By M. J. Pool, with Appendix by Larry Kaufman, R. W. Krenzer

Thermodynmic properties of the Cu-Mn system have been deterrrzined in the temperature range 973" to 1273°K by measuring the vapor pressure of manganese in equilibrium with alloys of compositions varying from 0.13 to 0.91 rnole fraction manganese using the Knudsen effusion technique. Activities of manganese calculated from the measured vapor pressures show large positive deviations. Calculated heats and entropies of mixing are positive with a maximum occurring at approximately 0. 7 mole fraction manganese. ThE investigation of thermodynamic properties of binary systems involving transition metals is of considerable interest at the present time. The incomplete subvalency electron levels of transition metals lead to unusual behavior in some alloys, and considerable information can be obtained by determining the thermodynamic characteristics of these systems and relating the thermodynamic behavior to observed physical properties. The Cu-Mn system, shown in Fig. 1,' provides an example of an alloy system in which the determination of the equilibrium phase diagram and various physical properties has received considerable attention, but very little work has been done on measurement of the thermodynamic properties. Elemental copper and manganese have comparable electronegatives, atomic sizes, and cohesive energies, but differ in crystal structure. They form a continuous series of solid solutions only at high temperatures and the structure varies in a continuous manner from fcc at the copper-rich end to fct at the manganese-rich end.' The purpose of this investigation was to measure the vapor pressure of manganese over a series of Cu-Mn alloys and from these values determine the thermodynamic properties of the binary system. Vapor pressure measurements were made in the temperature range 973" to 1273"K, remaining within the solid-solution region for each alloy studied. EXPERIMENTAL PROCEDURE The relative thermodynamic properties of solid Cu-Mn alloys were determined from vapor pressure measurements by means of the Knudsen effusion tech- nique. Several discussions of the theory can be found in the literature. In the case of copper and manganese, it is assumed that manganese is the only component subliming, so the vapor pressure of manganese over the various alloys can be determined directly by measuring the weight loss of the effusion cell. This is a valid assumption since the vapor pressure of manganese is about four orders of magnitude higher than the vapor pressure of copper in the temperature region of interest. The vapor pressure of manganese over the alloys at any given temperature is then related to the weight loss of the effusion cell per unit area per unit time. An upper limit of 1.5 x 10"s has been measured for the ratio of polyatomic to monoatomic molecules for manganese vapor in equilibrium with solid manganese at 1180°K, so it was assumed that manganese vapor is monoatomic. The effusion cells, fabricated from high-purity alumina, are 26 mm high, 18 mm OD, and have a wall thickness of 1 mm. Three different sized holes of 2.03, 2.54, and 3.18 mm diam were drilled in the lids from the inside face to minimize chipping, and the lids were then slip-cast onto the cells to provide a gas-tight seal. Alumina was selected for this particular application both because of its resistance to thermal shock and reaction with manganese vapor. In the ideal case, the orifice of the effusion cell should have a knife edge so that effusion through the orifice

Jan 1, 1970

Jan 11, 1951

By S. R. Zimmerley, John Gross

A survey of the status of ore dressing in 19231 placed particular stress on the need of research in the crushing and grinding of ore, especially on the need for a method of measuring the surface of the products obtained in crushing and grinding and for fundamental data on the law of crushing, in order that intelligent conclusions may be drawn from actual crushing or grinding experiments. There has been no satisfactory means of determining the surface of crushed products. The results have been judged entirely by the amount of the various sizes produced, based on sieve sizing for particles above 74 microns in size and on microscopic measurement or elutriation for particles below 74 microns, a method which could give only a general idea of what had been accomplished. The fact that the long controversy between the followers of Kick and of Rittinger has resulted in no accepted conclusion is evidence of the need for fundamental data on the crushing law. Some Methods of Measuring Surface of Particles A dissolution method was used by Wolff to measure surfaces of glass powder. A mixture of sodium carbonate and sodium hydroxide was the solvent and the amount of glass dissolved in two hours from the powder was compared with that dissolved from a glass plate.2 Lately Herbert F. Kriege has used the dissolution method in determining surface of calcite and limestone.3 Dr. Geoffrey Martin and his coworkers in England have also used a dissolution method to determine surface on quartz. They compared the amount of quartz dissolved from the sample in one hour by a hydrofluoric acid solution with the amount dissolved from a measured quartz

Jan 1, 1930

By William M. Barret

In order properly to evaluate the data related to geomagnetic surveys, it is highly desirable to have all the available information concerning the magnetic properties of the involved media. This is true of surface as well as subsurface formations and becomes of increasing importance as advancement in instrumental and interpretative technique permits the analysis of relatively slight magnetic reflections of buried masses. Since the magnitude and areal distribution of the usually complex resultant magnetic field at the surface of the earth is a function of the susceptibility1 of the involved matter, it necessarily follows that susceptibility determinations will afford valuable data for geophysical correlation. The present method was developed to meet the need for routine analysis of specimens in the geomagnetic laboratory where it was felt that general utility, ruggedness, ease of manipulation and reproducibility of results were of greater importance than extreme sensitivity. Electric Circuits The electric circuits are illustrated diagrammatically in Fig. 1. Current from the battery, B, passes through the variable resistance R1, reversing switch S1, double-break key K1 to switches S2 and S3. From S2 it flows through variable resistance R2, ammeter A2, to the primary coils of the fixed mutual inductance Mf and variable mutual inductance M,. . From S3 it passes through variable resistance R3, ammeter As, to the primary winding of the fixed mutual inductance MI, which is designed to receive the test sample. The ballistic galvanometer2 or fluxmeter3 G is connected in the circuit containing the double-break key

Jan 1, 1932

By Jonathan S. Jackson, Bayne B. McMillan, W. Joseph Schlitt

Various dump leach models have been developed by Kennecott, and these are reviewed with an eye toward production forecasting. Some of the models have been bated on first principles, utilizing the chemistry and physics of dump leaching. While providing considerable insight into the leaching process, these have proved to be too cumbersome for use in estimating production. Other models have been based on a declining leach rate for a single block of waste. These permit good short-term projections of solution grades and production, but are inflexible with regard to changes in mining parameters because the trends are based only on historical data. Therefore, a simple and flexible computer model has been developed to aid in leach production forecasting and to provide a tool for assessing the impact of different mining plans on leaching. This program, LEACH, is based on annualized blocks of waste; input parameters are described and examples of its use are given.

Jan 1, 1980

By J. D. Forrester, Erich Sarapuu, T. C. Cheasley

RANKING high in the nation's wealth of natural resources, readily available liquid and gaseous hydrocarbons are nevertheless falling steadily in supply, while industrial requirements for hydro- carbon compounds are greater today than during the peak period of World War II. Theoretically, several processes will increase the future supply of liquid and gaseous fuels, but the practical application of these methods depends on two controlling factors: 1-that enough carbon- bearing material be available to warrant industrial exploitation, and 2-that the given process be physically, chemically, and economically applicable. With regard to the first factor, the Western Hemisphere is fortunately well supplied, see Table I.

Jan 9, 1954

By Dozier Fircley

SOME nonmetallic minerals and their products, such as portland cement, common brick and hollow tile, sand, gravel, crushed rock, vitrified salt-glaze clay pipe, and the like, are a necessity in every community. They are mineral in nature but the establishment of plants for their production is usually a local and elementary problem. Yet it is probable that an economic study of the problem in every locality will show that such nonmetallic mineral commodities are not always obtained in the most economical way, or in the best quality. Other nonmetallic minerals are of such value that they may be shipped for long distances and sold in sufficient quantities to establish prosperous commercial ventures. Among these are phosphates, barium compounds, borates, nitrogen compounds, magnesium compounds, sulfur, asbestos, and potash. Success in marketing such products depends on quality, production cost, transportation, and similar conditions.

Jan 1, 1932

By S. J. Matas, R. F. Hehemann, R. H. Goodenow

The hot-stage metallographic method has been employed to determine radial growth rates of upper and lower bainite. Lower bainite appears to grow as individual plates that increase in both length and thickness while upper bainite grows as sheaves of closely spaced plates or needles. A discontinuity in the temperature dependence of the growth rate appears to be associated with the transition from upper to lower bainite and stepped quenching experiments suggest that lower bainite will not continue to grow when the temperature is raised to the upper range. Thus, a single process does not appear to control the growth of both upper and lower bainite. A tentative model based on the forces acting on a dislocation interface is proposed to account for the slow growth of bainite. It has been recognized since the early studies of Davenport and Bain that a close relationship exists between the martensite and bainite transformations in steels. However, diffusion of carbon during the transformation has lead to considerable controversy concerning the reaction mechanism.1-7 Many studies4,5,7-9 have emphasized the structura and kinetic aspects of the bainite reaction and, in particular, the difference observed between the two forms of bainite—frequently termed upper and lower bainite. A kinetic difference between the two types of bainite has been revealed in the activation energy determined from the overall reaction;4,5 however, many difficulties arise in an interpretation of these activation energies since a number of temperature dependent factors contribute to the kinetics of the overall reaction. The displacive surface relief10 accompanying the bainite reaction permits a separation of the nuclea-tion and growth contributions to the reaction and allows the kinetics of the growth process to be examined. Several investigations of this type have been conducted; however, they have been restricted to the low temperature range.3'6'11 Here, bainite plates are observed to grow slowly in both length and width. The present investigation extends such studies to include the upper bainite range. MATERIALS AND PROCEDURE Materials. The composition of the steels studied in this investigation are presented in Table I. The range of composition permitted a study of the effect of carbon content on the growth rate of upper bainite in the 9 pct Ni steels and consideration of both upper and lower bainite in the higher carbon steels. These steels were received as hot-rolled rounds and were forged to approximately 1/2 in. thick plates for preparation of metallographic specimens. In order to produce an essentially zero carbon steel, Steel A was decarburized in wet hydrogen at 1550°F for 15 days with the result tabulated as Steel AD. Experimental Procedure. In order to study the slow growth of the displacive transformation product, a commercially available Leitz hot stage was modified to permit heating of the specimen by its own resistance in a manner similar to that employed by other investigators.6 The furnace chamber was maintained at a pressure of 2 to 3 X 10-5 mm Hg prior to austenitizing at 2000° ± 12° F for 5 min. Samples could be cooled from the austenitizing to the transformation temperature in approximately 15 sec and the progress of transformation was recorded with a 9 cm by 12 cm single frame camera or a 16 mm movie camera. RESULTS AND DISCUSSION Growth Characteristics. The general growth characteristics observed in this investigation were analogous to those reported previously.3,6,11 Typical growth sequences for the high temperature and low temperature forms are illustrated in Figs. 1 to 5. In both temperature ranges, bainite plates increase in length at slow, temperature dependent rates until interrupted by a grain boundary, another plate, or

Jan 1, 1963

By J. M. Roberts, N. Brown

The stress-strain behavior of zinc single crystals was measured over a strain range of 10-6 to 10-2. The phenomenon of macroyielding was observed in detail and plastic strains were detected at almost zero-stress. Closed hysteresis loops were observed during loading and unloading in the strain region of about 10-5. From the hysteresis a frictional stress on the dislocation of about 6 psi was obtained. A preliminary analysis indicates that impurities are primarily responsible for the friction. Nonelastic Strains as much as 10 -4 were recovered depending on the amount of prior deformation. Part of the recovered strain occurs instantaneously upon unloading and the remainder occurs at zero stress. The time dependence of the recovered strain was measured. THIS investigation is concerned with the details of plastic deformation preceding the ordinary yield point as measured with the usual strain sensitivity of about 10-4. The approach leads to internal friction observations in the hitherto neglected frequency range below 10-1 cycles per sec. It is believed that if the phenomenon of macroscopic yielding is to be understood, then the stress-strain curve in the neighborhood of the macroyield point should be greatly magnified. It may then be possible to determine whether macroscopic yielding is a unique event or whether it is a process which begins gradually at a lower stress. In the case of low-carbon steel a unique event obviously occurs at the macroscopic yield point as indicated by a drop in the load, but copper appears to exhibit a gradual transition from the elastic to the plastic state. In zinc the yield point is rather abrupt although the data indicates that some plastic deformation precedes large scale yielding.' One of the purposes of this investigation is to determine whether there is an abrupt transition from the preyield microstrain region to the region of macroscopic deformation. Such a rapid transition would support the concept that there is a critical stress for yielding. The concept that yielding is a unique event associated with such phenomenon as activating a Frank-Read source, freeing the dislocation from solute atoms, dislocations cutting through dislocations, or dislocations moving freely by one another, has been expounded widely on theoretical grounds. It is hoped that highly sensitive measurements of strain in the neighborhood of the macroscopic yield point will shed some light on the event known as the "Yield Point". EXPERIMENTAL METHOD 1) Specimens—High-purity zinc was cast into spherical graphite moulds in air and grown into spherical single crystals by the Bridgman method under a positive pressure of Argon gas. Spectro-graphic analysis of cleaved sections from four crystals showed a purity of 99.994 pet Zn. The specimens were acid machined with an 1/8 in. gage section in a form similar to those used by Parker and co-workers.2 Bausch type grips were fastened to the specimen by Epon VI adhesive. The specimens were oriented so that only [1120] (0001) slip occurred. Fig. 1 shows two of the specimens in the grips. Prior to each test, the gage section of the specimen was given a concentrated HNO3 chemical polish followed by alcohol rinsing and air blast drying. 2) Test Method- The shear tests were performed on an Instron testing machine and the experimental set-up was made very "hard". Strain could be measured to a sensitivity of 10 -6 by means of a capacitance gage extensometer. The design and calibration of this type of extensometer to measure microstrain, as applied to pure shear and tensile tests of metals, will be the subject of a separate paper—therefore, only a brief account will be presented here. The method essentially consists of attaching a

Jan 1, 1961

By T. B. Massalski, C. S. Barett

THAT metals and alloys of the body-centered-cubic structure tend to become unstable at low temperatures is so nearly universal that any exceptions are worthy of special attention. Studies of the exceptions may disclose unrecognized examples of metastability or may shed light on the nature of some of the factors that stabilize the body-centered-cubic phase. Among the structurally analogous body-centered-cubic 3/2 electron compounds, the ß-phase in the Cu-Zn system deserves further attention for, although this phase is known to undergo partial mar-tensitic transformation on cooling below room temperature to the temperature of liquid nitrogen when the composition is less than about 42 wt pct Zn, it does not transform on cooling .when there is more than this amount of zinc present.1-4 The present authors recently found that an alloy containing 48.35 wt pct Zn could be transformed, however, if deformed severely at room temperature or lower temperatures.V his discovery led to the suggestion that the jerky flow of ß-brass single crystals6 and some of the unusual temperature variations of the yield strength and hardness are due to strain-induced transformation during the tensile tests. The present investigation is an extension of that work to cover the entire available range of compositions of Cu-Zn ß-phase alloys and certain interesting compositions of the ß-phase in the Cu-Zn-Ga system. Particular attention is given to the structure of the transformation product resulting from cold work, which is found to vary with alloy composition, and to the temperature range in which transformation can be induced in the various alloys. The composition limits of the body-centered-cubic phase in the Cu-Zn system, based on a recent review by Raynor7 and the precision determinations of Beck and Smith: are shown in Fig. la; in the ß region the alloys are disordered and in the ß region they are ordered. The rate of ordering is so rapid that a high degree of order is found in any of these alloys immediately after quenching. Experimental The nine binary and four ternary alloys of this investigation were prepared from cathode copper (99.99 pct purity), electrolytic zinc (99.99+ pct), and gallium (99.98+ pct). All alloys were cast in transparent Vycor tubing, homogenized at temperatures between 800° and 890°C, and quenched in water. Ternary alloys were cast in small amounts (-5 g) to predetermined compositions to fall along a line of constant electron concentration in the ternary system. Changes of weight during the casting operation of the ternary alloys were not greater than 1 part in 2500 from the intended nominal weights and therefore their compositions were accepted without chemical analyses. All binary alloys were cast in larger amounts (100 to 150 g), homogenized, and hot rolled after preheating to 800°C. The central portion of the rolled strip of each alloy was annealed for eight days and quenched in brine. All binary alloys were analyzed chemically. The compositions, heat treatments, and metallographic appearances of all alloys are tabulated in Table I. Various samples were subjected to heat treatment or cold work at several temperatures and were then examined metallographically or by means of X-rays. Specimens about 6x6x3 mm in size were examined metallographic ally to confirm the presence of the ß-phase after quenching. Cold work was introduced by fastening each sample between two pieces of steel, cooling the assembly to the desired temperature, and transfering it rapidly to a vise where moderate or severe compression was immediately applied. Cold working at liquid helium temperature was done by a chisel-shaped tool mounted on an X-ray spectrometer, described elsewhere.% A!! metal-

Jan 1, 1958

By S. R. Maloof, W. R. Mitchell, J. A. Mullendore

Preliminary experimental evidence is presented to show that the metallic impurities aluminum, iron, and silicon, and beryllium oxide as found in commercially pure hot-pressed beryllium powder can be reduced to lower Concentrations by Zone -Purification techniques. The reduction in the concentration of aluminum to extremely low levels (10 PPm) is noteworthy, since earlier work demonstrated that aluminum is a major factor contributing to the hot-tearing of beryllium during fusion welding. On the basis of present findings, a method is suggested for producing beryllium metal of improved weldability. EXPERIMENTAL research now being conducted on the purification of beryllium indicates that several of the metallic impurities and beryllium oxide can be reduced to lower concentrations by employing standard horizontal zone-refining techniques. For the preliminary work, commercially-pure hot-pressed beryllium having a purity of 97.84 pct was used. The chemical composition is given in Table I. The hot-pressed beryllium was machined into bars 5/8 by 5/8 by 4 to 6 in. in length. Beryllium-oxide boats which had been conditioned by prior heating in a vacuum of 10"5 mm of Hg at 1100°C for 3 hr were used to hold the beryllium while it was zone melted. The boat with its charge, along with a smaller beryllium-oxide boat containing scrap beryllium to be used for gettering purposes, was loaded into a quartz tube and evacuated to 10-6 mm of Hg. Alter alternately evacuating and flushing three times with purified argon, the furnace tube was backfilled to a pressure of 1/6 atm of A and sealed off by means of a vacuum-tight stopcock. It was then removed from the pumping equipment and mounted on the traveling carriage of the zone-refining apparatus. Heating was accomplished with a 10 kw 450 kc induc- tion heating unit using an induction coil consisting of two turns of 3/16-in. diam copper tubing. Before starting to zone melt, the atmosphere in the furnace tube was gettered by heating the scrap beryllium in the smaller boat to above its melting point and holding at temperature for several minutes. The carriage was then shifted so as to locate one end of the beryllium ingot in the large boat within the induction coil. A molten zone approximately 3/4 to 1 in. was established by loading directly into the ingot. The molten zone was moved very slowly along the length of the ingot. Before each pass was made the procedure for evacuating, flushing, and backfilling, and so forth was repeatedI' Speeds of 1 1/2 and 3 in- per hr were used with up to twelve zone passes. The appearance of a typical zone-refined ingot is shown in Fig. 1. After zone refining, the grains in the ingot appear to be elongated in the direction of zone travel, whilst before, they are essentially equi-axed. A microexamination revealed the presence of a network in the beryllium grains as seen in Fig. 2. Laue spots in back reflection pictures taken of the sample were not sharp, indicating the presence of subgrains in the structure. As can be seen, however, many of the network boundaries cross beryllium grain boundaries. It has been shown by Martin and Moore1 that beryllium solidifies as a bcc structure which then transforms to the hexagonal structure at about 1250oC.It is believed that the observed network is merely the outline of the bcc structure which formed from the melt and are not subgrain boundaries. In order to eliminate surface contaminants, approximately 1/16 of an inch of material was removed from the outer skin of each ingot after zone refining.

Jan 1, 1962

By E. R. Parker, D. L. Martin

In a previous paper one of the authors observed that the rate of cooling from the anneal prior to testing greatly influenced the life of copper under sustained load at 200°C. Furnace-cooled bars of oxygen-free copper (with and without silver) had a life four to twenty-five times that of the water-quenched specimens. The addition of 0.054 per cent silver to the oxygen-free copper increased the life at a stress of 20,000 lb. per sq. in. from about 2 hr. to 50 hr. Fractures in these bars were intercrystalline. An explanation was advanced to account for the profound influence of cooling rate on the rupture properties at 200°C. The suggestion offered was that at the high annealing temperature the minor constituents are distributed at random. By water quenching, this condition is maintained at room temperature, whereas furnace cooling permits some segregation at the grain boundaries. The higher concentration of the minor constituents in the grain boundaries results in a. strengthening, so that a longer life at a given stress and .temperature results. Small amounts of cadmium or manganese have also been found to increase the life of copper at 200°C., and to a much greater extent than silver.2 The increase in the long-time strength of copper resulting from small additions of cadmium or silver appears to be related, indirectly at least, to the higher softening temperatures of such alloys. The elements, such as silver or cadmium, which greatly increase the rupture life of copper also cause large increases in the softening temperature. As little as 0.05 per cent of cadmium or silver is sufficient to raise the softening temperature more than 100°.3,4 The effects of cooling rate and of minor constituents on the rupture properties are of considerable fundamental as well as practical interest; therefore a more detailed study of their nature was conducted and is reported in this paper. Experimental Procedure Materials The materials studied in this investigation may conveniently be classified in two groups: one consisting of a wide variety of commercial coppers, and the other composed of special high-purity, laboratory-prepared coppers. The commercial materials were tested to determine whether or not the effect of cooling rate occurred with all coppers, whereas the high-purity coppers were investigated in order to establish a basis for evaluating the effect of minor constituents on the rupture properties. In Table I are given the analyses of the coppers tested. The samples I to 6 are commercial materials and were obtained for the most part from stock supplies.*

Jan 1, 1944

By D. L. Martin, E. R. Parker

In a previous paper one of the authors observed that the rate of cooling from the anneal prior to testing greatly influenced the life of copper under sustained load at 200°C. Furnace-cooled bars of oxygen-free copper (with and without silver) had a life four to twenty-five times that of the water-quenched specimens. The addition of 0.054 per cent silver to the oxygen-free copper increased the life at a stress of 20,000 lb. per sq. in. from about 2 hr. to 50 hr. Fractures in these bars were intercrystalline. An explanation was advanced to account for the profound influence of cooling rate on the rupture properties at 200°C. The suggestion offered was that at the high annealing temperature the minor constituents are distributed at random. By water quenching, this condition is maintained at room temperature, whereas furnace cooling permits some segregation at the grain boundaries. The higher concentration of the minor constituents in the grain boundaries results in a. strengthening, so that a longer life at a given stress and .temperature results. Small amounts of cadmium or manganese have also been found to increase the life of copper at 200°C., and to a much greater extent than silver.2 The increase in the long-time strength of copper resulting from small additions of cadmium or silver appears to be related, indirectly at least, to the higher softening temperatures of such alloys. The elements, such as silver or cadmium, which greatly increase the rupture life of copper also cause large increases in the softening temperature. As little as 0.05 per cent of cadmium or silver is sufficient to raise the softening temperature more than 100°.3,4 The effects of cooling rate and of minor constituents on the rupture properties are of considerable fundamental as well as practical interest; therefore a more detailed study of their nature was conducted and is reported in this paper. Experimental Procedure Materials The materials studied in this investigation may conveniently be classified in two groups: one consisting of a wide variety of commercial coppers, and the other composed of special high-purity, laboratory-prepared coppers. The commercial materials were tested to determine whether or not the effect of cooling rate occurred with all coppers, whereas the high-purity coppers were investigated in order to establish a basis for evaluating the effect of minor constituents on the rupture properties. In Table I are given the analyses of the coppers tested. The samples I to 6 are commercial materials and were obtained for the most part from stock supplies.*

Jan 1, 1944

By E. A. Gulbransen, K. F. Andrew

Thermodynamic information on the solubility of hydrogen in exothermic metals is limited. Thus, the overall solubility decreased as the temperature rose, which suggests the heat of solution of hydrogen in the metal is negative; yet the terminal solubility in the metal phase increased, which suggests an endothermic reaction. A thermodynamic analysis, therefore, was made of the several equilibria involved when hydrogen dissolved in the metal. Equations were derived expressing the solubility, terminal solubility, and decomposition pressures of hydrogen in terms of the heat, entropy, and free energy of solution of hydrogen in the given phase. The relations between the thermodynamic functions for the a-zirconium and 8-hydride phase were developed. The thermodynamic quantities were determined experimentally by the measurement of the decomposition pressures over a broad composition and temperature range. Two new methods of analyzing the experimental data were developed for determination of the terminal solubility. STUDIES', ' of the impact strength of zirconium at room temperature indicated that small quantities of hydrogen, of the order of 10 parts per million, embrittles the metal. Micrographic' and X-ray diffraction' studies showed this embrittlement to result from the precipitation of a second phase upon slow cooling. These studies suggested that the terminal solubility of hydrogen in the metal phase increased with increase of temperature. This behavior appeared to contradict the effect of temperature on exothermic hydrogen occluders such as zirconium. For these metals, the solubility of hydrogen should decrease with increase of temperature. Before these facts could be understood, a thorough analysis of the several equilibria was essential. It was the purpose of this paper to consider the several equilibria involved when hydrogen was reacted with zirconium from both the theoretical and experimental points of view. Since the overall solubility of hydrogen in the metal has been considered by a number of workers, it was proposed to study the composition range 0 to 6 atomic pct H in detail. Literature Schwartz and Mallett' determined the terminal solubilities of hydrogen in the metallic phase from diffusion studies. They extrapolated concentration-penetration curves to the boundary between the solid solution phase and the hydride phase at the surface. Their results showed values of 2.6 atomic pct at 400°C and 5.2 atomic pct at 500°C. Extrapolations of the data to room temperature suggested very low values for the terminal solubilities. This study confirmed the hydrogen embrittlement results and indicated that the terminal solubilities increased as the temperature was raised. The solution of hydrogen in zirconium over the complete concentration range was studied by Hall, Martin, and Rees3 and by others. The results showed that hydrogen was absorbed up to a maximum composition of 66 atomic pct or ZrH This composition represented the t-hydride phase. The maximum amount of hydrogen absorbed increased with pressure and decreased with temperature. Due to this temperature behavior, zirconium was classed as an exothermic occluder." In 1930 Hägg studied the crystal structures of the Zr-H alloys over a broad composition range. Four hydride phases were found. However, the range of homogeneity of the several phases was not studied. Gulbransen and Andrew" recently studied the phase diagram of this system by X-ray diffraction methods and by a thermodynamic method based on decomposition pressure measurements. The results showed that only two hydride phases existed for low temperatures, the 6 and the .-phases of Hagg.' Both phases had broad regions of homogeneity. The lower limit of the two-phase region of a and d-phases suggested a terminal solubility of 4 atomic pct at 500°C. This value was in agreement with the results of Schwartz and Mallett.' To avoid hydrogen embrittlement at low temperatures, it was necessary to heat the metal in high vacuum at elevated temperatures. To choose the conditions of temperature and high vacuum, it was

Jan 1, 1956

By Arthur H. Wilson

INTRODUCTION The stratified deposits of the coal measures are strongly laminated and exhibit a high degree of anisotropy. The stronger rocks in the sequence possess joints and shear planes, the coal itself has a closely spaced cleat pattern, and the softer rocks are capable of flowage. To calculate the general distribution of stress in such a medium by analytical means based on the theories of elasticity is difficult, and has not yet been satisfactorily achieved. Nevertheless, some estimate is required to aid the design of supporting pillars and permit the correct siting of main roadways. This is important when laying out districts for longwall extraction, particularly if the results of previous experience are not available in the area to be exploited. Although elastic stress analyses, including finite element analysis, may not be very appropriate, the basic equilibrium conditions will apply. These, combined with logical deductions based on observed fact, can be used to give appropriate solutions which experience has shown to be capable of giving acceptable results in the design of pillars associated with longwall workings. Constancy of cover load is one of the fundamental equilibrium conditions. When mining below ground, the cover is not removed, therefore the average vertical load after mining must equal the initial cover load. If mining produces a local decrease in load in any particular area, it must be balanced by an equivalent increase in load nearby. Bending moments in the strata above are capable of compensating for the turning moments which this redistribution of load may produce, and the existence of a "rear abutment", much discussed between 1950 and 1960, is not an essential equilibrium requirement. If the distribution of vertical stress is plotted three-dimensionally, then the load on any small element of area 6S will be o.6S, where o is the average stress. This also represents the volume of the "stress envelope" which lies above 6s. By making the individual areas very small and summing together, it is possible to show that the total load on any particular area can be found by calculating the volume of the stress distribution envelope which lies above it. A similar consideration applies to the stress distribution in a two-dimensional situation. If the stress distribution curve is drawn, then the area below any portion will represent the load per unit depth of section. For example, Figure 1 represents the possible stress distribution across a caved waste and associated ribside. If AW is the load deficiency [ ] These loads must balance, therefore area AW = AS, and if one can be deduced, the other will then be known. Attempts have been made to measure stress distributions in the ribside and in the waste. Stress meters in soft rocks such as the coal measures have not proved very effective. Those based on the measurement of strain have experienced difficulty in strata capable of flowage, high modulus stress meters suffer from cross sensitivity, and overcoming to obtain absolute stress is almost impossible. Load measuring instruments left in the waste have also proved largely ineffective, mainly as a result of the difficulties of protecting the leads in a caving environment. Certain logical deductions, however, can be made about the conditions in the waste. CONDITIONS IN THE WASTE Over the area of the waste the surface trough which develops is remarkably consistent, despite the geological variations which occur from coalfield to coalfield. In Britain, an accuracy of 210% is claimed for subsidence prediction based on width of extraction and depth of cover (National Coal Board, 1975). The subsidence in the USA is more variable (Adamek and Jeran, 1981), particularly with respect to the point of inflexion, but the same general pattern occurs. At the shallower depths the somewhat harder roof strata involved in the caving in the USA may suffer less compaction, giving reduced values of subsidence. Subsidence at intermediate horizons below the surface

Jan 1, 1982

By J. W. Furness

Before attempting any discussion of the importance of tariff enactments as applied to exhaustible resources, certain basic factors should be emphasized. First, it must be remembered that minerals differ from organic substances in that they are irreplaceable, and when once taken from the earth's crust enter into uses which ultimately dissipate them, so . that they cannot be recovered for future use. A second factor entering into the problem is the unequal distribution of the mineral deposits of the world. No industrial nation has within its political confines a sufficient quantity of all the minerals necessary for the maintenance and advancement of present civilization; hence international exchange of these commodities is inevitable. As minerals are essential to modern industry, the supply available to any given nation constitutes a factor which limits its ambition to advance industrially. A nation which has this ambition endeavors to secure not only a supply of minerals sufficient for its current needs, but also sources which will assure it expansion. Should mineral raw materials be withheld from such a nation by enactment, it seems inevitable that every effort will be made to obtain them, and that, should the nation deem itself sufficiently powerful, its ultimate recourse will be force. Thus the importance of tariff enactments, not only from the standpoint of industrial prosperity but from the standpoint of international peace, can be appreciated.

Jan 1, 1932

By N. P. Goss

ASTERISM appearing in X-ray Laue dia-grams is an extremely sensitive index of changes in the internal structures of indi-vidual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.1-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not con-clusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made be-tween mosaic and distorted grain struc-tures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example,7 has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-14 to 10-15 c.c., or 10-5 cm. in size.

Jan 1, 1940

By N. P. Goss

ASTERISM appearing in X-ray Laue dia-grams is an extremely sensitive index of changes in the internal structures of indi-vidual grains of polycrystalline metals. It indicates the existence of various forms of subboundary structure or subdivision within the grain. The present viewpoint is that the grain is made up of lattice blocks having substantially the same size and shape.1-4 When these blocks all assume exactly the same orientation, the crystal is perfect and asterism is absent. Cleaves and Thompson5 observed that the hardness of iron is virtually constant over a range of grain sizes. It is quite possible that the subboundary structure caused this, and that the latter is just as important as grain size itself. While the experiments reported here are not con-clusive, they do support this viewpoint. Metals can, under certain conditions, be prepared entirely free from asterism, but this preparation does not necessarily require long heating or slow cooling, as will be shown here. In this paper a distinction is made be-tween mosaic and distorted grain struc-tures but the difference is only a matter of degree. In a previous paper9 it was shown that the grains can become distorted even during heat-treatment. The block structure exists inherently, even in a perfect crystal; the size and shape of these crystallites, or lattice blocks, varies, depending upon a number of factors. Goetz, for example,7 has shown that a metal before crystallizing from the molten state must go through a paracrystalline phase with oriented groups of atoms about 10-14 to 10-15 c.c., or 10 5 cm. in size.

Jan 1, 1940

By H. B. Emerick

An effort has been made to evaluate the individual influence of various factors in steel making and rolling operations upon the surface quality of semi-finished steel products. The thoughts expressed are not entirely theoretical, but rather are based upon several years critical observation of mill yields and rejec-tions and are supported by actual data wherever this has been possible.

Jan 1, 1940

By S. J. Rothman, A. L. Harkness, L. T. Lloyd

Self-diffusion in Y uranium has been measured using U235 as the tracer isotope. The diffusion coefficient fits an Arrhenius-type equation D = 2.33 x 10 -3 exp (- 28,5000/RT) cm2/sec The values of Do and Q are unusually low and are not consistent with the values expected from theories based on a simple vacancy mechanism of diffusion. CYLINDRICAL samples, 1 cm in diam and 1/2 to 1 cm long, were prepared from high-purity uranium containing 0.0343 pct u235, Table I. The samples were water quenched from 690°C (the a-ß transformation is at 668°C) to remove preferred orientation, and annealed at 450 "C to minimize residual stresses. One end of each cylinder was polished on a 1-µ diamond lap and electropolished in a phosphoric acid solution. After a final cleaning by cathodic sputtering, a 1- to 3-µ thick layer of the tracer isotope, uranium containing 93 pct u235, was sputtered onto the sample.' To prevent contamination during the diffusion anneal, the diffusion couples were placed in a tantalum cup and covered with another piece of uranium, and the whole assembly was sealed off in an evacuated quartz tube. Annealing temperatures were constant within +2.0°C. The samples were heated and cooled slowly between room temperature and the ß-? transformation (774°C) in order to minimize distortion of the sample surface that might arise from aniso-tropic thermal expansion and density changes during phase transformations. After machining off 1/16 in. from the radius to

Jan 1, 1961