By K. C. Liddell, B. Dou

"In producing multilayer films for magnetic data storage applications, the interfacial roughness must be controlled in order to obtain high quality materials with reproducible properties. The present understanding of the effect of roughness on multilayer properties such as magnetoresistance is sketchy, particularly for electrodeposited films. In this study, quantitative atomic force microscopy was used to characterize surface morphology before and after Ni films of varying thickness were deposited on Cu cathodes. A multinuclear multilayer growth mechanism is supported by both the deposition conditions and the AFM images, and a multinuclear multilayer model gave a satisfactory fit to measurements of the density of peaks on ultrathin Ni films between 0 and 8 nm thick.Alloys consisting of alternating ferro-and paramagnetic layers have begun to replace Permalloy in the sensing elements of magnetic hard drives. The operating principle of the new read heads is giant magnetoresistance (GMR), and they are smaller and more sensitive than previous inductive heads (1). Experimental studies on sputtered multilayers have emphasized the role of layer thickness and interlayer roughness in determining the presence and size of the GMR effect (e.g., 2,3,4,5,6). However, roughness in electrodeposited multilayers has rarely been measured, even though read heads are likely to continue to be made by this process for some time to come. Cu/Ni can be considered a model system for understanding processing-microstructure-property relationships in electrodeposited multilayers and is the most widely investigated of all such systems (e.g., 7,8,9,10,11,12). Nevertheless, the roughness of the interfaces in Cu/Ni electrodeposits has not been systematically characterized by quantitative techniques, and in all studies reported so far, the total deposit thicknesses were considerably greater than the 10 nm needed for most sensor applications (1). The thinnest such films were about 50 nm (7)."

Jan 1, 1998

By José Sancho, Julia Ayala, Purificación García, Begoña Fernández

"A study is carried out to see the adequacy of using flying ashes coming out from a Power Station to eliminate the copper present in waste cyanide waters that are generated in gold mines.Tests were carried out to see how effective the use of ashes taken from two Power Stations could become. Later, the tests are made using ashes coming from Narcea Power Station as this station is near the mine under study.The work is centred on looking for an economically adequate solution to close the waste decanting ponds of the mine. After several tests, a solution is reached through filtration in static layers.IntroductionThe use of coal to adsorb some water-soluble substances has been widely studied [1,2,3,4,] both in the treatment of drinking waters and in determined stages of selective detachment of cyanide gold complexes in cyanide lixiviation processes [5]. Flying ashes sent to the atmosphere by Power Stations as a sub-product of the combustion of this combustible are generally made of more of a 70 % of a vitreous aluminosilicated material and of an active residual material which may be changeable making them potentially useable as adsorbents. Nevertheless, the properties of each kind of ashes depend on the characteristics of the Power Station, of the combustibles being used, of the combustion system, etc.The aim of this work is to demonstrate the adequacy of flying ashes to eliminate the copper present in cyanide waters coming from gold mines either by adsorption or precipitation of the metal. For this study, tests are carried out with Asturian ashes which have a low quantity of lime. The results obtained in the tests demonstrate the effectivity of the method used. To be absolutely concrete, the work is carried out to establish the use of these ashes in the closing of Asturian installations of cyanide lixiviation"

Jan 1, 2008

By K. Morsi, S. K. Kassegne, A. El-Desouky, K. S. Moon

"Current Activated Tip-based Sintering (CATS) is a new process for the powder-based fabrication of macro, micro and possibly nano-scale features and shapes. This new and unique process enables selective sintering of powders by localizing electrically activated sintering conditions through a stationary or moving electrically conducting tip. We present preliminary experimental results on the effect of tip size in the CA TS process as well as the effect of initial powder particle size on the sintering behavior of nickel powder.IntroductionSpark Plasma Sintering (SPS) has been the center of attention of numerous researchers due its noticeable advantages over conventional sintering techniques such as rapid heating rates, lower sintering temperature and shorter holding times. Research on SPS has been applied on a wide variety of materials such as pure metals [ 1], ceramics [2], composites [3], nano-materials [ 4], biomaterials [ 5], shape memory alloys [ 6] and many other material systems. However, it has been mostly limited to bulk materials with simple shapes with a few exceptions ofresearch efforts where the effect of electric current was combined with metal forming processes such as spark plasma extrusion [7,8] and electric rolling of powders[9]. In this paper a novel process (Current-Activated Tip-Based Sintering (CATS)) is discussed where electric current and pressure are applied simultaneously through a small conducting tip (stationary or moving) over a conducting powder compact. This process has the potential advantages of sintering complex geometries with minimum energy requirements as unconventionally high current densities can be achieved due to the small contact area between the tip and the powder compact. Furthermore, by controlling the tip size, it can be possible to sinter features on the macro-, micro- and even nanoscales."

Jan 1, 2011

By Beatryz C. Mendes, Márcio Sampaio S. Moreira, Rita de C. S. S. Alvarenga, Juliano Correa

Over the last decades, modern technology to build wood structures have been substantially developed. Building solutions for floor systems of wood-concrete mixed T-beams with wood web and concrete flange stand out among these technologies. This work describes an experimental investigation of the performance of bond connectors made of round steel bars for wood-concrete mixed elements. Symmetric three-member specimens were built. The middle member was made of concrete and the other two were made of wood. The first kind of connector consisted of steel bar designed as straight pins with head, normally driven through the wood. The second kind consisted of arc-shaped connectors directly embedded into the wood or bonded using epoxy adhesive. The specimens were then tested in compression. The compressive strength and the force-displacement curve were obtained, in order to evaluate the failure mode and obtain the stiffness in the ultimate (Ku) and serviceability (Ks) limit states. The stiffness values were calculated in the interval corresponding to the secant straight line between, respectively, 10–40 and 10–70% of the ultimate strength. The obtained results indicate high strength and ductile failure mode for all of the cases. Bond stiffness gains were verified when using the arch-shaped connectors.

Mar 1, 2017

By Huang Chao

The thermodynamics analysis on reducing-matting smelting of sulfide ore of lead, antimony and bismuth which use ferric oxide as sulfur fixed agent is first analyzed. Due to the analysis of reaction mechanism, ferric oxide is first reduced to ferrous oxide, then ferrous oxide produce reducing-matting reaction with sulfide ore and reducing agent as reaction equation: MeS+FeO+CO=Me+FeS+CO2. The reaction thermodynamic calculation shows that the reducing-matting reactions of lead sulfide, antimony sulfide, Jamesonite, and bismuth sulfide are feasible, but is infeasible for zinc sulfide. These conclusion provide a feasible method for solve the pollution which produced in the smelting of sulfide ore of lead, antimony and bismuth.

Jan 1, 2006

By F. Ríos

Fundamental research, at laboratory scale, on the biomass adsorption capacity of a liquid mining effluent has been done. The biomass used corresponds to a Chilean seaweed called Gracilaria chilensis. The waste water effluent corresponds to clear water coming from thickeners of a Chilean copper mining operation. The biomass was dried, washed, treated with an acid solution, and then reduced in size. A characterization of Zeta potential was made, finding negative values in a wide pH range with a ZPC equal to 2.5 1. Adsorption tests were made- in an agitated system containing an artificial solution of CuS04 at a controlled temperature of 25 degrees Celsius; also, the effect of pH over the copper adsorbed was studied. Maximal adsorption of copper was found at pH equal to 6, and the Langmuir model indicated values for saturation of 52.08 mg/g and for standard free energy of about -21 KJ/mol. Kinetic adsorption was very high and fitted very well with a second order model equation, finding that 90 per cent of the adsorption occurred during the initial 10 minutes. After stoichiometric when 1 mol of copper is adsorbed, 2 mol hydrogen are released, showing that the main mechanism to remove heavy metals is the ionic exchange, and the seaweed ensures total discharge of copper adsorbed when the pH value is about 1. Experiments done with real waste water from thickeners lead us to conclude that optimal results for copper and molybdenum adsorption are at pH around 3.25 and the remaining treated water may be partially discharged into the water currents, thus showing that Gracilaria chilensis can be used to remove heavy metals easily from liquid effluents in the copper mining industry.

Jan 1, 1999

By Ting Luo, Hongmin Zhu, Kai Huang, Shuanglong Du, Tao Gui, Yifan Xiu

"Poplar cotton, a cellulosic material, was found to adsorb metals ions effectively. In the present study, the biosorption characteristics of Pb(II) onto poplar cotton, were evaluated as a function of pH, contact time, biomass dosage, initial concentration and temperature. Within the pH range investigated (1.0-6.0), the optimal pH value suitable for the uptake of Pb(II) was determined. The maximum adsorption capacity obtained from the Langmuir model is around 0.52mol kg for the poplar cotton sorbent. Equilibration is achieved in 60min for the studied concentrations. Results suggest that the poplar cotton can be directly used as an effective and low-cost biosorbent for removal of Pb(II) from aqueous solution.IntroductionHigh value utilization of various biowastes produced in agricultural, forestry, fishing industries, etc. have attracted great interest from many researchers [1], Biomass, due to its easy availability, great abundance, low cost, easy processing, eco-friendliness and biodegradability, has exhibited exciting potential for being used as raw materials for the preparation of many new hi-tech functional products [2]. For example, using biowastes to synthesize sorbents for application in the removal of toxic substances such as dyes [3], heavy metals from the waste water [4] or in the recovery of valuable metals [5] from the ore tailings and secondary metals resources has made great progress in last decade. In present study, poplar cotton, a kind of white light fluff of poplar trees, like that of dandelion, usually flying in the air each spring was tested as a biosorbent for the remove lead ions from the water. It may also provide some good ideas for new sorbent design. Lead, as one of the typical poisonous heavy metals, for its typical toxicity and extensive pollution, was chosen to test the adsorption behavior of poplar cotton in aqueous solutions."

Jan 1, 2012

By Shaohua Ju, Jin-hui Peng, Ya-jian Wang, Shuai-dan Lu, Li-bo Zhang, Lei Guo

"The granulation of a red mud is of great importance for recycling this material as an adsorbent for waste water or gas. A new granulating process was developed and its effect was evaluated. To reduce the cost of the granulation process, the wet filter cake (containing 25% water) was directly mixed with different cement contents (4%, 6%, 8% and 10% based on wet material). The mixtures were placed in a moist environment for 4 days, and then were washed with deionized water until the pH values of leachants were lower than 9.0. The efflorescence ratio, surface area and particle size of the aged mixture were determined, respectively, by bottle shaking experiments, N2 adsorption and screening. The results showed that the best addition of cement is 2%, and this yielded granulated material with a particle size of less than 2 mm, an efflorescence ratio of 4.83% and a specific surface area of 17.42 m2/g.IntroductionRed mud is a residue of the aluminium industry that is produced during the alkaline extraction of alumina from bauxite by the Bayer process. For every ton of alumina that is produced, the amount of red mud generated can vary from 0.3 to 2.5 tons, depending on the characteristics of the bauxite. In its typical form, red mud is brick red in colour, caustic, about three times as dense as water and, when un-neutralised, has a high pH, typically around pH 13 [1]. It is primarily composed of iron oxide, silica and alumina, along with traces of heavy metals. Red mud particles are quite small; typically 99% will pass through a 0.6 mm sieve and 87% through a 0.038 mm sieve [2],"

Jan 1, 2012

By Seksak Asavavisithchai, Natthida Jareankieathbovorn, Areeya Srichaiyaperk

"Recycling of ADC12 alloy scraps for fabrication of open-cell aluminium foams has been conducted via pressure infiltration method of replication process. The scrap, up to 50 wt.%, was melted with pure aluminium billet, followed by infiltration in a replicated mold of polyethylene foam structure. Compared with the pure aluminium foam, the compressive strength and hardness are higher for the foams with recycled scraps. The increase in foam mechanical properties is due to the presence of Si hard phase in Al matrix. The strength and hardness of the foams also increase with increasing contents of the scraps.IntroductionRecently, open-cell metallic foams have been brought to considerable attention of many industries due to their superior properties; such as large surface area, high specific strength, thermal conductivity, high service temperature and excellent anti-microbial activity, that cannot be found in conventional materials [1, 2]. Typically, open-cell foams are used in functional applications for which a requirement of high strength materials is not demanded. Good examples of such applications include heat exchangers, bone-replacement implants, interconnects, catalyst supports, and sound insulators.Among all types of open-cell metallic foams, aluminium (Al) is the most widely used base metal, due to low material cost, low density, low melting temperature and good corrosion resistance. To improve mechanical properties of Al foam, modification of foam microstructure with addition of alloy elements or ceramic particles is commonly carried out [3, 4]. ADC12 alloy is a typical die-casting Al alloy with high content of silicon (Si) close to the eutectic point in Al-Si binary phase diagram. The alloy is extensively used in the casting industry, due to high wear and corrosion resistance, low coefficient of thermal expansion and excellent castability [5]. The mechanical properties of Al-Si alloy are strongly dependent of Si content."

Jan 1, 2012

By Samir N. Shoukry, Mourad Y. Riad, Gergis W. William

"Setting of concrete material is defined as the transitional period between states of true fluidity and true rigidity. Initial and final setting times are measured in the laboratory on the mortar sieved from the mix in a controlled environment where temperature and moisture values are constant. On the other hand, field applications are held in outdoor environments where environmental variations have direct impact on setting time values. In this study, initial setting time of class K concrete, usually used for bridge decks and concrete pavements, are investigated highlighting discrepancies between laboratory and field measurements. 72 mixes have been cast in variable environments and collected data from concrete mixes and the ambient conditions are reported. In light of the collected data, the effects of variable setting times on early age cracking of concrete material are studied and means to minimize such cracks are presented.BackgroundSetting of concrete material is defined as the transitional period between states of true fluidity and true rigidity [1]. Continuous hydration of the cement within the matrix transfers the mix from a state of setting to hardening. Initial and final Setting times are measured in a laboratory setting following ASTM C 403 specifications. Initial setting approximates the time at which the cement paste can no longer be plastic under compaction (or can be handled in a proper fashion), while the final setting approximates the time at which hardening occurs. The standard test described in ASTM C 403 is conducted on the mortar sieved from the mix (paste passing from 4.75 mm sieve opening). Initial and final settings are described as the elapsed time after the initial contact of water and cement till the mortar reaches a penetration resistances of 3.5 MPa (500 psi), and 27.6 MPa (4000 psi) respectively."

Jan 1, 2012

By Chikabumi Yamauchi, Mitsuru Tanahashi, Toshiharu Fujisawa

"Thermodynamic properties of impurities in molten silicon are of prime importance in developing economical production methods of solar grade silicon. In the present research work, thermodynamic properties of boron, the most difficult element to remove from molten silicon, were measured by chemical equilibration techniques at 1723 and 1773 K. Activity coefficients and self-interaction parameters of boron in molten silicon were determined by equilibrating the melt with solid BN under controlled nitrogen partial pressures. Interaction parameters between boron and nitrogen in molten silicon were also determined by equilibrating the molten Si-B alloys with solid Si3N4• Based on the data obtained, the stability diagram of the Si-B-N system was established.IntroductionPhotovoltaic power generation using a silicon solar cell is expected to be the most promising energy source, because it is inexhaustible, cleaner and more safety than conventional energy sources, such as thermal or atomic power generation. At present, expensive off-grade silicon for semiconductor (SEG-Si) is used for a solar cell production. However, if a large-scale photovoltaic energy conversion using silicon solar cell comes into wide use in the near future, silicon will be sure to be in short supply for the cell. Therefore, a development of a new large scale process for solar grade silicon (SOG-Si) production is definitely necessary, which can remove contained impurities from silicon.Among the impurities contained in silicon, boron is one of the most difficult ones to remove by a zone melting or an unidirectional solidification, because its segregation coefficient in silicon is close to unity (0.8). In addition, boron behaves as a p-type silicon semiconductor dopant and, therefore, its content in SOG-Si must be severely controlled. Although some attempts to remove boron by various metallurgical methods have been carried out [I -4], quantitative analysis has not been made due to lack in the information on the thermodynamic properties of boron in molten silicon. From this view point, the activity of boron in molten silicon was determined in the present study by chemical equilibration techniques at 1723 and 1773 K."

Jan 1, 1998

By A. Mezei

A process has been developed to recover cobalt, gold and bismuth from the NICO deposit in Canada. The process consists of a bulk rougher flotation followed by an optional separation by flotation to produce a bismuth concentrate and a cobalt concentrate, grading on average 12.8 % Bi and 1.8% Co, respectively. Cobalt is leached by pressure oxidation at 97% efficiency, producing a pregnant solution suitable for further processing. Before optimization, about 38% of the bismuth is recovered in the selective concentrate, wherefrom it is recovered by ferric chloride leaching followed by cementation, at overall efficiencies exceeding 98%. The gold is recovered from the cobalt and bismuth leach residues by cyanidation, at 95% efficiency. Previous work described the results of the leaching of the concentrates, recovery of gold (Part I) and the recovery of bismuth (Part 11). This work describes the results of the cobalt recovery testwork and the resulting conceptual flowsheet. The sulfur dioxide-oxygen system was the most efficient for the oxidationlprecipitation of iron and arsenic from cobalt bearing pregnant leach solutions, producing purified solutions assaying <1 mg/L As and <8 mg/L Fe. The efficiency of cobalt solvent extraction (from the resulting purified PLS containing about 1 g/L Co) ranged from 9 1 to 98%; the co-extractions ranged from 88 to 100% for copper, from 28 to 33% for magnesium, from 6 to 7% for calcium and from 96 to 98% for zinc. Sulphide precipitation processes (using either sulfur dioxidelelemental sulfur or sodium sulfide) produced residual copper concentrations in the cobalt strip solution ranging from 0.1 to 2 mg/L Cu. About 90% of the calcium and magnesium were separated by scrubbing the organic with cobalt sulfate, producing residual concentrations of 12 mg/L Ca and from 180 to 330 mg/L Mg in typical feed solutions directed to cobalt carbonate precipitation tests. Cobalt carbonate precipitation efficiencies ranged from 75 to 78% when calcium and magnesium co- precipitations were restricted from 8 to 17% and 0.3 to 0.4%, respectively. The limits required by most stringent specifications on commercial grade cobalt carbonate products were met or exceeded.

Jan 1, 2002

By Per Anders Eidem, Merete Tangstad, Jens Davidsen

"During excavations of submerged arc furnaces producing silicomanganese, silicon carbide (SiC) has been found. Contributing to the size of the inactive area of the furnace, the active area of the furnace where reactions occur will decrease, thus reducing the potential for pre-reduction in the furnace.This work studied the formation of SiC from the liquid-solid reaction between slag, metal, and metallurgical coke. Slags and metals with different levels of silica (S1O2) and silicon (Si) have been studied. The slag and metal has been heated together with coke, and the samples investigated by microprobe. The results show that SiC was formed on the coke particle through reactions with both slag and metal. For the metal, the carbon most likely diffused through the SiC to react with Si in the alloy. SiC formation with slag is likely to go through the reduction of Si02 to Si.IntroductionToday, Silicomanganese (SiMn) is produced in submerged arc furnaces (SAF) by reduction of S1O2 and manganese oxides, mainly with metallurgical cokes. Typically, the tapped metal has a silicon content of 17 - 20 wt.%. To achieve higher levels of Si, the metal can be refined by adding off-grade silicon metal, yielding low carbon SiMn. [1]. What is believed to be SiC that has been found during dig-outs of SiMn furnaces producing high silicon alloy. It is possible that excess amounts of SiC in the furnace cause operational problems, since SiC will occupy furnace volume. As SiC accumulates, the active volume of the furnace will decrease, increasing the flow of material and gas in the active areas of the furnace. Formation of SiC is inevitable, so it is desired to keep the formation as low as possible. To be able to control the formation of SiC, one has to understand the basic mechanisms."

Jan 1, 2012

By G. E. S. Lima, J. V. B. Lemes, F. G. D. Machado, S. Monteiro, L. G. Pedroti, L. A. F. Fioresi, W. E. H. Fernandes, R. C. S. S. Alvarenga

With advances in industrial processes, new products have emerged and become essential in everyday life. These activities generate different types of wastes, which can be harmful tothe environmentif not properly disposed. Having this problem in sight and considering the importance of concrete in the construction industry, this study analyzes the behavio of Reactive Powder Concrete (RPC) with addition of granite processing waste. Scanning Electron Microscopic (SEM) tests, compressive strength and Young’s modulus tests after 1, 3, 7 and 28 days of production and shear and flexural strength after 28 days of production were performed during the analysis. The results indicated that incorporation of this residue into RPC does not affect its performance. RPC was still able to present high compressive and flexural strength.

Mar 1, 2017

By D. M. Fermino, C. G. Bastos Andrade, M. G. Fernandes, F. R. Valenzuela-Diaz

Treatments with high concentration solution of inorganic acid at temperatures under boiling point are a usual method for clay minerals structure modification. For many industrial uses bentonites must be cleared of impurities. In the present paper, a sample of Brazilian bentonite from Vitoria da Conquista, Bahia was modified by mild acid attack using hydrochloric acid under moderate conditions (90 °C, reaction times of 1, 6, 12, 18 and 24 h in close reactor, concentration of the aqueous solution of hydrochloric acid 1.5 M, acid solution/clay ratio of 1 g/10 mL). The attacked samples were characterized by CEC, XRF, SEM, EDS and Stereomicroscopy. The purpose of these attacks is to reduce the concentration of impurities with minimal damage in clay minerals structure. The modified bentonite presented good results and tends to be a good economic and environmental alternative to manufacturing products with high added value such as polymer/clay nanocomposites, cosmetics and medicines.

Mar 1, 2017

By Jun Chang, Jin-hui Peng, Jing Chen, Li-bo Zhang

The leaching of indium from refractory zinc oxide flue dust(ZOFD) is attempted to utilize microwave sulfating roasting process, followed by water leaching. The ZOFD and roasted product were characterized by XRD and SEM/EDS analysis. The effects of various roasting parameters, such as roasting temperature/duration, the proportion of sulfuric acid, as well as the leaching parameters such as the leaching duration and liquid/solid ratio, were assessed. The results indicate that nearly 97% of indium could be leached under the following conditions: mass ratio of concentrated sulfuric acid to ZOFD to be 0.5, roasting temperature of 150 ℃ and duration of 1.5 hours; while the optimal leaching conditions hold at temperature of 25 ℃ for 1 hour, with 4:1 of liquid/solid ratio. The indium leaching rate by the microwave roasting increased by 8% as compared with the conventional roasting process under identical conditions.

Jan 1, 2015

By M. Ramprecht, M. Wu, A. Kharicha, A. Ludwig, H. Holzgruber

"The influence of the frequency of AC power supply on the magneto-hydrodynamic during the electroslag remelting process is studied. The focus is on the electrodynamic field and its resulting mechanical effects on the flow and liquid interfaces. The possible influence of the electrochemistry on the droplet formation is qualitatively discussed.IntroductionThe electroslag remelting (ESR) process is a secondary melting technique which can be used for a variety of metals and alloys, provided appropriate fluxes (slags) and melting parameters are employed. The ESR process is presently operating mostly with AC current of about 50 Hz. However for reasons primarily of inductive losses in the electric circuit, furnaces for ingots larger than 1 m, use or are projected to use current of very low frequency (< 5 Hz). Effects of lower frequencies (2.5-5Hz) on macrostructure and non-metallic inclusions were recently studied by Chang [1]. Most of investigations were performed either with DC power or with AC of 50-60 Hz [2-4]."

Jan 1, 2012

By K. S. V. L. Narasimhan

Recently developed high energy permanent magnets SmCo5, Sm2Co17, Nd2Fe14B offer an interesting study of magnetic phenomenon. This publication discusses briefly the evolution of these magnets and the origin of the coercive force. Atomized SmCo5 coarse particles (150 to 300 microns) exhibit unusually large coercive force contrary to the experience in cast alloys. A brief discussion of utilization of these magnets into devices is also presented.

Jan 1, 1992

By Yongyong Gong, Qijie Zhai, Zhichen Zhang, Qixin Li, Zhishuai Xu

"Microstructure of semisolid slurry of Al-4.5wt.%Cu alloy was investigated with pulse magnetooscillation (PMO) treatment, the results showed that the PMO treatment can refine the crystal structures of Al-4.5wt.%Cu alloy significantly. The discharging frequency of PMO had a great effect on the solidified structure transformation of semisolid slurry of Al-4.5wt. %Cu alloy, and the primary a-Al particles become much finer and rounder with an increase of discharging frequency. However, over a certain discharging frequency, the grains of primary a-Al become coarse.IntroductionOver the last decade, a lot of attentions have been paid on metal rheoforming process [1-4], since it has higher mechanical properties of formed components, strength to weight ratio and age hardenablity. Nevertheless, semi-solid forming is always performed at high solid fractions (40%-60%), so it has the limitation of viscosity, a tends to be difficult to pour semisolid slurry into the hole of the shot sleeve. Therefore, a series of novel semi-solid slurry preparation methods and rheoforming techniques have been invented, such as, semisolid vibration treatment [5], rheocasting [6], pulsed magnetic field process [7], annulus electromagnetic stirring [8], via ultrasonic vibration process [9], equal channel angular extrusion (ECAE) process [l0] and straininduced melt activation (SIMA) process [11].The electromagnetic field is characterized by its effective grain refinement, green, convenient manipulation and without contamination of melt. The mechanisms of dendrite was fragmentation by electromagnetic field have also been largely proposed [12-14]. The broken dendrite arms then undergo a coarsening process to provide the globular structures and obtain much finer and rounder a-Al particles. When compared with other external electromagnetic techniques, Pulse Magneto-Oscillation (PMO) has obtained more fuvors, owing to narrower pulse width and much lower energy consumption. Furthermore, the PMO treatment can reach finer grains with shorter time treatment [16, 17]. This work aims to study the effects of different discharging frequency ofPMO treatment on the microstructure transition of the semisolid slurry of Al-4.5 wt.%Cu alloy."

Jan 1, 2014

By B. Mishra, W. A. Averill

"The application of various hydrometallurgical, pyrometallurgical and electrochemical processes in the extraction, purification and production of radioactive metals as well as the use of various materials, ego metals and alloys, ceramics, polymers, etc. in the process, construction and handling equipment in the nuclear industry has generated a large stockpile of radioactively contaminated waste material and scrap metal which can not be directly discarded, recycled or considered for long-term storage due to its volume and potential hazards, without the separation of radionuclides. This paper reviews the emerging methods that have been investigated and suggested for dealing with some of these wastes and scrap material.The separation technologies studied for the recovery of radioactive components from the pyrometallurgical and electrochemical processing wastes have been discussed in details with results from some of the recent theoretical and physical modeling work as well as the data obtained from the actual waste treatment. Specific processes shall be described in terms of its advantages and limitations. These emerging separation technologies are being considered by the US Department of Energy as alternatives for dealing with the issues of environmental management [EM] and decontamination and decommissioning [D&D].IntroductionThe high temperature carbothermic or metallothermic smelting reduction methods for metal production are associated with the generation of significant quantity of waste as slags, flue dusts, sludges, residues, effluent salts etc. Certain hydrometallurgical processes also generate lots of aqueous waste due to the inherent nature of the technique. Also, the gas-based reduction processes are not applicable to many stable metal compounds, such as alumina, titania, beryllia, lanthanide and actinide oxides, etc. due to thermodynamic considerations. All these methods cause substantial environmental hazard. There is a need to develop alternative processes which have low waste or ideally a ""zero-waste"" generation.Pyrochemical processes using molten salts provide a unique opportunity for the extraction and refining of many reactive and valuable metals either directly from the beneficiated ore (aluminum, beryllium, neodymium, plutonium, uranium, etc.) or from other process effluent that contain reactive metal compounds. The processes reduce metal compounds electrolytically (A12O 3 and BeCI2) on a carbon anode or by calciothermic reduction (Po, Nd). The by-product, in the latter case, is a calcium oxide saturated halide salt. The waste-treatment to recycle the halide has to be done as a separate step or stored as a contaminated waste. A successful separation technology can provide a new insight to the waste minimization strategy for the nuclear industry."

Jan 1, 1996