminifera1 biosporite). Its fossil content is 80 to 90 per cent and consists primarily of calcitornellid, ostracods, pelecypods and oolites with the remaining part intraclasts. There are hematite or limo-nite rims on some of the intraclasts. The porosity is approximately 20 per cent, but the permeability is less than 1 md. There is no apparent orientation in the structure. Triaxial tests have been conducted to determine the variation of the physical properties of Leuders limestone in three orthogonal directions', and it is known to be unusually isotropic and uniform. Physical parameters for this rock are: uniaxial compressive strength = 9,700 psi; F = 32 and C = 2,700 psi; where + and C are Coulomb equation values (t = C+u tan +). Impact tests were run under the combinations of confining and borehole pressures shown in Table 1. Samples were dry with atmospheric pore pressure in all cases. Tests, in which elevated borehole pressures were applied, used a single layer of household Saran-Wrap to prevent horehole fluid invasion into the sample. This proved to be simple and reliable. The blunt wedge used in all the tests was 0.75 in. long and had an included angle of 60" with a 0.05-in. flat. In addition, a sharp 60" wedge was used for all confining pressures at zero borehole pressure. The chipper speed

By Samuel Daniels

THE Al-Cu-Ni-Mg alloy is much benefited by heat treatment and, in such con¬dition, is preferable to the Al-Cu-Fe-Mg alloy either as cast or as heat-treated, when both are reheated to temperatures of from 400° to 600° F. and compared, cold, with respect to strength and to hardness. The main differences between the alloys do not arise until the reheating temperature exceeds 400° F., above which they gradually soften. This softening is characterized metallographically by the appearance of intragranular precipitate. The Al-Cu-Ni-Mg alloy is weakest and least hard after being reheated at 600° F., the AI-Cu-Fe-Mg alloy at about 700° F. The former starts to reharden at 700° F., the latter at 800° F. There is a tendency for both alloys to lose strength and hardness with prolongation of time at the reheating temperatures of 500° and of 700° F. The Al-Cu-Ni-Mg alloy is considerably stronger and harder than the Al-Cu-Fe-Mg alloy when both are heat-treated and reheated for long periods of time at 500° and 700° F. Although the latter can be made harder initially than the AI-Cu-Ni-Mg alloy by suitable quenching and aging, heat treatment, in general, favors the retention of this initial (strength and) hardness after reheating to a much greater degree in the Al-Cu-Ni-Mg alloy. The percentage of elongation of the two materials in any condition is very small. CERTAIN aluminum alloys have been used for pistons and other parts operating at temperatures up to 650° F. because of their lightness, high thermal conductivity and specific heat, fair strength and hardness at elevated temperatures, excellent machineability, and moderate resistance o corrosion. In the piston, the inertia forces and the bearing loading and with this the vibration are decreased. The piston head functions at a lower temperature (about 200° F. below one of cast iron), so that, because of the lessened tendency toward carbonization and detonation, higher compression ratios may be used. On the other hand, the aluminum alloys do not have the wearing and bearing qualities of cast iron; also they have a large coefficient of expansion, allowance for which must be made in the design.

Jan 2, 1926

By H. S. George

A method of illumination that enhances the value of microscopic study of opaque materials, as in metallography. By simulating natural lighting, structures. That possess relief are given a natural appearance. An example is included of the revelation of a hitherto invisible microconstituent. Erroneous interpretation is avoided. For example, etching figures in ferrite, heretofore considered to be pits, are revealed as pyramids, standing in bas-relief. Suggestions on technique are given, for, while the method is obvious, practice and attention to detail are requisite. ON one occasion when it seemed desirable to reveal under the microscope not only the metallic structure of an alloy, but certain small non-metallic inclusions, that are ordinarily obliterated by etching, it was discovered that, by partly eclipsing the illuminating pencil of light rays, the residual light was thrown on the object from one side and the structure was brought out in relief. At the same time, the non-metallic inclusions were retained in clear view. In this first demonstration of lighting obliquely through the objective a card was thrust part way into the light beam between the arc iris, and the light filter; the shadow of the card on the filter served to locate its position. Next several stiff-paper disks of various diameters were mounted on flexible wires some plasticine on the other end of the wires made it easy to adjust and maintain a disk at any desired position in the light beam. To facilitate manipulation, an assortment of disks, was mounted on a wheel, as shown in Fig. 1. The purpose of partly eclipsing the light beam was discussed in an earlier paper.1 There it was pointed out that the usual methods of illuminating opaque objects for microscopic examination lend an, un-natural appearance to, the view, while the new method, which has been termed conical illumination, revels the true relationship of constituents by simulating natural lighting.

Jan 3, 1924

By R. P. Carreker, R. W. Guard

True stress-true strain data are given for nominally pure molybdenum (99.95 pct) over the temperature range -196° to 1540°C (0.027 to 0.63 T/T). Strain rate sensitivity was determined by rate change tests and stress relaxation tests. Inhomogeneous yielding and strain aging effects were observed. The yield stress and tensile strength depend markedly on temperature below 400°C and are insensitive to temperature in the range 400' to 800°C. The ductile to brittle transition range is +25O to -25OC. Strain rate sensitivity and stress relaxation effects are very large near room temperature. THIS report presents data which were obtained as a part of a continuing program designed to document the deformation behavior of nominally pure metals over a wide temperature range.'" This research program is rooted in the conviction that sufficient tensile and creep data of appropriate quality and detail does not exist to provide precise phe-nomenological descriptions of the deformation behavior of pure metals as a function of temperature, strain rate, and grain size. Such knowledge is needed to provide a firm base for alloy design and an experimental framework to which theories of deformation must conform. These data also complement a parallel exploratory program investigating the properties of refractory metals, including molybdenum, and their alloys. Several important reviews and research reports dealing with the tensile properties of molybdenum as a function of temperature have appeared."-lo To a great extent the work to be reported in the present paper parallels that of Bechtold and of Pugh. The authors' results are in general agreement with those of Bechtold and Pugh. The principle differences be- tween the present experiments and those published previously are as follows: 1—Wire specimens prepared from arc cast molybdenum were used in the present experiments, bar specimens were used by others. Pugh used arc cast material while Bechtold's most extensive results" were obtained on powder metallurgy specimens. 2—Several different grain sizes were tested in the present experiments. 3—The testing range was extended to cover from -196°C to 1570°C (0.027 to 0.63 T/Tm). 4—The combination of wire specimens, high speed autographic recording, and a stiff testing machine permitted more detailed study of initial yielding. The principle contribution of the present paper is the demonstration of the relatively consistent mechanical properties of nominally pure arc cast molybdenum specimens of differing metallurgical history. Bechtold and Scotts have shown that arc cast and powder metallurgy molybdenum samples have comparable tensile properties in the range —75" to 200°C when processed to have the same re-crystallized grain size. Material The molybdenum used in this investigation was supplied by the Climax Molybdenum CO. Its metallurgical history is outlined in Table I; the final products were 0,030 in, diam wire specimens annealed at 1100' and 1375°C and 0.060 in. diam wire

Jan 1, 1957

By T. E. Leontis, R. S. Busk

WORK was initiated several years ago at The Dow Chemical Company to determine the applicability of powder metallurgy processes to magnesium and its alloys. Although it was found possible to apply the normal techniques of compacting and sintering, it was discovered early that the technique of extrusion offered special promise. This technique and the alloys produced were therefore studied extensively, and the present paper is a partial report of those studies. It is expected that a second paper will discuss more extensively some of the alloy systems simply mentioned here. Although the literature on powder metallurgy is very extensive, there are only two articles dealing with magnesium13,14 and there is no reference to the direct extrusion of the powder of any metal without the preliminary step of compacting. Furthermore, no mention has been made of the possibility of designing alloys by the technique of powder extrusion, particularly alloys that cannot be made in any other way. Sauerwaldl3 discusses the extrusion of magnesium and aluminum powder to produce alloys containing nonequilibrium phases, but again he emphasizes the importance of pre-compacting before extrusion. There seems to be general agreement that some form of hot-pressing is essential to obtain in a compact the full theoretical density of the metal used.'-" The nearest approach to the technique of direct powder extrusion is that of extrusion of pre-sintered compacts,'-" for which the best review through 1944 is that by Kieffer and Hotop.11 Ensign* discussed a specialized technique of "extruding" already compacted and sintered gears for the purpose of sizing. Sauerwa1d13 discussed the compacting and extrusion of magnesium and magnesium-aluminum alloy band-saw chips. The properties of the extruded compacts were found to be comparable with those of extrusions prepared from solid billets. He also extruded a compacted mixture of magnesium and aluminum powder and found the properties to be somewhat different from those obtained on an extrusion made from a cast billet of the same composition. The second reference dealing specifically with the powder metallurgy of magnesium is Stern's patent," in which is described the extrusion of scrap chips and turnings following a hot-pressing and sintering step. Considerable emphasis in most of these articles is placed on the necessity of atmospheric protection to minimize the danger of oxidation. Experimental Procedure The first experiments were made with the small extrusion press shown in fig. 1. With this press, billets of about 1/2 in. diam are used to produce wire

Jan 1, 1951

By H. R. Hanley

THE characteristics of alloyed anodes and their influence on the products of electrolysis and power consumption have been noted previously in the literature.1 This paper presents data in continuation of the subject given in an earlier paper by the authors.2 As noted in the authors' previous paper, the objectives of this work are the reduction in the cell voltage and the purity of the cathode product resulting from the use of alloyed lead anodes. The fundamental facts developed in the previous paper were: (1) that the presence of a small amount of calcium lowers the anode potential approximately 50 per cent. below that of pure lead; and (2) that thallium when present to the extent of 4 per cent. rendered the anode practically stable, thereby lowering the contamination of the cathode by lead to a very insignificant amount. The specific features determined in this recent work are as follows: 1. The lowest limit of calcium in the lead which will still give maximum lowering of the anode potential. 2. The characteristics of the thallium-calcium-lead anode. 3. The characteristics of the silver-calcium-lead anode. 4. The characteristics of the thallium-silver-calcium-lead anode. It was determined that 0.1 per cent. calcium in the anode was sufficient to lower the anode potential approximately 50 per cent. Table 1 shows the characteristics of alloyed anodes tested. The anode composed of 0.1 per cent. calcium, 4 per cent. thallium, and 95.9 per cent.

Jan 1, 1931

By J. L. Bray

IT is well known that iron markedly improves the physical properties and casting characteristics of aluminum bronzes. The use of 1 to 4 per cent iron as the principal modifying addition has become common practice in many foundries melting aluminum bronzes. Although the beneficial effects of iron are unquestioned, there is some uncertainty regarding the structural changes caused by it in the basic copper-alumi-num system. It is agreed that a new constituent appears in abundance when the iron content reaches 2 to 4 per cent. This constituent, which frequently occurs in shapes resembling clover leaves, is sometimes assumed to be an aluminum-iron intermetallic compound. If this were correct we might expect a change in the structural relationships of the matrix in the direction of decreased aluminum content. On the other hand, it has been reported that iron has a negligible effect in altering the fundamental relationships of copper-aluminum alloys1. Others2,3 have reported an additive coefficient. Apparently it will be necessary to know the equilibrium relationships between the phases of the copper-aluminum-iron alloy system to establish any such theory as fact. When this has been done it may very well be that a further revision in the structural relationships may be necessary to describe the changes to be expected in commercial cast alloys. It was with this latter problem before them that the authors attempted to

Jan 1, 1936

By D. D. Pollock, D. I. Finch

PREVIOUS work' on a four-component system (Cu-Mn-Ni-Fe) resulted in the development of consistent relationships between the chemical composition and the electrical properties of these manganin-type alloys. The present study was undertaken to develop alloys with temperature coefficients of resistivity and thermoelectric properties more desirable than those of the manganin type, and to determine whether the relationships which had been found for the Cu-Mn-Ni-Fe alloys could be extended to five-and six-component alloy systems. PREPARATION OF ALLOYS The five- and six-component alloys were made from OFHC copper rod, ARMCO iron, electrolytic nickel, manganese cathode chip, and special high-purity aluminum and indium. A Cu-Mg master was used for deoxidation. The compositions of these materials are given in Table I. The alloys were melted and cast as indicated previously,' except that no cover was used and the melts were teemed. EXPERIMENTAL PROCEDURE The finished wire size of 0.0808 in. diam was again selected for the reason that the test specimens would be self-supporting, thus eliminating any extraneous effects which might have been introduced by winding smaller diameter wire on spools or forms. The following tests were performed on the finished wires: A) Chemical Analyses—All of the components of these alloys were determined by premium gravimetric methods. The principle residual impurity contained in these alloys is 0.008 pct Mg (by weight), maximum. Tables II and 111 present the mean analyses computed from at least four determinations of each constituent. B) Electrical Characteristics—The test procedures forthe determination of the thermal emf vs copper, resistivity, and the resistance-temperature relationship are given in detail in Ref. 1. It was also shown that the resistance-temperature relationship is of the form Pt = P,n + At -B/2, [1] where P, is the resistance at t C expressed in percent of a given standard resistance, P, is this per- 0 centage at 0°C, and A and B are constants for a given, properly treated, composition. The results of the electrical tests are also given in Tables II and 111. INTERPRETATION OF DATA The modified Linde2 formula, known to be valid for dilute binary solid solutions, was applied to the complex Cu-Mn-Ni-Fe type alloys. This relationship is of the form where Ap is the increase in resistivity. Zb the valence of the solute, Zn the valence of the solvent, and K and K are designations assigned by Robinson and Dorn3 to the constants for the periodic group to which solute element belongs. The units of K, are -cm per valence difference squared per at. pct; those of K2 are pa-cm per at. pct. For the sake of brevity, these units are not repeated in the following discussion. Calculations were made to determine if this formula was accurate for five-component systems. No experimental studies were made of the Cu-In and Cu-A1 binary systems. The effects of indium additions upon the resistivity of copper are given by Linde. These data, along with those of the effects of Mn and Fe, permitted the calculation of the effects of Al.

Jan 1, 1959

By K. L. Komarek, P. F. J. Landler

Synthetic polycrystals of wustite were reduced ilz H2-H2O mixtures over limited roncentration ranges wiltun the wustite. field and the weight changes were continuously followed with a McBain quartz spiral balance. The reduction was. found to be controlled by a combined surface plus solid-state diffusion reaction. The solid-state diffusion had an activation energy of 38 kcal. Self--diflusioities of iron decreased with itzcreasing vacancy concentration. The activation energy of. the surface reaction runs different tor- different samples. The surface reaction-rate constan increased with increasirzg vacancy concentration. THE reduction of the oxides of iron has been studied for many years. Edstroem' has summarized the early work and has provided much information on the reduction of magnetite and hematite by hydrogen and carbon monoxide. More recent summaries are those by smeltzer2 and Themelis and Gauvin.3 Most investigators have reported that the iron metal which forms the outer layer during gaseous reduction is rather porous. According to Kohl and Engel14 the formation of such a porous iron layer depends on the properties of the underlying wiistite layer, on the reaction of the gas with the wustite surface, and on the transport of matter through the wustite layer. McKewan, Quets, Wadsworth, and Lewis, and Knacke 10 have found that, if a porous iron layer is formed, a surface reaction between gas and wustite at the bottom of the pores controls the rate of reaction. Seth and ROSS 11 and Warner 12 have pointed out that the influence of the gaseous pore diffusion through the porous iron layer cannot be neglected. It has further been shown that the wiistite layer formed during reduction is dense and that transport of matter across the layer occurs only by solid-state diffusion of iron ions.13,14 The solid-state diffusion rates observed by Edstroem and Bitsianis 14 and the surface reaction rates observed by Quets eta1.' show that an interaction of the two steps in controlling the reaction rate has to be considered. In this investigation the reduction of wustite was studied with respect to the interaction of the two steps, isolated from any other effects, by reducing wustite within the wustite field from higher to lower oxygen concentrations with H2-H2O gas mixtures. A similar study with CO-CO2 mixtures has been performed by Levin and wagner.15 Fused synthetic wustite polycrystals were reduced in steps of 0.4 wt pct from 24.4 to 23.2 wt pct 0 and over a temperature range from 700" to 1050°C. A few tests were also conducted with reduction steps from 24.4 to 23.6 wt pct 0 and 24.5 to 23.2 wtpct0. The Fe-O phase diagram is shown in Fig. 1 where the composition of the gas phase in equilibrium with the condensed phases is plotted as pct H2 vs the temperature. A careful study of the literature led to the conclusion that the fully drawn equicomposition curves (in wt pct O) in the wustite field used by Edstroem 1,16 and other authors needed some correction. Based on results by Darken and Gurry17 (shown as open circles) and on some of our own data, four corrected curves for 23.2, 23.6, 24.0, and 24.4 wt pct O were calculated (drawn as dashed lines in Fig. 1) which should replace the fully drawn equicomposition curves. MATERIALS AND APPARATUS Materials and Specimen Preparation. Wustite was prepared from iron sulfate (Fisher Scientific Co., New York) which had a purity of over 99.92 pct, with small amounts of manganese, copper, and zinc adding up to 0.03 pct. From the aqueous solution iron oxalate was precipitated and decomposed to magnetite according to Economos. 18 The magnetite powder was pressed into cylinders and sintered in vacuum at 900°C for several hours. The sintered compacts were placed in a platinum crucible of 2.5 cm diam which was fitted into a high-purity alumina crucible and then inserted into the center of the graphite heating element of an electric resistance furnace.lg The furnace was evacuated to below 1 p Hg and the magnetite sample was slowly heated. The evolution of gases during heating deter-

Jan 1, 1967

By Paul Foote

SEEBECK discovered, in 1821, that if, in a closed circuit of two metals the two junctions are at different temperatures, an electric current will flow in the circuit. In the case of an iron and a copper wire, for example, current will flow from copper to iron at the hot junction, or from iron to copper at the cold junction. Two factors combine to cause the current. An electromotive force exists between the two metals, the magnitude of which, depends upon the temperature and upon the metals; this is called the Peltier e.m.f. If a single wire of homogeneous material is heated at one end, an electromotive force is developed between the ends of the wire, the magnitude of which depends upon the metal and upon the difference in temperature; this is known as the Thomson e.m.f: The total e.m.f. acting in the circuit is the sum of the Peltier e.m.f. at the two junctions and the Thomson e.m.f. in each wire, consideration being given, of course, to the algebraic signs of the four e.m.f.'s. The total electromotive force thus depends upon the difference in temperature of the two

Jan 9, 1919

By Charles T. Holland

In connection with the problems of bumps in coal mines, much has been written concerning the manner in which roof action and methods of mining enter into the pressure effects observed but little has been written upon the relationship between the physical properties of coal and associated rocks and the cause of bumps. The question of the strength of bituminous coal, of its elasticity, and the energy it can absorb and store has been neglected to a considerable extent in connection with this problem. It is generally agreed that one of the necessary conditions for bumps is a strong coal.' Therefore, since the strength of coal is an important factor, a study of this property should be made. several investigators have conducted laboratory experiments upon the strength of coal, using small cubical or rectangular test pieces. An attempt will not be made to go into all of these investigations, but they are briefly summarized in Table I. Experiments of the U. S. Bureau of Mines and of Lawall and Holland (pp. 27 and 34 of ref. 9), however, indicate that regardless of whether the coal is a soft and weak semihituminous (Pocahontas No 3) or a hard and strong bituminous (Stockton) coal, the maximum ultimate unit stress developed in laboratory tests is higher in small cubes than in larger cubes of the Same coal.

Jan 1, 1942

By Charles T. Holland

In connection with the problems of bumps in coal mines, much has been written concerning the manner in which roof action and methods of mining enter into the pressure effects observed but little has been written upon the relationship between the physical properties of coal and associated rocks and the cause of bumps. The question of the strength of bituminous coal, of its elasticity, and the energy it can absorb and store has been neglected to a considerable extent in connection with this problem. It is generally agreed that one of the necessary conditions for bumps is a strong coal.' Therefore, since the strength of coal is an important factor, a study of this property should be made. several investigators have conducted laboratory experiments upon the strength of coal, using small cubical or rectangular test pieces. An attempt will not be made to go into all of these investigations, but they are briefly summarized in Table I. Experiments of the U. S. Bureau of Mines and of Lawall and Holland (pp. 27 and 34 of ref. 9), however, indicate that regardless of whether the coal is a soft and weak semihituminous (Pocahontas No 3) or a hard and strong bituminous (Stockton) coal, the maximum ultimate unit stress developed in laboratory tests is higher in small cubes than in larger cubes of the Same coal.

Jan 1, 1942