By Hans-Jürgen Schaller, Horst A. Brodowsky

Activity coefficients of boron in palladium were determined at concentrations up to PdB0.23 by reducing B2O3 between 870" and 1050°C in a controlled H2-H2stream and measuring the resulting weight gain. The deviations from ideal behavior closely resemble those of the system Pd-H and are interpreted in terms of three principles: 1) The solute atoms occupy octahedral interstitial positions. 2) They donate their valence electrons to the 4 d and 5s bands of palladium, raising its Fermi energy. 3) The lattice strain energy is lower for two nearesl -neighbor interstitial particles than for two farther separate ones. SOLID solutions of hydrogen in palladium are a useful subject for studying thermodynamic aspects of the formation of alloys and of nonstoichiometric systems.1-3 The activity of hydrogen is readily measurable to a high degree of accuracy,4'5 even at low temperatures where the deviations from ideal behavior are more pronounced, and its simple structure facilitates an interpretation of these deviations in terms of a detailed model. Two effects are discussed to account for the non-ideal properties:3 An "electronic" effect, connected with the rise of the Fermi energy, as electrons of the interstitial hydrogen atoms enter the electron gas of the metal, and an "elastic" effect, due to an interaction of the regions of strain around each interstitial atom. The electronic effect is based on the idea that the lowest energy levels of the dissolved hydrogen atoms are higher than the Fermi energy, so that the electron will not occupy a localized state but enter into the electron band of the metal.6 The elastic effect is based on the observation that dissolved hydrogen distorts and expands the palladium lattice. The hypothesis is put forward that the elastic strain energy is lower for two adjacent dilatational centers than for two separate ones; i.e., they attract each other. The resulting pair interaction can be used to calculate an elastic contribution to the thermodynamic excess functions by means of one of the statistical methods. This model permitted a detailed description of the solution properties of hydrogen in palladium3 and in palladium alloys.798 An extension of the approach to describe the excess functions of substitutional palladium alloys is possible.9 In order to further test and refine the model, an investigation of other interstitial alloys was started. Palladium dissolves considerable amounts of boron in homogeneous solid solution.10 The palladium lattice expands linearly up to nB = 0.23 (nB = B/Pd atomic ratio), the highest concentration studied." The expan- sion, extrapolated for 1 mole of interstitial per mole of palladium, is 17 pct of the lattice constant of pure palladium vs 5.7 pct in the case of hydrogen.12 The fact that the lattice expands rather than contracts is a strong indication that interstitial positions are occupied. According to neutron diffraction experiments, hydrogen occupies the octahedral sites of the fcc lattice.13 Unfortunately, this direct evidence is not available for the Pb-B system, mainly because of the high-reaction cross section of boron with thermal neutrons. However, by way of analogy and on the grounds of the rather close similarities between the two systems to be reported here, it seems safe to attribute octahedral positions to the dissolved boron, too. At higher boron contents, compounds of stoichiomet-ric compositions are reported such as Pd3B, which has the structure of cementite,14 so that a close structural relationship seems to exist with the system r Fe-C. In their study of hydrogen absorption in Pb-B alloys, Sieverts and Briining noted that alloys with an atomic ratio of about nB = 0.16 are no longer homogeneous15 This observation was confirmed in an extensive X-ray investigation.11,16 The phase boundaries of two miscibility gaps were established. One two-phase region was stable below a transition temperature of about 315°C and extended from nB = 0.015 to 0.178. The other one extended from nB = 0.021 to 0.114 slightly above the transition temperature and had an apex at nB = 0.065 and 410°C. All phases involved have the fcc structure of pure palladium with lattice expansions proportional to their boron contents. The occurrence of miscibility gaps, i.e., the coexistence of dilute and concentrated phases, points to an energy of attraction between the dissolved particles, in the Pb-B system as well as in the Pd-H system. The filling up of the electron bands seems to be analogous, too, in the two systems, as indicated by the hydrogen absorption capacit15,17,18 and by the suscepti bility of Pd-B alloys.l8 In both types of experiments, boron acts as an electron donor. A chemical method was used to measure the activity of boron in palladium. Boron trioxide was reduced in a moist hydrogen stream: B2O3 + 3H2 = 2B + 3H3O [l] At known activities or partial pressures of boron trioxide, hydrogen, and water, the activity of boron could be calculated from the law of mass action. The equilibrium concentration of boron corresponding to this activity was determined as the weight gain of the sample. EXPERIMENTAL The samples consisted of small pieces of foil of 0.1 mm thickness and about 100 mg weight. The palladium was supplied by DEGUSSA, Germany, and stated to be

Jan 1, 1970

By D. H. Woodard, G. W. Geil, W. D. Jenkins

In a series of papers, the authors and their associates have shown the influence of four important factors on the technical cohesion limit.3-l6 By "technical cohesion limitv is meant the technically determin-able resistance to fracture. The four importarlt factors are the stress system, plastic deformation, temperature, and the strain rate, The influence of any one of these factors may be represented by a curve of cohesion limits, although only one point on the curve may represent actual fracture. As the term "fracture stress" has come into general use with the same significance as technical cohesion limit, the authors are here using the shorter term with the understanding that it does not always refer to actual fracture. The previously mentioned series of papers contains ample evidence that plastic extension increases the fracture stress of any polycrystalline metal, In a recent paper of the series,l5 moreover, it has been shown that the effect of plastic deformation on the fracture stress cannot be attributed to reorientation of internal flaws but is a work-strengthening effect, similar to the effect on the flow stress, $ Plastic deformation of steels, however, may not only cause work hardening, but may result in additional hardness because of strain aging. Some evidence that strain aging affects not only the flow stress but also the fracture stress, has been presented in a recent paper.14 In that paper, a study is made of the influence Of Plastic deformstion at room temperature on the fracture stress of ferritic steels at -188°C. The study is based on the results Of two-stage tests. In the first stage each specimen was extended a predetermined amount at room temperature; in the second stage the specimen was tested to fracture in liquid air. In most Of these tests the specimen remained in the testing machine during the interval of about one hour between the first and second stages, it was kept under a tensile load of about 500 lb and maintained at liquid air temperature. The effects of various amounts of .plastic deformation on the fracture stress were thus determined and curves were obtained to represent the influence of plastic deformation at room temperature on the stress at brittle fracture in liquid air.14 Two specimens Of ingot iron, however, were removed from the testing machine at the end of the first stage and several days elapsed before the specimens were tested to fracture in liquid air, As shown in Fig 8 of that paper," the points representing fracture of these specimens are far above the curve representing the results of two-stage tests without a rest interval between the stages. The evidence thus indicated that the fracture stresses of these two specimens were increased not

Jan 1, 1949

By G. W. Geil, D. H. Woodard, W. D. Jenkins

In a series of papers, the authors and their associates have shown the influence of four important factors on the technical cohesion limit.3-l6 By "technical cohesion limitv is meant the technically determin-able resistance to fracture. The four importarlt factors are the stress system, plastic deformation, temperature, and the strain rate, The influence of any one of these factors may be represented by a curve of cohesion limits, although only one point on the curve may represent actual fracture. As the term "fracture stress" has come into general use with the same significance as technical cohesion limit, the authors are here using the shorter term with the understanding that it does not always refer to actual fracture. The previously mentioned series of papers contains ample evidence that plastic extension increases the fracture stress of any polycrystalline metal, In a recent paper of the series,l5 moreover, it has been shown that the effect of plastic deformation on the fracture stress cannot be attributed to reorientation of internal flaws but is a work-strengthening effect, similar to the effect on the flow stress, $ Plastic deformation of steels, however, may not only cause work hardening, but may result in additional hardness because of strain aging. Some evidence that strain aging affects not only the flow stress but also the fracture stress, has been presented in a recent paper.14 In that paper, a study is made of the influence Of Plastic deformstion at room temperature on the fracture stress of ferritic steels at -188°C. The study is based on the results Of two-stage tests. In the first stage each specimen was extended a predetermined amount at room temperature; in the second stage the specimen was tested to fracture in liquid air. In most Of these tests the specimen remained in the testing machine during the interval of about one hour between the first and second stages, it was kept under a tensile load of about 500 lb and maintained at liquid air temperature. The effects of various amounts of .plastic deformation on the fracture stress were thus determined and curves were obtained to represent the influence of plastic deformation at room temperature on the stress at brittle fracture in liquid air.14 Two specimens Of ingot iron, however, were removed from the testing machine at the end of the first stage and several days elapsed before the specimens were tested to fracture in liquid air, As shown in Fig 8 of that paper," the points representing fracture of these specimens are far above the curve representing the results of two-stage tests without a rest interval between the stages. The evidence thus indicated that the fracture stresses of these two specimens were increased not

Jan 1, 1949

Some Things We Don't Know about the Creep of Metals. By H. W. Gillett (T.P. 1087) Reduction of Iron Ores under Pressure by Hydrogen. By Michael Tenenbaum and T. L. Joseph (T.P. loll, with discussion) Induction Furnaces for Rotating Liquid Crucibles. By E. P. Barrett, W. F. Hol- bRook and C. E. Wood (T.P. 986, with discussion) Mechanism of Solidification and Segregation in a Low-carbon Rimming-steel Ingot,. By Anson Hayes and John Chipman (T.P. 988, with discussion) Solidification of Rimming-steel Ingots. By A. HultGRen and G. PhRagmen. (Contribution 112) Dendritic Structure of Some Alloy Steels. By Daniel .I. Martin and James L. Martin (T.P. 1066, with discussion) Occlusion and Evolution of Hydrogen by Pure Iron. By George A. Moore and Donald P. Smith (T.P. 1065, with discussion) Structure of Iron after Con~pression. Hy Charles S. Barrett (T.P. 977, with discussion) Structure of Iron after Drawing, Swaging, and Elongating in Tension. Ry Charles S. Barrett and L. H. LevensoN (T.P. 1038, with discussion) Magnetic Torque Studies of the Texture of Cold-rolled and of Recrystallized Iron-silicon Alloys. By Leo P. TaraSovJ(T.P. 1012, with discussion) Influence of Atmosphere and Pressure on Structure of Iron-carbon-silicon Alloys. By Alfred Boyles (T.P. 1046) Kinetics of the Decomposition of Austenite at Constant Temperature. By J. H. Austin and R. L. Rickett (T.P. 964, with discussion) Reaction Kinctics in Processes of Nucleation and Growth. By William A. Johnson and Robert F. Mehl (T.P. 1089, with discussion) Phase Changes in 3.5 Per Cent Nickel Steel in the Acl Region. By I. N. Bavarine (T.P. 1031, with discussion) Chromium in Structural Steel. By Walter Crafts (T.P. 1055) Surface Allotropic Transformation in Stainless Steel Induced by Polishing. By J. T. BuHwell and J. WUlff (T.P. 1032, with discussion) Nature of :Passivity in Stainless Steels and Other Alloys, I and 11. Ry H. H. Uhlig and John WUlff (T.P. 1050, with discussion) Thermal Expansion of Nickel-iron Alloys (Nickel from 30 to 70 Per Cent). Ry J. M. Lohr and Charles H. Hopkins (T.P. 987, with discussion) Low-temperature Transformation in Iron-nickel-cobalt Alloys. By L. L. Wy~Ian (T.P. 1013, with discussion) Fracture of Steels at Elevated Temperatures after Prolonged Loading. By R. H. Thielemann and E. R. Parker (T.P. 1034, with discussion)

Jan 1, 1939

Some Things We Don't Know about the Creep of Metals. By H. W. Gillett (T.P. 1087) Reduction of Iron Ores under Pressure by Hydrogen. By Michael Tenenbaum and T. L. Joseph (T.P. loll, with discussion) Induction Furnaces for Rotating Liquid Crucibles. By E. P. Barrett, W. F. Hol- bRook and C. E. Wood (T.P. 986, with discussion) Mechanism of Solidification and Segregation in a Low-carbon Rimming-steel Ingot,. By Anson Hayes and John Chipman (T.P. 988, with discussion) Solidification of Rimming-steel Ingots. By A. HultGRen and G. PhRagmen. (Contribution 112) Dendritic Structure of Some Alloy Steels. By Daniel .I. Martin and James L. Martin (T.P. 1066, with discussion) Occlusion and Evolution of Hydrogen by Pure Iron. By George A. Moore and Donald P. Smith (T.P. 1065, with discussion) Structure of Iron after Con~pression. Hy Charles S. Barrett (T.P. 977, with discussion) Structure of Iron after Drawing, Swaging, and Elongating in Tension. Ry Charles S. Barrett and L. H. LevensoN (T.P. 1038, with discussion) Magnetic Torque Studies of the Texture of Cold-rolled and of Recrystallized Iron-silicon Alloys. By Leo P. TaraSovJ(T.P. 1012, with discussion) Influence of Atmosphere and Pressure on Structure of Iron-carbon-silicon Alloys. By Alfred Boyles (T.P. 1046) Kinetics of the Decomposition of Austenite at Constant Temperature. By J. H. Austin and R. L. Rickett (T.P. 964, with discussion) Reaction Kinctics in Processes of Nucleation and Growth. By William A. Johnson and Robert F. Mehl (T.P. 1089, with discussion) Phase Changes in 3.5 Per Cent Nickel Steel in the Acl Region. By I. N. Bavarine (T.P. 1031, with discussion) Chromium in Structural Steel. By Walter Crafts (T.P. 1055) Surface Allotropic Transformation in Stainless Steel Induced by Polishing. By J. T. BuHwell and J. WUlff (T.P. 1032, with discussion) Nature of :Passivity in Stainless Steels and Other Alloys, I and 11. Ry H. H. Uhlig and John WUlff (T.P. 1050, with discussion) Thermal Expansion of Nickel-iron Alloys (Nickel from 30 to 70 Per Cent). Ry J. M. Lohr and Charles H. Hopkins (T.P. 987, with discussion) Low-temperature Transformation in Iron-nickel-cobalt Alloys. By L. L. Wy~Ian (T.P. 1013, with discussion) Fracture of Steels at Elevated Temperatures after Prolonged Loading. By R. H. Thielemann and E. R. Parker (T.P. 1034, with discussion)

Jan 1, 1939

All the TECHNICAL PUBLICATIONS and CONTRIBUTIONS published in 1939 are available at Institute headquarters, unless otherwise noted. They are also on file in many public, university and technical libraries and, when so indicated in the list, may be found in the TRANSACTIONS. TECHNICAL PUBLICATIONS in Classes A-Metal Mining, B-Milling and Concen-tration, H-Industrial Minerals, and ;I-Mining Geology are distributed in MINING TECHNOLOGY, which is issued every other month. Technical Publications in Classes C-Iron. and Steel Division, D-Nonferrous Metallurgy and E-Institute of Metals Division are distributed in METALS TECHNOLOGY, which is issued twice quarterly. TECHNICAL PUBLICATIONS in Class G-Petroleum Division are distributed in PETRO-LEUM TECHNOLOGY, which is issued quarterly. TECHNICAL PUBLICATIONS in Classes F-Coal Division, J-Mineral Industry Education Division, K-Mining Administra-tion, and L-Geophysical Methods of Exploration are issued as separate pamphlets. An Institute member is entitled to one copy of any TECHNICAL PUBLICATION or CON-TRIBUTION. Copies of TECHNICAL PUBLICATIONS listed have been mailed to members of the Institute according to their registration by classes. CONTRIBUTIONS and Other TECHNICAL PUBLICATIONS will be sent upon request. A member relay purchase an additional copy of a TECHNICAL PUBLICATION Or a CONTRIBUTION at One cent a page; minimum charge, 25¢. Nonmembers may purchase any CONTRIBUTION or a TECHNICAL PUBLICATION Of the F, J, K, or L classes at the same rate, but the nonmember price per copy for METALS TECHNOLOGY, MINING TECHNOLOGY or PETROLEUM TECHNOLOGY is $1. TECHNICAL PUBLICATIONS (separate pamphlet form), $2 per annum; Canadian and foreign postage 50 cents extra. METALS TECHNOLOGY, $7 per annum; Canadian and foreign postage 50 cents extra (Iron and Steel Division and Institute of Metals Division ferrous and nonferrous papers). MINING TECHNOLOGY, $6 per annum; Canadian and foreign postage 50 cents extra (metal mining, milling and concentration, Industrial Minerals Division, and mining geology papers). PETROLEUM TECHNOLOGY, $4 per annum; Canadian and foreign postage 50 cents extra. Bound volumes have been mailed to members that have requested them, and MINING AND METALLURGY is mailed each month. A member is entitled to one volume a year on his membership and lie may purchase for $2.50 one copy of a volume not already received; additional copies of 'the same volume, $5. Nonmembers may pur-chase the volumes listed, at $5 each, plus 60 cents for Canadian or foreign postage. Extra single copies of MINING AND METALLURGY, 25¢ current issue, back numbers 500 each to members; to nonmembers 50¢ current issue and $1 each, back issues. Subscription price to nonmembers and to members for extra copies, $3 per annum plus $1 for Canadian or foreign postage.

Jan 1, 1939

By E. W. Filer, R. P. Smith, L. S. Darken

The solubility of nitrogen gas in purified iron and low alloy steels is determined for the y region (930° to 1350°C). The diffusivtiy of nitrogen is estimated from the rate of approach to equilibrium. The investigation of aluminum-killed steels, held in nitrogen, discloses precipitation of aluminum nitride, the solubility of which is determined. ALTHOUGH several investigations of the solu-bility of nitrogen gas in y iron have been reported, all have made use of the method adopted by Sieverts in his classic work, whereby the solubility is determined by the pressure or volume change of the gas. The agreement between different investigators* is rather poor, particularly as compared to the self-consistency of results of several individual investigators. The present report represents a portion of our investigation of the equilibrium of nitrogen and nitrogenous atmospheres with iron and steels. The method adopted in this temperature region (910" to 1400°C) consists of holding the specimen in gaseous nitrogen, quenching (or cooling), and determining the nitrogen content by direct analysis (solution in acid followed by distillation and titra-tion of the ammonia).** Up to 1050°C a 20 in. vertical wire-wound (Kan-thal) furnace was used; this was wound in three sections so that by proper adjustment of relative currents, and use of a modulator1 and a commercial controller (using a chromel-alumel control couple), a zone almost 6 in. long could be maintained uniform within a few tenths of a degree. Since the temperature coefficient of the nitrogen solubility is low, the full precision was not utilized and a variation of l° to 2" was tolerated; a variation of a similar amount also occurred occasionally between the beginning and end of the experiment. At higher temperature a vertically mounted, tubular Globar furnace and control unit was used; the zone of uniformity (l° to 2"C) was here limited to about 2 in.; fluctuations with time were comparable to those in the wire-wound furnace. Reported temperatures were measured by use of a platinum-platinum-rhodium thermocouple, which was frequently com- pared with a similar standard couple which was calibrated at the gold and palladium points and also compared with one certified by the Bureau of Standards; error from this source is believed to be less than 1 "C. Nitrogen gas from a commercial cylinder was mixed with slightly over 1 pct H by use of a gas mixer described previously.' This mixture was passed over hot copper and through ascarite and phosphorus pentoxide to remove oxygen and water vapor. The purified gas contained 1.05 pct H. This procedure was adopted to prevent the formation on the specimens of oxide film, which is well known to be nearly impervious to nitrogen; its success was attested by

Jan 1, 1952

By F. H. Turan, F. W. Jessen

The gel strength and viscosity of two different suspensions of fractionated montmorillonite clay were measured by using a Stormer viscosimeter and Farm V-G meter. The amount of sodium poly-phosphate (sodium bexametaphosphate, sodium tetraphosphate and sodium acid pyrophosphate) adsorbed by the clay particles was determined. A relationship seems to exist between the amount of polyphosphate adsorbed and the nature of the surface, edge or plate, assumed to be the principal sites for selective adsorption. Reduction in viscosity and gel strength was found to be directly related to the adsorption. Both chemical bonding and physical adsorption seem involved in defloccula-tion Some indication of the axial ratios of particles of .l- to .04-micron average size is possible though study of the adsorption mechanism. INTRODUCTION AND PURPOSE A knowledge of surface areas of clay particles in a suspension and a precise determination of phosphate adsorption should provide a basis for a better understanding of reduction in viscosity and gel strength caused by molecularly dehydrated phosphates. The purpose of this investigation was to study the adsorption of sodium polyphosphates on suspensions of fractionated sodium montmorillonite. Although there is considerable uncertainty regarding details of the structure of montmorillonite, a generally accepted one is that suggested by Hofmann, Endell and wi1m.l The structure shown in Fig. 1 is an idealized one, and Marshall2 has postulated that it is possible for several isomorphous replacements to occur. Thus, aluminum may replace silicon, in which case an exchangeable cation would go along with the aluminum to neutralize what would otherwise be a net negative charge on the structure. There is disagreement among various investigators as to the particle size and shape of montmorillonite clays. Marshall2 reported the following results for the mean lateral dimensions of a Putnam clay (montmorillonite)— 3,730 A° for particles having average diameters ranging from 500 to 1,000 A, and 750 A° for those with an average diameter less than 200 A. The latter particles were estimated at 50A°in thickness, which would correspond to a stack of five unit cell layers. On the other hand, Shaw3 has interpreted micrographs as indicating that particles of montmorillonite ire readilv broken down to the individual cell layers by dispersion in water. Brindley4 and Merings indicate the ultimate particles to be of the order of 300 A° in mean lateral dimension. Van Olphen6 suggested the thickness of particles at four to five unit cell layers. It was suggested also that this number tends to become smaller with increasing dilution. Recently, Kahn and Lewis7 determined the size of sodium montmorillonite particles in aqueous suspension from electro-optical bi-refringence decay curves. The

By C. E. Jr. Reistle

ALL crude oils become more viscous when chilled, but the only oils that congeal and precipitate paraffin to such an extent as actually to cause production troubles are those that contain an appreciable amount of wax. In handling these oils of high wax content, three distinct problems may be encountered before the oil reaches the refinery. The first problem is the precipitation and accumulation of paraffin in the well, either in the oil string or on the face and in the pores of the sand. The second problem is the accumulation of paraffin and the congealing of oil in the transportation lines. The third problem is the precipitation of paraffin and the formation of tank bottoms.

Jan 1, 1927

By N. B. Pilling

The deleterious effect on the mechanical properties of copper, re-sulting from heating in contact with reducing gases, is well known, but the mechanism of the action does not appear to have been definitely established. The purpose of the present investigation was not to determine the exact variations in physical quality of commercial copper, with its various impurities, as dependent upon the composition of the gas, temperature of exposure, etc., but rather to study the nature of the action and the conditions under which it occurs. The physical result of the so-called "gassing" of copper has been generally described as the development of "brittleness." There appears to be a striking decrease in tensile strength, associated with a considerable loss of ductility, and a small copper strip or wire affected in this way can be snapped in two when bent. Larger articles may have an outer layer alone affected, which can be detached from the core by hammering or bending. Perhaps the earliest reference to this subject is that of Heynl in 1900, and among the later observers may be mentioned Archbutt,2 Bengough and Hill,3 Johnson,4 Mathewson and Thalheimer,5 and Ruder.6 Bengough and Hill, while working with arsenical copper, were the first to suggest the possibility of the formation of gases within the copper itself, while Ruder endeavored to explain the action by the reduction of the

Jan 1, 1919

By R. I. Jaffee, F. C. Holden, H. R. Ogden

IN a previous series of papers, the results of studies made on various types of high purity base titanium alloys were presented. Included in this work were the Ti-Mn' and Ti-Cu' alloys, representative of sluggish and active eutectoid systems, respectively. The present paper gives the results of a simi- lar study made on Ti-Mo alloys as an example of a ß-isomorphous alloy system. Experimental Procedures Alloy Preparation—Six ½-lb ingots were prepared from iodide titanium and high purity molybdenum stock. The ingots were arc melted in a water-cooled copper crucible under an argon atmosphere. Each ingot was melted at least twice to insure homogeneity and complete solution of the molybdenum. This was done by inverting the ingot in the crucible and remelting completely.

Jan 1, 1957

By M. B. Bever, A. B. Michael

The solidification of aluminum-rich aluminum-copper alloys was investigated for different solidification rates. The measured amounts of nonequilibrium eutectic were compared with the amounts calculated on the assumption of no diffusion in the solid. The morphology of the eutectic was studied and dendritic spacings were measured. Compositions of the cored primary solid solutions were determined by quantitative autoradiography after activation of the solute copper by neutron irradiation. CONSIDERABLE progress has been made in recent years toward an understanding of the solidification of metals. This is especially true for the factors involved in nucleation, the controlled growth of metal crystals from melts, and various aspects of the freezing of ingots and castings. Many features of the solidification process, however, are not understood adequately and much further work is required. In the research reported here the solidification of a series of aluminum-rich aluminum-copper alloys was investigated. Different degrees of deviation from the idealized case of equilibrium solidification were attained by varying the rate of solidification. Thermal analysis and microscopic examination were supplemented by lineal analysis and autoradiography. The latter required the use of radioactive tracers and was adapted to the quantitative determination on a microscale of concentrations of copper dissolved in aluminum. The tracers were produced in situ by activating the copper with neutrons. These techniques permitted a correlated interpretation of the temperature-time history, the amounts of nonequilibrium eutectic and the general morphology of the alloys, and yielded quantitative data on microsegregation. Nonequilibrium Solidification In the general case of the solidification of a solid solution in accordance with the phase diagram, the composition of the coexisting liquid and solid must change continuously. This change requires diffusion, which at best remains incomplete in the solid during solidification. The resulting inhomogeneity of the solid solution crystals is well-known as coring, dendritic segregation, or microsegregation. The generally accepted analysis of coring assumes that, 1—no diffusion occurs in the solid, 2—diffusion is complete in the liquid, and 3—the composition of the solid formed on cooling through any infinitesimal temperature interval is given by the solidus of the phase diagram. On this basis, In this equation m designates mass, x designates the concentration of solute and the subscripts L and S refer to the liquid and solid phases, respectively; the subscript o indicates the initial state, in which the liquid is identical with the entire system. Eq. 1 or its equivalent has been derived repeatedly'-7 and an analogous equation, known as Rayleigh's equation, has been used for distillation. The assumptions on which Eq. 1 is based do not include an infinitely fast cooling rate as sometimes stated. In fact, Olsen and Hultgren %ave shown by experiment that very high solidification rates suppress coring, presumably by preventing diffusion in the liquid and by the effect undercooling has on the composition of the nucleus. Coring thus occurs at rates of cooling which are too fast for a close approach to equilibrium in the solid and too slow to suppress diffusion in the liquid and to cause marked undercooling. If the liquidus and solidus approximate straight lines, Eq. 1 simplifies to The fraction of liquid present at any temperature during nonequilibrium solidification can be calculated from Eqs. 1 or 2. By the lever relation it is

Jan 1, 1955

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York L. W. FRANCIS, Chairman. WILLARD S. MORSE, Vice-Chairman. . THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. P. A. MOSMAN, Treasurer. LOUIS D. HUNTOON, Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH. Columbia F. A. THOMSON, Chairman. GEORGE W. RODDEWIG, Vice-Chairman. LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. R. S. McCAFFERY, S. H. RICHARDSON.

Jan 6, 1914

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York L. W. FRANCIS, Chairman, WILLARD S. MORSE,. Vice-Chairman. THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. P. A. MOSMAN, Treasurer. LOUIS D. HUNTOON. Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH. Columbia F. A. THOMSON, Chairman. GEORGE W. RODDEWIG, Vice-Chairman. LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. R. S. McCAFFERY, S. H. RICHARDSON.

Jan 8, 1914

Jan 1, 1967

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York L. W. FRANCIS, Chairman, WILLARD S. MORSE, Vice-Chairman. THOMAS -T. READ, Secretary, Woolworth Bldg., New York: N. Y. P. A. MOSMAN, Treasurer. LOUIS D: HUNTOON. Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH. Columbia F. A. THOMSON, Chairman. GEORGE W. RODDEWIG, Vice-Chairman. LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. R. S. McCAFFERY, S. H. RICHARDSON.

Jan 10, 1914

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York L. W, FRANCIS, Chairman, WILLARD S. MORSE, Vice-Chairman. THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. P. A. MOSMAN, Treasurer. LOUIS D. HUNTOON. Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH. Columbia F. A. THOMSON, Chairman. GEORGE W..RODDEWIG, Vice-Chairman. LYNDON K, ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. R. S. McCAFFERY, S. H. RICHARDSON.

Jan 7, 1914

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York L. W. FRANCIS, Chairman, WILLARD S. MORSE, Vice-Chairman. THOMAS T. READ, Secretary, Woolworth Bldg., New York. N. Y. P. A. MOSMAN, Treasurer. LOUIS D. HUNTOON. Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. TIMOTHY W. SPRAGUE, HENRY A. WENTWORTH. Columbia F. A. THOMSON, Chairman. GEORGE W. RODDEWIG, Vice-Chairman. LYNDON K. ARMSTRONG, Secretary-Treasurer, P. 0. Drawer 2154, Spokane, Wash. R. S. McCAFFERY, S. H. RICHARDSON.

Jan 9, 1914

EXECUTIVE COMMITTEES OF LOCAL SECTIONS New York, L. W. FRANCIS, Chairman, WILLARD S. MORSE, Vice-Chairman. THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. P. A. MOSMAN, Treasurer. LOUIS D. HUNTOON. WILLIAM A. POMEROY. Boston HENRY L. SMYTH, Chairman. ALFRED C. LANE, Vice-Chairman. AUGUSTUS H. EUSTIS, Secretary-Treasurer, 131 State St., Boston, Mass. ROBERT H. RICHARDS, ALBERT SAUVEUR. Columbia FRANK A. ROSS Chairman. RUSH J: WHITE, Vice-Chairman. LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. FREDERIC KEFFER FRANCIS A. THOMSON,

Jan 2, 1915

Coal Division Mineral Industry Education Division Industrial Minerals Division Minerals Beneficiation Division Mineral Economics Division Mining, Geology and Geophysics Division Council R C Stephenson, Chairman (Ind Min Div), M D Cooper (Coal), H F Yancey (Coal), S D Michaelson (MBD), Will Mitchell, Jr (MBD), J R Van Pelt, Jr (MIED), S S Cole (Ind Min Div), J D Forrester (MGGD), L E Shaffer (MIED), E L Clark (MGGD), C W Merrill (MED), E H Robie, Acting Secretary, 29 West 39 Street, New York 18, New York

Jan 1, 1955