By W. F. Drinkard

Many in the environmental movement have focused on this element. But, nothing they or anyone does will change the amount of arsenic in the world. This report is on actual commercial plants that we developed and operated to recover or stabilize arsenic values from metallurgical dusts from gold and copper pyro operations and arsenical gold bearing ores. When they were available gold and copper values were recovered. Our experience in arsenic extends over thirty years. My first corporation, Mineral Research & Development Corporation was the first in North America to manufacture the then new CCA (copper-chrome-arsenic) wood preservatives. This class of wood preservatives proved to be so effective that it made wood into an entirely new material of construction. It is not uncommon for wood properly treated with arsenical CCA preservatives to last for thirty; forty, and sixty years. Over a hundred years have been projected in some field tests. Hundreds of thousands of trees have been saved. Millions more trees would have been saved had environmentalists not decided that their arsenic phobia was more important than trees. There are several variations of CCA. The most popular is CCA-C. Its formula is: CrO3 . . . . . . . . . . . . . . . . . . . 47.5% CuO . . . . . . . . . . . . . . . . . . . 18.5% As2O5 . . . . . . . . . . . . . . . . . 34.0% Until recent restrictions were placed on the consumption of arsenical wood preservatives, annual consumption in North America was about 150,000,000 lbs./yr. About 64,500,000 of arsenic as the pentoxide was safely consumed this way. World CCA consumption has been about double the above figures or 300,000,000 lbs. as 100% CCA and 129,000,000 lbs/yr as As2O5. Close to 100% of all the arsenic used in wood preservatives is derived from gold or copper processing. The valence of arsenic required for CCA wood preservatives and many other markets is the same valence that is required for stabilization. The economic challenge is how to get there. We have built and operated eleven plants to oxidize arsenic trioxide to its pentavalent form. Most of these have been classic in that they used a common oxidants such as hydrogen peroxide or nitric acid to achieve this.

Jan 1, 2005

By Liang Yu, Yuhua Li, Yuanchi Dong

"High alumina slag, with alumina normally more than 15 pct, is encountered with blast furnaces in China because of high alumina/silica ratio in iron ore as well as sinter and high ash content in coke for cost reason. High alumina slag with high viscosity and high liquidus temperature would lead to higher slag volume and thereby, furnace productivity. In the present work, liquidus temperature of high alumina slag, based on Meishan factory, Baosteel China, were investigated. A liquidus temperature model was introduced in the present work based on basic physical chemistry theory and focused on the chemical composition area used in Meishan factory(pct): Al2O3 from 14 to 17.5 and MgO from 8 to 12, so that the blast furnace slag could be designed for optimum blast furnace performance.IntroductionBlast furnace slag composition[1] has very important bearing on its physicochemical characteristics which affects smoothness of operation, slag handling, coke consumption, the degree of desulphurization, hot metal productivity and its quality etc. The slag properties which affect most are liquidus temperature, viscosity, sulphide capacity and alkali capacity. Variation of these slag characteristics with composition and temperature has been a field of active researches as these its great influence on the blast furnace operation. In the early years, most of these studies were carried out over low alumina blast furnace slags with alumina normally less than 15 pct. High alumina slag was first introduced in India because of its high alumina/silica ratio iron ore as well as sinter and high ash content in coke[2]. And then this problem becomes common as higher alumina/silica ratio iron ore imported and used [2-5]. The most important problem caused by high alumina content is liquidus temperature and then viscosity of the slag.Generally speaking those reported works [2-5] investigated a pretty wide range of chemical compositions and then obtained complex model, respectively. In fact, every factory has its own interest because of different resources. For example, the Al2O3 content from 20% to 30% pct was studied in Tata Steel India [2], but it is too high for Baosteel Meishan. A very lower percentage of alumina content, 14-18 % pct, was mainly used."

Jan 1, 2008

By Fumitaka Tsukihashi

Phase diagrams of the CaO-SiO2-FeOx-MgO, Al2O3 systems are necessary for the analysis of copper smelting reactions and sintering process of iron ore. The effect of MgO and Al2O3 addition on the liquidus of the phase diagram of the CaO-SiO2-FeOx system at low oxygen partial pressure was observed. The liquid phase area changed by the addition of MgO and Al2O3 with a changing oxygen partial pressure from 10-8 to 10-3 atm (10-1 to 102 Pa) at 1573K. The effect of Fe3+/Fe2+ ratio on the melting mechanism is discussed.

Jan 1, 2003

By Ludwig Hermann

"Phosphorus is required by every cell of living organisms and essential for plant growth. It is a non-renewable resource that must be mined from natural deposits, going gradually into depletion. Abundant secondary resources are available in sewage sludge and meat and bone meal, with the highest exploitable P concentrations in ashes that remain from their widely used combustion with energy recovery. ASH DEC has successfully removed heavy metals and transformed sewage sludge ash into a marketable P fertilizer by application of a thermo-chemical treatment process. Pilot scale investigations in which ash was treated proved that generally heavy metal limits required by fertilizer legislation can be attained. To achieve a high P availability for crops – an essential fertilizer quality feature – was a more challenging R&D task. Our presentation demonstrates the scientific approach and R&D results that lead from assessment of market requirements to licensed products.IntroductionPhosphorus (P) is required by every cell of living organisms. It is one of the major elements for plant nutrition and therefore essential for crop production. P supply in plant nutrition depends entirely on external inputs into soils [1]. This is achieved by P-fertilizers deriving from rock phosphate deposits that are gradually going into depletion. Serious prognoses anticipate that rock phosphate will be the first low running resource in the world [2]. In the EU, last year 2.530 kt of phosphorus (P2O5 in fertilizers) was consumed and only 313 kt (P2O5 in rock phosphate) was mined. Since 2007, rock phosphate prices have increased by 500% because of a tight supply situation [3].For these reasons, P recycling is becoming an increasingly important issue. Suitable secondary raw materials with regard to their high P-content and abundance are sewage sludge and meat and bone meal. In the EU 989 kt P2O5 are accumulated annually in theses materials, of which 632 kt P2O5 are permanently lost to landfills and other forms of disposal. The main reasons for their limited recycling are concerns on heavy metal contents and organic pollutants that may incite health hazards. As an additional shortcoming, the availability of P from these materials to plants is poor and storage and transportation are problematic issues [4, 5]."

Jan 1, 2008

By I. A. Ibrahim

Ilmenite, in its natural form, is an inactive mineral from which the selective removal of iron is rather difficult. The reactivity of ilmenite. so that it can be leached with dilute hydrochloric acid, can be enhanced by chemical reduction in solution using a suitable metal as a reducing agent. The present paper aims at the evaluation of an Egyptian ilmenite ore for the production of synthetic rutile by direct leaching with hydrochloric acid in presence of iron powder. In this process, the titanium and iron contents are dissolved; meanwhile, the dissolved titanium is hydrolyzed and re-precipitated leaving mainly iron in solution. Leaching conditions were optimized to obtain less iron in the final solid product. Addition of sufficient amount of iron powder during leaching reduces the dissolved Fe3+ to Fe2+ and reduces the dissolved Ti4+ to Ti3+. The creation of Ti3+ in solution is assumed to have a role in dissolving the ferric iron and hence increasing the reactivity of the ilmenite ore. Synthetic rutile of about 90% TiO2 and 0.77% Fe2O3 was obtained from ore with a grain size 100% passing 200 mesh and a 5-hour leach time with 20% HCl at boiling temperature (110°C) and 0.11 g iron powder / g ore.

Jan 1, 2003

By Guanghui Li

In the paper, the recovery technology of gallium from zinc-leaching residue by cold-bonded coal-based direct reduction process following magnetic separation was developed. The results show that the scattered metal Ga can be concentrated obviously after the reduction of zinc-leaching residue briquette and magnetic separation of reduced product. At the same time, the volatilization of Zn in the residue is enhanced during the reduction. When the residue, bear¬ing 18.60% Zu.21.18% Fe and 527 g/t Ga, was reduced with coal at 1100°C for 150 min, the results of Zn volatilization of 9842% and Ga recovery of 89. 10% were obtained in reduction. After magnetic separation of the reduced product, the concentration of Ga in sponge iron is 2164 g/t, and the separation recovery of Ga reaches 92.42%. The enriched mechanism of Ga during reduction -separation process was studied by using electron microscope, scanning elec¬tron microscope, energy spectrum and mineralogical analysis. The investigations show that there is no formation of independent phase of Ga during reduction process. The Ga occurs mainly in metallic iron phase (the concentration of Ga in metallic iron phase is 0.04%-0,4%), in addition, there exists a little Ga in poorly crystalline sulphide (o.08%-0./5Y& Ow). But Go does not exist in most of glass and silicate phase. The affinity of Ga for metallic iron is the enrichment basis of Go in reduction, and it is also in favor of recovering Go during magnetic separation. Key Words: Gallium Zinc-leaching Residue Cold- Bonded Direct Reduction

Jan 1, 2003

By Bingguo Liu, Daifu Huang, Jinhui Peng

"The conditions to prepare U3O8 by calcination from ammonium diuranate were optimized, and the response surface design method was applied to analyze the influence on the total uranium and U+4 of calcination temperature, calcination time and mass of sample. A quadratic equation model for the total uranium and U+4 of U3O8 was built and the effects of main factors and their corresponding relationships were obtained. The analysis of variance shows that calcination temperature and calcination time significantly affected the value of total uranium and U+4 of U3O8. The optimal calcination conditions were as follows: calcination temperature 931.83 K, calcination time 24.32 min and 43.89 g. Under these conditions the value of total uranium and U+4 of U3O8 was 84.78% and 28.02%, respectively. The validity of the model was confirmed experimentally and the results were satisfactory.IntroductionNuclear energy is clean, effective, and a sustainable from of energy. It plays an important role in overcoming the impending global energy crisis, and in reducing energy vulnerability. In addition, nuclear energy is a possible cheaper and cleaner source of energy compared to fossil fuels, with no not really, mining of uranium produces CO2 contribution to green house gases [1]. Uranium dioxide, one of the most important fuel pellets used as nuclear fuel in light water reactors, is manufactured by calcining ammonium diuranate to triuranium octaoxide, followed by its reduction to uranium dioxide using cracked ammonia at 700°C [2]. Earlier attempts to optimize the important calcination process through several common techniques have not yielded desirable results [3]. These techniques either rely on the classical one parameter at a time approach that ignores the combined interactions between physicochemical parameters, or are theoretical in nature. Furthermore, these techniques also require large number of experimental data to be generated [4]. In order to produce triuranium octaoxide in an optimized manner, which considers the interaction of different process parameters [5], there is a need to adopt a multivariate statistical technique."

Jan 1, 2011

By Lilong Zhu, Shaoda Zhang, Qian Wang, Shengping He

The effects of ZrO2, Y2O3 and Sc2O3, which are transition metal oxides, on the melting temperature, viscosity at 1300 °C, and break temperature of three mold fluxes (two weak-reactive type and one non-reactive type) designed for the high manganese and high aluminum steels, and one another conventional CaO-SiO2 based mold flux is studied. The results indicate that the melting temperature and viscosity increases slightly, and the break temperature increases dramatically with the addition of ZrO2, Y2O3 and Sc2O3 content in the conventional CaO-SiO2 based mold flux system. While, the addition of ZrO2, Y2O3 and Sc2O3 in the weak-reactive or non-reactive mold flux systems has a negligible in fluence on the melting temperature, viscosity and break temperature, suggesting that these transition metal oxides are possible to regulate radiation heat transfer without changing the basic properties of mold fluxes.

Mar 1, 2018

By Zhihao Yue, Honglie Shen, Yahui Teng, Ye Jiang

"In this paper, manganous nitrate [Mn(NO3)z] was used to assist the etching of silicon wafer in hydrofluoric acid (HF) for the antireflective application, and alumina (Al2O3) layer was deposited on the surface of the etched sample by atomic layer deposition method for further antireflection. The surface morphological and compositional studies of these samples were performed by scanning electron microscopy attached with an energy-dispersive X-ray spectrometer. The surface reflectance measurements were carried out using UV-Vis-NIR spectrophotometer. Binary structures of pyramids and nanopores were obtained by etching the alkaline textured monocrystalline silicon wafer in HF and Mn(NO3)z mixed solution for not more than 15 min. But excessive increase of etching time of up to 30 min resulted in the whole destruction of pyramids. The average reflectances of the 5-min-etched sample before and after being coated with 75-nm-thick Al2O3 layer are 4.62% and 3.47% in the range of 200-1000 nm, respectively.1. IntroductionAs we know, the reflectance of silicon wafer after being sliced is so high that the maximal photoelectric conversion efficiency of silicon based solar cells is limited. Therefore, alkaline texturization process was used for silicon solar cell in industrial production. But the reflectance of this alkaline textured wafer is still greater than 10% and this process can only be used for monocrystalline silicon solar cell."

Jan 1, 2013

By Christopher B. Vierrether

Reflected light microscopy, scanning electron microscopy, and electron microprobe analysis have been used to determine the mineralogy, phase percentages, grain sizes, textures, and partitioning of cobalt and nickel in two cobalt-nickel rich mattes. These mattes were prepared by submerged bath smelting from a flotation cobalt-nickel concentrate containing 4.8% cobalt and 5.1% nickel. The concentrate was derived from lead-zinc-copper ores of the Viburnum Trend, southeast Missouri. Eleven discrete phases have been distinguished in the matte samples, three of which contain significant cobalt and nickel. The phases are cobaltpentlandite ((Co,Ni,Fe)9S8), cobalt-bearing marmatite ((Co,Fe,Zn)S), shandite (Ni3Pb2S2), bornite (Cu5FeS4), galena (PbS), magnetite (Fe3O4), pyrrhotite ((Co,Ni,Cu,Fe)1_xS), chalcocite (Cu2S), CuPbS phase, metallic copper, and metallic silver. Cobaltpentlandite and cobalt-bearing marmatite- occur in coarse grains (50 µm) that would separate readily during grinding, but shandite contains small (5 - 10um), abundant inclusions of pyrrhotite and bornite.. Some mineralogical variations between the two matte samples were due to differing degrees of oxidation during smelting,

Jan 1, 1988

By Singareddy R. Reddy, Ramana G. Reddy

"The Margules equation is used for interpreting excess Gibbs energy of several ternary systems. An expression for the activity coefficient of a dilute solute, 2(oxygen), in a binary solvent 1-3 is derived. It is used to calculate the logarithmic activity coefficient of oxygen in Pb-O-Gu, Pb-O-Bi, AgO- Sn, Pb-O-Sn and Ag-O-Pb metallic systems. Self interaction parameter of the solute is derived from the partial Gibbs energy of solute using constant compositional path. The derived equation is used successfully to deduce the self interaction parameter of oxygen in Pb-O-Gu and Pb-O-Bi metallic systems. The predicted thermodynamic parameter data i.e activity coefficient and self-interaction parameters are in an excellent agreement with the experimental data and also our predictions are far more accurate than the predictions made by other models.1 IntroductionThe nature of solute interactions such as oxygen, nitrogen and sulfur with the metallic solutions are important for a number of chemical and metallurgical processes. Several theories [1-23] have been developed to evaluate fundamental thermodynamic properties of solutes constituting two elements. The activity of solutes has been calculated using statisticalor quasi- chemical approach.Wagner's [4] Ideal Solvent Model is based on one energy parameter to describe the compositional dependencies of the activity coefficient of nonmetallic solutes such as oxygen in binary metallic solutions. This model depends on a constant energy of interaction for the exchange of atoms from the coordination shell of an oxygen atom to the shell of an interstitial site and cannot account for properties of strongly interacting systems [4]. Therefore, several attempts have been made to improve the Wagner's model for the strongly interacting systems. [10-16]."

Jan 1, 1996

By S. Tandon

Equilibria studies of selenium distribution for sodium-borate slags were initiated at 1473k under reducing condition as a function of slag composition and alloy composition. The Se distribution coefficient (% Se in slag/% Se in metal) increased from 0.4 to 2.9 with increase in basicity (0.53 to 0.86) for Cu-0.446% Se alloy. However, the results are not very useful from industrial application viewpoint. Therefore, in order to improve the distribution of Se, CaO (10% to 50%) was added to the sodium-borate slag of basicity 0.864. On addition of 502 CaO, the distribution coefficient increased roughly by 100% for slag composition - 44.5% Borax, 22.2% Na2C03, 33.3% CaO and Cu-0.44677 Se alloy. Further, the value of this distribution coefficient has been found to increase by an additional 80% on addition of 20% CaF2 to the above slag for all Cu-Se alloy compositions. Also with increase in initial concentration of Se, the distribution coefficient has been noted to increase.

Jan 1, 1992

By Laila A. Guirguis

Impurities are removed from crude phosphoric acid (57.75% P2O5) with a mixture of low and high molecular weight alcohols, one of which is hydrophilic and the other is hydrophobic i.e. methanol and hexanol. In a single stage, the phosphate values segregate to the high molecular weight alcohol fraction and the impurities segregate to the low molecular weight alcohol fraction. The optimum ratio for the extraction is found to be 0.5 part methanol, one part impure acid and four parts hexanol where an extraction percent of more than 95% is achieved. Re-extraction of the phosphate value from the solvent is obtained by 6% phosphoric acid and the different factors affecting the re-extraction process have been studied. Finally, the purified acid is concentrated under reduced pressure and passed through activated carbon column, whereas the alcohols are re-circulated. The produced phosphoric acid was found to be in good match with the international specifications of food grade quality acid. A technological flow sheet is elucidated.

Jan 1, 2006

By Xuyang Liu, Xuewei Lv, Chenguang Bai, Meilong Hu

"The electro-deoxidation process for ilmenite concentrate in molten salt was studied by cyclic voltammetry and AC impedance spectroscopy. The results from cyclic voltammetry are consistent with those of AC impedance spectroscopy. The results showed that the electro-deoxidation process for ilmenite concentrate consists of two steps. In the first step, Fe is reduced from the ilmenite concentrate. The second reaction is the decomposition of TiCh. CaTiCh is an intermediate product. At low voltage, the electrochemical reaction is the main step. With the increasing potential, the diffusion of ion is the main rate controlling step for the electro-deoxidation of FeTiO3.IntroductionTitania and titanium-rich products are mainly prepared from ilmenite concentrates (FeTi03), which contain about 40%-60% T1O2 after ore dressing and other physical or chemical processes [1]. At present, the main methods to prepare titania are the sulfuric acid process and the chloride process, but the sulfuric acid process consumes a large amount of sulfuric acid and the materials requirements for the chloride process are strict [2], Since the Electro-Deoxidization in Molten Salt (FFC) method was put forward in 2000, many researchers have successfully extracted the metal and alloys by this method, such as Ti, Cr, Tb, Si, Al-Si, TiV, FeTi, etc. [3-7], FeTi alloy is a typical hydrogen storage material, and because of its favorable properties, the preparation of FeTi alloy has become a hot research topic [7-9]. However, the mechanism of electro-deoxidization has not been studied thoroughly [10-11]. Therefore, in this study, the electro-deoxidation process for titanium concentrate was investigated by electrochemical methods, and the study makes a contribution to improving the current efficiency of the electrolysis."

Jan 1, 2012

By Wei Liu

A new process for extracting cadmium from the electric precipitated dust produced by ISP process was studied. A leaching rate of 89.1% of cadmium was attained by leaching the dust with NH3?H2O-(NH4)2SO4 system under the best leaching conditions: ratio of liquid to solid(l:s)=2.5, c(NH3):c(NH4+)=3:5, total concentration of ammonium and ammonia=8 mol?L-1, leaching time= 1.5h, temperature=35. The most troublesome impurity of lead could be deposited from the leached out solution automatically after put it static more than 15h when the total concentration of zinc and cadmium was up to 45gL-1 , and the final concentration of lead was 0.0047 gL-1, which meant 99% of it was removed. Metallic cadmium which contained cadmium more than 99% was prepared by electrowinning under the conditions: current density=750Am-2, total concentration of Cd2+ and Zn2+>25gL-1. The current efficiency was about 87% and the energy consumption for every ton of cadmium was about 548KWht-1. Main impurities of the metallic cadmium were copper and zinc and all of they could be got rid of in the following pyrometallurgical refining step.

Jan 1, 2006

By Fiseha Tesfaye, Pekka Taskinen

"A thermodynamic study of the equilibrium phase assemblage AgBi3S5-Bi2S3-S was made by an EMF-technique, using the RbAg4l5 solid electrolyte. The ternary phase was synthesized from the pure Ag2S and Bi2S3 in an evacuated silica ampoule and grinded into powder and mixed with appropriate compositions of B12S3 and S, in a series of experiments, for pressing in to pellets. The pellets were assembled to form the galvanic cells Pt (-) | Ag ] RbAg4ls | AgBi3S5+ Bi2S3 + S + (C) I Pt (+). The EMF-measurements were made in the temperature range 299 - 460 K.In this paper, thermodynamic functions of the ternary phase AgBi3S5 (pavonite) have been determined. The agreement between the obtained results and the literature values were established.IntroductionThe complex group of ore minerals constitutes from trace amounts to a major proportions of sulfosalts. Although the sulfosalts rarely form massive ore bodies, they are commonly associated with rich sulfide ore minerals for the base and precious metals and widely distributed in a metal poor sulfide minerals [1]. For instance, Ag-bearing sulfosalts are encountered in ore minerals for the production of the base metals and are common sources of silver. Nevertheless, thermodynamic properties of the sulfosalts are poorly known.Reliable thermochemical data are essential for quantitative modeling of the chemical behavior of the sulfosalts in equilibrium with sulfides, which in turn would promote the optimization of complex minerals treatment and extractive metallurgy of the valuable metals."

Jan 1, 2012

By D. T. Smith, L. M. Hsiung, J. J. Schmitt, J. W. Golz, R. L. Lankey, H. N. G. Wadley, J. Z. Zhang, B. L. Halpern

"The microstructure and mechanical properties of Al/AI2O 3 metal-oxide nanolaminates fabricated by' a novel Jet Vapor Deposition (JVD) process at substrate temperatures of ~25° and -250°C have been investigated using transmission electron microscopy (TEM) and nanoindentation methods. The thickness of the oxide layer was held constant between 2 and 5 nm, whilst the Al layer thickness was systematically varied from -3 to -50 nm. Continuity of the Al layers was significantly improved when the nanolaminates were deposited at an elevated substrate temperature (-250°C). The yield strength of the nanolamintes with Al layers greater than -25 nm follows a Hall-Petch type relationship, whereas that of the nanolaminates with Al layers less than -25 nm is better predicted by a Koehler-Lehoczky strengthening model. IntroductionAluminum-aluminum oxide (presumably A12O3) nanolaminates have been recently fabricated using a novel Jet Vapor Deposition (ND) process developed and patented by Jet Process Corporation [1-4]. ND uses sonic, high purity helium (He) gas jets to entrain atomically dispersed vapor and deposit films. It is of interest here because it can deposit multilayered structures (laminates) inexpensively at high rates. Materials with a thin, multilayer structure are of interest because they potentially offer novel mechanical and physical properties [5]. Koehler in 1970 used an image force model to investigate the strength of laminated materials and proposed the use of alternating layers of high and low shear modulus metals to produce high strength composite materials [6]. He predicted that dislocations would have to overcome a large repulsive image force in order to move from metal layer B of lower shear modulus (uB) into metal layer A of higher shear modulus (uA)' The image force (F) is given by the relation:"

Jan 1, 1994

By Rui Mao, Ke-Xin Nao, Jian-Liang Zhang, Xiang-Nan Xu, Meng-Fang Wei

"In this research, fundamental characteristics of dust and sludge containing iron from the dusting system of sintering process, blast furnace, oxygen converter and rolling process in steel enterprise were studied by chemical analysis, X-ray diffraction analysis, optical microscope analysis, scanning electron microscopy analysis, particle size analysis and other analysis means. Development direction of resource utilization for dust and sludge containing iron from steel enterprise was put forward on the basis of above study.IntroductionDust and sludge containing iron for steel enterprise mainly come from the dusting system of sintering process, pelletizing process, blast furnace, oxygen converter, rolling process and other related process. Iron content of dust and sludge is between 30% and 70%, and they also contain certain content of carbon, calcium oxide, magnesium oxide and harmful elements [1-3]. Output of dust and sludge is determined by raw materials conditions, technological processes, equipment configuration and management level. Dust output in sintering process accounts for about 2% to 3% of the sinter production, while dust and sludge from iron making and steel making process respectively take up 3% to 4% of hot metal and crude steel production, and the solid waste from rolling process accounts for about 0.8% to 1.5% of the output of rolled products [4,5]. Dust and sludge contains Fe, CaO, MgO, C and other valuable resources, it will not only result in the waste of resources, but also cause serious pollution to environment ifthe dust and sludge are not recycled. China's crude steel production in 2012 is about 700 million tons and output of dust and sludge containing iron is nearly 60 million tons, so, it is of great significance to have a resource recycling for dust and sludge containing iron from steel enterprise."

Jan 1, 2014

By Min Chen, Lei Xu, Liang-yu Jin, Xue-liang Yin

For the purpose to reduce the high cost and heat storage loss of Al2O3-MgO bricks used as ladle linings, Al2O3-MgO-CaO bricks with lower theoretical density were fabricated and the densification behavior as well as mechanical property of this refractory was investigated. With addition of CaO, the initial sintering temperature of Al2O3-MgO refractory was decreased from 1300 to 1100°C associated with the expansive formation of CA2, and the compressive strength was also enhanced owing to the formation of bond linkage between CA6 and spinel. At high temperature, brick with 4% CaO content showed poor sinterability with high porosity because of the formation of platelet structure of CA6 grains, whereas brick with 8% CaO content was well sintered with higher relative density but lower bulk density than Al2O3-MgO brick, indicating that the densification as well as lightweight of Al2O3-MgO refractory was effectively promoted.

Jan 1, 2015

By Shadia J. Ikhmayies

SnO2:F/CdS:In bilayers were produced by the spray pyrolysis technique on glass substrates. The structures were characterized by recording and investigating their transmittance curves, I-V plots, X-ray difractograms (XRD) and by observing their scanning electron microscope (SEM) images. From the I-V plots it was found that the SnO2:F forms an ohmic or quasi-ohmic contact with CdS:In. XRD patterns show the polycrystalline nature of the films and show that there is a small shift in the position of the (200) line of SnO2:F without the appearance of new peaks. The morphology of the structures are compared with those of SnO2:F alone and CdS:In alone on glass substrates.

Jan 1, 2009