By John Mathews

DURING the prosecution of the aircraft-production program in 1917 and 1918, the writer visited many plants engaged in the manufacture of motors, planes and parts, in carrying out his duties as chairman of the Committee on Aircraft-engine Forgings. On several occasions, when the question of expansion was discussed, it was noted that there was confusion in the use of the terms: the true coefficient of expansion, a physical constant, and distortion in hardening. One engineer, referring to a steel shown in the accompanying table; stated that he could not consider it for crankshafts because of its excessive coefficient of expansion, while another steel, also listed in the table, as said to be especially good because it had no coefficient of expansion, since it came out of the oil bath perfectly straight. Many years ago one of our employees designed anew oil furnace; when asked what became of the products of combustion, he replied: "There ain't any, we burn them all up." While the coefficient of expansion is not without its effect in volume changes in hardened steel, it is not a determining factor in the matter of distortion and going out of shape. Irregular heating, uneven furnace bottoms, and carelessness in withdrawing the part from the furnace, as well as the manner in which the part enters the quenching bath are of greater moment. Generally speaking, also, steels of relatively low hardening temperature will distort less than those requiring higher hardening heats. The coefficient of expansion must be considered in engineering design most frequently when different metals or alloys are used in the same construction. For example, the difference of expansion between a steel crankshaft and an aluminum crank-case might be of real importance and a steel with no coefficient of expansion would be much less desirable than one with the normal coefficient. About 15 years ago, the writer made many determinations of the coefficient of expansion at low temperature ranges, usually between 20° and 100° C. Among the materials tested were: Pure forged electrolytic iron, 11.73 parts per million for 1° C.; cast aluminum (99.93 per cent. Al.),

Jan 2, 1920

By C. E. Ells, A. Sawatzky

The effect of neutron irradiation on tensile properties of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy has been evaluated for integrated neutron fluxes up to 3 x 1020 n per sq cm (E > 1 Mev). Specimen temperature during irradiation was normally 300°C. The material was studied both in annealed and in quenched and aged conditions. When the alloy (fab-ricatedfrom sponge zirconium) is quenched from a temperature =40°C below the a + ß/ß transformation and aged 6 hr at 535oC, neutron irradiation up to the maximum studied has little effect 071 reduction in area, although there is a drop in uniform elongation and the yield strength is increased by = 25 pct. Conversely, irradiation of the alloy in an annealed condition can result in much greater changes in properties, with yield-strength increases of up to 200 pet. The dose dependence of irradiation hardening obeys the saturation equntion proposed by Makin and Minter to explain hardening in copper and nickel: Act = C[1 - exp(-Døt)/1/2 A rnodel is proposed to explain the effect of niobium content and metallurgical condition on irradiatiotz behavior. THE Zr-Nb alloys form a class of material susceptible to marked strengthening by quench and age heat treatment. With niobium concentrations as low as 2.5 wt pet, strengths can be developed which are double those of annealed zircaloy-2.1 Since the neutron-capture cross section of the Zr-2.5 wt pet Nb alloy is nearly identical to that of Zircaloy-2, significant gains in power-reactor neutron economy could be obtained by replacing stressed in-reactor components of Zircaloy-2 with the heat-treated Zr-Nb alloy. When the solution heat-treatment temperature is in the high (a + ß) phase, then the tensile properties of the quenched (and aged at 500°C) material have been shown to be relatively insensitive to neutron irradiation.1-3 Addition of small quantities of copper to the binary Zr-2.5 wt pet Nb alloy gives a useful reduction to the corrosion rate in air and carbon di- oxide,&apos; and a ternary alloy of composition Zr-2.5 wt pet Nb-0.5 wt pet Cu was chosen for one component in the Douglas Point Reactor. This application utilizes both the corrosion resistance to a moist air-carbon dioxide environment and the strength developed by a quench and age heat treatment. By suitable choice of solution heat treatment and aging temperatures, tensile properties of the ternary alloy can be made nearly identical to those considered as optimum for the binary alloy. One effect of the copper addition, however, is to give marked changes in the aging kinetics of the alloy.&apos; For this reason, it appeared that neutron irradiation might promote overaging in the ternary alloy, particularly at the elevated service temperature (=300°C). This paper describes the effect of neutron irradiation on the tensile behavior of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy in several metallurgical conditions pertinent to its use as a reactor material. The metallurgical conditions included those for which aging occurs in the unirradiated material, and fully annealed conditions for which a higher degree of thermal stability could be expected. 1) EXPERIMENTAL Two batches of alloy were used, both made from sponge zirconium. The fabricator&apos;s analysis of principle constituents showed no significant difference between the two batches, Table I. The rod material was rolled to 1.5 in. diam, and then swaged to final sizes of 0.5 to 0.375 in. diam at nominal temperatures of 785" and 625°C for the AM and AS batches, respectively. Subsequent hydrogen analyses at CRNL confirmed that the hydrogen concentration of the as-received rod was indeed <20 ppm. However, it was found that the (a + ß)/ß transus for the AM material was approximately 25°C lower than that of the AS material, indicating rather more difference in oxygen concentration than given in Table I. Except for a small difference in yield-point behavior, the tensile prop-

Jan 1, 1965

By Nicholas J. Grant, Oliver Preston

PUBLICATION of data by Irmann&apos; indicating outstanding thermal stability and elevated-temperature strength properties in a sintered aluminum powder product (SAP) stimulated interest in the strengthening of metals by means of a highly dispersed oxide phase. This material was produced by compacting, sintering and extruding a fine flake aluminum powder, resulting in a dense product containing 10 to 16 volume pct alumina, which arises from the thin oxide film on the starting powder, highly dispersed in a matrix of pure aluminum. The method of producing SAP, and the stable high-temperature properties obtained from it, introduced the possibility of developing superior materials for high-temperature service by powder metallurgy methods. The composition of the materials of this type which are presently under consideration is predominantly metallic, containing from less than 1 pct up to about 20 volume pct of the oxide. As a result, other properties of these materials, such as electrical and thermal conductivity, thermal shock resistance, and to a certain extent ductility, notch sensitivity, machinability and hot working properties, are also predominantly metallic. These alloys do not constitute, therefore, a completely new class of materials as do the cermets, but rather present a new means of modifying the properties of a metallic matrix. In this sense, SAP type alloys are more closely analogous to the alloy aging systems. While the strength properties realized in the oxide-pure metal systems at the lower temperatures are substantially less than the best attainable in the aging systems, the thermal instabilities in the latter make them of less value for use at temperature much above their optimum aging temperatures, as indicated in Fig. 1. While the means of obtaining an oxide dispersion are more difficult and costly than conventional aging processes, in the light of the as yet limited understanding of such systems there is considerable promise of improved high temperature properties arising from the thermal stability of these structures. Since the development of SAP in 1946, its properties and the properties of a series of similarAl,O,-A1 products containing from about 1 to 20 pct aluminum oxide have been fairly extensively studied and reported.&apos;- "articular attention has been given to

Jan 1, 1958

By H. E. Nold

THIS paper is an effort to explain in a simple manner the fundamental principles involved in examining a clay deposit for both quantity and quality and in operating a clay mine, either open-pit or underground, SO that the best quality of finished material can be made from the raw material available. The writer is aware that what is recommended in this paper is everyday practice in many refractories plants and in some other heavy-clay products plants, but observations made while visiting practically every clay mine in Ohio have convinced him that the practices herein discussed are not as widely used as their importance warrants. It is true that the problem of mining for quality is more acute in refractories plants than in most heavy-clay products plants, yet some of the latter are finding it profitable to pay more than ordinary attention to the selection and blending of their raw materials. It is hoped that this short paper may prove helpful to some who are now finding it difficult to produce a uniform product of as high quality as their clay deposit seems to warrant. The coordination of the work of the clay mine or pit with the manufacturing plant, to the end that the best product possible be made from the raw material available, presupposes a rather intimate knowledge of the clay deposit. The knowledge must include not only information of the amount of clay available but also rather detailed information about both vertical and horizontal variations in quality of the clay. This information should cover three things: quality, quantity, and location. Sampling Undeveloped Deposits In the case of an undeveloped deposit with a shallow overburden, pitting may be the cheapest way of testing. For thick deposits or deposits with rather heavy overburden, the diamond drill, using a double core barrel, offers the best means of testing. When using the diamond drill in clay testing, it is doubtful whether it pays to take less than 2-in. cores; it is difficult to get complete cores with smaller drills, and the quantity of material obtained with smaller cores is not sufficient for the necessary tests.

Jan 1, 1929

By G. Ostberg

OXYGEN has frequently been considered responsible for phenomena in the metallurgy of cast iron which are not sufficiently explained by the presence of other elements. Oxygen and oxides have been regarded as critical factors, particularly for the solidification process, and specifically in the formation of graphite. However, the evidence for an influence of oxygen has mostly only been indirect or qualitative. Furthermore, quantitative data on the oxygen content of cast iron presented in the literature have often been less conclusive as being apparently determined with insufficient regard for the difficulties associated with the sampling and analysis. These problems, experimental and theoretical, have been studied in this investigation. An attempt is made to bring the views on the soluble amount of oxygen in cast iron on a level with the present understanding of the thermodynamics of these types of alloys. Although there are no experimental data on the complete multicomponent cast-iron alloys some conclusions have been drawn from investigations on simpler systems. The order of magnitude of the solubility of oxygen in cast iron is considered in the first part of the paper. The second part deals with the oxygen content actually present under practical conditions. First the possible sources of errors in sampling and analyzing methods are examined. Finally some observations on the oxygen and oxide content of malleable iron during the production process are made. THERMODYNAMICS OF OXYGEN SOLUBILITY When cast iron is saturated with oxygen the saturation phase is essentially carbon monoxide or silicon dioxide depending upon the composition of the iron, the temperature, and the rates of formation of the oxides.* The latter occurs accordiw to the O + C = CO, Kc0 - a COa J 20 + Si = SiO2, Activities are used here instead of weight pct concentrations, since activities are believed to show more sensitively the effects of the interaction of all the alloying elements. Calculations involving activities are, however, seriously hampered by lack of experimental data on the interactions between the components encountered in the multi component cast-iron system Fe-O-C-Si-Mn-P-S- and so on. In order to make an estimate of the oxygen solubility reason-

Jan 1, 1959

By J. M. Hodge

This paper represents a start on the problem of choosing alloy steels for a given application on the basis of toughness as indicated by the room temperature notched bar impact value at the desired hardness level, and as such, is very useful. I believe, however, that the authors will agree that it is only a start on this problem. The authors state that neglecting temper brittleness or other possible effects of the tempering temperature level, the impact values at a given grain size level will be determined principally by the hardenability. This is, of course, true inasmuch as the hardenability determines the microstructure, but it serves to emphasize the broad field that hardenability now covers, since this study apparently includes mi¬crostructures ranging from full martensite to coarse pearlite. Furthermore, the + or - 20 ft-lb spread in the correlation with hardenability, which certainly limits the usefulness of these results for many applications, indubitably reflects the wide range of microstructures corresponding to a given value of hardenability in terms of the difference between full martensite and asquenched hardness.

Jan 1, 1947

By L. J. M. Smits

A theoretical equation is developed describing membrane potentials of shaly sands as a function of the cation-exchange capacity per unit pore volume of the rock and saturating water salinity. This equation is based on the same simple physical model as that employed earlier7 describing the electrical conductivity of shaly sands. Experiments conducted with NaCl solutions showed that the equation is obeyed, except in the case of saturated salt solutions where minor deviations were observed. A possible explanation is given for this discrepancy. As the clay content and the porosity of shales may vary appreciably, shale membrane potentials also vary. It was found that membrane potentials of shales can be calculated accurately with the aid of the same theory. Consequently, changes in membrane potentials can be accounted for by simple measurement of cation-exchange capacities per unit pore volume of both shales and shaly sands. Charts are given to facilitate interpretation of the electrochemical part of the SP in terms of cation-exchange capacities and the salinities of mud filtrate and formation water. INTRODUCTION A spontaneous potential (SP) log is a record of the way in which the electrical potential of a sonde varies as it passes down a borehole. Such variations frequently reflect rock texture, e.g., permeable beds intercalated in an impermeable series often are indicated by a sharp change in potential. Nowadays it is recognized that SP logs may be interpreted in terms of formation-water salinity and formation shaliness. The four sources of the SP are illustrated in Fig. 1. El and E4 represent streaming potentials generated by the flow of mud filtrate through mud cake opposite permeable formations and through shale, respectively. An extensive review of the literature on the evaluation of these streaming potentials is given by Lynchl and will not be discussed here. The remaining part of the SP generally is called the electrochemical potential, which is divided into two parts: a membrane potential across the shale (E3, Fig. 1) and a membrane potential in the permeable sand at the diffusion boundary between formation water and mud filtrate (E2, Fig. 1). It was found by wyllie2 that the membrane potential across the shale, E3, is the most important contribution to the electrochemical potential, the shale acting as a semi permeable membrane. When the sand is clean it does not influence the diffusion process, so E2 equals the value of the so-called liquid-liquid junction potential observed when the two solutions diffuse freely into each other. When the sand contains clay, however, this interferes with the diffusion process and affects the diffusion potential generated. The greater the proportion of clay, the stronger this effect will be. Wyllie,3 Doll4 and Poupon et al.5 took this effect into account theoretically, starting from a physical

Jan 1, 1969

By C. O. Worden, E. K. Landgraf, C. A. Zapffe

Following the discovery of Parke and Ham that deoxidation control of cast molybdenum can be predicated upon simple fractographic examination, a special study of that metal was undertaken to investigate those patterns ascribed to forge-ability and nonforgeability. An elaborately developed system of cleavage patterns immediately rewarded the study; and they are reported here as a necessarily preliminary contribution calling attention to information which is both new in type and in origin. In general, the present observations confirm those of Parke and Ham, and Wood-side; but they also disclose a wealth of detail and correlated phenomena which greatly expand the earlier information. For example, the oxide pattern of nonforgeability is found to be complex, perhaps involving as many as three distinctive patterns, And the nature of the carbide seems to be at least twofold. In addition, transgranular facets are here shown for the first time. Elaborately complex, but in a characteristic manner, these facets depict distortion in original crystal growth which provides truly extraordinary patterns. No carbide and oxide forms display themselves transgranularly, except in profile as exceedingly thin superficial films at the grain boundaries. Crys-tallographic features are also rare—a condition undoubtedly resulting from the great substructural distortion; but occasionally registrations are found of cleavage on {00I}, and faulted areas believed to be Neumann-type deformation on I I121. Introduction Parbe and Ham,&apos; and again Woodside,2 have reported that the forgeability of molybdenum cast by their Vacuum-electric-arc Process can be predicted with great dependability by a simple fractographic observation. They state that nonforgeability is the result of a grain boundary oxide which can be readily identified on the fracture facet at high magnification; and they convert the nonforgeable condition to a forgeable one by increasing the carbon content of the melt until the oxide structures subsequently observed in the fracto-graph become replaced by a second strongly marked pattern characteristic of carbide and coincidentally indicative of forgeability. Considerable importance immediately attaches to such observations: (I) because of their direct commercial application to one of metallurgy&apos;s inviting and relatively unexplored metals; (2) because of a general scientific curiosity regarding the nature of these characteristic markings; and (3) perhaps more important, because of

Jan 1, 1949

By William E. Harris

Time and experience have demonstrated that by means of the Waelz process zinc, lead, cadmium, arsenic, antimony, bismuth and tin can be volatilized satisfactorily. In this way difficult gold ores are being treated to allow for the recovery of the precious metal. Iron ore containing zinc is being treated to remove the zinc and recover the iron. In Germany, thallium is being recovered in commercial quantities from the zinc oxide fume; indium, germanium and gallium are also concentrated to a degree warranting recovery, even though these rare metals are only recognizable in the ore by means of the spectroscope. The physical, chemical or mineralogical condition of the raw material affects very little the applicability of the process. The name Waelz is derived from the German word Waelzen, meaning a "trundling motion," which very aptly describes the movement of the charge through the slowly rotating kiln. The recovery of zinc and lead by volatilization in a rotary kiln has its origin in a process patented in 1910 by Edward Dedolph, of British Columbia. The Dedolph patent was taken over by the Metallgesell-schaft of Frankfurt-on-Main, Germany, which in cooperation with the Griesheim-Elektron, now a part of a large industrial combine, introduced certain improvements (Ohlmer, Specketer patents), but without bringing the process to a state suitable for large-scale operations. The war temporarily stopped all work on the process, and it was not until after the war that the Krupp Grusonwerk, of Magdeburg-Buckau, Germany, quite independently of the Metallgesellschaft, instituted research work in this field of metallurgy, which in 1923 led to the Waelz process proper. The Krupp Grusonwerk and the Metallgesellschaft A.G. later on collaborated, and by their joint efforts further developed and perfected the Waelz process, which they are marketing together as "Waelz-Gemeinschaft." The process is capable of treating a varied type of material; for instance, oxidized and sulphide zinc ores, calamine (zinc carbonate ore) waste dumps, jig tailings, jig slimes, table concentrate slimes, brass ashes, zinc-bearing iron ores (where the iron sinter is the real objective and the zinc oxide a by-product), electrolytic-zinc leach residues, zinc muffle residues and works sweepings, lead-furnace slags, tin ores and slags, anti-

Jan 1, 1937

By Karl L. Fetters

In the process of making steel in the open-hearth furnace the refining of the metal during the working period of the heat is largely accomplished through the agency of the slag. From the birth of the process until the present day steelmakers have recognized the importance of the slag in determining the composition of the metal and the quality of the product. The general relationships between slag composition and metal analysis have long been known, at least in a qualitative or approximate fashion. For examples, the iron oxide content of the slag is higher on lower carbon heats; the more basic slags are higher in iron oxide for a given carbon content; certain amounts of iron oxide and lime arc required for phosphorus removal and a high lime-silica ratio is needed if the sulphur content of the metal is to be diminished. In recent years a number of quantitative relationships involving these and other variables have been developed through plant and laboratory studies by numerous investigators in this country and abroad. The direct comparison of laboratory and open-hearth data involves the question of the degree to which each approaches the conditions of chemical equilibrium, a question which, from the open-hearth standpoint, we are scarcely yet in position to answer. And, although a considerable body of dependable equilibrium data has been obtained in the laboratory, this work has not yet been extended to cover the ranges of slag composition encountered in basic open-hearth practice. In the present study we shall not attempt to draw comparisons between data from the two sources; nor do we attempt to draw conclusions as to the approach to chemical equilibrium in the open-hearth furnace. Many of the operating variables that are likely to be erratic or unrecorded during the earlier stages of the heat become more consistent and arc more readily subject to observation and control during later stages. For example, undigested lime or ore gradually goes into solution, the rate of carbon drop levels off, and the temperature of the metal is brought under control. For these and other reasons a greater degree of self-consistency is likely to be found among data obtained during the

Jan 1, 1940

By Karl L. Fetters

In the process of making steel in the open-hearth furnace the refining of the metal during the working period of the heat is largely accomplished through the agency of the slag. From the birth of the process until the present day steelmakers have recognized the importance of the slag in determining the composition of the metal and the quality of the product. The general relationships between slag composition and metal analysis have long been known, at least in a qualitative or approximate fashion. For examples, the iron oxide content of the slag is higher on lower carbon heats; the more basic slags are higher in iron oxide for a given carbon content; certain amounts of iron oxide and lime arc required for phosphorus removal and a high lime-silica ratio is needed if the sulphur content of the metal is to be diminished. In recent years a number of quantitative relationships involving these and other variables have been developed through plant and laboratory studies by numerous investigators in this country and abroad. The direct comparison of laboratory and open-hearth data involves the question of the degree to which each approaches the conditions of chemical equilibrium, a question which, from the open-hearth standpoint, we are scarcely yet in position to answer. And, although a considerable body of dependable equilibrium data has been obtained in the laboratory, this work has not yet been extended to cover the ranges of slag composition encountered in basic open-hearth practice. In the present study we shall not attempt to draw comparisons between data from the two sources; nor do we attempt to draw conclusions as to the approach to chemical equilibrium in the open-hearth furnace. Many of the operating variables that are likely to be erratic or unrecorded during the earlier stages of the heat become more consistent and arc more readily subject to observation and control during later stages. For example, undigested lime or ore gradually goes into solution, the rate of carbon drop levels off, and the temperature of the metal is brought under control. For these and other reasons a greater degree of self-consistency is likely to be found among data obtained during the

Jan 1, 1940

By Reinhardt Thiessen

IN THE general study of coal, all evidence points in the one direction -that coals had their origin in a manner analogous to that of peat. The best method of studying coal, whether it concerns its chemistry, composition, or physical condition, is to study peat. The essentials in a study of peat are a knowledge of the chemistry of plants, knowledge of decay and of the transformation process of plant-substances into peat. A number of facts must be emphasized, namely, (1) peat is formed under wet conditions only; (2) plants grow in the place where peat is formed; (3) all the plant substances go into the bog; and (4) all the plant substances are subjected to a series of phases of decay which are (a) in the air completely above the water level but in relatively moist conditions; (b) above the water level, but covered by debris; and (c) completely submerged by both water and debris.

Jan 3, 1925

By W. Henry Weimer

A successful surface coal operation requires the combined efforts of engineering and operating personnel. In the planning for a mine, machines should be selected to do the best work in getting the coal uncovered, loaded, and transported to the preparation plant. The best system and extent of cleaning will be determined by the market. After the fundamentals of operation have been established, the operating personnel should see they are carried out. There is no simple solution to some of the every day problems facing the operating officials. Here the production engineer with the technical approach, time studies, control methods, past experience, and available records can help in detecting causes of inefficient phases of the operations. With these studies, a careful analysis can be made in setting up the expected standards to be followed. Management can then compare the job under study with the standards and make corrections to solve the problems. 5.2-1. Annual or Daily Coal Production. Once the production cycle has been established, it is paramount that coal sales keep the productivity of the mine as high as possible. A successful company does this by what they call "the control approach." The daily tonnage report is one of the things that is a potent control tool in attaining the goals to be achieved. If production is falling short of the goal, the daily tonnage report will reveal what has to be done in the remaining days of the month or year to achieve the expected schedule. When goals are reached or exceeded, then budgeted tonnages and costs will be reached or exceeded and thus assure attainment of a profit. Failing to keep to the scheduled pace shows up quickly and prominently, facilitating any necessary action to get things back to the projected plans. The sales target is usually set a little higher than the operating production. The sales tonnage is scheduled and sales are made accordingly, slightly

Jan 1, 1968

THE composition and quality of finished steel depend upon selection and proportioning of the raw materials of the charge as well as on control of furnace practice. This chapter deals only with those raw materials of the basic open-hearth process which are important in determining the composition of the steel or slag. They are the metallic charge, oxygen-bearing materials, fluxes, and alloying and deoxidizing additions. Refractories, which may also affect the slag composition, are discussed in the previous chapter. Wide variations are possible in the type and composition of charged materials, but in all cases certain fundamental relationships among the elements of the charge must be maintained. Since the process consists essentially of refinement by oxidation of undesired elements, a balance must be established between the sources of oxygen and the elements in the charge that are subject to oxidation (see Chapters II and VII). For example, if it is desired to use a high ratio of blast-furnace hot metal to scrap, it is necessary to add an oxygen-bearing material such as ore or mill scale to eliminate the excess carbon and silicon that are present in the hot metal. An example of the opposite extreme would be the use of a metallic charge composed entirely of steel scrap. With this type of charge, it is common practice to substitute burnt lime for limestone as a flux and to charge some carbonaceous material such as coke to avoid an excess of oxygen in relation to the elements of the charge that are subject to oxidation. Elements such as copper and nickel, which are not subject to oxidation or other reactions resulting in their elimination, may be introduced into the charge only to the extent to which they are permissible in the finished steel. An example of adjustment of the charge for elements of this type would be found in the use of steel scrap high in copper. In this case, metallic components of the charge other than the scrap should below in copper, or a sufficiently high ratio of pig iron to scrap should be charged to dilute the copper from the scrap, so that the average copper content of the melt will be below the required maximum.

Jan 1, 1944

By James W. Lower

IN developing the orebody on lower levels of the Star mine at Burke, Idaho, Hecla Mining Co. is faced with a serious problem in driving raises. Levels are at 200-ft intervals. As a raise is being driven between levels, at points about 70 and 130 ft from the sill, heavy pressure arches develop and the raise becomes extremely hazardous. Eventually, following a blast, caving occurs, making it impossible to recover the raise. In February 1957 it was decided to attempt sinking a small winze on the vein from the 5500 to the 5700 level. This shaft (winze-raise No. 2) was to be used as a raise prior to stoping. It was assumed, and correctly, that the heavy ground pressure could be controlled by timbering close to the bottom after each advance.

Jan 7, 1958

By J. H. Schloen, C. W. Clark

Two papers have been written previously concerning operations at the Montreal East plant of Canadian Copper Refiners Limited. The first one,&apos; written in 1932, described silver-refinery operations at the time for producing silver and gold bullion from tankhouse anode slimes; the second,2 published in 1933, consisted of a description of the entire plant. Since publication of these papers the refinery has become the world&apos;s largest producer of refined selenium. The first selenium was produced in August 1934. Tellurium production on a commercial scale followed in October 1935. This paper will deal with selenium and tellurium production and also with present operations in the silver refinery. Blister cakes from Hudson Bay Mining and Smelting Co., Flin Flon, Manitoba, and commercial anodes from Noranda Mines Limited, Noranda, Quebec, are refined at Montreal East. Both these bullions have unusually high gold, selenium and tellurium content. The average assay of raw slimes produced from domestic and Noranda anodes is about 40 per cent Cu, 3600 oz. per ton Ag, 800 oz. per ton Au, 22 per cent Se and 3.7 per cent Te. Early Silver-refinery Operations From the start of operations in 1931 until July 1934, the raw slimes were oxidize-roasted at 700" I?. in a Nichols-Herreshoff furnace, acid-leached with tankhouse discarded foul electrolyte (20 per cent H²SO), filtered and charged directly to the doré furnace for refining to doré meta1. This is the customary method for treating tankhouse anode slimes but was not suitable at the Montreal East plant because of the high selenium and tellurium content of our slimes. In the acid-leaching process about 50 per cent of the selenium and tellurium in the roasted slimes was dissolved in the electrolyte. These elements were recovered with the copper as a sludge in a small electrolytic

Jan 1, 1943

By C. W. Clark, J. H. Schloen

Two papers have been written previously concerning operations at the Montreal East plant of Canadian Copper Refiners Limited. The first one,&apos; written in 1932, described silver-refinery operations at the time for producing silver and gold bullion from tankhouse anode slimes; the second,2 published in 1933, consisted of a description of the entire plant. Since publication of these papers the refinery has become the world&apos;s largest producer of refined selenium. The first selenium was produced in August 1934. Tellurium production on a commercial scale followed in October 1935. This paper will deal with selenium and tellurium production and also with present operations in the silver refinery. Blister cakes from Hudson Bay Mining and Smelting Co., Flin Flon, Manitoba, and commercial anodes from Noranda Mines Limited, Noranda, Quebec, are refined at Montreal East. Both these bullions have unusually high gold, selenium and tellurium content. The average assay of raw slimes produced from domestic and Noranda anodes is about 40 per cent Cu, 3600 oz. per ton Ag, 800 oz. per ton Au, 22 per cent Se and 3.7 per cent Te. Early Silver-refinery Operations From the start of operations in 1931 until July 1934, the raw slimes were oxidize-roasted at 700" I?. in a Nichols-Herreshoff furnace, acid-leached with tankhouse discarded foul electrolyte (20 per cent H²SO), filtered and charged directly to the doré furnace for refining to doré meta1. This is the customary method for treating tankhouse anode slimes but was not suitable at the Montreal East plant because of the high selenium and tellurium content of our slimes. In the acid-leaching process about 50 per cent of the selenium and tellurium in the roasted slimes was dissolved in the electrolyte. These elements were recovered with the copper as a sludge in a small electrolytic

Jan 1, 1943

By Samuel B. Christy

The present paper is a continuation of a study of the reductionworks of New Almaden, the first part of which was published under the title " Quicksilver-Reduction at New Almaden," in the Transactions of this Society, vol. xiii., p. 547.* Frequent reference will be made to some of the data there given. The following is an outline of the contents of this paper: I. Condensing appliances used at New Almaden: a. Brick condensers, b. Iron condensers—flues and " water-backs," c. Glass and wood condensers, d. Friction-coudensers—filters and revolving screens, e. Flues, towers, and chimneys. II. Analysis of condensing-systems. III. Temperature of condeusers. IV. Product of condensers. V. Treatment of soot. VI. Losses of treatment: a. Nature of losses, b. Composition, weight, and volume of dry gases, c. Volume of wet gases, d. Specific weight of quicksilver vapor, e. Vapor-loss at various temperatures. VII. Comparison with New Almaden practice. VIII. Comparison with results at Idria, Austria. IX. Comparison with results at Almaden, Spain. X. Future improvements in quicksilver-condensation. I. Condensing Appliances. The complete condensation of mercurial fumes in a large way presents numerous practical difficulties, familiar to all who have had to retort amalgams. In condensing the quicksilver-fumes discharged

Jan 1, 1886

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By Robert E. Green

Experiments were performed in order to investigate the influence of magnitude of driving force, recouery, and previous heat treatment on grain boundary migration in deformed aluminum crystals. The frequency of occurrence of strain-free grains possessing Preferred crystallographic orientations was studied both as a function of heat treatment and as a function of amount of deformation of the matrix crystal. Aluminum of such composition as to exhibit precipitation-hardening behavior was used. CONSIDERABLE work has been devoted to the factors influencing grain boundary migration in metals.1&apos;52 Aust and Rutterl-9 have studied grain boundary migration into matrix crystals containing a striation substructure, which provided a thermally stable driving force during the course of the migration experiments. These authors state that, while variations in the striation pattern were sometimes observed, it was possible to obtain reasonably uniform and reproducible striation structure by careful control of the solidification conditions. Admittedly, this source of driving force is a unique one and has served well in numerous experiments. However, although the striation substructure provides a thermally stable driving force, the subject of its reproducibility from crystal to crystal is questionable. In fact, Aust and Rutter3 attribute the scatter shown in some of their experimental points and several anomalies in boundary migration rates to variations in the substructure driving force along a single specimen. A further limitation on striation-induced driving force is that the driving force cannot be varied over wide ranges in a controlled manner. More often used as a source of driving force is the strain energy stored in a crystal during plastic deformation. This type of driving force has the disadvantage that it is not thermally stable due to recovery taking place simultaneously with the grain boundary mobility measurements. On the other hand, this strain-induced driving force is very reproducible from crystal to crystal since it is very easy to grow single crystals possessing the same purity and crystallographic orientation and then to strain them identically. In order to measure grain boundary migration rates two different methods are primarily used. Most often the technique employed is the heat-cool-etch method1&apos; which involves thermal cycling, while the other technique, developed by Graham and Cahn11 using an X-ray diffractometer and goniometer furnace, involves continuous heating only. Thus the influence of thermal cycling vs continuous heating is a factor to be considered in grain boundary migration rate measurements, particularly in cases where the source of driving force is the strain energy stored in the deformed matrix, and recovery is likely to occur. Numerous recent investigations have shown that extremely small impurity additions to zone-refined metals exert a marked effect on grain boundary migration rates1-5, 9, 12-27 and a few have considered the effect of the distribution of impurities.28-35 The concentration of impurities and their distribution as influenced by heat treatment must also be taken into account in migration-rate studies. In the present article consideration is given to the influence of the magnitude of driving force, recovery, and previous heat treatment on grain boundary migration rates. In order to vary the driving force over a large range it was necessary to use as a source of driving force the energy stored in the matrix crystal during plastic deformation. A majority of the investigations were performed on aluminum specimens which were of such compositions as to exhibit precipitation-hardening behavior.

Jan 1, 1965