By Alden B. Greninger

The study of mosaic structure of crystals1 has been confined until recently to the field of theoretical physics. Crystallographers, in general, have neglected the subject, although X-ray crystallographers constantly make use of formulas for intensities of X-ray reflection as modified by mosaic structure. Work on mosaic structure has centered chiefly on the task of proving or disproving the secondary-structure theory of Zwicky,² and very little attention has been paid to the visible imperfections of crystals. A. Goetz has been responsible for most of the supposed experimental confirmations of Zwicky's theory.3 On the other hand, Smckal,4 and Orowan,5 among others, maintain that there is neither theoretical nor experimental evidence to substantiate Zwicky's secondary structure. Lately the subject has been intensively investigated by Buerger,6 one of whose recent papers led to a symposium on mosaic structures.'

Jan 1, 1935

By S. Jana, C. M. Wayman

The reverse transformation of bcc martensite to the fcc phase was studied in an Fe-33.95 wl pct Ni alloy by nzeans oj dilatometry, melallography, and electron microscopy. Upon "slozc" heating (-1°C per min) length cJmnge us temperature plots showed u gradual contracLion over the temperature range 200" to 280"C ,followed by a more abrupt contraction beginning a1 -280°C. Howet,ev, zchen the heating rate was increased -4°C per tnin, no gradual contraction was observed and only the abrupt contraction starting at -2BO"C was found. Thus on slower heating- the AS "temperature" for the subject alloy, unlike the MS temperature, is better defined as a range of temperatures. Both optical and transmissiorl electron microscope observations showed that some of the martensite plates exizibited a partial loss of transformation twins during reversal. The midvib region of the martensite plates disappeaved relatively early duirng the reversal. Metallographic observations slowed that the earliest detectable stage of the rezlerse tvansforrvration begins (axd Moues inulardly) at The Martensens i te - parent interface. At higher temperatirres, the. formation of martensitically reversed jcc plates within the bcc martensite plales was observed. It is concluded that the reverse transformation consists of a diffusion less process (martensitic); but this is ps-obably aided by a prior or simultaneous dijjusiorz-comltvolled process, at leasl in the case of slower heat-ing' experiments. ALTHOUGH numerous investigations have dealt with the parent-to-martensite ("forward") transformation (fcc — bcc) in Fe-Ni alloys, comparatively little is reported on the ("reverse7') martensite-to-parent transformation.'-4 Even though such reverse transformations have been studied in detail in some nonferrous systems, one of the difficulties of studying the reverse transformation in most ferrous mar-tensites is that the martensite decomposes by tempering during heating. However, carbonless Fe-Ni alloys do not exhibit this difficulty since the transformation in these alloys is completely reversible. The present investigation represents an attempt to shed more light on the nature and mechanism of the martensite-to-parent transformation. 1) EXPERIMENTAL PROCEDURE 1.1) Alloy Prepatation. Fe-Ni alloys of compositions near 34 wt pct Ni were prepared from zone-refined iron (99.994 wt pct Fe) and high-purity nickel (99.999 wt pct Ni) by induction melting in recrystallized alumina crucibles in an argon atmosphere, with prior vacuum evacuation to 10"3 mm Hg. The alloys were homogenized by induction stirring in the molten state for 5 min. After solidification, the alloys were further homogenized in evacuated quartz capsules for 96 hr at 1230°C. 1.2) Dilatometry. Slices of the ingot were hot-forged (750°C in air) into approximate rod form and these specimens were then hot-swaged (750°C in air) into long cylindrical rods 0.55 mm diam. From the rods, specimens about 1 in. long were cut. These were then vacuum-annealed for 24 hr at 1200°C, cooled to room temperature, and subsequently transformed to martensite in liquid nitrogen (whereby about 40 pct transformation was obtained). Dilatation measurements were made by observing length changes in a vacuum dilatometer with an externally mounted LVDT sensing element. 1. 3) Preparation of Electron Microscope Specimens. Slices of the ingots were cold-rolled (with intermediate vacuum anneals) to -0.020 in. Out of these rolled sheets, specimens (about 1 by 1 in.) were cut. These were then vacuum-annealed, transformed to martensite by cooling in liquid nitrogen, and subsequently heated from room temperature to various temperatures to effect either partial or complete reverse transformation. These specimens were then chemically polished to 0.002 in. in l:l HsOz (30 pct) and &PO4 (85 pct) solution, and thinned to electron transparency in an electrolyte consisting of 150 g CraOs, 750 ml glacial acetic acid, and 30 ml ~~0.~ Observations were made with a 100-kv Hitachi HU-11 electron microscope equipped with an HK-2A tilting device. 1.4) Optical Microscopy. Metallographic observations were made with a Leitz MM5 metallograph on the same 0.020-in. sheet specimens as were used for electron microscopy and on bulk specimens which were 0.2 in. or more on a side. The chemical thinning solution when cooled below 20°C also served as an etchant for this alloy. Observations of surface relief were made with a Zeiss interference microscope employing a Thallium light source of wavelength 0.54 p. Specimens for interference studies were prepared by two-stage polishing on Buehler vibromet polishers using 0.3 and 0.05 p alumina abrasives. 2) EXPERIMENTAL RESULTS 2.1) Comparison of the MS,AS, and Af Tempera-tures wTth Previous Re sults. The AS aLd Af tempera -tures of several Fe-Ni alloys were determined dila-tometrically. The MS temperatures of the same alloys were determined by continuously lowering the temperature using a mixture of isopentane and liquid nitrogen and observing the highest temperature at which a prepolished specimen showed surface upheavals. For the present the As temperature is defined as the temperature at which an abrupt decrease in length occurs in the dilatation plot. The Ms,As7 and A determinations in the present investigation and those of Kaufman

Jan 1, 1968

By Francis R. Conley, John A. Sievert, John N. Dew

A brief review is presented of the past performance of a number of large, thin, highly permeable reservoirs with low dips in the Bolivar Coastal fields of Venezuela. The performance of these reservoirs indicates that the fluids are segregated vertically within the sand section by gravity. With this assumption, equations are developed which describe the performance under pressure maintenance operations. Methods of solving these equations and results of simple example calculations are presented. Example calculations indicate that under pressure maintenance conditions injected gas tends to {tow preferentially along the top of the sands and that encroaching water has a tendency to flow preferentially along the bottom. The expected performance of segregated fluids is discussed and compared with that of fluids which are uniformly distributed in any sand section. INTRODUCTION The field performance of a number of reservoirs described herein indicates that the fluids are segregated vertically within the sand section by the force of gravity. Thus, it was felt that any method used to predict the future performance of these reservoirs should consider the effects of segregation in the sand sections. A study of the available information on some of the reservoirs suggests that increased recoveries may be expected if the reservoir pressure is maintained by either crestal gas injection or flank water injection. To predict future performance of reservoirs under pressure maintenance operations, a method of analysis was needed which would account for segregation of fluids in the sand sections. Several methods of analysis have been developed to take into account the segregation of fluids in the reservoir as a whole1,3 To our knowledge no method considers segregation of the fluids within sand sections in the manner indicated by the past performance of several reservoirs in the Mara-caibo Basin. This paper outlines part of the work done in studying some of these reservoirs and contains a description of their performance characteristics. The analysis presented is restricted to pressure maintenance conditions, since space limitations prevent a full discus- sion of the development of the mathematical relations and the various methods of solving them. Only a sketch of the development of the mathematical relations is given. The various methods of solving these relations are pointed out, but the actual determination of solutions to various problems are omitted except for one example. It is felt that these results may aid in the study of reservoirs outside the Maracaibo Basin. Some concepts on which the present analysis is based are outlined by D. N. Dietz. However, the analysis presented herein includes several factors not considered by Dietz: (1) variations in permeability and in the cross section, (2) various shapes of the cross section, and (3) the production of fluids. Also, the mathematical development presented by Dietz differs considerably from our corresponding analysis. RESERVOIR CHARACTERISTICS The reservoirs under consideration, large and thin, with low dip and high permeability, are large to the extent that they contain from 0.5 to over four billion bbl of oil initially in place. The section thicknesses vary from 100 to 400 ft and the lengths from 10,000 to 40,000 ft. Thus, a length-wise cross section of the producing formation appears to be long and thin. The dip angles vary from 0 to 6 degrees and the average permeabilities vary from 0.5 to over three darcies. The reservoirs contain from 20 to 50 per cent shale inter-laminated with the productive sands. Most shale breaks within the major sands do not correlate from one well to the next, and correlation is often difficult, even between wells drilled from the same location. However, it is often possible to correlate the shale breaks between major sands for some distance. Herein we are concerned with the performance of reservoirs containing oil of gravities over 20" API. Past reservoir performance indicates good pressure communication and, in cases where pressure sinks have developed, large amounts of fluid migration have occurred. Few of the reservoirs have had initial gas caps, but also, few have been found to be highly under-saturated. Due to gravity segregation, secondary gas caps usually form before the pressure has been reduced more than 25 per cent of its initial value. The effect of gravity has not only been apparent on a reservoir-wide basis, but has also caused segregation of the reservoir fluids in productive sections. Proof of this is found from the results of selective well tests, workovers, and electric and various other types of logs. Evidence that

By A. Blake Caldwell

The Anaconda Company, an organization of mining people, enters a new world of copper production as it brings on stream its recently constructed Twin Buttes operation some 25 miles south of Tucson, Ariz. Twin Buttes comprises the largest earth-moving task performed in the history of mining. Some people liken this job to moving enough earth and rock to complete the famed Aswan High Dam in Egypt. In all, some 236 million tons of overburden and rock were removed from over the ore deposit.

Jan 1, 1970

By Norman Pilling

The micrographic analysis of silicon steels is possible if a dilute solution of nitric acid and methyl alcohol in nitrobenzol is used. The action of this reagent differs from that of sodium picrate in that there is no persistent deep-seated staining and the solution is used cold. THE technical difficulties hampering the metallographic analysis of silicon steels are chiefly the result of the extreme corrodibility of these alloys. The addition of silicon to iron in increasing quantities, up to about 6 per cent., rapidly increases the susceptibility of the alloy to chemical attack, not only in acid solution, but in water. This renders the preparation of metallographic sections very difficult, because of a non-selective attack upon the finely polished surface by the water used as a lubricant in polishing. This water attack masks the true structural details revealed by suitable etching reagents. It is thus necessary to use alcohol as a polishing lubricant in the last stages of preparation and to avoid all etching reagents having an aqueous base. A specific reagent for the identification of iron carbide in ferrous alloys, and the one hitherto used almost exclusively by metallurgists, is an alkaline aqueous solution of sodium picrate, which stains this constituent selectively. Its application to silicon steels has not proved successful, as its distinctive selective action is more or less completely hidden by the general attack of the aqueous solvent on the silico-ferrite, greatly accentuated by the fact that this reagent must be used at its boiling temperature (105° C.). Thus, a powerful metallographic aid to the study of the higher silicon alloys, such as transformer steels, is lost. A new reagent has been developed for the purpose of overcoming this difficulty. It is with some hesitation that the list of etching reagents, already overburdened, is increased, but the properties of this new reagent are advantageous in several ways and a definite field for it may be found in the metallography of ferrous alloys.

Jan 1, 1924

By G. H. Alani, H. T. Kennedy

One of the major difficulties in predicting the performance of oil reservoirs from their early pressure history lies in the uncertainty of estimating the volume of the liquid hydrocarbons contained in them. As a first step in filling this need, an equation was developed to determine the Inolal liquid volume of pure hydrocarbons over a wide range of temperature and pressure. The second step consisted of adapting the equation to apply to mixtures, with the heary hydrocarbons expressed as c The equatious are similar in form to van der Waals equation. hut the constants a and b tire considered as furnctions of temperature. In addition to the gas constant R, there are four constants characteristic of each hydro- When comptired with experimental values jound in the literal the. the average absolute deviation in the calculated molal volumes is found to be a Maximum of 0.33 per -cem for any of the pure liquid hydrocarbons studied. This maximum deviation was that found when comparing the calculated and observed values over a temperature range of 86° to 482°F and a pressure range from the bubbl-point ro 10,000 psis. The equations expressing the correlation for. mixrurrc were developed from 647 experimental measure-rilents of volume on 47 bouom-hole samples covering ; temperature range of 72" to 250°F and a pressure znge from bubble-point ro 5,000 psig. The average absotute deviation was found to he 1.6 per cent with the maximum for any measurement of 4.9 per cent. INTRODUCTION Accuratc information of the pressure-volume-temper-iiture behavior of hydrocarbon liquids is of considerable importance in the field of both applied and theoretical science and, especially, in the solution of petroleum reservoir engineering problems. These PVT relationships can be expressed graphically, in tabular form or as equations of state. Equations of state for gases have been developed based on the ratio of pressure, temperature and volume to the pressure, temperature and volume at the critical points of the hydrocarbons. These equations have been successful in yielding values fairly accurate for reservoir engineering purposes. For liquids, however, relations of this type are more complex and have not yielded useful results. The composition of reservoir liquids is normally expressed in terms of the moles of hydrocarbons C,? C,. C,. elc, per mole of mixture. The composition must include the fraction of a mixture such as C,,, which cannot be separated with reasonable time and effort into specific hydrocarbons. Although there are several equations of state having variable degrees of accuracy applicable to pure liquid hydrocarbons, none includes a means for estimating the volume of mixtures as a function of temperature. pressure and composition expressed in this manner.

By N. J. Grant, A. W. Mullendore, Y. Ishida

Creep tests were performed at 500°F on polished specimens of A1-3 pct Cu at stresses of 2000, 4000, and 6000 psi. The effects of the size and distnbution of the second phase were studied in connection with the mechanisms of deformation, especially grain boundary sliding. Although the amount of grain boundary sliding varied considerably for the different heat treatments, yestriction of grain boundary sliding is not due primarily to precipitate on the grain boundary. NUMEROUS prior investigations of grain boundary sliding, notably those of McLean, 1 Rachinger, 2 Rhines, Bond, and Kissel, 3 and Brunner and Grant,4 have established the importance of this phenomenon in the deformation of pure aluminum and its solid-solution alloys at elevated temperatures. An extension of this kind of study to the case of a simple two-phase structure is an important step towards understanding the deformation behavior of more complex alloys. A two-phase A1-3 pct Cu alloy was selected for this study. The creep behavior of alloys in this system has been studied by Sully and Hardy,5 by Underwood, Marsh, and Manning,' and by Pelloux, Chaudhuri, and Grant.7 In these studies, the prior heat treatments were such that some precipitation took place during the tests in most cases. Pelloux, Chaudhuri, and Grant7 studied the creep of A1-2 and 3 pct Cu alloys in the overaged condition. Their results indicated that the structure most effective in promoting high-temperature strength consisted of a fine, closely spaced grain precipitate and large, widely spaced particles on the grain boundary. The present work consists of quantitative meas- urements of grain boundary sliding during creep of an A1-3 pct CU alloy with four different precipitate distributions. The aims were to quantitatively define the role of the second phase on grain boundary sliding, and to obtain information regarding the mechanism of grain boundary sliding. MATERIALS AND PROCEDURE A high-purity A1-3 pct Cu alloy, kindly supplied by Alcoa, was used in this investigation. The composition of the alloy in weight percent was as shown in Table I. This composition is such that A12Cu exists as a second phase at temperatures below 850°F. A homogeneous grain size of 0.6 to 0.8 mm was obtained by annealing the machined test bars for 5 min at 1000°F, furnace cooling to 930°F, and homogenizing for 5 hr. Following the recrystalli-zation and homogenizing anneal, four different heat treatments shown in Fig. 1 were utilized. The F7 and F5 treatments utilize a furnace cool to the aging temperature while Q7 and Q5 have a water quench from the homogenization temperature before aging. Figs. 2 to 5, and Table 11, show the size and shape of precipitate dispersions obtained with the above heat treatments. The heat treatments produce variations in the dispersion both in the grains and along the grain boundaries. Precipitate particles along the grain boundaries are rounded and large (about 1.5 p diameter) in the F5 and F7 structures (Figs. 3 and 5). The grain boundary precipitate was somewhat smaller (0.9 p diameter) in the Q7 structure and no grain boundary precipitate was detected in the Q5 structure using light microscopy. The pre-

Jan 1, 1964

By G. S. Tint, M. Herman, V. V. Damiano

Dislocation arrays and substructures were studied in cadmium doped zinc crystals using a newly devised etching technique. Cadmium precipitates delineating the dislocations were revealed by etching a surface closely parallel to the (0001) slip plane. Cinephotomicrography of the continuous etching process revealed the three-dimensional aspects of dislocations in the bulk crystal. Dislocation etch patterns were studied in both deformed and annealed crystals after suitable aging at room temperature. The effect of annealing was evidenced by a rearrangement of the dislocations into low-angle boundaries and hexagonal networks. ETCH pit techniques have been used extensively to study dislocations in both deformed and annealed bulk metal crystals. Ideally one hopes to obtain a one-to-one correspondence between the etch pits and the points of emergence of the dislocations at the surface. One then attempts to deduce the way in which dislocations are arranged in the bulk crystal from the arrangement of etch pits on the surface. It is clear that one can obtain only limited information of the dislocation configurations inside the crystal from etch pit studies of single surfaces. Considerably more information is obtained if one is able to follow the course of the dislocations through the crystal using progressive etching technique. Techniques of this sort were used by Gilmanl to study dislocations on the slip planes of NaCl crystals and by Damiano and Tint2 to study dislocation arrangement in zinc crystals grown from the melt. The present paper makes use of a technique first described by Tint and Damiano3 to observe and continuously record the dislocation structures which appear while a crystal surface was being progressively etched. Studies were made on cleaved (0001) surfaces to reveal the dislocations along their length on the surface closely parallel to the slip plane. The technique for revealing segments of dislocations along their length by etching is well known. Wilsdorf and Kuhlmann-wilsdorf4 revealed disloca- tions along their length in aluminum containing a few percent copper, when precipitates segregated along the dislocations. The technique was used by Low and Guard5 to study dislocation configurations on the slip plane in Fe-Si alloys containing carbon. In the present work the technique was applied to zinc containing cadmium since it was shown by Gil-man6 that a cadmium-rich phase could be made to precipitate from supersaturated solutions along dislocations in zinc. Segments of dislocations delineated by the precipitates were revealed by etching a surface prepared by cleaving the crystal. The three-dimensional nature of dislocations and substructures was thus studied from the cinephotomicro-graphic record of the continuous etching process. EXPERIMENTAL Single crystals of zinc containing the order of 0.1 pct Cd were prepared by slowly lowering a graphite crucible containing the melt through a temperature gradient of 15°C per cm at a rate of 1.5 X 10-3 cm per sec. "As grown" crystals were aged for periods of 1 month at room temperature, then cleaved in liquid nitrogen, and etched according to the procedure used by Gilman.' The etchant containing 32 g of CrO3, 6 g of hydrated Na2SO3 in 100 ml of water behaved as a chemical polish for zinc and etch pits were produced at the site of precipitates or inclusions. After the precipitates or inclusions were removed from the surface, the etch pits left behind were eventually polished smooth. This behavior enabled one to continuously observe the surface while the specimen was immersed in the etchant. Best results were obtained when the specimen surface was vertical and the reaction products of polishing were continuously removed by gravitational convection. Some crystals were heavily deformed in excess of 25 pct strain, others were lightly deformed the order of a few pct by compression such that the deformation occurred essentially by basal glide. Some crystals were etched immediately after deformation, others were allowed to age at room temperature for several weeks prior to etching. Heavily deformed crystals were annealed at various temperatures and etched on the cleavage plane immediately after annealing, others were allowed to age at room temperature for several weeks prior to etching. The etched structures of deformed and annealed structures were studied. Similar experiments were conducted on 99.9999 pct pure zone refined Tadanac zinc crystals which

Jan 1, 1963

By H. J. Levinstein, H. J. Guggenheim, C. D. Capio

An optical incestigation of the phase transformations in RbFeF, has been conducted. Details of the ferromagwetic phase transition and the metamagnetic state are disczrssed. The three-dimensional magnetic domain structure existing in bulk crystals of RbFeF3 is described, as well as the effect of the magnitude and direction of the applied magnetic field on the domain struclure. The strong magnetoelastic interaction in RbFeF, is demonstrated. The results of the direct observation of the role of dislocation subboundaries and slip bands as nucleation sites and as pinning sites for magnetic domain walls are reported. THE perovskite compound RbFeF, has recently been shown to exhibit three magnetic states.''' Above 102°K it is paramagnetic, between 102" and 87°K it is antiferromagnetic. and below 87°K it is ferromagnetic (i.e., exhibiting remanence) with a modification of the magnetization occurring at 40°K. The changes in magnetic structure at 102o, 87°. and 40°K are accompanied by shear transformations to successively lower crystal symmetry classes.3 At 102°K a second-order phase transformation to a tetragonal crystal structure occurs. The c/o ratio increases with decreasing temperature to a value of 1.0034 at 87°K where the crystal undergoes another shear transformation to an ortho-rhombic crystal structure. The magnetic modification at 40 K is also accompanied by a shear transformation to a lower crystal symmetry. RbFeF3 is unique in that in the ferromagnetic state it is transparent in the bulk to visible light, has a low saturation magnetization, a large magnetic rotation. and has good optical properties.' All these features make it an ideal material for the investigation of magnetic domain structures in bulk crystals. In addition a dislocation etch has been developed which reveals the point of emergence of dislocations with the (100) surfaces of RbFeF3,5 making it possible to determine the dislocation arrays in the material. As a result domain wall dislocation interactions can be observed in the bulk crystal. In this paper we report on 1) the crystallography of the phase transformations in RbFeF3. 2) the domain configurations as a function of magnetic field and crystal orientation. 3) the interaction of dislocations and magnetic domain walls in RbFeF,. EXPERIMENTAL PROCEDURE Since the temperature range of interest is below room temperature the dewar shown in Fig. 1 was employed. It was designed to fit on the stage of a Leitz panphot metallograph, and permitted examination of the sample at a magnification up to 150 times. The dewar consists of a double-walled glass cylinder bent into an L shape. The space between the walls is evacuated. The viewing wirldows were made of four optically flat quartz discs aligned parallel to each other and sealed to the sides of the concentric cylinders. The specimens were mounted in a holder attached to a flexible plastic shaft. Various holder designs were employed depending upon the type of observations to be made. For studies of the phase transformation between the antiferromagnetic and ferromagnetic state the holder shown in Fig. 2(d) was employed. This holder permitted accurate temperature control at 82" to 88°K by balancing the heat input from the carbon resistance heater against the heat loss to a heat sink immersed in liquid N2. Magnetic field studies were conducted by employing the holders shown in Figs. 2(a) and (b). The holder shown in Fig. 2(n) has a solenoid imbedded in it. such that the magnetic field direction is in the same direction as the incident light. The magnetic field provided by the holder in Fig. 2(b) is perpendicular to the incident light direction. The holder in Fig. 2(r) was employed when observations of the specimen were desired while an elastic bending stress was applied to the sample. The stress was applied to the sample by pulling a wire from outside of the dewar. The wire was attached to a lever pivoted on the holder. which caused the knife edge of the lever to push against the sample. The crystal growth and the sample preparation were described previously.' PHASE TRANSFORMATIONS The first phase transformation in this system is from the cubic perovskite structure to n tetragonal

Jan 1, 1970

By K. M. Rolls, J. Wulff, D. A. Colling

Solid-solution alloys of the Ta- Ti system containing up to 70 at. pct Ti were melted and fabricated into wire. Steady magnetic-field measurements of cold-worked wires at 4.2°K indicate that the resistive critical field increases smoothly with increasing titanium, reaching a maximum of 93 kG (J = 1 amp per sq cm) for a composition of about 50 at. pct Ti. The composition dependence of the resistive critical field indicates it is largely paramagnetically limited for alloys containing more than 35 at. pct Ti. For cold-worked wires the value of the critical current density, Jc , was found to be insensitive to composition changes for compositions in excess of 20 at. pct Ti. It was observed that Jc could be increased by final-size heat treatment at 400°C without altering the value of- the resistive critical field. Experimental data are used to calculate the electronic specific-heat coefficient and the "upper critical field" for the alloys studied. THE effect and importance of metallurgical structure on superconducting properties have been summarized by Livingston and Schadler.1 Specific work on solid-solution alloys such as Nb-zr2-7 and Nb-Ti5-7 have shown that critical current density (Jc) and superconducting transition temperature are structure-sensitive. Berlincourt et al.6,8,9 in their studies of transition-metal alloys find that Ta-Ti alloys remain superconducting at fields comparable to Nb-Ti alloys. 6,8 Transverse critical current tests of a Ta-10 at. pct Ti alloy10 and longitudinal critical current tests of a Ta-25 at. pct Ti alloy1' indicate that such alloys are capable of carrying high currents at intermediate fields (-40 kG). The work reported in the present paper was undertaken to explore the superconducting properties of further compositions in the Ta-Ti alloy system as well as the structure sensitivity of the superconducting properties. I) EXPERIMENTAL PROCEDURE Alloys were prepared by melting tantalum (Fansteel Metallurgical Corp., 99.96 pct purity) and iodide, crystal bar titanium (Foote Mineral Co., 99.92 pct purity) mixtures in an arc furnace on a water-cooled copper hearth using a tungsten electrode. Melting was accomplished in a purified, gettered argon atmosphere at pressures from 250 to 400 Torr. Each alloy was turned and remelted fourteen times to assure complete mixing of tantalum and titanium. Ex- cessive coring in the cast samples was, nevertheless, observed. This was somewhat reduced by annealing in vacuo at 1000°C for 13 hr. The ingots were then machined to 0.250 in. diam, jacketed in Type 304 stainless-steel tubing, and swaged to 0.140 in. diam. They were then drawn to 0.010-in.-diam wire. Alloys containing up to 70 at. pct Ti were readily cold-drawn to wire in this manner. Later experiments showed that oxygen additions up to -3000 ppm could also be cold-worked into wire. Test samples for superconductivity measurements in the 2-in, air-core Bitter solenoids of the M.I.T. National Magnet Laboratory were prepared from 10-in. lengths of 0.010-in.-diam wire, cleaned of residual wire-drawing lubricant. Current contacts were made by clamping clean copper tubing over both No. 18 current lead wire and the ultrasonically indium-tinned ends of the specimen wire.12 Potential leads of No. 32 copper wire were connected to the specimen by ultrasonic soldering in an indium bath. The potential lead separation was about 4 cm, corresponding to the circumference of the Bakelite rod to which the wire was affixed with half-mil Teflon tape. The final specimen configuration is shown in Fig. 1. Specimens were lowered into a liquid helium bath (4.2oK) in a double solenoid dewar and positioned so that the maximum magnetic field was oriented transverse to the wire axis of the gage section. Measurements were made by passing a current through the specimen at a preset solenoidal magnetic field. The current was increased until a 1-pv potential difference appeared across the gage section (1/4 µv per cm). At low magnetic fields, however, it was not possible to use this criterion because power-dissipation difficul-

Jan 1, 1967

By W. O. Philbrook, L. D. Kirkbride

IN the normal operation of the iron blast furnace, reduction of the iron oxides is accomplished almost entirely above the tuyeres.' Blast furnace slags usually contain less than 0.5 pct FeO, although higher values may occur with abnormal operation. There is reason to conjecture, however, that incompletely reduced ore may sometimes reach the hearth and enter the slag as a result of heavy slips or, perhaps, even from cores of excessively large lumps of a charge material of poor reducibility. The possibility of reoxidation of iron droplets falling in front of the tuyeres has been considered by several writers. It would be of interest, to know how rapidly iron oxides reaching the slag for any of these reasons could be reduced by reaction with coke or with the high carbon liquid iron in the hearth. In comparison with the hundreds of papers that have appeared on various aspects of the reduction of solid iron oxides by gases and in the presence of several forms of carbon, little work has been published on the reductioin of liquid oxides or slags. Dancey measured rates of reaction of the pure liquid oxides, both FeO and Fe,O,, with molten iron containing about 4.3 pct C. The oxide was dropped into the cup formed in the upper surface of the iron by rotating the crucible and melt. Under these conditions, reduction of either FeO or Fe,O., was completed in less than 10 sec. The present study was concerned with the reduction of FeO from blast furnace-type slags containing less than 5 pct FeO and melted over carbon-saturated iron in stationary graphite crucibles. The results were considerably different from those found by Dancey, as will be discussed later. Although this work is of interest in relation to hearth reactions in the blast furnace, interpretations must be made with caution because the experimental conditions do not duplicate those within a furnace and may not even lead to the same reaction mechanism. The authors were motivated in undertaking this work by an additional interest—the part played by FeO reduction in the mechanism of de-sulphurization of iron by slags under similar experimental conditions. Derge, Philbrook, and Goldman eveloped detailed experimental evidence to support a three-step mechanism for desulphurization like that originally proposed by Holbrook and Joseph' (These reactions are written in molecular form for convenience, but this is not intended to imply the existence of molecules of FeS in the bulk metal phase nor to deny the likelihood of ionic reactions in the slag.) Earlier work by Chang and Goldman" had shown that the overall reaction follows first-order kinetics with respect to sulphur and that the rate of reaction is proportional to the slag-metal interface area, which observations have been confirmed by subsequent work. Later studiese,' have established the influence of al.loying elements on the first and last steps of the reaction. This paper reports a study of step 3 alone, uncomplicated by the simultaneous process of sulphur transfer. Apparatus and Procedure The experiments were made in a conventional high frequency induction furnace powered by a 35 kva Hg spark gap converter. The graphite crucibles used for most of the runs were 14 cm (5.5 in.) deep and 4.8 cm (1.9 in.) ID with 0.75 cm (0.3 in.) wall. An insulating cover with a small opening for withdrawing samples was used to minimize heat loss and infiltration of air into the furnace. The crucible was charged with 300 g of carbon-saturated iron and either 65 or 100 g of prefused slag analyzing 38.0 pct SiO,, 15.4 pct A10 and 47.1 pct CaO. To obtain the cleanest possible interface at the start of the reaction, the metal and slag were brought to temperature together to prevent the rejection of kish graphite that would have been caused by the chilling effect of a large addition of cold slag to carbon-saturated iron. After temperature control had been established, the desired amount of iron oxide was added in the form of a prefused slag of composition 73.6 pct FeO, 7.7 pct AWX and 19.0 pct SiOl. This slag addition was observed to be molten in somewhat less than 1 min, and a very vigorous reaction proceeded for 1 to 2 min after its introduction. Zero time was taken as 2 min after the ferrous silicate slag addition. Slag samples weighing about 0.5 g each were taken periodically by a copper chill sampler." The weight of the initial slag was large relative to the weight of samples removed, so that the slag weight never varied by more than 5 pct during any run. Temperature was measured by a calibrated W/Mo thermocouple immersed in the metal, with a graphite tip cemented over the fused silica protection tube to prevent attack by slag and metal. After some difficulties with uncertain temperatures during the first two runs, the practice adopted to position the thermocouple for reproducible results was to lower the protection tube to touch the bottom of the crucible and then raise it 0.5 cm. The apparent temperature gradient between the bottom of the crucible and the top of the slag was found to be 15°C (27°F). but much of this spread was probably the result of inadequate immersion of the protection tube to off-set conduction losses along the graphite tip when the thermocouple was inserted only into the slag. The temperature of the bath was controlled within 25°C (9°F) during a run.

Jan 1, 1957

By F. P. Bullen

Empirical relationships between fracture stress, orientation angle, and diameter of crystal have been determined at 77°K. Orientation ranges of markedly different behavior were found—a law of constant normal stress&apos; of value a (diameter)-1/2 for the fracture of ductile crystals, and a condition of shear stress (or strain) for more brittle crystals. The observations are not consistent with current theories. An interpretation is advanced which is also applicable to observations on the effect of prestrain at room temperature on the subsequent fracture stress at 77°K and to the effect of cyclic stressing on the cleavage strength.&apos;&apos; The law of constunt normal stress&apos; and the brittle ductile transition are also explained. The interpretation is more consistent with the initiation of cracks by intersecting dislocations than with theories based on stress -concentration by dislocation arrays. ZINC single crystals are particularly suited to the study of cleavage because fracture occurs on the basal plane over a wide range of crystal orientations. Analysis of the conditions of stress and strain at fracture in crystals of different orientations should indicate which parameters control the cleavage process. Unfortunately, controversy has arisen over the correct empirical relationship between tensile fracture stress and orientation. Schmid&apos;s observations1,2 favored a &apos;law of constant normal stress&apos;, as observed in other materials.2 For zinc, however, the observed values are far below the theoretical strength and cannot represent the true limit of cohesion between neighboring atomic planes. Hence, the interpretation of such a &apos;law&apos; is not straightforward. Deruyttere and Greenough3,4 found a complex variation between tensile fracture stress and orientation; this variation did not agree with a &apos;law of constant normal stress&apos;. Two theories have been advanced to account for their observations: a) the propagation of cracks from low-angle boundaries,5 and b) the release of energy from piled-up dislocations during crack-propagation.4 The present work resolves the apparent discrepancy between the observations and shows that neither of the above theories are applicable to the tensile fracture of zinc single crystals. A phenomenological explanation, along the lines suggested by Gilman,&apos; is advanced and successfully applied to previously unexplained effects. EXPERIMENTAL DETAILS &apos;Crown Special&apos; redistilled zinc was used, except for one comparison series op tests using &apos;Tadanac&apos; electrolytic zinc. Crystals of 1 mm diam, subsequently called &apos;1 mm crystals&apos;, were grown from the melt in vacuo in precision-bore Pyrex tubes internally coated with graphite. Several specimens 1 in. long were cut from each crystal and chemically polished. Jigs were used to minimize handling strains, and crystals were mounted in the Polanyi machine the day prior to testing to allow recovery from any such strains. One-mm crystals were chemically polished for long periods to obtain 0.1 mm (approx) crystals. One-mm crystals were cemented into miniature gimbals by &apos;Araldite&apos; casting resin. The Appendix gives the reasons for using gimbals and the results obtained by other methods. More complete details of all techniques are given elsewhere.7 The symbols and terminology used are as follows: X = orientation angle (angle between tensile axis and line of greatest slope in the basal plane). T = tensile stress (on true cross-section) S,N = shear and normal stress (components of T with respect to the basal plane) ? = shear strain D = crystal diameter. The subscript &apos;f&apos; will be used to denote values at fracture. PART I-ANNEALED CRYSTALS EXPERIMENTAL OBSERVATIONS One-mm crystals were used to establish the variation of fracture stress at 77°K with orientation at fracture (Xf), Fig. 1. For 18 deg = Xf = 55 deg, a &apos;law of constant normal stress&apos; was observed. For Xf > 55 deg, the fracture condition approximated to a constant shear stress. At Xf< 18 deg, twinning occurred before fracture so that the results were not typical of homogeneous single crystals,4,8— such specimens will not be considered herein. The dependences of fracture stress upon Xf were of similar type for 6 mm,* 1 mm, and 0.1 mm crystals,

Jan 1, 1963

WE the undersigned, being all persons of full age and citizens of the United States, and a majority residents of the State of New York, desiring to form a corporation pursuant to the provisions of the Membership Corporations Law for the purpose of incorporating, as provided in Section 6 of Article I. of said law, the existing unincorporated association known as American Institute of Mining Engineers, do hereby make, acknowledge and 6le this Certificate for that purpose, and do Certify as follows: I. That the American Institute of Mining Engineers is an unincorporated association organized and existing with the object of promoting the arts and sciences connected with the economic production of the useful minerals and metals and the welfare of those employed in these industries by means of meetings for social intercourse and the reading and discussion of professional papers, and to circulate by means of publications among its members and associates the information thus obtained. 11. That the persons duly appointed or designated to manage the affairs of said association are designated by the rules thereof Members of its Council; that the under- signed are all members of said Council as the same was constituted on the 29th day of December, 1904.

Jan 1, 1944

WE the undersigned, being all persons of full age and citizens of the United States, and a majority residents of the State of New York, desiring to form a corporation pursuant to the provisions of the Membership Corporations Law for the purpose of incorporating, as provided in Section 6 of Article I. of said law, the existing unincorporated association known as American Institute of Mining Engineers, do hereby make, acknowledge and 6le this Certificate for that purpose, and do Certify as follows: I. That the American Institute of Mining Engineers is an unincorporated association organized and existing with the object of promoting the arts and sciences connected with the economic production of the useful minerals and metals and the welfare of those employed in these industries by means of meetings for social intercourse and the reading and discussion of professional papers, and to circulate by means of publications among its members and associates the information thus obtained. 11. That the persons duly appointed or designated to manage the affairs of said association are designated by the rules thereof Members of its Council; that the under- signed are all members of said Council as the same was constituted on the 29th day of December, 1904.

Jan 1, 1941

By W. D. Robertson, W. L. Phillips Jr.

Stress-strain curves were obtained for single crystals of alpha brass in tension and in direct shear. Specimens were strained various amounts in a given slip direction, unloaded, and immediately strained in a second slip direction 60°, 120°, or 180&apos; from the original slip direction. Crystals strained in tension and direct shear had comparable critical resolved shear stresses and stress-strain curves. The density of slip lines in direct shear and in tension was essentially the same. The stress-strain curves obtained in shear were independent of initial orientation, choice of {111 } slip plane, choice of <110> slip direction, prior annealing temperature, and rate of cooling after annealing. There was no recovery after annealing for 4 hr at room temperature or 200°C; recovery was observed after 4 hr at 400°C. The crystals showed no asterism and mechanical properties were completely recoverable up to 20 pct strain. It was found that there is a barrier to slip in all latent close-packed directions, and that the magnitude of these barriers, evaluated at 3 pct strain, is proportional to prior strain and independent of the choice of latent direction in the {111} plane. The formation of Cottrell-Lomer barriers is discussed as a possible explanation for the hardening of the latent systems. AN idealized concept of plastic deformation indicates that a single crystal should yield at some stress that is dependent on crystal perfection and it should then continue to deform plastically by the process of "easy glide," which is characterized by a linear stress-strain curve and a low coefficient, ds/dE, of work-hardening. Hexagonal metal crystals generally conform to this ideal concept of laminar flow. In face-centered cubic metals the range of easy glide is always restricted in magnitude and it is strongly dependent on orientation, composition, crystal size, shape, surface preparation, and temperature. Since one of the principal differences between the two crystal systems, both of which deform by slip on close-packed planes, is the existence of secondary (latent) slip planes in the face-centered cubic crystals, it has been proposed that the transition from easy glide to turbulent flow, characterized by rapid linear hardening, is due to slip on secondary planes intersecting the primary plane.&apos;-.; However, the characteristic differences between individual face-centered cubic metals remain to be explained; in particular, it is not clear why the range of easy glide should vary so greatly in different metals and alloys similarly oriented for single slip. An investigation and comparison of different metals with respect to latent hardening on the primary slip plane should provide some of the information required to specify the necessary and sufficient conditions governing the transition from easy glide to turbulent flow. But, in order to accomplish this purpose, plastic strain must be produced by simple shear in a chosen plane and in a predetermined direction by some form of directed shear apparatus, the results of which must be correlated with the corresponding tension experiments. Two such experiments have been performed previously with zinc and with aluminum. Edwards, Washburn, and Parker" and Edwards and Washburn7 found that the strain-hardening coefficients in two latent directions in the basal plane of zinc were the same as in the primary direction. However, to initiate and propagate slip in either the [2110] or the [1210] direction, following primary slip in the [1l20] direction, it was necessary to increase the stress above that required to continue slip in the primary direction; when the direction of shear was reversed 180 deg plastic strain began at a much lower stress than that required to initiate slip in the original direction and the stress to propagate slip in the reverse direction was lower than the stress to continue slip in the forward direction, indicating a permanent loss of strain-hardening. Rohm and Kochendorfer observed softening in aluminum for all latent close-packed planes and directions. They also found that the critical resolved shear stress obtained from their direct shear apparatus was 50 pct lower than the value obtained from conventional tension tests, that the stress-strain curve was linear at 50 pct plastic strain, and that slip lines were not visible at strains less than 30 pct. At present it is uncertain whether these diverse results correspond to real differences in work-hardening characteristics of the close-packed planes of aluminum and zinc or to differences in experimental technique. In view of Read&apos;s analysis &apos;" of the stress distribution in the experimental arrangement of Rohm and Kochendorfer, there is some reason to question the significance of the latter results. In order to resolve this problem it is necessary to re-valuate the direct-shear technique and either repeat the previous measurements or investigate a third system. The latter choice seemed most likely to produce significant results with respect to work-hardening, and accordingly, it was decided to examine the hardening characteristics of the latent slip directions in alpha-brass. The choice of alpha-brass was dictated by the fact that easy glide is more extensive in this alloy than in any other face-centered cubic metal or alloy and, presumably, more nearly like the idealized hexagonal system. Experimental Procedure Crystals were made in graphite by the Bridge-man method in the form of cylinders, 11/2 in. diam and 8 to 9 in. long. Material for the crystals was 70/30 brass containing the following impurities:

Jan 1, 1959

WE the undersigned, being all persons of full age and citizens of the United States, and a majority residents of the State of New York, desiring to form a corporation pursuant to the provisions of the Membership Corporations Law for the purpose of incorporating, as provided in Section 6 of Article I. of said law, the existing unincorporated association known as American Institute of Mining Engineers, do hereby make, acknowledge and 6le this Certificate for that purpose, and do Certify as follows: I. That the American Institute of Mining Engineers is an unincorporated association organized and existing with the object of promoting the arts and sciences connected with the economic production of the useful minerals and metals and the welfare of those employed in these industries by means of meetings for social intercourse and the reading and discussion of professional papers, and to circulate by means of publications among its members and associates the information thus obtained. 11. That the persons duly appointed or designated to manage the affairs of said association are designated by the rules thereof Members of its Council; that the under- signed are all members of said Council as the same was constituted on the 29th day of December, 1904.

Jan 1, 1936

By W. P. Blake

FORGING under the hydraulic press, which was introduced by Haswell in the year 1861, at the machine shops of the Imperial State Railway Company of Austria, has since been greatly improved, so that at the present time there are very few parts of machines which cannot be produced in this way, and at no greater cost than iron castings. The process is now used at Vienna chiefly for such parts of locomotives as cross-heads, link-bars, axle-box frames, etc., especially where the form is intricate, and there are many angles and projections. These objects weigh from 50 to 150 lb. or more, and it is claimed for them that they are not only much cheaper than ordinary forgings, but are much more regular in form and stronger. The results which Mr. Haswell has attained, after years of patient experimenting, were well shown in the Austrian Department of the Vienna Exhibition by a collection of the pressed objects in iron and steel, just as they left the moulds, with some of them cut asunder longitudinally and the surfaces etched, so as to show the internal structure or direction of the grain. Through the courtesy of Mr. Haswell and his son I saw the hydraulic presses in full operation at the works, drawing down large Bessemer ingots, cutting them up into blocks of convenient size, and forming various parts of locomotives. They have two large hydraulic presses in use; the largest, with a piston 24 inches diameter, gives 1200 tons pressure, and the second, with an 18-inch piston, gives 600 tons pressure. The pressure in the pumps is 600 atmospheres. The action is vertical ; the piston descends upon the work, and for forging ingots is armed with a hammer-like head. An ingot of No. 7 soft Bessemer steel, which was forged in my presence, weighed 2030 lbs. One end being placed upon the anvil, the piston is brought slowly down and crowded into the mass as if it were putty or dough, forcing it each way, but chiefly in the direction of the length of the ingot, this being the narrowest section of the anvil and hammer. The piston is then raised and the ingot is moved forward for a second squeeze, and so on, until the first half of the ingot has been reduced in thickness, when it is turned on edge and the operation is repeated. The ingot is then turned end for end and forged until the whole length has been re-

Jan 1, 1874

By Henry Fay

The erosion of guns is a complex problem which can be solved only by a detailed study of all the factors involved. In the present paper it is proposed to submit the results of observations and experiments which have extended over several years. Certain facts have been established and preliminary reports have been published.&apos; Conclusions have been reached since then which, it is believed, are worth presenting for the purpose of promoting discussion, and with the hope that ultimately the whole truth will be known. The particular phase of the problem which will be presented here is the hardening of the inner surface of the gun tube. It has been known for a long time that after firing a large caliber gun for some time, the surface of the metal becomes hard and brittle, cracks, and wears away.2 The character of this phenomenon may be learned by an examination of some results which are typical, obtained from a detailed study of a 12-in. gun. The gun was trepanned and rings representing various sections of the gun were cut out for examination. The first ring represented the metal at the muzzle end, and the other rings were removed at approximately 120, 240, 325 and 337 in., respectively, toward the breech end. The appearance of the surface of the metal in the different sections is shown in Fig. 1. The greatest amount of wear and maximum amount of hard surface layer was found in section marked E, which is nearest the powder chamber and at the beginning of the rifing; the maximum amount of cracking in D; the maximum amount of copper deposition in C. Section B showed heat cracks on both lands and grooves, and section A showed heat cracks on the driving edge of the lands only. There was much flow of metal in both sections E and D, and there was progressively less effect noticeable toward the muzzle end. The polished cross-section of these same pieces is shown in Fig. 2. The extent of the erosion is greatest nearest the powder chamber, and diminishes toward the muzzle end.

Jan 1, 1917

By E. R. Dean

A wire-feed mechanism has been employed to fabricute metal alloy film resistors to various sheet resistivities on oxidized silicon substrates. The effect of several thousand hours storage in air at elevated temperatures on the resistance and temperature coefficient of resistance is presented. Unprotected films of- sheet resistivity between 100 and 500 ohms per sq fabricated at 300°C substrate tenzperatures were unstable when stored at 150°Cfor extended periods. The higher sheet resistivity films exhibited the greatest instability; however, even the 100 ohms per sq films drijted excessively for device application. When stored at still higher temperatures, the normalized resistance increases to maximum, then decreases until a minimum value is obtained, then finally increases in resistance until open. The use of a protective overcoating of SiO has had considerable benejicial effects on the film stability, so that 250 ohms per sq films deposited on 300°C substrates are now stable after 1000 hr storage at 250°C and possess a temperature coefficient of resistance less than 200 ppm per C. The use of a low substrate temperature during depositon (100°C) enables the preparation oj resistors with very low tenperature coefficients of resistance (10 to 20 ppnl per &apos;C). However, these films are less stable than their higher substrate temperatuve counterparts. During extended storage, the resistance of the protected films always decreases with lower substrate films exhibiting larger normalized resistance decreases. This resistance decrease is accompanied by a linearly related increase in the temperature coefficient of resistance. The electrical behavior of these films may be explained by postulating That the structure of the films is in the transition region between thick continuous films and ultrathin island structure films so that the conductivity is the restlt of both electron scattering and tunneling-activated charge carrier creation between neighboring grains. The annealing behavior when thermally aged is the result of defect anneal, grain growth, and selective oxidation. TheRE is a considerable interest in thin metallic films for use as resistor elements in microelectronic circuits.1,2 These resistor films must be stable when exposed to elevated-temperature storage or operating ambient, possess low temperature coefficients of resistance (hereafter referred to as T.C.R.), and be of a high enough sheet resistivity to be useful. The resistivity and T.C.R. of a thin metallic film are determined by the structure and thickness of the film. Hence the stability of the film when exposed to stress would depend on the stability of the structure. The resistivity of a thin film is the result of the electrons&apos; interaction with the lattice vibrations (electron-phonon scattering), scattering of electrons due to impurities, defects, and grain boundaries and specula reflection from the film surfaces.3&apos; All of these effects serve to reduce the electron mean free path and result in a resistivity higher than the ideal bulk. In ultrathin films possessing essentially an island structure consisting of a planar array of aggregates separated by a few to a few tens of angstroms, conduction is dominated by a combination of tunneling and activated charge carrier reation. Thin films would be characterized by relatively low resistivity, positive T.C.R., and reasonable structure stability whereas ultrathin films possess unstable structures, negative T.C.R., and exhibit high resistivity. Feldman6 has investigated films intermediate between the two regions and postulates that the resistivity of a film in the transition region is composed of two linearly additive parts: that due to the resistance of the grains and that due to the gaps. The grain resistivity would represent the scattering of the conduction electrons by defects, surfaces, and phonon interaction while the gap term represents the tunneling contribution. For gold and platinum films, he found as the film structure becomes progressively less continuous, corresponding to thinner films, the absolute value of the T.C.R. becomes progressively smaller until negative values are observed with respective zero T.C.R.&apos;s at about 35 and 150 ohm per sq, respectively. Recently the author7 investigated the behavior of a multicomponent alloy of nickel, chromium, and iron and found the T.C.R.&apos;s of these films decrease with decreasing substrate temperature during deposition. The lower T.C.A. associated with lower substrate temperatures was attributed to an increased contribution to the total resistivity from the negatively temperature-dependent gap tunneling since it is well-known that thin films deposited on low-temperature substrates consist of a higher density of smaller grains than the same sheet resistivity films deposited on higher-temperature substrates. Under conditions of thermal anneal, the author found that, when various sheet resistivity films fabricated at 300°C substrate temperature are exposed to extended storage in air at 300°C, the thinner films increase in resistance until open, while the thicker films

Jan 1, 1967

By J. Bruce Wagner, Roger L. Levin

Lattice-parameter measurements have been carrzed out at room temperature on undoped and on chromium-doped wustite as a function of oxygen concentration. Results may he expressed by for the undoped uustite. These data are in agreement with and extend the work of&apos; Jette and Foole. The present results are consistent with the cation vacancy model. for metal- deficil wuslite, both undopen and doped. SEVERAL investigators have made room-temperature lattice-parameter measurements on wustite as a function of composition. Jette and Foote used these measurements to determine the phase limits of wustite. Willis and Rooksby and Benard have also measured the lattice parameters of wustite at room temperature, but their values of a. vary considerably from those of Jette and Foote. In conjunction with Studies&apos; on the transition from surface-controlled heterogeneous reactions involving CO-C02 oxidation of metals, lattice-parameter measurements on undoped and chromium-doped wiistite have been performed. These studies are especially needed to clarify conflicting data of previous authors, to extend the data to the stability limits of wiistite as determined by Darken and urr,6 which include a larger range of existence than that found by Jette and Foote, and to test by X-ray means the role of chromium as a vacancy producer in wiistite.

Jan 1, 1967