By M I. Pownceby, A Torpy, C Johnson, N C. Wilson

To extract uranium from low-grade, calcrete-hosted uranium (CHU) ore is challenging owing to the presence of carbonate and swelling clay gangue minerals that require an alkaline lixiviant to be used. Western Australia possesses ~75 000 U3O8 t in CHU resources. Improvements to alkaline leach extraction practices would improve the economic potential of these deposits.A column leach study of CHU ore was run for 105 days using an alkaline carbonate-bicarbonate lixiviant. The uranium content of the liquor plateaued after 75 days at ~275 mg U/L; the calculated maximum solution capacity was 800 mg U/L. Spiked peaks and troughs were seen in the data set beyond the 60th day, where concentrations ranged from 220 - 290 mg U/L, indicating possible cyclic uptake and loss of uranium from the solution.Pristine and leached ore samples were geochemically analysed and mineralogically characterised at high resolution using a field emission gun-electron probe micro-analyser (FEG-EPMA). Results showed that leached ore samples from the top of the column contained less carnotite than pristine ore. In contrast, leached ore samples from the column base contained regions with more carnotite than pristine ore, indicating precipitation. Three carnotite grain micro-structures were identified in the leached ore; fan-spherulite, granular and core-shell cubes, with evidence for multiple growth phases.Evidence of carnotite precipitation was seen at the edge of and in pore spaces within montmorillonite and dolomite grains. The point of zero charge of both minerals is lower than the pH of the lixiviant (pH 10.8), thus the mineral surfaces are negatively charged and would not attract UO2(CO3)34- ions out of solution. Similarly, the decrease in the uranium content of the lixiviant is not attributed to super-saturation, as this was unlikely to have been achieved. Work is ongoing to understand the reason for carnotite precipitation and the fluctuations in the lixiviant uranium concentration that are seen.CITATION:Johnson, C, Pownceby, M I, Wilson, N C and Torpy, A, 2013. Microscale characterisation of pristine and processed ore - implications for leaching calcrete-hosted uranium ore, in Proceedings The Second AusIMM International Geometallurgy Conference (GeoMet) 2013 , pp 303-316 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Sep 29, 2013

By Miezitis Y

A weak airborne radiometric anomaly was examined in the field and the presence of uranium confirmed. Rotary-percussion drilling showed the presence of uranium but a subsequent programme of diamond and rotary percussion drilling indicated that the concentration of uranium was uneconomic. Within the tufts and volcanics of the prospect the uranium existed as uranyl phosphates within the oxidized zone. Geological mapping and the diamond drill core showed that the Stag Creek Volcanics are part of the Lower Proterozoic Masson Formation, probably with member status, rather than the expression of an Archaean basement ridge. This change in the interpretation of the fundamental structure of the Pine Creek Geosyncline has led to a reexamination of the stratigraphy and to suggestions which differ from the current concept.

Jan 1, 1977

By Hayward SB, First DM

The Maragorik Prospect represents a partially eroded Pliocene acid sulphate style epithermal gold system hosted within the Sigule Volcanics and Riet Bed sediments which is inferred to have formed from a degassing porphyry body at depth. A regional sinistral rotation provided by transform faults associated with the opening of the Manus Basin imparts a dilational character to mineralised NE trending faults formed parallel to the Warangoi Graben. A controlled-source audio magneto-tellurics (CSAMT) survey has identified E-W trending buried conductors which may represent alteration formed within dilation zones. While some gold mineralisation occurs within vuggy silica at Palang Hill, the target is auriferous enargite (luzonite)-bearing breccias from the LK1 and Gureki areas.

Jan 1, 1991

By Kumar A, Mishra N. C

For each tonne of chromite ore mined in Sukinda, approximately ten tonnes of fine overburden material is generated. The overburden typically contains about 30 - 60 per cent Fe2O3, 0.3 - 1.1 per cent Ni, four to nine per cent Cr2O3 and 0.04 - 0.2 per cent cobalt and is being discarded leading to loss of valuable metals and creating environmental pollution. In order to take the advantage of presence of iron, nickel and chromium, the present studies advocate the utilisation of nickel lateritic chromite overburden for production of Ni bearing pig iron through blast furnace extracting maximum iron and nickel from the chromite overburden. The present paper deals mainly with the beneficiation of chromite overburden, sintering characteristics and thermodynamic studies. The beneficiation study shows that a beneficiated concentrate having Fe - 50 per cent and Ni -- 1.1 per cent can be achieved from chromite overburden having Fe - 30 per cent and Ni -- 0.7 per cent. Sintering studies have been carried out with bed height of 300 and 450 mm at a suction of 600 and 900 WG respectively. The results reveal that good quality sinter can be produced from chromite overburden concentrate with a basicity of about 1.0 and coke breeze consumption rate about 16 per cent. In all the experiments, Tumbler Index, Abrasion Index and Shatter Index was found to be in the range of 65 - 70, 4.5 - 5.5 and 85 - 90 respectively. The other parameters namely softening temperature, melt down temperature, reduction degradation test and relative reducibility have also been determined. A thermodynamic analysis has also been carried out to make a technological assessment of the process for the production of alloyed pig iron from chromite overburden in blast furnace which shows that it is possible to produce nickel bearing pig iron in blast furnace using the sinter up to 80 per cent. Techno-economic analysis reveals that this route will yield a substantial profit even after accounting for cost of beneficiation, extra coke, raw materials and extra slag produced.

Jan 1, 1999

Judicious placement of a range of geotechnical instruments was employed at the Tasmania gold mine, Beaconsfield, Tasmania, as a key strategy in the monitoring of rock mass conditions over the past four years. The range of instruments employed included vibrating wire stress-meters and hollow inclusion cells to monitor changing stress conditions, resistance wire and multipoint borehole extensometers to monitor the impact of stress changes on the integrity of the rock mass, and instrumented cable bolts and threadbar bolts to monitor the static and dynamic impact of rock mass changes on the installed ground control system. Initially the monitoring was of a qualitative nature, monitoring change from the time of installation. The value of the output was considerable when considered in relation to the ongoing seismic record which was also being monitored. It was clear from the seismic record and the monitoring results that stope blasting was the primary trigger for changing rock mass conditions. However, it was unclear how well observed behaviour was reflecting conditions anticipated by elastic numerical modelling. The latter had predicted significant stress increase in the near field of man-access footwall development. Qualitative monitoring and visual inspection did not support the modelling prediction, and this led to a program of quantitative measurement being undertaken. Measurement of the absolute stress condition in the backs of footwall development immediately adjacent to monitoring hollow inclusion cells provided the benchmark for tracking quantitative stress change. The program provided insight into the evolution of principal stress field magnitude and orientation in relation to rock mass change observed with extensometers and instrumented ground control elements, as well as providing a degree of calibration between the elastic numerical modelling and the virgin stress field. Calibrated monitoring data has also provided a useful benchmark for finite element modelling which is to be used for future mine-wide design.

Nov 25, 2010

The object of this talk is to bring before members the importance of the prospector and the' State Battery system to the wealth and prosperity of the mining industry in particular and the State of Western Australia in general, and to touch on the more important features.Customs plants of any sort are usually subject to a good deal of critioism, usually on the large profits made at the expense of the customer, etc., and this often clouds the real value of the work being done.Prospectors, on the whole, are a good class of men; they work under conditions and difficulties which would deter those less spirited. Food, water and mining supplies are often difficult to obtain and frequently have to be transported great distances. Their mining tools are usually of the most primitive type, yet during last year over 109,000 tons of prospectors' ore were handled by the State Battery system for 73,250 fine oz. valued in Australian currency at over £587,000, the value being 57/- per long ton at par.This production brings the State Battery system into fourth position amongst the producers of the State, the yield being exceeded by the Lake View and Star, Wiluna and the Great Boulder.In passing I might mention that these notes were written at the end of the year 1940, and the above figures were for the previous period. The figures for last year, 1940, were not quite so good, being 101,000 tons for approximately 60,000 fine oz., valued in Australian currency at £572,000.In spite of this drop the State Battery system maintained its position as fourth in order of gold output for the State.The extractions, as a whole, throughout the system, were 92·54%, made up of 68·86% by amalgamation and 23·68% by cyanidation. These figures, for a group of 20 plants treating widely different classes of ore, must be considered satisfactory. The total production since inception is over £11,000,000 in Australian currency.State Batteries are usually more or less of a standard design. Ore is reduced to about 2i in. maximum size before being sent to the bins. Challenge automatic feeeders control the feed to each mill unit, amalgamated copper plates collect the free gold. Corduroy strakes are used with some ores after amalgamation, but in only a few cases has this been found of any advantage to the customer.The pulp from the battery is sampled, after leaving the tables, with a "Tazewell" sampler and pumped to dams for subsequent cyanide treatment.The "Tazewell" sampler is a machine driven by the moving pulp; and takes about fifteen dips per .minute from such pulp through a slotted...

Jan 1, 1941

By J L. Mauk

The Favona low-sulfidation epithermal deposit in the Hauraki Goldfield is less than one kilometre southeast of the world-class Waihi deposit. The veins are hosted by Miocene andesite of the Waipupu Formation, have a total strike length of over 900 m, a vertical extent of at least 350 m and are on average 1-3 m wide. Individual veins have been traced for 200 m with vein widths up to 25 m. The dominant vein textures are massive, crustiform and colloform banded veins and vein breccias, with subsidiary textures including comb, zonal, flamboyant, lattice-bladed, ghost-bladed, microbotryoidal, feathery, ripple and dune, and mosaic. Quartz is the dominant gangue mineral in the veins at Favona. Accessory gangue minerals include pyrite, chlorite, adularia, illite, calcite, and apatite. Electrum is the only gold-bearing mineral and is associated with acanthite, tetrahedrite, pyrite, sphalerite, chalcopyrite, and rare galena. Whole rock geochemical analyses indicate that gold grades correlate with textures/vein types. The highest gold and silver grades are associated with vein breccias and banded veins, with the former containing 28 g/t Au and 136 g/t Ag on average. To date, veins with significant base metal sulfide minerals, and massive and crystalline quartz veins lack significant precious metals (Au and Ag), except for one banded base metal sulfide-rich vein at Favona. An overall zonation of the veins exists, with base metal sulfide minerals dominant at depth (1050 m RL) of the system are characterised by massive quartz veins.Fluid inclusions from a total of 31 quartz, amethyst, and platy calcite veins reveal homogenisation temperatures of ~190-250¦C, with final ice melting temperatures between 0.0 and -0.8. Ice melting temperatures correspond to apparent salinities of 18O value of the water that formed these veins is approximately -4.3 per mil, which is similar to meteoric water-dominated, near neutral chloride fluids in geothermal systems in the Taupo Volcanic Zone.

Jan 1, 2002

CrusherMapperTM - A New Tool for Crusher Condition Monitoring The efficiency of mineral processing plants is entirely dependent on the availability of the plant equipment critical path. This typically concerns comminution circuits consisting of primary crushers and primary grinding mills. Crusher and mill availability are determined by the frequency and duration of maintenance shutdowns, which are primarily driven by the need for replacement of sacrificial liners. The change of crusher and mill liner shape over respective life cycles also strongly affects plant efficiency. It is therefore highly desirable to accurately monitor the condition of mills and crushers in order to optimise plant efficiency through maximised availability and targeted liner shape. Traditional comminution liner and other production parameter condition monitoring has been attempted through ineffective methods which prevent satisfactory management of crusher and mill maintenance and reduce operational control. This situation has recently dramatically improved for grinding mills through the development and commercial deployment of MillMapperÖ, a technology based on three-dimensional laser scanning data and dedicated software (Franke, Lichti and Stewart, 2006; Franke and Lichti, 2007; 2008; Franke, 2008; Franke, Redman, Johnson and Michalek, 2009). At the time of writing in late 2009, MillMapperÖ is in successful use at a rate of approximately 170 surveys and associated reports per annum at processing plants in Australasia, South America, North America and Africa. This paper presents the introduction of CrusherMapperÖ, the MillMapperÖ equivalent for crushers. CrusherMapperÖ also utilises high density, high accuracy laser scanning data, and features dedicated algorithms for three-dimensional monitoring of wear on crusher concaves and mantles. This facilitates the detection of wear hot spots or zones or localised liner failures, and accurate forecasting of reline tonnages and dates. It also for the first time provides the means to establish optimised concave and mantle shapes in order to achieve production targets. In contrast to any other currently utilised condition monitoring method, CrusherMapperÖ data collection can occur remotely and does not require any shutdown or crusher isolation. This method therefore does not interrupt crusher production while at the same time eliminating any confined space risk normally associated with taking measurements inside the crusher cavity.

Sep 13, 2010

Bacteria can play a key role in the processing of 'difficult' ores. Bioleaching opens the way to potentially extract copper from vast amounts of otherwise hard to process refractory low-grade chalcopyrite. In my talk I will outline our research philosophy to develop bioleaching as a Precision Processing unit process step. In our view, Precision Processing is a sophisticated approach to mineral processing where the ultimate goal is to measure and characterise the ore body in-ground and in real time during mining, allowing the down-stream unit processes (bioleaching, in this case) to be continuously tailored and tuned via feedback and feed-forward controls to obtain the highest possible recoveries at the lowest possible cost and environmental impact. I will describe some of the work that we are undertaking to better understand the interfacial phenomena underlying the fundamental bioleaching process with the aim of coming to a Precision Processing approach. We use techniques such as interfacial electrochemistry (scanning electrochemical microscopy, SECM), AFM, zeta potential measurement, and synchrotron science to elucidate the parameters that drive bacterial selectivity and adhesion, bacterial metabolism, and dissolution and precipitation processes for model systems and real chalcopyrite ores. As examples of our research, I will discuss in some detail our method to produce and characterise micro-patterned CuxS - silica thin films as model substrates for electrochemical and bacterial adhesion work and our approach to the interfacial chemical characterisation of extracellular polymeric substances of bio-active bacterial cells. I will also cover some of our recent findings relating to measurement and interpretation of bacterial adhesion on sulfidic substrates and its implications for bacterial adhesion and substrate selectivity. After having identified and discussed crucial leaching parameters, such as pH, Eh, T, [Cu2+], and [O2], the talk will go on addressing some of the early achievements and challenges encountered in our work to design and prepare low-cost, rugged sensing devices that allow the in-situ (in this case, in-dump or in-heap) localised measurement of these parameters. I will conclude my talk by painting the picture of how the work of our group might contribute to realising the dream of transforming bioleaching into genuine high-tech Precision Processing of minerals. This is an ABSTRACT ONLY. A full-length paper was not prepared for this presentation.

Sep 13, 2010

By Kadoya H, Kondo Y

The Harima works were established in 1964 and started operation in 1966. The initial capacity was 3500 t/month of zinc and 1500 t/month of lead. Until 1990 a lot of improvements had been made and the capacity had increased 6600 t/month of zinc and 2200 t/month of lead without enlarging the furnace size. During the ten weeks campaign shut-down at the end of 1990, many modifications were carried out including the enlargement of the furnace shaft area. By these changes, the capacity has gone up to 7500 t/month of zinc and 2500 t/month of lead. In the sinter plant, the amount of SO2 rich gas supplied to the acid plant was raised to 50 000 Nm3/h from 43 500 Nm3/h. An electrostatic precipitator was adopted instead of a venturi scrubber to clean the rich gas. Oxygen enrichment has been continuously operated since August 1991, because the furnace capacity is more than the rate of sinter production. Utilisation of the sinter plant is high being as much as 97 per cent and the sulphur burning rate has been increased. In 1990 the furnace was replaced except the hearth. The shaft area was enlarged to 19.4 m2 from 15.3 m2. The target blast was designed to be more than 36 000 Nm3/h. Tuyere layout was changed to prevent slag breakouts. Due to these modifications shaft condition has been very good. Automatic launder jacket cleaners were installed to increase the lead cooling efficiency. Many other improvements and developments were also made. Coke powder injection from the tuyeres has been successfully operated since April 1987.

Jan 1, 1993

By N Cusworth

The development of a resource project inevitably requires the investigation of a vast range of issues across most engineering disciplines û mining, metallurgical, chemical, civil, electrical, mechanical and environmental û as well as the geosciences. It is also a characteristic feature of the resource industry that no two orebodies û and hence no two development projects û are the same. So these technical issues have to be addressed to a greater or lesser extent in evaluating any resource projectÆs development potential. Not surprisingly then, technical issues tend to predominate when assessing the development potential of a project in the process typically referred to as ædoing a feasibility studyÆ. But the principal purpose of a æfeasibility studyÆ is to determine whether a development opportunity makes good business sense, not just whether it is technically possible. Resolution of technical issues is often seen as the primary focus of a feasibility study, whereas in reality, these technical issues are the basis upon which an asset delivery and business plan is built. This is not to say that technical issues are unimportant û they are a prerequisite to the demonstration of a projectÆs viability. The feasibility study process must therefore demonstrate that not only have the technical issues been satisfactorily addressed, but also that the broader commercial, economic and social issues have been considered in the development of a comprehensive business plan, which includes an assessment of the risk-reward profile of the proposed development. This paper will present a framework for the conduct of æfeasibility studiesÆ and provide guidance to minimum standards and best practice.

Jan 1, 2007

By Ralph B. S

Bacterial leaching of low grade quartz felspar porphyry copper ore was studied in large-scale laboratory percolation leaching columns.Limitations in the release of soluble copper showed up before fifty per cent recovery, due to occluding precipitates of iron oxides and hydroxides. Precipitates were removed by increasing the acidity of irrigation feed four-fold with respect to sulphuric acid. However, irrigation at low pH (pH 1.5) inhibited copper leaching. Resumption of bacterial leaching at pH2 was achieved by introducing a period of non-irrigation. The results suggest a 'direct' attack by bacteria on the chalcopyrite substrate rather than an 'indirect' ferric-leach mechanism.

Jan 1, 1981

The C.S.I.R.O. acid alumina process employs the essential steps of digestion, hydrolysis and calcination to produce pure alumina from ores too high in silica or too low in grade for the Bayer process. The two latter stages have been described in some detail previously but the digestion stage requires separate discussion since ores vary widely in composition and reactivity. Kaolinitic clays require roasting to 800°C to render the alumina soluble in the 11 per cent sulphuric acid used in the process while some ferruginous laterites require roasting to reduce the reactivity of iron minerals.The iron content of pregnant solutions is kept at a low figure by digesting at temperatures where the solubilities of ferric oxide or basic ferric sulphates are small. A two-stage, counter-current digestion is necessary to extract a high percentage of alumina from the ores and to produce a basic pregnant liquor with an SO3 : AI 203 ratio of 1'\1 suitable for high temperature hydrolysis. The second stage of digestion, called the modification stage, treats slightly acid liquors with excess of ore in the temperature range 1200-1400C.The first stage operates at 170°-1900C to extract further alumina from modification residues, using recycled acid obtained from later steps of the process. Both temperature ranges are critical for economic operation and for proper control of the iron content of solutions. In batch experiments, 30 min is regarded as a suitable retention time for digestion and modification; ores which require much longer than this are less suitable for the process. Impurities such as silica, and titanium and vanadium oxides are discarded in the residue along with iron oxide, and do not contaminate the final product. Bivalent metallic sulphates such as MgSO4, can build up in the circuit to a very considerable degree without affecting product purity.Comparison with other processes shows that the C.S.I.R.O. process is superior for control of contamination by iron, which is the major problem in acid processes. The pure intermediate product (3Al203.4S03.9H20) is also more convenient for calcination to alumina than the hydrated aluminium sulphate usually recovered in other processes. Detailed cost comparisons must await pilot-plant evaluation of the C.S.LR.O process.

Jan 1, 1964

Winzes are usually sunk 9 ft. 6 in. long by 6 ft. 0 in. wide and are divided into two compartments, 4 ft. 0 in. by 5 ft. 0 in. inside the timbers. The general practice is to sink the winze to a depth of from 9 to 12 ft., put in bearers and three or four rings of timber, and then erect a sinking headframe before continuing sinking operations.GENERALThe main feature governing the design of the headframe was that all parts could be transported on timber trolleys in No. 2 Shaft. Except for some minor details the structural members consist of steam pipe. Joints are sections of steam pipe welded to one member and into which the other member fits and is held in place by a 1-in. bolt. The headframe consists essentially of two bedpieces to carry the winch and to form a seat for the four legs. The legs support the sheave bearers, the tipping door and the brace.Except during tipping operations the door is in a nearly vertical position. For tipping it is lowered to an inclined position and a hook suspended from one of the bracing members of the headframe is attached to a "D" welded to the bottom of the kibble. This causes the kibble to tip when it is lowered on to the tipping door. The capacity of the kibble is 4 cubic feet.THE HEADFRAMEThe dimensions of the headframe are:Height to top of sheave .. .. 14 ft. 10 in.Distance centre to centre of legs 4 ft. 4 in.Length of bedpieces .. .. .. .. 8 ft. 9 in.The weight is approximately 2,000 lb., the tipping door and bedpieces being the heaviest members. They weigh 240 lb. and 170 lb. respectively.One compartment of the winze is decked over, and the bedpieces, which are 8 ft. 9 in. lengths of 6 in. pipe with three short lengths of plate welded to the underside, are placed over the sinking compartment, either transversely or parallel to the winze. Three 3 inch pipes act as spreaders between them.Welded to the top of each bedpiece is a 6-in. by iHn. plate 3 ft. 0 in. long with four 4-in. by 1.5-in. slots cut longitudinally at 10 in. centres. Two 10 in. by 4-in. timbers are bolted to these plates, the distance between them being adjusted to suit the holes in the winch bedplate, which is bolted to the 10-in. by 4-in. timbers.Two short lengths of 3 in. pipe are welded to each bedpiece at 4 ft. 4 in. centres. These form the seats for the legs of the headframe, which are...

Jan 1, 1941

KIeeman (1968) described practice in the Mount Hebbard dump concentrator, Broken Hill, N.S.W. The purpose of this note is to give data on flotation pulp chemistry in the plant for comparison with results of Woodcock and Jones (1970a, 1970b).Ten chemical parameters were measured at ten points in the circuit using the techniques of Woodcock and Jones (1970a, 1970b). Fig. 1 shows a condensed time plot of some continuous measurements in conditioner overflow and rougher feed. Fig. 2 shows average values of selected parameters at the start and end of each of the three rougher flotation stages.DISCUSSIONpH and redox potentiaIsFig. 1 shows that pH and Eh were relatively constant at the start of sulphide lead flotation. There was a fairly steady increase in pH throughout the circuit (Fig. 2), but flotation was always conducted in a slightly acid pulp in spite of the large amount of alkaline reagents added. Eh values became more positive as the pulp progressed through the circuit (Fig. 2) in accord with results elsewhere.

Jan 1, 1973

The spatial and temporal evolution from the porphyry to high-sulphidation epithermal environment can be assessed by integrating new results on such deposits (Arribas et al, 1995; Hedenquist et al, 1998) with past studies of plutonic and porphyry systems (Dilles and Proffett, 1995; Cline, 1995; Shinohara and Hedenquist, 1997; Hedenquist and Richards, 1998). Some time ago, Sillitoe (1973) argued for the nature of the tops and bottoms of porphyry deposits. He concluded that epithermal deposits may form over the tops of some porphyry systems. We can now conclude more confidently what the tops and bottoms of many high-sulphidation ore deposits appeared like while active (Arribas, 1995; Hedenquist, 1995). In addition, we better understand the nature of the zonation of high-sulphidation epithermal systems from the intrusive to surficial environment (Sillitoe, 1999), and how these two styles of ore deposit are related. Geological and geochemical evidence clearly indicates a continuum between these two ore environments. This improved understanding of genesis allows more efficient exploration for these deposits. There are many examples of spatially associated porphyry and epithermal ore deposits. A genetic connection has been suggested by some, and argued against by others. Nowhere is this spatial association better seen than in northern Luzon, Philippines, where the Lepanto high-sulphidation epithermal Cu-Au deposit overlies the Far Southeast (FSE) porphyry Cu-Au resource (Figure 1). Together these mineralised bodies contain a resource of >3.8 M tonnes Cu and >550 tonnes Au. Lepanto was largely mined out in early-1997. Post-war production until 1995 was 0.73 Mt Cu, 115 t Au and 393 t Ag at an average grade of 2.2 per cent Cu, 3.5 g/t Au and 11 g/t Ag. The recent discovery of the adjacent Victoria low-sulphidation quartz-Au-base metal vein deposit, with a resource of >68 tonnes Au (Cuison et al, 1998), illustrates the variety and abundance of mineralisation in the Mankayan district. This district also hosts the Guinaoang porphyry Cu-Au deposit (Sillitoe and Angeles, 1985) and other epithermal vein occurrences (Figure 1). This brief summary reviews the results recently published on the Lepanto-FSE deposits (Arribas et al, 1995; Mancano and Campbell, 1995; Claveria, 1998; Hedenquist et al, 1998), and stresses the evidence for coupling of mineralisation between the porphyry and high-sulphidation epithermal environments.

Jan 1, 1999

By Rayner B

Five wells have been drilled in the Basker/Manta Block of VIC/P19, Gippsland Basin, resulting in sub-economic Intra-Latrobe Group oil and gas discoveries at Basker-1 and Manta-1. A total of 21 individual hydrocarbon bearing sandstones were intersected by the two wells. These reservoir sand bodies were deposited by fluvial processes in a lower coastal plain environment. The modelling of sand body orientation and geometry is a critical component in the evaluation of the two accumulations. Seismic resolution of the thin (average 2 m to 5 m) sand bodies is inadequate for mapping their orientation and distribution. Dipmeter data has been successfully applied to the problem of orienting the sand bodies using FMS images acquired during the drilling of Gummy-1 and reprocessed HDT data from Basker-1 and Manta-1. Prediction of lateral extensiveness (geometry) of individual sand bodies has also been attempted. Interpreted palaeocurrent direction from all three wells is dominantly from the NW to the SE. Reservoirs in the Manta-1/Gummy-1 area are interpreted to be predominantly channel sands, deposited by relatively low sinuosity streams. As such they would tend to have a laterally extensive, elongate geometry. Sand bodies deposited in the Basker-1 area show a predominance of laterally accreted cycles deposited by meandering streams. Channel geometry may then be limited in the downstream/upstream direction by internal permeability barriers such as clay plugs.

Jan 1, 1992

An enhanced gravity concentrator was installed in conjunction with an intensive leach reactor at the Sadiola plant in Mali last year and commissioned in December 2007. There has been much debate over the years as to the effect of gravity concentration on overall plant performance. The late Dr Laplante suggested that for every ten per cent of gold recovered by gravity, there was a corresponding 0.1 per cent to one per cent additional overall plant recovery. The results at Sadiola are consistent with this hypothesis with an overall four per cent gain in plant recovery. With total gold recovery of 12 per cent in the gravity section, grades are increased from 3.54 g/t in the gravity feed to an average of 2 600 g/t in the concentrator feed to the inline reactor. The recovery of gold in the inline reactor is in excess of 98.5 per cent. This paper discusses the background to the project, the laboratory test work prior to the equipment selection, the operational results of the system, as well as the benefi ts of the future application of high mass yield centrifugal concentrators in base metals, sulfides and industrial minerals. Bench scale, pilot scale and plant practice examples are also presented.

Aug 1, 2010

By B Hannah, M Uriarte, F Labarca, C Madore, G Ganapathi, L Martin, T Haase

BechtelÆs Mining and Metals projects across the globe are executed in remote arid and semi-arid countries where providing even basic water supplies impose considerable challenges. Opportunities for water conservation measures using a Six Sigma initiative were proactively pursued to address the potential business impacts of limited availability of water resources. The initiative investigated areas driving water-optimisation during concrete operations and camp management. This paper details the water conservation evaluation of alternatives and cost/benefit analysis based on current and predicted water usage for development projects. Optimisation of water consumption through institutionalising more prescriptive standards for camp design and defining water conservation requirements have resulted in a new standard specification. Based on our projected mining project workload across the globe, it is estimated that for the period 2012 - 2015, a potential 5.5 M m3 water savings resulting in US$11 M could be realised for construction camps and savings of 4 M m3 of peripheral concrete process water resulting in potential cost savings of US$8 M could be achieved as a result of these revised standards.CITATION:Haase, T, Hannah, B, Ganapathi, G, Martin, L, Madore, C, Labarca, F and Uriarte, M, 2013. Water conservation at construction projects, in Proceedings Water in Mining 2013 , pp 251-258 (The Australasian Institute of Mining and Metallurgy: Melbourne).

Nov 26, 2013

THE furnace described in this paper was installed and has been used by the writer for the melting of rich gold-bearing material, and has given complete satisfaction. It may, therefore, prove of interest to other metallurgists who are faced with a similarproblem. A furnace of this type should be most suitable for the reduction of "cyanide preeipitate," "charcoal ash," "anode sludge," &c. formerly the melting was done in fire-clay crucibles, using coke or crude oil as fuel, but this method is costly, slow, and unsatisfactory. A small water-jacketed blastfurnace was also tried on this material after briquetting it, but was discarded in favour of the electric furnace. The furnace may be described as a simple form of the Heroult resistance furnace, with an adjustable upper electrode and a fixed bottom electrode. This is in accordanee with Stansfield's classification of electric furnaces. The heating is mostly due to the resistance offered the current by the molten slag. The melting chamber consists of a steel drum 14 in. in diameter and 21 in. high, and is lined with silica bricks specially made to fit the shell. The internal diameter is G in. The bricks contain 92 % silica, are made from calcined quartzite bonded with fireclay, and are similar in composition to those used for lining steel converters. They are set in a mixture of finely-ground quartzite and clay, and well dried out. The shell is bolted to a steel plate, which forms the decking of a truck running on rails, so that the furnace can be moved under ahood for carrying off the fumes. A cast-iron slag spout is bolted to the shell below the tapping hole, which is 4 in. from the bottom of the shell. Opposite this another hole 1 in. in diameter is drilled through the shell and lining for the passage of the lower...

Jan 1, 1918