By Zhucheng Huang, Ronghai ZHONG, Liangming Wen, Tao Jiang

The reduction roasting-magnetic separation and its strengthening of high silicon coal-containing mini-pellets by sodium additives were researched. The results show that the carbon gasification reaction and reduction of fine hematite in high silicon coal-containing mini-pellets with 3% sodium additives were enhanced. Comparing with no sodium additives, the gasification rate of carbon with 3% sodium additives reacting with CO2 for 40 minutes at 950 and the metallization rate of reduced pellets with 3% sodium additives after roasting for 35 minutes at 960 increased from 35.15% and 58.72% to 86.98% and 86.15%, respectively. The analysis of SEM equipped with EDS demonstrates that the inner pore of reduced pellets with 3% sodium additives was more developed and the iron grains size significantly enlarged, meanwhile, the iron grade of concentrate increased from 60.45% to 80.23% and the iron recovery rate decreased from 84.67% to 80.78% after grinding-magnetic separation.

Jan 1, 2016

Testing is in progress to address compatibility issues with regard to long term storage of plutonium in contact with two different intermetallic systems. The two intermetallic systems are: 1. dental amalgam, i.e., mercury plus silver alloy powder, and 2. liquid gallium alloy plus copper powder. Both of these are plasto-metallic materials that undergo a solidification reaction at room temperature. Each system is allowed to react in contact with both high-purity alpha plutonium and a delta stabilized plutonium alloy at varying temperatures in an argon atmosphere. Wetting characteristics and possible interaction will be studied metallographically in the post-mortem condition. Complete results including metallographic examinations will be presented.

Jan 1, 1995

By H. Kohno

The Onahama No.3 tankhouse started commercial operation in early 1973, with the capacity of 8,500 metric tons per month. When the No.3 tankhouse was constructed, the starter sheet stripping section was rebuilt at the No.2 tankhouse and electrolyte purification section was expanded. The previous AIME paper in 1976 described the design principles of the No.3 tankhouse and its layout, This paper describes the starter sheet stripping machine in the No.2 tankhouse and the electrodes handling system in the No.3 tankhouse and all these equipments were developed for the operation of the No.3 tankhouse. A Hazelette continuous casting machine was also introduced in order to cast thin anodes with accurate shape. Owing to the adoption of thin anodes, gold, silver and copper inventory is reduced by 40%. Jumbo tanks and newly developed mechanical equipments were adopted and no work on cells during pulling up operation was achieved. Using thin anodes with accurate shape, inspection work was completely abolished while maintaining high current efficiency and high cathode quality. Labor cost was reduced by 70% and only six operaters can produce? 8,500 metric tons of cathodes per month. The same new electrolysis process is appreciated and has been used as a newly built independent tankhouse by Kidd Creek Mines Ltd., in Canada in 1981 with excellent results

Jan 1, 1987

By Toshiaki Tsuru, Takeshi Ohgai, Hisaaki Fukushima, Shigeo Kobayashi, Tetsuya Akiyama

"Electrodeposition behavior of Zn-Cr alloys from the methanol baths was investigated. In the methanol baths of low Cr3+ concentration, Cr (III) compound was incorporated in the deposits and no lusfrous Zn-Cr alloys was deposited. However, Cr was existed as metallic state in the deposits obtained from the baths of higher Cr3+ concentration. With an increase in water content in the baths, the chemical state of Cr in the deposits changed from metallic to trivalent state. Under the condition that metallic Cr can be electrodeposited, Zn deposition was significantly polarized to the potential of Cr deposition.INTRODUCTIONAn attention has been paid to Zn-Cr alloy plated steel sheet because of its excellent properties for body panels of automobile and electrical appliances [1]-[4]. This plating process can be operated using the sulfate solutions containing Cr3+ ion [1] - [6].In decorative single Cr plating, on the other hand, many attempts have been made to electroplate Cr from trivalent electrolytes, which is motived by environmental deficiencies of the presently used hexavalent process [7]. [8]. However, it has been reported that in the aqueous solutions the behavior of the electroreduction of 0 3+ is atypical due to the complicated nature of the chemistry and electrochemistry of cr3+ species [9]-[11]. Even in Zn-Cr alloy plating, it is difficult to codeposit metallic Cr with Zn in simple sulfate electrolytes [l]-[4], [12]. Therefore, it can be expected that the electrodeposition behaviors of Zn-Cr alloys as well as Cr are significantly changed when the electrodeposition is conducted in non-aqueous plating solutions.In this study, the electrodeposition of Zn-Cr alloy was conducted from methanol solutions to clarify the electroreduction mechanism of Cr3·-Cr0 in the alloy deposition process."

Jan 1, 2000

By Yang Xianwan, Zhu Xiaoyun, Guo Zhongcheng, Zheng Yanping, Zhai Dacheng

"Corrosion resistance of RE-Ni-W-P-SiC composite coating and 3 l6L stainless steel in corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions at different concentrations by means of immersion methods and anodic polarization curves obtained by DHZ-1 electrochemical synthetic tester and HDV-7 transistor constant potentiometer. Immersion experiment results show that corrosion rate of RE-Ni-W-P-SiC composite coating as-deposited in HCl solutions increases with the rise of HCl concentrations, on the contrary, the corrosion rate of the composite coating after heat treatment decreases with increasing the HCl concentrations the corrosion rates of the coatings as-deposited and after heat treatment in H2SO4 and H3PO4 solutions respectively decrease with the rise.of H2SO4 and H3PO4 concentrations the corrosion rate of the deposit as-deposited in FeC13 solutions decreases with increasing FeC13 concentrations, while the rate of the composite coating after heat treatment increases .with the rise of FeC13 concentrations.In addition, the corrosion rate of 3 l 6L stainless steel in the corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions at different concentrations increases with rising of concentrations. Furthermore, the corrosion rate of 316L stainless steel in the corrosion media of H2SO4, HCl, H3PO4 and FeC13 solutions respectively is much greater than that of the RE-Ni-W-P-SiC composite coating as-deposited and after heat treatment in the same corrosion media.1. IntroductionAll the materials and their products, when processed, stored and used, it is inevitable that the corrosion, wear, fatigue and crack occur owing to the actions of surroundings. Those early failure and abrasion, through all kinds of departments and profession that corrosion consumes one percent of tens of the steel products of the whole world; and two or four percent of the GDP is lost because of the corrosion."

Jan 1, 2000

By T. Shibaraki

A new larger, more efficient and economical Mitsubishi furnace line at Naoshima was put into operation in May 1991. Naoshima Smelter had produced previously about 230,000 mtpy anode copper with two smelter lines, i.e., a conventional reverberatory furnace line and Mitsubishi furnace line, which had been shutdown at the same time of the start up of the new smelter. At the beginning of the operation, there were several initial problems at the area of off gas trains and feeding system. By overcoming them now the process has been continuing satisfactory operation at the design rate. The paper describes about the design concepts and the actual operation of the new smelter.

Jan 1, 1993

By R. Hurman Eric

The electrode in a slag-resistance electric furnace is the central factor in the design and operation of the furnace by its role of conveying the smelting power, i.e. heat needed for the operation. The control parameters are the size and positioning in the slag bath which are defined by slag resistivity, furnace resistance, cell constant and power input sequence all of which are closely interrelated. The flow of heat generated by the electrode current determines the energy distributions and thus the furnace dimensions. Heat flow models concerning vertical, horizontal and combined two-dimensional flows are discussed. All these considerations are based on the experimentally determined slag properties such as its resistivity.

Jan 1, 1995

By Manabu lshimaru

Solid-liquid interfaces as well as defect formation processes during crystallization of melted silicon (Si) have been examined by using molecular-dynamics (MD) simulations. The ordinary Langevin equation employing the Tersoff interatomic potential was used for the calculation of the atomic trajectories. A solid-melt interface has a tendency to form {]] I} microfacets during the crystal growth in the [001] direction, while it is essentially flat during the (Ill) crystallization. Because of the difference of the interfacial structures, the structures of grown-in defects and defect evolution depend strongly on the growth direction. We discuss defect structures and their formation processes within the context of our results as well as previous experimental observations.

Jan 1, 2001

By Ramiro Escudero

Michoacan?s beach sands with interesting concentrations of ilmenite were studied to produce titanium by hydrometallurgical techniques. Nevertheless, among titanium species, there are different additional components of Michoacan?s beach sands which could be of interesting applications. Some of them are likely to be applied for the manufacture of nanocrystalline ceramics. Although, the most applied mineral dressing to treat these kind of sands, that contain magnetic species (i.e., ilmenite, magnetite), is a combination of gravity separation and magnetic separation, it could be of a great deal of benefit to apply the information regarding the surface characteristics of the sands? components, in order to study the application of flotation technologies to separate selectively those species with commercial value.

Jan 1, 2006

By Jin Liu

The mechanism and rate of carbon reduction of each of the phases that are formed in the flash flame, i.e. sulfide (matte) and oxysulfide, was investigated. Graphite-slag reduction was conducted for comparison purposes. The objective of these tests was to measure the rate of solid graphite reduction of respectively matte, oxysulfide, slag, and matte+slag mixture at different temperatures. More in particular, these tests were expected to permit understanding and explaining the reduction mechanism of each material by comparing the respective reaction rates, product reaction gas compositions and CO/CO2 ratios, reduced material assays, activation energies, and other relevant parameters. Direct visual inspection of the test crucibles would provide additional information.

Jan 1, 2006

By Lionel Ryan

In 1996, the Dominican Republic operation of Falconbridge (Falcondo) developed a 5-year Process Control Plan in conjunction with the corporate Process Control group located in Sudbury, Ontario, Canada. This plan was further refined into an analysis of the areas of the highest potential economic return for the company with the reduction shaft furnace operation being the most promising. Historically, the reduction plant, which comprises 12 shaft furnaces, has been the bottleneck of ferronickel production. Since 1996 there has been a history of control development, and the current status is that all 12 furnaces are using advanced model-based multi- variable predictive control. The combination of advanced process control (APC), improved control system performance and improved process information management has resulted in an increased throughput of 6% per shaft furnace and a reduction in operating costs of 4.5 US cent/lb of Ni. This paper reviews some of the major milestones that have been achieved in this development Keywords: Advanced Process Control; Model Based Predictive Control; Connoisseur, Reduction Shatt Furnace; Nickel Laterite Ore; Ferronickel; MonitorMV

Jan 1, 2004

By Kensuke Sassa, Shigeo Asai, Norihisa Waki

"A new method for separating inclusions from a molten metal using a high magnetic field has been proposed. The principle of this method based on the magnetization force has been confirmed in experiments of separating intermetallic compounds imitating inclusions from molten Al-Si-Mn-Fe and Al-Si alloys. In order to measure a magnetic susceptibility, the Gouy's method has been so modified by using a super-conducting magnetic as to work in a high temperature up to 1473K. A theoretical expression for the magnetization force, which is indispensable to evaluate the magnetic susceptibility, has been derived. The magnetization forces acting on intermetallic compounds which were used in the magnetic separation were measured over the range of liquidous to solidous temperatures and the magnetic susceptibilities of the intermetallic compounds were obtained from measured magnetization forces by use of the theoretical expression.I. IntroductionRecent developments in the technology of super-conducting magnets have given rise to the circumstance that a high magnetic field over a relatively large space is readily available without liquid helium. Then, it has been found that a high magnetic field provides magnetic effects to nonmagnetic substances and various interesting phenomena have been reported in the broad science fields of physics, chemistry and biology1). ""A science related to a high magnetic field"" in which many fields are transversally viewed from the standpoint of a high magnetic field2 ) is going to be established. In particular, new phenomena and functions brought by the science related to a high magnetic field are also useful for Material Science and Engineering so that the creation of Materials Science and Engineering related to a high magnetic field"" has been conceived 3).Now, when a substance regardless of being magnetic or nonmagnetic is put in a magnetic field, it feels a magnetization force, which is familiar to such a force that a magnet attracts iron. The force is in proportion to the product of magnetic field strength, its gradient and susceptibility so that a precipitated substance can be separated from a molten metal based on the difference between susceptibilities of a substance and a melt. This is a basic principle of the magnetic separation. So far the application of the magnetic separation has been limited to the separation of ferromagnetic substances from a nonmagnetic medium. A high magnetic field, however, has enabled to separate nonmagnetic substances from a nonmagnetic medium.In this study, a new method to separate inclusions from a molten metal using a high magnetic field has been proposed. The principle of the method was verified by experimental works and the feasibility on the elimination of inclusions in steelmaking processes has been studied"

Jan 1, 2000

By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn't favor the economic metals' recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By Hiroshi Ono

"By newly developed ICP method, trace amounts of As(III), As(V) .,Sb(III) and Sb(V) were precisely determined within accuracy of sub ng/ml. As(III) and Sb(III) were separated from As(V) and Sb(V) by extracting into ·xylene as diethyldithiocarbamate complexes using diethylammonium diethyldithiocarbamate (DDDC), and then back-extracted into nitric acid for a quantitative determiruition by ICP-AES equipped with hydridegeneration system The recoveries of As(III) and Sb(III) were satisfactory throughout the extraction with 0.04mol/l DDDC in xylene from lmol/l hydrochloric acid solution and the back-extraction with 7 mol/l nitric acid. As(V) and Sb(V) were reduced to As(III) and Sb(III) by ascorbic acid and potassium iodide, and their quantities were determined as mentioned above. The detection limits were found to be 0.58ng/ml for As(III), 0.63ng/ml for Sb(III) using 50ml of a sample. The proposed method was applied to analysis of the real sample.Introduction In drain, arsenic(AS) concentration is prescribed below 0.lmg/l, so As must be removed. As is existed at .the form of As(III) or As(V) in solution. For t1Jeir difference of chemic;µ property, it is not easy to remove As in solution. So it is an urgent necessity to develop for determining concentration of As(III) and As(V). Antimony( Sb) has resemblance .chemical property to As. So Sb was experimented the same as As.The separation and determination of As(III) and As(V) have been carried out using several methods, such as ICP after copreclpitating separation, HPLC, direct hydride generation atomic absorption. However these methods have some problems. One of main problems is that HPLC and direct hydride generation atomic absorption methods are influenced by coexisting elements."

Jan 1, 2000

By Shun Fujieda, Shigeru Suzuki, Kozo Shinoda, Tetsuo Fujita

"Dowa Metals & Mining Co. Ltd. has developed and plant-practiced a unique scorodite synthesis technology (DMSP®) for arsenic immobilization by oxidizing Fe(ll) ions in the presence of As(V) ions. Dowa has improved the DMSP® technology and has developed the process extensively for other applications. This paper focuses on the applicability of the DMSP® for various cases of copper smelting, and introduces other technologies for fixing arsenic and recycling gallium from GaAs, simultaneously processing (fixing) arsenic and thallium, and fixing and recovering arsenic from dilute arsenic solutions. The DMSP® was found to be applicable not only for various processes in nonferrous smelting, but also for other applications with a high potential for reducing environmental problems.IntroductionDowa Metals & Mining Co. Ltd. developed a method for synthesizing scorodite at ambient pressure [1], The scorodite is precipitated by oxidizing Fe(II) ion in a high-concentration As(V) solution. The scorodite produced in this way does not readily release arsenic because of its high crystallinity. Dowa built a demonstration plant for this technology at the Kosaka Smelter and established the production of scorodite at 30 t As/month by treating intermediate products from copper smelting as the starting material. The DMSP® was demonstrated to be favorably applicable to copper smelting [2]. We are engaged in further increasing the amount of arsenic fixation by the use of this process. Further improvements in productivity, cost reduction and applicability in various processes have been devised. Dowa has been endeavoring to resolve other problems as well as to improve productivity. We have gained extensive knowledge on arsenic treatment in our endeavors, enabling us to solve problems and improve productivity. This paper introduces the investigations and developments related to DMSP®."

Jan 1, 2012

By Katsunori Okaya, Gjergj Dodbiba, Hiroyuki Ono, Toyohisa Fujita, Seiji Matsuo

"In an attempt to raise the copper grade of Printed Circuit board (PCB) by removing other components, carbonization treatment was investigated. The crushed PCB without surface-mounted parts was carbonized under nitrogen atmosphere. After screening, the char was classified by size into oversized pieces, undersized pieces and powder. The copper foil and glass fiber pieces were liberated and collected in undersized fraction. The liberation of copper foil from the oversized pieces was also investigated. The copper foil was liberated easily from glass fiber by stamping treatment. Liberation rate of copper foil was high at high carbonized temperature. The experimental results indicated that 90% of oversized char was liberated and the copper foil recovery from PCB carbonized at 1073K was 110kg/t. The copper recovery from char powder by flotation was also investigated. 15% of the copper grade and 80 % of the copper recovery were obtained, whereas the removal rate of silicon was 55%.IntroductionWaste Electrical and Electronic Equipments (WEEEs) should be recycled because they have many kinds of valuable materials and most WEEEs include Printed Circuit Boards (PCBs). In Japan, about 30 km2 per year of Printed Circuit board (PCB) has been produced [1], PCBs are normally separated from WEEEs and picked up by hand and sold to non-ferrous metal market because PCBs include high grade of copper and other precious metal such as gold, silver and palladium [2]. However, PCB also has impurities such as silicon, aluminum and calcium which are slag materials in non-ferrous smelting process, and other harmful elements such as lead, bromine and antimony. Low grade PCBs are sold after removal of invaluable parts or sometimes land filled without any treatment"

Jan 1, 2011

By Junji Shibata

The waste acid mixture whose main component is phosphoric acid, is discharged from the etching process in the liquid crystal production industry. In order to separate impurity acids from the phosphoric acid, trioctyl phosphate (TOP) is used as an extractant. TOP can extract acetic and nitric acids selectivity. The extraction and stripping operations are carried out for the acid mixture by beaker-scale experiments and countercurrent multistage operations with mixer-settler equipment. TOP selectively extracts the acetic and nitric acids in the acid mixture. From the results of the McCabe-Thiele analysis obtained by beaker-scale tests, the extraction for acetic and nitric acids are approximately 100%, respectively, by 6-stage extraction with a phase ratio (A/O) of 0.4. On the other hand, almost all of acetic and nitric acids are stripped with water from the organic phase by 4-stage stripping with a phase ratio (A/O) of 1.0. About 95% of acetic and 98% of nitric acids can be removed from the acid mixture without extracting phosphoric acid in case of the mixer-settler equipment operation. There are several steps such as slicing, lapping, chemical etching and mechanical polishing in the silicon wafer production process. The chemical etching step is necessary to remove any damaged layer caused in the slicing and lapping steps. The typical etching liquor is the acid mixture comprising nitric acid, acetic acid and hydrofluoric acid. The waste acid is treated by a neutralization method with a high alkali cost and balky solid residue. A solvent extraction method is applicable to separate and recover each acid. Acetic acid is first separated from the waste liquor using 2-ethlyhexyl alcohols as an extractant. Then, nitric acid is recovered using TBP (Tri-butyl phosphate). Finally hydrofluoric acid is separated with TBP solvent extraction. The expected recovered acids in this process are 2mol/L acetic acid, 6mol/L nitric acid and 6mol/L hydrofluoric acid. The yields of this process are almost 100% for acetic acid and nitric acid. On the other hand, it is important to recover and reuse the metal values contained in various industrial wastes from a viewpoint of environmental preservation. Most industrial products are made through processes to separate impurities in raw materials, solid and liquid wastes being necessarily discharged as industrial wastes. Chemical methods such as solvent extraction, ion exchange and membrane separation, and physical methods such as heavy media separation, magnetic separation and electrostatic separation are considered as the methods for separation and recovery of the metal values from the wastes. Some examples of the application of solvent extraction to the treatment of wastes such as Ni-Co alloy scrap, Sm-Co alloy scrap, fly ash and flue dust, and liquid wastes such as plating solution, the rinse solution, etching solution and pickling solution are introduced.

Jan 1, 2003

By Masatsugu Morimitsu

"The novel smart anode, MSA ™, for electrowinning of non-ferrous metals such as copper, zinc, nickel, and cobalt has been developed by thermal decomposition. The smart anode consists of a titanium substrate coated with a catalytic oxide layer which comprises amorphous or less crystalline oxide coatings. The catalytic layer contains an iridium oxide-based mixture or a ruthenium oxide-based mixture. The smart anode provides a remarkable reduction in cell voltage compared to other anodes, e.g., commercially available coated titanium electrodes and lead alloy electrodes. The test data has demonstrated that a maximum voltage reduction by ca. 30% is possible compared to lead alloy anodes. The smart anode also gives some additional merits in suppressing unwanted deposits on the anode; i.e., deposition of MnOOH, Pb02, or CoOOH. The electrowinning with the smart anode is possible to be an environmentally friendly process with less energy consumption and less anode deposits.IntroductionA coated titanium electrode iridium oxide-based or ruthenium oxide-based catalytic layers is well known as an insoluble anode for oxygen or chlorine evolution in industrial electrolysis such as chloro-alkali electrolysis, electrogalvanizing or electrotinning of a steel, a thin film production by electrodeposition such as copper foil production (CFP), water electrolysis, and electrowinning of nonferrous metals. The anode is commercially produced by thermal decomposition of a precursor solution painted on a titanium substrate, and the decomposition is usually performed at 450 °C or more. The obtained catalytic oxide coating formed on the substrate contains crystalline oxide as an active component to oxygen or chlorine evolution. The author of this paper had met a problem of such a crystalline oxide coating in the application of copper foil production; the anode was unable to use for a long period because of a large amount of lead oxide (Pb02) deposited on the anode, and the cell voltage was seen to continuously increase and drastically rise by the accumulated Pb02. In this case, the voltage reduction by replacing a lead alloy anode with the dimensionally stable anode was initially observed, but was gradually lost and disappeared. Therefore, the author of this paper aimed and investigated to suppress the unwanted side reaction on the anode, and finally invented a new class of coating based on an amorphous iridium oxide mixture in 2003 [!]. The invented coating was obtained at a low temperature thermal decomposition, e.g., 360 °C, and the coating consisted of amorphous iridium oxide and amorphous tantalum oxide. This invention achieved that oxygen evolution potential shifted more negative so that the cell voltage was reduced, and no Pb02 was deposited in the electrolyte of CFP [2,3]."

Jan 1, 2012

By Ilija Ilic

Recovery of tin from tinplate and production of good-quality detinned-plate for further processing in ironworks has been the subject of interest for many years. Tinplates are mostly used for production of tin containers for food industry and consumer goods. The research carried out so far included determination of the parameters of dissolution of tin from tinplates by alkaline solution of NaOH and electrochemical recovery of tin from the alkaline solutions. During leaching, NaNO3 and methanitrobenzoic acid (MNBA) as oxidants were studied. By leaching the waste tinplate which contains 0.31 % of tin with a solution of 1.12 mol/dm3 NaOH, 0.26 mol/dm3 Na2CO3 and 0.09 mol/dm3 MNBA at temperature of 70°C for 60 mm, a degree of tin leaching of 97 % was attained. MNBA facilitates oxidation of Sn2+ into Sn4+ suitable for obtaining compact, and not spongy, Sn cathode deposit, as it was the ease earlier. Recovery of tin by electrolysis from solutions obtained by leaching was studied to determine the effect of electrolyte composition on the quality of cathode deposit and the degree of electric current efficiency. Experimental results obtained at a laboratory level were checked on an enlarged laboratory set up where continuos leaching of tin from waste tinplate and its electrolytic recovery from the solution obtained were carried out. The experimental set-up -operated under semi-industrial conditions, and about 500 kg of waste tinplate was processed yielding about 1.160 kg of tin (99 % Sn).

Jan 1, 2000

By Gaifeng Xue, Jingxuan Zhou, Shangchao Liu

"Both COD and TOC can characterize organic pollution of coking wastewater. In theory, there is a linear correlation between these two indicators. After continuous monitoring TOC and COD of coking waste water, linear regression relationship between of these to indicators was studied with the use of mathematical statistics. And conversion equation between these two indicators was established, and using t-test method for significance testing. The results showed that the linear relationship of COD and TOC was significant. Also interval estimation of equation slope and intercept were given in the condition of 95% confidence level. A linear regression equation established can be used to indirectly convert TOC to COD with high precision and accuracy.IntroductionBoth chemical oxygen demand (COD) and total organic carbon (TOC) are measure of the degree of characterization for organic pollution of water bodies. The current COD standard analytical methods is Potassium dichromate titration method [1] . there are some disadvantages in this method, such as only part of organic matter in the water bodies being oxidated, the refluxed steps, a long time needed for each measurement, high cost. It is the most important that sulfuric acid silver and mercury sulfate reagents used in the measurement may easily lead to secondary pollution. In contrast, the measurement of TOC is by the method of combustion or Photocatalytic Oxidation. The result could be easily got from the instrument. There are some advantages in this way, such as easy operation, short time and little expenses for each measurement and no secondary pollution 121• In addition, the measurement of TOC has higher degree of precision and accuracy than the measurement of COD both in the determination of calibration standards and actual samples. The meaning and contrast of TOC and COD are listed in the table 1."

Jan 1, 2013