By J. L. Bray

LEAD has often been suggested as a protective coating for iron and steel. Such a protective coating should possess: (1) good adhesion, (2) durability, (3) ease of application, (4) freedom from pinholes, (5) good appearance and (6) low cost, but, unfortunately, lead coatings so far produced do not have all of these characteristics. Because of the necessity of carrying out the coating process cheaply, and because lead solutions have poor plating characteristics, most of the efforts have been directed toward the hot-dipping process rather than electroplating. The hot-clipping processes using lead have not been successful chiefly because of the lack of adherence between iron and lead. In any coating process involving iron a bond can be obtained only by the formation of an intermetallic compound, the formation of a solid solution, or mechanical means. Lead forms with iron two immiscible liquid solu-tions, and in the solid state no intermetallic compounds or solutions. It is necessary, therefore, to employ some other element or elements as a binding agent. Tin may be used as in terneplate, or copper in the form of a thin film of electrolytically deposited metal to which the lead will adhere. Because of its physical and chemical properties, lead as a coating medium would undoubtedly be limited in its use to sheet and wire and then only when the article is not subject to abrasion or wear. A very large tonnage of these products are being used under such conditions and a successful lead-coating process should be a valuable contribution to the science. Two other difficulties stand in the way of successful lead coating-that of poor appearance of the weathered surface and the tendency of the lead to form pinholes during solidification. Since lead is commonly accepted as cathodic to iron, these exposed areas are ones of accelerated corrosion.

Jan 1, 1937

By Everett G. Trostel

AMERICAN industry in 1943 emerged from the construction phase into the production phase, and American military operations passed from preparation into full action in the many theaters of the global war. The increased pace of industrial and military operations has resulted in a tremendous demand for petroleum and its products.

Jan 1, 1944

By R. W. Cahn, C. D. Graham

Two predictions of the oriented growth theory of recrystallization textures have been tested by measuring the orientation dependence of the rate of growth of a single grain into a strained single crystal of aluminum, and determining the orientations of artificially and spontaneously nucleated grains growing preferentially into strained aluminum single crystals. Growth rates are found to be insensitive to orientation, except that new grains with orientations similar to the matrix or to a twin of the matrix have very low mobilities. Similarly, new grains growing preferentially into a strained crystal have random orientations, except that orientations near that of the matrix or its twins are avoided. The predictions of oriented growth theory are thus not confirmed. BASICALLY, the oriented growth theory of re-crystallization textures1 rests on the assumption that the rate of growth of a recrystallizing grain depends strongly on the orientation of the growing grain relative to the strained matrix into which it grows. In particular, the theory holds that in face-centered-cubic metals the orientation which corresponds to maximum growth rate is one in which the growing grain and the matrix are related by a rotation about a common <111> direction. The amount of rotation, as derived from several kinds of experiments,2-1 has been assigned various values, generally in the range between 20" and 40". (A <111> rotation of 60" is a twin relationship.) The conclusion that boundary migration rates depend strongly on orientation is based almost entirely on indirect evidence; there have been very few direct measurements of boundary migration rates as a function of orientation.* " The present investigation was undertaken to provide such measurements, to help make possible a decision between the oriented growth and oriented nilcleation theories of recrystal-lization textures. The basic experimental program consisted of measuring the rate of growth of a single recrystal-lizing grain consuming a strained single crystal, with the orientations of both grains preselected so that the effect of orientation on growth rate could be determined. A prerequisite for such an experiment is a strained single crystal which will support the growth of a new grain but which will not spontaneously nucleate new grains on heating. That is, the crystal must support the growth of a grain nucleated artificially, but contain no recrystalliza-tion nuclei which will become active at the testing temperature. Beck was apparently the first to note that such a condition could exist," and to make use of the condition for am experiment of the type described here.&apos; The present work was actually suggested, however, by a report of Tiedema". " that an aluminum single crystal strip, oriented with a (111) plane in the plane of the strip and a < 112> direction parallel to the tensile axis, would not recrystallize after 20 pet extension even when heated almost to the melting point, provided that the strip was heavily etched before being heated. This result could not be duplicated in the present work. In fact, it was found that any crystal which deformed in multiple slip (<100>, <112> and <111> orientations) underwent spontaneous nucleation after 15 pet extension, even if etched. However, crystals which deformed in single slip, and which did not develop heavy deformation bands, could be extended 15 pet without showing spontaneous nucleation at temperatures up to 600°C. Crystals oriented within about 10o of <110> which developed heavy deformation bands could be extended 10 pet without showing spontaneous nucleation. In all cases a heavy etch was required to prevent nucleation. Etching was necessary because of the presence of an oxide layer on the crystal surface at the time of straining, which leads to preferential nucleation at the surface.&apos;&apos; Grain Growth Rates Experimental Procedure and Results—Aluminum strips of 99.6 pet purity (principal impurities 0.19 pet Fe and 0.12 pet Si), 1 mm by 1 cm in cross section, were grown into single crystals of controlled orientation by the strain-anneal method of Fuji-wara.&apos;"&apos; " A sharp temperature gradient was maintained in the strips during growth by lowering them into a salt bath controlled at 650°C. Crystal orientations were determined by the etch-pit method of Barrett and Levenson" to an accuracy of ±2O. The crystals were extended by 10 or 15 pet in a simple hand operated tensile machine. Crystal orientations were rechecked after extension, and were found to be in agreement with the orientations predicted by the formula of Schmid and Boas." After extension, the grip ends of the single crystal specimen were cut off with a jeweller&apos;s saw, and the crystal heavily etched (at least 20 pet wt loss) in hot 10 pet Na or KOH solution. A region of severe local deformation was then introduced at one corner of the strip, usually by cutting off the corner with shears. Heating this end of the strip caused a large number of new grains to nucleate at the sheared edge. One of these grains grew to occupy the full width of the strip. The appearance of the strip at

Jan 1, 1957

By M. R. J. Wyllie, P. F. Southwick

The importance of the so-called "dirty sand" or "conductive solids" problem in electric log interpretation was first stressed in a paper presented in 1949. Since that time the problem has been generally recognized as a most serious one. Several research papers bearing on the theory of the effects of clay contaminants on reservoir rock resistivities have appeared. These papers, while contributing to the theory of the problem, have not offered any practical solution. In the present paper an experimental investigation has been made of the effects of ion-exchange materials on the electrical properties of natural and synthetic porous media. The method used to make synthetic dirty sands is entirely novel and has proved a valuable guide to a better understanding of the properties of dirty sands generally. The effects of ion-exchange materials on both the resistivity and self potential (S.P.) logs have been examined. From the data obtained it has been possible to formulate a simple, practical method whereby electrical logs of dirty sands can be qualitatively interpreted. The method is in all essentials identical to that presently in use for interpreting clean sands. New light has also been thrown on the significance of the term formation factor when it is applied to dirty sands. In 1949 a paper was presented1 which showed that the presence of so-called "conductive solids" introduced considerable complexities into the analysis of the resistivities of dirty sands, i.e., permeable formations containing clay. The reduction of the self potential (S.P.) resulting from the presence of interlaminated shale or interstitial clay in permeable formations has been discussed by Doll.2,3 Noteworthy papers which dilate further upon the effects of shale and clay on the resistivity of permeable formations are those of deWitte,4,5 Berg,6 Wyllie,7 and most recently, Winsauer and McCardell.8 The last authors have endeavored to elucidate the chemistry of the resistivity phenomena in dirty sands in terms of an adsorption hypothesis. Specifically, they attribute the electrolytic conductivity of shales and clays within a permeable formation to an ionic double-layer effect and, for this reason, regard the term "conductive solids" as a misleading one. Some consideration has been given to the effect of dirty sands on the S.P. by Wyllie7 and by McCardell, Winsauer and Williams." Published work to date has cast light only on certain theoretical aspects of the problems created by the presence of clays and shales within permeable formations. One object of this paper is to describe experiments which serve to elucidate further the theory of the dirty sand problem and particularly the significance of the term "formation factor" as applied to dirty

Jan 1, 1955

By Richard W. Bayley

The Atlantic City district encompasses several districts and has been previously called by different names, e.g., Atlantic gold district, Atlantic City-South Pass mining district, and Sweetwater mining district. The district is located in a terrane of folded and faulted early Precambrian metamorphic rocks which lies near the south end of the Wind River Range in Fremont County, Wyoming, Historically it is a gold district of little production, but today is an iron district of considerable importance. Gold was discovered in placer deposits about 1842 and in quartz-arsenopyrite veins about 1867, after which there occurred a mining boom lasting a few years. Minor, intermittent gold production from placers and lodes has continued to date, but the total production has probably not exceeded a few millions of dollars. Past lode mining was generally shallow ( in the oxidized zone), the deepest about 3 60 feet. The deeper, less oxidized and sulfide ores on the same lodes have not been explored. They appear to hold the only hope for future gold mining. Sedimentary iron-formation, similar to the Lake Superior taconite, occurs in the northern part of the district. Locally, where the ironformation is thickened by folds and faults, sufficient tonnages are present to be minable, as at Iron Mountain, where the U.S. Steel Corporation produces about 1.3 million tons of iron-ore pellets annually. Exploration of the iron deposits began in 1954, and the first ironore pellets were shipped to Provo, Utah in August 1962. Indicated reserves of iron-formation (about 30 per cent Fe) are reported to be about 300 million tons.

Jan 1, 1968

By C. R. Kuzell

INTRODUCTION KNOWLEDGE of the thermal capacity of gases is of great importance in making metallurgical calculations. The metallurgist is, frequently called upon to investigate and determine furnace efficiencies in which the heat carried into or out of the furnace by gases is a large item in the heat balance. Not only do such problems present themselves in the determination of furnace efficiency, but also in the study of the application of heat is accessory apparatus, such as stoves, regenerators, waste-heat boilers, driers,.etc. The thermal effect of the use of excess air in the combustion of fuel, the theoretical temperatures of combustion, the quantity of heat in hot blast at various temperatures, the effect of hot blast on furnace temperatures, are a few more examples of frequently occurring calorific problems involving gases. So many are the applications of the data on the heat capacity of gases that the subject merits careful study. The heat in a gas maybe due to its heat of combustion, if it is a combustible gas, and to its temperature. The latter is called its sensible heat and is the heat absorbed or evolved by a gas as its temperature is raised or lowered. The heat of combustion of gases is well established and is commonly known. The values can be found in almost any mcdern treatise on metallurgy. The sensible heat of gases has not been so well established because it is in most cases a function of the temperature, and the values of specific heats of gases over a wide range of temperatures have only recently been determined. It is the purpose of this paper to deal with the sensible heat of gases.

Jan 8, 1914

By N. F. Schulz, H. A. Lex, J. D. Zetterstrom

A green ball of iron ore faces many perils from the time it is formed until it finally emerges from the pelletizing furnace as a hardened pellet. For instance, if the rate of heat transfer into a ball is sufficient to produce vapor from either the free or combined water more rapidly than it can escape at a tolerable pressure, the ball may split, spall, or even explode, a failure commonly known as decrepitation. To avoid such failures, one must either limit the rate of heat transfer during the drying and preheating stages, at the expense of production rates, or improve the decrepitation resistance of the green balls. The latter remedy may often be accomplished through changes in ore preparation, balling procedures, or the judicious use of binders or other additives. INTRODUCTION Pelletization has become established as an especially desirable method for the agglomeration of fine taconite concentrates and it promises to be equally satisfactory for improving the physical structures of certain natural ores. A high-quality pelletized iron ore consists of uniformly sized spheres, usually about 1/2-in. diam, which are strong enough to resist abrasion and breakage during handling and which reduce well without disintegration in the blast furnace. The unfired agglomerates, "green balls", are subject to several destructive effects that must be avoided or minimized if a high-quality product is to be obtained by pelletization. Among these are abrasion and impact deformation or breakage during handling of the wet green balls, deformation and breakage by compressive forces in the bed of ore in the pel-letizing furnace, decrepitation during drying and preheating, wind erosion, and radial cracking at firing temperatures. Moisture condensation from the warm saturated gases downstream from the drying zone on wet, cool balls may cause bed collapse if it becomes excessive. Decrepitation is defined as the sudden disintegration of green balls, usually with an audible pop, that occurs when they are heated too rapidly during the drying or preheating stages of the pelletization process. The extent of ball disintegration may vary from merely splitting off a small fragment to almost total disintegration into the original ore particles making up the ball. Such ball destruction results in a decreased yield of pellets, and the fragments, which also tend to interfere by obstructing the gas flow through the bed, must eventually be screened from the fired product and recycled. The closely related type of ball failure that sometimes occurs during the high temperature firing stage, resulting in radial cracks without fragmentation, was not considered to be decrepitation for the purpose of this investigation. Failure by decrepitation is not usually a serious problem in the pelletization of taconite concentrates. The problem is significant, however, in the pelletization of some natural ores, especially those containing hydrous iron oxides. In some instances, economicd production rates cannot be maintained if the drying and preheating rates are slowed down enough to avoid decrepitation. OBJECTIVES This investigation was undertaken to: (1) Develop a practical laboratory means for quantitatively measuring the tendency for green balls to decrepitate in iron ore pelletizing furnaces, and (2) Investigate the causes and cures of ball decrepitation. MATERIALS Two iron ores were used in the work reported here: a taconite concentrate at 90% minus 325 mesh, containing 65.0% Fe, 8.4% SiO2, and no loss-on-ignition; and a crude oxidized ore at 54% minus 325 mesh, containing 59.1% Fe, 3.6% SiO2, 1.1% A12O3, and 9.5% loss-on-ignition. For a special test of effect of particle size distribution on decrepitation, two other

Jan 1, 1967

By M. J. Marcinkowski, D. B. Crittenden, A. S. Sastri

A study co.mbining stress-strain .measurements in conjunction with transmission electron microscoPy has been made with near equiatomic Fe-Cr alloys which were aged for various times at 500°C. Associated with this aging is a marked increase in deformation twinning. The outstanding feature of these twins is that they generate stress fields sufficiently great so as to give rise to spontaneous dislocation loop nucleation nearly normal to the propagating twin. This observation is in agreement with the theoretically predicted elongation of the stress field of a dislocation Perpendicular to its direction of motion as it moves near the speed of sound. Dislocation loop nucleation is more difficult in the longer aged alloys so that this energy absorption mechanism is not effective in hindering twin propagation. Since crack nucleation can readily occur near the tip of a twin, the aged alloys become extremely brittle when deformed in tension. Iron-chromium alloys in the vicinity of the equiatomic compositions become severely embrittled when aged at about 500°C. Fisher et 01.&apos; have shown that this embrittlement is related to the decomposition of the original random Fe-Cr solid solution into a chromium-rich and an iron-rich phase. In addition, Mar-cinkowski et a1.&apos; have shown that twinning becomes an increasingly more important mode of deformation as the aging time is increased. These results have been recently corroborated by the transmission electron microscopy study of Mima and amauchi . The Fe-Cr alloy thus seems ideal for verifying the predictions made in Parts I4 and 115 of this investigation where the behavior of large static or blocked twins and those of large dynamic or propagating twins, respectively, were investigated numerically. It was thus decided to measure the stress-strain curves generated by embrittled alloys that were aged for various times and to examine sections by transmission electron microscopy. EXPERIMENTAL PROCEDURE Electrolytic iron and electrolytic chromium were vacuum-melted and poured into ingot form. The composition of the resulting alloy was found to contain 46.0 wt pct Cr (47.8 at. pct), the remainder being iron. The resulting ingot was swaged above 850°C into 0.250-and 0.400-in.-diam rounds. Compression samples of 0.250 in. diam and 0.400 in. long were cut from the smaller-diameter rounds. These samples were then sealed in evacuated quartz tubes and annealed for 30 min at 1150°C to produce a uniform and equiaxed grain size of mean diameter equal to 1.73 mm. They in turn were rapidly quenched from 850°C so as to preserve the condition of random solid-solution characteristic of the elevated temperature. The samples were then aged for various times up to 300 hr at 500°C in a massive Pb-Bi alloy bath. The samples were next polished and tested in compression at room temperature as described in Ref. 6 using an Instron tensile testing machine. The strain rate used was 0.05 in. per in. per min. The remaining larger round was converted into compression specimens of 0.325 in. diam and 0.500 in. long. This larger diameter enabled wafers of sufficient size to be prepared for examination by trans-mission electron microscopy techniques after subjecting them to a suitable strain. Foil preparation is described in some detail in Ref. 6. All foils were examined in a type HU-11A Hitachi electron microscope operating at 100 kv. RESULTS AND DISCUSSION Fig. 1 shows the effect of aging at 500°C on the room-temperature stress-strain curves of the FeCr alloys. For greater clarity the origin of each curve has been displaced upward. The same origin has been used for both the 0 and the 0.1 curves. It is apparent that with increased aging times a sharp drop in load is observed at the yield stress which becomes more pronounced as aging proceeds. A loud sonic burst accompanies this drop and subsequent metallographic examination shows the sample to contain numerous twins. For intermediate aging times, a number of smaller twin bursts follow the initial large one. The total plastic strain associated with the twinning mode of deformation can be obtained by adding up the contributions AE~ from all i twin bursts, i.e., £,¦££,-, in the manner illustrated schematically in Fig. 2. The contraction of the specimen, as measured from the strip chart of the Instron, after suitably correcting for the elasticity of the machine, was converted into true strain using the assumption that there was no volume change and that the sample remained cylindrical. The dashed lines are all drawn parallel to the

Jan 1, 1970

By H. J. Morel-Seytoux

The influence of patten, geometry on assisted oil recovery for a particular dispIacement mechanism is the object of investigation in this paper. The displacement is assumed to be of unit mobility ratio and piston-like. Fluids are assumed incompressible and gravity and capillary effects are neglected. With these assumptions it is possible to calculate by analytical methods the quantities of interest to the reservoir engineer for a great variety of patterns. Specifically, this paper presents (1) very brieily, the methods and mathematical derivations required to obtain the results of engineering concern, and (2) typical results in the dorm of graphs or formulae that can be used readily without prior study of the methods. Results of this work provide checks for solutions obtained from programmed numerical techniques. They also reveal the effect of pattern geometry and, even though the assumptions of piston- like displacement and of unit mobility ratio are restrictive, they can nevertheless be used for rather crude but quick, cheap estimates. ,These estimates can be refined to account for non-unit mobility ratio and two-phase flow by correlating analytical results in the case M = 1 and the numerical results for non-piston, non-unit mobility ratio displacements. In an earlier paper1 it was also shown that from the knowledge of closed form solutions for unit mobility ratio, quantities called "scale factors" could be readily calculated, increasing considerably the flexibility of the numerical techniques. Many new closed farm solutions are given in this paper. INTRODUCTION BACKGROUND Pattern geometry is a major factor in making water-fIood recovery predictions. For this reason many numerical schemes have been devised to predict oil recovery in either regular patterns or arbitrary configurations. The numerical solutions, based on the method of finite difference approximation, are subject to errors often difficult to evaluate. An estimate of the error is possible by comparison with exact solutions. To provide a variety of checks on numerical solutions, a thorough study of the unit mobility ratio displacement process was undertaken. To calculate quantities of interest to the reservoir engineer (oil recovery, sweep efficiency, etc.), it is necessary to first know the pressure distribution in the pattern. Then analytical procedures are used to calculate, in order of increasing difficulty: injectivity, breakthrough areal sweep efficiency, normalized oil recovery and water-oil ratio as a function of normalized PV injected.

Jan 1, 1967

By D. J. Rose, W. M. Armstrong, A. C. D. Chaklader

The wetiability of single crystals of MgO by specimens of vacuum-cast iron was studied using the sessile drop technique in vacuo at 1550ºC. Formation of FeO at the liquid-vapor interface caused the contact angle (6) to decrease from 117 to 65 deg during the first minute. After cooling, all specimens possessed a peculiar annular interfacial deposit of Fe,O,. Within the annulus the interface showed no sign of chemical attack. Chemical reaction occurred where the iron was alloyed with Ti, V, Cr, Nb(Cb), Ta, cmd Zr. Vnriation of 6 with alloy concentration was studied. Although vanadium md chromium improved the wettability of MgO by iron, the effect of Zr, Ti, Nb, and Ta was indeterminable because the 8 derived from sessile drop considerations was that of the metal against a restrictive peripheral volume of liquid oxide wetting the substrate. INTEREST in the nature of metal-ceramic interactions has been stimulated by progressive development of metal-ceramic combinations. One of the more valuable methods used for bond investigation is the sessile drop technique. Recent attempts to improve wettability through solute additions to the drop have revealed that the solute may a) react with the oxide creating new compounds at the solid-liquid interface, b) adsorb at the interface in a monolayer formation, or c) distribute throughout the drop uniformly causing no wettability variation. This work, part m in a series1,2 of investigations of interface reactions between metals and ceramics, embraces a study of the Fe-MgO system. MgO possesses a large negative free energy of formation (-173 kcal per g mole 0, at 1550ºC) compared to FeO at this temperature (-73 kcal per g mole 02). Hence the electronegativity difference between the drop and substrate allows selection from an extensive group of metal solutes with intermediate electronegativity differences that would, in the absence of chemical reactions, be expected to adsorb pre- ferentially at the solid-liquid interface. However, the high oxygen pressure of MgO in vacuo creates an oxidation environment which influences the solute behavior. Recent studies of the Fe-MgO systemJ74 have been restricted by chemical reactions that obscured observations. In view of the current interest in liquid-phase sintering of metal-ceramic combinations under partial oxidizing conditions,5 a more comprehensive study of the Fe-MgO system seemed beneficial. EXPERIMENTAL PROCEDURE 1) Specimen Preparation. Optical-grade MgO single crystals and Ferrovac vacuum-cast iron were used in all experiments. A spectrographic analysis of the iron indicated 0.008 C, 0.05 V, 0.005 Mo, 0.01 Ti, 0.002 S, 0.01 Cr, 0.001 Mg, 0.01 Si, 0.003 A1 (wt pct). The MgO crystals were cleaved along (100) planes into plates approximately 20 by 20 by 1 mm. Following annealing in vactto at 1100°C for 3 hr, surface irregularities were removed by a chemical etch in phosphoric acid at 100°C. The iron rod was machined into small cylinders approximately 0.250 in. in diam and length and these were carefully cleaned in organic and acidic solutions to remove surface impurities. All specimens were weighed to the nearest 0.1 mg. 2) Apparatus. The apparatus described in detail by previous authors1,2 was modified for this work. A Polaroid Land Camera was incorporated into the optical system so that drop measurements at ten-second intervals after melting were possible with ultra-high-speed self-develop ing film. 3) Procedure. The iron cylinders were placed upright on the MgO plates and positioned in the molybdenum susceptor. After furnace assembly the system was pumped down to a vacuum of 1 µ and flushed with H2 at 800°C. The system was again evacuated to 5 x 10-5 mm of mercury and the temperature raised to 1550°C within 2 min. The molten drops were photographed at appropriate time intervals. TWO min after melting the iron vapor pressure caused gas discharge, or corona, within the tube. The specimens were then slowly cooled to room temperature, sectioned and examined metallographi-cally. X-ray identification of interfacial reaction products was attempted by the powder diffraction technique. Alloying elements (Ti, V, Cr, Zr, Ta, Nb) were added to the iron in various concentrations up

Jan 1, 1963

By Thomas Leonard Watson

Introduction,...... Historical Statement,....644 Geology of the District,....645 The Weisner Quartzite,....647 Topography,. .....653 Rock-Weathering,..... The OcheR-Deposits,.....655 Petrography of the Quartzite,..655 Associated Ore-Deposits,....657 Chemical Composition of the Ocher,. 658 Mode of Occurrence of the Ocher,..659 In the Fresh Rock,....660 In the Residual Clays,...661 Origin of the Ocher,....662 Economic Features,..... Methods of Mining,..... Preparation of the Ocher,...664 Uses,........ Introduction. Knowledge of the existence of yellow-ocher deposits in Bartow county, Georgia, dates back to the early mining of manganese- and iron-ores in the vicinity of Cartersville. Systematic mining of the ocher in this area really began, however, probably not longer than a decade back, although the date of its first working is as early as the year 1877. The district has been, for a number of years, one of the principal producers of yellow ocher in the United States; and at no period of its development have mining activities been greater and more successful than at present. Systematic field-study of the ocher- and manganese-deposits of Georgia was begun by me while I was a member of the

Jan 1, 1904

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,&apos; magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By M. Cohen, R. T. Howard

It has long been realized among metallurgists that a fast, reliable method for the quantitative determination of the percentage of microconstituents in an alloy would be of great benefit in studies of equilibrium and transformation in the solid state. For example, Polushkinl has shown that the compositions of two coexisting phases in a binary system at a given temperature may be calculated very simply with the aid of two alloys lying in the two-phase field if the relative amounts of the two phases in each alloy can be determined. Recently, Grange and Stewart2 have traced the course of the austenite-martensite reaction in a series of commercial steels by making visual estimates of the percentage of martensite formed as a function of cooling temperature. The correlation of mechanical properties with structure, a subject of wide-spread current interest, is likewise dependent upon quantitative microanaly-sis. Yet, there are very few investigations described in the metallurgical literature, wherein methods of quantitative microscopy are employed. Usually, the relative amounts of the microconstituents are estimated in a qualitative or semiquantita-tive way. The authors were faced with this problem some time ago in studying the kinetics of austenite decomposition. Several aspects of this research could not be treated satisfactorily by other quantitative tools, such as specific volume,&apos; magnetic,6 dila-tometric, electrical resistance7 or x-ray measurements.a It became necessary to find an impersonal quantitative method that could be applied to microstructures. Fortunately, it was noted that geologists and petrographers had coped with quantitative microscopy to a considerable degree in their attempts to evaluate the mineral contents of rocks. A number of excellent articles were found on this subject, and since they appear to be unknown generally to many metallurgists, the first part of the present paper is concerned with a review of the literature in some detail. With this survey as a background, the authors have adapted the so-called methods of point-counting and lineal analysis to metallography, as described in the second part of the paper. Austenite-martensite structures were selected for illustration not only because they are important in many ways, but because such fine intermixtures are notoriously difficult to estimate visually. Literature Survey Perhaps the earliest work on quantitative microscopic analysis goes back to Delesse9 (1848) who proved mathemati-

Jan 1, 1948

By R. W. Kewish

The preparation of massive uranium metal containing very low concentrations of a number of light elements by bomb reduction of UF4, with calcium is described. Details of procedures are given for preparing high-purity ingredients for the bomb reduction. The as-reduced uranium metal contained, on the average, less than the following amounts of light element impurities, in ppm: Li, 0.1; Be, 0.1; B, 0.1; C, 25; 0, 70; Na, 1; Mg, 3; Al, 2; and Si, 7. Other impurities for which the metal was examined averaged, in ppm: Ca, < 10; V, < 10; Cr, 2; Mn, 6; Fe, 50; Co, < 5; Ni, 8; and Cu, 1. THE preparation of very high-purity uranium metal in massive form for research purposes is of great importance. Recently the kilogram-scale preparation of uranium metal containing less than 70 ppm of detected impurities was accomplished by Blumen-thal and coworkers by vacuum remelting of high-purity crystals of uranium obtained by fused salt electrolysis.1"3 Albert and coworkers4 have reported successful experiments in lowering the concentrations of certain impurity elements in uranium, notably iron, to a few ppm by the zone-melting method. The present paper describes the preparation of high-purity massive uranium metal by the bomb reduction of UF4, with calcium. Early in 1951 a program was undertaken at the Los Alamos Scientific Laboratory to prepare uranium metal of very high purity with respect to a number of the light elements. The methods considered for this purpose were 1) bomb reduction of a uranium halide with calcium, 2) electrolysis of fused salts, and 3) hot wire decomposition of UI4, The first of these processes had been used extensively at Los Alamos since 1943 (and still is used) for the production of uranium metal.5 In considering the three processes it was evident that either of the last two would require an extensive development program with no certainty of success. On the other hand, a study of available data showed that uranium metal of very high purity with respect to some light elements had occasionally been made in routine processing by the first method. It was therefore decided that an intensive study of the bomb-reduction process would be made to see if it could be improved to yield uranium metal with very low concentrations of light elements. DEVELOPMENT OF PROCEDURES The bomb-reduction process used at Los Alamos consists of reducing UF4 with calcium, using iodine as a booster. The reaction is carried out in a magnesium-oxide crucible enclosed in a steel bomb. Argon is used in the bomb to avoid objectionable side reactions which would occur in the presence of air. All ingredients for this bomb-reduction process were examined as possible sources of light elements. It was known that high-purity UF4 was required. The calcium used in the reductions was a source of carbon and magnesium. The magnesium-oxide crucibles were sources of boron, silicon, and magnesium. The iodine did not appear to be a source of any impurities. Pure UF4- The UF4 for bomb reduction is prepared from U3O3 , by successive reduction to UO2, with hydrogen and hydrofluorination of the UO2, with anhydrous HF. Since it was known that no impurities were normally introduced during the gas-solid reactions, effort was directed toward the preparation of high-purity U3O3. Of the many possible procedures for the purification of uranium solutions the following were investigated: 1) Precipitation of uranium peroxide. (Two procedures were tried. The first consisted of simultaneously adding hydrogen-peroxide and ammonium-hydroxide solutions to a uranyl-nitrate solution, containing citric and malonic acids, at such relative rates that precipitation was carried out at a constant pH of 1.5 The second consisted of simultaneously adding uranyl-nitrate, ammonium-hydroxide, and hydrogen-peroxide solutions to an aqueous solution

Jan 1, 1960

By R. M. Treco

THE purpose of this work has been to investigate recrystallization characteristics of zirconium after cold working and annealing. In order to do this, hafnium-contain ing crystal bars of Foote Mineral Co. iodide zirconium were selected for high purity. maximum diameter (about ½ in.), brightness of surface, and absence of core wire. A typical lot analysis is shown in Table I. In order to obtain uniformity of starting material, all bars were cold-swaged to 0.310 in. diam, annealed for 2 hr at 1000°C, and furnace cooled.

Jan 1, 1957

By Nelson Severinghaus

Consolidated Quarries Corp. must conduct operations for an average sales price of $1.25 per ton, about the same price at which stone was sold 25 years ago when the dollar was worth twice what it is now. To maintain success in a competitive business, the company must solve the usual production problems, which will be discussed here in the order they occur in the flowsheet. Most crushed stone quarries must first remove soil and decomposed rock. Although seasons of lower sales sometimes release regular quarry excavating and haulage equipment for this purpose, overburden is often too extensive for this method to be used. In such cases, special equipment must be assigned or the job may be contracted. As many earthmoving contractors have heavy duty specialized equipment well suited to overburden removal, they should be seriously considered before the job is undertaken. Pockets of clay beneath peaks of hard stone sometimes defy mechanized removal. Pick and shovel laborers at this point might be supplanted by more ingenious use of pumps and water or some other mechanical means. Where overburden is extremely heavy or difficult to remove, underground mining must be considered.

Mar 1, 1956

By Roshan B. Bhappu, Thomas J. Lien

The DYNA WHIRLPOOL Processor (DWP) is a cylindrical dynamic heavy media vessel. It is used to beneficiate fine ore sizes from one and one-half inches in diameter down to 65-mesh. Process units available treat up to 80 tons per hour. Units can be manifolded for higher capacity plants. Finely ground magnetite and ferrosilicon are used for media. , Installed capital costs are from $4,000 to $6,000 per ton hour of feed. Operating costs are from $0.30 to $0.50 per ton of feed. The DWP is used to beneficiate metallic and non-metallic ores and coal. The OCC Vessel is a static heavy media separator used to beneficiate coarse ore up to six inches in diameter and auto scrap. Process units available treat up to 300 tons per hour.

Jan 1, 1978

By G. P. Airey, R. F. Mehl, T. A. Hughes

The coarsening of cementite particles in a ferrite matrix has been studied in a series of steels with 0.15 pct C only and 0.15 pct C plus 1 pct Ni, Mn, and Cr, respectively. Two initial states were employed: quenched nartensite, and quenched and cold-rolled martensite. A series of tempering temperatures between 500&apos; and 700" and tempering times of up to 190 hr were used. The structures were studied by replica and transmission electron microscopy. Particle size distribution curves were determined. From the average size value coarsening curves were obtained. These were plotted in accordance with the Wagner analysis assuming diffusion control. A discussion of the significance of the results is given. L HE reactions occuring upon the tempering of martensite have long engaged the attention of metallurgists. The latter stages, when cementite particles coarsen in a ferrite matrix, have been studied both qualitatively and quantitatively. Studies of such coarsening processes have recently been spurred by the publication of the Lifshitz-Wagner theory1, and the extension of this to the a Fe-Fe3C system by Oriani3 and by Li, Blakely, and einold. Following Wagner the coarsening process is often designated as "Ostwald Ripening". The only quantitative data on the rate of coarsening, except for the work of Hyam and uttin,&apos; in the a Fe-Fe3C system are those of Bannyh, Modin, and odin&apos; for a commercial eutectoid steel and those of Heckel and ereorio" using a pure eutectoid steel. The data of Bannyh, Modin, and Modin have been employed by 0riani3 to derive the a Fe-FeE interface energy. The reaction is one of the most important ones in steel and is worthy of detailed study. This is the purpose of the present study. Laboratory heats were prepared; these were steels with approximately 0.15 pct C, selected so that the num ber of carbide particles would be relatively small and thus so that the overlapping diffusion fluxes would be minimized, presumably a desirable circumstance.&apos;-3 In addition to Fe-C alloys, comparable heats containing 1 pct of Ni, Mn, and Cr, respectively, were included with a view of appraising the effect of alloying elements. This report includes an account of the micro-structures observed, primarily with the electron microscope, and of kinetic data and their interpretation. MATERIALS AND TREATMENT The alloys were prepared from electrolytic iron ("Plastiron") and high-purity graphite; these were melted in a zirconia crucible using a vacuum furnace. The alloy steels were made by adding electrolytic nickel, electrolytic manganese, and "vacuum grade" chromium, respectively, under a partial pressure of argon. Each melt was poured into a mold within the vacuum furnace and cooled in the mold. The ingots were 2 in. in diam. and 8 to 10 in. long. The analysis of the alloys is given in Table I. These ingots were hot-rolled to strip 0.1 in. thick, then cold-rolled to 0.05 in. and each alloy split into two batches. One batch was austenitized at 1200 for 1 min, quenched in cold brine, then cold-rolled to 0.02 in.; samples given this treatment are hereinafter designated as "worked". The other batch was cold-rolled to 0.025 in., austenitized at 1200" for 1 min, and quenched in cold brine; such samples are hereinafter designated as "quenched". These two batches were then tempered, as below. The purpose of the treatment given the first batch was to provide an initial structure of cold-worked martensite, with the expectation that the additional defect structure created by cold work would encourage a higher rate of nucleation of cementite on tempering and hence a more uniform distribution of cementite particles. Individual specimens were sealed in evacuated quartz or Pyrex tubes, then tempered in a muffle furnace. The temperature control was better than 3&apos;C at 700. Tempering treatments wer: performed at 400°, 500°, 550°, 600°, 65o°, and 700C for time periods between 15 min and 190 hr. PREPARATION OF SPECIMENS Specimens for optical and replicalelectron microscopy were mounted, polished conventionally, and etched with 2 pct nital. For electron microscopy, single-stage "formvar" replicas were made, dry-stripped and rotary-shadowed with chromium at an angle of 30 deg. Carbide extraction replicas were prepared from electropolished specimens usirig the method described by Smith and uttin.&apos; Thin foils for electron transmission microscopy were prepared by chemical thinning in an H202-HF bath prior to electropolishing in a chromium trioxide-acetic acid solution. The most

Jan 1, 1969

By D. R. Irving

Prior to this time, ample supplies of high grade mineral fillers, such as clay, have been available close to consuming centers. Now depletion of these accessible deposits, coupled with other factors such as increasing demand due to population expansion and standard of living rise, has made development of upgrading techniques attractive to producers. Various investigations being carried out by the U.S. Bureau of Mines are described. Factors making the development of improved methods for upgrading clays attractive to producers include: depletion of accessible deposits of high-grade clays, rising transportation and labor costs, more exacting specifications, and increased demand resulting from an expanding population and a constantly rising standard of living. Industry recognizes the need for upgrading presently unusable materials and has cooperated with the U.S. Bureau of Mines by providing samples from submarginal deposits and by evaluating the products that USBM upgrades. Following are some examples of recent clay beneficiation work by the Bureau. FIRE CLAY BENEFICIATION At the Rolla Metallurgical Center, Rolla, Mo., the Bureau is conducting research to develop technically and economically feasible mineral-dressing methods to remove quartz, pyrite, and other impurities from submarginal fire clays. The research has been spurred by the growing shortage of high-grade bur-ley, flint, and plastic clays in the Missouri fire-clay district resulting from increased consumption and the low rate of discovery of new deposits of adequate quality. There apparently is ample tonnage of submarginal flint and plastic clays to maintain the industry for many years if such material can be upgraded to commercial quality. Samples have been submitted to USBM by several major producers of refractories, including A. P. Green Fire Brick Co.; Harbison-Walker Refractories Co.; Mexico Refractories Div., Kaiser Aluminum and Chemical Corp.; and Wellsville Fire Brick Co. Research on some samples has been completed and still is in progress on others. The Bureau has found that specimens containing quartz or pyrite in grains coarser than the accompanying clay generally can be upgraded either with a gravity table or hydraulic cyclone. The improvement in quality is notable not only in chemical analysis but in an increase in pyrometric cone equivalent (PCE) of one or more cones. As an example, consider the results attained on a sandy flint—a fine-grained mixture of kaolin and halloysite with quartz and minor quantities of iron and manganese oxides. Chemical analysis was: 35.4 pct alumina (A12O3) and 47.8 pct silica (SiO2). The sample contained 9.2 pct free silica as quartz. The PCE was 33. The sample was crushed to -10-mesh, blunged with water, and then stage-ground to -48-mesh. The ground sample was tabled to yield a clay fraction containing 37.6 pct A12O3, and 45.3 pct SiO2 of which 2.4 pct was free silica. The PCE was 34. Recovery of alumina by this process was 73.6 pct. Concentration of the same clay in the hydraulic cyclone was even more effective in respect to quartz removal. The clay fraction analyzed 38.6 pct A12O3, 45.0 pct SiO2 of which 0.5 pct was free silica as quartz, and had a PCE of 34. Recovery of alumina was 71.9 pct. The hydraulic cyclone was also effective in reducing the pyrite content of a plastic clay which likewise was a mixture of kaolin and halloysite, plus some pyrite, quartz, and carbonaceous material. It analyzed 30.6 pct Al2O3, 52.3 pct SiO2, 2.3 pct Fe2O3, and 0.76 pct S. The sample was blunged and screened through 10-mesh to remove some coarse pyrite, then ground to -65-mesh and cycloned to remove most of the remainder. The final product recovered 81.8 pct of the alumina at a grade of 32.3 pct A12O3, 50.9 pct SiO2, 1.4 pct Fe2O3, and 0.1 pct S. The PCE was 32-1/2, compared with a PCE of 31-1/2 for the crude clay. The fine beneficiated clays, of course, must be pelletized and dried or fired to meet commercial acceptance. This operation has already been solved by industry. Little progress has been made on two remaining problems. One is that of fine-grained impurities, not separable by table or cyclone. Flotation is being investigated to solve this. Although fine pyrite is readily rejected, a satisfactory quartz-clay separation has not been attained. The second problem, a stubborn one, is that of alkali. Samples containing as much as 5 pct potas-

Jan 1, 1961

By William Mikulas Lars Thomassen, Clair Upthegrove

Little work has been done in the field of the nickel-tin binary system. The complete diagram has been investigated on two occasions, but the results are in very poor agreement. The structure of a compound NiSn and the solubility of tin in nickel have been determined by X-ray methods. Several investigations have been made of the liquidus curve, and the compositions of the eutectics have been determined. A study of the literature, however, shows that there is no satisfactory agreement between the data presented in the various papers. The present investigation was undertaken in an attempt to determine the equilibrium conditions, and to correlate X-ray with metallographic data. The equilibrium diagram was determined by thermal and metallographic means, and the solubility of tin in nickel further investigated with X-rays. Powder diagrams were made of the intermetallic compounds, and three of the structures were partly determined. NO attempt was made to determine the range of homogeneity of the intermetallic compounds. Review of the Literature Vigorouxl prepared alloys of tin and nickel containing 74 and 92 per cent of tin. By treating these alloys with very dilute nitric acid or with sodium hydroxide he was able to separate residues, both of which analyzed 66.7 per cent tin. This corresponds to the compound NiSn and was reported as such. Guillet2 made the first investigation of the complete binary diagram Fig 1) The maximum point of the liquidus is at 43.5 per cent nickel. Several solid solution areas were found, and the compound NiSn was included on the strength of Vigoroux&apos;s work. The investigation was

Jan 1, 1937