By Henry Eyring, Jay W. Fredrickson

MANY theories have been advanced to explain the phenomena of elastic and plastic deformation. The object of this report is to present a mechanism for deformation, not radically differing from existing theories, but embodying certain principles and concepts of these theories. This proposed theory cannot be the complete answer to the age-old problem of deformation but it is believed that it will be a step further in the proper direction. The plastic properties of solids have recently been reviewed by Seitz and Read.1 Zener2 has reviewed and correlated the existing work on the anelasticity of metals. With these and othersa3,4,5 present theories of deformation are well-known. Of the many theories now extant, those receiving most attention have been proffered by Griffith,6 Becker,7 Smekal,8 Polanyi,9 Orowan10 and Taylor.11Although differing quite widely in details, these theories are based more or less on a common principle of flaws or dislocations that exist in the crystal lattice. The effect of stress concentrations surrounding a flaw or crack has been treated most recently by Fisher and Hollomon.12 The various authors differ as to the exact nature of the flaws or dislocations, the causes of their appearance, or the manner in which they initiate slip. All of the theories agree that the number of dislocations increases with progressing deformation. It is universally agreed that the shearing process is not a simple gliding of ideally perfect atomic lattice planes. It is also agreed that the "macroscopic process of gliding, or slip, is brought about by the spreading of a large number of locally initiated "glide steps" through the whole crystal. The occurrence of these "glide steps" is closely related to the presence of some kind of deviations from the "ideal" lattice structure, even in the undeformed crystal. These deviations are overcome "one at a time," in a manner of speaking, due to some stress-concentrating effect." PROPOSED THEORY Many solids show a continuously increasing deformation if subjected to a constant load of suitable magnitude in an extended range of temperature for a sufficient time. This deformation, or flow, may be said to be due, in general, to the tendency of the atoms or molecules in an elastically stressed body to readjust themselves in such a way that if the deformation were kept constant, a release of stress would take place. If rupture does not occur, this process of relaxation causes the rate of flow to obtain a final constant value, as shown in the curve (Fig I) obtained by Taylor and Quinney.14 In. this state the release of stress by relaxation exactly counterbalances the increase due to the elastic strain on the test pieces. .

Jan 1, 1948

By L. A. Rapoport, W. J. Leas, C. W. Carpenter

A program of scaled flow model experiments has been undertaken to study the performance of five-spot water floods. The modeling procedures are discussed and the construction and operation of the flow models are described. The tests were specifically designed to investigate the effects of injection rate and of oil-to-water viscosity ratio on oil recovery. The areal sweep of five-spot water floods was also studied, and direct comparisons between five-spot and linear flooding behavior have been established to permir better utilizatfon of core analysis results for purposes of field waterflood evaluations. INTRODUCTION For a long time reservoir engineering procedures have been confined to the consideration of idealized, one-dimensional or linear systems.11* However, direct application of the linear waterflood mechanism to the evaluation of actual field performance is justifiable only for the purposes of rough approximation. To obtain a realistic analysis of field behavior, it is necessary to account for reservoir geometry and well distribution, and to take into consideration the configuration of the flow of fluids between injection and producing wells. In the past it has been attempted to account for the complex nature of the fluid movement in the reservoir by associating each well pattern with a certain "sweep-efficiency constant", e.g., a sweep efficiency of 72 per cent for the conventional five-spot pattern.' More recently, methods of waterflood evaluation have been improved by the introduction of variable sweep-efficiency factors, defining the areal coverage as a function of cumulative water injection and viscosity or "mobility" ' ratio.""' These variable sweep-efficiency factors, derived from miscible fluid displacement experiments, require the assumption of piston-like displacement of oil by water. This implies that only one fluid, either oil or water, is moving at any one point of the reservoir ht any moment. Such an assumption, however, is incompatible with the bulk of the experimental evidence and also theoretical considerations which indicate that usually in the area invaded by water, both oil and water are flowing in varying proportions, in accordance with the relative permeability characteristics of the porous medium. Another recent approach toward the evaluation of five-spot flooding behavior involves correlations of the areal sweep efficiency (observed in immiscible fluid experiments) with a "mobility ratio," based on the consideration of the "average" relative permeability to the displacing fluid. Combination of these correlations with a modification of the Buckley-Leverett frontal-drive equation leads to a computational procedure for predicting the recovery performance of areal water floods. While of considerable interest, this approach has no complete theoretical justification and, therefore, does not entirely clarify the features of five-spot water floods. Rigorous, theoretical treatment of waterflood behavior in two- or three-dimensional systems as encountered in the reservoir, including proper consideration of relative permeability and capillary-pressure functions, is as yet beyond the scope of analytical or computational methods. The, behavior of such water floods can, however, be studied by means of scaled flow model ekperiments, which is the approach followed in these investigations. The flow model experiments described in this paper simulate a uniform, horizontal formation of constant thickness with fully penetrating wells. The system under consideration is entirely liquid saturated and not influenced by compressibility effects, which is representative of the situation achieved after gas fill-up under practical conditions. Gravity segregation effects are assumed to be negligible, which implies a relatively thin reservoir formation and/or low vertical permeability. THEORETICAL CONSIDERATIONS For a flow system of uniform thickness with no appreciable effects of gravity segregation, the analysis of water-oil displacement can be confined to a two-dimensional treatment based on the consideration of a "slice" of unit thickness. Referring to previously established derivations," the displacement of oil by water in such a system can be described by the following, dimen-sionless equations:

By W. L. Fink, R. S. Archer

This paper describes results obtained on aluminum-beryllium alloys and aluminum-beryllium-copper alloys in the preparation of which aluminum of 99.95 per cent. purity was used. The constitution and structure of the high purity binary alloys are given. The aluminum-beryllium eutectic occurs at 0.87 per cent. beryllium and 645° C. The solid solubility of beryllium in aluminum at 631° C. is 0.05 per cent, beryllium, and at room temperature is less than 0.013 per cent. beryllium. The densities of the alloys are substantially the same as the values calculated on the assumption that the densities of the elements are not changed by alloying. All of the alloys age-harden at room temperature after a solution heat treatment, and the chill cast aluminum-beryllium-copper alloys age-harden at room temperature without a prior solution heat treatment. Hardness and tensile properties are given. Salt spray corrosion tests on sheet specimens are described. It is shown that beryllium docs not lower the corrosion resistance of aluminum to salt spray provided the alloy has received a solution heat treatment. Commercial Possibilities of Beryllium Alloys Beryllium has certain properties such as low density, high hardness, good corrosion resistance, low thermal expansion and fairly good electrical conductivity, which would indicate that it is worthy of consideration as an ingredient of light alloys. It was not until recently, however, that beryllium could be produced with sufficient ease to encourage research along this line. The production of beryllium by electrolysis from a fluoride bath has now developed to the stage where it could be used commercially if there were sufficient demand for the element. Claims made in certain newspapers and technical articles in regard to thc strength and corrosion resistance of thc aluminum-beryllium alloys are not justified by experimental results. Moreover, beryllium is an expensive metal ($200 a pound at the time this work was done) and, on account of the nature of its ore and the consequent difficulty of its extraction, it will in all probability continue to be a relatively expensive metal, although the cost would undoubtedly be a great deal less than $200 a

By J. L. Gillson

Historically, rock deposits and sand deposits of titanium minerals came into production about the same time, although there may be some argument as to what is meant by production. Beach deposits of heavy minerals in India (Figs. 1-4) and Brazil (Figs. 5) were worked for monazite about the turn of century, but as there was then no market for titanium minerals, these were thrown away. The rock rutile deposits at Roseland, Va., Fig. 6, were worked to supply rutile for titanium chemicals and for coloring ceramics long before there was a titanium pigment business. The pigment industry started about the middle twenties, both in Europe and the U. S., and almost simultaneously the rock deposits at Ponte Vedra Beach near Jacksonville, Fla., were worked for titanium content. Since those days, production from both types of deposits has continued to grow at a rapid rate; many deposits of both types have been found, and reserves have grown to very large figures. In total tonnage of reserves, there is no doubt that the rock deposits are far ahead of the sand deposits; nevertheless there is a very large tonnage of commercial sands available. It is the quality of titanium mineral in the sand and the relatively lower costs of operating sand deposits that have kept them abreast, at least in annual tonnage produced, with the rock deposits. The principal titanium mineral used is ilmenite, but as soon as that mineral began to be sought as a titanium ore, it was obvious that there are ilmenites and ilmenites. Textbook ilmenite should have the composition FeOTiO2 and should analyze 52.6 pct TiO2 and 36.8 pct iron as Fe. The Indian ilmenite, for almost a generation the standard ore for manufacturing pigment in the U. S., was found to analyze about 60 pct TiO, and only 24 pct. Fe, and most of the iron is in the ferric condition. The whole process of pigment manufacture in the U. S. was built up on the use of a raw material of that grade, and the American chemical engineers who operate the pigment plants shuddered at the thought of using a rock ilmenite with 45 pct or so of TiO, and nearly 40 pct Fe. Intensive search was made around the world to find other deposits of rich black sand, like the Indian beaches, but although a few were found, there was some objectionable feature about each. A deposit in Senegal, south of Dakar (Fig. 7), was worked for a while, but an organic coating on the grains made attack by acid difficult. Modern practice would have included a scrubbing operation, in a caustic soda bath, to eliminate the organic coating. Brazilian deposits were numerous, but individually small, and shipping from them difficult. Deposits on the east coast of Ceylon had many attractive features, but the ilmenite analyzed only 54 pct TiO2 and could have been used only with a penalty. Sand deposits with 2 pct ilmenite, like those now worked in Florida, would not have been considered commercial ore, even if they had been known at that time. Most rock ilmenites are associated or mixed with hematite or magnetite, which accounts for the lower titanium and higher iron values than in the sand ilmenites. The Norwegians, English, and Germans, with cheap Norwegian rock ore at hand, learned to install in their pigment plants adequate capacity on the black side, as it is calltd, and counterbalanced the extra cost of plant, and larger amount of acid used, by the lower cost of ore. When World War II arrived, two of the largest pigment manufacturers in the U. S. had to learn how to use the Adirondack ilmenite, but one of them very gladly went back to sand ores when the Florida deposits came into large-scale production after the war. The other continues to use Adirondack ilmenite and finds it commercially attractive to do so. Rutile is not a raw material for titanium pigment manufacture by the sulfate process, since it is insoluble in sulfuric acid. In addition to its small consumption in chemicals and ceramics it began to be used in quantity in welding rod coatings. With the outbreak of World War 11, and the tremendous need for welding rods in shipbuilding and other structural steel construction, rutile suddenly became in heavy demand. The sand deposits on the eastern shore of Australia (Fig. 8A) which had been worked in a small way since 1934 were brought into production, and some stream placers in Brazil were worked and rutile concentrates shipped to American

Jan 1, 1960

With the exception of the mentions of coal in Illinois in the period 1660-1680, already referred to, the first coal found in the United States was in the James River, Virginia, field. In 1699 a large tract of .land above the present city of Richmond was allotted for a settlement of French Huguenots by the colonial, government, near the present Manakin, about fourteen miles above Richmond. They soon found coal, tradition says it was uncovered by a hunter pulling out a small tree in a. steel) bank near a stream, and Colonel William Byrd, F.R.S., the most prominent man of his day in the colony, wrote to the Colonial Council of Virginia, May 10 and 11, 1701: "The 10th of May, last., I with Coll. Randolph, Capt. Epes, Capt. Webb, &c., went up to the new settlements of ye French Refugees at ye Manaken Town.... We went tip to ye Cole, w'ch is not above a mile and a half from their settlement on the great upper Creeke, w'ch, riseing very high in great Raines hath washed away the Banks that the Coal lyes bare, otherwise it's very deep in the Earth, the land being very high, and near the surface is plenty of Slate.", Some of the Frenchmen were evidently familiar with the use of coal, as on May 22, 1702, "David Menestrier a black smith and one of ye french Refugees Inhabiting at Luciana Petitioning his Excellency that he may have leave to use ye coal mines lately discovered there for his forge his Excellency by and with ye advice of ye Council loth hereby give Leave to ye said David Menestrier to take what coales he shall want. out of ye said Coal mine for ye use of his forge according to ye Prayer of ye said Petition."2 There was some uncertainty about the grant of these lands to the Huguenots which caused the request for leave to use this coal, as a Virginia patent in its usual form allowed the owner to mine all minerals excepting gold and silver, which were subject to royalties for the Crown. After the visit to the coal above mentioned, "Wm. Byrd, understanding the land had not been granted to the French, took out a patent for 344 acres, including the same, (the coal) which patent was dated October 20, 1704".3

Jan 1, 1942

By L. F. Coffin

Monotonic tension and controlled cyclic-strain tests have been conducted on an annealed steel at various strain rates and temperatures in the weep range. Evidence of a strain-induced precipitate reaction abozle 500°C was determined from pronounced cyclic-hardening effects, increase inflow stress, inter granular fracture, drastic decrease in low-cycle fatigue resistance, and loss in tensile fracture ductility, as well as through electron-microscopy examination. It was found that strain rate as well as temperature had a pronounced effect on these observations. A parameter of the form P = T(7.95 - log ip) was determined, which was directly related to the ductility, defined either as the true strain at fracture in the case of simple tension, or as 2N 1/2 ? E p in the case of cyclic plastic strain. A highly satisfactory comparison of the cyclic life as measured and as computed from the ductility predicted by this parameter was obtained for a range of temperatures from 400° to 650°C and for crosshead speeds of 0.002 to 0.2 in. per min. MANY metals subjected to sustained loading at elevated temperatures derive resistance to creep from solid-state reactions of various alloying constituents. These reactions can be many and varied, and occur as a consequence of time and temperature according to reaction-rate principles. Strong evidence exists that many of these reactions are influenced by plastic strain, the argument being put forth that dislocations act as sites for nucleation and growth for the new phase.' Many examples can be cited where plastic strain during transformation influences the structure, and as a consequence affects the properties.2 The low-alloy steels serve as particularly good examples for investigating the effect which aging reactions have on resulting properties. Alloying elements such as carbon and nitrogen, and carbide formers such as manganese, chromium, molybdenum, and so forth, can, by the particular aging reaction which occurs, produce strengthening effects at various temperatures, and so endow strength to the alloy over a broad range of temperatures. These effects have been systematically studied by Glen both during creep3 and for constant strain-rate tension testing.4,5 The work of Glen is of considerable interest in connection with the present study, particularly in regard to the effect of various alloying additions on the true stress-strain curve and on fracture ductility at various elevated temperatures. He has shown that strain-age hardening occurred during plastic straining, which was quite specific both to the temperature of the test and to the alloying element involved. When strain-age hardening was noted at a particular temperature, a .minimum in reduction of area was also obtained. Provided the temperature for the minimum reduction of area exceeded 300°C, all minimum ductility fractures were found to be inter-crystalline in nature. For carbon steels containing molybdenum, two minima in reduction of area were noted, one occurring at 200° to 250°C, the precise temperature depending on the percentage of molyb-

Jan 1, 1964

By E. W. Engle

For several years the Fansteel Products Co. has been engaged in e production and development of various of the rarer metals. It is at present engaged in the commercial production of tantalum, tungsten, and molybdenum in a very high state of purity. The information contained in this paper is partly a general compilation from various sources and partly information obtained as a result of recent years of work in the laboratory of this company. Tantalum, tungsten, and molybdenum form a group peculiar to themselves among the commercially available metals. Their very high melting points (tantalum 2770' C., tungsten 3350' C., and molybdenum 2550" C.) set them apart so far as the metallurgical processes for their production are concerned. Further, when properly prepared and treated they will stand a somewhat unusual degree of cold work, that is work below the temperature at which marked crystal growth takes place. Such cold-worked metal may show a high tensile strength; tantalum to 130,000 lb. per sq. in., tungsten to 490,000 lb., and molybdenum to 260,000 lb., in the form of fine wire. In physical appearance, these metals are not unlike some steels; they may be better described by saying that polished tantalum somewhat resembles lead; polished tungsten, iron; and polished molybdenum, nickel. The polished surfaces of all three remain untarnished in ordinary air. Air containing corrosion-producing impurities will, in general, show molybdenum the least resistant to corrosion and tantalum the most resistant. Molybdenum has, however, a high degree of resistance to corrosion by hydrochloric acid, a property that should render it of commercial interest. On the other hand, it is markedly attacked by some of the weaker organic acids. The three metals oxidize rapidly when heated at or above a dull red in air. This feature limits their use in many applications where their high melting point and strength make them appear usable. Tungsten and molybdenum, at red heat, are quite inert to hydrogen and nitrogen; while tantalum has a rather remarkable affinity for all the ordinary gases, which results in its becoming embrittled in their presence. This

Jan 1, 1925

By Leon H. Nelson

Several factors which affect the segregation and solidification of killed hot-topped steel ingots are: (1) pouring temperature, (2) volume in the hot top, (3) taper in the ingot, (4) pouring rate by varying the nozzle size, (5) segregation of several elements, (6) moving ingots before completely solidified. In most of this discussion, segregation will be measured in terms of carbon variation only. All the data given are results on S.A.E. 1040 analysis of fully killed steel direct-poured in hot-topped molds giving 20-in, square ingots. Thus the variables of analysis and ingot size and contour are eliminated. Segregation results are all on the rolled-bloom size, not on the ingot itself. They are results from plant-control work and not results of special research on ingot segregation. Pouring Temperature The temperature (or, more correctly, the amount of superheat above the liquidus-solidus) of the steel entering the ingot is, of course, one of the most important factors influencing segregation and solidification. Table 1 gives the average segregation of a number of heats of S.A.E. 1040 steel with normal pouring temperatures of 2775" to 2825" F. The table also gives some data on segregation in hot heats (pouring temperature 2840" to 2870" F.) and in cold heats with some skull (poured at 2725" to 2760" F.). The results in Table 1 are on steel ingots with 20-in. square cross section and 60 in. long to the hot top. The ingot weighs 7100 lb. and the hot top contains 14.3 per cent of the total ingot volume and 11.2 per cent of the total ingot weight. The results are from drillings after rolling the ingots to bloom size. Segregation results obtained on the bloom are probably not as great as they would be in the ingot itself, since heating the ingots for rolling can perhaps cause some migration of carbon from regions of high and low carbon to those of average carbon content.

Jan 1, 1937

Jan 4, 1976

By W. E. Keck, Paul Jasberg

THERE is a considerable tonnage of iron ore in the Menominee Range of Michigan that is unsalable only because it has too large a content of sulphur. Beneficiation of such ore is economically desirable, as a relatively large quantity of finished concentrate would be obtained (deleterious sulphur mineral content being generally less than 5 per cent) and because large blocks of such ore have been developed incidentally during search for low-sulphur ore. Research on the flotation beiieficiation of these high-sulphur ores consisted of: (1) a study of the flotative properties of the principal minerals in a nearly pure state, (2) flotation of synthetic mixtures of these pure minerals and (3) application of this experimental information to samples of the ores. Gypsum in iron ores is extremely deleterious; but when sufficiently free from impurities it is a valuable commodity. In 1934, the United States produced 1,500,000 tons of calcined and uncalcined gypsum valued at $13,700,0001. Of this quantity and value, Michigan produced approximately 19 per cent4. Thus this investigation may also prove to be of interest in connection with the gypsum industry if minerals separation, such as flotation, becomes necessary in the future processing of gypsum. Data on the flotative properties of gypsum would also be of interest to the science of flotation because such information has been extremely limited. The technical literature reveals one reference to the flotation of gypsum, in which was discussed the use of the mineral, with several others, to determine the relation between the floatability of minerals and the pH of the flotation solution2. This investigation necessarily was not comprehensive in regard to gypsum, but it did show that the mineral could be floated with oleic acid under varying pH conditions.

Jan 1, 1937

By Clarence Thom

This chapter presents, in summarized form, standard procedures for making separations of minerals from their ores by the froth flotation process to produce marketable concentrates. These are typical mineral separations which are being made commercially with the reagents and conditions generally used in the mining industry. Typical separations are presented for 17 metallic and 11 nonmetallic ores. The review of each includes a brief description of the mineral and the particular problem presented, general market specifications for its concentrates, an outline of treatment method, and kinds and quantities of reagents usually employed. This chapter does not include de- tails about ore preparation (crushing, grinding, and classification), elements of ore and pulp transportation (conveying and pumping), or concentrate preparation for market (thickening, filtering, and drying). In each presentation it is assumed, if not detailed further, that the ore is ground to the economical point of liberation of the minerals to be separated. Specific information, such as ratio of concentration and recovery, that depends upon the grade of ore being treated is considered beyond the scope of this chapter. Effective flotation separations that produce marketable concentrates may produce widely varying results in terms of percent recovery and still be economically profitable operations. Details of plant practice on specific ores are presented in Chapters 16 and 17. In this chapter the chemical names of the reagents are given. The extent to which different reagents are used in flotation plants in the U. S. is presented in Chapter 4. A compilation of the various flotation reagents, their trade names, manufacturers, and use has been prepared by H. T. Spedden. ANTIMONY The principal ore mineral of antimony, stibnite (Sb2 S3), is generally found in the U. S. in ore bodies in association with other valuable minerals such as galena (Pbs), sphalerite (ZnS), chalcopyrite (CuFeS2), or tetrahedrite (3Cu2 S – Sb2 S3), The sulfo-salt minerals of antimony, such as tetrahedrite or pyrargyrite, are often associated with high silver values, so that the presence of antimony may indicate economic importance even though the actual antimony content is low. Antimony is also significant to the mineral economy because of its occurrence in some ores where lead, gold, and silver are the

Jan 1, 1962

By Edward Skewes

In view of the importance of the Cripple Creek district, the large amount of the publications concerning it, and the circumstance that many members of the Institute reside in it, or are familiar with it through repeated visits, it is surprising that our Transactions should have remained so long without any contributions on the subject. The same observations may be made with regard to the Witwatersrand, in South Africa, the other great productive gold-field of recent development. And I suppose the explanation is the same in both cases, namely, that the members of the Institute persoilally acquainted with the

Jan 1, 1897

By L. W. McKeehan

Jan 1, 1934

By C. W. Lawr

THE ores mined by the Santa Gertrudis Co. at Pachuca, Mexico, are mainly silver-bearing; they also yield some gold and carry a little copper. Strong cyanide solutions are used to dissolve the silver and gold, and the mechanical loss of cyanide at the tailings filter has been considerable. Prior to the year 1923, the pulp, after agitation, was given a 35 to 37-min. wash with barren solution in a Butters-type leaf filter; the discharged slime cake was repulped and pumped into eight Merrill self-sluicing slime presses in which the slime was given a further wash with barren solution for 25 to 35 min., followed by a 10-min. water wash. At that time the barren solution titrated around 0.350 per cent. free KCN and 0.500 per cent. total KCN. (Aero brand cyanide is used.) It can readily be seen that a 10-min. water wash would leave considerable cyanide in the filter cake, which of course was a total loss. This averaged 0.522 kg. (1.15 lb.) KCN per ton of solution. As the daily discharge to. the dam was 1600 tons1 of slime of a 2: 1 ratio of liquid to solid, the value of this mechanical loss of cyanide was an important item and its recovery held alluring possibilities.

Jan 1, 1929

By Harold B. Goldman, Don Reining

The sand and gravel industry is the largest nonfuel mineral industry in the nation (Drake, 1972), Table 1. In 1970, the production of sand and gravel totaled 944 million tons valued at $1.1 billion. California, which leads the nation with more than 140 million tons, together with Michigan, Ohio, Minnesota, Illinois, Wisconsin, and New York, account for 43 % of the total production in the nation. In commercial usage, "sand" applies to rock or mineral fragments ranging in size from particles retained on a No. 200 sieve (0.074 mm openings) to those passing a No, 4 sieve (4.76 mm openings). "Gravel" consists of rock or mineral fragments larger than 4.76 mm, ranging up to 3%-in. maximum size. The construction industry consumes 96% of the sand and gravel produced; the remainder is sand used for specialized products such as glass (see the chapter on "Silica and Silicon"). Utilization The building industry uses sand and gravel chiefly as aggregate in portland cement concrete, mortar, and plaster; the paving industry uses sand and gravel in both asphaltic mixtures and portland cement concrete. Aggregate is commonly designated as the inert fragmental material which is bound into a conglomerate mass by a cementing material such as portland cement, asphalt, or gypsum plaster.

Jan 1, 1975

By N. J. Grant, C. F. Flo, F. B. Cuff

An investigation of the Ti-Cr system has shown the presence of a complete series of solid solutions in the ß phase, with a minimum in the solid us near 50 pct Cr. An intermetallic compound, TiCr2, forms during cooling from the ß solid solution. There is a eutectoid reaction at the low chromium side of the system. IN view of the recognition of the potentialities of titanium and its alloys as important structural materials there has arisen a need for a systematic investigation of various titanium binary diagrams. Of these, the Ti-Cr system was of particular interest because of the improved properties imparted to titanium by small chromium additions. A literature survey disclosed a partial constitution diagram that had been suggested by Vogel and Wenderott,¹ This diagram, shown in Fig. 1, is the result of work done on the Fe-Cr-Ti ternary system. Alloys containing less than 43 pct Cr were not investigated. In addition to this, a study of alloys in the Ti-Cr system was reported by McPherson and Fontana.² Adenstedt3 furnished a number of dilato-meter curves obtained from specimens containing 5, 10, and 15 pct Cr. Very recently, McQuillan4 submitted a proposed diagram covering the complete range of compositions between titanium and chromium. This diagram was in general agreement with the one described here. Experimental Procedure Sponge titanium (99.7 pct) and electrolytic chromium (Bureau of Mines analysis: 99.03 pct Cr, 0.40 pct Fe, 0.53 pct O2) were used for the initial determination of the system. Subsequent refinement of points, particularly for the low chromium side of the diagram, was accomplished by using iodide titanium and high purity chromium (National Research Corp. analysis: 0.050 pct C, 0.045 pct O2). The Ti-Cr alloys were prepared by melting 25 g charges in an enclosed, water-cooled copper crucible using a movable tungsten electrode. The atmosphere was helium, prepurified by first passing it through a drying agent and then through sponge titanium heated to 850°C. Particular care was taken to avoid any large scale segregation resulting from insufficient mixing of the components. Each charge was melted and kept molten for approximately 1 min, allowed to cool, inverted, remelted, and kept molten for an additional minute. In order to ascertain the amount of impurity pickup (oxygen and nitrogen) during the melting procedure, three iodide titanium specimens were melted in sequence and then checked for increased hardness. The specimens in the as-cast condition showed a relatively large hardness increase over the hardness of the as-received iodide titanium. The scattering on these readings was large. However, after the specimens had been homogenized at 840 °C for 2 hr and slowly cooled, the measured increase in hardness over the as-received titanium was small with a corresponding decrease in scatter. The reason for this hardness change is that in heat treating these specimens below the transformation temperature (885°C) there was a conversion from the as-cast structure to the more nearly equilibrium structure of the annealed specimen. The alloys were analyzed for chromium content and although the actual percentage was invariably low the deviation from the nominal composition never exceeded 0.6 pct Cr.

Jan 1, 1953

By Richard L. Gordon

THE PROBLEMS AND POSSIBLE SOLUTIONS Toward the end of the 19th century, American industry began a drastic reorganization. The many, small, often-regional firms were supplanted by large national corporations-often produced by mergers among the existing firms. Giant companies appeared throughout American industry and many of them were engaged in the mineral industries.a The largest combines, by far, to emerge during the period were United States Steel and Standard Oil. Long before the restructuring had run its course, widespread concern arose over the process of concentration. Efforts were made to control, if not stop, the transformation. The concern produced the Sherman Antitrust Act of 1890 and the first of many federal regulatory agencies-the Interstate Commerce Commission (see Refs. 24, 31, 42). The basic objectives of these policies remain unclear to this day. The crucial issue is whether the goal is primarily to insure development of a more competitive economy or to preserve a social structure leaving more scope for small businesses. Complications arise from difficulties in agreeing upon the meaning of these terms. Studies of the early years of the antitrust movement suggest that it involved no particular concern over the mineral industries. Objections were directed at big companies in general. To be sure, the conservation movement arose in roughly the same period and did stress the evils of monopoly control of minerals. However, direct, continuing influence of conservation policy on antitrust is not apparent. Many of the most important antitrust cases, nevertheless, involved minerals. This, of course, may be sheer coincidence; the choice of cases has never followed any obvious pattern. Certainly, no simple hypothesis can explain the interest consistently. Once it may have been true that mineral industries were more likely than other sectors to be dominated by a few large companies. Yet, often sharp reversals of such tendencies -e.g., in oil and aluminum-have not removed antitrust interest. The importance of minerals to the economy cannot satisfactorily rationalize antitrust interest. The equally

Jan 1, 1976

IT will be recalled that when educational instruction for the mineral industry began at Freiberg, at the beginning of the eighteenth century, the original aim was to organize and systematize the procedures previously followed by young men in gaining familiarity with the technology then in use. There must have been many other ideas current, even then, as to just what a young man needed to learn in order to become capable of assuming responsibility for the supervision and direction of such technical work. The problem in Europe was decidedly different from that in nineteenth-century America, because some of the European mines were actually owned and operated by the governing authority and the others were supervised, regulated, and taxed by it. The American problem was the efficient performance of technical operations; the European one was regulatory supervision. It was natural, therefore, that in the development of educational processes in Europe stress was laid on those factors which conserved and protected the interests of the state. The study of mineralogy and geology, leading to correct judgments as to the workability and value of mineral deposits; assaying, which gave the means of quantitative measurements, as did surveying; chemistry, which furnished a better basis of understanding for assaying, mineralogy, and geology; and physics and mathematics, which are the bases for the understanding and efficient use of mechanical appliances, became the core of systematic instruction for the mineral industry. It was early recognized that men could learn more than was already known about all of these subjects and education took on that dichotomy which still characterizes it; the teaching of established knowledge to the unlearned, and that of extending of the bounds of knowledge, now loosely termed research, which after two and a half centuries of work still shows

Jan 1, 1941

By G. V. Woody, J. D. Price

Many producers of by-product coke have spent considerable time and given considerable thought to the use of a substitute for low-volatile coal as an admixture with high-volatile coking coal for charging high-temperature by-product coke ovens. Generally speaking, there are two principal reasons for this, one being occasioned by the lack, in certain localities, of low-volatile coal delivered at a cost sufficiently low to permit its use, and another being the desirability of finding a substitute product with a delivered cost lower than the cost of the low-volatile coal. It was for the first of these reasons that the Colorado Fuel and Iron Corporation was particularly interested in this subject. This paper deals with the experimental work and the results obtained by that company in producing and using low-temperature char. Overcoming Defects in Coke from Colorado Coals Colorado coking coals are all of the high-volatile type and were all laid down during the Cretaceous period, which makes them something like 80 million or so years younger, geologically, than eastern coals. They behave, when coked alone, something like the Pittsburgh-seam coals. They make a very brittle, highly cross-fractured, fingery coke of fair shatter value but quite low in resistance to abrasion. Mixed with a low-volatile coking coal such as Poca- hontas or certain Oklahoma coals, they make a coke that is equal to virtually any of the eastern cokes. The inferior quality of Colorado coke has long been recognized, and a considerable amount of time, effort and money has been spent upon investigations of means for improving its physical properties. While it has been found that some improvement in quality of coke can be secured by the adjustment and control of such variables as pulverization, moisture content, oven temperature and bulk density of charge, and through the addition of certain inert materials such as pulverized coke breeze, pitch, high-volatile noncoking or semicoking coal, the benefits so gained have been comparatively small. There are no low or medium-volatile coking coals available within a reasonable freight-cost distance. Therefore a substitute for low-vol-atile coal was developed through low-tem-perature carbonization—or, more correctly speaking, through the partial devolatiliza-tion—of high-volatile coals. The blending of this lower volatile char with the high-volatile coking coal distinctly improves the quality of coke made from Colorado coal. There is nothing especially new about this idea. In 1908 a Japanese patent was taken out by Kotaro Shimomura, whose claim was: The method of making a nonfingery coke out of bituminous coals, without using natural coals of low-volatile matter; according to which a certain coal is heated at a temperature between about 300°C. and about 600°C. so as to leave about 15 to 25 per cent volatile matter in the coal; this coal is mixed with the

Jan 1, 1944

By J. D. Price, G. V. Woody

Many producers of by-product coke have spent considerable time and given considerable thought to the use of a substitute for low-volatile coal as an admixture with high-volatile coking coal for charging high-temperature by-product coke ovens. Generally speaking, there are two principal reasons for this, one being occasioned by the lack, in certain localities, of low-volatile coal delivered at a cost sufficiently low to permit its use, and another being the desirability of finding a substitute product with a delivered cost lower than the cost of the low-volatile coal. It was for the first of these reasons that the Colorado Fuel and Iron Corporation was particularly interested in this subject. This paper deals with the experimental work and the results obtained by that company in producing and using low-temperature char. Overcoming Defects in Coke from Colorado Coals Colorado coking coals are all of the high-volatile type and were all laid down during the Cretaceous period, which makes them something like 80 million or so years younger, geologically, than eastern coals. They behave, when coked alone, something like the Pittsburgh-seam coals. They make a very brittle, highly cross-fractured, fingery coke of fair shatter value but quite low in resistance to abrasion. Mixed with a low-volatile coking coal such as Poca- hontas or certain Oklahoma coals, they make a coke that is equal to virtually any of the eastern cokes. The inferior quality of Colorado coke has long been recognized, and a considerable amount of time, effort and money has been spent upon investigations of means for improving its physical properties. While it has been found that some improvement in quality of coke can be secured by the adjustment and control of such variables as pulverization, moisture content, oven temperature and bulk density of charge, and through the addition of certain inert materials such as pulverized coke breeze, pitch, high-volatile noncoking or semicoking coal, the benefits so gained have been comparatively small. There are no low or medium-volatile coking coals available within a reasonable freight-cost distance. Therefore a substitute for low-vol-atile coal was developed through low-tem-perature carbonization—or, more correctly speaking, through the partial devolatiliza-tion—of high-volatile coals. The blending of this lower volatile char with the high-volatile coking coal distinctly improves the quality of coke made from Colorado coal. There is nothing especially new about this idea. In 1908 a Japanese patent was taken out by Kotaro Shimomura, whose claim was: The method of making a nonfingery coke out of bituminous coals, without using natural coals of low-volatile matter; according to which a certain coal is heated at a temperature between about 300°C. and about 600°C. so as to leave about 15 to 25 per cent volatile matter in the coal; this coal is mixed with the

Jan 1, 1944