By A. W. Fahrenwald

Cell depth has been for many years a controversial question in a flotation-machine performance. In the impeller type of machine, we are really talking about impeller submergence—i.e., the depth in the pulp at which the impeller is required to produce aeration. The Flotation Machine a Compressor A flotation machine can be considered as an air compressor or blower in which the aeration mechanism takes in air under atmospheric pressure† (14.7 Ib. per sq. in.) and blows it into the pulp (the pulp being the receiver) against a head of 14.7 plus cell depth in feet times 0.4333 lb. per sq. inch. In commercial machines the impeller is submerged in the pulp to depths ranging from about 2 ft. in the smaller machines to as much as 5 ft. in some of the larger ones. In the 2-ft. cell, the hydrostatic head on the impeller is (2 X 1.25 =) 2.50 ft. (assuming a pulp density of 1.25), equal to (2.50 X 0.4333 =) 1.078 Ib. per sq. in. For the 5-ft. cell, the hydrostatic head against which the impeller must make air is (5 X 1.25 X 0.4333 =) 2.708 Ib. per sq. inch. In the small 2-ft. machine, the volume reduction is (1.078 ÷ 0.147 + 0.01078 =) 6.85 per cent and in the large, 5-ft. machine, the volume reduction is (2.708 0.147 + 0.02708 =) 15.5 per cent. It is obvious that for unit volume of free air intake the larger machine receives a lesser (8.65 per cent less) volume of aeration* than the smaller machine. The bubbles in escaping from the pulp expand and are greater in volume at the surface than at the moment of their formation in the pulp; 7.33 and 18.4 per cent larger, respectively, in the small and large machines. Just how this situation affects flotation is not known. It is interesting to note, however, that the bubbles are smaller in the zone of the coarsest particles and largest in the upper zones of the her, more easily suspended mineral particles. It would seem that the relationship might be reversed advantageously. The deep cell is at a greater disadvantage in this respect than the shallow cell. Nothing, however, presumably can be done about this situation. The shallow cell is a partial corrective. Not only does the compression ratio of aeration increase with impeller submergence but the hydrostatic head against which the impeller must operate also increases. The Flotation Machine as a Pump Since, in impeller machines that rely upon their own operation to produce aeration, pulp Passes through the im-

Jan 1, 1947

By T. H. Alden, H. W. Schadler

The strain rate dependence of the flow stress of the eutectoid Zn-Al alloy has been determined as a function of mechanical processing, microstructure, and temperature. The best superplastic properties result from the ultrafine, equiaxed structure produced by solution treatment and isothermal transformation at 0°C. Lamellar structures produced by isothermal transformation and coarse equiaxed structures produced by annealing also exhibit strain rate sensitivity in excess of 0.5, but at higher stresses and lower strain rates than the finest structure. Solution treatment and isothermal transformation eliminate the effect of prior processing history. Small composition variations in the binary alloy do not influence the mechanical properties. Below the eutectoid transformation temperature (.275C) increasing temperature lowers the flow stress at all strain rates. The data do not favor any of the present proposals for the mechanism of superplastic flow. ALLOYS of zinc and aluminum, near the eutectoid composition, have been investigated for: 1) the flow stress-strain rate and elongation behavior,1, 2) the transformation kinetics,3 and 3) structure,3"5 but the structure sensitivity of the mechanical properties is poorly understood. Using a near eutectoid alloy water-quenched from 380°C, Backofen et aL2 estab- high and increases with increasing strain rate. They found a correlation between strain rate sensitivity and tensile elongation as expected from the increased resistance to necking that a high strain rate sensitivity provides.296 The large elongation at high strain rates is attractive for metal forming. Since most other superplastic alloys7-l3 do not show high strain rate sensitivity at such a high strain rate (for the exception see Ref. 12) there is the possibility of a unique deformation mechanism for this alloy. The sensitivity of the mechanical properties of the eutectoid alloy to thermal history1 suggests a structure sensitivity that has not been demonstrated. Gar-wood and Hopkins3 identified a lamellar product for material transformed between 200" and 260°C. The size of the lamellae decreased with decreasing temperature. They also demonstrated that an unresolved transformation product formed below 200°C. A granular two-phase material was resolved for specimens quenched to below 150°C by Mitbauer and sauerwald4 who observed coarsening of the structure after annealing. The role of grain boundaries in superplastic deformation is suggested by the strong effect of grain refinement in encouraging this phenomenon at high strain rateS7-11, 13 and is emphasized in several proposals about rnechanism7, 8, 12 and in a theory14 of high-temperature deformation. Alden8 showed metallographic evidence that grain boundary sliding is occurring extensively at strain rates where m is large but less at high strain rates where normal plasticity is observed. Holt and Backofen10 have shown that sliding also oc-

Jan 1, 1969

By W. A. Backofen, D. Lee, F. S. Jabara

THE empirical character of plasticity analysis insures a continuing need for measurements of the yield surfaces of anisotropic materials. Recently, Wheeler and Ireland (W-I) proposed that an octahedral yield locus could be constructed on the basis of six Knoop hardness indentations. Such simplicity would have obvious appeal, if it led to consistently dependable results. In other recent work, a much more straightforward (and more tedious) method of measurement was used to establish all quadrants of the plane-stress yield loci for two substantially anisotropic titanium alloys.2,3 The same materials have since been reex-amined by the W-I method with results being reported here. A full description of the stress state under a Knoop indentor would be complex. In principle, however, this can be avoided in relating the hardness number to a plane-stress yield locus, by the expedient of superimposing the appropriate hydrostatic component on that state of stress. Six possible orientations of in-dentor on orthogonal (symmetry) planes, along (principal) coordinate directions, are illustrated in Fig. 1(0). Pictured in Fig. l(b) are normal-stress components nominally associated with indentation n: o2(H), directly proportional to the Khn in this case, together with By overlaying a hydrostatic tension, ah, that in general is equal to the stress state around the indentation is reduced to one of plane stress in the x-y plane for which the stress ratio is a The key step in the W-I yield-locus construction is to represent the Khn for any indentor orientation as a vector quantity on the octahedral plane. In the plotting, the vector is given as deviatoric stress components along the principal axes in the ratio , where represents the direction of the minor (width) diagonal and 1 that of the major (length) diagonal. There is no attempt by W-I to justify the 7/1, although it might be supposed that the value originates in the usual ratio of major to minor diagonals in a Knoop indentation of about 7/1. If that were its origin, the link to the deviatoric stress ratio would presumably be made by first taking 7/1 and then turning to the Levy-Mises equation for isotropic material: Interpreted in this way, the W-1 approach seems arbitrary and even contradictory. Yet it would still be favored by two circumstances: the deformation under a Knoop indentor approaches plane strain: when dcw/del =a; and the shape of the locus where plane strain is represented is not overly sensitive either to the exact value of dc,/dcl or to the degree of anisotropy, within a rather wide range of both variables. The second point is illustrated below, after a few additional comments on applying hardness

Jan 1, 1968

By Walter Crafts, C. M. Offenhauer

IN a previous study' of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is a more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about r1to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, 1 per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to 1-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudomartensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously' that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By P. A. Beck

ACCORDING to a recent hypothesis of Sully,' xY. binary CT phases are characterized by 1.7 bonding 3d electrons per atom, which completely fill the first Brillouin zone. This hypothesis appears to imply that there are no empty 3d orbitals in the u phase, and that, correspondingly, this phase must be dia-magnetic, or at most weakly paramagnetic. On the other hand, Bowen and Hoar' reported that a u phase extracted electrolytically from an alloy steel became ferromagnetic when cooled to about —113°C. In view of the fundamental interest of the problem from the point of view of the electron structure of the u phase, it seemed worthwhile to study the magnetic properties of massive u phase specimens of various known compositions. Sigma specimens of the following compositions were tested: 1—40 atomic pct Fe, 40 atomic pct Cr, and 20 atomic pct Mo 2—35 atomic pct Fe, 35 atomic pct Cr, and 30 atomic pct Mo 3—48.7 atomic pct Fe, 50.2 atomic pct Cr, and 1.1 atomic pct W 4—40.7 atomic pct Co and 59.3 atomic pct Cr All specimens were found to be strongly paramagnetic at room temperature, particularly alloy No. 1. At liquid nitrogen temperature, alloy No. 1 be- came ferromagnetic; the other u alloys remained paramagnetic. Even though apparently not all u alloys become ferromagnetic at liquid nitrogen temperature, in view of their strong paramagnetism it is probable that the electron structure proposed by Sully is not correct. Similar qualitative studies were made with the p, P, and 8 phases." A p phase specimen of 57.2 atomic pct Co and 42.8 atomic pct Mo; a P specimen of 19.9 atomic pct Cr, 37.8 atomic pct Ni, and 42.3 atomic pct Mo; and a 8 specimen of 50.4 atomic pct Ni and 49.6 atomic pct Mo were tested at room temperature, and all were found to be paramagnetic, although considerably weaker than the u phase specimens described above. A test at liquid nitrogen temperature gave similar results for all specimens; none became ferromagnetic. Thanks are due to D. K. Das for preparing several of the alloys and to Pol Duwez of California Institute of Technology for kindly loaning four specimens of cr alloys. References 1 A. H. Sully: The Sigma Phase in Binary Alloys of the Transition Elements. Journal Inst. Metals (1951) 80, p. 173. - K. W. J. Bowen and T. P. Hoar: Low Temperature Ferromagnetism of Sigma Phase in an Alloy Steel. Research (1950) 3, p. 484. 3 S. Rideout, W. D. Manly, E. L. Kamen, B. S. Lement, and P. A. Beck: Intermediate Phases in Ternary Alloy Systems of Transition Elements. Trans. AIME (1951) 191, p. 872; Journal of Metals (October 1951).

Jan 1, 1953

By R. P. Smith

The carbon content of a number of alloys ranging (before carburitation) from purified iron to purified cobalt was determined for fixed activities of carbon by equilibration with each of six CO-CO2 atmosphere at 1000°C. At fixed carbon activity, the carbon content decreases continuously with increasing cobalt content. For concentrations of 0 to 50 at. pct Co the results can be expressed by a linear interaction equation of the type In y2 = 7.76n2/(n1+n3)+ 2.30 n3/(n1+n3) where y2 is the activity coefficient of carbon (standard state such that y2— 1 as n2 — 0 in the Fe-C binary) and n1, n2, and n3 are the number of atoms of iron, carbon, and cobalt per unit weight of alloy. The results are also given in terms of the a functions. In the same concentration range, the results are in accord with the regular solution theory of Alcock and Richardson. THE carbon content of Fe-Si, Fe-Mn, and Fe-Ni alloys at fixed activities of carbon has been reported previously.'-, The present work extends R. P. SMITH, Member AIME, is Research Chemist, E. C. Bain Laboratory for Fundamental Research, United States Steel Corp., Research Center, Monroeville, Pa. these measurements to a series of Fe-Co alloys. These alloys, like the Fe-Ni alloys, are fcc ("aus-tenitic") over the entire range of composition at 1000°C. EXPERIMENTAL PROCEDURE The alloys were made from electrolytic cobalt and Plast-Iron in a small vacuum-melting furnace. A small amount of graphite was added to each melt to keep the oxygen content low. The ingots were analyzed for iron and carbon: the amount of cobalt was obtained by difference. Analysis of the top and bottom of the ingots indicated that they were uniform in alloy content. Except for the pure cobalt the ingots were hot-rolled to approximately 0.15 cm thickness, cleaned by sandblasting, then cold-rolled to about 0.045 cm. We were not successful in cold rolling the pure cobalt; therefore it was hot-rolled to the final thickness. The last traces of surface oxide were removed by acid pickel, then the samples were treated in a hydrogen-2 pct water vapor mixture at 1100°C to remove carbon and most of the oxygen. The carburizing procedure was similar to that previously described.1,2,4 The alloys in the form of strips about 1.7 cm wide, 7.5 cm long, and 0.04 cm thick, together with a similar specimen of purified iron, were equilibrated with each of six CO-CO2 mixtures of fixed composition, then quenched in the

Jan 1, 1965

By A. W. Fahrenwald

CELL depth has been for many years a controversial question in a flotation-machine performance. In the impeller type of machine, we are really talking about impeller submergence-i.e., the depth in the pulp at which the impeller is required to produce aeration. THE FLOTATION MACHINE A COMPRESSOR A flotation machine can be considered as an air compressor or blower in which the aeration mechanism takes in air under atmospheric pressure[t] (14.7 lb. per sq. in.) and blows it into the pulp (the pulp being the receiver) against a head of 14.7 plus cell depth in feet times 0.4333 lb. per sq. inch. In commercial machines the impeller is submerged in the pulp to depths ranging from about 2 ft. in the smaller machines to as much as 5 ft. in some of the larger ones. In the 2-ft. cell, the hydrostatic head on the impeller is (2 X 1.25 =) 2.50 ft. (assuming a pulp density of 1.25), equal to (2.50 X 0.4333 =) 1.078 lb. per sq. in. For the 5-ft. cell, the hydrostatic head against which the impeller must make air is (5 X 1.25 X 0.4333 =) 2.708 lb. per sq. inch. In the small 2-ft. machine, the volume reduction is (1.078 [-] 0.147 + 0.01078 =) 6.85 per cent and in the large, 5-ft. machine, the volume reduction is (2.708 [=] 0.147 + 0.02708 =) 15.5 per cent. It is obvious that for unit volume of free air intake the larger machine receives a lesser (8.65 per cent less) volume of aeration* than the smaller machine. The bubbles in escaping from the pulp expand and are greater in volume at the surface than at the moment of their formation in the pulp; 7.33 and 18.4 per cent larger, respectively, in the small and large machines. Just how this situation affects flotation is not known. It is interesting to note, however, that the bubbles are smaller in the zone of the coarsest particles and largest in the upper zones of the finer, more easily suspended mineral particles. It would seem that the relationship might be reversed advantageously. The deep cell is at a greater disadvantage in this respect than the shallow cell. Nothing, however, presumably can be done about this situation. The shallow cell is a partial corrective. Not only does the compression ratio of aeration increase with impeller submergence but the hydrostatic head against which the impeller must operate also increases. THE FLOTATION MACHINE AS A PUMP Since, in impeller machines that rely upon their own operation to produce aeration, pulp passes through the im-

Jan 1, 1946

By C. C. Hatch, C. R. Larsen, A. L. Mular

INTRODUCTION As part of a general project to simulate a concentrator, the Brenda Mines Limited secondary crushing plant, located near Peachland, B. C., was sampled during the summer/winter of 1975 and during the summer of 1978 to develop a digital crushing plant simulator specific to the Brenda operation. The purpose of this simulator was to study the influence of manipulable process variables on important responses, to permit study of alternative circuit configurations if desired and to perform off-line optimization. This chapter describes the methodology employed to develop the simulator (1,2) along with typical applications thereof. SECONDARY CRUSHING PLANT FLOWSHEET Figure 1 is a schematic diagram of the Brenda Mines Ltd. secondary crushing plant circuit. The 41,000 tonne coarse ore stockpile(a) is -17.8 cm oversize (3B belt) from two 2.4 m x 6.1 m double deck vibrating screens (not shown). The screens are fed by 2 conveyor belts operated in series with two 198 cm apron feeders that handle discharge from a 152 cm x 226 cm primary gyratory crusher(520 KW). The primary crusher (not shown) treats up to 2725 tonne/hr of run of mine ore. Minus 1.9 cm undersize from the primary screens (#19 belt), referred to as the primary fines, joins secondary screen undersize (#18 belt) for conveyance to fine ore bins (not shown). Feed from the coarse ore stockpile is transferred by means of vibrating feeders and two 120 cm conveyors (#6 and #7) to transfer belts #8 and #9 (Figure 1). The belts feed two secondary 2.1 m standard heavy duty cone crushers (bl and b2). Each crusher is equipped with a modified coarse mantle liner and a standard coarse bowl liner. Mantle throw is 9.2 cm; nominal close side set is 3.2 cm. Crusher .countershafts (443 rpm) are driven by single 260 KW synchronous motors (710 rpm). Discharge from the secondary cone crushers joins discharge from four 2.1 m tertiary heavy duty shorthead cone crushers (fl, f2, f3 and f4). With the exception of the cavity (modified medium mantle liner and standard coarse bowl liner; close side set is nominal .84 cm) and motor (224 KW), these machines are similar to the secondary crushers. The combined discharge is transferred from a 183 cm conveyor to #14 belt which empties into a 1452 tonne secondary screen surge bin (c). Vibrating feeders beneath the bins feed five 2.4 m x 6.1 m double deck vibrating screens (dl, d2, d3, d4 and d5) sloped at 200 from the horizontal. The upper decks are punched plates with 2.7 cm x 7.6 cm slots. Lower decks are woven wire (1.27 cm diameter) sections with

Jan 1, 1982

The Carol concentrator of the Iron Ore Company of Canada was completed in 1962 and through expansions .has become one of the largest iron ore beneficiation plants in the world with a new feed capacity of 147,000 It (149,350 mt) per day. The Carol ore contains specular hematite and magnetite having a bulk density of 166 lb/cu ft (2660 kg/m3) It is crushed to 7 in. (178 mm) for feeding to autogenous mills for subsequent concentration by Humphrey’s s spirals. Mine ore is loaded into 150 It (152 mt) trucks by 10 cu yd (7.65 m3) shovels and then, at a transfer station, is loaded into side-dump rail cars of 100 It (101.6 mt) capacity. Each train is composed of twenty cars and operates completely automatically as it hauls the ore to the primary crushing station, dumps its loads, and returns to the loading station, a 11.5 mile (18.5 km) round trip. The primary crushing station is composed of two 60 in. by 89 in. gyratories installed in 1962 and 1972. Neither crusher has a grizzly ahead of it. Rail cars are dumped into 300 It (305 mt) pockets which contain splitters for spider protection. What few oversize boulders which do not go through the crushers are drilled and blasted. Liners in the dump pocket and the crushed ore pokcet under the crusher are manganese steel. Both crushers are direct driven by 700 hp (5 15 kw) motors, and the hardness of the ore causes them to pull almost their full power. Crushed ore drops into a 160 It (163 mt) pocket equipped with radioactive level control units for low-intermediate, and high level indications. The low level unit stops and starts the apron feeder, the intermediate unit controls the feeder speed, and a high-level reading stops the car dumping. Apron feeders are 72 in. (1. 82 m) wide and are variable speed from 12 to 52 fpm (3. 7 to 15. 8 mpm). They discharge to 60 in. (1.52 m) wide takeaway belts. Crushing capacity, nominal and maximum for each crusher, is 4, 000 ltph (4. 064 mtph) and 4,600 ltph (4,674 mtph). The crusher eccentric is removed by a conventional cart which travels on removable rails. Mainshaft removal and maintenance is done by 65 and 75/10 ton cranes. Mainshaft replacement requires eight hours, a usual time, but concave replacement requires only sixteen hours, a result of a fine maintenance organization. Mantle relining is done at grade next to a repair track. Zinc is used for backing both mantles and concaves. Both the electrical rooms and the dust collectors are located below grade,

Jan 1, 1978

The Ortiz Mountain property is located approximately 40 km (25 miles) southeast of Santa Fe and 13 km (8 miles) from the village of Cerrillos. The property embodies a Spanish mineral grant from which Gold Fields acquired about 2, 200 hectares (900 acres of surface and mineral rights. Following a period of exploration, metallurgical testing and development of a feasibility study in 1974, the decision was made, because of the higher gold price in the fall of 1978, to place the property into production. the gold is confined in a quartzite breccia; it is an unusual occurrence because the gold in this host rock is leachable at minus 19 mm (3/4 in. ). Total ore reserves are estimated at approximately 3.6 million mt (4 million st) averaging 1.89 g per mt (0.055 oz per st) based on a cut-off of 0.7 g (0.02 oz). The ore will be recovered by open pit mining at a stripping ratio of 1. 2:l. Production is scheduled for 13,600 mt (15,000 st) of ore per week or approximately 680,000 mt (750,000 st) per year. Primary crushing of pit-run material is by a 1,070 by 1,015 mm (42 in. by 40 in.) jaw crusher. Crushed ore is conveyed to stockpile and then to a 2.13 m (7 ft) standard crusher with the screened over- size crushed in a 1.5 m (5 ft) tertiary cone crusher. The screen undersize, the final product for leaching, is minus 19 mm (3/4 in. ). A 1, 360 kg (3,000 lb) sample is cut from the crushed ore stream, further crushed in a small jaw crusher and then sampled in two more stages by Vezin samplers to produce a final 13.6 kg (30 lb) sample for assaying. Pebble lime is then added to the ore on the belt as it is sent to the conveyor gantry spanning the leach pads. A tripper on this moving gantry stacks the leach ore without compaction. The entire crushing plant and conveying system is of open-air construction. Leach pads have a total length of 515 m by 60 m (1,700 ft by 200 ft) wide with usable dimensions of 490 m by 58 m (1,600 ft by 190 ft). The directional length slope is 3. 870 with 370 on the width. The pad is constructed of 175 mm (7 in. ) thick asphalt containing a rubberized asphalt membrane. It is divided by a 300 mm (1 ft) high curb into eight segments. Each segment is loaded with 13,600 mt (15,000 st) of ore, which is one week's production. Optimum working height of a pad is considered to be 3. 0 m (10 ft) with a maximum height of 4. 0 m (14 ft).

Jan 1, 1981

By Walter Crafts, C. M. Offenhauer

In a previous study of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is 2 more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about I to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, I per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to I-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudo-martensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously1 that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By Walter Crafts, C. M. Offenhauer

In a previous study of the carbide phase of chromium steels, it was shown that chromium carbide (Cr7C3) is 2 more stable carbide than cementite (Fe3C) at tempering temperatures above about 500°C. in quenched steels containing from about I to 7.5 per cent chromium. Below this temperature the carbide phase was found to consist of cementite in all of the steels examined. In the present investigation it was found that a similar change in the carbide phase takes place in molybdenum and in chromium-molybdenum steels at approximately the same tempering temperatures. The approximate ranges of occurrence of the alloy carbides Cr7C3, Cr4C, and Mo2C have been determined in steels containing up to 5 per cent chromium, I per cent molybdenum and 0.60 per cent carbon. The experimental steels were made in small high-frequency furnaces from Armco ingot iron, low-carbon ferrochromium and calcium molybdate and were poured into 2-in. ingots, which were forged to I-in. round bars. Sections of the bars were heated to the carbide-solution temperature and cooled rapidly to induce austenite transformation at relatively low temperatures. The steels were subject to some segregation, therefore comparatively high temperatures were necessary to dissolve all of the carbides. The microstructure of the quenched specimens was examined to verify the belief that the carbides had been dissolved, and also to determine the nature of the nonmartensitic structure of incompletely hardened steels. Ferrite and pseudo-martensite were present in some of the specimens, but all specimens were quenched at such a rate that pearlite was not formed, in order to ensure the formation of the carbides at temperatures lower than about 500°C. It had been found previously1 that in chromium steels the chromium carbide could be produced by transformation of austenite in the pearlite range above 500°C., and, in order to start the tempering treatment with the carbide present as cementite, the absence of pearlite was considered to be essential. The specimens were tempered for 64 hr. to permit the formation of the stable carbide. After tempering, the specimens were submitted to microscopic and X-ray examination. The carbides were separated either electrolytically in a 5 per cent HCl electrolyte or with an acidified copper-potassium chloride solution. The crystal structure of the carbide phases was determined by the Debye-Scherrer type of X-ray patterns. The X-ray patterns obtained from specimens near the boundaries between two types of carbides were generally weak and diffuse as compared with the other patterns. For this reason, and because the more soluble components may be masked, the boundaries between the phases could not be determined precisely. However, the X-ray analysis of electrolytically separated carbides has given consistently reproducible results

Jan 1, 1943

By Keith G. Wallace

Small scale open pit mining of the Lucky Mc property in the Gas Hills district of central Wyoming was started in the spring of 1954 and the first uranium ore went to Vitro's mill in Salt Lake City that July. Shortly after mining started it became apparent that accurate ore control for mining purposes would be an absolute requirement. A systematic drilling program was initiated in the spring of 1955, and has been continued up to the present time. Two main mining areas have been developed. Mine 1, at the site of the original ore discovery in the Gas Hills, covers a mineralized zone roughly 600 x 2800 ft. This orebody was outlined and developed by drill holes on 50-ft centers. Approximately 1300 holes were drilled in the area before preliminary mining plans were made and mineable reserves calculated. Reserve estimates were based almost entirely on chemical assays of drill hole samples.

Jan 10, 1958

By M. T. Melvin, N. P. Kripakov

The practical application of a post-processing modeling procedure to simulate progressive rock failure around the periphery of coal mine entries is presented. This numerical scheme utilizes a simple rock model that incorporates easily obtainable input parameters consistent with basic rock mechanics principles. These parameters include the cohesion, angle of internal friction, modulus of elasticity, and Poisson's ratio of the bedded deposits that comprise the imediate roof, coal seam, and immediate floor. The geometry of the entry, along with the in situ stresses existing at a mine site prior to mining, are also considered in the analysis. The potential of this procedure as a predictive tool in determining the extent of pillar rib fracturing and yielding of the immediate roof and floor is evaluated assuming a Mohr- Coulomb failure criterion. The procedure is designed to be user oriented and is adaptable to any finite element code with linear elastic capability, making it particularly attractive to users with limited budgets and computer size.

Jan 1, 1983

By Frank C. Appleyard

Southwest of the town of Saltville in western Virginia is Plasterco, a small village that has been a source of gypsum production since 1815. Boasting the deepest underground gypsum mine in the world, Plasterco has been the site of mining operations by United States Gypsum Co. for more than half a century. And although its own ore supply is dwindling, Plasterco's position as a source of gypsum and gypsum products has been ensured by the recent opening of the nearby Locust Cove mine, one of U.S. Gypsum's newest projects. In the early days, production of gypsum at Plasterco was very small, the primary use of the mineral limited to that of "land plaster"-ground gypsum spread on the land to sweeten the soil. Initial mining was confined to surface outcrops containing gypsum, but the construction of a local plaster-producing calcining plant in the late 1800's coupled with al- most total depletion of the surface rock spurred the start-up of underground operations.

Jan 3, 1965

By P. R. Bradley

This paper gives a brief history of the mining and milling operations in the Juneau gold belt, and a general description of the geology of the district, followed by a suggestive discussion of the general problem of sampling gold ores and a detailed description of the mining methods used in the Alaska Juneau mine. The paper indicates that variations in assaying ore similar to that from the gold belt are unavoidable on account of the erratic distribution of the gold. A caving system that accepts dilution was adopted for the Alaska Juneau mine; the ore is sorted and the final mill feed has nearly twice the assay value of the ore trammed. THE property of the Alaska Juneau Gold Mining Co., covering the Juneau gold belt for over a mile in length, consists of 136 claims and 24 mill sites; these are near Juneau, Alaska, in what is known as the Harris mining district.

Jan 3, 1924

By Louis A. Panek

Caving of previously undisturbed ground was conducted for a period of about 20 months at two locations about 600 m (2000 ft) apart in an Arizona porphyry copper deposit. When mining was suspended the width of the mined zone at both sites was on the order of one-half the depth and the thickness of ore extracted was only a fraction of the rock column. Thus the results have potential application to predicting the subsidence above a cavern-type excavation. Break cables were used to detect the upward progress of caving. Analytical aerotriangulation was used to determine the vertical and horizontal displacements of 400-plus surface targets covering a 1585 m (5200 ft) square area. The measurements are summarized and interpreted with a view to predicting the rate of rise of a caving brow, detecting the initial surface subsidence, and characterizing the extent, the location, and the varying degrees of expected damage to surface facilities.

Jan 1, 1984

By R. W. Smith, C. Schroeder, R. Haddenham

Amphoteric surfactants are heteropolar organic compounds which possess at least two functional (ionic) oppositely charged groups per molecule. The ones studied are manufactured by General Mills and possess one or more long hydrocarbon chains plus a carboxyl group (s) and an amino or imino group. Hallimond tube and M. C. Fuerstenau micro flotation cell flotation tests were performed on quartz and hematite as a function of pH using amphoteric, cationic, and anionic surfactants as collectors. For the most part, flotation could be correlated with an interaction of charged groups on the collectors with oppositely charged sites on the minerals plus association of hydrocarbon chains. The comparison of flotation in a Hallimond tube and an M.C. Fuerstenau cell shows that one should use care in using the latter if one excludes an additional frother from the system. Also, it is interesting to note that sometimes greater collector concentrations are required in the Fuerstenau cell for comparable flotation recoveries.

Jan 1, 1974

By George C. Toland

In 1950 the phosphate fertilizer market warranted the design and construction of a new fertilizer plant by Cominco at Kimberley, B.C. The initial rated capacity of the plant was 70,000 tons per year of high- grade ammonium phosphate. The plant was placed on-stream in 1953. One of the major problems in operating the fertilizer plant was the disposal of the gypsum tailings slurry which was a by-product of phosphoric acid manufacture. The original weight of dry tailings produced by the mill was 500 tons per day. This quantity increased over the years until a projected 2200 tpd was selected for the pond design described in this paper. The original gypsum tailing area was located south of the fertilizer plant and adjacent to the St. Mary's River. By 1965 the original disposal area had proven inadequate and Cominco's engineering staff had selected a 500 acre disposal site to the east of the plant.

Jan 1, 1971

By H. Rush Spedden

When Robert H. Richards wrote Ore Dressing, the famous four-volume work published in the first decade of this century, the ore dresser was still largely concerned, with the mechanical treatment of ores. Since then, however, economics have transformed him into a mineral processing engineer who must increasingly deal with closely integrated facilities designed to produce a commodity for manufacturing. Moreover, this change will grow marked as the complex low- grade ores of the future make it ever more necessary for him not only to use the best combination of pyrometallurgical, hydrometallurgical and physical separation processes, but also to integrate these processes at the mine site. Nor are economic pressures the only ones propelling the processing engineer into a new era. The ecology drive has thrown him into a new situation in which his economic base is radically altered, and it could well precipitate as drastic a revolution in his technology as that which took place when flotation was developed.

Jan 1, 1971