By K. Moriyamo

Operation improvement efforts at Hyuga Smelting Co., Ltd. have focused on calcining capacity in the reduction rotary kilns ("the kilns"), whose limited feed rate capacity had capped production at around 18,000t-NiN since 1995. To improve the kilns' feed rate capacity of 80 wet t/hr, attempts were made to increase the gas flow in the kilns by increasing the capacity of the off-gas fans. However, as the increased gas flow resulted in only limited improvement of the kilns' feed rate, a scoop feeder was installed on each kiln to add coal to the middle of each kiln's interior to gain a higher efficiency of thermal supply and conversion. With these gas flow and coal charge addition operations, the kilns' feed rate capacity increased up to 120 wet t/hr, with burner fuel efficiency increasing by approx. 10% (approx. 5% in total with the additional coal included). As a result, production was raised to a level of 22.000t-Ni/Y Keywords: reduction rotary kiln, scoop feeder, additional coal charge.

Jan 1, 2004

By A. P. Paiva

With the aim of establishing a valuable alternative to the conventional methods, studies regarding the recovery of precious metals by solvent extraction have been increasing over the past few years. In this work, the selectivity of extraction presented by Cyanex 471X toward silver is investigated. Simulated chloride solutions considering contents of iron and copper usually present in actual leaching practice were used. The characterization of the aqueous solutions - in terms of the multiple equilibria established by the chlorocomplexes of the different metals and their relation to the total chloride concentration of the base-electrolyte - was successfully carried out by cyclic voltammetry. The results obtained support the important contribution of the electrochemical techniques for the understanding of the overall extraction phenomena.

Jan 1, 1994

By Patrick R. Taylor

Thermal plasma technology has a wide range of applications in extractive and process metallurgy. Beneficiation of complex ores, oxide reduction, melting/remelting of refractory metals and scrap, and the recovery of precious metals from waste products are some examples of potential uses for plasma technology. The highly concentrated enthalpy provided by plasma torches is a cleaner energy source and may give higher processing rates per reactor volume than conventional technologies. Some of the other advantages may be: controlled furnace atmosphere, ability to treat fine feed materials and rapid quenching. A review of some of the uses for plasma processing in non-ferrous process and extractive metallurgy is presented.

Jan 1, 1993

By D. Holdridge, D. Liao, S. Waterfall, N. Strobl, S. Sun

High melting point inclusions, such as spinel, alumina and AlO rich calcium-aluminates, have a strong tendency to agglomerate on the tundish stopper rod and Submerged Entry Nozzle (SEN) during the steel casting process, and eventually to cause SEN clogging. Calcium treatmen by wire injection during steel refining during Ladle Metallurgy (LM) is commonly used to modify these troublesome inclusions to lower melting point inclusions. However, too much Ca injection (Ca over-treatment) can cause operational issue (e.g. slide gate plate erosion),as well as increase Ca cost. Therefore, it is desirable to add an appropriate amount of Ca to avoid either under-or over-treatment. Based on inclusion analysis with an ASPEX® computer controlled scanning electron microscope (ASPEX) instrument, AlO and AlO rich calcium-aluminates were identified as a major cause of SEN clogging at ArcelorMittal Dofasco Electric Arc Furnace (EAF) steelmaking stream. A Ca treatment index was developed to improve the inclusion modification. The improved inclusion control has reduced SEN clogging and enhanced steel quality.

Mar 1, 2017

By Ruixuan Zhang, Yan Li, Shusen Cheng

The measurement of raceway temperature in the blast furnace is a critical issue, which is very significant for judgment of, prediction and diagnosis of the racewa yburning state. This paper deals with mathematical models by Monte Carlo method to approximately simulate the radiation heat transfer in the race-way and establish matrix equations using CCD cameras, which are solved to obtain the three-dimensional temperature field. Due to the existence of fluctuation error, CCD camera measurement error and others,this is analyzed and random error is added in the measurement data to demonstrate the effectiveness and stability of the reconstructed temperature field. The results show that the reconstructed three-dimensional temperature field of the raceway is very close to the exact temperature.

Mar 1, 2017

By Mikio Kobayashi

Extraction of valuable metals from sulfide ores continues to be a very important, process and so the strict control of discharge of harmful metals in effluents from refineries becomes more important in the future. The recovery methods for heavy metals have been developed. Some metals such as Se and As are still difficult to be removed to very low concentration, although the techniques for recovery and removal for many kinds of heavy metals have already been developed. Especially, in case of Se the recovery system from water with low concentration has not be developed yet, although the WHO decided Se to be harmful for human beings and then the discharge control is under obligation now. In general Se exists as selenite ion and/or selenate ion in aqueous phase and selenite ion is able to be recovered by coprecipitation with ferric hydroxide or by reduction to solid selenium by general reductants. Selenate ion, however, has a strong resistance to conventional treatments. Therefore the new technique for the recovery of Se from water including selenate ion has to be developed. In this presentation the new approach for removal of selenate ion using the reaction in which ferrous ion is oxidized to ferric ion is presented. Selenate ion is reduced to selenite ion during the reaction and then to solid selenium, while ferrous ion is oxidized to ferric ion. The coexistence of activated carbon is very useful to increase the reaction rate. The use of iron powder is also effective and very useful for reducing gel-like precipitates mainly consisted of ferric hydroxide. The concentration of the residual selenate ion is probably under 0.1 ppm after recovering Se by the mentioned-above approach. In addition to the mechanisms of these reactions, the effects of pH, coexistent positive and negative ions, and reaction temperature are also presented. Furthermore the investigation of the behavior of selenosulfate is presented.

Jan 1, 1998

By Petre Stelian Nita

In small steelmaking shops, in foundries and forging plants, there are not too many option to recycle the basic slags, which are not suitable for many purposes of recycling, because of their low chemical and structural stability. A solution of an adequate recycling is a direct recycling in EAF. Several quality requirements, physico-chemical properties and proportions of slags must be analysed. The progress in this fields permites to establish an adequate proportion of recycled slag, based on enough exact computation of the related property. For oxydizing slag, obtained during melting and in the first part of decarburization operation, the problem of phosphoms contents can be analysed using the phosphate capacity (C PO34-). For reducing periods, during deoxidization operation, desulphurization also occurs and the problem of the sulphur contents can be analysed using the sulphur and sulphide capacities ( Cs / Cs) Between this two complex thermodynamic indicators of the slags. a direct relation is established, using thermodynamic aspects, resulting from the equilibrium constants for dephosphorization and desulphurization process and also, using the optical basicity of slags, computable from the chemical analysis of the slags. On this basis starting from the steel quality requirements. adequate strategies can be established in order to obtain high rates of recycling (between 50-80%) of steelmaking slags. Important cost savings are obtained through this procedure, based on the correct amounts of the fresh lime, iron ore and fluidizers. Keywords: Slag, Properties, Recycling

Jan 1, 2003

By Denise C. R. Espinosa

The amount of secondary batteries are increasing about 15% by year. Among these batteries, it can be highlighted the NiCd ones, due to their high consumption. In Brazil, the consumption of NiCd batteries grown quickly in the last 5 years, due to the dissemination of cellular telephones and other electronic devices. The first step of a process to recycle spent NiCd batteries is the pretreatment through unit operations of mining treatment. The aim of this work is to define a physical pretreatment to conditioning the waste to a pyrornetallurgical recycling process of spent NiCd batteries used in cellular telephones. Batteries were disassembled by hand to release the different components. The studied batteries are basically composed (by weight) of: 78% nucleus, 18% plastic case and 2% circuits. The grinding of the batteries was performed by knife mill and also by hammer mill. After grinding the material was screened and submitted to a magnetic separator.

Jan 1, 2001

By J. L. Liow

Studies have been carried out on the causes and effects of slopping in an annular cylindrical geometry such as the top submerged combustion reactor. Properties of standing waves formed such as the wave profile, period, pressure distribution and velocity have been derived analytically. The wear profile due to wave erosion was calculated based on the assumption of linear motion and that the wear is a dissolution process. The use of the j, factor showed that the wear was proportional to the square root of the wave velocity at any point. Using the dimensions of the lsasmelt reactor given by Errington et al. (1987)[11, the wear profile due to wave erosion was calculated using the analytical solution. The wear profile calculated was shown to have a maximum just below the initial bath surface. The wear was found to be concentrated in the region where the first asymmetric standing wave was most active. The results showed that the refractory near the bath surface will be affected by wave erosion, more so than any other parts of the reactor. The contribution of wave erosion on wear must be accounted for in assessing the total refractory wear of a vessel in which slopping exists.

Jan 1, 1991

By L. Klinger, T. Werber, LA Levin, A Katsman

"The process of catastrophic carburization known as ""metal dusting"", whereby a solid metallic material is converted into fine particles in a carburizing atmosphere, was analyzed. It was shown that this conversion is the result of plastic deformation and subsequent fracture accompanying diffusional phase formation in the near-surface layer. The process is controlled by internal stresses arising during phase transformation. Competition between stress generation and relaxation may result in the attaining the ultimate strength in the near-surface layer and its fracture. Such a mechanism of metal disintegration may occur in a certain temperature interval depending on the kinetic and geometrical parameters of the system - the diffusivities of the alloy's components, the ratio between specific volumes of the new and the old phases, and the ultimate plastic strain. The temperature interval for disintegration of carbon steel, the rate of disintegration, and the period of the disintegration cycle, were evaluated and compared with experimental data. IntroductionCatastrophic carburization, known as ""metal dusting"", consists in conversion of a solid metallic material into fine particles. The process occurs in a carburizing atmosphere at elevated temperatures. The corrosion product, usually named ""coke"", consists of metallic particles dispersed in a loose carbon matrix. Under industrial conditions metal dusting takes place, for example, in a gas mixture of CO and H2 or in hydrocarbon environments. Steels, nickel- and cobalt alloys are susceptible to this kind of wastage in the temperature range 400-800°.A mechanism of metal dusting in steels was proposed by Hochman [1] and later developed by Grabke and coworkers [2-5]. According to the proposed model, the process consists of the following reaction steps:"

Jan 1, 1996

By Feng Chen, Lirong Chen, Yufeng Guo, Wenjie Weng, Tao Jiang

"In this paper, the carbonthermal reduction behavior and the influencing factors of Panzhihua ilmenite under the condition of carbon-burdened were systematically investigated. The results show that the ilmenite forms into titanium nitride during the reduction process at 1200 °C under the condition of carbon-burdened. Carbon-burdened is beneficial to the reduction of iron oxide, but less favorable for the growth of iron grain.IntroductionThe titanium ferrous resources are very rich in Panzhihua-xichang area, accounting for about 38.85% of the world's proved reserves [1]. However, TiO2 grade of this kind of ilmenite is low and calcium magnesium content is high, it generally requires preconcentration to titanium-rich material—titanium slag or synthetic rutile.Chlorination process is an advanced method for production of titanium dioxide, which should takes high quality titanium-rich material with low content of calcium and magnesium as raw materials (the content of MgO and CaO are less than 1.0%). Ilmenite in Panxi area, however, contains high calcium and magnesium; it is not suitable as a raw material for chloride process. Methods of producing titanium-rich materials which have been applied in industry are electric smelting, various acid leaching and reduction rust [2-5]. There still exist some problems such as CaO and MgO removed not thoroughly, low resource utilization, high energy consumption and environmental pollution."

Jan 1, 2012

By Anil Saigal, Mark H. Shooter, Michael A. Zimmerman

Liquid Crystalline Polymers (LCPs) provide favorable dielectric properties for extremely high frequency (30–100 GHz) radio frequency device packaging and printed circuit board substrates. The material studied in this work is a proprietary, thermotropic LCP composite developed and manufactured by iQLP (Woburn, MA, USA). Dielectric constants measured in the flow direction of the post-processed materials differ between the two processes, 3.51 in injection molded plaques, and 4.23 in cast films. This investigation sought to determine the cause of process-induced variation in the dielectric constant between injection molded and cast film extruded LCP. The complex thermomechanical environment present during processing of LCPs creates a through-thickness hierarchical structure, simplified in this study as a skin and core layer. The volume fraction of skin layer of the post-processed LCP was determined to be the differentiating factor, and responsible for the difference in dielectric constant between the injection molding and cast film extrusion processes. The resulting dielectric constant is a function of this volume fraction with a near linear relationship.

Mar 1, 2017

By Lv Guozhi, Niu Liping, Liu Yan, Zhao Qiuyue, He Jicheng, Zhang Ting’an, Dou Zhihe

"This paper proposed a new method of Mg and Cl2 circulating for titanium sponge production by direct pyrolysis and thermal reduction process. Effects of pyrolysis temperature, pyrolysis time and partial pressure of oxygen on pyrolysis efficiency were researched, and the crystallite structural transformation of MgO productions at different pyrolysis temperature and time were analyzed by XRD. The experimental results indicates that the pyrolysis temperature and time effects the pyrolysis efficiency obviously, and the reasonable pyrolysis conditions by using MgCl2 in molten state are as follows: the pyrolysis temperature is 1100?, pyrolysis time is 60min and the partial pressure of oxygen is 100%, the pyrolysis efficiency get above 95% at this conditions. The dynamic analysis of molten magnesium chloride pyrolysis reaction shows that, as a chemical reaction process control, the response of the apparent activation energy Ea=70.4 kJ/mol.IntroductionTitanium is a young metal, it is applied in industrial until the Second World War. It is 160 years from the discovery of titanium to the industrial production of ductility titanium by magnesium reduction method in the United States in 1948. As a new kind of metal, titanium and titanium material are better than the traditional metal materials in mechanical properties, heat resistance and thermal conductivity. Titanium is a kind of landmark structure and function material, which is called “space metal”, “Marine metal”, “Intelligent metal” [1-3]. Although the study of new methods of titanium melting get more at present, Kroll method and Hunter method are really applied to industrial production methods for titanium smelting, and Hunter method is already discontinued because of costs at present. The core technology in Kroll method of sponge titanium production process can be ome down to two circulation, namely the cycle of magnesium and chlorine in preparation-process of titanium sponge. In the traditional Kroll method, the cycle is realized through magnesium chloride which is produced by the electrolytic magnesium reduction process in hot molten state. But because investment of equipment for electrolysis method is too high, this method has not been used by most titanium sponge production enterprise in China. At present most titanium sponge production enterprise in China produce titanium sponge by the outsourcing of titanium tetrachloride, but the main disadvantage of this method is that the by-product of magnesium chloride is difficult to deal with."

Jan 1, 2012

By Yasuhiro Konishi, Yoshiyuki Noda

"This paper describes a new processing of rare-earth oxide precursor, in which rare-earth carbonate powders are precipitated directly from emulsions of rare-earth loaded carboxylate solutions, using CO2 gas and water. This synthetic route of rare earth carbonate is a combined process of the stripping and precipitation stages in a conventional solvent extraction. Using this technique, lanthanum carbonate and yttrium carbonate were prepared at temperatures of 10 to 80°C and CO2 pressures of 0.1 to 3.0 MPa for 120 min. The rates of carbonate precipitation in a batch autoclave were sensitive to processing parameters such as CO2 pressure, temperature, and organic-phase composition. The particle size distributions of the carbonate powders were markedly dependent on temperature and C02 pressure.IntroductionSolvent extraction is the most appropriate commercial technology for separation and purification of rare earths. In typical commercial processes, the rare earths are stripped from loaded solvent extractants using aqueous solutions of mineral acid. After adjusting the pH of the aqueous strip solution, the rare earths are precipitated as insoluble powders of oxalates or carbonates, from which oxides can be produced by calcination. Such conventional processing can be simplified when the stripping and precipitation stages are combined by emulsifying rare-earth loaded solvent extractant with aqueous oxalic acid solution. It is likely that the single-stage precipitation stripping results in a marked decline in the consumed amounts of precipitating and neutralizing agents, thereby saving on both running and capital costs.Yoon and Doyle1) first demonstrated that oxalate powders of lanthanum and yttrium are directly precipitated from rare-earth loaded carboxylic acid solvent extractant when contacted with aqueous oxalic acid solution at ambient temperature and atmospheric pressure. Yttrium oxalate pow4ers were also prepared by precipitation stripping of di-(2 ethylhexyl) phosphoric acid. (D2EHPA) extractant using oxalic acid-hydrochloric acid solutions. 2) Moreover, neodymium oxalates were directly precipitated from organic solutions of tertiary aliphatic monocarboxylic acid and 2-ethylhexyl phosphonic acid mono-2- ethylhexyl ester using aqueous oxalic acid solutions, and powder characteristics of the resulting oxalates were compared with those of powders by the conventional solvent extraction routes. 3 • 4) Recently, attention has been directed towards the influence of processing parameters on the particle size distributions of yttrium oxalate precipitates. 5)"

Jan 1, 2000

By P. D. Nolan

Smelters operating under pollution control orders have become increasingly dependent upon the reliable operation of sulphuric acid plants and no factor affects the long term reliability of those plants more than efficient gas cleaning. The sources and characteristics of contaminants in smelter of fgases and the conventional approaches to removing these contaminants to accepted levels are discussed. New technology is described which offers advantages of lower capital cost, lower operating cost and reduced space requirements over the conventional approaches. This new technology has been developed by LAB s.a. and is licensed for metallurgical gas applications by Chemetics International Company.

Jan 1, 1983

By R. M. Lamya

A considerable part of gold encapsulated in some refractory sulphides can be dissolved during sulphide matrix decomposition in non-complexing aqueous media. This has been concluded from laboratory results of gold extraction from pyritic and arsenopyritic concentrate containing 172.8ppm Au, into 10% hydrochloric, sulphuric and nitric acids. The degree of sulphides decomposition in the non-oxidative acids limits the gold extraction from this specific concentrate to about 10%. In the case of nitric acid, the gold dissolution follows the rapid decomposition of sulphides, reaching 32 to 42% of extraction at almost total decomposition of the sulphidic minerals. Accumulation of gold in this acidic and non-complexing solution to several ppm was not affected by the soluble products of the sulphides decomposition. An attempt to explain this gold behaviour is undertaken and some practical implications are discussed. In the investigated concentrate the "soluble gold" is mostly associated with arsenopyrite. This is consistent with the latest findings of other authors that gold disseminated in arsenopyrite can occur as cation Au3+. In a comparative test the gold extraction into highly concentrated chloride solution, in the same oxidative conditions, amounted to 92.34%.

Jan 1, 1995

By Garrett May

We present a periodic technique for measuring the thermal conductivity of thin, disk-shaped samples. In samples of this type, temperature measurements must be made across the sample faces and are therefore subject to large error due to the interface resistance between the temperature sensor and the sample. The technique uses measurements of the amplitude and phase of the periodic temperature across both a reference sample and the unknown material at several different frequencies. Modeling of the heat flow in the sample allows the simultaneous determination of the thermal parameters of the sample as well as the interface resistance. The technique is demonstrated on nanocomposite samples less than 1.0 mm thick.

Jan 1, 2008

By M. J. Adam

The U.S. Bureau of Mines has investigated the partitioning of complex minerals to simpler phases using sulfidation reactions for selective extraction of mineral values. This report describes research in which thermal processing of the complex Ti-bearing mineral ilmenite (FeTi03) resulted in partitioning of the valuable Ti metal to the simpler compound rutile (TiO2). Samples of ilmenite were blended with elemental S for thermal treatment at various temperatures under controlled atmospheres in an effort to dissociate the Fe from the ilmenite complex. Product characterization revealed that the Fe was partitioned 'from the ilmenite, forming a rim of pyrrhotite/pyrite (FeS/FeS2) on a rut il e core. The products were agate milled and then subjected to cursory magnetic and flotation techniques in an attempt to physically separate the partitioned phases. Partitioning results and phase concentration data are reported relative to thermal treatment variables and physical separation techniques.

Jan 1, 1991

By John J. Moore

This paper discusses the application of a video technique to construct stability diagrams for the combustion synthesis of ceramic-metal composites. Several model exothermic combustion synthesis reactions have been used to investigate the effect of the reaction parameters, eg. stoichiometry, green density, etc, on the stability of the propagating combustion reaction front and subsequent product morphology. The effect of varying the reactants and their stoichiometry to provide a range of reactant and product species ie. solids, liquids and gases, in the synthesis of both dense and expanded (foamed) ceramic and ceramic-metal composites was also investigated with respect to their corresponding combustion front stabilities.

Jan 1, 1993

By E. J. Peuraniemi

Primary copper production using suspension smelting techniques like Outokumpu Flash Smelting always causes some dust formation. Flue dust particles are formed when sulphide feed material reacts violently with oxygen inducing particle disintegration and total desulphurisation of fragments. In the process, flue dust follows the off-gases to the heat recovery boiler (HRB) where its sulphation takes place because of prevailing conditions. Sulphation releases heat and causes also a drop in particle melting temperature and, further, particle sticking to the walls and heat exchange tube banks. Sulphation of synthetic CU20 particles were examined using a laboratory scale fluid-bed reactor. This study aims to a better understanding of flue dust behaviour in a HRB and, thus, to a better operational practise and design of a HRB. The effect of PSO/PO2 -ratio and temperature on the sulphation kinetics were tested. Standard chemical analysis, light optical and scanning electron microscopy with energy dispersive spectroscopy were used to examine the samples.

Jan 1, 2001