Search Documents

By W. A. Young

Polynomial functions of temperature were obtained for the specific heats, thermal diffusivities, and thermal conductivities of zirconium hydrides containing 4 at. pct U. Three hydrides (H/Zr atom ratios of 1.58, 1.65, and 1.70) were studied over the range a" to 900°C and a fourth (H/Zr = 1.81) was studied over the range 0° to 760°C. The specific heats were determined from enthalpy measurements which were obtained using a unique drop calorimeter specifically designed for use with materials in which high temperature phase transitions and/or high dissociation pressures occur. Thermal diffusivities were measured by the flash method using a pulsed laser. The thermal conductiuities were obtained as the product of specific heat, thermal diffusivity, and density. The specific heats agree, within 10 pct, with values derived using a theoretical model in which the hydrogen and zirconium atoms are treated as Einstein and Debye oscillators, respectively. RELIABLE values of the thermophysical properties of the fuel are required to predict the operating temperatures and temperature response of SNAP nuclear reactors. Among the most important of these properties are the thermal conductivity, specific heat, and thermal diffusivity. A considerable number of investigations1-4 have been made of these properties for the Zr-H and Zr-H-U systems.* However, little of the drides, however, this direct method cannot yield meaningful results, since the hydrogen will redistribute under the influence of the thermal gradient, thus forming a concentration gradient; hence, one has a spectrum of compositions, rather than a homogenous alloy. Although the "average" composition of the material may be identical to the initial uniform concentration, the directly measured value of conductivity will be dependent on the thickness of the specimen, due to the highly sensitive dependence of transport properties on hydrogen content. This dependence is strikingly illustrated by the work of Bickel,5 who found that the electrical conduction of zirconium hydrides ranges from primarily hole conduction to primarily electronic conduction, depending upon the hydrogen content. Fortunately, the direct measurement of thermal conductivity is unnecessary, since it can be expressed as the product of the specific heat, thermal diffusivity, and density, all of which can be directly measured with considerable accuracy. EXPERIMENTAL Specimen Preparation. The combined fuel-moderator material used in SNAP reactors is a hydrided zirconium-uranium alloy containing -10 wt pct U. The alloy used in this work was representative of that used in nuclear reactors except that normal uranium was substituted for the enriched uranium required for reactor usage. It was produced by a triple-arc-melt and double-extrusion process. All specimens were prepared from a single cylindrical extrusion which contained 10.30 pet U, 89,35 pct Zr, and 0.35 pct impurities, The specimens for each composition were hydrided simultaneously with ultrapure hydrogen (10 ppm total impurities) using standard fuel production techniques which routinely yield homogeneous, crack-free fuel with negligible increases in the impurity levels. The hydrogen content of each specimen was determined from its weight gain and the density was measured by liquid displacement, Chemical analyses yielded hydrogen concentrations which agreed with the weight gain data within ±0.02 in H/Zr atom ratio) the concentrations of all other elements agreed almost exactly with the initial values after adjustment for the added hydrogen. The specimens used for the determination of specific heat were centerless ground to 2.00 cm diam after hydriding. A thin slice was carefully removed From each end for metallographic examination. In every case, this examination revealed a uniform structure as evidenced by the appearance and distribution of the two phases present in the fuel at the hydrogen concentrations used. TWO specimens (H/Zr = 1.600 and 1.632) appeared to be entirely 6 phase with equi-axed grains; the specimen with H/Zr = 1.756 showed

Jan 1, 1970

By R. L. Schmidt, J. D. Verhoeven

The diffusion coefficients and electrotralzsport mobilities of aluminum, gallium, and arsenic have been determined in molten germanium with the capillary reservoir technique. The diffusion coefficients are slightly higher than those determined by the solidification technique of Brirton et a1.1 It was found that aluminium and gallium migrate to the cathode in molten germanium) whereas arsenic migrates to the anode under an electric field. A possible technique for producing p-n junctions by means of electric field freezing is discussed in view of the experimental data. In the past decade or so the literature has abounded with articles concerning the solid-state properties of the semiconducting elements germanium and silicon. It is surprising by comparison how little has been published concerning the liquid-state properties of these materials. In the production of doped germanium or silicon the diffusion coefficient of the dopant in liquid germanium or silicon is an important quantity. Yet, to the best of our knowledge, no one has ever made a direct measurement of the diffusion coefficient of solutes in either molten germanium or silicon. A number of authors'-4 have determined some diffusion coefficients by the indirect technique developed by Burton et al.1 This technique appears to give numbers of the correct order of magnitude but it does depend upon a number of assumptions in the analysis and also requires prior knowledge of the viscosity of the melt. In the present work a more direct measure of the diffusion coefficients of arsenic, gallium: and aluminum in molten germanium has been made. It has been shown independently by two groups of authors5, 6 that, when an electric current is passed through the interface of a solidifying metal containing an impurity, the resulting electrotransport in the liquid boundary layer at the interface offers a mechanism for control over the redistribution of the impurity accompanying the solidification. These authors show that the degree of control is proportional to the mobility, U of the impurity atoms in the liquid boundary layer, where the mobility is defined as the drift velocity relative to the solvent per unit electric field. In principle the results apply to the solidification of a doped semiconductor and offer an interesting technique for control of the doping of a semiconductor. In the present work the mobilities of aluminum, gallium, and arsenic were determined in molten germanium in order to evaluate the potential usefulness of electro-transport as a technique for solute control when applied to the solidification of doped germanium. EXPERIMENTAL PROCEDURE Both the diffusion coefficients and the mobilities were measured using high-purity alumina capillaries and a resistivity technique for analysis. A schematic diagram of the electrotransport apparatus is shown in Fig. 1 and the details of the cell design are shown in Fig. 2. For the mobility experiments electrical contact with the bottom of the capillary was made with graphite, as shown in Fig. 2. In order to prevent electrical contact with the melt the graphite was coated with a thin layer of alumina using a plasma spray torch. The cell assembly, a graphite electrode, and another assembly containing two blank capillaries were fastened to the lavite disk shown in Fig. 1. To make a run the system was evacuated and the doped germanium was outgassed at the operating temperature of 1030°C. The cell and blank capillaries were then submerged beneath the melt and a slightly positive pressure of helium was introduced to fill them. After passing current through the cell for a given time the cell and blank capillaries were raised from the melt and the furnace was shut off. The temperature of the cells dropped below the freezing point of germanium within 1 to 2 min after the furnace was shut off.

Jan 1, 1968

By H. Kahata, I. Iwasaki, Y. Takahasi

A combined process of segregation roasting-flota-tion or magnetic separation was developed to recover nickel from lateritic iron ores and oxidized nickel ores. An ore was mixed with a halide, such as sodium or calcium chloride, and a solid reductant, and roasted, whereby the nickel content was segregated out as discrete metallic particles. Either by magnetic separation, or by flotation using a sulfhydryl collector together with a heavy metal salt as an activator, the metallic nickel could be concentrated, Effects of such variables as the types and amounts of the halide and solid reductant addition and of the roasting conditions were extensively investigated. The concentration results on several types of ores from Japan, the Philippines, and New Caledonia are presented. Laterite is a residual product of rock decay in tropical and subtropical regions, and consists mainly of hydrated oxides of iron and alumina. Those derived from serpentine sometimes become enriched in nickel, cobalt, and chromium contents. Oxidized nickel ores are of the similar origin, but their nickel as well as silica contents are higher due to gamierite-type silicates. Apparently, nickel enrichment is more pronounced in the transition region between the surface layer of iron laterite and the underlying serpentine. Iron laterites often contain over 50% iron, and their reserve is reported to exceed 22 billion tons, corresponding approximately to 20% of the world iron ore reserve.1 It is readily apparent, therefore, why the iron laterites have attracted much attention of the steel industry as a potential source of iron ores. Numerous attempts to remove nickel and chromium as byproducts, have been reported in literature.' Worldwide discoveries of high-grade iron ore deposits in recent years have inevitably lessened the interests in iron laterites. However, in view of the tremendous potential for their gross value and supplies of nickel, cobalt, chromium, and alumina along with iron, the problem remains as a challenge. Much of the chromium in laterites is present in the form of relatively coarse particles of chromite, and various classification methods have successfully been applied for its removal.2,3 The nickel, however, is intimately associated with limonite, and ordinary concentration techniques are totally ineffective. Much attention has, therefore, been given to hydro-metallurgical or pyrometallurgical means. Yet, all the known processes appear to have limitations either economically or for the use of products as iron raw materials due to a high residual content of nickel. Some attempts have been made to pre-roast laterites or oxidized nickel ores, particularly with sulfidizing agents, and to remove nickel either by magnetic separation,' or by flotation.4 It is apparent that any such concentration process would require grain growth of nickel during roasting for effective separation. Oxidized copper ores are reported to be concentrated by the segregation roasting-flotation process,5 in which the ores are roasted with a chloridizing agent and a carbonaceous reductant in order to promote the growth of metallic copper through repeated cycles of copper chloride volatilization and its reduction on the solid reductant surfaces. Examination of a vapor pressure-temperature diagram of various metal chlorides indicates that a separation of nickel from iron may be effected by a similar process. In fact, the segregation roasting of laterites was reported to increase the extraction of nickel by the ammonia leach process, as compared to the ordinary reduction roasting.6 In the present article some of the preliminary experimental results of the segregation roasting, followed by either flotation or magnetic separation, on laterites and oxidized nickel ores are reported. The effects of various parameters in the roasting as well as in the concentration steps are discussed. MATERIALS AND METHODS An oxidized nickel ore from Thio, New Caledonia, and three laterites from Homonhon, the Philippines, Wakasa and Miyagawa, Japan, were selected for the

Jan 1, 1967

By O. D. Gonzalez, R. A. Oriani

A thermo-osmosis technique has been used to measure the heat of transport, Q* , of hydrogen and of deuterium dissolved in a iron and in nickel, and of hydrogen in Feo.6Nio.4 in the tempevature range 400° to 600°C. For all these systems, Q* is negative and has a large temperature coefficient; an isotope effect can be established for the solutes only in nickel. The magnitude of Q* is considerably larger than the activation energy, E , for migration in the case of these isotopes in a iron, so that all variants of the Wirtz model must be rejected. The phenomenological definition of Q* is developed to show that Q* is related to the mechanisms by which the activation energy is dissipated back into the lattice, and that Q*/E is a function of the ratios of the mean free paths of electrons and of phonons to the distance of jump of the diffusing atom. A correlation is shown to exist between the sign of Q* in thermal diffusion and that of the effective charge in electro migration, and may be understood as due to the large ratio of the mean free path of electrons to that of phonons. THE study of nonisothermal diffusion in the solid state is of interest because certain aspects of the mechanism of diffusion are made manifest which remain concealed though still present in the isothermal case. The thermodynamics of irreversible processes characterizes nonisothermal diffusion, known as thermal diffusion or as the Ludwig-Soret effect, by a quantity, Q*, called the heat of transport, which essentially measures the sign and the magnitude of the steady-state concentration gradient produced by the imposed temperature gradient. The problem then is to understand the quantity Q* at the atomistic level. There does not exist a theory for the atomistic interpretation of the heat of transport. There are, however, two classes of simple models which seem to afford some physical insight into Q*. Wirtz's model1, z and its subsequent generalizations partition the activation energy, E, for the migration of the atom spatially about the region of the migrating atom, so that Q* is the difference between the portion of the activation energy centered about the original site of the jumping atom and that portion about the arrival site. Clearly, the magnitude of Q* cannot on this model be larger than the activation energy for migration. The model of Oriani3 also considers the spatial distribution of E not only before but also after the atomic jump, and Q* is related to the variation of the spatial distribution of E that is produced by the jump. The simplest kind of system with which to compare the consequences of these ideas is the interstitial solid solution, since one may easily choose a temperature at which only the interstitial component moves, the solvent lattice serving as a completely satisfactory frame of reference. Thus, one avoids complications arising when both species in a binary system move. In addition, one avoids the necessity of knowing the energy for the formation of a vacancy, something which is needed for the analysis of thermal-diffusion data on metals which diffuse by the vacancy-exchange mechanism. However, the number of well-measured interstitial systems is extremely small, and, in particular, there are almost no data in the published literature for the temperature dependence of the heat of transport. If one works with solutes which are gases in the pure state at ordinary temperatures, one may use the technique of thermo-osmosis4 which permits thermal diffusion to be measured over a small temperature difference so that the temperature dependence of Q* can be more easily determined. The choice of dissolved hydrogen in iron and nickel was based on these considerations as well as on the desire to look for an isotope effect associated with localized

Jan 1, 1965

By R. M. Rose, K. A. Jones

Resistive measurements ulere made on superconducting niobium single crystals in transverse magnetic fields. Crystals were grouln in both high and ulfrahigh vacua, doped with stnall quantities of oxygen, and annealed in ultrahigh vacua at temperatures from 900' to 1350°C. Maxima in the fluxoid pinr~ir~g force were observedfor the [100] and [210] directions. The increase of the critical current density with dissoved oxygen was seen to saturate at relatively low concentration. This behavior, and the variation of J, and residual resistivity (as a function of oxygen content and annealing) of both clean and dirty gassy) crystals, is seen as a consequence of the formation of clusters with (210)~b habit planes and (200)ffo common boundaries. These suboxide clusters are apparenlly stable at high temperatures and very low oxygen concentrations. It is generally known that dissolved oxygen at concentrations well below the solubility limit sharply increases the critical current density of superconducting niobium.' Such a result would not be expected if Nb-0 solutions were random, not even as the result of segregation on the scale usually encountered in solid solutions. According to the Kim-Anderson theory of flux creep,' the critical transport current density is determined by the pinning force Fp associated with some feature of the microstructure. As the Lorentz force. a or (J X R), of the transport current in the magnetic field approaches Fp, flux creep and then flux flow occur. The pinning force is expected to be quite small if the heterogeneity involved is significantly smaller than tte range of coherency which for niobium is circa 250~.~ Although the strain field of an individual oxygen atom in the niobium lattice is relatively large, it does not seem plausible that individual atoms could be so effective as to account for the data. Also, ~ramer~ found that straining and strain aging specimens containing small amounts of oxygen on occasion decreased the residual resistivity. A possible explanation for the above behavior may be found in the work of van Ooijen and van der Goot,= who found that annealing changed J, for niobium foils containing oxygen, and they attributed the changes to ordering of the oxygen atoms. This phenomenon has been observed by other investigators using X-ray and PROCEDURE Cylindrical 4-in.-diam niobium single crystals with axial orientations [ill], [110], [112], and [oo~] were grown from pure niobium, see Table I for analysis, in an ion-pumped ultrahigh-vacuum system using the electron beam floating zone technique. Total pressure during growth was lo-'9 torr: the oxygen partial pressure was less than lo-" torr, as determined by a mass spectrometer. These crystals will be referred to as the "clean" crystals. Similar crystals were also grown in another system at a pressure of 5 X 10"6 torr. These crystals will be referred to as the "dirty" crystals. Specimens 14 in. long were cut from the as-grown crystals and one end was polished down to no. 600 carbide paper smoothness. A back-reflection Laue photograph was then taken in order to fix the crystallo-graphic directions transverse to the crystal. The critical current density J,, the current density necessary to produce a voltage drop of 1.0 pv between voltage leads placed a in. apart, was determined as a function of the magnitude and direction of the transverse magnetic field and of the oxygen concentration. The technique and experimental arrangement was essentially similar to that of Tedmon et al.' In the remainder of this paper, the azjmuthal angle $ for the field H is referenced to the [ I101 direction in all four crystals, and oxygen was added in small equal increments by anodization and annealing.7 The resistivity ratio, RR, of the resistance at room ternperature to that at 4.2"K (H =7.00 kG) was determined as well.

Jan 1, 1970

By T. K. Perkins, R. N. Hoffman, O. C. Johnston

A simplified theory of viscous fingering in miscible systems has been developed. It predicts the correct functional relationship between pertinent variables and permits the calculation of the order of magnitude of fingering behavior for simple systems, such as linear or radial. The theory is based on the following four observations: (1) cross-flow takes place only near the ends of fingers; (2) the relative finger width is about 0.5; (3) fingers can be suppressed by transverse dispersion, the suppression being quantitatively described by a critical ratio of dispersion times; and (4) the widths of extending fingers are close to the minimum size finger that can grow at any stage of displacement. Fingering is studied in two-dimensional linear and diverging radial systems, both theoretically and experimentally. For linear systems, the length of the fingered region is proportional to mean displacement; the finger width is proportional to square root of mean displacement; and there is a small initial region void of fingers because of suppression by longitudinal dispersion. For the radial system, two limiting conditions are recognized. If the mean displacement is small compared with the wellbore radius, the length of the fingered region is proportional to the mean displacement. The width is proportional to the square root of mean displacement. If the mean displacement is large compared with wellbore radius, length of the fingered region is proportional to mean displacement, but the number of fingers approaches a constant value. Also, in the radial case there is a small initial region void of fingers because of longitudinal dispersion. INTRODUCTION The behavior of viscous fingers in miscible systems has been of interest to the oil industry for many years. Previous studies have clearly shown the existence and nature of fingers in small models.1,2,3,4 Engineering techniques for extrapolating to reservoir situations have been proposed. 5,6 Still, because of the lack of a real understanding of the mechanics of fingering, there remains uncertainty and disagreement as to the best way to scale or calculate fingering behavior in the reservoir. In this paper we discuss a study of the mechanics of fingering in miscible systems (i.e., why do fingers behave as they do?). A simplified theory is developed which we believe will (1) predict the correct functional relationship between pertinent variables, (2) permit us to calculate the order of magnitude of fingering behavior for simple systems such as linear and radial, and (3) give further insight into the problem of scaling or otherwise extending the results to more complicated reservoir conditions. The paper includes the following sections: (1) brief summary of the mixing behavior of miscible fluids in linear and radial systems; (2) four fundamental observations of fluid flow (under fingering conditions); (3) based on these four observations, a simplified theory of fingering in linear and radial systems is developed; and (4) the theoretical equations are compared with experimental fingering data measured in laboratory models. A REVIEW OF DIFFUSION AND DISPERSION As will be shown later, the behavior of viscous fingers in miscible systems is controlled in large degree by the mixing between the two fluids. A quantitative description of fingers will first require a quantitative description of mixing. Fortunately, much work has been done to clarify this subject; a fairly comprehensive review has been presented in a previous paper. 7 For present purposes let us (1) briefly summarize the quantitative description of diffusion and dispersion (both longitudinal and transverse) within a differential element; (2) present a simplification of the "width of mixed zone"; and (3) describe the effect of geometry on width of mixed zone. If one fluid is displaced from a porous medium by another miscible fluid (in the absence of fingers)

Jan 1, 1966

By R. G. Jones, W. L. Kinney, R. E. Schilson, R. S. Wilson, G. A. Clark, H. Suralo

This paper discusses the results of the Fry conventional or cocurrent in situ combustion test, which was conduct-ed in a 3.3-acre inverted five-spot. The depth of the formation was between 880 and 936 ft; the oil had a specific gravity of 28.6° APl and a viscosity of about 40 cp at the reservoir temperature of 65°F. Preceding the combustion test, air injection tests were conducted which, in conjunction with geological studies, were used to evaluate the characteristics of the reservoir. Combustion was initiated on Oct. 13, 1961, with ignition being accomplished by a 40 kw electrical heater. The test phase of the project ended on Oct. 1, 1963. During the test, the average air injection rate was 1,520.-000 scf/D. Throughout the test, production of all fluids— gas, oil, and water—was monitored. Cumulative oil production credited to the project was 100,586 bbl. The cumulative air-oil ratio was 11,500 scf/bbl oil, and the oxygen uti1ization efficiency was 87 per cent. INTRODUCTION The Marathon Oil Co. conducted a successful in situ combustion test, beginning Aug. 22, 1961, at the Fry unit, Crawford County, 111. The purpose of the project was to test the feasibility of cocurrent in situ combustion as a means of oil recovery in the Fry type reservoir. Interest in in situ combulstion as an oil recovery tool has been stimulated mostly by the existence of large reserves of heavy viscous crudes with low expected recovery, usually less than 10 per cent. These are the so-called unrecoverable reserves, and most combustion tests to date have been conducted in this type of reservoir.1-4 In contrast, the Fry combustion test was conducted in a reservoir with a relatively high gravity oil having a relatively low viscosity. This paper discusses the performance of the test. The geology of the reservoir and the field operations are discussed in separate papers.5 TEST SITE The Fry combustion test was carried out in a 3.3-acre inverted five-spot portion of a lenticular body of Robinson sandstone. Net sand was 50 ft thick, porosity averaged 19.7 per cent, oil saturation was 68 per cent of pore volume, and water saturation was 20 per cent of pore volume. The oil in place was estimated at 1,040 bbl/acre-foot, or 171,600 bbl within the 3.3-acre pattern. The water in place was 326 bbl/acre-foot, or 53,800 bbl. The oil has a specific gravity of 28.7° API and a viscosity of 40 cp at the reservoir temperature of 65°F. AIR INJECTION PERFORMANCE Air injection took place in two phases, the phases separated by ignition of the reservoir. In the pre-ignition phase, air injection tests were conducted in the summers of 1960 and 1961. These indicated that the Fry reservoir was confined, and a high return rate of injected air could be expected. This proved to be an outstanding characteristic of the project, as cumulative gas production was 95.3 per cent of the air injected. The difference between the cumulative air injected and the total gas produced can be largely accounted for by the quantity of air stored in the reservoir. An estimated 16 X 10 cf of air remained in the burned-out portion of the reservoir and an indeterminate amount of gas was stored in the unburned but pressurized reservoir. Hence, a complete material balance of gases would account for nearly 100 per cent of the air injected. At times during the test, the daily gas production rate was 98 per cent of the daily air injection rate. Fig. 1 presents the air injection history of the Fry com-

Jan 1, 1966

By R. E. Ogilvie, J. I. Goldstein

The a and y solubility limits in the Fe-Ni phase diagram have been redetermined at temperatures above 500°C. Both a diffusion-couple and a quench and anneal technique were used. The solubility limits were measured with an electron-probe micro-analyzer. The nickel concentration at the phase boundary is increased below 700°C and the a solid-solubility range is much larger than had been previously measured. The solubility limits are also extrapolated to 300°C. It is suggested that the solubility of nickel in a FeNi reaches a maximum in the temperature interval 400o to 500°C. THE equilibrium diagram has been of great use in the field of meteoritics, where the phase relations between kamacite (a) and taenite (?) in metallic meteorites can be described by means of the Fe-Ni diagram. The study of metallic meteorites by electron-probe microanalysis has cast some doubt on the accuracy of the presently available Fe-Ni diagrams.1, 2 Recent thermodynamic studies of the Fe-Ni system also suggest that the diagram may be in error.3 For these reasons the high-temperature (800o to 500°C) part of the diagram was redetermined. INTRODUCTION The currently accepted Fe-Ni diagram is that of Owen and Liu.4 Above 910°C, there is a region of complete solid solubility, ? (fee). Below 910°C, the a (bee) phase is stable in pure iron. The effect of increasing amounts of nickel is to stabilize the y phase. The phases that form when Fe-Ni alloys are heated or cooled bear little relation to the equilibrium diagram. If an alloy is cooled from the y state and held at a temperature within the a + y field, no evidence has been found for the occurrence of the y - a transformation.5 If the alloy is cooled to low enough temperatures the y phase breaks down into a supersaturated bee phase called a2. In fact, in alloys over 27 pet Ni the y phase is retained at room temperature.6 The a, phase has the same composition as the original y. The temperature at which a2 forms, the M, temperature, has been determined experimentally.' A state of equilibrium can be approached by cooling below M, to form a2 and then reheating the alloy into the two-phase region of the diagram. The y phase will then begin to precipitate out of the a2 phase and grow. The growth of the phase, however, is quite slow. Using the interdiffusion coefficients -Da of Goldstein et al.,8 it is estimated that it takes about 1 year to grow a 10-µ-wide region of ? at 700°C in a 5 pet Ni alloy. Owen and Liu4 used the technique just described to form the equilibrium phases. The phases present were determined by means of X-ray analysis. The accuracy of their diagram depends on the number of alloys available near the phase boundary at a given temperature. In this study two different techniques were used to determine the a/a + ? and ?/a + ? solubility limits. The inherent accuracy of both techniques was greatly improved over that used by previous investigators because the phase-boundary compositions were measured with an electron-probe microanalyzer. PROCEDURE The two methods used to determine the Fe-Ni diagram are the diffusion couple (D.C.) and the quench-and-anneal (Q.+A.) techniques. In the first method, diffusion couples whose diffusion path goes through a two-phase region of the phase diagram were used. A description of the technique used for making the diffusion couples has been described in a previous paper.' After the diffusion treatment a discontinuity in the resultant concentration vs distance profile was measured. The nickel concentrations in the a and ? phases at the interface of the discontinuity are the solubility limits of the a and ? phases in the phase diagram at the diffusion temperature. If the interface com-

Jan 1, 1965

By H. I. Aaronson

ONLY limited studies have been made of pro-eutectoid a morphology in hypoeutectoid Ti-Cr alloys during previous investigations, 1-3 The nature of the eutectoid reaction, ß?a + TiCr2, has been considered in somewhat more detail.1,2,4,4 Inasmuch as the proeutectoid ferrite reaction in plain carbon steels has recently been extensively investigated in this laboratory, advantage has been taken of the opportunity to compare the morphologies developed in two rather different eutectoid systems in order to permit a preliminary estimate to be made of the degree of generality which may be ascribed to the various results obtained. Experimental Procedure The chemical analyses of the alloys used are given in Table I. The 7.22 pct Cr alloy was prepared by the Battelle Memorial Institute from iodide titanium and high purity chromium. The initial ingot was made by arc melting a master alloy and iodide titanium. The resultant ingot was twice remelted. by the consumable electrode technique. Upset forging at 950°C reduced the final ingot to 3/4 in. sq bars. The 10.94 pct Cr alloy was prepared by the Titanium Metals Corp. of America from sponge titanium and chromium of ordinary purity. This alloy was melted twice by the consumable electrode technique, forged at 1200° to a 3/4 in. sq bar, and rolled at 815°C to a 1/2 in. round. Specimens 1/4 in. x 1/4 in. x 1/16 in. were cut from the 7.22 pct Cr alloy; halves of disks 1/2 in. in dlam and 1/16 in. thick served as specimens of the 10.94 pct Cr alloy. These specimens were individually encapsulated in Vycor, Each capsule was evacuated three times to a pressure of 2 to 6 x lo-' mm Hg and flushed twice with a reduced pressure of argon prior to sealing. The inclusion of two small packets of zirconium chips permitted the capsules to be outgassed and internally gettered, without heating the specimen, prior to heat treatment. The specimens were solution annealed for 40 min at 1000°C, isothermally reacted in deoxidized lead pots, and quenched in iced water. Most of the isothermal reaction treatments were carried out at 25" intervals between 725° and 550°C on specimens of the 7.22 pct Cr alloy and at 650°C on specimens of the 10.94 pct Cr alloy. Results and Discussion Morphologies of Proeutectoid a*—Kinetics of the ß?a Reaction: Fig. 1 shows the TTT-curves for the beginning of the proeutectoid a and the eutectoid reactions in the temperature range investigated in the 7.22 pct Cr alloy. The M, temperature in this alloy is below 0°C. The curve for the beginning of the proeutectoid a reaction is in good agreement with that of Frost, Parris, Hirsch, Doig, and Schwartz' for a 7.54 pct Cr alloy, appears at considerably earlier reaction times than the corresponding curve presented by Rostoker4 for a 7 pct Cr alloy, and lies athwart the curve of Spachner and co-workers11 for an 8 pct Cr alloy. Differences in criteria for the beginning of the a reaction and the relatively high rate of this reaction at lower temperatures presumably account for some of these divergences and may also explain, in part, the apparent failure of an iodide-base 7.22 pct Cr alloy to react more slowly than sponge-base 7 to 8 pct Cr alloys. Grain Boundary Allotriomorphs: Crystals of this morphology nucleate at and grow preferentially and more or less smoothly along the matrix grain boundaries.5-7 Allotriomorphs are the first morphology to precipitate at most grain boundaries at reaction temperatures from 725°C, the highest temperature studied, at least through 575°C. Fig. 2 Shows typical allotriomorphs, formed during an early stage of transformation at 725°C. Grain boundary allotriomorphs are not the predc=iaant morphology at late reaction times at any temperature studied. However; from 725" through

Jan 1, 1958

By R. Kerby, T. R. lngraham

The rates of cadmiuln cementation from buffered solutions were studied on both the cylindrical and circular faces of a rotating zinc disk. The activation energies are equivalent on both surfaces, but the rate is more rapid on the cylindrical face. At higher temperatures and at pH values above 6.4, the rate of deposition increases because of an increase in the cathodic area of the deposit. The rate may also be increased by decreasing the thickness of the diffusion layer by rapid stirring. The presence of small amounts of copper, cadmium, lead, iron, or aluminum in the zinc does not affect the cementation rate, but when srnall amounts of copper, cobalt, and arsenic were present in the solution cadmium deposition ceased shortly after it started. Small amounts of copper in solution become cemented with the cadmium to form a coarse deposit of Cd3Cu. When zinc ores containing cadmium are processed for electrolysis, the cadmium appears with the zinc in the leach liquors. Because of the discharge potential of the cadmium ion and the hydrogen overvoltage on metallic cadmium, the cadmium ion must be removed prior to zinc electrolysis to prevent its codeposition. Cadmium is usually removed from acidic zinc sulfate solutions by cementation on zinc. When zinc sheets are used with the appropriate conditions of pH and temperature, a finely divided, high-purity cadmium powder is obtained; it floats to the surface with attached hydrogen bubbles and, after careful washing, may be processed directly to a marketable product.' The reaction on zinc sheets is relatively slow because of the limited amount of exposed cathodic area on the sheets. A much more rapid reaction is obtained when zinc powders are stirred into the solution, but this procedure does have a potential disadvantage: some unreacted zinc may be trapped in the cemented cadmium and thus lower its grade.1 The equilibrium constant at 25°C for the displacement of cadmium by zinc is of the order of lo", which indicates that at equilibrium the displacement would be essentially quantitative and no back reaction need be considered. This indication is not entirely true, however, because in the presence of oxygen any loose cadmium which is out of contact with metallic zinc tends to redissolve after cementation.' The overall effect is much the same as that to be expected if the equilibrium constant were much smaller. Previous experimental work on cementation reac- tions3 is in general agreement that the rates of cementation usually follow first-order kinetics. The metal on which cementation occurs is considered to consist of anodic areas from which metal dissolves and cathodic areas onto which the reactive metal is cemented. For the reaction to continue, the cemented deposit must remain open and porous for the removal of ions. Usually, the deposited metal influences the rate of cementation; when it blocks the pores in the deposit, the rate of cementation will be decreased. Alternatively, when the cemented metal grows as den-drites or as coarse powder the cathodic area is correspondingly increased and the rate of cementation increases,3 Thus, it is only during the initial stages of cementation, prior to the development of deposit effects, that the kinetic behavior of the reaction may be studied without ambiguity. In this paper, experiments will be described for cementation of cadmium from dilute solutions onto the surface of a rapidly spinning zinc cylinder. The effects of ionic concentration, disk rotation speed, temperature, and impurities will be described. APPARATUS AND PROCEDURE The apparatus used for the experiments was described in a previous paper.4 It consisted of a 2-liter vessel in which the contents were protected, against oxidation, by a stream of prepurified nitrogen. The vessel was immersed in a water bath which controlled

Jan 1, 1970

By J. Handin

Triaxial compression tests with independently applied external confining pressures and internal pore pressures show that the ultimate compressive strengths of representative oil well cements are nearly linear functions of effective pressure — the difference between external and internal pressures on the jacketed cylindrical specimens (to 15,000 psi). The strengths are little affected by the test temperature to 350F (not to be confused with the curing temperature). At an effective pressure of 15,000 psi, strengths are in the rage of 30,000 to 50,000 psi, comparable to those of sedimentary rocks under similar conditions. The cements become very ductile even under low effective pressures; permanent shortenings of 30 per cent or more are attainable without rupture. INTRODUCTION Since the pioneering work of Richart, Brandtzaeg and Brown1 on the failure of cement under combined compressive stresses, it has been recognized that ultimate compressive strength is greatly enhanced by the application of confining pressure. More recently, Mc Henry2 showed that the strength of concrete was a linear function of the effective pressure (the difference between the external confining pressure on a jacketed specimen and the internal fluid pore pressure), at least for a range of 0 to 1,500 psi. The effect of temperature had not been investigated, and no previous systematic triaxial compression testing of naterials used for oilwell cementing seems to have been done. The present work was suggested by the late J. hi. Bugbee3 who stated that "consideration of the common application of high-pressure hydraulic fracturing to the initial completion or recompletion of wells, and the large pressure drawdowns in some producing wells, particularly those in abnormally high-pressure gas-condensate reservoirs, raises the question of what is a suitable cement strength for various completions. The intuitive belief exists that cement strength need be no greater than formation strength. Tests should, however, be conducted at downhole conditions." The ultimate compressive strengths of rocks penetrated by the borehole must rise several fold with increasing depth.4 This marked enhancement of strength is due to the influence of the effective pressure, the total weight per unit area of the overburden less the hydrostatic pore pressure. (The effect of temperature due to the geothermal gradients is relatively small for depths to 30,000 ft.) .A significant comparison of the strengths of rocks and cements at downhole conditions requires knowledge of the confined compressive strengths of cements as well. EXPERIMENTAL PROCEDURES The theory and technique of triaxial compression testing are fully discussed in earlier reports.4-6 Briefly, cylindrical specimens 1-in. long and 0.5-in. in diameter are jacketed in thin copper tubes of negligible strength, placed in the test chamber and subjected to an external confining pressure of kerosene and loaded axially by the piston at a strain rate of 1 per cent per minute. Pore pressures of water (or kerosene) are applied independently through the hollow piston and are maintained constant during the shortening of the specimen, Tests at sensibly 0 pore pressure are arranged so that any free water in the cement can escape to the atmosphere. (If egress of water were denied, pore pressure would rapidly attain the value of the external confining pressure because of reduction of pore space.) The test chamber can be heated for high-temperature experiments. Unless otherwise noted, the cement samples were air dried for about a week. Recorded during a test are pore and confining pressures, shortening and axial differential force (total force less the product of the confining pressure and the area of the piston). True stress-strain curves are constructed by dividing the measured differential force by the actual cross-sectional area of the specimen at a given

Jan 1, 1966

By M. A. Grossman

The harden ability of most steels can be predicted within 10 to I5 per cent provided the complete chemical composition is known, including "incidental" elements; and provided the as-quenched grain size is known; and provided, finally, that the composition and heating temperatures for hardening are such as to result in austenite free from carbide particles. In the method proposed herein, the steel is considered as having a base hardenability due to its carbon content alone (the hardenability of a "pure steel" of the given carbon content, without any other elements), and this base hardenability is multiplied by a multiplying factor for each chemical element present. After multiplying all these together, the final product is the hardenability. Grain size may be taken into account either in the base hardenability or after the multiplication. Hardenability is stated in terms of "ideal critical diameter", namely, the diameter of bar, in inches, that will just harden all the way through (absence of un-hardened core) in an "ideal" quench, and the calculation may also be related to the Jominy test The data bring out certain features rather clearly. For example: i. It is quite useless to attempt to predict hardenability unless all elements, including "incidentals,,) are known; thus an "incidental,, chromium content of 0.20 per cent increases the hardenability by about 50 per cent. 2. The relative effectiveness of different alloys is sometimes unexpected; thus molybdenum when calculated in this way appears to be of the same order of effectiveness as manganese, rather than much more powerful, as would appear to be common experience; observe that an increase from no manaanese to 0.20 per cent Mn provides a multiplying factor of 1.67, and an increase from no molybdenum to 0.20 per cent Mo provides a factor of 1.63, an increase of over 60 per cent in each case. However, if to a steel containing 0.50 per cent Mn there is added "20 points of manganese," the factor is raised from 2.65 (for 0.50 per cent Mn) to 3.35 (for 0.70 per cent Mn), or an increase of only 26 per cent. Thus the fist small addition of an element has a much more powerful percentage effect than an equal further addition when some is already present, and in most cases the effect of molybdenum is considered in relation to a steel in which molybdenum is absent. 3. If two elements are equally effective, a greater hardenability will be obtained by using, for example, 0.5 per cent of each than by using I.o per cent of either of them alone. 4. A knowledge of the as-quenched grain size is essential for precise work, since a difference of only one grain size number (say No. 7 instead of No. 6) makes a difference of almost 10 per cent in hardenability (in these units); this, however, does not apply to certain It should be emphasized that in chromium steels (over 0.30 per cent Cr) and chrome-molybdenum and chrome-vanadium steels, un-dissolved carbides are likely to be present in the steel as quenched, and that in such cases the charts can indicate only a maximum Passible hardenability, whereas the extent of hardening actually obtained may be much less. Thus tests on a number of chrome-molybdenum steels have indicated a degree of hardening amounting to only 50 to 65 per cent of the maximum possible, and in chromium steels from full hardening (100 per cent) down to as low as 70 per cent. On the other hand, when the amount of such elements is small (Cr under 0.30 per cent, Mo up to 0.25 per cent in the

Jan 1, 1942

By M. A. Grossman

The harden ability of most steels can be predicted within 10 to I5 per cent provided the complete chemical composition is known, including "incidental" elements; and provided the as-quenched grain size is known; and provided, finally, that the composition and heating temperatures for hardening are such as to result in austenite free from carbide particles. In the method proposed herein, the steel is considered as having a base hardenability due to its carbon content alone (the hardenability of a "pure steel" of the given carbon content, without any other elements), and this base hardenability is multiplied by a multiplying factor for each chemical element present. After multiplying all these together, the final product is the hardenability. Grain size may be taken into account either in the base hardenability or after the multiplication. Hardenability is stated in terms of "ideal critical diameter", namely, the diameter of bar, in inches, that will just harden all the way through (absence of un-hardened core) in an "ideal" quench, and the calculation may also be related to the Jominy test The data bring out certain features rather clearly. For example: i. It is quite useless to attempt to predict hardenability unless all elements, including "incidentals,,) are known; thus an "incidental,, chromium content of 0.20 per cent increases the hardenability by about 50 per cent. 2. The relative effectiveness of different alloys is sometimes unexpected; thus molybdenum when calculated in this way appears to be of the same order of effectiveness as manganese, rather than much more powerful, as would appear to be common experience; observe that an increase from no manaanese to 0.20 per cent Mn provides a multiplying factor of 1.67, and an increase from no molybdenum to 0.20 per cent Mo provides a factor of 1.63, an increase of over 60 per cent in each case. However, if to a steel containing 0.50 per cent Mn there is added "20 points of manganese," the factor is raised from 2.65 (for 0.50 per cent Mn) to 3.35 (for 0.70 per cent Mn), or an increase of only 26 per cent. Thus the fist small addition of an element has a much more powerful percentage effect than an equal further addition when some is already present, and in most cases the effect of molybdenum is considered in relation to a steel in which molybdenum is absent. 3. If two elements are equally effective, a greater hardenability will be obtained by using, for example, 0.5 per cent of each than by using I.o per cent of either of them alone. 4. A knowledge of the as-quenched grain size is essential for precise work, since a difference of only one grain size number (say No. 7 instead of No. 6) makes a difference of almost 10 per cent in hardenability (in these units); this, however, does not apply to certain It should be emphasized that in chromium steels (over 0.30 per cent Cr) and chrome-molybdenum and chrome-vanadium steels, un-dissolved carbides are likely to be present in the steel as quenched, and that in such cases the charts can indicate only a maximum Passible hardenability, whereas the extent of hardening actually obtained may be much less. Thus tests on a number of chrome-molybdenum steels have indicated a degree of hardening amounting to only 50 to 65 per cent of the maximum possible, and in chromium steels from full hardening (100 per cent) down to as low as 70 per cent. On the other hand, when the amount of such elements is small (Cr under 0.30 per cent, Mo up to 0.25 per cent in the

Jan 1, 1942

By Tasuku Fuwa, John Chipman, David H. Kirkwood

Fe-C-Si alloys in silica crucibles were held at 1600°C in a controlled atmosphere of CO and Co2 and the approach to equilibrium was obsertsed. Results were not of sufficient precision to establish the activity and interaction coefficients. Observations 012 the equilibrium provided an average value for the standard free-energy change which differed by + 1.1 kcal from the earlier accepted value. The C-SL relation at other temperatures is calculated and shown graphically. IN the refining of steel in an acid-lined furnace, it is well known that, unlike in basic refining, a very significant amount of silicon may remain dissolved in the metal even when the carbon content approaches a final endpoint. Further, it is known that the residual silicon increases with increasing temperature. The quantitative relation between silicon and carbon can be calculated for equilibrium conditions from data already available on the Fe-C-O and the Fe-Si-O systems. Such equilibrium calculations could show us approximately the limitations within which the reaction would be expected to operate in practice. In the oxidation of a bath containing both carbon and silicon it is well known that at low temperatures silicon is preferentially oxidized first. It can be shown by calculation that at high temperatures carbon will be oxidized preferentially. It is the purpose of this paper to record direct observations on the Si-C relation by means of experiments carried out in an atmosphere of carbon monoxide for Fe-C-Si alloys contained in silica crucibles. When such a system is brought into equilibrium, at a fixed temperature, the composition of the liquid metal is governed by the following equations: Both K1 and K2 are known with a fair degree of accuracy, and may be calculated from the tabulated In general the percentage of CO2 is extremely small compared to that of CO and in the experiments to be described the partial pressure of the latter was generally only slightly below 1 atm. EXPERIMENTAL METHOD The induction furnace employed was the same as that described by Rist and chipman' and by Fuwa and chipman.2 It was modified slightly in view of the change from alumina to silica crucibles. The small silica crucible was surrounded by a thin susceptor of molybdenum sheet which in turn rested inside a zirconia crucible. Since the zirconia was subject to breakage, it was supported inside an alumina crucible. The charge consisted of 30 to 35 g of electrolytic iron along with the required amounts of refined silicon and graphite to produce a melt of required composition. Purified carbon monoxide and carbon dioxide were passed into the furnace through carefully calibrated flow meters. Two separate and independent series of experiments were carried out. In Series I (D.H.K.) the melt was held in the furnace at 1600°C for periods of time up to 6 hr. Samples were taken at intervals in silica tubes and were analyzed for carbon and silicon. The results of the last one or two samples taken from each experiment and the direction in which equilibrium appeared to be approached are shown in Table I. In Series II (T.F.) the silica crucibles were of less satisfactory strength and the melts were held at 1600° C for periods of only 2 to 4 hr. In heats number 29 to 45 inclusive, the metal was cooled in the furnace and the ingot itself served as a sample for analysis. In heat 46 and all subsequent heats, samples were withdrawn in silica tubes at the termination of the heat, and these samples were analyzed. The results of all of these experiments in which equilibrium appeared to be approached are listed in Table II.

Jan 1, 1965

By M. H. Caron

THE most outstanding property of ammonia liquors, used in the ammonia leaching process is their very limited ability to dissolve all compounds present in reduced ore except nickel and cobalt. Although they do have such a high degree of purity, even the smallest amounts of impurities contaminate the precipitate of basic nickel carbonate that may be obtained from pregnant liquors by straight distillation. Figures have been given in a separate paper regarding the extent of such contamination. The product of straight distillation is likely to contain small amounts of Fe, Mn, MgO and SiO2 as well as some sulphate and sulphide. The sulphur can be readily eliminated by calcination of the product at the proper temperature and MgO and SiO2 by reduction and melting of the metal with a suitable flux. After such treatment the metal is relatively pure, and the iron and manganese content will be very small. The cobalt content, however, may vary considerably, depending upon the ore treated. The metal obtained from pure true garni-erite ores usually has only a small cobalt content of less than 1 pct. Metal obtained from medium grade iron-rich nickel ores may show cobalt values from 2 to 3 pct, and the alloy obtained from laterite is likely to contain as much as 10 pct cobalt. By proper treatment a good deal of cobalt may be recovered from lateritic nickeliferous iron ores, and cobalt will become the major constituent of the pregnant liquor if asbolan ores or similar products are treated. The pregnant liquor of "run of mine" nickel ores may have a pinkish shade, indicating the presence of cobalt. It is evident that from such liquors the metals should be recovered separately. Even if cobalt is present in only very small amounts, it would probably be economically justifiable to recover both metals as pure as possible if a suitable process could be devised. The author has made investigations along this line and has patented some processes adapted to the treatment of this type of solutions. Selective Dissolution of Nickel from Basic Nickel Carbonate Containing Some Cobalt: Basic nickel carbonate obtained from true garnierite ores by straight distillation of the pregnant liquors, always contains some cobalt as well as the normal impurities. In. order to improve the quality of the nickel product and to recover most of the cobalt, the following process has been devised. By using liquors with a low CO2 to NH3 ratio, nickel can be redis-solved preferentially to cobalt. It is not a sharp and clean separation but a selective one, for the bulk of the nickel may be redissolved with a small amount of cobalt, and a small residue may hold the bulk of the cobalt. The greatly increased cobalt content of the residue is indicated by a pronounced olive green color, in contrast with the light green color of pure basic nickel carbonate. The following example is given from Dutch patent No. 52788, Klasse 40a. 43 granted June 17, 1942: The original precipitate contained about 0.55 pct cobalt calculated on total nickel + cobalt. Eight hundred and fifty grams of the basic nickel carbonate were redissolved in leach liquor containing 7.12 pct NH3 and 2.12 pct CO2. The weight of the dry residue was about 3.5 pct of the original weight. By analysis it was found that the residue contained: Fe 1.93 pct, Co 6.01 pct, Ni 34.87 pct and also a certain amount of silica. The clear filtered blue liquor was distilled and the precipitate of basic nickel carbonate from this analyzed: Fe 0.008 pct, Co 0.0146 pct, Ni 42.37 pct. It is obvious that this product is considerably more pure, since calculation shows that about 94 pct of the original cobalt remained in the residue. Cobalt and nickel can be recovered by further

Jan 1, 1951

By John Wulff, David A. Stevenson

The solubility of iron and cobalt in liquid lead, the solubility of chromium in liquid tin, and nickel in liquid silver were determined up to 1300°C in an atmosphere of hydrogen. Liquid samples were taken at different temperatures and analyzed. The data obtained were plotted to show the relationship between log mole fraction of solute and the inverse of the absolute temperature. Resulting values for the differential heat of solution (AH) and the excesspartial molar entropy (S)are: for the iron-lead system = _24,200 cal per mole and AT = 5.0 e.u. for the a phase, and AH = 18,300 and S = -0.1 e.u. for the y phase; for the cobalt-lead system AH = 16,500 cal per mole and AS =0.7 e.u.; for the chromium-tin system AH = 15,600 cal per mole and AS = 8.5 e.u.; for the nickel-silver system AH =18,000 cal per mole and AS = 4.0 e.u. RECENT developments in coating, brazing, and heat transfer have focused attention on specific cases of solid-liquid interaction in metal systems, particularly those involving dilute liquid solutions. One fundamental quantity of interest in such systems is the equilibrium phase distribution between solid and liquid phases. In any effort to fully understand such interactions, one must be able to describe the equilibrium state precisely. Furthermore, in order to develop genera! relations for such systems, one must know the equilibrium state in a number of different cases. This investigation was devoted to a study of the equilibrium phase distribution in four binary systems: solid iron-liquid lead; solid cobalt-liquid lead; solid chromium-liquid tin; solid nickel-liquid silver. The iron-lead system was previously studied by Shepard and parkman' and later by Fleischer and Elliott2 with differing results. Both investigations were carried out by sampling the saturated liquid, and analyzing it chemically. The cobalt-lead system was previously reported by Pelzel,3 who noticed no discontinuity near the transformation. A limited investigation of the chromium-tin system was made by Wlodek and wulff4 using a weight loss method. This work was done in conjunction with the development of a process for coating molybdenum with chromium from tin solutions. To more fully under- stand the kinetics of the process, a more accurate determination of a solubility was desirable. No significant data were found in the literature on the nickel-silver system. Data on the latter system were, however, relevant to the investigation of the corrosion kinetics of copper-nickel alloys in liquid silver as carried out by Harrison and wagner,5 EXPERIMENTAL APPARATUS AND PROCEDURE Of the techniques available for the study of such systems the most effective appears to be that of liquid sampling,2,6,7 which is the method used in the present investigation. A schematic diagram of the sampling furnace is given in Fig. 1. Large pieces of solute metal, in excess of saturation solubility, were added to 200 g of the solvent metal, and the entire charge placed in an alundum crucible. Analytical reagent or materials of chemically pure grade were used in all investigations. The crucible was contained in a zircon muffle tube positioned vertically in the uniform hot zone of a Globar resistance furnace. The tube was provided with a number of ports which permitted sampling at temperature and in controlled atmospheres or vacuum; the ports were also useful for evacuation and introduction of gases as well as for thermocouple measurements. A chromel-alumel thermocouple Sheated in a porcelain tube was used for temperature measurements. A purified hydrogen atmosphere was employed in all experiments reported in this paper. The hydrogen was purified by passing it first over hot copper gauze to remove oxygen and then through a molecular sieve immersed in

Jan 1, 1962

By E. S. Machlin, Morris Cohen

The isothermal formation of martensite in a 71 pct Fe, 29 pct Ni alloy is found to take place mainly by the nucleation of new plates rather than by the growth of existing ones, and is dependent on the temperature and time of the isothermal hold, the amount of atherrnal martensite present, the state of internal strain, and the application of tensile stress. The conclusion is reached that the isothermal nucleation is activated by thermal fluctuations superimposed on localized regions of very high strain. The reaction-path concept, involving martensite nucleation at strain embryos by athermal activation on cooling, or by thermal fluctuations on holding, reconciles the athermal and isothermal modes of transformation, and offers a unified picture of the kinetics of martensite formation. THE phenomenon of isothermal martensite formation has been the subject of considerable study lately,'-' and its reality has been thoroughly established. The existence of such isothermal transformation has been claimed to confirm the nucleation and growth hypothesis as applied to the martensitic reaction.1 " However, the isothermal formation of a martensitic phase is also compatible with the reaction-pathw escription of the transformation. The purpose of this investigation is to examine the isothermal mode of the martensitic reaction, both theoretically and experimentally, in order to test the likelihood of the above two mechanisms. Material and Methods The alloy used in this study contained about 71 pct Fe and 29 pct Ni. The complete analysis was 29.5 ± 0.2 pct Ni, 0.036 pct C, 0.02 pct N, 0.19 pct Mn, 0.09 pct Si, 0.008 pct P, and 0.006 pct S. The amount of isothermal transformation was determined by electrical resistance measurements using a Kelvin double bridge. The specimens were in the form of rods 1/16 in. diam x 4 in. long. Aus-tenitizing was performed at 1095°C for % hr either in a pre-purified nitrogen atmosphere or in an evacuated Vycor tube, followed by oil quenching to room temperature. After this treatment, the samples were completely austenitic, and the transformation studies were conducted at subatmospheric tempera- tures. Lineal analysis and X-ray determinations of retained austenite were used to calibrate the electrical resistance changes in terms of the percentage of martensite. The martensite range curve for this alloy is given in Fig. 9 of ref. 6. The M, temperature occurs at about -18°C (255°K). Reaction-Path Theory The nucleation and growth description of the martensitic transformation that occurs isothermally has already been given by Kurdjumow.','2 However, no comparable treatment exists using the reaction-path concept." Consequently this section presents the reaction-path description of the isothermal mode of the martensitic transformation. According to the latter theory, there is a reaction path (a strain) which describes the relative motion of the atoms during their transference from the austenitic to the martensitic state. The possibility exists, therefore, that the nucleation of a martensitic plate is accomplished by an embryo that comprises a state intermediate between that of austenite and martensite. This state may be attained within a finite volume by means of a homogeneous strain of the austenitic matrix. There is a free-energy barrier (F.) along the reaction path, corresponding to a critical strain in a critical volume. When activation is achieved, a spontaneous increase in strain and volume of the embryo takes place to generate the full-size martensitic plate. This mode of nucleation is to be distinguished from the more conventional mode involving embryos of the martensitic phase that merely grow in size by an interface motion. There are two ways whereby embryos in the austenitic phase can achieve the critical state of strain for isothermal nucleation: 1—through the formation of internal strains by plastic deformation or by stress; and 2—through thermal fluctuations, preferably superimposed upon existing internal strains. The activation free energy F,, must be supplied either mechanically by internal strains or thermally by energy fluctuations, or by a combination of both.

Jan 1, 1953

By R. E. Collins

The existence of fluid migration across fixed boundaries in oil and gas reservoirs has been known for many years. Several techniques have been developed in the past for estimating The rate of migration across fixed boundaries as an aid in planninng field development and in the valuation of oilfied properties. The principal de/errc7nt to the use of these techniques lies in the rather extensive reservoir and field data required for ca1cula1ion.s of fluid migration. For this reason, a new, simplified procedure has been developed which makes possible the calculation of fluid migration with a minimum of field and resrvoir data. This new technique is based on certain. solutions of the differential equations describing flour in the reservoir which assume, for the portion of the reservoir of interest, that the formation can be approximated by a homogeneous rock of uniforrn thickness, that only a Single mobile fluid phase exists, and {hut fluid production at the well is solely a result of expun.rioti of rile resersoir fluds. The results of the, present work are compiled in a set of curves. These curves can he used to calculate both rule and cummulative fluid migration when the abovc assumptions ore ju.r/ifiril. The only data required for such calcu1ations are the production hisrories of all wells in the field, the permeability and porosity of the reservoir., the, compressibility and viscosity of the fluid. and the shape of the reservoir, INTRODUCTION The migration of fluids across fixed boundaries in oil and gas reservoirs has long been recognized as an engineering and economic problem, but no methods for estimating the extent of migration during the development stage of a reservoir have been published. The investigation reported here has been directed toward providing a simple technique for estimating the extent of such migration and has therefore been restricted to the simple case of a homogeneous reservoir of uniform thickncss containing compressible liquids. It is assumed that only a single mobile fluid phase exists and that fluid production at the wells is solely by expansion of the reservoir fluids. Obviously, few, if any. reservoirs conform to these assumptions during their entire productive life. On the other hand, most reservoirs approximate fluid expansion reservoirs during their initial stages of primary production. Consequently, the present work should be applicable during the field development of most reservoirs, regardless of whether or not they ultimately are gas cap, dissolved-gas, or water-drive reservoirs. The mathematical analysis of this problem has been outlined in the Appendix, while the results of the investigation are presented in the following discussion. DISCUSSION OF CALCULATION PROCEDURE SLNGLE Well, Ini-iimite Reservoir The procedure for calculating fluid migrations is based on solutions of the partial differentia1 equations describing the flow of a homogeneous compressible liquid in a homogeneous reservoir of uniform thickness. This differential equation has the form of the well-known diffusion equation. The equation, as applicable to our problem, is where p is fluid density, is porosity, EL is viscosity, c is compressibility,* and k is permeability; .r, y and t are the space coordinates and time. Derivation of this equation is given in the Appendix. The analytical solution of this equation for a single well of negligible radius producing at a constant rate. q, from a reservoir of infinite areal extent for a time, 1. can he readily obtained. From this solution the rate of flow and also the cumulative flow across a straight line segment of length, 1, at a perpendicular distance. 6. from the well can be computed. One end of the line must be on the perpendicular joining the well to the

By A. J. Griest, A. P. Young, P. D. Frost

A study was made of the effect of ß grain size on the tensile ductility of a-ß titanium alloys haet treated to strengths in the range 165,000 to 180,000 psi. It was concluded that the primary cause of $ embrittlement is the large grain size which is obtained so rapidly in many a-ß titanium alloys when heated into the ß field. It was also found that grain-boundary a and acicular intragranular a in the microstructure are not necessarily detrimental to the tensile ductility if the prior ß grain size is sufficientlv fine. BETA embrittlement occurs in a-ß alloys when the finish hot-working or stages of the subsequent heat treatment have been done at temperatures in the ß field. In order to avoid this embrittlement, for-gings must be finished at temperatures under the ß transus. For better workability, it would be desirable to forge at temperatures in the ß field. For this reason, research has been conducted to determine the cause of ß embrittlement. Although ß grain size has been considered as a possible contributing factor to ß embrittlement, only limited research has been done to evaluate its effect. The effect of addition elements on ß grain growth in unalloyed titanium has been studied by Liu.' Complete mechanical property data, however, were not obtained for correlation with grain size. Ogden and coworkers2 have investigated the effect of both a and ß grain size and grain shape in Ti-Cr-Mo alloys. Their data indicated that tensile ductility was relatively insensitive to ß grain size at annealed strength levels (140,000 psi ultimate). No study has apparently been made to determine the relationship between ß grain size and ß embrittlement in a-ß alloys heat treated to high strength (180,000 psi ultimate). The high-strength condition is that in which ß embrittlement is particularly severe. Beta grain size is not easily varied through the use of a range of annealing times and temperatures in the ß field, because of the rapidity with which ß grain growth occurs. Short-time heating techniques are needed to obtain the smallest ß grains. EXPERIMENTAL PROCEDURE In this research, the experimental procedure was as follows: 1) Tensile and microimpact specimen blanks were resistance heated to produce a range of ß grain sizes. 2) The tensile and microimpact blanks were then solution-treated in the a-ß field and aged to produce predetermined ultimate tensile strengths in the range 165,000 to 180,000 psi. Tensile and impact ductility were then correlated with a grain size for constant strength levels. Materials—The alloys Ti-6A1-4V, Ti-4A1-4Mn, and Ti-16V-2.5Al are representative of the heat-treatable a-ß types in which ß embrittlement can be severe. The compositions and ß transi of the heats studied are given in Table I. The Ti-16V-2.5Al heat was melted and fabricated to 1/4 in. round at Battelle; the other alloys were obtained as 1/4 in. round rolled from commercial heats. The micro-structures of the as-rolled alloys were fine a-ß mixtures. This structure is typical of titanium alloys hot-worked extensively in the a-ß field. Resistance-Heating Treatments to Establish ß Grain Size—For direit resistance heating, a 1/4-in.-diam s~ecimen was heated with a 3000-watt transformer rated for 1000 amp with adjustable secondary voltage. The apparatus included a spray quench fixture. Both heating and quenching periods could be automatically controlled. For temperature measurements, 28-gage Chromel-Alumel wires were tack-welded to the specimen at its midpoint. A high-speed recorder-controller was used to control the heating cycle.

Jan 1, 1960

By R. B. Adair, J. S. Browning

The laboratory batch and continuous flotation pilot plant tests demonstrated the technical feasibility of recovering high grade mica concentrates from weathered mica pegmatite ores of Alabama and Georgia. The research indicated that combinations of anionic and cationic collectors may be used effectively for flotation of fine size mica from weathered pegmatite ores. In continuous tests, concentrates containing 98.5% mica were obtained from the Georgia pegmatite ore; the Alabama pegmatite ore concentrates contained 98.4% mica. The recoveries were 91 and 89% respectively. INTRODUCTION The principal uses of fine ground mica are as a filler in wallboard joint cement, as a filler and surface coating for roofing, as an ingredient in paints, and in oil well drilling mud. The mineral has other uses in the manufacture of rubber, wallpaper, plastics, welding rods, electric insulation, house insulation, and textiles, and as an annealing agent in metal treatment. In recent years, more than 99% of the domestic mica produced has been scrap and flake mica (mica which does not meet specifications for sheet mica and is used for producing fine ground mica). There has been a continued increase in mica production for several years, the 1963 production of scrap and flake mica totaling 117,251 tons.1 Ground mica is obtained primarily by crushing and milling pegmatites and schists. To a lesser extent, mica is produced as a byproduct of kaolin washing and feldspar and spodumene flotation operations. The processes used in recovering mica by crushing and milling pegmatites are generally simple, consisting of various combinations of alternate roll crushers and trommel screens that separate the mica and gangue at screen sizes coarser than 6-mesh. As these processes are designed to recover only coarse mica, high losses in the plant rejects are common. Large tonnages of tailings from the crushing and screening plants have been accumulated in a number of areas. Methods for treating such products were developed by the Bureau of Mines in 1941,2 but have not been generally applied. More recently, mica flotation research has been completed and published by the Bureau of Mines.3 These methods required complete removal of 150- to 200-mesh materials from the flotation feed with consequent fine mica losses. Later, the Bureau of. Mines investigated methods for-recovering fine size mica from pegmatite ores after desliming sufficiently to remove clay materials, but not so drastically as to remove the fine sands. This report summarizes the results of these studies. The process developed was effective on pegmatite ores from two locations and should be applicable to the commercial treatment of other mica-bearing pegmatite ores and fine rejects that have been accumulated at various mica-milling operations. DESCRIPTION OF ORES The ores used in the investigation were obtained from the Dixie Mines, Inc., Heflin, Alabama, and the Ruberoid Corporation, Hartwell, Georgia. The sample from Alabama contained muscovite and quartz, with a high percentage of clay, and minor amounts of biotite, kaolin, limonite and tourmaline. The mica in the ore was essentially all minus 4-mesh in size and was free of attached mineral grains. The Georgia sample contained muscovite and quartz, with minor amounts of biotite, kaolin, and limonite. The mica in the ore, which was essentially all minus 4-mesh, was liberated. Petrographic analyses of the two samples are given in Table I. THE ANIONIC-CATIONIC MICA FLOTATION METHOD Previous investigators2,3 have reported that complete desliming of mica ores at 150- to 200-mesh was required prior to flotation with cationic collectors to obtain satisfactory selective separation of the mica from the other mineral components. Numerous tests were made at the Tuscaloosa Metallurgy Research Center to determine if some reagent combination could be used to selectively float finer size mica without complete desliming. The investigation led to development of a process using a simple reagent com-

Jan 1, 1967