Search Documents

By Wang Yun-yan

In order to examine the adaptability and the kinetics of leaching different gold ores in alkaline thiourea system, six kinds of gold concentrate and/or calcine with different physical and chemical properties were chosen as objects. The leaching behaviors in alkaline thiourea system with high stability, acidic thiourea system and alkaline cyanide system were compared. Changes of phase, surface appearance, particle distribution and specific surface area of six kinds of gold ores before and after leaching were studied in virtue of modern analytic techniques, e.g., XRD, SEM, and so on. The results indicate that alkaline thiourea solution can be used to leach gold ore, for oxidized gold concentrate removed arsenic by microbe pretreatment(4#) the leaching rate of gold is up to 82.68%, such conclusion overthrows the parlance reported that pH value must be less than 1.78, or gold can not dissolve in thiourea solution. Chemical components and phase are related to gold leaching rate, different gold ores are fit for different leaching system, and alkaline thiourea solution is suitable for the pretreated oxidized gold ores with low content of sulfur and in which the main phase was SiO2, phase almost does not change after leaching basically. Generally speaking, when leaching in alkaline thiourea solution, surfaces of gold ores with glaze change greatly to ones with coarseness, distinct trace and holes of corrosion. Particle size decrease and specific surface area increase of gold ores after leaching in alkaline thiourea solution with high stability except gold concentrate of Zhongyuan gold smelter(5#).

Jan 1, 2006

By Z. Smieszek, J. Botor, Z. Miczkowski, S. Sobierajski

"From 1978, the direct process for the smelting of chalcocite concentrates in a flash furnace by the Outokumpu method has been applied at the Glogów II copper smelter. The chemical composition of these concentrates make it necessary to control the process very strictly. In this paper, the method for controlling and measuring the main technological parameters of the copper production by flash smelting is being presented. It includes the determination of the chemical composition of the concentrate, its grain structure, the temperature of liquid products of the process, oxygen content in process gases, as well as lead concentration in copper and copper concentration in slag.The main process parameters are determined from the mass and energy balances. The relations between parameters, such as an effect of grain structure of a concentrate on oxygen and oil consumption, and dependence of chemical composition of a concentrate on capacity and products quality are discussed. 1. IntroductionThe Polish copper concentrates, as most concentrates occurring worldwide, contain from 18% to 30% Cu, and less sulphur (7-11%) and iron (2-5%). The main copper-bearing mineral contained in the concentrates is chalcocite, while bornite and chalcopyrite are present in smaller quantities. Moreover, the organic carbon (5-7.5%), arsenic (0.05-0.3%) and lead (1.2-3.0%) are also contained in the concentrates. The gangue consists mainly of silica, aluminosilicates, calcium carbonate and magnesium carbonate. Their proportions make the addition of slag-forming agents unnecessary.The composition of Polish concentrates, especially their low iron content, allows their application in the direct flash smelting process for blister copper production. Low sulphur content is the factor which determines the necessity of oxygen application in this process."

Jan 1, 1989

By Qinmeng Wang

The oxygen bottom blown copper smelting process is a new technology which has been widely applied to the copper production in China. In this work, a computational thermodynamics model for this technology has been established, based on smelting mechanism and theory of Gibbs free energy minimization. The calculated results from the model agree well with the actual industrial data, indicating that the model can be used for the predictions under different operating conditions. The tendencies of the key parameters (such as Cu losses and Fe3O4 content in slag) and the distribution ratios of the minor elements (such as Pb, Zn, As, Sb and Bi) can be predicted by adjusting the oxygen/ore ratio charged into the bottom blown copper smelting furnace. The model can be used to monitor and optimize the industrial operations of the oxygen bottom blown copper smelting process.

By Wen Chen, Xinghua Liu, Zeyou Peng, Qiulin Wang

"Limonite is a collective for iron hydroxide argillaceous materials. It is very difficult to be treated due to the wide variation in specific gravity and magnetism and the high argillization rate in the course of grinding and beneficiation. The iron ore in Huangmei, Hubei, China is the typical representative of limonite. If the limonite is processed using conventional physical beneficiation methods (e.g. magnetic separation, gravity separation, flocculation-desliming-flotation, or a combined process of the three), it can only be obtained an iron concentrate grade of 51.98% and an iron metal recovery of 86.64%. However, the technique of flash magnetic roasting-magnetic separation can improve the concentrate grade to 61.03%, iron recovery to 91.17%. This paper describes the tests of recovering limonite by flash magnetic roasting in detail.IntroductionLimonite (mFe2O3, nH2O)[1] is a general designation for hydrous iron hydroxides and argillaceous matters. Limonite is hard to be separated because of its complicated geneses, comparatively weak magnetism, nonuniform grain size and being easily slimed during grinding. So most small and medium enterprises sell deslimed limonite product which was dealt with just by simple methods of washing, magnetic separation or gravity separation and so on. In recent years with the iron ore prices soaring, significant progress was made in mineral processing research of limonite. Laboratory research and industrial test results showed that flocculation-desliming-flotation process and roasting-magnetic separation process are the two best methods to recover limonite till now. To compare these two methods, roasting-magnetic separation process is superior to flocculation-desliming-flotation process in aspects of beneficiation indexes and industrial stability."

Jan 1, 2012

By Atsushi Shibayama

The aim of this research was to develop a copper recovery process from mine tailings (0.34%Cu) using flotation followed by high-pressure oxidative leaching (HPOL) and solvent extraction. The results of HPOL using the concentrate of mine tailings obtained by flotation under the optimal conditions of the previous study shown that an efficient copper dissolution of 94.4% was achieved in an H2O media, while the copper concentration of PLS reached to be 2.9 g/L. The solvent extraction of PLS obtained from the optimal HPOL showed that 91.3% copper was recovered in stripped solution under the determined optimum conditions, in which the copper concentration achieved to be 44.8 g/L. Finally, a proposed copper recovery process from the concentrate of mine tailings was developed by combination of HPOL and solvent extraction, while a total copper recovery of 86% was achieved.

By Jordan Mayorga, Joseph Kopp, Robert Boehm, Daniel P. Cook

"Solar generated power has long been considered a useful energy source only for low-energy density and non-mission critical use, such as providing electricity for residential applications. The success of Concentrating Solar Power (CSP) facilities, such as the 64 MW Nevada Solar- 1 near Las Vegas, have demonstrated that solar does have application to high energy density industries such as materials and chemical production. This paper will discuss the current operating con_guration of the Solar-1 facility and show how proposed modi_cations, such as addition of thermal storage and use of liquid salts as the working uid, can further improve the e_ciency and energy production of the plant.IntroductionThe United States as a nation is the largest consumer of energy in the world at an estimated 29 trillion kWh per year[1], which is roughly 15% of total global energy consumption[2]. On a per capita basis, the United States also leads most of the world, using an average of 96,000 kWh per person[3]. Roughly 40% of the energy consumed in the United States was produced from petroleum, 23% from coal, 23% from natural gas, 9% from nuclear and the remaining 5% from renewable sources such as solar, geothermal, wind, and hydroelectric[1].Energy demands associated with the industrial-scale production of chemicals and materials is a signicant portion of the United States total energy consumption. Roughly 33% of the energy consumed in the United States is used by the industrial sector, with 22% of this amount used in chemical production, 16% used in petroleum rening, and 14% used in the smelting and rening of metals[1]. Energy costs are also a signicant, if not the most signicant, portion of the total production costs for many materials. For example, roughly 30% of the cost of producing aluminum is the electricity used in the Hall-Heroult process [4], while the cost of energy is roughly 15% of the total cost of producing steel products [5].The primary sources of power for the industrial sector have been coal, petroleum, hydro- electric and nuclear. The use of alternative energy sources, e.g. solar, wind, geothermal, for industrial materials production has been slow in coming because they are intermittent and low-energy density sources, i.e. no solar power at night, no wind power when the air is still, etc. The success of Concentrating Solar Power (CSP) facilities, such as the 64 MW Nevada Solar-1 (NS-1) near Las Vegas, have demonstrated that solar can have application to high energy density industries such as materials and chemical production.This paper will discuss the current conguration of the NS-1 facility, and potential modications to the facility that will increase both its power e_ciency and power density."

Jan 1, 2010

By Kun Wang, Weipeng Luan, Qingbo Yu, Qin Qin

The oxygen uncoupling property of the oxygen carrier is essential for the chemical looping gasification process. In this paper,the combined Cu-based oxygen carrier were prepared by mechanical mixing method. XRD and SEM were used to characterize the oxygen carrier prepared. TG experiments were performed in a thermal analyzer to investigate the oxygen uncoupling property. The XRD pattern of the fresh oxygen carriers showed that the phases of the oxygen carriers were stable.The active phase of oxygen carrier was CuMnO. With the increasing of x 3-x 4 heating rate, the starting and ending temperatures of the reduction reaction increased. However, the reaction time decreased and the reduction rate increased. With the increasing of oxygen concentration, the starting temperatures of the reduction reaction shifted to high level. Temperature had great effect on the reduction rate and the reduction rate increased with increasing of the reduction temperatures.

Mar 1, 2018

By Yuan Zeping

The distributions of impurities in the copper melt, the slag and the gas phase in copper flash smelting process were under study in the Guixi smelter, particularly during operating conditions of high oxygen enrichment with production of high grade matte. Several methods for the removal of impurities such as As, Sb and Bi in the copper smelting process were developed and implemented at the Guixi smelter. This paper described the effects of high oxygen enrichment, elevated matte grade, high temperature and high production rate on the distribution of impurities, methods adopted at the smelter for the removal of impurities, and the associated benefits in the utilization of these removal techniques which include the mathematical model for material blending, high thermal intensity operation at the flash furnace, extended converter blowing, and injection of slag modifiers consisting of Na2CO3 and CaO powder mixture to the converters and anode furnaces.

Jan 1, 1999

By Hector M. Lizama

A new technology, known as the HydroZinc? process, is described for the recovery of zinc from sulphide ores that includes heap leaching, neutralization, solvent extraction and electrowinning. Unit operations were scaled up from bench-scale to a 1-t/d zinc cathode demonstration plant. Bench-scale studies defined the process chemistry and a process flowsheet. Column tests were used to design full-scale heaps for zinc bioleaching, and mini-pilot equipment was used to design a solvent extraction circuit. The characteristics of the process required development of a bleed circuit for water and impurities. The complete integrated process was tested on a demonstration plant scale for two years, with about 10 000 t of zinc sulphide ore being bioleached in two 6-m-tall test heaps. In addition to 1 t/d of zinc cathode, iron hydroxide and gypsum residues were produced. The process also generated a small effluent bleed. Over the course of the two-year demonstration test, a number of technical hurdles were overcome and several improvements were made. Some of the more significant ones are presented along with process descriptions and experimental and demonstration plant data. Some engineering aspects and economic evaluations of the new process are also discussed.

Jan 1, 2003

By Baozhong Ma, Yonglu Zhang, Yongqiang Yang, Chengyan Wang, Yongqiang Chen

During the past decades, slurry electrolysis (SE) has been implemented commercially for the processing of bismuthinite and complex Pb-Cu bearing gold concentrates. Recently, SE was proven effective for the treatment of As-rich antimonic gold concentrates. Laboratory test results suggest over 98% of the antimony was extracted, while the extraction of arsenic and gold was less than 0.5%, and that of iron was less than 6%. Moreover, the cathode antimony contained over 98% antimony and less than 0.3% arsenic. Considering the disadvantages of traditional 3 kA slurry electrolysis baths, such as smaller electrode area, reduced capacity, and greater electrode deterioration, the authors have developed an innovative 12 kA slurry electrolysis bath equipped with mesh and fence type titanium alloy electrodes. Furthermore, the technique was successfully used within a pilot scale plant yielding results similar to those observed in the laboratory. The technique yielded ametallic antimony ingot of 99.9% purity after arsenic removal via the addition of Na2CO3.

Jan 1, 2014

By Wei Yu, Tiejun Chun, Jian Pan, Deqing Zhu

In this paper, the technology of producing fluxed pellets by using hydrated lime as binder instead of bentonite was carried out. Green balls with 0.8% bentonite and others with 2% hydrated lime were obtained under the same conditions of 1.5% coke, 1.45 basicity and balling at 8.5% moisture for 13 min in disc pelletizer. The properties of two types green balls were as follows: drop numbers of 4.8 to 5.0 times/0.5m, compressive strength of 19.7 to 24.2 N/pellet and thermal shock temperature of 280 to 385?, respectively. Comparing with bentonite as binder, the compressive strength of fired pellets with hydrated lime is elevated by 13.8% and climbs up to 3113 N/pellet under the following conditions: preheating at 1050? for 10 min and firing at 1300? for 15 min. The hydrated lime also improves the metallurgical performance of fired pellets. The reduction index was enhanced from 68.6% to 70.6%, RDI+3.15 increased from 90.1% to 98.8% and reduction swelling index dropped from 22.4% to 7.4%, respectively. Therefore, hydrated lime can not only replace bentonite as binder to enhance the firing behaviors of green balls, but also effectively improve the metallurgical performance of fluxed pellets which can be used as high quality feed for blast furnace.

Jan 1, 2011

By Vinod K. Namilakonda

In situ synthesis of discontinuously reinforced aluminum alloy metal matrix composites was investigated. Aluminum alloy (A356: Al-7 wt% Si) was reinforced with dispersed AlN particles. Thermodynamic calculations were made for the composition determination of various phases formed during bubbling of NH3 gas into the Al alloy melts in the temperature range 1173-1473 K. Experiments were carried out for in situ production of AlN particles with the reaction between Al melt and NH3 gas in high temperature resistance furnace at 1473 K. The products were characterized using SEM, EDS and XRD. Effect of bubbling time of NH3 gas on the AlN formed in the composites was studied. The amount of AlN reinforcement in the Al alloy composites was observed to be in the range of 5 to 35 wt%. Good agreement was observed between the experimental and thermodynamic calculated data on the composition of AlN in Al alloy composites.

Jan 1, 2006

By Liangying Wen, Feng Xia, Chenguang Bai

"The situation of the Ti-V-Magnetite samples reduced with microwave has been investigated in laboratory. Firstly, the paper focuses on the heating behaviors of vanadium-titanium magnetite and characteristics of carbothermic reduction of V-Ti-magnetite in the microwave field. The effect of concentrate's size, quality on heating behaviors and reduction processes were researched. Results show that microwave heating may be a new heating resource replace of carbonic combustion reaction in reducing reaction. When the allocation of carbon is (16.7-30)%, carbothermic reduction of V-Ti-magnetite in the microwave field can proceed; with the increasing of carbon mixed, the metallization rate increases; and Fe, V can be reduced from their oxides in the microwave field; Titanic low oxide can be reduced from TiO2.1. IntroductionThe resource of Ti-V-Magnetite is abundant in the western area of Panzhihua in China, so far a mineral deposit of 4.64 billion tons have been proved up, it contains 14.75 million tons of V2O S which accounted for 87% of the vanadium and 5.93 hundred million tons of TiO2 accounted for 94% of the titanium resource respectively in China. The previous study proved that the major composition of mineral of the Ti-V-magnetite are Ti-magnetite, limonite, iron spinel, magnesium spinel etc, and the main elements of the Ti-V-magnetite in this area are Fe, Ti, V, Cr, Co, Ni, Ga, Sc etc[1] Due to the restrict of the BF-BOF process technical, during the smelting of the iron, the level of extracting the vanadium, titanium as well as other metal elements is limited. This results serious wasting of resources. To develop a new reduction process of Ti-V-magnetite is on the agenda, the microwave assistant reduction could meets this need, based on its characteristic of easy controlling of heating rate. To make use of the microwave energy to substitute the released heat sources of carbon combustion with air, use the solid phase state reduction at a relative lower temperature, make the beneficial element in Ti-V-magnetite transferred into the metal phase, then separated from the impurity. It is well worth to point out that once the microwave based reduction method has its industrial scale, it will take an outstanding position by its less release of carbon dioxide. This new environment-friendly process will play a vital role in the development of social industry and economy."

Jan 1, 2008

By Carla Lupi

In this work, nickel-cobalt electrodeposition under galvanostatic conditions was investigated. Ni-Co alloy was electrowon from an acid sulphate bath containing 40 g/L Ni and2-8 g/L Co.. The effect of electrolyte composition, current density, temperature, solution pH and presence of buffers such as H3BO3 and (NH4)2SO4 on Co content of the binary alloy has been investigated. In particular, current densities ranging from 180 to 400 A/m2 and temperatures ranging from 27 to 60°C were tested. The composition of Ni-Co alloys may be diversified through the selection of process parameters. The experiments show that the highest cobalt content of the alloy is reached by using a buffer free electrolyte without solution pH control. Though, in these conditions, the most homogeneous, fine and regular deposit morphology is obtained, energy requirements are the highest in tests lasting just two hours.

Jan 1, 2003

By Guojun Ma

The entrainment of charge materials, evaporation or volatilization of elements and ejection of slag and metal by spitting or the bursting of gas bubbles are mechanisms whereby stainless steel plant dust are generated from the electric arc furnace and refining converter. TCLP and ASTM D 3987-85 tests on dust that was collected from the baghouse filter system of a South African Stainless Steel plant showed that this dust can be considered hazardous according to South African legislation, due to the high degree of Cr (VI) leachability (~13mg/l for TCLP and ~8mg/l for ASTM vs. regulation threshold of 0.05mg/l in drinking water). The dust is therefore considered to be harmful to both the environment and human health, due to its high solubility in water and carcinogenic properties. It should therefore be treated before being stockpiled or land filled. This paper consequently describes an investigation into the formation of Cr(VI)-containing stainless steel plant dust and the stabilisation thereof in a sintering process, whereby the dust was mixed with a silica-rich clay. It is postulated that Cr(VI) form when the (Mg,Fe,Mn,Cr)3O4spinel phase, CaO, Ca(OH)2 and CaF2 (all of which are present in the dust) react. This reaction was found to take place both at ambient and at high temperatures (1100°C). Stabilization of Cr(VI) in the dust could be achieved at an optimum sintering temperature of 1100°C for a 50mass% dust : 50mass% clay mixture. Chromium emission during the sintering process was found to be low, and within environmental limits.

Jan 1, 2006

By Yuanbo Zhang, Daoyuan Zhang, Youlian Zhou, Guanghui Li, Tao Jiang

"Modified humic acid (MHA) has been developed by Central South University (CSU) and authorized in China. It has been reported that MHA is an effective binder for oxidized pellets prepared from specularite concentrates. In this research, effects of MHA binder on roasting behaviors of the specularite pellets are studied. MHA is an organic binder, containing much carbon, hydrogen, oxygen, etc. During the roasting, MHA can provide some heat because of combustion of hydrocarbon, which is beneficial for the recrystallization of Fe2O3 in the specularite pellets at high temperature. Simultaneously, part of hematite particles within the pellets are firstly reduced to magnetite, then, magnetite is oxidized into secondary hematite, which obviously improves the roasting performance of specularite pellets.IntroductionOxidized pellets have been widely used in steel production as a kind of high quality burden for blast furnace ironmaking [1]. In recent years, production of oxidized pellets is developing very fast. Therefore, the supply of high quality magnetite concentrates, which is the most suitable for pellet production, becomes scarce. It is imperative to pursue new alternative materials for oxidized pellet production [2]. Specularite concentrates have attracted widespread attention due to the advantages of high total Fe grade and low impurity content. However, due to the poor ballability and firing performance, specularite has not yet been widely applied into pellet production [3, 4]."

Jan 1, 2012

By Tao Li

The development of DP(Dual Phase) steels and TRIP(Transformation Induced Plasticity) steels has received much attention in recent years due to their high strength and simultaneous good ductility, which provides the potential for weight reduce and resource savings on certain components in automobile or other industries. So a controlled rolling process was simulated in the present study by thermomechanical simulator (Gleeble 1500) for producing DP steels on a kind of low carbon steel containing a small amount of Si and Cr. F+M dual phase microstructures have been obtained during continuous cooling processes of a wide cooling rate range from 10°C /s to 60°C /s. The grain size of the dual phase steel developed can be refined to less than 5 m through the mechanism of deformation induced ferrite (DIF) transformation. The ultrafine ferritic grains are equiaxed with high-angle boundary, and the martensite islands of an average size less than 5m disperse uniformly in the ferrite matrix. The ultrafine martensite islands not only inhibit the growth of ultrafine ferritic grains and improve the bonding of F/M interface, but also increase remarkably the strain hardening rate in the processing of the present Dual-Phase steel. As a result, the tensile strength of ultrafine grained Dual-Phase steel reaches higher than 1000 MPa. The result shows that an ultrafine grained Dual-Phase steel of low carbon and low alloy is promised to exhibit desired F+M microstructure by means of this new TMCP process.

Jan 1, 2006

By Alysson Tadeu Pereira Almeida

Steels with low concentrations of nitrogen, hydrogen and carbon have been in large demand lately. The RH process is a secondary refining process that can simultaneously attain significant levels of removal of these interstitial elements from liquid steel. In the RH process, the melt circulation rate plays a very important role in determining the productivity of the equipment, since it affects the decarburization rate. In the present work, a physical model of a RH degasser in a 1:5 scale of an industrial reactor has been built and used in the study of the circulation rate and of the kinetics of decarburization. The effects of the gas flow rate and of the configurations of the nozzles used in the injection of the gas have been analyzed. The decarburization reaction of liquid steel was simulated using a reaction involving CO2 and caustic solutions. The concentration of CO2 in the solution was evaluated using pH measurements. The experimental results indicated that the kinetics of decarburization can be described by a first order equation. Based on the results, it was possible to determine the contributions of the decarburization in the upleg snorkel and in the vacuum vessel.

Jan 1, 2006

By Y. H. Liu

Several foaming aluminum samples of different density were prepared in a semi?industrial scale experimental system, Their properties such as the energy absorption characteristics, mechanical properties, heat conductivity and acoustical properties were measured. The results showed that the foaming aluminum with a density of 0.5 to 0.6 g/em3J has the best energy absorption and this makes it suitable as the ensuring bar of the automobiles and also as a cushion material for the engine. The foaming aluminum with a density of 0.25 to 0.4 g/em3 has the best acoustical properties and heat conductivity resistance, which is suitable for the door filling material, the ceiling and the partition or the car engine.

Jan 1, 2003

By Darryl Lovato, Ramiro Pereyra, Daniel S. Schwartz

"During an annual inventory of nuclear material, a plated steel container which contained plutonium oxide failed. The container had been packaged for temporary storage but had been overlooked and remained in storage for more than 23 years. Although it was determined that the failure occurred through the slip-top rim, a metallurgical evaluation was requested to help to determine the integrity of the container.Optical metallography and scanning electron microscopy were used to analyze the character and degree of corrosion in the container. The depth of corrosion, measured at approximately 10 µm, did not pose a threat to the integrity of the container. However, the corrosion morphology and chemistry did suggest that a galvanic cell had developed between the tin and steel from the condensation of water. The morphology also suggests that the attack of the steel took place over a series of cycles due to changes of the environment.IntroductionMetallographic analysis was requested as part of the investigation into the mechanism of the failure of a slip-top container (#38621) containing plutonium oxide (PuO2) powder. The container had leaked during a special nuclear material (SNM) annual inventory causing contamination and closure of the vault. A photograph of the container and interior container is shown on the right in Figure 1. An initial investigation established that the source of contamination was the consequence of the failure of multiple layers of containment. Initially by the deterioration of the interior plastic bottle and polyvinyl chloride (PVC) bagout bag, and finally through the lid and steel container interface at a location where tape had not adhered properly [1]. Although the source of the breach was established, it was determined that metallographic analysis was important to establish the extent of deterioration of the steel container."

Jan 1, 2008