By Craig R. Barrett

The influence of the stress dependence of the dislocation density on the overall stress dependence of The steady-state creep rate is discussed. Experimental measurements of dislocation densities and creep rates jor an Fe-3.1 pct Si alloy tested over a wide range of stress are presented which indicate a close correlation between the two quantities. EXPRESSING the stress dependence of high-temperature steady-state creep rates has been the subject of numerous investigations over the past decade. From these investigations have emerged a few general equations which fit most of the available data reasonably well. Garofalo 1 has proposed that for a wide range of stress and temperature the creep rate, i, can be expressed by a relationship of the form: where A, ß, and n are temperature-dependent and is the applied stress. Eq. [I] gives a stress dependence of a at low stresses and exp(nßo) at high stresses, both consistent with experimental observation where n = 5. A number of other investigatorshave proposed a similar expression where: where m and w are in general functions of temperature. Theoretical justification for Eqs. 111 and [2J comes from two different approaches, theories based on dislocation glide3-5 and theories based on the balance between work-hardening and recovery.' Dislocation glide theories predict where p is the mobile dislocation density and V is the activation volume. In order for Eq. [3] to predict a on stress dependence at low stresses with n = 5, it is necessary for p to be a strong function of stress, about proportional to u3 or u4.436 Recovery models of creep start with the general expression:' where r is the recovery rate and h is the work-hardening rate, and then employ a detailed model to determine the stress dependencies of r and h. As example, weertman2 has described a model based on pile-up hardening which results in an expression similar to Eq. [2] with m = 2 and p = 2.5. A recent, seemingly more general approach suggested by McLean is to use Friedels dislocation network growth expression to calculate the stress dependence of r. This model predicts r = p 3,2 and, as h is taken to be a relatively weak function of stress, the stress dependence of i should be about proportional to p3, 2. Once again, it is required that p be a strong function of stress to yield i This recovery model is by no means complete as the stress dependence of network growth is calculated in the absence of an applied stress meaning that r should probably be a stronger function of stress than given by p3, 2 and also some recent work by Mitra and McLean8 suggests that the stress dependence of h may be as large as Because of the importance of the stress dependence of p in determining the overall stress dependence of the strain rate it seems reasonable to examine this relationship in some detail. Measurements made on dislocation densities present during high-temperature steady-state creep generally obey the following relationship a =o0 + aGVWp [5] where uo is usually called a friction stress, a is a numerical constant about equal to unity, G is the shear modulus, and b is the Burgers vector. Depending on the magnitude of uo, data obeying Eq. [5] can give rise to a range of stress dependencies of p. For example, if we assume that the expression where 6 is some constant, adequately represents the stress dependence of p over a range of o, then from Although Eq. [6] obviously breaks down when u 5uo for uo 6 can vary over a wide range of values. In particular, if u > a, > 0 then 6 will be greater than 2. As an example the data of Ishida and McLean are plotted in Fig. 1 showing excellent agreement with dynes per sq cm) and also showing good agreement with a p cc u3 dependence when plotted on a log-log basis. As oo increases 6 tends to increase and correspondingly the stress dependence of the predicted creep rate should also increase,* as-

Jan 1, 1968

By Evangelo Agelopas

Steelmaking operators are familiar with the costs involved when ingot molds must be scrapped prematurely because of the failure of a stripping or turning lug. Some mold sizes can be expected to produce one hundred or more ingots per mold before normal wear causes the mold to become unserviceable. Therefore, the failure of lugs at less than the average life for that mold size represents a sharp increase in terms of mold cost per ingot ton produced. To combat these wasteful and costly occurrences, it was determined that an efficient method of replacing lugs should be developed to extend the life of molds which are otherwise in good condition. The purpose of this paper is to describe a lug welding method which has proved effective and economical. This method is known as the Oxygen and Mapp Process.

Jan 1, 1972

By L. W. Casteel, E. A. Jones

MINING the lead deposits of Southeast east Missouri has reached a high stage of technical development dictated by the scattered occurrences of low-grade ore through favorable horizons in the Bonne Terre formation. The rock-breaking, handling, and related practices described here have evolved as the best way of mining these particular deposits. These methods are applied in the production of about 19,000 tons of lead ore per operating day from four mines in Southeast Missouri. Development drilling Drifts 10 ft wide and either 8 or 9 ft high are driven in this district on contract. Miners are guaranteed standard wages plus a bonus on the footage advanced, if earned. Labor, fuse, caps, wire, and dynamite used are charged against the contract. Normally the cycle of operations in drifting is performed by a two-man crew, a motor operator and a shovel operator who first load out the rock broken by the preceding shift. The drift crew then sets up two vertical column and mounts the drills. Cleveland HC-10's are used which have a steel lug integral with the cylinder for connection with the air feed. All drilling in drifts is wet. Air pressure is 85 to 100 lb at the face. From 28 to 32 holes are drilled per swing in a pyramid cut. Cut holes

Jan 1, 1947

By Narendrakumar A. Chevli

Exploratory work was conducted in the fabrication of integrated circuitry, specifically linear amplifier circuits, by three general methods: 1) monolithic diffused silicon; 2) a combination of metal thin-film and monolithic diffused silicon; and 3) a hybrid of metal films and diffused silicon on an alunina substrate. In these linear amplifier integrated circuits the followzng conditions were desired: very high-frequency response, high voltage gain, and good thermal tracking stability of electrical characteristics. The resulting circuit designs imposed problems of isolation between elements, layout and smallness of size of active elements, and close tolerances on electrzcal characteristics of the passive elements. Interconnection problems for specific designs resulted from the small dimensions involved and the topography of the hybrid fabrication techniques. The desired integrated-circuit characteristics were achieved with the technologies of categories 2 and 3 above. Solutions to the problems imposed by these characteristics lay in the ability to isolate czrcuit elements of small size while providing a layout designed to minimize element-to-element variations. Sufficient freedom in the formation of passive elements was achieved by uniting the metal film and the monolithic silicon technologies. The most satisfactory designs were based on the beam-lead interconnection and isolation technique. SINCE the advent of integrated circuits, major emphasis has been on fabricating digital integrated circuits. Linear circuits require high performance, high voltage, and tighter tolerance components which are not always compatible with the capability of process technology available for fabrication of these circuits into integrated form. Fortunately the growth of newer and improved processes and materials for fabricating integrated circuits has been an accelerated one. This has now made possible the translation of stringent performance requirements of the linear circuits into microminiature integrated circuits of the same performance. In the exploratory work of fabricating high-performance Linear Integrated Circuits—LIC, the following objectives were formulated: i) fabrication of high-frequency transistors such as the type 2N918 isolated on a single silicon substrate; ii) fabrication of medium-frequency transistors having a very high gain at low collector currents such as the types 2N930/2N2484 isolated on a single substrate ; iii) fabrication of tight-tolerance, high-valued resistors having low temperature coefficients of resistance and stable thermal tracking characteristics, these resistors to be fabricated on an active or passive substrate; iv) simultaneous fabrication of complementary transistors—pn and pnp-on the same silicon substrate; v) fabrication of newer active elements such as MOS, FET transistors along with the conventional active and passive elements on the same silicon substrate. State-of-the-art assessment f all the available processes, materials, and technology to meet above objectives indicated that economic fabrication of LIC cannot be achieved by a single technology for all types of linear circuits. Where design and performance of a given linear circuit can be modified and tolerated to the extent of a particular technology, then alone is it possible to fabricate a LIC using a single process technology such as all diffused, planar technology. In order to evaluate this economic breakpoint with design and performance compromise in fabricating LIC, it is essential that a thorough understanding be obtained of techniques, potentials, and limitations of all the various process technology and materials

Jan 1, 1967

By A. Hultgren

PAGE Outline of Progress of Knowledge and Theories about Gas Evolution in Steel Ingots, and Its Influence on Crystallization and Segregation 2 Object of Present Investigation 16 theoretical Discussion of Process of Solidification 17 Gas Given Off from Rimming Steel during Solidification 17 Equilibrium Diagram of the Iron-carbon-oxygen Alloys 19 Solidification of Pure Iron-carbon-oxygen Alloys 25 Solidification When Carbon Monoxide Is Given Off at Constant Pressure... 25 Solidification When Gas Evolution Is Suppressed 26 Schematic Application on Solidification of Rimming-steel Ingots 27 Influence of Manganese, Sulphur and Phosphorus 28 Experimental Work 30 Liquid Steel and the Mold Gas 30 Ingots Investigated and Methods Used 33 Ingot Structure 42 Structure of Rim Zone 42 Structure of Core 49 Structures Obtained under Special Conditions of Freezing 50 Distribution of Metalloids 55 Other Observations Made 60 General Discussion of Solidification Process 63 Condition of Liquid Steel before Casting 63 Rimming Period 70 Composition of Rim Zone 93 Freezing after Top Is Closed 96 Slag Inclusions and Ingot Scum 102 Reaction between Gas in Blowholes and Surrounding Solid Steel during Cooling 103 Summary 105 Appendix-Preparation and Etching of Ingot Sections 106 References 107 IN 1934, Jernkontoret (The Swedish Ironmasters' Association) appointed a committee for the study of the structure of rimming-steel ingots and the various phenomena associated with their solidification. The members of the committee, including those who have joined it later, have been: I. Bohm, B. D. Enlund, B. Kalling, M. Tigerschiöld, 1. Wohlfahrt and the authors. The present paper? is a somewhat

Jan 1, 1939

By William T. Folwell

The Lucky Friday mine east of Mullan, Idaho, is an outstanding example of a property in the Coeur dlAlene district where a small and insignificant-appearing silver-lead-zinc vein at the surface has changed at depth into a large vein of great importance. The Lucky Friday vein has little if any surface expression and above the 1200 level the ore shoots are small and discontinuous. Between the 1200 level and 2450 level, the lowest developed level, the main ore shoot has shown remarkable improvement on each succeeding lower level, and today the mine is one of the major lead-silver producers in the Coeur d'Alene district. History: The Lucky Friday property is on the north side of the South Fork of the Coeur d'Alene River in sections 25, 26 and 35, T. 48 N., R. 5 E., Hunter mining district, Shoshone County, Idaho. This is about one mile east of the town of Mullan, which serves the eastern portion of the Coeur d'Alene district. The southern part of the property is crossed by a branch line of the Northern Pacific Ry. and by U. S. Highway 10. This highway is the principal road crossing the panhandle of Idaho and connects the district with Spokane, Wash., on the west and Missoula, Mont., on the east. The main portal and surface plant of the Lucky Friday mine is at an elevation of 3365 ft, only a short distance above the valley floor and a few hundred feet from U. S. Highway 10. so the mine is readily accessible for year-round operation. The property is comprised of six claims, known as the Lucky Friday group, owned outright by the Lucky Friday Silver-Lead Mines Co. There are four patented claims, Good Friday, Lucky Friday, Northern Light, and Lucky Friday Fraction No. 2 (Mineral Survey No. 3028), and two unpatented claims, Hunter and Creek. In addition, Lucky Friday owns an undivided one-half interest in the Hunter Creek property. which adjoins the Lucky Friday group on the north: a 90 pct interest in the mineral rights in the Jutila Ranch (160A), which adjoins the Lucky Friday group on the east; and a 60 pct interest in the Lucky Friday Extension claim group, which adjoins the Lucky Friday group on the west. The company also has a long-term mining lease on the Hunter Ranch, which adjoins the Lucky Friday group on the west. The claims of the Lucky Friday group were located between 1899 and 1906. The Lucky Friday Mines Co. was organized in 1906 and did considerable exploration work by surface trenching and shallow underground workings, only to see the property sold by the Shoshone county sheriff to satisfy labor claims totaling $2000 in 1912. Another firm, Lucky Friday Mining Co., bought the claims in 1914 and spent 12 years driving what is now known as the tunnel level crosscut. This tunnel intersected a vein previously exposed in a higher tunnel, but it was only a few inches wide. The vein was followed a short distance westerly but was so unpromising that the work was discontinued in favor of extending the main crosscut tunnel several hundred feet north. No ore was found and all work was discontinued. The property was held in such low esteem by the firm that it let taxes amounting to less than $15 a year go delinquent for nine years. Then the property lay idle for two more years until in 1938 John Sekulic, a Mullan service station operator, took a lease, with a $15,000 purchase option, on the advice of an old miner who had worked in the mine. Sekulic re-opened the tunnel level crosscut and explored the vein with an easterly drift for about 200 ft. The vein was too narrow to be of commercial value but was believed interesting enough to warrant further exploration at depth. Lacking funds to explore the vein at depth, Sekulic tried to get the district's larger operating companies to take over his lease and option. They were not interested because of the lean tunnel level showing and the fact that the property lay between the White Ledge fault on the north and Osburn fault on the south, an area which geologists always considered unworthy of exploration. Sekulic then organized the present company and assigned his lease and option to it for stock. This was in 1939. Enough stock was sold locally to finance sinking of a shaft 100 ft from the tunnel level east drift. The vein at this additional depth still was not commercial but showed some improvement. Treasury stock was offered at 5 to 10C a share

Jan 1, 1959

By L. W. Jones, B. H. Bennetts

The removal and disposition of large quantities of slag from blast-furnaces is a question of great importance in the design of works, and various methods have been devised, from time to time, in order to take the best advantage of local conditions. With blast-furnaces treating copper-ores or lead-ores, it is necessary to use a fore-hearth, or matte-settler, in order to collect, if possible, every particle of valuable matte which, otherwise, would be carried away with the out-flowing slag. In all of these cases, the slag overflowing from the fore-hearth is caught in pots and then conveyed to the dump. If the slag is of no value and the necessary water-supply, grade and dumping-space be available, the disposal of the slag by granulation is by far the cheapest and best method. It involves a minimum of labor, both at the furnace and at the dump; and it permits a continuous outflow of slag from the furnace or settling-pot, thereby avoiding frequent tapping and plugging. When the conditions of water-supply, grade and dump-area will not permit slag-granulation, there are three other methods in common use. Large steel or cast-iron pots, or ladles, supported by trunnions on heavy cars which are moved by steam-, air-, or electric locomotives; some type of mechanical conveyor; and small pots or buggies moved by hand. The pots on the slag-cars are generally circular or oval in shape, and each one contains from 15 to 40 or more cu. ft. of molten material. The mechanism for tipping them is more or less elaborate; and, as a general rule, the slag is dumped alongside, and quite close to, the track. They are more or less costly to construct and to keep in repair, and, in order to use them to best advantage, it is necessary to have a good elevation of track above the dumping-ground ; furthermore, the rails must be of heavy weight, and well-supported on heavy ties. Other disadvantages of the slag-pots are—1, that the slag cannot be removed continuously

Jan 1, 1906

By Robert M. Grogan

Fluorspar is the commercial name for fluorite, which is the mineral having the composition CaF2, calcium fluoride. Its valuable properties are due to its content of fluorine, and it is the only important commercial source of that element. The name is derived from the Latin fluere, to flow, because the mineral melts easily and is a good flux. History The mineral has been known since Greek and Roman times, when it was used for drinking cups and ornamental slabs. Various peoples including the Chinese and the American Indians have carved ornaments from large crystals. Its usefulness as a flux was known to Agricola, who wrote about it in 1546.1 Mining began in England about 1775 15 and at various places in the United States during the period 1820 to 1840.28 Substantial production was achieved first in the period 1888 to 1900 in consequence of the development and widespread adoption of the basic open hearth method of making steel, in which fluorspar is used as a flux. After that, production and usage was stimulated by growth in the steel, aluminum, chemical, and ceramic industries and accelerated by World Wars I and II. The organic fluorides called "Freons" entered the picture in 1931, and the use of anhydrous HF as a catalyst in the manufacture of alkylate for high octane fuel blends began in 1942. The development of the froth flotation process in the late 1920's, a differential flotation scheme for separating fluorspar from galena, sphalerite, and other minerals in the 1930's, and the application of heavy-media concentrating methods to the treatment of low-grade ores in the 1940's were outstanding technological contributions that enabled increased production of fluorspar concentrates. Composition and Properties Fluorite in its purest form contains 51.1 pct calcium and 48.9 pct fluorine. Substitution of small percentages of cerium and yttrium for calcium have been noted.4 Mechanical inclusions of gases and fluids such as petroleum and water, and of other solid minerals such as pyrite, marcasite, and chalcopyrite are common. The fluorspar of commerce contains attached and admixed mineral impurities, chiefly calcite, quartz, barite, celestite, and various sulfides. It is interesting that the purest commercial form in which the mineral is sold, acid grade concentrate, contains a minimum of 97 pct CaF2, and as such is of comparable purity to many reagents used in chemical laboratories. Fluorite has a marked tendency to occur in large, well-formed crystals sometimes six to ten inches on a side. It crystallizes in the isometric system, frequently forming cubic and octahedral crystals or combinations thereof. The mineral also occurs in massive and in earthy forms, and in crusts or globular aggregates with radial fibrous texture. Crystalline fluorspar exhibits a great array of colors, from colorless and water clear to yellow, blue, purple, green, rose, red, bluish and purplish black, and brown. The colors are often arranged in alternating bands parallel to cube faces. They may be altered by exposure to X-rays, heat, ultraviolet light, and pressure, and are caused by a variety of factors including the presence of trace impurities and displaced ions in the lattice. Sometimes the changes induced by X-rays can be reversed by ultraviolet radiation. The mineral has a hardness of 4, and is the model of that hardness on the Mobs scale.

Jan 1, 1960

By R. C. Himes, K. Zanio, J. B. Wagner, J. W. Moody, J. F. Miller, W. Johnson

The recent research with which this paper deals has been concerned with the preparation of pure PbTe crystals suitable for control of radiative processes and othe.v electronic applications. The research has been directed toward the developrnent of methods for the preparation of puve, homogeneous, loul-ca,wier-density PbTe crystals suitable for use in the fabrication of optically pumped and electrically pumped diode lasers. Steps in the preparation of the crystals include 1) purification of the starting materials, 2) synthesis and purification of the PbTe, 3) growoth of PbTe crystals, and 4) adjustt~zertt of composition of the crystals This Paper describes the general preparation procedure employed and discusses some investigntiotzs of purification processes. THE as-received lead and tellurium are nominally 99.999 to 99.9999 pct pure. Assays furnished by the suppliers, obtained by emission spectrographic analysis, show only the presence of about 2 ppm Mg in the tellurium. Such analyses are not very informative, however, since they give no information on the concentrations of normally gaseous impurity elements such as oxygen. Both the lead and the tellurium in the as-received state usually contain appreciable concentrations of oxygen—primarily in the form of oxides on the surfaces of the material. To reduce the oxygen content, the lead is held in the molten state in hydrogen at -700°C for several hours. For this treatment, the lead is contained in a graphite boat which is rf-heated, and the hydrogen is passed through a liquid-nitrogen trap prior to use. Tellurium is subjected to multiple distillation in hydrogen to remove oxygen and other foreign impurities. If, in conducting the distillation, approximately the last 10 pct of the charge at each "stage" is left as the discard cut, purification of the tellurium proceeds as indicated in Fig. 1.l Tellurium used in this work has been distilled two or three times to reduce carrier concentration to about 10" per cu cm. The PbTe is prepared from the purified elements by reacting them in the molten state in sealed, evacuated, or hydrogen-filled silica ampoules. The charge is usually held above the melting point of PbTe (923°C) at 1000 C for 24 hr to ensure that it has been homogenized. Two methods have been employed for the growth of the required single crystals of PbTe: growth from the melt, which will be discussed first, and growth from the vapor phase. Large single crystals of p-type PbTe can be grown readily from the melt by the Bridgman method. For this method of crystal growth, the PbTe is synthesized in situ from proper proportions of the purified elements. Growth (dropping) rates in the range 1.3 to 6.5 mm per hr are employed. Material near the maximum melting composition (about 50.012 at. pct Te) is utilized to avoid composition change on freezing, and thus to obtain crystals of nearly uniform composition. Crystals prepared by use of procedures described up to this point were sufficiently pure and perfect that they could be used for the preparation of laser crystals in studies at Lincoln Laboratory.2-5 ADJUSTMENT OF COMPOSITION Good n-type crystals of PbTe cannot readily be grown from the melt. Further, growth from the melt of crystals of any compositions (n or p type) other than those near the maximum melting composition is difficult because of the large composition changes that must occur on freezing.'" However, melt-grown crystals can rapidly be brought to other desired compositions by isothermal equilibration through the vapor phase with a two-phase Pb-Te stock material, essentially as described by Brebrick and Allgaier.1 The work to be discussed has been concerned with the preparation of n-type crystals; thus, the two-phase stock which was employed contained excess lead, and all ensuing discussion is of the preparation and properties of n-type crystals. The equilibration was designed to the shift composition to the lead-rich limit of stability at the selected temperature. Initial treatment of the crystals at high temperature was employed to minimize the total time required for the equilibration. Final adjustments of the composition and state of the crystals were made by use of low-temperature heat treatment at temperatures in the range 200" to

Jan 1, 1968

By John A. Mathews

RESEARCH in the steel industry, as in other lines of manufacturing, has for its principal purpose the increasing of profits. That is what manufacturing companies are for, and all departments of the organization must be so coordinated as to lead to profitable operation. To divide a payroll into productive and non-productive labor is misleading. Productive labor, in fact, is necessary labor, and non- productive labor is the labor we can get along without. One might as well say that the steering wheel is not a part of an automobile as to say that the directing minds of an industry are non-productive. Legitimate manufacturing profits in a steel company or any other company are the reward that the public pays for service rendered or risk taken. The desire for profits is the impelling motive that leads investors .to take risks and build up industries that give employment to others. Every department of a company, be it executive, manufacturing, financial, sales, or research, must contribute to the one end which brings success-profits.

Jan 1, 1921

Official Program

Jan 8, 1950

By P. Wynblatt, J. E. Dorn

The effect of strain rate, temperature, and interstitial impurity concentration on the flow stress was investigated in a poly crystalline Fe-2 pct Mn alloy. The temperature dependence of the flow stress was found to be independent of the interstitial impurity concentration, removal of interstitials merely decreasing the atherma1 stress level. Below 160%, the large temperature dependence of the flow stress was interpreted in terms of the Dorn-Rajnak theory of the Peierls mechanism of plastic deformation. Above 160"K, some other thermally activated intrinsic meckanisln seems to be operating. The strong temperature dependence of the flow stress of bcc iron at low temperatures has been studied by numerous investigators and interpreted in terms of several different thermally activated dislocation mechanisms. The following mechanisms have been proposed: a) interaction of dislocations with interstitial impurity atoms1 or with solute atoms in general; b) interaction of dislocations with clusters of impurity atoms;3 c) resistance to the motion of dislocations due to jogs on screw dislocations;* d) resistance to the motion of dislocations due to the Snoeck effect;' and e) interaction of dislocations with the intrinsic resistance of the bcc lattice or Peierls "hills". In previous work: it was found that the plastic behavior of polycrystalline iron containing 2 wt pct Mn (and 100 ppm C + N) is in good agreement with predictions based on the Peierls mechanismlo from 77" to 160°K whereas from 160" to about 370°K another as yet unidentified thermally activated mechanism is operative. The purpose of the present investigation was to determine the effect of interstitial impurities on the temperature dependence of the flow stress, by purifying the previously investigated alloy with respect to interstitial impurities. The investigation revealed that removal of the interstitial impurities to a level that eliminated Cottrell locking and the Portevin-LeChatelier effect (i.e., serrations in the stress-strain curve due to dynamic strain aging) affects neither the strong temperature dependence of the flow stress at low temperatures nor the general characteristics of the higher-temperature behavior. Such purification, however, lowered the athermal yield stress. I) EXPERIMENTAL PROCEDURE AND RESULTS The material used in this investigation consisted of an Fe-2 wt pct Mn alloy having the following additional elements present: 0.004 pct C, 0.006 pct N, 0.05 pct 0, 0.004 pct S, 0.003 pct P, and 0.001 pct Si. This was the same material as that studied in the previous investigation and will henceforth be referred to as the "impure material". The as received -jr by 2 in. hot-rolled bars were cold-rolled to 0.08-in. thickness, recrys-tallized under argon for 30 min at 80O0C, and further cold-rolled to 0.053-in. thickness. Flat tensile specimens 3 in. wide having a 1.625-in.-long gage section were machined from the sheet and then purified. The first stage of purification consisted of holding the specimens at 850°C for 24 hr in a stream of hydrogen saturated with water vapor at room temperature. Material prepared in this fashion will subsequently be referred to as "wet hydrogen purified material". It has been estimated that this type of treatment reduces the carbon content of iron to less than 5 ppm.' The second stage of purification consisted of holding the specimens in a closed system through which hydrogen was circulated past the heated specimens as well as a zirconium hydride getter. The specimens were held at 850°C and the getter at 800°C. The process was continued for 212 hr. The starting material for this process was wet hydrogen purified material. Material prepared in this manner will be referred to as "ZrHz purified material". The technique used was substantially the same as that described by Stein et al.' who have shown that the carbon level at the end of the process is reduced to about 5 parts per billion. The mean grain size of the three materials was found to be -60 C( for the impure material and -160p for the wet hydrogen and ZrHz purified materials. All tensile testing was carried out on an Instron Testing Machine either in controlled-temperature baths or at fixed-point baths such as boiling liquid nitrogen, and so forth. When fixed points were used the temperature was kept constant to better than *1°C whereas in all other tests the temperature variation was less than *2°C. Test of Purity. It was not possible to determine the purity achieved at each stage of the purification because the resulting level of interstitial impurities was near or below the limit of sensitivity of standard analytical techniques. It was possible, however, to obtain a qualitative measure of the extent of purification from the appearance of the stress-strain curves for the three materials. Fig. 1 shows the stress-strain curves for the three different materials tested at 300°K. It can be seen that the effect of wet hydrogen

Jan 1, 1967

By M. R. Lorenz

Efficient visible light emission from p-n junctions in semiconductors is currently achieved in the four materials, Sic, GaP, ]Ga1-xAs and GaAs1-x,. Recent advances in materials preparation and p-n junction formation are briefly reviewed. The radiative recombination processes in the different materials depend largely on the band structure and the impurity states of each material. The spectral distribution of the emission ranges from the blue in Sic, to green in Gap, yellow in Sic and red in Gap, Ga1-x AlxAs and GaAs1-x Px. The origin of the various processes are discussed. The conversion of the electrical power into optical power and the measurement of the conversion efficiency are reviewed. The currently maximum quantum efficiencies at 300°K are: 3 pct in GaP(red), 1 pct in SiC(yellow), 0.1 pct in GaP(green), 0.2 pct in Ga1-x AlxAs at 66001, and 0.1 pct in GaAs1-x Px at 6800. The brightness and the interplay of the quantum efficiency and the luminous efficiency are given detailed consideration. VISIBLE light generated by the application of a direct current to a semiconductor crystal was first observed by Lossev1 in 1923. Light emission came from naturally occurring junctions in Sic crystals but little was known then with regard to the mechanism of charge transport and light emission. Some nearly 30 years later and with a vastly increased understanding of semiconductors the phenomenon of electroluminescence was studied in more detail, for example in p-n junctions of germanium.2 In these early studies, the efficiency of converting the electron current into a photon current was very low and therefore aroused little interest toward practical application. More recently it became apparent that in certain materials, for instance GaAs, and under certain conditions, the conversion efficiency was not low at all.3 The subsequent discovery of the p-n junction laser4-6 provided the impetus for increased studies of electroluminescence. Light emitted from GaAs occurs in the infrared region of the electromagnetic spectrum and is not visible to the eye. At nearly the same time the use of GaAs1-xPx led to laser action at low temperatures which was visible to the eye.7 Later a red light emitting diode, made from Gap, was reportedS which emitted incoherent radiation at 300°K with an external quantum efficiency of about 1.5 pct. The fact that such efficient devices were obtainable led to a more concentrated effort in the search for highly efficient room-temperature semiconductor light sources. It is some of this later work on p-n junction luminescence with which we will be concerned here. Since our aim is centered on visible light, with hv =1.8 ev ( ?=7000?), only the wider band gap semiconductors are of interest, i.e., Eg 1 1.8 ev. Although many compounds meet this criterion, only a limited number of those are also good semiconductors, i.e. contain low resistance n and p regions. Some of the more promising candidates are listed in Table I. We will only be concerned with light generation from a p-n junction. This limitation excludes essentially the group II-VI binary compounds, although we will briefly review the case of ZnTe and the solid solution ZnTe1-xSex. As we will show they may contain a p-n junction but only of a special kind. Most of the discussion will deal with the four materials, Sic, Gap, Gal-xAlxAs, and GaAs1-xPx. These appear to be at the present time the best visible light emitting semiconductors. In the following sections we will briefly consider: 1) the electrical properties of p-n junctions; 2) some recent advances in materials preparation; 3) the formation of p-n junctions; and then in somewhat greater detail we will consider: 4) the various radiative recombination processes; 5) the measurement and observation of the external quantum efficiency; 6) the luminous efficiency; 7) the brightness of light emitting diodes (LED'S). THE P-N JUNCTION The p-n junction in a semiconductor crystal is the interface between two differently doped regions. More specifically the p region is doped predominantly with acceptor impurities and the n region contains predominantly donor impurities. The energy band structure of a degenerate p-n junction at thermal equilibrium is shown in Fig. l(a). The excess electrons on the n side of the junction are confined to this region by the barrier potential Eg. Similarly the excess holes on the p-side of the junction are confined to the p-region by a similar potential barrier. If we now apply a dc voltage V such that the p region is made positive and the n region negative, the barrier potential EB is reduced by the applied voltage, V and the junction is said to be forward biased. With the barrier potential lowered, electrons and holes can drift toward the p region and n region, respectively, see Fig. l(b). The current voltage characteristics of p-n junctions in most wide band gap materials can be described by the relation: J = Joexp(eV/BkT) [1] where the functional form of Jo is determined by the recombination mechanism. Jo is generally a complicated parameter which depends on a number of different factors including temperature, junction width, bias voltage, and carrier lifetimes. The parameter B also depends on the recombination mechanism but

Jan 1, 1970

By F. B. Plummer

PROGRESS during 1940 in oil-production technology has been confined largely to a steady advancement in practices inaugurated in previous years, rather than the introduction of any new startling process or technique. The usual changes, improvements and additions in production equipment have been introduced. An increased attention to, and interest in, research has been noteworthy, resulting in improved efficiency in operation of oil wells. control, utilization of reservoir energies and reduction of production costs.

Jan 1, 1941

By Jonas Svensson

A new method is described for the production of cold-bonded pellets using a hydraulic binder, such as portland cement. Large-scale pilot-plant tests have proved that self-fluxing pellets of high reducibility and good handling strength can be made by the method. Blast-furnace trials have shown that the pellets are an acceptable burden material, comparable with self-fluxing sinter or heat-hardened pellets. Economic factors of commercial-scale production are discussed. The Grangcold Pellet Process—for which patents have been applied or already granted in a number of coun-tries—uses a hydraulic adhesive such as portland cement, slag cements, pozzolanic cements, etc., for the production of cold-bonded pellets. The idea of using a hydraulic binder for the agglomeration of iron-ore fines is not new. Portland cement was proposed as an adhesive for cold-bonded iron-ore briquettes in patents granted more than 50 years ago.' In a report on the briquetting of iron-ore fines, published in Stahl und Eisen in 1959; it is stated that briquettes bonded with portland cement are used on a small scale at an ironwork in Germany. According to the report, the briquettes showed excellent strength in the blast furnace although their general use was made impossible because they required a long hardening time, during which they are sticky, soft, and difficult to store and handle. The Grangcold Pellet Process has overcome this particular disadvantage by mixing the balls with a suitable amount of the balling concentrate before storing them. The pellets are embedded in the concentrated during storing in such a way that they are isolated from each other and thus prevented from sticking together to form clusters. Thanks to the embedding concentrate, the pellets are subjected to a more or less uniform pressure from all sides which does not deform them. Thus, the mixture can be stored in a stockpile or in a bin until the pellets have hardened sufficiently. The concentrate is separated from the pellets by means of screening. The concentrate is returned to the balling operation and the pellets are either shipped to the blast furnace or stored for final hardening. The binder preferred for the Grangcold Pellett Process is portland-cement clinker, ground without the admixture of gypsum in order to avoid sulfur in the pellets as far as possible. Usually a 10% binder content is used. Two-thirds of the portland-cement clinker consist of lime and the rest is silica, alumina, and ferric oxide. Thus, self-fluxing or overbasic pellets are produced with this binder if the amount of silica in the concentrate used does not exceed 4%. The Grangcold Pellet Process was developed by the mineral Processing Laboratory of the Granges Co. Work started in 1963 with batch-scale tests. In 1966, a small pilot plant was put into operation in which 1800 tons of pellets were produced using 10% of rapid-hardening portland cement as a binder. Favorable results from a blast-furnace test with this batch led to the decision to erect a larger pilot plant which went into production in the summer of 1967. Since then, approximately 100,000 tons of cold-bonded pellets have been produced, mostly with 10% gypsum-free portland cement as a binder. Several full-scale blast-furnace trials have been performed with the pellets. The results of the trials indicate that the Grangcold pellets constitute a satisfactory blast-furnace feed. An industrial plant for the production of Grangcold pellets with a rated capacity of 1.5 million tpy is now under construction at the Granges Co.'s mine at Grangesberg. The plant will come into operation in the summer of 1970. Results from Laboratory Work Pellets made from iron-ore concentrate bonded with portland cement harden slowly and their handling is very critical until they have hardened enough to loose their stickiness. It is therefore especially important to study the progress of the hardening action and the factors influencing it. This is best achieved by investigating the relationship between the compressive strength of the cement-bonded pellets and the curing time under varied conditions. The general course of this relation-

Jan 1, 1971

By K. Torssell, U. Lindborg

The kinetics of precipitation deoxidation is considered from a theoretical point of view. The size distribution and the total content of deoxidation products are estimated statistically as a function of time, taking into account Stokes and gradient collisions between the particles and separation at the top surface of the bath. The assumption is made that two particles coalesce into one larger particle as a result of a collision. General expressions are derived and calculations are carried out numerically for the case of silica particles in liquid iron. The analysis predicts a three-stage behavior for the removal of oxygen, an incubation stage, a stage of rapid separation, and a slow final stage where the content approaches the equilibrium value. The agreement with experimentally determined size distributions and deoxidation times is considered to be good. A quantitative estimation of such growth mechanisms as diffusion from the melt and redistribution of oxygen from small particles to large ones shows that these latter mechanisms cannot explain the experimentally observed gvowth of inclusions. This also indicates that collisions provide the important growth mechanism. OXIDE inclusions precipitate when a deoxidizer like silicon or aluminum is added to a steel bath. The inclusions grow and the large particles tend to separate from the bath. For each type of oxide the growth determines the sizes of the final inclusions as well as the total inclusion content of the steel. The mechanism of growth is controversial, however. It has been suggested that an inclusion grows principally by diffusion of atoms through the melt to the inclusion particle or principally by collisions and coalescence with other inclusions. Diffusion growth is always present to some extent but recent experiments and calculations by Torssell,' Kniippel et 'a1.,2 Sano et al. and Miya-shita4 indicate that collisions may be more important than previously realized. A detailed analysis has so far been lacking. The present paper is a quantitative, statistical analysis of the growth and separation of inclusions and is based on a collision theory. Nuclea-tion is not considered. The numerical estimates are based on the experimental conditions of Torssell's' investigation and comparisons are made with his observations. Torssell' studied the growth and separation of silica particles in liquid iron. Samples were taken from a 0.6 kg iron bath at various times after the addition of silicon. By a particle-counting technique developed by Bergh and Lindber~the size distribution of the inclu- sions was determined. The number of particles at the first sampling, 10 sec after silicon addition, was of the order of 3 x lo7 to 10' per cu cm, the largest particles having a radius of 2 to 4 pm. The volume fraction was 0.001 to 0.004; i.e., the dispersion was very dilute. During subsequent holding the largest particles increased their radius by a factor of 10 after about a minute, and the whole size distribution was displaced toward larger values. These results were obtained with allowance for precipitation of the equilibrium concentration of oxygen during solidification. The bath contained less than 0.01 pct of C. Figs. 1 and 2 show the typical appearance of the inclusions. Most particles are very closely spherical and appear to have been liquid or semiliquid in the melt. The observed number of inclusions, about 5x 10' per cu cm, is of the same order of magnitude as found by ~er~h.' This is a large value. It follows that the diffusion distances are very short and that the precipitation

Jan 1, 1969

By J. T. Williams

The equilibria in the V-Zr alloy system were investigated by solidus temperature determinations, thermal analysis, dilatometry, electrical resistance measurements, microscopic examination, and X-ray diffraction analysis. There is a eutectic reaction at 1230°C between a compound, V2Zr, and a solid solution containing 10 pct V in ß zirconium. V2Zr decomposes at 1300°C into liquid and a solid solution containing about 10 pct Zr in vanadium. The eutectic composition is probably about 30 pct V. A eutectoid reaction between V2 Zr and a zirconium takes place at 777°C at a very high rate. The eutectoid composition is 5 wt pct V. The limit of solubility of zirconium in vanadium was estimated to be 5 pct at 600°C. No attempt was made to determine the liquidus for the system. THE recent availability of large quantities of high purity zirconium has stimulated the study of zirconium binary systems. The equilibrium diagram for the V-Zr system has received little attention, however. Wallbauml appears to have made the first report concerning the equilibria in these alloys. He reported the existence of a compound, V2Zr, having the MgZn2 ((214) type of structure with a, = 5.277 kX and c° = 8.647 kX. Anderson, Hayes, Roberson, and Kroll2 made a survey of some potentially useful zirconium binary alloys and found that zirconium probably dissolves a small amount of vanadium. They reported the probable existence of a compound between the two elements and suggested that the zirconium-rich solid solution undergoes a eutectic reaction with this compound. Pfeil," in a critical review of the existing information, estimated that the solubility of vanadium in zirconium is less than 4.7 pct and probably less than 1.8 pct. Rostoker and Yamamoto' proposed a partial diagram for the V-Zr system in a survey paper on vanadium binary alloys. Their diagram indicates the compound, V,Zr, a eutectic reaction at 1360°C, a peritectic reaction at 1740°C, and a limit of solubility of zirconium in vanadium of about 3 pct. They obtained no information on the equilibria in the zirconium-rich alloys. In view of the potential utility of the V-Zr alloys and the incomplete knowledge concerning the equilibria in the system, an attempt was made to establish the constitutional diagram. Preparation of the Alloys Raw Materials: The vanadium for making up these alloys came from the Electro Metallurgical Corp. Zirconium came from two sources. In the beginning of the investigation, sponge zirconium from the Bureau of Mines was used in making some of the alloys. Later, iodide metal made at the Westinghouse Atomic Power Development Laboratories became available. This material was used in the preparation of all the dilatometric and resistance specimens and about two-thirds of the solidus temperature specimens. A typical manufacturer's analysis of the vanadium is shown in Table I. No other analysis of the vanadium was made. The metal contained a dispersed second phase and did not have a sharp melting point. Typical results of spectrographic analysis of the Westinghouse zirconium are shown in Table 11. These data indicate a very high purity. The Bureau of Mines sponge metal was probably less pure but had good ductility. Melting: All of the alloys used in the investigation were made by melting pieces of vanadium and zirconium together in a dc electric arc furnace similar to those of Geach and Summers-Smith, craighead, Simmons, and Eastwood," and others. Melting was done in an atmosphere of helium scavenged of residual air by the preliminary melting of a separate charge of zirconium. Each ingot was turned over and melted at least three more times before removal from the furnace to aid in the attainment of homogeneity. Alloys prepared for use in the investigation are listed with the results of solidus determinations in Table III with the exception of the following compositions upon which no solidus determinations were made: 0.29, 0.54, 4.57, and 5.55 pct V. Analysis: The weight of each ingot made from iodide zirconium was within 0.1 g of the total weight of the initial charge, about 90 g. Since each component of each charge was weighed to the nearest 20 mg for amounts less than 10 g and to the nearest 0.1 g otherwise, the gross composition of an ingot could be calculated accurately. Chemical analysis for the vanadium content of several alloys agreed

Jan 1, 1956

By R. L. Moment

The anisotropic elastic behavior of rolled beryllium sheet has been measured, using a pulse echo technique, and compared with X-ray diffraction data. Calculated elastic stiffness constants compared favorably with published values for beryllium single crystals which were attributed to the strong (0002) rolling plane texture. Variations of Young's modulus in the yolling plane could be associated with the velative distribution of (0002) planes out of their ideal position in the rollitzg pkule. WHEN a metal is subjected to cold working such as drawing, forming, or rolling, a crystallographic texture develops which can significantly alter its physical properties. One method for detecting this texture is X-ray diffraction, but Alers and Liu' have recently pointed out how the prediction of anisotropic physical properties from pole figures alone is not always accurate due to differences in interpretation. Variations in Young's modulus with orientation or, more completely, the values of the effective elastic constants of the worked metal, also serve to indicate the presence of a texture. In fact, as Alers and Liu' pointed out, calculated variations in Young's modulus for assumed orientations, when compared with experimental data, can be used to eliminate some of the uncertainty in interpretation of X-ray pole figures. Thus, elasticity measurements can serve not only to clarify any unusual elastic behavior of worked metal, but also to detect and in part determine the nature of its texture. X-ray determination of the texture of rolled beryllium has been reported by Smigelskas and Barrett,2 who found a strong texture of (0002) in the rolling plane with (1070) planes normal to the rolling direction. In the case of metal rolled at room temperature, they reported that [1010] directions also appeared at positions 60 and 120 deg from the rolling direction in the rolling plane, while in more recent work Keeler3 found these directions were also tilted towards the rolling plane. The texture for beryllium rolled at 80O0C, however, only showed (1010) planes normal to the rolling direction and the spread of (0002) planes out of the rolling plane was less. In looking for elastic anisotropy one might consider unidirectional rolling of a metal as introducing an or-thorhombic symmetry through reorientation of the grains, since the three deformations, compression, extension in the rolling direction, and extension in the cross direction, are orthogonal to each other and unequal in magnitude. Thus the rolled sheet could be treated like an orthorhombic single crystal and the nine stiffness constants of the elasticity tensor used to calculate the anisotropy of Young's modulus, the shear modulus and Poisson's ratio. In this case we could write: which is symmetric about its diagonal. Borik and Alers4 have recently used this approach on rolled die steel with very good results. They found, however, that instead of displaying orthorhombic elastic symmetry their specimens could be considered tetragonal in which case Cr1 = c22, c13 = Ca, and c44 =cjj. This conclusion was made solely on the basis of the measured tensor elements, and serves to point out the advantage of this method for studying the anisotropy of rolled metals. Their calculated values for Young's modulus as a function of angle in the rolling plane also checked very well with direct measurements made on different specimens using the resonance technique. In the present study, cross-rolled beryllium was used which had been unidirectionally rolled about 11 pct for the final reduction. This imparted a slight anisotropy in the rolling plane which was detected both by X-ray techniques and elasticity measurements. For purposes of discussion in this paper, the rolling direction is that direction in which the most reduction passes were made and cross direction is the normal to the rolling direction in the rolling plane. It was also decided to consider the rolled sheet as displaying orthorhombic symmetry for the purpose of obtaining elasticity samples with the direction defined as in Table I. Any change in the final symmetry attributed to the sheet would then be made on the basis of the measured elastic stiffnesses. The final data would then be compared with that expected from the X-ray study and that reported for beryllium single crystals. EXPERIMENTAL PROCEDURE Rolling Schedule. The samples used in this study were taken from a large sheet which, because of its size, had to be unidirectionally rolled for the final reduction. The resulting texture was that of cross-rolled metal with a slight unidirectional texture superimposed. A cast beryllium ingot, 9.500 in. sq by 3.325 in. thick, was cross-rolled to 81 pct reduction followed by unidirectional rolling for an additional 11 pct to give a total reduction of 92 pct. The thickness of the final sheet ranged from 0.265 to 0.280 in. Reduction up to 67 pct was done at 980°C and the final 25 pct at 870°C. Analysis for metallic impurities showed aluminum 0.06 pct, iron 0.19 pct, and silicon 0.11 pct, giving a beryllium purity of 99.64 pct.

Jan 1, 1968

By E. H. Kelton

The purposes of this paper are to describe the use of adjustable cut and draw tools as a control test of drawing properties and to point out that no other well-known test or combination of tests determines this quality in zinc and zinc alloys. Rolled zinc has been used for making drawn articles, particularly battery cans, for many years. The development of rolling treatments satisfactory for these purposes followed the usual course of trial and error experimentation depending upon cooperation with customers to determine what type of material was suitable. A quick test of drawing quality was highly desirable, of course. Scleroscope hardness and temperll having no apparent relation to drawing quality, were used simply to check the duplication of rolling treatment and grade of metal. The dynamic ductility1 test, on the other hand, was believed to be so like the drawing operation as to provide a reliable index and came to be taken as the criterion of good drawing properties. Faith in this test was strengthened by the fact that metal having the highest ductility was more satisfactory for operations, such as the manufacture of battery cups, that required several redraws. No distinction was made at that time in specifying metal as to whether it was to be subjected to simple cut and draw, redrawing or forming operations. It developed, however, that in some grades of metal the highest ductility did not coincide with the most satisfactory quality when the material was used for a single draw. When zinc-base alloys, with their wider ranges of effective rolling treatments, came into increased use, their dynamic ductility and drawing quality appeared to have no connection whatever. Furthermore, comparisons of known drawing quality with other physical properties of the metal, including tensile strength, elongation and dynamic cold bends, were fruitless in yielding any clear relationship. Almost any test value produced in one piece of metal could be duplicated by another rolling or annealing treatment with attendant different drawing characteristics.

Jan 1, 1934

By E. C. Tveter, L. A. Roe

The authors present a general outline of the theory and development of heavy-liquid application to mineral processing. Patent literature and processes are reviewed with special emphasis on liquid recovery systems which have been employed or proposed. Advantages and disadvantages of the process are discussed together with the recent developments which have revived interest in this old concentration method. The most important single factor in this resurgence of interest is concluded to be the narrowing gulf between chemical engineering and mineral dressing which has opened the field for new concepts of mineral plant design. A partial summary of patents on heavy liquid separations is included. In spite of the fact that heavy-liquid separation with organic liquids has been used in the laboratory for over 50 years, this process has never graduated to large scale commercial use for any extended period. However, a variation of this process, the sink-float or heavy-media separation process has found wide acceptance and is used to separate minerals from diamonds to gravel. Materials used to increase the specific gravity of the pulps used as heavy media include sand, clay, barite, magnetite, galena, hematite, atomized lead and ferrosilicon. Because of the greater ease of recovery, the magnetic materials, magnetite and ferrosilicon, are the preferred media today. In the U. S. alone, heavy-media iron ore plants with a capacity of over 10 million tons of concentrate per year are in existence. Heavy-media separation involving use of solid, inorganic particles suspended in water rapidly found a wide range of commercial use with the introduction of magnetic media. The minerals engineer is experienced in working with suspensions and quickly learned to develop and control such media at a cost compatible to the type of separation desired. The natural superiority of a heavy liquid with uniform chemical and physical properties has never been questioned since its first use in laboratory mineral separatory procedures. It offers the only method for gravity separation of fine particles of relatively close specific gravity. The most important early attempt to make heavy liquid separations commercial were made by the DuPont Co. which began experimental work on Virginia limonite in 1904. The appended "Partial Summary of Patents" compiled by W.L. O'Connell of The Dow Chemical Co. demonstrates the quantity and sequence of this work. Both inorganic and organic parting liquids were investigated and numerous patents were issued on the use and recovery of these liquids. The work culminated in the heavy liquid plant of the Weston Coal Co. at Shenandoah, Pa. Chemical engineering design of this plant was the responsibility of Francis I. and Hubert I. DuPont. Heavy-liquid separation of coal almost achieved commercial status at this plant which actually processed over 20,000 tons of coal. The liquids used were tetrabromethane, pentachloroethane and trichlo-roethylene, with liquid losses ranging from 8.9 to 12.4 oz per ton of cleaned coal. The reasons for failure of this plant are not clear but probably involved toxicity problems as well as other problems in chemical engineering. Excellent economics were reported. A more recent pilot plant was built in 1954-55 by Norris Goodwin for the Inerto Co. to treat hectorite clay. This plant employed carbon tetrachloride in jigs with liquid recovery by evaporation. Although good separation was achieved, incomplete removal of the CCl, from the clay prevented commercial operation. The only present operations known to the authors employing heavy liquids for gravity separations are limited to the use of calcium chloride in certain coal washers and bromochloromethane in a small batch operation (one ton solids per day) for the separation of beryllium metal particles from slag materials. This is not strictly a minerals beneficiation problem but it has demonstrated the feasibility of such separations. PROBLEMS Critics of early attempts to commercialize heavy-liquid separation of minerals summarize the draw-

Jan 1, 1963