By Steve Lloyd, Ryan J. Foy, Brandon Steinborn, Jerome P. Downey

Research was performed to evaluate copper and silver extraction from samples of bornite flotation concentrate. Sulfation roasting experiments were performed in a rotary tube furnace, a fluidized bed reactor, and a static bed muffle furnace. Roasting was plagued with rapid, lowtemperature calcine sintering, apparently related to the presence of organic matter in the concentrate. Calcine entered a weak acid leaching process to remove copper, and silver was extracted from the weak acid leach residue in a ferric chloride and hydrochloric acid solution. Copper extraction efficiencies in excess of 90% were attained in the weak acid leach while 90% silver extraction was achieved in the ferric chloride leach, along with copper and lead extractions as high as 93% and 99% respectively. The two-stage leaching process resulted in overall extraction efficiencies of 99% copper and 90% silver.

Jan 1, 2015

By Victor Stancovski, Uday Pal, Stephen C. Britten

"An in situ electrochemical technique for measuring the concentrations of easily dissociable oxides in slags at temperatures between 1200-1600°C is being developed. The technique utilizes a partially-stabilized-zirconia solid electrolyte (PSZ), which conducts oxygen ions, to separate a reference-gas compartment from the slag of interest. Three types of measurements are currently under investigation which yield different information concerning the slag phase and hence will be combined into a single amperometric device for monitoring the properties of easily dissociable slags.Type I utilizes an open-circuit-voltage measurement between the reference gas and the slag phase. Type II utilizes a potentiostat to apply a direct current potential step or sweep between the inner and outer compartments of the electrolyte, driving oxygen ions from the slag into a reference gas. With the use of open-circuit-reference electrodes, the resulting current-potential profile reveals the dissociation potential and concentration profile of dissociable oxides such as those of iron, manganese, and chromium. Information on the transport properties of the cations can also be generated from these measurements. Type III utilizes a potentiostat with reference electrodes to carefully electrolyze a known volume of slag by removing large quantities of oxygen ions from the slag to the reference gas. The coulombs of charge removed at different applied potentials can be used as a direct indication of the concentration of each dissociable oxide species present within the slag."

Jan 1, 1997

By A. McLean, S. Dawson, N. D. G. Mountford

"IntroductionIn order to predict the accepted industrial practice for the year 2000, it may be helpful to first consider the rate of development of scientific knowledge. If the speed with which man can travel on commercial vehicles is taken as a criterion for determining the rate of progression, then it can be seen from Figure 1 that advancement in our present century is very rapid. Likewise, if computer technology is used as a criterion for the measurement of scientific advancement, it becomes evident that technological evolution can be highly exponential. These two examples are sufficient to demonstrate that engineers and managers cannot afford to regard scientific development as being linear with respect to time if they are to avoid underestimating the needs of society.Within this framework of overall development, the time required for individual ideas to progress from inception to regular application has decreased considerably. For example, X-rays first discovered by Roentgen in the 1890's and now used widely in medicine and engineering, required a developmental period of some eighty years. The motorcar evolved from early beginnings at the turn of the century to a position of great social impact in sixty years. Rectifier materials used in high frequency radar to the present explosion in communications, required forty years. As illustrated in Figure 2, the period is shortening rapidly.The use of sound waves appears to be following a similar path. There is now a considerable body of knowledge concerning their behaviour and exceptional advances have been made. In medicine and engineering the sonic approach to examination is well established, and acoustic testing forms the basis of several diagnostic and quality control applications. With respect to metals engineering, ultrasonic testing has contributed to the understanding of the relationship between the size and number of internal defects and the probability of premature failure. This has allowed the designer to incorporate appropriate safety factors in his designs; but more importantly, the realization of the deleterious effect of inclusions on the performance of the final product has resulted in a continuous pressure on the material suppliers to reduce the number of defects in their products.It is not only the designer who is demanding defect free material but also the fabricator, as material breakdown during manufacture can be prohibitively expensive. Examples of this can be found in both the aluminum and steel industries where ultra clean sheet is required to ensure that rejections are minimized during beverage can manufacture and other deep drawing operations."

Jan 1, 1988

By P. Lussiez

Precipitates consisting of amorphous ferrihydrite and crystalline goethite have been prepared by aging hydrolyzed Fe (III) solutions at room temperature. The precipitates have been characterized by x-ray diffraction and differential thermal analysis. The amorphous ferrihydrite transforms to goethite with time. The ferrihydrite to goethite transformation is affected by the presence of small amounts of copper or nickel coprecipitated with the iron. .The addition of copper decreases the amount of goethite at a given aging time and increases the amount of coprecipitate which is initially dissolved in sulfuric acid, but it does not seem to affect the dissolution of the crystalline part'. It is proposed that adsorption of copper hydroxo species on goethite nuclei delays the ferrihydrite to goethite transformation. The effect of nickel is less dramatic than that of copper. Apparently a portion of the added nickel is adsorbed on the goethite crystallite surface rather than incorporated into the goethite lattice.

Jan 1, 1981

By C. Dresen

This paper discussed the reaction kinetics of the reduction of industrial phosphate pellets for P4 production. In the reduction process of various phosphate ores, the following parameters were investigated: Diffusion of the phosphorus oxide and other gaseous products from the reaction mixture after having been reduced on the reductant (coke) surface. Influence of silica on reaction kinetics. Temperature influence. Influence of mineralogy and morphology (different ores). Particle size influence of silica and coke. Experiments were carried out in a vertical tube furnace with 2 ores, 2 types of silica and one type of coke. Selected experimental conditions simulated furnace conditions. The following conclusions could be made: Reaction rate increases with the addition of SiO2 into the pellet. The reaction rate increases above 1350°C (melting temperature of the slag). Mixing different ore types in the pellets leads to differences in reduction kinetics. Particle size of the coke particles influence reduction kinetics. The amount of slag formation is influenced by silica addition, coke size and temperature.

Jan 1, 2002

By Hong Ro Lee, Seang Suk Cho, Byung Sun Chun, Chang Whan Won

"The preparation of Al203-SiC-TiC composite powders was studied by SHS process using silica (source of Si02) powder instead of Si which is expensive. And, aluminum powder was used as reducing agent of silica and charcoal activated was used as carbon source. Effects of the molar ratio in raw material mixtures and compaction pressure and initial temperature of reactant on the products and combustion process were studied. The most important variable affecting the synthesis of Al203-SiC-TiC was the molar ratio of carbon. The combustion reaction generated in powder state without preheating. But the unreactants exist in the product on all molar ratio. When the preheating temperature is over 400 °C, the combustion reaction was able to be generated in pellet state. Without preheating, the combustion reaction was possible by Ti02 addition. The optimum condition in this system was the molar ratio of Si02:Ti02:Al:C=2.5:0.5:4:3.1. INTRODUCTIONCeramics have demonstrated a capability as a cutting tool, especially in competition with WC-Co cermets (ceramic-metal composites) as inserts for metal turning and milling operation. The advantage of ceramics compared with carbides is retention of high hardness, strength, and chemical inertness to temperatures in excess of 1000 ·c . This allows use of the ceramics at much higher machining speeds than can be tolerated by carbides. However, the ceramics have lower toughness than the carbide materials, and have only been used successfully in the limited operations of turning and milling. There are several classes of cutting tools. The addition of TiC or PSZ, or both, and reinforcement with SiC overcame the poor fracture toughness and thermal-shock resistance that limited Al203 use in the past [1]."

Jan 1, 1998

By Akira Yazawa

In the field of pyrometallurgy, the equilibrium evaluation has recently become easy by use of thermodynamic software, but it is strongly desired to estimate the amounts of non-equilibrium minor components to simulate practical processes. However, simple physico-chemical technique can not be applied to evaluate practical non-equilibrium components for many reasons. As an engineering solution for postulated equilibrium system, the activity coefficient is modified and introduced as the simulation parameter referred to as the "adjustment coefficient." This modified thermodynamic calculations were adopted to various sulfide roasting processes where many solid phases are participating and the system is not necessarily in equilibrium. Successful simulation was realized by assigning suitable adjustment coefficients for minor components which form a pseudo solid solution in the calcine. Some examples from sulfation roasting and dearsenizing roasting were discussed. In the smelting system, the loss of copper in slag is caused by equilibrium and non- equilibrium reasons, that is, chemical dissolution and entrainment of copper in slag. The total copper content of slag was simulated by use of the adjustment coefficient for entrained copper.

Jan 1, 1998

By Li Xi

This paper describes how a back-propagation neural network is built for predicting the properties of engineering materials from their other properties, compositions or processes. A predicted result of the impact toughness of a 12Cr-2Ni-1.5Mo stainless steel from its tempering temperature is presented. Furthermore, the combination of this neural network for prediction is able to supplement the unpredictability of the expert system outside its domain of expertise. An integrated system may perform more intelligently and solve more complex problems as well as human expert, in some case even better.

Jan 1, 1992

By G.A Subagyo

The condition of slag in a pyrometallurgical reactor is vital to ensuring control of the process. A new technique based on multivariate image analysis (MIA) of digital images has been developed to provide an online measurement of important slag characteristics, such as the presence of exposed metal, the presence of solid phases, and temperature. This paper shall describe the technique and provide some results from analysis using industrial plant data.

Jan 1, 2003

By Seong-Jong Kim

The formation behavior and corrosion characteristics of anodic oxide films on pure Mg and Mg-AI alloys were investigated focusing on the effects of anodizing potential, Al content, temperature and NaOH concentration. Pure Mg and Mg-AI alloys were anodized for 10 min at 3, 10, 40, and 80 V in NaOH solutions. Mg(OH)2 was generated by an active dissolution reaction at the surface of the specimen and the product was affected by temperature while MgO generation increased with NaOH concentration. Moreover, the current density after anodizing for 10 min at a constant potential decreased with increasing AI content in Mg-AI alloys,

Jan 1, 2003

By Chikabumi Yamauchi, Mitsuru Tanahashi, Toshiharu Fujisawa

"Thermodynamic properties of impurities in molten silicon are of prime importance in developing economical production methods of solar grade silicon. In the present research work, thermodynamic properties of boron, the most difficult element to remove from molten silicon, were measured by chemical equilibration techniques at 1723 and 1773 K. Activity coefficients and self-interaction parameters of boron in molten silicon were determined by equilibrating the melt with solid BN under controlled nitrogen partial pressures. Interaction parameters between boron and nitrogen in molten silicon were also determined by equilibrating the molten Si-B alloys with solid Si3N4• Based on the data obtained, the stability diagram of the Si-B-N system was established.IntroductionPhotovoltaic power generation using a silicon solar cell is expected to be the most promising energy source, because it is inexhaustible, cleaner and more safety than conventional energy sources, such as thermal or atomic power generation. At present, expensive off-grade silicon for semiconductor (SEG-Si) is used for a solar cell production. However, if a large-scale photovoltaic energy conversion using silicon solar cell comes into wide use in the near future, silicon will be sure to be in short supply for the cell. Therefore, a development of a new large scale process for solar grade silicon (SOG-Si) production is definitely necessary, which can remove contained impurities from silicon.Among the impurities contained in silicon, boron is one of the most difficult ones to remove by a zone melting or an unidirectional solidification, because its segregation coefficient in silicon is close to unity (0.8). In addition, boron behaves as a p-type silicon semiconductor dopant and, therefore, its content in SOG-Si must be severely controlled. Although some attempts to remove boron by various metallurgical methods have been carried out [I -4], quantitative analysis has not been made due to lack in the information on the thermodynamic properties of boron in molten silicon. From this view point, the activity of boron in molten silicon was determined in the present study by chemical equilibration techniques at 1723 and 1773 K."

Jan 1, 1998

By Thomas J. Keefe, O&apos

The effects of cobalt, B-naphthol, glue and antimony on the polarization behavior of zinc sulfate electrolyte were investigated. It was found that B-naphthol was beneficial in reducing the detrimental effects of cobalt while antimony and excess glue were each harmful. Since the nu cl eat ion over potential was insensiti1ve to coba1t, other regions of the polarization curve were used to indicate electrolyte balance. The low? current density area occurring in the reverse or anodic sweep direction was? often an indicator when an ?unstable condition existed. The two parameters evaluated were the degree of inflection in the polarization curve in the low current density region during scanning and the rate of current rise observed when the sample was potentiostated at -0.781 Volts (SHE). Using this technique, a two-additive system was shown to be desirable to control cobalt and antimony containing electrolytes. The structure of the deposits was examined using scanning electron microscope techniques.

Jan 1, 1985

By James J. Komadina, Robert R. Beebe

"Heap leaching of gold ores has enjoyed wide acceptance in the arid and semi-arid regions of the western U.S., Australia and South America. There are areas, however, where cold weather or excessive precipitation can limit the usefulness of heap leaching. Even in Nevada difficulties can be encountered which call for special operating procedures.The paper discusses the general climatological limitations and some of the techniques used to extend heap leaching into colder conditions. A case history of the Cripple Creek and Victor Gold Mining Company operation in Colorado examines 'valley-fill"" technology as an ideal cold-climate solution, where topographical conditions permit.AcknowledgementsThe authors gratefully acknowledge the management of Independence Mining Company for their permission to present this paper. The contributions of Golder Associates; Pikes Peak Mining Company Environmental Affairs Department staff, and the Colorado Department of Mines and Geology were all invaluable in successfully concluding this project.BackgroundWhen heap leaching of oxidized gold ores was introduced in the rnid-1970s it was aimed at large tonnages of low-grade material which could not, in general, be developed via conventional milling. Normally, the reasons for this were economic rather than technical: capital and operating costs for milling were simply too high. At first, grade was almost the only criterion, but deposits too small to justify milling were also potential targets for heap leaching.Renewed interest in gold was centered in the western United States and Australia, where exploration for milling-grade deposits had never really died. When heap leaching came along, it was in these areas that the first developments took place. Coincidentally, these same areas were favorable for heap leaching: climates were temperate for most of the year and competing land uses were limited. Even so, in the western United States in particular, winter temperatures were low enough to complicate operations. Precipitation was less a problem, although heavy snowfalls could periodically interfere as well."

Jan 1, 1997

By K. S. Kumar

FLS miljø, Inc. markets, designs and supplies particulate collection devices for dusts, fumes, and mists; In this paper, the application of both wet and dry electrostatic precipitators (ESPs) in smelting, and roasting plants is discussed.

Jan 1, 1998

By Larry M. Southwick

There is much ongoing work in research and development of new processes for the recovery and recycling of met.a.ls and other materials from various waste and scrap streams. Commercialization of such new technologies requires the bringing together and successful execution of a considerable effort involving a variety of activities. These include process conceptualization, research and development, detailed design and construction, and then plant startup and operation. Processes evolve through all of these steps by engineering due diligence, making objective and critical analyses of results, and troubleshooting processing steps to, hopefully, arrive at a sequence that has the best chance to succeed operationally and economically. After a summary review of the above steps, several processes will be described in more detail that provide mostly successful examples of the above procedures. Finally, some observations will be made on areas that will become critical in the near future to the success of new processes for wastes and residues.

Jan 1, 2000

By V. Jiricny

There is a growing need to process galvanized steel scrap from automobiles, etc., in order to remove the zinc coating that otherwise causes problems in remelting of the scrap in electric arc furnaces. One approach that has moved to the pilot plant stage is that of Metal Recovery Technologies, Inc., of East Chicago (MRI). That company leaches the zinc fiom the scrap with a sodium hydroxide solution. The leached and washed scrap can then be returned to the steel industry. What is left is a sodium hydroxidelzincate solution which must be processed to recover the zinc and the NaOH. Presently, this is done by MRI using electrodeposition on planar electrodes at moderate current density and the resulting zinc is in the form of fine powder which is hard to process into, say, zinc for galvanizing. MRI has supported an investigation of a novel electrode, the spouted bed electrode (SBE), for zinc electrodeposition. In laboratory cells, zinc particles with low porosity have been grown up to 3mm in size. Microanalysis of the deposited zinc showed low level of impurities. DC energy consumption values were usually in the range of 2-2.5 kWg which is well below the energy consumption of the existing cells (and of present-day cells for electrowinning from acid sulfate electrolytes). These results were achieved at current densities (few thousand A/m2) that are much higher than possible with conventional electrodes. Discussion is provided of the scale-up of the cell to a commercial scale.

Jan 1, 1998

By Jaeheon Lee

Gold-copper alloys are shown to form during the cementation of gold on copper in a solution containing 0.25M [S2O32-] at 25oC. The alloy composition is strongly dependent on the initial Cu:Au ratio in solution and ranges from Au3Cu to AuCu3. XPS results for Au, Cu, S, and O are reported as a function of depth through an entire deposited film with an initial solution containing 20 ppm [Au] and 30 ppm [Cu]. The deposit contained about 20 atomic % gold and was predominantly Cu3Au. Underpotential deposition (UPD) theory is discussed as a mechanism for explaining the formation of these alloys. Several other systems that produce alloys during contact reduction/cementation are also discussed.

Jan 1, 2003

This symposium is dedicated to the lifetime achievements of Professor H.Y. Sohn. It covers the scientific fields, processing routes and investigation techniques in which Prof. Sohn has worked during his career and is based in the equally important three topical areas: Principles, Technologies, and Industrial practice. Professor Sohn was General Chair of the very first TMS Fall Extraction and Processing Symposium in 1983 in San Francisco which led to the Annual such symposia as this International symposium. Furthermore, the theme of that symposium was sulfide smelting, which is also included in this symposium. [ ] Professor Sohn was born in a beautiful dynastic capital Kaesung, Korea on August 21, 1941. He received his B.S. degree in 1962 from Seoul National University, M.Sc. in 1966 from the University of New Brunswick, Fredericton, N.B., Canada, and his Ph.D. degree in 1970 from theUniversity of California at Berkeley all in Chemical Engineering. After working as a Research Associate at the State University of New York at Buffalo and as a Research Engineer at Du Pont?s Engineering Technology Laboratory, Dr. Sohn joined the Department of Metallurgical Engineering at the University of Utah in 1974 and currently holds the ranks of Professor of Metallurgical Engineering and Adjunct Professor of Chemical Engineering.

Jan 1, 2006

By Gabriel Riveros

Fire refining of copper consists of two stages copper oxidation and copper reduction. Very frequently the capacity of the anode furnace is determined by the rate of copper reduction, The analysis of factors affecting the rate of the oxygen reduction from a liquid copper with solid carbon or injected hydrocarbons pointed out the role of the mass transfer in a liquid copper in final stage of the reduction. Experimental results of copper reduction with graphite and injected natural gas in laboratory-scale crucibles showed two stages of the reduction process with a sharp change of the controlling mechanism. The estimated dynamic surface area of gas bubbles based on the measured bubble frequency and the gas flowrate allowed for the determination of the reaction constant as a degree of the partial pre-combustion of the air/natural gas mix. The variation of the used reductant as a function of the oxygen concentration and temperature has been evaluated based on the determined kinetic model. The intensification of copper reduction in fire refining has been discusses on the basis of obtained kinetic data and analysis of various factors determining the time of reduction.

Jan 1, 2003

By Nils Lippmann, Ulrich Weber, Siegfried Schmauder, Jr. Mishnaevsky

"A computational approach to the optimization of fracture resistance of multiphase materials (here - high speed steels) by varying their microstructure is presented. The main points of the optimization of steels are as follows: (1) development and verification of the model: numerical simulation of crack initiation and growth in real microstructures of steels, (2) computational experiment: simulation of crack growth in different idealized quasi-real microstructures and (3) the comparison of fracture resistances of different microstructures and the development of recommendations to the improvement of the fracture toughness of steels. Numerical simulations of crack growth in real microstructures of steels and different idealized carbide distributions are carried out. On the basis of the simulations, recommendations for the improvement of high speed steel microstructures are given. It is shown that the fracture resistance of the steels is much higher for the fine than for the coarse version of the same type of microstructures.IntroductionThe purpose of this work is to develop an approach to the optimal design of multiphase materials on the basis of numerical simulation of their behaviour under mechanical loading. We suggest here the following strategy:1. Collecting input data for the simulations: taking a micrograph of a microstructure, and determining mechanical properties and failure conditions of the material constituents [1, 2],2. Simulation techniques and assumptions are tested for a real microstructure of the material: crack growth in a real microstructure is simulated and then compared with the experimental data,3. Computational experiments: different microstructures of materials are tested in the numerical model under the same loading conditions. The calculated service properties of the different microstructures are compared, and recommendations are developed. As differentiated from the ""real"" experimental techniques, the computational experiment is much cheaper and not labor- and time-consuming."

Jan 1, 2001