By John P. Hager, Igor A. Wilkomirsky

The thermodynamic properties of the Pb-Ag system have been determined between 775° and 950°C by the cell: Electrotransport measurements on silica-saturated PbO-SiO2 melts established that the conduction was entirely ionic and that lead is present only in the divalent state. The activities of lead and silver exhibit Positive deviations from ideal behavior. In dilute solutions the activities of lead and silver follow Henry's law. The values obtained for yhb and yig at 1200°K are 1.49 and 1.69, respectively. Determination of a portion of the liquidus curve agrees well with the established phase diagram. provides an accurate means for the thermodynamic study of liquid alloy systems. However, Wagner and wernerl have shown that cells of type I are limited to alloy systems for which the reaction at the alloy-electrolyte interface will be extremely small. The traditional electrolyte for cells of type I has been a low melting point mixture of group IA chlorides, to which a small amount of the compound ACIZa has been added. However, the choice of a chloride electrolyte may not always be practical, in that the Gibbs free energies of formation of the compounds ACIZ, and BCIZb may not be sufficiently different to minimize Reaction [I]. On the other hand, the Gibbs free energies of formation of the oxides of metals A and B may be sufficiently different to minimize Reaction [I]. In this case, the use of molten oxide electrolyte would be clearly advantageous. In the present study, the thermodynamic properties of the Pb-Ag system have been investigated using the cell: Previous galvanic cell studies on the Pb-Ag system2'= are not reliable due to the displacement reaction between the alloys and the chloride electrolyte. Wagner and ~erner,' using Laitinen and Liu's' value at 450°C for the standard electrode potential of Reaction 111, have estimated the percent error in the activity of lead bPb) when using a chloride electrolyte. At 1000°C the error for xpb = 0.10 is 12 pct. Taking the Gibbs free energies of formation for PbClz and Ag cI,' and the equations of Wagner and Werner,' the error in apb at 1000°C and Xpb =0.10 was calculated to be 140 pct. However, using the Gibbs free energies of formation for Pb O' and an estimated value for Ag 20, the error in apb when using a molten oxide electrolyte at 1000°C was estimated to be less than 1 pct for The virtual reaction of cell I1 for the passage of n Faradays of positive electricity from left to right in the cell is: where 5 is the Faraday equivalent (23,063 cal per v equivalent), E is the electromotive force of the cell in volts, and n is the number of Faradays of electricity required for the transfer of 1 g-atom of lead through the cell. The value of n should be equal to 2 since lead is generally divalent in oxide melts. However, the presence of either tetravalent lead ions or electronic conductivity through the molten oxide electrolyte will result in a value of n greater than 2. Bockris, Kitchener, and Davies' have determined the amount of ionic conductance in a liquid PbO-SiO2 mixture (xPbO= 0.50) at 920°C by measurement of the volumes of CO and C& evolved at a carbon anode during electrolysis. From their data a value of 2.13 * 0.16 was calculated for n. Although their measurements indicate the possible presence of multivalent lead ions and/or electronic conductivity, their measurements were not at silica saturation and no definite conclusions can be drawn. However, as a result of the electrotransport measurements described in the next section the ;due of n can be taken as equal to 2.

Jan 1, 1969

By C. F. Jenkins, G. V. Smith

Serrated plastic flow in stable austenitic alloys based on Fe/Ni has been shown to be related to the presence of carbon and/or chromium in the systems. Strength peaks and plateaus in the serrated-flow temperature region for a commercial alloy correlate with an increased dislocation content, arising, presumably, from enhanced multiplication as a result of a strong interaction between dislocations and solute atoms. The data generally support a mechanism controlled by migration of vacancies, with the energy for vacancy motion being modified by the presence of chromium. Chromium atom -dislocation interaction is responsible for effects above 500°C, whereas the defect interacting with dislocations between 200" and 500°C is suggested to be a carbon-vacancy Pair. ThE phenomenon of jerky flow, serrated flow, or the Portevin-le Chatelier (P-C) effect in austenitic stainless steels is usually attributed to substitutional at1,2 mospheres1,2 or to precipitates&apos;-4 which form at dislocations during plastic deformation. On the other hand, evidence exists which supports a direct inter-stitial-dislocation interaction mechanism for serrated flow in fcc Ni-C,5,6 Ni-H7-9 and in nickel-austenites containing carbon." The present work consists in a study of serrated plastic flow in stable austenitic al-loys. The effects of carbon and of chromium were investigated separately, and a commercial stainless steel with different levels of interstitial impurity concentration was studied in an attempt to delineate the combined effects of the alloying elements. EXPERIMENTAL TECHNIQUES a) Materials and Fabrication. A commercial AISI 330 stainless steel and several specially prepared aus-tenitic alloys have been studied. The experimental alloys were prepared by arc melting the constituents under purified argon. Analyses of the materials are given in Table I. The commercial alloy was obtained as 5/8 in. bar stock and rolled to 0.092 in. sq, with several intermediate anneals. At this stage some of the material was annealed in Pd-purified hydrogen at 1100°C to establish different levels of interstitial content. All other heat treatments were in vacuum (10-5 torr). The "pure" alloy ingots were swaged to 0.120-in. rod and annealed in Pd-purified hydrogen at 1100°C. The analyses for these conditions are also contained in Table I. Following the above treatment, the final wire sizes Table I. Chemical Analyses of Test Materials Hrin Hydrogen at Cr, Ni, Alloy 1lOO°C wt pct wt pct C, ppm* N, ppm* Type 330 As-received 14.78 33.25 430 300 Type 330 64 14.78 33.25 40 50 Type 330 200 14.78 33.25 27 21 Fe/35 Ni 72 - 35.10 <10 62 Fe/35 Ni 200 35.10 <I0 44 Fe/35 Nil15 Cr 72 14.95 34.94 <I0 61 Fe/35 Ni/15Cr 200 14.95 34.94 <10 45 Fe/35 Ni/C $ 35.OM 380 *Sensitivity: N t 5 ppm Ct10ppm. f Nominal Ni content. % A master NiC alloy was used in preparation of this material; courtesy of D.E. Sonon. were obtained by either swaging or cold drawing. The test results did not vary with these techniques. b) Specimen Preparation. Two sizes of specimen and two gripping systems were used. i) 0.070-in. wire with a chemically milled gage section: 0.75 in. long, 0.060 in. in diam. These were fastened into grips containing tapped grooves. ii) 0.050 in. wire, gage length 1.5 in. Ball bearings were welded to the ends of the wires and the gage length was taken to include all material between the welds. Socket-type grips were used with these specimens. With specimens of type ii), joining was performed in a specially constructed brass jig, under argon, and automatic timing was utilized in the procedure. No adverse effects of welding were noted. Specimens were encapsulated and solution treated for 1 hr at temperatures selected to produce the same average grain size, -50 µ. Annealing twin boundaries as well as normal crystal boundaries were counted. The temperatures used are listed in Table 11. Table 11. Specimen Size. Temperature of Heat Treatment and Resulting Grain Diameters for Test Materials Recrystallization Resulting Material Condition Temperature Grain Sue AISI 330 Not H purified 0.070 120O°C 45 to 55µ in, wire AlSl 330 H , pure, 0.070 in. 1150°C 45to55µ wire Fc/35Nil15Cr Pure, 0.070 in. wire 1000°C 45tossp Fe/Ni Pure. 0.070 in. wire 775°C 45 to 55µ Fe/Ni/C Pure, 0.050 in. wire 850°C 10 to 20p AlSl 330 Not purified, 0.050 1150CC 45to55p in. wire AlSl 330 ti, pure, 0.050 in. 1150°C 45to55p wire

Jan 1, 1970

By A. E. Back, S. F. Ravitz

When manganese ores are leached with sulphur dioxide, a large part of any zinc in the ore usually is extracted with the manganese.1 In the dithionate process,2,3 in which the manganese ore is leached with dilute sulphur dioxide gas and the manganese is subsequently precipitated by adding lime to the pregnant solution, the zinc is precipitated with the manganese. These facts suggested the possibility of applying the dithionate process to the recovery of zinc from oxidized ores or calcined sulphide concentrates. Accordingly, an investigation was begun, and preliminary tests were made on several ores and concentrates. The results were encouraging, but the need to devote available funds and personnel to other projects made it necessary to drop the work before the various factors involved in the process could be studied in detail. A brief mention of the process,4 however, elicited a number of inquiries, so that it appeared desirable to report the results of the preliminary work. The dithionate process as applied to zinc may be summarized briefly as follows: The ore or calcined concentrate is leached with dilute SO2 gas to dissolve the zinc, largely as zinc sulphate, in accordance with the following equation in which [ZnO] represents the "oxide zinc" in the ore or calcine: [ZnO] + SO2(g) + 1/2 O2 = Zn++SO4— [1] If, in the leaching step, the ore or calcine is suspended in calcium dithionate solution, the sulphate ion, as it is formed, is precipitated immediately as calcium sulphate, which is subsequently filtered off with the insoluble ore residue: Zn++SO4— + Ca++S2O6— = CaSO4(s) + Zn++S2O6- [2] An alternative procedure is to suspend the ore in water, filter off the insoluble ore residue after leaching, add calcium dithionate to the resulting zinc sulphate solution, and then filter off the calcium sulphate precipitate. In either event the zinc is obtained in the form of a pregnant solution of zinc dithionate, from which it can be precipitated as relatively pure zinc hydroxide by adding milk of lime: Zn++S2O6— + Ca(OH), = Zn(OH)2(s) + Ca++S2O6- [3] The zinc hydroxide precipitate is calcined to form the final zinc oxide product: Zn(OH)2 = ZnO(s) + H2O(g) [4] Theoretically the process is completely cyclic with respect to dithionate ion, the calcium dithionate required for reaction 2 being replaced by that formed in reaction 3. In practice, of course, small amounts of dithionate would be lost in the various filter cakes, depending on the economic washing limits. In the leaching step, however, some of the SO2 is oxidized to dithionale instead of sulphate, accord- ing to the following overall reaction: ZnO + 2SO2(g) + 1/2 O2(g) = Zn++S2O6-, [5] so that the dithionate losses are made up, at least in part. Ores and Concentrates Tested The analyses of the ores and concentrates tested are summarized in Table 1, which also includes the analyses of the calcines produced from the concentrates. The concentrates were roasted in a laboratory muffle furnace at the temperatures indicated until evolution of SO2 could no longer be detected; shallow clay dishes ordinarily were used; but calcines 2a and 2c were prepared in iron dishes, with the result that these two calcines were badly contaminated with iron scale. The "complex" concentrate, sample 1, consisted essentially of sphalerite grains containing inclusions of pyrite and other sulphide minerals too minute to be liberated by grinding within economic limits. In the " marmatitic" concentrate, sample 2, the iron was present largely as marmatite (that is, as iron sulphide in solid solution in zinc sulphide) rather than as pyrite inclusions. The zinc was present largely as the carbonate in the two "oxidized" ores, samples 3 and 4, and as the silicate in the "willemite" ore, sample 5. Leaching Tests The leaching cell was a 3-liter glass beaker placed in an electrically heated water bath manually controlled to maintain a temperature of 35°C in the leach slurry. The slurry was agitated by means of a flat paddle-type stirrer

Jan 1, 1950

By John D. Sullivan

Leaching of copper ores is a comparatively old art, probably dating back to medieval times. The leaching of mixed oxidized-sulfide ores, however, is modern. The first modern plant leaching mixed ores was at Ajo, Ariz., where commercial operations commenced in 1917. While the ore at Ajo was primarily oxidized there was always some sulfide present. The Inspiration leaching plant, which was put in operation in 1926, may be considered the first plant constructed for the extraction of both sulfide and oxidized copper. The pioneers in leaching mixed ores had a difficult task before them since they had very little fundamental data on the chemical and physical factors of leaching. For the very large amount of painstaking experimental work that was done before building the Ajo and Inspiration leaching plants the reader is referred to the original articles.&apos; For a period of several years the writer worked on problems connected with the chemistry and physics of leaching mixed oxidized-sulfide ores. This paper summarizes the experimental work and discusses various factors involved in leaching ores. It also presents many data heretofore unpublished. Among the new data are those on chrysocolla, pages 518 to 519, inclusive; dioptase, page 519; covellite, page 529; virtually all those on chalcopyrite, pages 531 to 533, inclusive; enargite, page 533; and tetrahedrite and tennantite, pages 534 and 533. The oxidized copper minerals of commercial importance in American ores are azurite, Cu3(OH)2(CO3)2; malachite, Cu2(OH)2CO3; chrysocolla, CuSi03.2H2O; tenorite (or melaconite), CuO; and cuprite, Cu2O. Dioptase, CuSiO3.H2O is less common. Brochantite, CuSO4.3Cu(OH)2, while the chief mineral in the ore at Chuquicamata, is not of major importance in the United States. Metallic copper, while chemically not so, is frequently classed as an oxidized mineral of copper. The most important sulfide minerals are chalcocite, Cu2s; covellite, CuS; bornite, Cu5FeS4; and chalcopyrite, CuFeS2. Less important complex sulfides are enargite,

Jan 1, 1934

By J. Washburn, R. Drouard, E. R. Parker

Temperature dependence of the rate of recovery in zinc single crystals after a simple shear deformation at low temperature was investigated. Some tentative suggestions regarding the annealed and strain-hardened states of a crystal are discussed. RECOVERY may be defined as the gradual return of the mechanical and physical properties of strain-hardened metal to those characteristic of the annealed material; an increase in temperature increases the rate of recovery. The annealing process in strain-hardened polycrystalline metals is complicated by the inhomogeneity of strain which always exists in aggregates. Polygonization in bent regions of the crystals and growth of new almost strain-free grains starting at points of severe local distortion1-:&apos; make it almost impossible to isolate and study the recovery process. Homogeneously strained single crystals, however, do not polygonize or re-crystallize and hence they can be used advantageously to study recovery. In such crystals strain hardening is completely removed by recovery alone. Since recovery is a process whereby certain lattice disturbances introduced by plastic flow are gradually reduced, a knowledge of the rate and temperature dependence of this process for various conditions of prestrain might be helpful in formulating a model of the strain-hardened state. For simplicity it seemed desirable to limit the type of prestrain to the simplest obtainable, i.e., simple shear strain. In the experiments to be described, recovery was studied by observing changes in the stress-strain curve of prestrained zinc single crystals held for various times at temperatures above that employed for straining. Single crystals were grown from the melt by a modified Bridgeman technique from Horse Head Special zinc 99.99 pct pure, and from spectrographically pure zinc 99.999 pct pure. They were grown as 1 in. diameter spheres and acid-machined&apos; to the final specimen contour. The test section was a cylinder about 1/8 in. high and 3/4 in. in diameter. The conical sections adjacent to the test section were cemented into the grips so the load could be transmitted to the crystal as uniformly as possible. The specimens were oriented so that in testing the maximum shear stress was applied along one of the slip directions, [2110], in the (0001) plane. Details of the production and testing of such specimens have been presented.&apos; Each test was carried out according to the following schedule: 1—The crystal was strained at — 50°C until it reached a maximum shear stress, ,,,. The strain rate was approximately 5 pct per min in all cases. 2—After straining, the crystal was unloaded before the temperature was changed. Unloading required about 3 min. 3—The temperature of the specimen was then increased from — 50°C to the temperature, T, of recovery. This change in temperature was completed in a time of less than 2 min. The specimen remained at temperature, T, for a time, t, which differed for the various specimens. 4—Thereafter the temperature was again reduced to — 50 °C in approximately 3 min. 5—While at —50°C, the stress-strain curve after recovery was obtained. 6—The specimen was then unloaded and annealed for 1 hr at 375 °C in a helium atmosphere to bring about complete recovery. Cooling to room temperature after anneal required 90 min. 7—The same crystal could be re-used for another test because the plastic properties after annealing closely duplicated those of the original crystal. The specimen was immersed during the test in a bath of methyl alcohol which, through a system of tubes, could be pumped through either of two heat exchangers to regulate the temperature; this was accomplished by circulating the liquid through coils immersed in a bath of acetone and dry ice for cooling or in a bath of warm water for heating. Test temperatures were thus maintained constant within ±1°C. The — 50°C temperature was low enough so that no measurable recovery occurred during unloading and reloading. The stress-strain curve continued after recovery along a path below, but approximately parallel to, the path of a curve obtained in an uninterrupted test. Fig. 1 shows some of the results from a specimen of 99.999 pct Zn. The amount of downward displacement of the curve due to recovery was a

Jan 1, 1954

By N. J. Grant, B. C. Giessen, R. Koch

The system Nh-Ir was investigated over the complete concentration range by metallography and X-my techniques, using forty one alloys. The solubility limits of terminal and intermediate phases and the solidus temperatures were determined. Five intermediate phases were found: a Nb3Ir, cubic, Cr3O type; tetragonal, ofecr thorhomhic, isostruc-turn1 with (ta-Rh); and a Nhlr3. cubic, AuCu, type. a Nb3lr and a Nbfr3 melt congruently; three eutectic and three pentectic reactions occur. The phase diagram of the Nb-Ir system had not been fully treated in the literature; only surveys of intermediate phases were found.1"5 In this study, the details of the phase boundaries were investigated as well as the crystallography of the intermediate phases. EXPERIMENTAL METHODS The experimental procedures such as arc melting of powder compacts, heat treatments, solidus measurements, X-ray, and metallographic observation were identical with those used in the work on the Nb-Rh phase diagram.&apos; They will therefore not be repeated here except where the conditions differed. The purity of the niobium powder was as stated in Ref. 6; the iridium powder of 99.9+ pct purity from J. Bishop and Co., Malvern, Penn., did not contain impurities exceeding 100 ppm, except rhodium (200 ppm). The melting points and vapor pressures of both elements are very similar. This fact contributed to a very small weight loss on melting and facilitated preparation of homogeneous alloys. As shown in Ref. 6 for Nb-Rh, no oxygen pick-up exceeding 200 ppm had to be considered; this was regarded as valid also for Nb-Ir. A total of forty one alloys were used in the determination of the phase diagram; their concentrations are shown in Fig. l, which presents the phase diagram. The concentration limits as determined by the weight-loss method averaged <0.2 at. pct, and never exceeded 0.5 at. pct. Heat treatments were carried out as described in Ref. 6. Depending on the concentration, only tantalum, tungsten, or iridium containers were employed, avoiding oxide crucibles altogether. Alloys from 0 to 25 and from 65 to 100 at. pct Ir were homogenized at 2095°C for 15 hr, intermediate compositions from 25 to 65 at. pct Ir for 65 hr at 1780°C. A typical annealing-time schedule is presented in Table I. Solidus points were measured as described in Ref. 6 with the modification that samples rich in niobium were held between pieces of tantalum foil and samples of high iridium concentrations were held between rhenium platelets or in iridium wire. After each run it was ascertained metallographically that no reaction with the holder had occurred. Rhenium was selected as holder material after it had been shown in separate tests that the melting points of Re-Ir alloys rise continuously from 2440°C. Metallographic examination was carried out as described in Ref. 6, and the same procedure and etchants were used successfully. While metallographic discrimination between a Nb3lr and o was easily possible, X-ray diffraction was necessary to separate al and ct2. X-ray powder patterns were taken and evaluated as for Nb-Rh6 yielding the error limits indicated in Table 111, to be introduced later. For the determination of the invariant reactions and phase boundaries, the same techniques as for Nb-Rh6 applied. The general accuracy of invariant concentrations is regarded as somewhat higher than for Nb-Rh due to the small slope of most solvus lines.

Jan 1, 1964

By James J. Halbouty

The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44&apos; gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year&apos;s sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

By James J. Halbouty

The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44&apos; gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year&apos;s sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

Lake Superior Meeting . PAGE Gathmann, Emil.-Casting and Molding Steel Ingots. Discussed by J. W. Richards.. 2 McCaffery, R. S.-The Acid Bessemer Process. Discussed by Bradley Stoughton, J. W. Richards 3 Elliott, S. R.-Athens System of Mining. Discussed by F. W. Sperr, Lucien Eaton 4 Mercer, H. T. and Paulson, A. C.-Handling and Treatment of Rock-drill Steel at Copper Range Mines. Discussed by Harrison Souder, H. T. Mercer, W. H. Schacht, C. M. Haight 5 Hayden, J. E. and Eaton, Lucien.-Building Reinforced-concrete Shaft Houses. Discussed by William Kelly, T. L. Condron, Lucien Eaton 7 Eaton, Lucien.-Mechanical Ventilation at Lake Mine. Discussed by C. A. Mitke 8 Schacht, W. H.-Steam Regenerators Reduce Coal Consumption. Discussed by 0. P. Hood, W. H. Schacht ? 9 Linton, Robert.-Standardizing at North Butte Mining Co. Discussed by Grant H. Tod, C. A. Mitke 10 Smith, H. DeWitt and Sirdevan, W. H.-Mining Methods and Costs at United Verde Mine. Discussed by C. A. Mitke 12 Davy, Myron A.-Reflecting Microscope for the Mining Engineer. Discussed by C. P. Berkey, W. A. Rukeyser 14 , Norden, J. A. and Willson, A. R.-Hoisting Equipment at Utah-Apex Mining Co. Discussed by E. M. Norris 17 Aldrich, H. R.-The Dip Needle in Stratigraphy. Discussed by H. R. Aldrich, W. 0. Hotchkiss, Carl Zapffe, E. A. Kronquist 18

Jan 1, 1921

By Michael Epstein, Daniel E. Rosner

Fume nucleation sufficiently close to vaporizing suvfaces can augment net vaporization rates into cooler environments. Environmental conditions favoring large vaporization rate enhancements are briefly discussed and a previous theoretical treatment of this nucleation phenomenon is generalized to account for the self-regulating effect of condensalion-heat release within the boundary layer. Despite kinetic limitations on homogeneous nucleation, and latent heat release, non-diffusive condensate removal processes appear to make possible large enhancements in steady-state vaporization rates, provided surface temperatures are well below the boiling point. When condensed phases vaporize (or dissolve) into cooler media, the diffusion-limited mass loss rate can be strongly influenced by the process of nucleation/con-densation (or precipitation) within the thermal boundary layer. This condensation process (which typically leads to mists or fumes in the case of evaporation into cooler gases) has the effect of steepening the vapor pressure profiles near the evaporating surface, since the condensation zone acts as a vapor sink. However. the resulting enhancement in the diffusion-limited evaporation rate can be estimated (as first done by Turkdogan1 for the case of molten iron/nickel alloys evaporating into helium) only if one has independent knowledge of the critical supersaturation, sCrit(T), required to homogeneously nucleate the vapor.* In a recent reformulation and generalization of the theoretical model of Ref. 1 it has been shown that, when log sCrit is approximately linear in reciprocal temperature, rather simple expressions can be derived4 for the ratio of the actual rate of vaporization j" to either the minimum (no condensation) rate j"min, or the maximum (equilibrium condensation) rate j"max In the present communication we wish to briefly report on further developments and implications of the formulation of Ref. 4, with emphasis on i) environmental conditions favoring large enhancements in vaporization rate, and ii) the self-regulatory influence of condensation heat release (neglected in Refs. 1 to 4) on predicted vaporization rates. Additionally, we take this opportunity to correct several misprints appear- ing in Ref. 4, and comment on Elenbaas&apos;s recent criticism5 of Ref. 1. MAXIMUM POSSIBLE VAPORIZATION RATE IN PRESENCE OF CONDENSATION A nonequilibrium theory is of interest because of the very large difference between the minimum (no condensation) and maximum (equilibrium condensation) vaporization rate. The magnitude of this maximum possible enhancement can be shown quite clearly by combining a result of Refs. 3 and 4 with the fact that for most liquids there is a simple relationship between the molar heat of evaporation, A, and its boiling point, i.e., A/(RTBp) = C, where the constant C, often called the Trouton ratio, takes on values not very different from 11.* More generally, for any substance (including The Trouton ratio (which for water is 13, for methane, 10, and so forth) will be recognized as the ratio of the molar entropy change upon vaporization (at TBP or Ttransf) to the unlversal gas constant R. Its near constancy reflects the fact that the change in atomic order upon vaporization depends only weakly on the kinds of molecules involved. those that sublime under ordinary conditions) we can define a characteristic transformation temperature. Ttransf, by a relation of the form Ttransf =A/(CR), and then examine the maximum possible evaporation rates as a function of how far removed from Ttransf are the surface temperature, Tw, and ambient temperature, T. Subject to the assumptions: 1) equilibrium vapor pressure, pv,eq, everywhere small compared to prevailing total pressure, p, and 2) negligible effect of condensation heat on temperature profile, the maximum enhancement ratio was found (Eq. [17], Ref. 4) to be: where, for most vapors, Nu/NuD (the ratio of heat transfer coefficient to mass transfer coefficient for the same configuration) is a number near unity.* Ex- *An alternative derivation of the Nu = NuD special case of this equation. revealing its validity for arbitrary velocity/temperature profiles in a laminar boundary layer, is given in Ref. 3. amining this result for a "Trouton substance", one obtains the results shown in Fig. 1, constructed for C = 11. Since we are concerned with vaporization enhancements (j&apos;max/J"min > 1) at surface temperatures below Ttransf, this area of interest is shown unshaded. One notes that at a fixed ambient temperature (hence, T/TtranSf) there is a unique surface temperature, 2T , at which j"max/j"min attains its peak value; moreover, the peak enhancement ratio, see dashed locus. Fig. 1, is: (NuA/NuD)(C/4)(Ttransf/T,). Hence, if Nu = NuD, when the ambient temperature is less than 1/4 of TtranSf the peak enhancement exceeds the Trouton

Jan 1, 1969

By H. R. Deeth, C. J. Koenig

About ten years ago nepheline syenite was introduced to the ceramic industry and the material has now found application in the various branches of the industry, namely, as a vitrifying agent in white-wares and as a source of alumina and alkalies in glasses, glazes, and porcelain enamels. Spencel described the early mining and processing developments regarding this material. Since the time of his article many research papers have appeared relating to the usage of nepheline syenite but little has been published relative to subsequent mining and processing methods. A complete indexed review of the literature was issued recently by Ohio State University.2 Since "Lakefield" nepheline syenite from Blue Mountain, Ontario (Fig I); is the only commercial ceramic-grade nepheline syenite now being marketed on this continent, discussion is limited to this operation carried on by American Nepheline Limited, Lakefield, Ont., and its subsidiary in the United States, American Nepheline Cory. at Rochester, N. Y. The Deposit Blue Mountain is a long ridge rising to an elevation of about 350 ft at its highest point above the surrounding country and extending for about six miles in a northeasterly direction across Methuen township, Peterborough County. The rock of the Blue Mountain central alkaline intrusive is fine grained, light colored and of even granitic texture. The solidified mass consists predominately of the minerals albite, nepheline and microcline in order of abundance. The average mineralogical composition for the deposit obtained by a study of 112 samples taken regularly over the whole formation is as follows:3 Volumetric Mineral Per Cent Albite.................... 54 Microcline................ 20 Nepheline................ 22 Muscovite................ 2 Mafics.................... 2 (Biotite, hastingsite, magnetite) Total................... loo The mineral nepheline (or nephelite) belongs to the feldspathoid group but is lower in silica content than are the feldspars. It is a silicate of soda, potash, and alumina (NaKAl2O32SiO2). Its presence with albite (Na2oA12O3 6SiO2) and microcline (K2O A12O3 6SiO2) gives the Blue Mountain deposit an alkali content of 15 pct and an alumina content of approximately 24 pct. While this huge alkaline mass is somewhat variable mineralogically, it has a uniform chemical composition. When the iron, mostly in the form of magnetite, is removed during processing, a remarkably uniform finished product is obtained. Geological surveying has disclosed many million tons of nepheline syenite in the Blue Mountain deposit. Diamond drilling in the area where mining is now being carried out indicates a block of about one million tons.

Jan 1, 1949

By Nicholas J. Grant, Ulf Kalling, John Chipman

D. E. Babcock (Republic Steel Corp., Youngstown, Ohio)—I would like to know what evidence you have to prove the MnO was pure MnO. I would also like to know whether you might not explain it on the basis of a temperature reversion; and, was it due to the oxidizing power of MnO? N. J. Grant (authors&apos; reply)—Briefly, we have no proof that pure MnO was used. The manganese oxide was added as chemically pure MnO,. MnO is assumed as the oxide in the reacted slag following standard molecular slag theories, especially under the reducing conditions of these experiments. The noted sulphur reversion cannot by any means be explained on the basis of a temperature reversion since the temperature effect is shown in this paper to be very small. Until a more logical explanation can be offered, backed I hope by some experimental proof, we propose to explain this sulphur reversion as stated in the paper, namely, that it is due to the oxidizing effect of the added manganese oxide. Member—How did the oxygen in the slag give you a reversion of sulphur? What was the mechanism there?

Jan 1, 1952

By N. S. Stoloff, J. N. Mushovic

Age hardening response of a Mg-Th-Zr alloy has been studied at temperatures in the range 60° to 450°C. Transmission microscopy revealed clustering of thorium atoms at low aging temperatures, supporting a previous report of GP zone formation. Peak strengthening, which is observed at 325°C, is due to the formation of a coherent, ordered, DO19 type superlattice structure, of Hobable composition Mg3Th, as plates parallel to the matrix prism planes. These plates later reveal a Laves phase structure of composition Mg2Th. The equilibrium Mg4Th phase begins to precipitate in two different forms at an early stage, competitively with the Mg2Th plates. RECENT work on the Mg-Th system indicated that, unlike most magnesium-base alloys, complex precipitation phenomena may be occurring. The partial phase diagram of the Mg-Th system indicates that an equilibrium phase, Mg5Th, is the sole intermediate phase.&apos; sturkey,&apos; however, has reported, using X-ray and electron diffraction techniques, that a metastable fcc Laves phase, Mg2Th, precedes the formation of the equilibrium compound, which he identified as closer in composition to Mg4Th. Murakami et al.3 reported that the equilibrium phase precipitates preferentially on grain boundaries and dislocations in a Mg-1.7 wt pct Th alloy; Kent and Kelly4 aged a more dilute alloy, Mg-0.5 wt pct Th, for 4 days at 220°C and found similar results. In addition, they reported that a platelike phase with a structure close to that of the magnesium matrix forms perpendicular to the basal plane and is probably ordered. Research on a Mg-4 wt pct Th alloy by electrical resistance measurements and transmission electron microscopy has suggested that GP zones may form at low aging temperatures.3 However, the electron micrographs purporting to show this phenomenon were not conclusive. In view of the fragmentary evidence concerning the nature of the precipitation processes in the various Mg-Th alloys, an aging study was undertaken to clarify the characteristics of the various precipitates which form and to correlate the mechanical properties of the system with the direct precipitate-dislocation interactions. The latter results are presented elsewhere.&apos; The purpose of this paper is, therefore, to discuss the precipitation sequence in this system. EXPERIMENTAL PROCEDURE Sheet stock (0.060 and 0.010 in. thick) of a commercial Mg-3.93 wt pct Th-0.42 wt pct Zr alloy (designated HK3lA) similar to that studied by sturkey2 was supplied through the courtesy of Dr. S. L. Couling of Dow Metal Products Co. Zirconium does not enter into any precipitation reactions,&apos; but is present primarily as a grain refiner. The alloy was chill cast, warm rolled to 0.090 in. thick stock, and then finally reduced by a combination of hot and cold rolling. The alloy chemistry is given in Table I. This material was solution treated at 580°C for 4 hr in a dry CO2 atmosphere, and then water quenched. Material in this condition was fairly clear of precipitate particles and was fully recrystallized. Aging at temperatures less than 200°C was accomplished by immersing the alloy in a silicone oil bath; for higher temperatures, aging was done in a salt pot. Age hardening treatments were conducted at 60°, 80°, 105°, 135°, 160°, 250°, 325°, 350°, and 450°C for times ranging from 5 min to 400 hr. Hardness tests were performed on chemically polished 0.060-in.-thick blanks of solution treated material which were aged at the various temperatures for increasing lengths of time. For aging temperatures above 150°C the Rockwell Superficial 30T scale was employed, while samples hardened at temperatures below 150°C were monitored with the 45T scale. Each data point consists of at least three separate readings. Yield stresses also were measured at room temperature on both 0.060 and 0.010 in. sheet specimens aged at 325°C. The aged foils were thinned by the window method in a solution of 80 pct absolute alcohol and 20 pct concentrated perchloric acid (70 pct) maintained at 0°C. A stainless steel cathode was used and the applied voltage was 10 to 15 v. Thinned samples were rinsed in distilled water and pure methanol. After the me-thanol rinse the thin foils were quickly dried between filter paper. Foils prepared by the above method were examined in a Hitachi HU11B electron microscope operating at 100 kv. RESULTS A) Hardness. The hardness data are depicted in Figs. 1 and 2. Peak strengthening occurs at 325°C after aging about 6 min, see Fig. 1. Significant strengthening is achieved also at 350°C, but aging at 450°C produces only softening. The stepped curve at 250°C indicates that a complicated precipitation process may be occurring at that temperature. Fig. 2 suggests that at least two hardening mechanisms exist since the lowest temperature hardness peaks are displaced to the left of the peaks obtained at 135° and 105°C. A great deal of scatter is observed at long times in all cases due to magnesium surface degradation caused by the silicone oil bath. B) Identification of the Strengthening Precipitates. The structure formed atlowagingtemperatures (c10O°C) was not clearly resolvable by transmission microscopy. The only bright-field evidence for a change in structure was a mottled appearance which could be observed at extinction contours, as shown in Fig. 3(a), and the disappearance of this effect when dislocations produced under the influence of the electron beam passed through the matrix, as noted in

Jan 1, 1970

Graham Macfarlane, Louisville, Ky. (communication to the Secretary*):—In the paper by S. Whinery under the above caption mention is made of the occurrence of Clinton iron-ore in Kentucky and Tennessee. I believe that this is really a ferruginous limestone in what the Tennessee Geological Survey calls the Fernvale formation. In Davidson and Sumner counties, Tennessee, this occurs at about the horizon stated by Mr. Whinery. The maximum thickness of the deposit is from 10 to 12 ft., but it averages between 6 and 8 ft., lying practically horizontal. The Red River Furnace Co., under my direction, opened a mine in the Fernvale " red rock" near Goodlettsville, Tenn., several years ago. When it was first found we assumed it to be Clinton ore, but the absence of the characteristic Clinton fossiliferous structure and other evidence satisfied us that it is really limestone saturated with iron oxide. I think the very low ratio of SiO2 and Al2o3 to iron content as compared with the usual ratio in the Clinton ore is also evidence in favor of its being the Fernvale. The Tennessee Geological Survey states that at outcrops where this ore has been leached it carries about 44 per cent. of iron; under cover, from 20 to 25 per cent. of iron and from 3 to 6 per cent. of silica, the remainder being chiefly calcium carbonate. Its phosphorus content is irregular and generally rather high for a foundry-iron mixture. Since it is more than self-fluxing, we have at times operated with a mixture of brown hematite and red ore with no limestone.

Jan 1, 1913

C. D. Demond, Anaconda, Mont. (communication to the Secretary*) :—In order to throw some light on this interesting subject, a series of experiments were made with strips of mild steel, containing about 0.14 per cent. of C and 0.22 per cent. of Ma. These strips were thoroughly cleaned and brightened before use, salts were added to distilled water until it corresponded as nearly as possible to the analysis given by Mr. Lee, and in this water at different temperatures were placed four strips of steel; while four other strips, at corresponding temperatures, were placed in the water used at the Washoe Reduction Works. The latter plant has had no trouble from corrosion of furnace-jackets, pipe-lines or boilers. The analysis of the water used at the Washoe works is: Grains er U. S. Gallon. CaCO3........... 2.92 CaSO3........... 0.76 MgCI3........... 0.64 MgCO3........... 0.58 A1203........... 0.12 Fe2O3........... 0.12 SiO2........... 0.58 NaCl........... 0.35 Organic matter, etc.,........ 1.16 7.23 This water is neutral to litmus; while the artificial Copper Queen water was very slightly alkaline, which Mr. Lee informs us is also true of the water at Douglas. Both waters mere well aerated by pouring from beaker to beaker, and by blowing in air from the experimenter&apos;s lungs. The results of these tests, given in Table I., show that there is no significant difference between the effects of the two waters.

Jan 1, 1909

By E. W. Davis

IF the tonnage of merchantable iron ore remaining in the Lake Superior district is divided by the average of the annual shipments for the past 20 years, it will be found that this ore supply will be exhausted in approximately 35 years. This computed exhaustion period would be an indication of the future activities of the iron-mining industry if it were not for the fact that merchantable ore is being manufactured from low-grade ore, of which there is an almost inexhaustible supply in the Lake Superior district. It is true that at present only the simplest of these low-grade ores are being concentrated to any considerable extent, but progress is being made with the treatment of the more complex ores, and now, in addition to 20 washing plants on the Mesabi Range, three plants are equipped with jigs for the treatment of ore that cannot be concentrated simply by washing. The latest addition to the ore-treating plants of the Mesabi Range is a magnetic roasting and concentration plant at Cooley, Minn., in which ore that cannot be concentrated either by washing or by jigging is roasted to the magnetic state and concentrated on magnetic separators. This plant is beginning its third season of operation, and while it is too soon to make definite predictions, there are strong indica-tions that this new process may make commercially possible the manu-facture of high-grade, merchantable iron ore from large quantities of low-grade ore now considered worthless. After the iron oxide contained in an ore has been converted to mag-netite, almost any desired grade of concentrate can be produced, using magnetic-concentration equipment of the types now in general use for the concentration of the natural magnetites of New York, New Jersey and Pennsylvania. The conversion of hematite (Fe2O3) to magnetite (Fe3O4) is easily accomplished by heating the ore to a dull red tempera-ture in a reducing atmosphere. The reaction is slightly endothermic, and while it requires 200 B.t.u. to heat to 900° F. one pound of hematite ore containing 45 per cent Fe, it requires only 100 B.t.u. to convert the oxide into magnetite. In the laboratory, using small quantities of ore, this conversion is very simple, but large furnaces suitable for commercial

Jan 1, 1936

By Frederick Prime

In this second supplementary list no titles to which an * is pre fixed hare been seen by tlie compiler; and he will be most thankful to have any omiesisne or inaccuracies in the list sent to hiin to be ptiblisi~cd as a third supplement in the next volume of the actiotra. The author is indebted to Prof. J. J. Stevenson, of New Tork, Prof. P. R. Uhlcr and John &apos;CV. M. Lee, Esq., of Balti more, and Lloyd P. Smith, Esq., of Philadelphia, for valuable assistance. office, allkntorn iron compaxy, 30 South Third Street, Philadelphia, September 5th, 1881. Alabama. Geologiml Survcy of Alabama. report of Progress for 1879 and 1880, by Eugene A. Smith, State Geologist. Montgomery, 1881. 8vo., 158 pp., and 2 maps. California. Omit Report of Hon. T. Butler Ring, iu sopplemeut I. For Trask&apos;s Geology and Illdustrial honrecp, etc., in Supplenlvut I., read Tyson&apos;s, etc. Fremont&apos;s Menloir on Upper Califijrnia, is also published as XXXth Congress, lat Session. Senate Ms. Doc., No 148, and has a map. For Randall&apos;s Report in Supplement I, rend Report of the Special Committee in favor of a Geological Snrvey, subrn-itted by Mr. Randall, April 24th, 1861. n.d., 1851. 8cWo., 19 yp. XXXIst Congress, 1st Session, Sen. Ex. Doc., No. 47, Part 2 [Part 1 is Tyson&apos;s Report.) RejW of the Secretary of War in further compliance with the Resolution of the Senate?, calling for Colbies of

Jan 1, 1881

By L. A. Roe, E. A. Elevatorski

Wollastonite, named after William H. Wollaston, an English chemist, is a calcium metasilicate, CaSiO3; CaO: 48.30%, SiO2: 51.70%. It has a short history as an industrial mineral. The earliest production of wollastonite is reported to be from a deposit near Code Siding, located north of Randsburg, CA. At this locality small tonnages of wollastonite were quarried during 1933-34 and 1938-41, and processed into mineral wool. This operation was largely experimental and virtually no United States production was again reported until the 1950s when a large deposit near Willsboro, NY, was developed by the Cabot Corp. A processing plant was placed onstream in 1953, with nearly continuous production to date. It is currently operated by NYCO, a division of Processed Minerals, Inc. Since 1958, wollastonite deposits in the Little and Big Maria Mountains of Riverside County, and in the Panamint Range of Inyo County, both in California, have operated intermittently for production of both ornamental and commercial wollastonite. During 1980, the United States was the major producing country, furnishing about 75% of the world&apos;s output. Current production comes from Finland, Mexico, India, and Kenya. Small amounts have been shipped intermittently from the USSR, New Zealand, Republic of the Sudan, Republic of South Africa, and Namibia (South-West Africa). The principal use of wollastonite is in the manufacture of plastics. Other uses are for paints, ceramics, adhesives, fluxes, glazes, thermal insulation board, and refractory products. Mineralogy Pure wollastonite, CaSiO3, has the composition of 48.3% CaO and 51.7% SiO2. However, it is seldom found in the pure state due to the ease with which it takes into solution the metasilicates of manganese, magnesium, iron, and strontium. Predominantly, wollastonite occurs as a contact metamorphic deposit forming between limestones and igneous rocks. Commonly associated minerals are garnet, diopside, epidote, calcite, and quartz. It has a specific gravity of 2.8 to 3.0, and hardness of 4.5 to 5 on Mohs&apos; scale. When pure, it has a brilliant white color, but with impurities it may be grayish or brownish. Luster is vitreous to pearly. Melting point of wollastonite is about 1540ºC. Wollastonite occurs in coarse-bladed masses, rarely showing good crystal form. It is usually acicular or fibrous, even in the smallest of particles. The most unique property of crushed and ground wollastonite is its cleavage. Fragments of crushed wollastonite tend to be needle-shaped, imparting a high strength, and this property is the basis for many of its uses. The fiber lengths are commonly in the ratio of 7 or 8 to 1, length to diameter. The average diameter of wollastonite is 3.5 µm. Some crystals of wollastonite fluoresce under short-wave or longwave ultraviolet light, or both, with colors ranging from yellow-orange to pink-orange. Specimens may also show phosphorescence. The acicularity of wollastonite is a property of considerable importance to the marketplace. The plastics industry makes utilization of high aspect ratio grades of wollastonite (20:1) for reinforcing thermoplastics and thermoset polymer compounds. The naturally high pH of 9.9 (10% water slurry) is a prime property to the coatings industry. The coatings industry uses milled grades of wollastonite as a pH stabilizer in interior and exterior PVA and acrylic latex systems. Processed wollastonite can have a G.E. brightness of 90 to 93. Chemically, wollastonite is inert and this property makes it useful as a filler and reinforcing agent. There are two polymorphs of calcium silicates: wollastonite, a low temperature form, and pseudowollastonite, a high temperature

Jan 1, 1983

By Craig R. Barreft, Oleg D. Sherby

The steady-state creep characteristics of pure polycrystalline copper were studied in the temperature range 400" to 950°C and in the stress range 400 to 7000 psi. Tests were conducted in dry deoxidized hydrogen and all specimens exhibited high ductility before fracture. Two activation energies for creep were established as a function of temperature. Above about T/T, = 0.65, the activation energy for creep was 48,000 cal per mole whereas between 0.5 and 0.65 T, it was 28,000 cal per mole. The observed temperature dependence of the activation energy for creep follows the same trend as exhibited by the self-diffusion coefficient of copper in copper single crystals and silver in silver single crystals. It is therefore believed that the rate-cmtrolling mechanism in creep of copper in the stress and temperature range studied is diffusion-dependent and is probably associated with a dislocation-climb process. The low activation-energy region is attributed to enhanced volume difFusion from the presence of dislocations which act as short-circuit paths for diffusion. THERE is extensive experimental evidence1,2 that the activation energy for creep, Q,, for pure poly-crystalline metals tested at temperatures above one half the absolute melting temperature (0.5 Tm) is a constant and equal to the activation energy for volume self-diffusion, Qsd This equality is generally interpreted as meaning that creep in this temperature range is controlled by a dislocation-climb process. The existence of high-temperature creep activation energies not equal to the respective self-diffusion values has been suggested both theoretically3"5 and experimentally.6-8 Two examples of apparent nonequality between Q, and Qsd have been reported for the cases of silver7 and copper,&apos; where activation energies for creep much lower than those for self-diffusion persist to rela- tively high temperatures (up to 0.6 T,). These observations suggest that dislocation climb may not be the only important process in the high-temperature deformation of these metals. That dislocation climb does indeed occur relatively slowly in these two metals due to their low stacking-fault energy has been suggested by many investigators.9-10 Although the creep behavior of copper has been studied extensively at low temperatures, the high-temperature activation energy for creep is not well-defined. The data of Feltham and Meakin8 indicated that Q, is temperature-dependent above one half the melting temperature, equaling a value of -30,000 cal per mole at temperatures up to 550°C and increasing to a value of -49,000 cal per mole at 700°C. No data has been reported above 700°C. The value of 49,000 cal per mole is very near the value of Qsd for copper reported by Kuper et al." as 47,100 cal per mole. In view of the lack of high-temperature creep data and the apparent temperature dependence of Q, for copper the present investigation was undertaken to determine the value of Q, over the temperature range of 400" to 950°C. It was hoped that such a study would clearly document the temperature dependence of Q, and yield significant information as to the nature of the rate-controlling creep mechanisms. MATERIALS AND PROCEDURES The material used in this investigation was high-purity OFHC copper. After rolling and recrystal-lization treatments spectrographic and chemical analyses showed only 0.0008 pct Ag, 0.0002 pctCa, 0.0002 pct H2, and 0.002 pct O2 as trace impurities indicating a purity of greater then 99.995 pct. Specimens were machined from cold-rolled sheet and the gage sections polished with 2/0 emery paper prior to annealing treatments. Annealing was done in both vacuum and dry deoxidized hydrogen atmospheres. No variation in creep strength was found as a result of the different annealing atmospheres. The final annealing temperature was either 700°, 800°, or 1000°C depending on the temperature range to be studied. These treatments resulted in average grain diameters of 0.03, 0.4, and 1.0 mm, respectively. The precise mechanical-thermal history of these

Jan 1, 1964

By N. N. Breyer, W. R. Warke, S. Dinda

A model for the low-temperature peak, LTP, in fcc metals is presented. In high stacking fault energy metals, e.g., aluminum and nickel, it is proposed that a reversible dislocation glide and climb process might give rise to the observed high relaxation strengths and activation energies equivalent to volume self-diffusion values. In low stacking fault energy metals such as copper, gold, and silver, dislocation climb is energetically unfavorable at T < 0.5 Tm and the relaxation process is therefore mainly one of reversible glide. This model is used to explain the effect of a change in grain size and impurities on the LTP. THE low-temperature grain boundary damping peak, LTP, in spectroscopically pure aluminum,&apos; copper,17&apos; gold,2 nickel,3 and silver4 has recently been the subject of a detailed investigation by our laboratory. The main results are summarized in Table I. An empirical relationship was found between the peak relaxation strength, AE, and the width of the dissociated dislocation, do,* given by: do = µa2/24p? (Ref. 5) [I] where p is the shear modulus, y is the stacking fault energy,6-8 and a is the lattice parameter, Table 11. 4E is plotted against do in Fig. 1. Two regions are apparent: region (a)! which contains all but one of the metals, where AE decreases linearly with increasing do, i.e,, AE 1/do; and region (b), where ?E is approximately independent of do. A similar trend is observed when the ratio Qp/QL is plotted as a function of do, Fig. 2. (Qp and Ql are the activation energies for the peak and for lattice diffusion, respectively). In the past, when Qp and QL were found to be comparable, the relaxation peak was explained in terms of grain boundary sliding.10 The equivalence of Q, and Qb. the activation energy for grain boundary diffusion, prompted the suggestion that it was a consequence of reversible grain boundary migration on an atomic scale." A new model for the LTP, which is based on the experimental relationships in Figs. 1 and 2, is presented. In region (a) it is suggested that stress relaxation occurs through the reversible glide and climb of grain boundary dislocations; in region (b) only reversible glide can take place. The resultant effect on the grain boundary might be sliding or "a bowing out", but, since the total distance moved will be 50A, the atomic movements are considered of primary im- portance. It must be emphasized that this is only a qualitative model, but at the moment it appears the most likely way to explain the widely varying, but re-

Jan 1, 1969