By G. Gutierrez, D. A. Elgillani, M. C. Fuerstenau

The zero-points-of-charge of apatite, calcite, and fluorite are pH 6.4, 10.8, and 10.0, respectively. Scheelite is negatively charged above at least pH 3. In this article, the flotation responses of these minerals in the presence of potassium oleate and sodium silicate are described and compared with electrokinetic data. Colloidal silica appears to be the species principally responsible for calcite depression, while silicate anion is the species responsible for fluorite depression. Additions as high as 1 x 10-3 mole/liter silicate have no effect on the flotation responses of apatite and scheelite. Selective flotation of nonmetallic minerals is difficult to achieve with fatty acids or soaps by themselves. As a result, specific reagents are added to aid these separations, and one of the reagents commonly employed for this purpose is sodium silicate. Flotation separations of various calcium-bearing minerals such as fluorite from calcite1-3 and scheelite from calcite2,4 and apatite,2,5 for example, almost always involve the use of sodium silicate. The mechanisms by which sodium silicate functions as a depressant are still not understood, probably for a number of reasons. For one thing, the dissolution process of sodium silicate is complex, giving rise to a number of ionic and colloidal species.' Moreover, the type and concentration of these species depend on the ratio of Na2O to SiO2, the concentration of sodium silicate, and the pH of the system.' At the present time, it is not known which species, colloidal silica or silicate anion, is responsible for depression. If colloidal silica is the species that is adsorbing, then adsorption must occur by electrostatic attraction between the colloid and the mineral surface. Silicate anion, on the other hand, may adsorb either physically or chemically. The objective of this paper is to determine first the active species of sodium silicate and then the conditions under which this species will adsorb and function as a depressant. EXPERIMENTAL MATERIALS AND METHODS Pure samples of apatite (Durango), calcite (Iceland-spar), fluorite, and scheelite were used in this investigation. Pure potassium oleate was used as collector, while reagent-grade HC1 and KOH were employed for pH adjustment. The sodium silicates used were samples obtained from the Philadelphia Quartz Co. In one series of experiments, various sodium silicates containing different ratios of SiO2 to Na2O were added to calcite systems. These sodium silicates contained SiO2-to-Na2O ratios of 3.75 to 1, 3.22 to 1, 2.40 to 1, and 1.60 to 1. All other experiments were conducted with the sodium silicate containing the ratio of 3.22 to 1, which is the one that is normally used in industry. Flotation experiments were conducted with 21/2-g charges of 48 x 150-mesh material in conductivity water with an apparatus and technique described previously. Electrokinetic experiments were conducted with both a Zeta Meter and streaming potential apparatus. Particle size was 48 x 65 mesh for the streaming potential experiments. EXPERIMENTAL RESULTS The first series of experiments involved flotation of scheelite in the absence and presence of sodium silicate. As shown in Fig. 1, flotation response was not affected with even the relatively high addition of 1 x 10-3 mole per liter sodium silicate. Interestingly though, no flotation was effected below pH 6 with this collector addition. The responses of apatite to flotation under these same conditions are given in Fig. 2. Similarly, no depression was obtained in basic media under these conditions. Similar experiments were conducted with fluorite, and in this case, depression was noted above about pH 11 with 1 x 10-3 mole per liter sodium silicate (Fig. 3). When calcite was floated with these same levels of addition of sodium silicate, essentially no flotation was possible above pH 7 (Fig. 4). The effect of collector addition with a constant addition of sodium

Jan 1, 1969

By W. M. McKewan

Magnetite pellets were reduced in flowing hydrogen at pressures up to 40 atm over a temperature range of 350° to 500°C. The rate of weight loss of oxygen per unit area of the reaction surface was found to be constant with time at each temperature and pressure. The reaction rate was found to be directly proportional to hydrogen pressure up to 1 atm and to approach a maximum rate at high pressures. The results can be explained by considering the reaction surface to be sparsely occupied by adsorbed hydrogen at low pressures and saturated at high pressures. PREVIOUS investigation1,2 have shown that the reduction of iron oxides in hydrogen is controlled at the reaction interface. Under fixed conditions of temperature, hydrogen pressure, and gas composition, the reduction rate is constant with time, per unit surface area of residual oxide, and is directly proportional to the hydrogen pressure up to one atmosphere. The reduction rate of a sphere of iron oxide can be described3 by the following equation which takes into account the changing reaction surface area: where ro and do are the initial radius and density of the sphere; t is time; R is the fractional reduction; and R, is the reduction rate constant with units mass per area per time. The quantityis actually the fractional thickness of the reduced layer in terms of fractional reduction R. It was found in a previous investigation2 of the reduction of magnetite pellets in H2-H,O-N, mixtures, that the reaction rate was directly proportional to the hydrogen partial pressure up to 1 atm at a constant ratio of water vapor to hydrogen. Water vapor poisoned the oxide surface by an oxidizing reaction and markedly slowed the reduction. The enthalpy of activation was found to be + 13,600 cal per mole. It was also found that the magnetite reduced to meta-stable wüstite before proceeding to iron metal. The following equation was derived from absolute reaction-rate theory4,8 to expfain the experimental data: where Ro is the reduction rate in mg cm-2 min-'; KO contains the conversion units; Ph2 and PH2O are the hydrogen and water vapor partial pressures in atmospheres; Ke is the equilibrium constant for the Fe,O,/FeO equilibrium; Kp is the equilibrium constant for the poisoning reaction of water vapor; L is the total number of active sites; k and h are Boltzmann's and Planck's constants; and AF is the free energy of activation. Tenenbaum zind Joseph5 studied the reduction of iron ore by hydrogen at pressures over 1 atm. They showed that increasing the hydrogen pressure materially increased the rate of reduction. This is in accordance with the work of Diepschlag,6 who found that the rate of reduction of iron ores by either carbon monoxide or hydrogen was much greater at higher pressures. He used pressures as high as 7 atm. In order to further understand the mechanism of the reduction of iron oxide by hydrogen it was decided to study the effect of increasing the hydrogen pressure on rebduction rates of magnetite pellets. EXPERIMENTAL PROCEDURE The dense magnetite pellets used in these experiments were made in the following manner. Reagent-grade ferric oxide was moistened with water and hand-rolled into spherical pellets. The pellets were heated slowly to 550°C in an atmosphere of 10 pct H2-90 pct CO, and held for 1 hr. They were then heated slowly to 1370°C in an atmosphere of 2 pct H2-98 pct CO, then cooled slowly in the same atmosphere. The sintered pellets were crystalline magnetite with an apparent density of about 4.9 gm per cm3. They were about 0.9 cm in diam. The porosity of the pellets, which was discontinuous in nature, was akrout 6 pct. The pellets were suspended from a quartz spring balance in a vertical tube furnace. The equipment is shown in Fig. 1. Essentially the furnace consists of a 12-in. OD stainless steel outer shell and a 3-in. ID inconel inner shell. The kanthal wound 22 in. long, 1 1/2, in. ID alumina reaction tube is inside the inconel inner shell. Prepurified hydrogen sweeps the reaction tube to remove the water vapor formed during the reaction. The hydrogen is static in the rest of the furnace. The sample is placed at the bottom of the furnace in a nickel wire mesh basket suspended by nickel wire from the quartz spring. The furnace is then sealed, evacuated, and refilled with argon several times to remove all traces of oxygen. It is then evacuated, filled with

Jan 1, 1962

By Robert E. Green, Wolfgang Sachse

Simullaneous ultrasonic attenuation measurements of both quasishear waves propagating in single cryslals of aluminum indicate that, in the undeformed annealed state, the dislocation density is generally not uniform on all slip systems. Change oof attenuation measurements made during plastic defortnation of crystals , which possessed specific orientations ideal for studying the orientation dependence of dislocation damping, indicate that, for low strain levels, dislocation motion occurs on additional slip systems besides the primary one, even for crystals oriented for plastic deformation by single slip. THE sensitivity of internal friction measurements permits such measurements to be used successfully in studying the deformation characteristics of metal crystals. On the basis of experimental observations, T. A. Read1 was the first to associate internal friction losses with various dislocation mechanisms. Since that time further work2-' has been performed and a dislocation damping theory has been formulated by Granato and Lucke.6 In the amplitude independent region, this theory predicts the attenuation a to be dependent on an orientation factor O, a dislocation density A, and an average loop length L. if is a constant, independent of crystallographic orientation. For a given crystallographic orientation, changes in dislocation density and loop length give rise to the observed attenuation changes accompanying plastic deformation. The Granato-Liicke theory suggests the investigation of the orientation dependence of attenuation measurements in hopes of obtaining information to separate dislocation motion losses from other losses.7 An experimental study of the orientation dependence of attenuation in undeformed annealed single crystals should yield an insight into the uniformity of dislocation distribution throughout the entire specimen. A similar study on crystals plastically deformed in a prescribed fashion should give information about the alterations in the dislocation distribution on the slip systems activated during plastic deformation. The possible modes of elastic waves which can be propagated in aluminum,8 copper,9 zinc,10 and other hexagonal metals" have been calculated. Associated with each mode of wave propagation are dislocation damping orientation factors, which are based on the resolution of the stress field of that particular elastic wave onto the various operative slip systems in the material. These orientation factors have also been calculated as a function of crystallographic orientation in the papers cited above. Einspruch12 obtained agreement between predicted and observed attenuation values of longitudinal and shear waves in (100) and (110) directions of two undeformed aluminum crystal cubes. He ascribed the slight deviations between predicted and observed values to a nonuniform dislocation distribution, or to other loss mechanisms. In shear deformation of zinc crystals, Alers2 found that the attenuation of shear waves having their particle displacements in the slip plane was very sensitive to the deformation, while the longitudinal wave attenuation was affected only when the wave propagation direction was not normal to the slip plane. Using aluminum single crystals oriented for single slip, Hikata3 et al. found that during tensile deformation the change of attenuation of the shear wave (actually quasishear) having particle displacements nearly perpendicular to the primary slip direction exhibited the easy-glide phenomena, while longitudinal waves did not. Similar results were reported by Swanson and Green5 during compressive deformation of aluminum crystals. These results are in qualitative agreement with the calculated orientation factors for specimens of this orientation. In well-annealed, undeformed aluminum crystals, the damping is expected to be due to dislocations vibrating on all twelve slip systems. The orientation factors associated with this initial damping will be designated by O2 and O3, where a, represents the average orientation factor for the slow shear (or quasishear) wave and O3 represents the average orientation factor for the fast shear (or quasishear) wave. The calculation of these values for aluminum crystals by Hinton and Green8 shows that they vary very little as a function of crystallographic orientation—at most, by a factor of 2.47. If the dislocation density and loop length are uniform, then in the initial undeformed state, Here the subscript zero refers to the initial value of the attenuation. Also for aluminum, the calculations8 show that the orientation factors for primary slip only, associated with each shear wave, exhibit a sharp minimum for particular crystallographic orientations. A composite plot of the two shear wave orientation factors for primary slip only is shown in Fig. 1. Since these orientation factors are associated with dislocation motion occurring on the primary slip system only, the proper condition to check these factors might be attained by slightly deforming a single crystal oriented for primary slip. For dislocation motion on the primary slip system only,

Jan 1, 1969

By W. L. Fink, L. A. Willey

DURING the war there was introduced a new higher strength aircraft alloy designated 75S.1,2.3 The properties of this alloy assure extensive applications in both military and commercial aircraft. It is therefore important to understand its limitations as well as advantages. The properties of 75S alloy in the heat-treated tempers, like those of many other aluminum alloys, are affected by the rate of quenching. In general, low quenching rates tend to cause low strengths and to adversely affect the resistance to corrosion. Commercial quenching procedures are usually sufficiently rapid to permit the development of maximum properties. However, in the center of heavy sections, such as large rolled and extruded shapes, the quenching rates may not be rapid enough to develop maximum strength or resistance to corrosion. The investigations of 75S alloy described herein reveal the most critical range of temperature and the effects of quenching sheet and extrusions at different rates through that temperature range, on the tensile properties and resistance to corrosion. PROCEDURE Preparation of Specimens Sheet specimens (3 in. by 9 in.) were prepared from a commercial lot of 75S "as rolled" sheet (0.064 in. thick). The composition° was as follows: Weight Percentage Cu Mn Mg Zn Cr Al with Normal Impurities 1.64 0.16 2.58 5.66 0.27 Remainder The specimens employed for the determination of the time-temperature relations during quenching of sheet were prepared by the following procedure: the hot junction of a 28-ga. iron-constantan thermoelement (asbestos insulated) was brazed to a thin strip of aluminum which was in turn brazed into the end of a 3/16 in. i.d. by ¼ -in. o.d. by 30 in. long aluminum protection tube. Before brazing, the tube was flattened to 0.064 in. thickness over the junction and adjacent lead wires for a distance of 1 ½ in. The flattened end of the tube was fitted into a slot cut from one edge to the center of the 3 in. by 9 in. by 0.064 in. sheet and brazed into place. The brazed joint was dressed to the thickness of the sheet and the entire specimen buffed to approximately the brightness of "as rolled" material. Because of the brazing operations required, these specimens were prepared using 3S alloy. For the investigation of quenching rates in heavy sections, there were used 75S extrusions which had compositions similar to that of the sheet. The specimens consisted of 14 in. lengths of ¾ in., 2 in., 3 in. and 4 in. diam cylindrical rods and a roughly rectangular extruded section which was approximately 4 in. by 7 ½ in. Thermocouples were peened into the bottoms of 1/8 in. diam wells drilled into one end and parallel to the axis to a depth of

Jan 1, 1947

By W. D. Robertson

A considerable quantity of experimental data is available on the effect of time, temperature, work-hardening and composition on the mechanical properties and corrosion resistance of aluminum alloys. There is, however, little unity of purpose or generality in most of the studies and, because the number of variables is large, the results often are not applicable to the problems that arise in practice. Furthermore, the customary expression of the effect of different variables as separate curves or as three-dimensional diagrams with time, temperature and the dependent variables as coordinates, renders the task of selecting the optimum time and temperature of precipitation treatment, with respect to their simultaneous but unequal etfect on the various properties, exceedingly difficult. The introduction of precipitation treatments to raise the yield strength of 24s-type alloys has created a need for a method of correlating and summarizing the effect of time and temperature on the mechanical properties and susceptibility to inter-crystalline corrosion. Correlation is particularly desirable because the choice of time and temperature is of necessity a compromise to achieve the best possible combination of properties, and the optimum conditions cannot he accurately specified unless the data are in a form in which the alternatives can be readily compared. Therefore, the work described here was undertaken to find a common relationship that would be capable of expressing the effect of precipitation time and temperature on the various properties and by means of which the relative effects could be correlated and their interpretation facilitated. Review of Previous Work In connection with an investigation of the interrelation of age-hardening and creep performance of nickel-silicon-copper alloys, Jenkins and Bucknalll demonstrated that the time required to attain maximum hardness and tensile strength could be expressed by a relationship of the form: t = K • io"^ (i) where t is the time in hours and T the temperature of aging, expressed in degrees absolute, and m and K are constants. They also pointed out that this expression is analogous to that which describes the change of the diffusion coefficient D with temperature; namely, D = Ae-~/m (2) Later, Cohen used this relationship in studies of the mechanism of age-hardening of a silver.rich copper alloyZ and of duralumin.3

Jan 1, 1946

By W. D. Robertson

A considerable quantity of experimental data is available on the effect of time, temperature, work-hardening and composition on the mechanical properties and corrosion resistance of aluminum alloys. There is, however, little unity of purpose or generality in most of the studies and, because the number of variables is large, the results often are not applicable to the problems that arise in practice. Furthermore, the customary expression of the effect of different variables as separate curves or as three-dimensional diagrams with time, temperature and the dependent variables as coordinates, renders the task of selecting the optimum time and temperature of precipitation treatment, with respect to their simultaneous but unequal etfect on the various properties, exceedingly difficult. The introduction of precipitation treatments to raise the yield strength of 24s-type alloys has created a need for a method of correlating and summarizing the effect of time and temperature on the mechanical properties and susceptibility to inter-crystalline corrosion. Correlation is particularly desirable because the choice of time and temperature is of necessity a compromise to achieve the best possible combination of properties, and the optimum conditions cannot he accurately specified unless the data are in a form in which the alternatives can be readily compared. Therefore, the work described here was undertaken to find a common relationship that would be capable of expressing the effect of precipitation time and temperature on the various properties and by means of which the relative effects could be correlated and their interpretation facilitated. Review of Previous Work In connection with an investigation of the interrelation of age-hardening and creep performance of nickel-silicon-copper alloys, Jenkins and Bucknalll demonstrated that the time required to attain maximum hardness and tensile strength could be expressed by a relationship of the form: t = K • io"^ (i) where t is the time in hours and T the temperature of aging, expressed in degrees absolute, and m and K are constants. They also pointed out that this expression is analogous to that which describes the change of the diffusion coefficient D with temperature; namely, D = Ae-~/m (2) Later, Cohen used this relationship in studies of the mechanism of age-hardening of a silver.rich copper alloyZ and of duralumin.3

Jan 1, 1946

By D. R. Miller

Internal friction and elastic modulus variations in electrorefined titanium, iodide refined titanium, and alloys of the latter material with oxygen, nitrogen, aluminum, and zirconium were investigated. No oxygen peak was detected with electrorefined titanium but, provided precautions were taken to prevent increases in background damping, an oxygen peak at about 410°C could be resolved with each of the other materials. An additional partially resolved peak was observed at 500°C in a Ti-N alloy. An anomaly in the variation of rigidity modulus with temperature was observed. Possible mechanisms for the formation of any oxygen peak have been discussed. PRATT, Bratina, and Chalmersl investigated the internal friction of commercial purity titanium and alloys of this material containing 1.5, 3.5, and 4.5 at. pct O. With commercial titanium the internal friction curve consisted of two components, a background which increased steadily with temperature and a peak at about 600" C which was due to grain boundary relaxation. In the Ti-O alloys, however, an additional internal friction peak was observed at 430" to 450°C and, since this peak increased in height as the oxygen content was increased, it was thought to be associated with the presence of oxygen. The diffusion of oxygen in titanium at temperatures between 300" and 500° C is believed to have marked effects in its tensile properties2'3 and the present internal friction measurements were undertaken to obtain further information on this diffusion, using material of higher purity than that of Pratt et d. and an apparatus of very much greater sensitivity. In the course of the investigation a number of important limitations on the work of Pratt et al. were revealed and results have been obtained which emphasize the need for ensuring that in this type of experiment, internal friction is independent of strain amplitude and that the values obtained are reproducible. 1) MATERIALS AND APPARATUS The basis material from which the majority of the specimens was prepared was iodide-refined titanium, the major impurities in which were oxygen and nitrogen—the metallic impurities being present at concentrations less than 0.001 at. pct. The hardness of this material after arc melting, forging, and swaging to rods 1/4 in. diameter was Dph = 110. Specimens 10 in. long and 0.020 in. (0.51 mm) diameter were prepared from these rods by further swaging and wire drawing and were finally annealed in vacuo (5 x 10-6 mmHg) for 24 hr at 800°C. The oxygen alloys were prepared from iodide-

Jan 1, 1962

By H. Jehn

Like some other Pt-group metals palladium shows a low but considerable solid solubility of oxygen, which was found already from oxidation studies. The oxygen solid solubility of palladium in equilibrium with gaseous oxygen has been investigated at 900 - 1300 °C in oxygen (665 mbar) and air by gassing and analyzing polycrystalline samples. The 0-concentrations range from 40 to 90 ppm and decrease with rising temperature. The isobaric solubility can be represented by the least-squares fit log c0 = 0.5 log p02- 0.32 + 920/T (c0 in wt. ppm, p02 in mbar, T in K). The thermodynamic data of the exothermic solution reaction are calculated to ?H°= -17.6 kJ?mol-1 and ?S° -76.5 J?mol ? K-1. The behaviour of palladium in an oxygen atmosphere is characterized by the simultaneous reactions of the solution of oxygen in the metal and the formation and evaporation of volatile oxides besides the pure metal evaporation.

Jan 1, 1984

By T. R. Braithwaite

The brief comments made in this chapter deal mainly with shaft sinking, but don't assume that freezing techniques apply only to shaft sinking. They can be used on tunnel work, on such things as liquid gas storage in sediment, and I think you will probably see other applications for it as we go along. The method was first developed in 1883 and was used to sink shallow shafts through water-bearing overburden in Germany and in England. One of the early shafts was in Germany and was sunk by freezing to 310-ft depth. The project required 17 months for drilling, roughly 5 1/2 months for freezing, and another 7 months for sinking, giving an average progress of 10 ½ fpm. Fortunately there have been numerous improvements and new developments in this technique through the years. With equipment and techniques available today, we can take a 20-ft-diam shaft down through 2000 ft of water-saturated overburden and the time schedule runs roughly 4 months for site preparation, freeze-hole drilling, installing the casings, and setting up the plant; 4 ½ months for freezing; and 6 months for excavating and installing permanent linings. This gives a progress rate of about 140 fpm, on average. I might qualify that a little in that the special linings that are required for some formations can affect the time. If it's straightforward sinking where one can use a heavy concrete lining, up to 630-640 fpm may be achieved in a shaft; but with special cast-iron tubbing or types like that, 5 fpd is pretty good progress, so the lining does affect the time. The freezing method is used mainly for sinking shafts through unstable water-bearing formations which cannot be grouted either effectively or economically and which are too deep to enclose in pile casing. Even with overburden, grouting methods available today can handle roughly 100 lb water pressure; in the range of, say, 100 to 150 ft from the surface, it's very often best to grout 40 or 50 ft. You normally drive a pile casing and go through it. Below that range, freezing is very often the economical

Jan 1, 1970

By P. Marier, T. R. Ingraham

When cylindrical powder compacts of nickelous oxide (NiO) are heated in an equilibrated stream of SO3, SO,, and 02, in the temperature range 500°to 800°c, tlickelous suljate (NiSO4) is formed as an adherent layer on the oxide. The reaction is diffusion-controlled, with an activation energy of 13 ± 3 kcal per mole. When cylindrical powder compacts of NiSO4 are heated in a stream of dry nitrogen in the temperature range 1000 0to 11500C, NiO is formed at a well-defined interface between the sulfate and oxide. The interjhce migrates into the sulfate at a constant rate at a constant temperature and gas flow. The reaction rate increases with increasing gas flow and decreases with increasing partial pressure of SO3 in the gas stream. Resolution of the partial-pressure data with a Lang-itzliir Adsorption Isothern suggests that about 80 pct of the NiO interface is covered with SO3. The heat of adsovption is about 68 kcal per mole. The activation energy of the decomposition process is 61 ± 3 kcal per mole. MOST of the work reported on the formation and decomposition of nickel sulfate is related to thermodynamics.1-3 No quantitative work has been reported on the decomposition process. The only kinetic work reported on the formation is that by Fletcher and shelef.4-6 whose main purpose was to study the effects of alkali metal sulfate additions on increasing the rate of nickel sulfate formation. They found that, in the absence of an additive, only small amounts of sulfate were formed and the kinetic data were difficult to interpret. However, they suggested that the sulfa-tion of nickel oxide is a diffusion-controlled process for which the activation energy is approximately 17 kcal per mole.6 In this paper, both the formation and decomposition reactions will be examined; and based on the effects of temperature, flow rate, interfacial area, and partial-pressure of sulfur trioxide, mechanisms and activation energies will be suggested for both processes. EXPERIMENTAL Material. The nickel source material used in all experiments was Baker and Adamson Reagent Grade NiSO4. 6H2O, for which the following analysis was supplied by the manufacturer: C1, 0.001 pct; NO3, 0.005 pct; Co, 0.02 pct; Cu, 0.005 pct; Pb, 0.002 pct; Fe, 0.001 pct: insol, 0.005 pct. The anhydrous sulfate was prepared by heating the hydrate at 420°C in a muffle furnace for 5 hr. Nickel oxide was prepared by decomposing the sulfate at 950°C over a period of 10 hr. Method. The technique used for measuring the rates of formation and decomposition was developed earlier in these laboratories.7-8 The method is based on the observation that the kinetic parameters of a reaction can be established in a flow system, with specimens prepared by compacting powder to a uniform pellet shape. The results are identical with those established with solid polycrystalline specimens or single

Jan 1, 1967

By D. Turnbull, J. H. Hollomon, J. C. Fisher

The concepts of nucleation and of growth have adequately described the isothermal phase transformations to which they have been applied.ls2 However, these concepts have not yet been used successfully to describe the kinetics of a number of transformations that are not observed to take place isothermally. A typical reaction of this type is the austenite to martensite transformation in steels, for which the new phase appears only during cooling of the parent phase. If the cooling is interrupted, transformation ceases; yet had the cooling continued, transformation would also have continued. Nuclei of a new phase do not leap into existence all at once by the simultaneous cooperation of a large number of atoms or molecules of the parent phase; rather they are formed at finite rates by gaining or losing atoms one at a time from the surrounding materiaL3,4 Further thermo-dynamic considerations require a finite concentration of small transitory nuclei of all unstable phases to exist at equilibrium in a stable phase.= For steel in particular, nuclei of ferrite (a iron) exist at equilibrium in austenite (y iron) at temperatures where austenite is the stable phase. If a high-temperature phase a be cooled sufficiently rapidly from temperature TI above the a-ß equilibrium temperature To, to temperature T-1 below To where ß is the stable phase, the equilibrium distribution of ß nuclei corresponding to the high temperature will be retained. There are two limiting possibilities of particular interest: I. The steady state rate of nucleation of ß may be appreciable at T_1, and may require a concentration of sub-critical nuclei exceeding that retained from the high temperature. Time will be required then for the concentration of nuclei to build up to the steady state value, and an induction period will be observed during which the rate of nucleation will increase to the steady state value. 2. The steady state rate of nucleation of ß may be negligible at T-l, while the critical size for continuous growth of ß nuclei, which decreases with increased subcooling of the a phase, may reach a value so small that some. of the retained high-temperature nu-

Jan 1, 1949

By E. A. Gulbransen, J. W. Hickman

Recent work by the authors1 on the oxide films formed on alloys of titanium and zirconium with nickel and copper indicated that an investigation of the oxides which form on alloys of copper and nickel might permit the relative rates of formation and diffusion of the ions of these metals to be determined. This binary system is of further interest since the alloys which form are of the solid solution type over the entire range. In addition nickel is much more oxidation resistant than copper. A comparison of the free energies of formation of the simple oxides which may occur on these alloys indicates that nickel oxide should be observed over the entire time and temperature ranges of oxidation for all alloy compositions~i In order for nickel oxide to predominate on the surface, it is necessary that nickel ions form and diffuse to the surface. Two factors which may influence the formation of nickel oxide may be the ionic sizes, where cu+ is o.,,6-,4 and ~i++ is o.,oh;, and the charges on the ions. On the basis of size, Ni++ should diffuse more readily than Cu+ while on the basis of charge, Cu+ should form more readily than Ni++. According to Uhlig2 passivity to corrosion in an alloy appears at a critical composition which for copper-nickel alloys is related to the tendency of the d band of electronic energy states to fill with elec-trans. This in in the copper- nickel alloys corresponds to 40 at. pct nickel at which composition Uhlig2 (quoting La Que's data) states that the alloy system becomes passive. Magnetic and specific heat data indicate that the d band of copper-nickel alloys is flied at 60 at. Pet Or or 4O at. pct nickel. Matt and Jones3 have shown that if, on alloying nickel with copper, one considers a copper atom to be identical with a nickel atom except for an extra electron (nickel has the configuration: 3ds 4s2 and copper: 3 dl0 4s) then at 60 at. pct copper or 40 at. pct nickel enough electrons are contributed by copper to fill the d band of the alloy. At this composition the magnetic susceptibility approximates zero according to Grew.4 Although the electron diffraction data will not determine the rates of the several reactions which may occur during oxidation, yet a determination of the structures of the surface oxides may yield information concerning the relationships, if any, which may exist between the oxide structures which form and that composition where the magnetic susceptibility approximates zero. It is quite possible, of course, that the mechanisms of the oxidation and corrosion reactions may be so widely different that no correlations between them may be possible. Survey OF Literature The metals, copper and nickel, which are face-centered cubic, form solid solution alloys which are face-centered cubic with no superstructure for all compositions. Three oxides of nickel have been investigated structurally by X ray diffraction. Of

Jan 1, 1949

By D. F. Hewett

[In an increasing degree in recent years, especially since the war, men in many parts of the world are turning their attention to the problems of the future, attempting to appraise the basis and extent of man's progress and interpret the problem that he faces in the near future. The war made clear to ma persons the degree to which modern industry depends upon t continuous flow of enormous quantities of raw materials, a especially of the minerals. In many circles throughout t world, the question of adequate supplies of the mine especially the fuels and metals, for near as well as more remo needs is receiving serious consideration. As a result, persons representing the state as well as industry are looking to geologists and engineers for all the data that throw light on the distribution, extent and availability of the minerals that must serve coming generations.] Obviously, in a brief research I have been able to consider only a few sources of the metals in Europe, perhaps fifty out of a total of many hundreds. In order that the conclusions may have value, however, I have chosen districts which have been important sources during some epoch of the last three hundred years or more.

Jan 1, 1932

By Nicholas J. Grant, Noboru Komatsu

Metallographic and X-ray studies were made of oxide dispersion strengthened Cu-12 vol pet SiO2 and Cu-3.5 vol pet Al2O3 alloys following time exposures at temperatures approaching the melting. point of the matrix metal. Changes in hardness, oxide particle size and crystal structure were studied to determine the time-temperature stability of these alloys. An interpretation of the mechanism of oxide agglomeration is proposed. One of the most striking features of dispersion strengthened metal-metal oxide alloys is their stability at elevated temperatures, both with respect to recrystallization and maintenance of mechanical properties after exposure at high temperatures. A small amount of work has been done on the re-crystallization phenomenon in dispersion hardened metal-metal oxide alloys'l and several theoretical treatments have been advanced regarding the stability of these alloys by Lenel and Ansell,8 and by Grant and his co-workers.9, 10 This paper reports on metallographic and X-ray studies following various heat treatments of Cu-AI2D3 and Cu-SiO2 alloys at elevated temperatures and the effect of subsequent cold work on the recrystallizalion temperature. An interpretation of the recrystallization behavior of this type of alloy, based on the decomposition and agglomeration of oxides, is proposed. EXPERIMENTAL PROCEDURE Cast ingot bars of copper-1.59 pet Si and Cu-0.77 pet Al, 7/8 in in diam, were annealed in argon for 80 hr at 1000CC for homogenization. The homogenized rods were machined into fine chips and ball milled. Milled particles in the range minus 20 to plus 60 mesh were separated for internal oxidation. The internal oxidation was accomplished by the same method used by Preston and Grant,9 except that the oxidalion temperature for the Cu-Si alloy was 750°C, and for the Cu-A1 alloy was 800°C. These powders were then hydrogen-reduced at 450°C, compacted in a copper container, evacuated at room temperature to 0.04 µ, and sealed for extrusion. They were extruded at 1400°F (760°C) with a ram speed of 55 in. per min for an extrusion ratio of 15.6 to 1 to give a rod 0.38 in. diam by about 3 ft long.

Jan 1, 1962

By R. P. Harvey, J. E. Walstrom, A. A. Brown

In view of the large number of wells directionally drilled from offshore platforms and urban drillsites, greater interest is being focused on the directional survey and on the uncertainty inherent in calculating the position of the bottom of the hole, or other benchmarks in the wellbore. Of the two methods presented here for evaluating this uncertainty, the first is analytical and uses the principles of probability and statistics. The second method uses Monte Carlo simulation to generate a pattern of the scatter of possible bottom-hole locations. Both methods are based on a model for which the usual assumption is made that the curvilinear axis of the wellbore is adequately represented by a large number, M, of linear segments joined end to end from the top to the bottom of the hole and closely following the course of the hole. The errors due to this approximation are assumed to be negligible and are not studied here. One form of the model is to consider that for a given hole there exists a perfect set of data describing it, of the above form. Each linear segment has an angle of inclination with the vertical 7, in radians, an azimuthal angle from true north xi in radians, and a length Si, in feet. The subscript variable, i, extends from 1 to M. Each of the M linear segments representing the axis of the wellbore has three components in the X, Y, and Z directions. These components are calculated from the equations: The bottom-hole coordinates as determined from the reference set of data for the wellbore are given by the following for i = 1 to M: X=SX, Y = Sy, Z=SZ; . (2) A directional survey instrument, lowered into the wellbore to the M segments, or stations, measures the values of the 7; and the 3,. In general, because of errors from various sources, the resulting angular measurements will not be precisely equal to the 7" and xi. Random variables l, and Ai are therefore considered with associated probability density functions fi(li) and gi(Ai), respectively, which represent the distributions of potential survey measurements for this hole. Since it is assumed that the values Si are accurately measured they are treated deterministically. The random variables corresponding to the surveyed bottom-hole coordinates are given, for i = 1 to M, by:

Jan 1, 1970

By Frank B. McKune

This is something new in my life. A lot of you men here today I do not know, and some I do know. So if you have any remarks to make, I wish you would give your name and the name of your company. This is the first Acid Meeting which has been held under the auspices of the National Open-Hearth Steel Conference, and I hope it is a success. Whether it is a success or not depends entirely upon the support we get. If it does get good support, I have the idea it will be continued as a regular feature of the National Open-Hearth Steel Conference. We all think we have pretty good practices. But we can all learn and I hope that you, gentlemen, who take issue with the things someone else has said will stand up and give your opinions. Otherwise, the meeting will fall rather flat, and we won't get a great deal out of it; and there will not be enough interest shown by the National Committee to continue to place the meeting on the regular yearly program.

Jan 1, 1940

By P. H. Lindon, J. C. Billington

Fe-O melts containing 0.045 pct 0 were deoxidized with Mn-Si-A1 alloys. Product compositions were reluted to the melt and alloy compositions and were found to be most sensitive to the aluminum content of the alloy. Low residual oxygen contents could be obtained when aluminum oxide was present in the Products because of the reduction of silica and manganese oxide activities. Flotation of the Products from a quiescent melt was followed both by analysis of the oxygen content and metallographic measurement of inclusion concentration. MnO-SiO2-A12O3 products were found to float most rapidly when their composition was such that their viscosity may be expected to be low. Changes in the particle size distribution indicates that particle coalescence occurred and differences in the degree of coalescence are thought to be responsible for the different flotation rates observed between products 0f differing composition. Measured flotation rates were slower than those Predicted from a model based on Stoke's Law, although alumina flotation might be reasonably accounted for by this model. Interfacial effects between oxide particles and the melt are believed to be responsible for the discrepancy. It has been recognized that deoxidation products constitute a large proportion of the nonmetallic inclusions present in killed steel. The amount of oxide inclusions which originate as deoxidation products depends largely upon three factors. These may be summarized, according to P16ckinger1 as: 1) Amount of primary products remaining in the steel prior to cooling. 2) Residual dissolved oxygen content of the steel after deoxidation. 3) Amount of secondary products, formed during cooling and solidification, which remain entrapped in the solid steel. In a well-deoxidized steel containing residual aluminum and/or silicon, the equilibrium dissolved oxygen content is usually very low and so the maximum amount of oxide which may be produced as secondary deoxidation products is small in comparison with the amount of primary products. It may be seen, therefore, that the amount of indigenous nonmetallic inclusions may be minimized if a low dissolved oxygen content is achieved by deoxidation and if the primary deoxidation products are efficiently removed. Oxides which originate by reaction of the metal stream with the atmosphere during teeming are not considered in the present study. It is known that two or more deoxidizers may result in a lower equilibrium oxygen content when used in conjunction with one another than when any of the individual deoxidizers are used alone. Equilibrium studies by Hilty and crafts2 and by Bell3 have shown that manganese increases the effectiveness of silicon as a deoxidizer, and Walsh and Ramachandran4 relate this to a reduction in the activity of silica in the products as the manganese :silicon ratio in the steel increases. It was also shown by Herty's work on deoxidation of steel by silico manganese alloys,5 that there existed an optimum ratio of manganese to silicon which gave a minimum inclusion content. This ratio was in the range 4:l to 7:l and the (FeO-MnO-SiO2) products formed by such deoxidation practice were found to lie in a composition range having very low liquidus temperatures (1170 to 1250°C approx). The optimum manganese:silicon ratio was then explained by postulating that these fluid products were able to coalesce and that the larger particles formed floated out of the steel very quickly as predicted by Stoke's Law. The present work examines the effectiveness of various Mn-Si-A1 alloys as deoxidizers and their effects on the composition and removal of primary deoxidation products from a quiescent melt. EXPERIMENTAL TECHNIQUE Approximately 250 g of prepared Fe-O alloy, containing 0.045 to 0.055 pct O, were melted in an alumina crucible and deoxidized at 1550°C by plunging a thin steel cartridge containing the deoxidizer below the melt surface. A high frequency induction furnace supplying current at 8.5 kHz was used to heat a graphite susceptor, the interior of which had been machined to give a wall thickness of 0.85 in. to form a receptacle for the alumina crucible. The iron melt was essentially quiescent as the induced current was concentrated at the external surface of the graphite susceptor by the skin effect. A nonoxidizing atmosphere was maintained over the melt by passing a continuous stream of argon through the lid of the susceptor. The melt temperature was measured before deoxidation, and again at the end of an experiment by means

Jan 1, 1970

Conquista, the uranium mining and milling complex owned jointly by Continental Oil Co. and Pioneer Nuclear, Inc., has begun operations in Falls City, Texas. The mill has been designed to produce 1.5 million lb of U3O, from 600,000 tpy of ore mined. Currently, the plant processes a maximum 2000 tpd of ore. Mine Planning Texas ore deposits are small and scattered in comparison to other uranium mining districts. Those to be mined at Conquista range from a few acres to more than 100 acres in size. Ore thickness ranges from a few inches to over 15 ft, and depth from less than 20 ft to more than 170 ft below ground surface. Distance from the mill ranges up to 35 mi.

Jan 8, 1972

By G. R. Speich

A cellular precipitation reaction in which cells consisting of an Ni3Ti (DO24) phase and austenite are formed has been studied in an austenitic Fe-30 Ni-6 Ti alloy. The variation of the growth rate and interlamellar spacing of the Ni3Ti cells with temperature has been determined m the range 400" to 975°C; the interlamellar spacing is proportional to the degree of undercooling; the growth rate can be expressed by an equation of the form G = K?T)2 exp(-Q/RT). The habit of the Ni3Ti lamellae is (001)Ni3Ti (111)y;[010]Ni3T2 [010]y. An almost perfectly coherent interface is formed between Ni3Ti lamellae with this orientation rela -tionship and the intervening austenite. This first Ni3Ti cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. CELLULAR precipitation reactions have been studied in copper-base,1,2 Au-Ni,3 pb-sn,4 and iron-base ferritic5,6 solid solutions, and this mode of precipitation has been treated theoretically by smith," Turnbull,8,9 cahn,10 and more recently by bohm.11 In the case of substitutional austenitic iron-base alloys little or no data are available, Cellular precipitation reactions are well known in austenitic nickel-base alloys12,13 but usually these reactions do not proceed to completion because of general precipitation occurring in the matrix, and they have not been studied in detail. Precipitation from an austenitic Fe-30 Ni-6 Ti alloy was studied as part of a larger investigation of the mechanisms of precipitation from substitutional iron-base alloys. This alloy, austenitic at high temperatures, decomposes at lower temperatures by a double cellular precipitation reaction. The first decomposition product consists of alternate lamellae of an Ni3Ti(DO24) phase and austenite. The reaction proceeds to completion, consuming all of the original austenite. This first cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. The first cellular reaction was studied in detail by light and electron microscopy, hardness measurements, and by X-ray and electron diffraction. Interlamellar spacings and growth rates were measured during isothermal aging in the range 400" to 975°C. The orientation relationship between the Ni3Ti and austenite lamellae was determined and indicates that an almost perfectly coherent interface exists between the two phases. This first Ni3Ti cellular reaction is of particular interest because it occurs over such a wide temperature interval. This allows cellular growth rates and interlamellar spacing data to be obtained for much larger degrees of undercooling than reported hitherto. MATERIALS AND EXPERIMENTAL PROCEDURE The Fe-30 Ni-6 Ti alloy was prepared from electrolytic iron, Mond nickel shot, and sponge-purity titanium* by vacuum melting in a zirconia crucible

Jan 1, 1963

Victor G. Hills, Cripple Creek, Colo. (communication to the Secretary): In continuation of the subject of the perform ance of "baby machine-drills," presented by Mr. Thane, I sub mit the following records of work done with these drills in the Cripple Creek district of Colorado. Two years ago, the Anchoria-Leland mine began to use baby drills ; and, to make the experiment more complete, began by purchasing two machines, of the same size, but of different make. The little drills were first used for stoping and up raising, in which they achieved at once an unqualified success. Soon after, they began to be used for the smaller branch-drifts and prospecting cross-cuts, while the large two-man drills were still used for the main drifts. Now they have almost entirely superseded the large drills, since it has been found that they will do any ordinary work in the mine at less cost, both for labor and for powder, per ton of rock broken. The large drills, of course, make more rapid progress; but it is only where time is a specially important factor that they are now used. The Portland mine, where, until within a year, only the large machines were used, is now using some small drills for stoping, and also for drifting. Mr. Thane speaks of having two men to operate a baby-drill; but in this district the baby-machine is always worked by one man without help. Again, in Prof. Christy's postscript, the quoted extract from a letter of Mr. L. T. Seymour, the South African engineer, mentions a " 2 1/2-inch Little Giant," as though that were the smallest machine used in that region. These statements leave some doubt as to just what Mr. Thane means by a " baby-drill." To avoid any such uncertainty as to the present communication, I will say that the large or two-man drill in common use at Cripple Creek has a 3 1/8-inch cylinder; while a few mines employ a 3-inch, and a few, in running large tunnels, a 3 1/2-inch drill. What we call a baby-drill here has a

Jan 1, 1900