Search Documents

By Adele Garkida

Compacts of crushed waste window glass, fluorescent tubes, drinking glasses and laboratory glass wares were made at various proportions from 106 microns and minus 75 microns powders in combination with 5% bentonite as binder for each glass type, after several trials to determine compatibility of particle sizes. They were made using the uniaxial press at 10,000 psi and sintered at a temperature range of 700- 750oC. The results showed anisotropic shrinkage behavior for all the samples, exhibiting an axial shrinkage lower than the radial shrinkage. Sintered compact from waste drinking glass which comprised of 60% 106 microns and 40% minus 75 microns powders showed the least sintering shrinkage factor of 1.125, fused at 700oC and the highest shrinkage factor of 1.286 obtained at 750oC. This shrinkage behaviour connotes that sintering can be employed to utilize these waste glasses up to the maximum of 95% recycled glass content in ceramic tile production.

Jan 1, 2008

By Gavin K. W. Freeman

The efficient separation of cobalt from nickel is a fundamental objective in the refining of cobalt. Based on recent experience at the Corefco refinery in Fort Saskatchewan, the identification of a novel process for the selective precipitation of cobalt from aqueous ammonia leach liquors is described. The addition of calcium sulphate, CaSO4.2H2O (gypsum), to an aqueous solution containing cobalt(III) hexammine sulphate, [Co(NH3)6]2(SO4)3, will result in the precipitation of a sparingly soluble double salt having the stoichiometry, [Co(NH3)6]2(SO4)3.2CaSO4.xH2O, where x = 4 or 6. Leach residues, which may contain a significant quantity of cobalt associated with the cobalt calcium double salt, can be washed with process solutions that contain ammonium carbonate. After contact with ammonium carbonate, the cobalt is recovered into solution, while the calcium is re-precipitated as the insoluble carbonate. The simplicity of this elemental separation and its high selectivity for cobalt, as well as the demonstrated usefulness in improving cobalt recoveries, are the basis for the potential applications of this process.

Jan 1, 2003

By M. T. Baquera

A comparison of microstructures associated with W single-crystal ([001], [011], [111]) rods prior to deformation (as grown), and after quasi-static compression (at a strain rate of ~1/s) by transmission electron microscopy (TEM) shows several orders of magnitude difference in dislocation density. Dislocation substructures were not significantly different amongst the deformed sample orientations. In contrast, [001] W rods penetrated into steel targets, at impact velocities of ~1.3 km/s, exhibited heavy dislocation densities and dynamic recrystallization as very distinct microstructural regimes accommodating the penetration process. Twinning on {112} also occurred as a precursor to, or remnant of, these microstructures near the projectile head. These results suggest that deformation accommodating the extreme strains and strain rates associated with the penetration of a single-crystal rod into a metal target is not adequately represented by conventional deformation

Jan 1, 2006

By Feng Chen, Lirong Chen, Yufeng Guo, Wenjie Weng, Tao Jiang

"In this paper, the carbonthermal reduction behavior and the influencing factors of Panzhihua ilmenite under the condition of carbon-burdened were systematically investigated. The results show that the ilmenite forms into titanium nitride during the reduction process at 1200 °C under the condition of carbon-burdened. Carbon-burdened is beneficial to the reduction of iron oxide, but less favorable for the growth of iron grain.IntroductionThe titanium ferrous resources are very rich in Panzhihua-xichang area, accounting for about 38.85% of the world's proved reserves [1]. However, TiO2 grade of this kind of ilmenite is low and calcium magnesium content is high, it generally requires preconcentration to titanium-rich material—titanium slag or synthetic rutile.Chlorination process is an advanced method for production of titanium dioxide, which should takes high quality titanium-rich material with low content of calcium and magnesium as raw materials (the content of MgO and CaO are less than 1.0%). Ilmenite in Panxi area, however, contains high calcium and magnesium; it is not suitable as a raw material for chloride process. Methods of producing titanium-rich materials which have been applied in industry are electric smelting, various acid leaching and reduction rust [2-5]. There still exist some problems such as CaO and MgO removed not thoroughly, low resource utilization, high energy consumption and environmental pollution."

Jan 1, 2012

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By Kurt Westerlund

Three. years operating experience of the FLUXFLOW waste heat boiler (WHB) 20.000 nm /h at Boliden Ronnskar Sweden on a TBRC smelting palena (PbS). Operating experience from the Kivset flash WHB 11.900 nm /h at Samim, Porto Vesme, Sardinia, Italy. Conceptual features of the 93.600 nm3 /h FLUXFLOW (WHB) on the Isasmelt smelting in melt furnace for 180.000 t Cu/a at Mount Isa, Australia.

Jan 1, 1992

By Natalya. N. Ankusheva

The problems of ore-bearing palaevolcanic structures in folded belts are actual because of their high productivity in nonferrous, ferrous and noble metals ores. Now relationships of location and conditions of formation for sulfide-massive and gold-bearing deposits are investigated very well in Urals. But carboniferous sulfide-barite mineralization, for example the barite veins in Arcaimsky palaevolcano are?nt studied enough now [3-5]. The purpose of this research is the studying of mineralogy and thermobarogeochemistry of barite from the hydrothermal veins. It will allow to determine the conditions of its formation and to compare it to the similar mineralization of others ore types.

Jan 1, 2006

By N. Panagiotopoulos

A low-grade (1.06% Ni, 0.06% Co) hematitic type lateritic ore from Triada, Euboea Island, Greece, has been leached with sulfuric acid at atmospheric pressure for the extraction of the contained Ni and Co values. The effect of various parameters, including reaction time and leaching temperature, acid strength, pulp density, etc., on Ni, Co extraction and Fe dissolution was determined. By leaching at 95°C for 4h with a 3N sulfuric acid solution at 25% pulp density, Ni and Co extractions were 82 and 75% respectively, and Fe co-dissolution 28%, yielding a pregnant solution containing 2.7 g/l Ni, 0.16 g/l Co, and 33 g/l Fe. Overall acid consumption was 850 kg/t ore (or 100 kg/kg Nil. Preheating of the laterites at 600°C before leaching resulted in much faster leaching kinetics for Ni, but the final extraction and acid consumption remained unaffected; Fe extraction was not influenced. Three-stage counter-current leaching at 9S°C, using 2N acid strength at each stage and 35% pulp density, reduced acid consumption to 350 kg/t ore (41 kg/kg Nil, and yielded 81% Ni recovery. Percolation leaching of -10 mm laterite at ambient temperature with 3N acid for 7 days resulted in 58% Ni extraction.

Jan 1, 1988

Cuspidine (3CaO?2SiO2?CaF2) is one of the most important compounds crystallized in mold flux films during casting in the continuous casting process of steel. The primary crystallization field of cuspidine has been experimentally developed in the CaO-SiOrCaF2-SiF4 system. The cuspidine-NaF binary and cuspidine-CaF2-NaF ternary systems have been also experimentally determined to study effects of addition of NaF on the primary field of cuspidine. In order to discuss its thermodynamic stability the standard Gibbs energy of formation of cuspidine has been determined by an electromotive force method using CaF2 as solid electrolyte and a transpiration method as follows: The chemical potential diagram and constituent activities for the CaO-Si02-CaF2 system have been evaluated based on the obtained thermodynamic data.

Jan 1, 2003

By Huaming Yang

The vanadium-doped SnO2 nanoparticle was synthesized by the co-precipitation reaction and subsequent calcination from the vanadium(III) chloride and tin(IV) chloride. The crystal size, pore size distribution, micrograph and properties of the nanocrystalline powders were examined by differential thermal analysis (DTA), thermogravimetric analysis (TGA), X-ray diffraction (XRD), desorption isotherm (Barrett-Joyner-Halenda method) and transmission electron microscopy(TEM). Thermal treatment of the precipitate powder at 600°C led to the formation of V -SnO2 nanoparticle of -10mm in crystal size. Most of the pores in the nanoparticle are about 5~15nm in diameter. Effect of doped vanadium on the crystal size of the nanopartic1e was discussed.

Jan 1, 2003

By Habib Saridikmen

In this experimental study the effects of slag composition on the phosphide capacities of the slag as well as on the phosphorus distribution ratios between the slag and metal phases encountered in ferromanganese smelting have been determined at 1500°C under carbon monoxide atmosphere. The distribution results were employed to calculate the phosphide capacities of the SiO2-Al2O3-CaO-MgO-MnO slags in equilibrium with the Mn-Fe-Si-Csatd.metal phase. The classical gas-slag-metal equilibrium-quenching technique was employed using CO gas atmosphere and graphite crucibles to saturate the metal phase with respect to carbon. The phosphorus distribution ratio increased from 0.045 to 0.375 when the slag basicity increased from 0.72 to 1.39. As expected, the distribution ratio decreased from 0.375 to 0.105 when silica increased from 37 % to 45.8% in the slag phase. The phosphide capacity values were calculated by using the results of experiments. Empirical relationships were developed to express the phosphorus distribution ratios and phosphide capacities of the above slags.

Jan 1, 2006

By Geoffrey Brooks, Mehedi Bin Mohammad, M. Akbar Rhamdhani

Molten alkali nitrates are used commercially as thermal storage fluids (HTF) for solar thermal electricity generation. Their range of operation is limited by the thermal stability and this limits the energy (steam-Rankine cycle) efficiency of these processes. In this study, the effect of atmosphere on the thermal stability of nitrates was investigated using simultaneous thermal analysis techniques (STA). The use of oxygen (O2) as a blanket gas was found to delay the decomposition point of the ternary NaNO3–KNO3–LiNO3 (13.23–57.14–29.63 weight ratio) mixture by 55 °C. By which operating range will increase 65 °C more compared to the binary solar salt. Higher heating rates increased the decomposition point but had less effect on premelting and melting properties. Nitrogen monoxide, and O2 evolution after melting indicates concurrent reversible reactions. Similar phenomena were observed for single and binary nitrates. The eutectic melting point of ternary nitrate obtained from the STA agreed well with FactSage eutectic composition prediction.

Mar 1, 2017

By Naixiang Feng, Shaohu Tao, Zhihui Wang, Yuezhong Di

"A novel vacuum aluminothermic reduction lithium process was developed in present work which used lithium carbonate, alumina and calcium oxide as raw material. The process mainly contained three steps. The first step is that LiA102 clinker is prepared in ambient environment, then metal lithium is vacuum extracted from LiAl02 clinker with aluminum power as reducing agent, and the last step is that alumina is leached from the reduction residue with a mixture of sodium hydroxide and sodium carbonate. The results show that the lithium reduction ratio can be over 95% under the conditions of reduction temperature 1423K, reduction time 3h, and aluminum excess 20%. The main components of reduction residue are CaO· Al203 and 12Ca0·7Alz03. The alumina leaching rate of calcium aluminate in residue is over 80%. High-whiteness aluminum hydroxide can be obtained by carbonation precipitation of the reduction slag leaching solution.IntroductionWith a density about half of water, lithium is with the lowest density of all solids, mere 0.5 g/cm3 at 20 °C [l]. Lithium is widely used in aerospace, aviation, nuclear-generated power and electric battery industry. Nowadays, over 90 % of the world's primary lithium is produced by molten salt electrolysis [2-4]. But the development of molten salt electrolysis will be effected by some factors: cost, environment, and so on. Vacuum thermal reduction may be used extensively in future because of its low-energy consumption, high-purity and short-cycle."

Jan 1, 2013

By Gökhan Hardal, Berat Yüksel Price

Negative temperature coefficient (NTC) thermistors are required to have good electrical stability for many domestic and industrial applications. The aging phenomenon of NTC thermistors can be described as the change in electrical resistance due to thermal stress with time. In this study, Ni0.5CoxMn2.5−xO4 (x = 0.5, 0.8 and 1.1) ceramics were fabricated by the conventional solid-state reaction method. The powder mixtures of manganese, cobalt and nickel oxides were ball-milled for 5 h. The powders were calcinated at 900 °C for 2 h. The samples were sintered at 1100 °C for 5 h. To investigate the aging behaviour, the samples were held at 150 °C for 400 h. Aging in the samples were calculated by the following equation; ΔR/R0 = (R − R0)/R0 in which R0 is the resistance at 25 °C before the aging test, and R is the resistance at 25 °C after the aging test.

Mar 1, 2017

By A. K. Riihimäki

The description deals with duplex stainless cast steels and austenitic high molybdenum steels used in pumps for severe condition service. The main modem nitrogen alloyed duplex cast steels are presented in the ASTM standard A-890. Two grades of high molybdenum austenitic stainless steels there are presented in ASTM A-744 (-96) standard i.e. CN-3MN and CK-3MCuN. The latest and most corrosion- resistant stainless steel grade is AVESTA 654 SMO?. Avesta Sheffield the trademark owner has granted Ahlstrom Pumps license to produce the material. This new stainless steel as pump material for severe service has improved properties in the hydrometallurgy and electrorefining processes of metal and especially in the copper industry compared to duplex stainless steels. The paper deals briefly with the foundry process to manufacture high alloy stainless steel pump castings. The AOD-method (AOD= Argon Oxygen Decarburization) is an important prerequisite for the melting of low carbon, high chromium and molybdenum alloyed nitrogen steels. The properties of these steels are included. The main topic is the corrosion resistance of the above-mentioned pump materials in severe service. Results of short-time erosion and corrosion tests are discussed and compared with the results of plant tests. Practical results of pump materials performance in severe service for the copper industry are given. The new high alloyed cast stainless steel (main elements; Cr-24%, Ni-22%, Mo-7,3% and N-0,5%) has shown improved corrosion and erosion properties as process pump material in several severe service applications e.g. in the metal industry.

Jan 1, 1999

By Robert Fritzsch, Ragnhild E. Aune, Mark William Kennedy, Behzad Mirzaei

"The quantitative particle concentration can give important information about the cleanliness of melts for quality control in primary and secondary production of aluminum. Manual quantification of the particle concentration is normally a time consuming process and human control can bias the acquired images and particle count.The present paper explains the automated image-processing steps for the quantification of SiC-particles, with equivalent diameters from 2 to 25 µm, in solidified A356. A total of 700 micrographs, acquired with a standard white light microscope with 10 x magnification, were analyzed. The applied software (Image Pro-Plus 7.0 from MediaCybemetics®) allows for programming of macros which in tum provides the user with a higher degree of control. The automated results are compared with the results obtained by manually counting the particles in the same micrographs. The impact of the automated results on the estimated filtration efficiency was established to be only -3%.IntroductionInclusions are both indigenous and exogenous particulates that are present in commercial metals such as aluminum. If large individual or large numbers of inclusions are present, they can have a significant negative impact on the appearance, mechanical and chemical behavior of products produced from the metal. Aluminum is known to contain large numbers of inclusions: =50 µm in size, e.g. typically <l ppm by volume or <100,000 inclusions of>20 µm per kg of metal as detectable using a Liquid Metal Cleanliness Analyzer, LiMCA [1]. Depending on the final application of the aluminum, inclusions can render the metal 'not fit for purpose', and result in serious economic consequences to metal producers.It is not surprising that the aluminum industry has developed a number of treatment processes to improve metal cleanliness, given the large number of high value products whose quality can be adversely affected by inclusions. CFFs are the most commonly applied filtration process and have been used to filter >50% of the world production of aluminum since the 1990's [2].Inclusions in aluminum may be particles, bifilms [3] or clusters of: oxides (Al2O3 , SiO2), spinels (MgO· Al2O3), carbides (SiC, Al4C3), nitrides (AlN), borides (TiB2), sulfides, phosphides and intermetallics [ 4]."

Jan 1, 2013

By Dave Tahija

"Many investigations are being performed with the goal of removing carbon dioxide from the atmosphere and permanently storing it in geologically stable settings. At the same time, carbon dioxide in the form of dissolved carbonate is steadily accumulating in the world's oceans. Both carbon dioxide sequestration and oceanic accumulation are constrained by the aqueous thermodynamics of the carbonate system. These constraints are illustrated using the STABCAL computer model to generate potential-pH and aqueous distribution diagrams of seawater in contact with various pressures of carbon dioxide gas. STABCAL diagrams and titration simulations are also used to model some potentially useful cation-carbonate sequestrationsystems.IntroductionAtmospheric carbon dioxide concentrations have risen dramatically in the past couple of centuries and are rising still, primarily as a result of human activities, especially the burning of fossil fuels. Increased atmospheric carbon dioxide concentrations have been implicated as a main cause of global warming but have other effects as well.Rising levels of atmospheric carbon dioxide result in increased concentrations of dissolved carbonate complexes in water, including the oceans. These dissolved carbonates interact with other dissolved substances, altering overall seawater chemistry, most noticeably causing lowered pH levels.Some of these chemical changes are observed directly, for instance the general drop in oceanic pH, [1], while others can be inferred and predicted using thermodynamic modeling. The chemistry of dissolved carbonate in seawater is not especially intricate, as such chemical systems go, but neither is it simple enough to be worked out on the back of an envelope. Interactions between the several simple carbonate species and all the major dissolved cations in seawater should be considered, as well as the effects of competing anions, especially chloride and sulphate, since they are much more abundant than carbonate in seawater."

Jan 1, 2011

By Wellington Pereira Inácio

This work investigated the toughness behavior of polyester matrix composites reinforced with up to 30% in volume of long, continuous and aligned sisal fibers by means of Charpy impact tests. It was found that the addition of sisal fibers results in a marked increase in the absorbed impact energy of the composites. Macroscopic observation of the post-impact specimens and SEM fracture analysis showed that longitudinal rupture through the sisal fiber interface with the polyester matrix is the main mechanism for the remarkable toughness of these composites.

Jan 1, 2010

By Jinwu Kang

The hydraulic turbine blade of the matensitic stainless steel (Cr13%,Ni5%,Mo1%) is a kind of large and curved shape, which is susceptible to deformation in both casting and heat treatment processes. The coupling analysis of heat transfer, phase transformation and stress in heat treatment process of the turbine blade for Three Gorges Project is carried out by using Deform-3D software. Its temperature fields, phase fields and stress fields in heat treatment process are obtained. And its deformation is predicted. In the cooling process of normalizing, the blade exhibits relatively large deformation. Based on the stress analysis and deformation prediction in heat treatment process, an algorithm for the determination of reverse deformation of the blade casting in heat treatment process is presented. And the reverse deformation distribution of blade is obtained.

Jan 1, 2010

By Ahmad-Bitar¸ Riyad N., Shadia J. Ikhmayies

"CdSi-xTex thin films with O<x<0.3 were prepared on glass substrates by the annealing of CdS:In thin films produced by the spray pyrolysis technique. The annealing was performed in nitrogen atmosphere at 400 --,C in the presence of Te vapor. The compositions of the films were determined by energy dispersive X-ray detection (EDAX) measurements. Scanning electron microscopy (SEM) was used to investigate the morphology of the films. The transmittance of the films was measured at room temperature in the wavelength range 400-1100 nm and used to produce the absorbance of the films. The first derivative of the absorbance was used to estimate the optical bandgap energy Eg by using the minima in the first derivative. The relation between the bandgap energy and the fraction x was found to fit with a parabola and bandgaps in the range 2.196: =Eg: =2.480 e V were obtained. Urbach tailing in the bandgap was also investigated.IntroductionPolycrystalline thin film CdS/CdTe solar cells are promising candidates for low cost and high efficiency photovoltaic applications. The fabrication process of these cells involves the deposition of a p-type CdTe absorber layer on top of an n-type CdS one which acts as a window. The efficiency of the solar cell is affected by the method of preparation of both layers [1, 2].Interdiffusion processes taking place at the CdS/CdTe interface have largely been realized to significantly affect the device performance [3] by changing the bandgap of both CdTe and CdS which modifies the spectral response of the solar cell [ 4]. The formation of a mixed crystal or a graded layer causes a reduction in the lattice mismatch at the CdS/CdTe junction [5] which is about 9% [ 6] and then a reduction in the number of interfacial states and recombination centers, thus enhancing the solar cell performance [7, 8]. A complete understanding of the properties of the intermixed layers CdSxTe1-x that usually constitutes the interfacial region in the CdS/CdTe solar cell is essential. According to our knowledge, a lot of research was devoted to the investigation of the diffusion of S into CdTe [3-5, 9]; but little on the direct investigation of the diffusion of Te into CdS [6]."

Jan 1, 2011