Cobalt is recovered from square type of spent lithium ion batteries (LIBs) containing 5~20 % Co, 5~7 % Li, 5~10 % Ni, 15% organic chemicals, and 7% plastics together with Cu, Al, Fe, and Mn. The waste LIB was prepared by physical treatment. After screening, the crushed LIBs were separated to +8 mesh, -8/+16 mesh, and -16 mesh powder. Among these, -16 mesh powder was selected for leaching. The leaching test was investigated at 2 M H2SO4, 6 vol.% H2O2, reaction temperature 60 ?, agitation speed 300 rpm, solid/liquid ratio 50 g/ 500 ml, reaction time 1 h. The leaching efficiency of cobalt was more than 99 % and its concentration was 24.9 g/L. For removing of impurities such as copper, iron, and aluminum in the leaching solution before cobalt solvent extraction, the impurities were eliminated by pH control with alkali solution. For selective extraction of cobalt, the aqueous phase removed impurities was equilibrated with different volumes of 0.4 M Cyanex 272 saponified of 50 %. Extraction efficiency of cobalt was about 80 % at first step. Separation coefficient (ßCo/Li) of cobalt and lithium extractions was 206.5. Over 9.0 % of pure cobalt sulfate solution was obtained after stripping with H2SO4 solution.

Jan 1, 2008

By Zengjie Wang

Kinetic study of hydrochloric acid leaching of Panzhihua ilmenite from China is presented. Both temperature and concentration of hydrochloric acid have significant effects on the rate process of Fe dissolution from ilmenite ore, while the ratio of liquid to solid has little effect on the Fe dissolution. The Fe dissolution is found to follow the spherical model f (??) =1-(1- ??)1/3 and the apparent activation energy is calculated as 47.21 KJ/mol, suggesting a chemical reaction controlled mechanism. The dissolving behaviors vary at different kinetic stages. At the beginning the amount of the dissolved Fe and Ti increased monotonically with leaching time, while about 15 minutes later the dissolved Ti in the form of TiOCl2 began hydrolyzed into TiO2 fines reunited on the ilmenite ore surface, as observed by SEM and EDS technique. For the unreacted ilmenite particles covered by a layer of hydrolyzed TiO2, the leaching seemed to be as a selective leaching of iron and because Ti dissolved from and hydrolyzed rapidly again into the unreacted ilmenite particles. The leaching process can be ended 4 hour later when almost of Fe has dissolved into the solution and TiO2 remains as solid residues. The effects of acid concentration and leaching temperature were also investigated.

Jan 1, 2009

By Dong Liang, Honggang Zhong, Zhenxing Yin, Qijie Zhai

"2507 super duplex stainless steel (SDSS) has been widely applied in a marine environment, attributing to its excellent pitting corrosion resistance and mechanical properties which are particularly determined by the nitrogen precipitation behaviors and volume fraction of ferrite. In this paper, various cooling rates were obtained by applying four different moulds with the common gating system. By which the influence of cooling rates on nitrogen precipitation behaviors and the ferrite fraction in cast 2507 SDSS was comparatively investigated. The results showed that nitrogen porosity could easily precipitate in cast 2507 SDSS under standard atmospheric pressure. The number of nitrogen holes increased with decreasing the cooling rates, and the holes mainly distributed in three zones, i.e. the interface between the horizontal and vertical columnar grains, top vertical columnar grains and the final solidification region. Additionally, higher ferrite fraction was obtained with lower cooling rates.IntroductionDuplex stainless steels (DSS) have a dual-phase microstructure consisting of ferrite (d) and aus-tenite (?). Due to the combined advantageous properties of d and ? phase, their application rapid-ly increased in industry [1, 2]. Super duplex Stainless Steel (SDSS) is the third generation of du-plex stainless steels, of which the alloy elements Cr, Ni and N content are higher than the stand-ard 2205 DSS. Because it has high contents of alloy elements, the SDSS has better mechanical properties, and its pitting resistance equivalent number (PREN) reached a point 43. Hence SDSS has been used in petroleum chemical industry, the marine equipment and harsh corrosion environments [3]. SDSS contains ferrite stabilizing elements, such as Cr, Mo and Si, and austenite stabilizing elements like Ni, Mn and N [4]. Many researchers have studied the effects of these elements on the stabilization of d and ? phase and the ratio of the two phases. High nitrogen con-tent is another prominent feature of SDSS. Nitrogen addition to SDSS is very effective for improving its mechanical properties [5] and corrosion resistance [6], such as pitting resistance in NOx environment. To increase the nitrogen content in steels, a lot of work had been done. N. Nakamura and S. Takaki [7] examined the behavior of nitrogen absorption in Fe-23Cr alloy powder by sintering in nitrogen gas atmosphere, they found nitrogen content easily up to 1.0 wt. %. Using devised NH3 gas injection system, W. Park et al. [8] successfully produced austenitic Fe–23.5Cr alloys containing over 3 wt. % of nitrogen. Further-more, W.P. Tong et al. [9] stated that nitrogen percent was extraordinary high (about 10 wt. %) in pure iron plate. However, the above methods are difficult to be applied to large-scale industrial production."

Jan 1, 2012

By Manfred K. Walther

"Tests were conducted on instrumented plates cast in the Abex Experimental Foundry to compare recorded solidification histories with results computed for corresponding models simulated with the C.A.S.T. program. The first plate was cast of low alloy steel and the second of carbon steel with a graphite chill at one end. Both were cast in molds of bonded silica sand. Temperature histories were recorded in the castings, molds and chill. Exceptionally good agreement was achieved between computed and experimental data. Other investigators will find the results useful as a benchmark against which they can compare the results of their own calculations.IntroductionSince the early 1970's our foundry engineers have used both two- and three-dimensional versions of the G.A.S.T. program to gain knowledge of the solidification process [1,2,3]. Study of the computed data gave insight as to how the rigging and risering of specific castings might be changed or adjusted to improve quality and yield. New schemes based on such analyses were then recommended for implementation on the foundry floor. The degree of success of the new practice was subsequently evaluated after the part had been poured, shaken out and examined. Similar conditions were noted in the sectioned castings whenever porosity and voids had been predicted by the computations. Appropriate modifications, when found successful in the model, were applied to the process. This led to a reduction, if not complete elimination, of the defects. Such results gave credence to the use of these programs as an aid in the production of better castings.Earlier investigations on simple shapes revealed excellent correlation between output derived with the G.A.S.T. program and exact solutions. Results also compared favorably with data calculated using other codes as reported in the literature [4] and summarized in the Appendix. However, since the computer program had not been verified by direct experiment, it was decided to run instrumented tests to check the theoretical predictions with actual measurements."

Jan 1, 1986

By W. K. Tolley

The Bureau of Mines is investigating hydrometallurgical processing techniques to recycle metals from semiconductors and other advanced materials. Cadmium and tellurium were recovered from CdTe scrap produced in the manufacture of infrared optic devices. Sulfation, ferric chloride leaching, and oxygen-pressure leaching have been tested. Cadmium dissolution was achieved using oxygen-pressure leaching in dilute sulfuric acid. However, no satisfactory scheme for dissolution of the higher valued tellurium has been devised. Leaching the ground CdTe for 75 min at 110°C in 1.1M H2S0, under 120 psig 0, yielded 99.5% Cd extraction. Tellurium remained in the leach residue as TeO, and elemental tellurium; residual cadmium was less than 0.5%. The cadmium in the leach liquor was purified of coextracted metals such as gallium and iron by adjusting the pH. The cadmium was recovered as cadmium sulfate crystals by evaporating the solution. Recovery of by product metals, notably gallium, is possible.

Jan 1, 1991

By E. Açma

In this study, the production of Cu, Co, and magnetic iron oxide from the ancient copper, slags, located in Küre-Turkey, is investigated. In the process under development, fayalitic slags containing 1% Cu, 0.43% Co are reduced in a D.C. arc furnace with coke or graphite additions. A metallic alloy, consisting of 3.8% Cu, 3.3% Co, 2.1% S, and the rest being Ice, is produced by granulation of the liquid metal. About 85% recoveries of Cu and C:o are achieved by hot sulfuric acid leaching of these granules followed by H2S precipitation. The, production of magnetic iron oxide is possible from the discarded leach solution, loaded v:ith FeS04, by using a method with geothite precipitation, dehydration, controlled reduction, and re-oxidation steps. The magnetic oxides produced have 20 m2Jg surface area, 1:8.3 aspect ratio, and the coercivity of 330-380 Oersted.

Jan 1, 1993

By Ann M. Hagni

Reflected Light Microscopy (RLM) And Scanning Electron Microscopic-Energy Dispersive Spectroscopic Analysis (SEM-EDS) Study Of Electric Arc Furnace (EAF) Dusts Have Shown That Their Mineralogy Is Complex And Varied. The Particles Are Largely Spherical, And Can Be Seen In RLM Sections To Be Composed Of Franklinite, And Zincite, But They Show Significant Solid Solution With Each Other And May Contain Small Amounts Of Chromium. These Crystalline Phases Occur As Crystals And Skeletal Growths Within Ca-Fe-Si Glass. Because Chlorine Is A Deleterious Constituent In Recovered Zinc Products From EAF Dusts, Special Attention Has Been Given To Chlorine-Bearing Phases, And They Include Hydrophylite (Cacl2), Lime (Cao), And Organic Phases. Pyrohydrolysis-Treated EAF Dusts With Silica (Si02), Tungstite (W03), Alumina (A1203), And Bunsenite (Nio) Additives Contain Franklinite, Scheelite (Cawo4), Willemite (Zn2SiO4), And Hematite (Fe2O3)

Jan 1, 1992

By Senlin Cui, In-ho Jung

Significant amount of commercial aircrafts will be retired in 2020, and the recycling of Al components in such aircrafts becomes an important issue in aerospace and Al industry. Recycling of Al from obsoleted Al products can effectively reduce the energy consumption and CO2 emission which is more economical and ecofriendly. In the present study, thermodynamic analysis for the various recycling technologies of Al alloys were performed based on the comprehensive and accurate thermodynamic database. The recycling technologies reviewed in this work include the vaporization process to reduce Zn, precipitation process to reduce Fe, Mn, Si, Ti, Zr, flux treatment for Al 2O3 and MgO, etc. Several key issues and limitation of the recycling of the aircraft Al were discussed. The recycling technologies discussed can also be utilized to recycle other Al alloys for common usage. All the thermodynamic calculations were performed using the FactSage FTlite database.

Mar 1, 2017

By Georges J. Kipouros

Anhydrous neodymium trichlorids (NdCl3), containing ~1 weight percent neodymium oxychloride (NdOCI) was prepared by the dehydration of neodymium trichioride hexahydrate (NdC13.6H2O). Dehydration of the hexahydrate was conducted in three steps. First, the hexahydrate was slowly heated in air to about 250 °C until all the low temperature water of crystallization was removed. In the second stop, the neodymium hydroxychloride (Nd(OH)2C1) fanned in the first step was decomposed by heating under argon to 430 ° C. Finally the salt was ground and then treated with HCl gas at 330 °C until practically all of the NdOCl was converted to NdCl3.

Jan 1, 1992

By Peter Fischer

A demonstration plant for QSL technology with a continuous through-put of up to 10 t/h concentrate has been in operation at the Berzelius smelter, Duisburg, Germany since early 1981. In the QSL-process, both oxidation and reduction steps are performed in a single horizontal long cylindrical reactor. In the present demo-reacior, 2.5 M diameter by 22 M long, these steps are separated by a low partition wall with an underflow opening, to prevent backmixing of slag. -Tests on a variety of concentrates, including high-lead Missouri-type material and lower grades, have shown recoveries and consumables indicating very attractive economics. Investment cost estimates further enhance the economic attractiveness. Environmental protection afforded by the QSL system is a major advantage. The process has proven its reliability and versatility and is now ready for commercialization. Continued test work, including smelting secondary lead materials, is planned.

Jan 1, 1983

By Baohua Li, Yanhui Liu, Shengping Li, Xuewei Lv, Yun Chen

There are almost ten billion tons of vanadium-bearing titanomagnetite in Panzhihua-Xichang area. However, iron ores in Hongge, which has the most abundant reserves in the four mine areas in Panzhihua, have not been utilized sufficiently so far. The reason behind this is the relatively high Cr2O3 in the ores (0.49 %~0.82 %), that due to its high melting temperature will negatively influence the blast furnace reduction and slagging process. Therefore, in the blast furnace process, Cr is hope to be reduced into molten iron, which can reduce slag viscosity problems. Slag iron reduction experiments were conducted to quantify the Cr reduction. Experimental results shows that with the increase of TiO2, the content of Cr in the hot metal is decreased when balanced. And during the initial stage of the reduction reaction, the reaction kinetic model is a first-order reaction.

Jan 1, 2016

By Junmo Ahn

This study investigated leaching kinetics by alternative lixiviants for copper leaching from chalcopyrite (CuFeS2), the most abundant copper resource in the world. As a refractory sulfide mineral, chalcopyrite shows low copper extraction due to passivation on chalcopyrite surface. Also, decrease of copper grade with high portion chalcopyrite requires the alternative leaching procedure to increase copper recovery. Therefore, alternative lixiviants such as sulfurous acid and methanesulfonic acid (MSA) were tested for both concentrate and low grade ore to enhance copper extraction. Also, an oxidant, hydrogen peroxide, was compared to ferric to find out the improvement of leaching kinetic. In concentrate leaching tests, 30 g/L MSA showed the highest copper extraction (47%), compared to other lixiviants at 75 °C. Periodical H2O2 addition enhanced copper extraction, and above 90% of copper extraction was observed within 96 h by periodical addition of 0.6% H2O2 at 75 °C. The activation energy of chalcopyrite leaching by MSA and H2O2 achieved 40 kJ/mol, which is chemical reaction control. The results of low grade ore leaching tests indicates that no significant difference among lixiviants (H2SO4, H2SO3 and MSA) with ferric was observed, all of which achieved around 37% within 24 h at room temperature. However, significant increase of copper extraction (>80%) was observed at both 20 g/L MSA and 10 g/L H2SO4 conditions by the addition of 10% H2O2.

By Musa Karakus

In an attempt to explain the phenomena of lead entrainment during Cu drossing of lead bullion, two different synthetic lead bullions were heated to 1050°C, cooled slowly to various temperatures, and then quenched. The morphology and composition of dross particles that form when Mn is used to desulphurize bullion also were examined. Polished sections of these pyrometallurgical products were examined by process mineralogical techniques to identify the impurity phases, determine their chemical compositions, examine the morphology of the impurity phases and evaluate the potential for lead entrainment in such crystals, and characterize pre-quench and quench-generated phases. The phases crystallized were metallic lead, metallic copper, galena, chalcocite, albandite, Cu14.4Pb2S9. and 5.5Pb2S3.5. Metallic copper formed isometric skeletal crystals, chalcocite formed platy and skeletal crystals, and 1formed crystals and eutectic intergrowth with chalcocite and Cu14.4Pb2S9 or Cu5.5Ph2S3.5. The pre-quench crystals are larger and usually exhibit skeletal forms; the quench-generated phases are only a few micrometers across and disseminated throughout the lead matrix. Skeletal crystals of metallic copper and chalcocite form three dimensional networks that entrain large amounts of metallic lead.

Jan 1, 1989

By D. C. Azubike

Wolframite (FeWO4) usually having cassiterite (SnO2) as a major impurity is a primary source of tungsten. Its direct reduction/carburisation with carbon in the temperature range 1000-1400°C, and with hydrogen at 600-900°C followed by carburisation with CO at 900°C are described. Depending on the conditions and reactants employed, Fe, Fe2W, B-Sn,WC, W2C, Fe3W3C and Fe6W6C are the products. Tin was found to inhibit the overall reduction and carburisation reactions significantly. The potential for either efficient separation of iron and tungsten or a one-stage production of an iron-based metal carbide composite is discussed.

Jan 1, 1992

By Shan He, Qiang Wang, Xuling Chen, Min Gan, Lishun Yuan, Xiaohui Fan

"The sintering properties of vanadium-titanium magnetite concentrate(VTC) was studied in this paper. Through the optimizing the sintering process of VTC, the suitable granulation moisture and coke proportion were determined. The sintering velocity decreased from 23.05 mm/min to 18.22 mm/min. With the increase of VTC proportion from 0 to 46%, the specific productivity and tumbler index were respectively decreased from 1.55 t/(m2·h) to 1.21 t/(m2·h), and 62.93% to 57.73%. The temperature of liquid phase formations of mixtures increased, the amount of liquid lowered, and the content and sharp of sintering mineral gradually changed with the increase of VTC ,these lead that sinter quality became worse.IntroductionIn recent years, the steel industry of China is developing rapidly. And the steel production was 627 million tons in 2010. At present, the resources of vanadium-titanium magnetite concentrate(VTC) was about 14.4% of the total national iron reserves of China[1]. VTC has been used as sintering material by Magang, Chenggang and Pangang. The amount of VTC in Pangang is maximum. However, there exist many problems in VTC sintering, which involve in high specific productivity, bad sintering tumbler strength and high energy consumption[2~5]. That’s why the proportion of VTC is limited in sintering.The high quality of iron ore resources is worse in China. Therefore, it’s necessary to study the properties of VTC sintering, and to find out the reason how the VTC ratio affect the sinter performance. Purpose and significance of the research is to get high-quality sinter with the proportion of VTC greatly raised."

Jan 1, 2012

By Yuanbo Zhang, Ruijun Wang, Qian Li, Zhao Jing, Guanghui Li, Zhengwei Yu, Chen Liu

The high content of sodium and potassium in sinter is harmful for blast furnace ironmaking. Reductive sintering technology can remove more alkali metals than conventional sintering process. In order to improve the removal ratios of Na and K, reductive sintering with both CO-containing flue gas circulation and carbon-bearing pellet was conducted in this study. Experimental results show that all indexes except the VSV and P were improved in reductive sintering with CO circulation. Flue gas circulation technique combined with carbon-bearing pellets were beneficial to reductive sintering, because it could maintain good sintering indexes and enhance the removal of Na, K. The best removal ratios of Na, K and reduction degree of iron oxides were 20.37%, 63.73% and 23.76%. In reductive finished sinter, silicate mineral becomes the important binder phase, and main iron mineral phases are wustite (FexO) and magnetite (Fe3O4).

Jan 1, 2016

By Hui-gang Wang, Mei Zhang, Min Guo

Metal-doped Ni–Zn ferrite with spinel structure was directly synthesized from treated zinc-containing electric arc furnace dust (Zn-containing EAFD) by solid state reaction method, realizing the transformation of Zn-containing EAFD from solid waste to high value-added material. A certain mass of NiCl26H2O was added to the treated Zn-containing EAFD before calcination. Then the effects of the mass ratio of treated Zn-containing EAFD to NiCl26H2O (RTZE/N, g g−1) and calcination temperature on the synthesis and magnetic properties of as-synthesized samples were systematically investigated by X-ray Diffraction, Raman Spectroscopy and Physical Property Measurement System. It is indicated that RTZE/N and calcination temperature had important influences on the synthesis of single-phase spinel ferrite and their magnetic properties. Pure metal-doped Ni–Zn ferrite, which exhibited good magnetic properties of higher saturation magnetization (Ms, 60.5 emu g−1) and lower coercivity (Hc, 49.8 Oe), was obtained when the calcination temperature was controlled at 1100 °C for 2 h with RTZE/N of 1:0.9.

Mar 1, 2017

By E. O. Ávila-Davila, F. R. Barrientos-Hernández, I. A. Lira -Hernández, Miguel Pérez-Labra, M. Reyes-Pérez, J. Antonio Romero-Serrano

Slag from smelting reduction processes were characterized by chemical analysis, XRD, SEM-EDS and XRF. The results revealed Ag concentrations of 362 g/t of slag, the slag mineralogical characterization by XRD and SEM-EDS showed mineralogical species oxidized complex containing Pb, Zn, Ca, Si, Fe, As, S in its structure, silver was found in globules associated lead in the slag and the furutobeite specie. The leaching study was conducted to evaluate process variables such as NaCN concentration: from 7.8x10-3M - 1.26x10-1M, temperature: 25-50°C, particle size: +140 mesh to -400 mesh, stirring speed of 750 rpm - 900 rpm. All studies were performed with a NaOH concentration of 0.2 M. The optimal values of silver recovery encountered in conditions of 7.8x10-3M NaCN, agitation rate of 750 rpm, temperature of 35°C and with a treatment time of 240 min. We also observed that a particle size -400 mesh will have optimum recoveries compared to +140 mesh, +200, +270 and +325.

Jan 1, 2015

By Wantae Kim

In order to establish the optimized recovery process for heavy minerals from Korean beach sand, we investigated the several physical separation methods such as gravity and magnetic separation followed by mineralogical characterization. There was clear relationship between the particle size and heavy mineral content that heavy minerals were mostly concentrated in the particles below 100mesh. Gravity separation using the spiral and shaking table separators made it possible to concentrate heavy minerals by rejecting the light and coarse particles consist mainly of quartz and other non-valuable minerals. The high-intensity magnetic roll separator and subsequent induced magnetic separator were applied to fractionate magnetic particles according to their magnetic susceptibility. The content of TiO2 of high susceptible ilmenite-rich fraction was 43.98wt.% while those of ZrO2 of non-magnetic and magnetic residue were 6.78wt.% and 3.11wt.%, respectively.

Jan 1, 2006

By L. J. Lutz

The U.S. Bureau of Mines has developed an electrorefining process to recover Ni, Co, Cr, and other metals from mixed and contaminated superalloy scrap. The superalloy scrap is cleaned then directly electrodeposited as a Ni -Co deposit. The process recovers approximately 90 pct of the Ni-Co available from the scrap as a 99t pct pure Ni-Co alloy. During electrorefining the electrolyte undergoes a purification process which results in Cr and other refractory metals reporting to the purification residue. Operating data is given for a 3-L compartmented electrolytic cell. Techniques for the removal of Fe, Cr, and trace impurities from the recycled electrolyte are outlined. The economics of a facility producing 15 mt/d of a Ni-Co alloy are also discussed.