STANFORD UNIVERSITY, CALIFORNIA Our activities for the year 1918-19 have closed with the coming of summer. It has been a most successful year in many respects, especially in the reorganization necessary after the war conditions had passed. An INITIATION SCENE AT STANFORD UNIVERSITY. "old-days" initiation was held on the Stanford campus by the Society a few weeks ago. The accompanying picture explains some of what took place when the following men were taken into the membership: W. P. Winham, Salinas, Calif. ; T. L. Wark, Long Beach, Calif.; P. L. Henderson, Greeley, Colo.; T. E. Bassett, Palo Alto, Calif.; and R. G. Wheelton, Long Beach, Calif. CHAS. A. DOBBEL, Secretary.

Jan 8, 1919

Annual Meeting, February 17 to 19, 1914.-The following Committees have been appointed to have charge of the arrangements for the Annual Meeting in New York City: . General Committee: Louis D. Huntoon, Chairman; Arthur S. Dwight, Vice-Chairman; W. deL. Benedict, George F. Kunz, Thomas T. Read, E. Maltby Shipp. Reception Committee for Each Day: Chairmen to be announced later. Banquet Committee : Theodore Dwight, Chairman. Luncheon Committee: E. Maltby Shipp, Chairman. Ladies' Committee: Mrs. Arthur S. Dwight. Badge Committee : George F. Kunz, Chairman; E. Maltby Shipp, Vice-Chairman. Program Committee: Thomas T. Read, Chairman. Bureau of Registration and Information: Burr A. Robinson, Chairman.

Jan 1, 1914

By Charles Eichrodt

THE ore that is being treated by the present plant lies between the leached zone, or capping, and the mixed sulfide and oxide zone. The principal copper minerals are chalcanthite (CuSO4.5H20), brochantite (CuS04 3Cu (OH)2) and atacarnite, (CuC12.3Cu (OH)2). There are, in addition, some other minerals such as cuprite and kröhnkite (CuSO4. Na2SO4.2H20). These minerals, with many others, occur in a greatly crushed granodiorite rock. Most of the copper-bearing minerals occur in the cracks and veinlets, but there are disseminated values and it is probably the relative proportion of these that accounts for some otherwise unexplainable variations in extraction. The entire mineralization of the ore is complex and varies with depth. This variation, the problems presented thereby, and the effect of various constituents of the ore will be taken up in detail. An analysis of an unweighted composite of the ore treated during 1927 follows:

Jan 1, 1930

By H. H. Richardson, E. H. Dix

Of all the alloying elements used in commercial aluminum alloys, copper stands out as by far the most important, and it is perhaps for this reason that the constitution of the aluminum-copper system has received the attention of a number of experimenters covering a period of approximately 20 years. It would be expected that during this time the equilibrium relations would have been thoroughly and exactly worked out. In a general way this is true, but there is a surprising lack of agreement in the details of the high aluminum end of the diagram, particularly in regard to the solid solubility of copper in aluminum, which has been given variously as 2 per cent. to 5 per cent. at the eutectic temperature. The importance of this is much greater than might at first appear to one unfamiliar with modern commercial aluminum alloys. This is true because, with one exception, the susceptibility of the strong alloys to heat treatment depends, in part at least, upon the solid solubility relations of copper in aluminum. In 1919, Merica, Waltenberg, and Freeman1 published the first detailed information on these solubility relations. They found that the solubility of copper decreases with falling temperature from about 4 per cent. at 525" C. to about 1 per cent. at 300" C. and is apparently still diminishing at lower temperatures. In 1921 there was published a brief account of the results obtained in the National Physical Laboratory, Teddington, England.2 This laboratory, however, reported that 5 per cent. of copper is soluble in aluminum at 540" C., and that this amount decreases to about 3 per cent. at 20" C. In the same year Ohtani and Hemmi3 reported a solubility of 4.8 per cent. copper at 520" C., 2.6 per cent. at 460" C. and 1.5 per cent. at 420" C.

Jan 1, 1926

By J. E. JR. Johnson

AT the Cleveland meeting of the Institute in October, 1912, I had the honor to present a paper outlining the conditions surrounding the charcoal iron industry, and giving some of the results of an investigation started about three years ago for the purpose of determining the reason for the poor reputation of the Lake Superior charcoal irons as compared with the Southern and Eastern irons. In that paper I explained the effect of high carbon on quality, and tried to make clear that that paper was a preliminary one, as we felt convinced that we should eventually discover other factors affecting quality. The progress of the investigation has brought out facts that seem to us of the utmost importance practically and theoretically, and the purpose of the present paper is to present these facts with the proofs which seem to us to establish them. The closing year of the nineteenth century saw the publication of the first definite and connected statement of the relationship between the cast irons and the steels.' The metallurgical world was ready to accept the fundamental unity of these two series, acceptance being greatly hastened by Professor Howe's classic paper, The Constitution of Cast Iron, presented at the Richmond meeting of the Institute, February, 1901.

Jan 1, 1914

By C. C. Harris

An analytical solution of the integro-differential equation of batch grinding is proposed as a first appoximation to the xYt surface. The size distribution equation (xY plane) is a three parameter equation previously suggested. Possible refinements are outlined. Comminution kinetics research is presently following several related courses. Some are equivalent, in that they represent different ways of viewing the same facet of the problem, though the entire endeavor cannot be described as being completely integrated. The purpose of this note is to propose and discuss a framework into which the various approaches might be fitted. This must clearly be founded upon an analysis of the xYt surface.' (See also Fig. 1 of Reference 26.) The investigations referred to above comprise mainly researches into the following: (1) The kinetics of the creation of the finer sizes during relatively small grinding times. This is the Fahrenwald-Arbiter-Bhrany 2-3 approach which leads to equations equivalent to a special case of the charles4 relationship. It emerges that initial production of fines follow essentially zero order* kinetics. (2) Disappearance kinetics of the coarser fractions. This appears to be a first order relationship.5-6 (3) Prediction of the xYt surface via the selection and breakage functions utilizing computer-programmed or approximate solutions of the integro-differential equation of batch grinding.5,8-17 A recent discussion by Mika et al.5 references the relevant literature up to about 1966. In addition to these main-stream researches there is some work on the minor topic of extremely long grinding time considered as a limiting case.18-19 The field is supported by investigations into the size distribution of fragments produced by breakage processes, some of this work being most valuably statistical-mechanical in nature.20-25 Better fitting equations, however, are obtained by statistical and curve-fitting methods.26 This

Jan 1, 1969

By Lo-Ching Chang, K. M. Goldman

The kinetics and mechanism of transfer of a constituent across a slag-metal interface are fundamentally important because many metallurgical processes involve the existence of a slag phase and a metal phase. Industrial processes seldom proceed to equilibrium, and information of the rates and modes of reactions are therefore often of greater practical importance than equilibrium data. A study of the kinetics of sulphur transfer across a slag-metal interface under reducing conditions will contribute a great deal toward a better understanding of desulphurization in the blast furnace process. The general principles existing in the transfer of a constituent, such as sulphur, across a slag-metal interface can be extended to similar transfer phenomena in other metallurgical processes. The present paper will demonstrate how such studies will lead to fruitful results from both the practical and theoretical standpoints. EXPERIMENTAL METHOD The apparatus used was, simple. A graphite crucible 15/8-in. id, a wall 1/8-in. thick, and a depth of 4 in., was packed in an outer fused silica tube with powdered magnesia. The crucible assembly was rotated at a speed of 235 rpm inside an in- duction coil. A charge of 250 g of Armco ingot iron was introduced into the graphite crucible and melted by induction heating. The melt was held at a desired temperature for 3-5 "'in., aftcr which 7.5 g of granular ferrous sulphide was added and the bath was held for another 3-5 mi11. A metal sample was then taken by means of a fused silica tube and a rubber suction bulb. Immediately after the metal sample was taken, 30 g of a prefused and crushed slag were introduced. The slag reached the ternperature of the furnace in 1 to 1 1/2 min. Slag

Jan 1, 1949

By K. M. Goldman, Lo-Ching Chang

The kinetics and mechanism of transfer of a constituent across a slag-metal interface are fundamentally important because many metallurgical processes involve the existence of a slag phase and a metal phase. Industrial processes seldom proceed to equilibrium, and information of the rates and modes of reactions are therefore often of greater practical importance than equilibrium data. A study of the kinetics of sulphur transfer across a slag-metal interface under reducing conditions will contribute a great deal toward a better understanding of desulphurization in the blast furnace process. The general principles existing in the transfer of a constituent, such as sulphur, across a slag-metal interface can be extended to similar transfer phenomena in other metallurgical processes. The present paper will demonstrate how such studies will lead to fruitful results from both the practical and theoretical standpoints. EXPERIMENTAL METHOD The apparatus used was, simple. A graphite crucible 15/8-in. id, a wall 1/8-in. thick, and a depth of 4 in., was packed in an outer fused silica tube with powdered magnesia. The crucible assembly was rotated at a speed of 235 rpm inside an in- duction coil. A charge of 250 g of Armco ingot iron was introduced into the graphite crucible and melted by induction heating. The melt was held at a desired temperature for 3-5 "'in., aftcr which 7.5 g of granular ferrous sulphide was added and the bath was held for another 3-5 mi11. A metal sample was then taken by means of a fused silica tube and a rubber suction bulb. Immediately after the metal sample was taken, 30 g of a prefused and crushed slag were introduced. The slag reached the ternperature of the furnace in 1 to 1 1/2 min. Slag

Jan 1, 1949

By Peter T. Luckie, Harold L. Lovell, E. R. Palowitch, A. W. Deurbrouck, James K. Kindig

PART 1: DENSE MEDIUM SEPARATION by E. R. PALOWITCH and A. W. DEURBROUK INTRODUCTION During 1965, 64.9 percent of the 512 million tons of bituminous coal and lignite produced was cleaned mechanically, of which 95 million tons was cleaned by dense medium processes.l The percentage of bituminous coal and lignite cleaned mechanically by dense medium processes rose from 7.0 to 28.5 percent from 1938 to 1965. Dense medium separations include those coal preparation processes which clean raw coal by immersing it in a fluid having a density intermediate between clean coal and reject. As there is a general correlation between ash content and specific gravity, it is possible to achieve the required degree of removal of ash-forming impurities from a raw coal by regulating the specific gravity of the separating fluid. Dense medium processes offer the following advantages over other coal cleaning processes : 1. Ability to make sharp separations at any specific gravity within the range normally required even in the presence of high percentages of the feed in the range of e 0.1 specific gravity units. 2. Ability to maintain a separating gravity that can be controlled with ±0.005 specific gravity units. 3. Ability to handle a wide range of sizes (up to 14 inches). 4. Relatively low capital and operating costs when considered in terms of high capacity and small space requirements. 5. Ability to change specific gravity of separation to meet varying market requirements. 6. Ability to handle fluctuations in feed both in terms of quantity and quality. HISTORY Sir Henry Bessemer patented the first dense medium process in 1858. Solutions of the chlorides of iron, manganese, barium and calcium were proposed as separating liquids; the separation was made in a cone-shaped separator. One large-scale plant using calcium chloride was erected in Germany but soon was abandoned. The Chance process, using a mixture of sand and water, was first

Jan 1, 1968

By C. W. Spencer, B. F. Addis, G. H. Bishop, C. A. Steidel

STUDIES of the inter granular attack of metals by liquids have generally been confined to polycrys-talline specimens. This note reports the results of preliminary studies of the penetration of bismuth-rich Ni-Bi liquids into oriented bicrystal specimens of nickel. It is found that isothermal penetration follows a parabolic rate law and shows a definite anisatropy with respect to direction on the grain boundary surface. Nickel bicrystals containing < 100> tilt boundaries were grown using the Czochralski method. Relative misorientation of the parent crystals was controlled to ± 1deg. The boundaries are straight in the growth direction, i.e., the common <100>, and generally straight in the transverse direction, as shown in Fig. 1. The starting material, Inco HPM grade nickel was contained in a recrystallized alumina crucible and maintained under argon. Bicrystals typically contain 30 ppm C, less than 10 ppm S, O, N, and 50 ppm residual metallics, principally iron and silicon. Specimens, as schematically illustrated in Fig. l(c),were cut from bicrystal ingots using a thin water-cooled abrasive wheel. To insure removal of all residual strain, which accelerates the penetration, specimens were round through 600 grit silicon-carbide, chemically polished, and annealed for 4 hr at 1375°C under argon. The procedure described by Cheney et al.1 for exposing specimens to

Jan 1, 1962

All the TECHNICAL PUBLICATIONS and CONTRIBUTIONS published in 1940 are available at Institute headquarters, unless otherwise noted. They are also on file in many public, university and technical libraries and, when so indicated in the list, may be found in the TRANSACTIONS. TECHNICAL PUBLICATIONS in Classes A-Metal Mining, B-Milling and Concen-tration, H-Industrial Minerals, and I-Mining Geology are distributed in MINING TECHNOLOGY, which is issued every other month. Technical Publications in Classes C-Iron and Steel Division, D-Nonferrous Metallurgy and E-Institute of Metals Division are distributed in METALS TECHNOLOGY, which is issued twice quarterly. TECHNICAL PUBLICATIONS in Class G-Petroleum Division are distributed in PETRO-LEUM TECHNOLOGY, which was issued quarterly in 1940 but will be issued every other month in 1941. TECHNICAL PUBLICATIONS in Classes F-Coal Division, J-Mineral Industry Education Division, K-Mining Administration, and L-Geophysical Methods of Exploration are issued as separate pamphlets. An Institute member is entitled to one copy of any TECHNICAL PUBLICATION or CONTRIBUTION. Copies of TECHNICAL PUBLICATIONS listed have been mailed to members of the Institute accord-ing to their registration by classes. CONTRIBUTIONS and other TECHNICAL PUBLICA-TIONS will be sent upon request. A member may purchase an additional copy of a TECHNICAL PUBLICATION or a CONTRIBUTION at one cent a page; minimum charge, 25¢. Nonmembers may purchase any CONTRIBUTION or a TECHNICAL PUBLICATION of the F, J, K, or L classes at the same rate, but the nonmember price per copy for METALS TECHNOLOGY, MINING TECHNOLOGY or PETROLEUM TECHNOLOGY is $1.25 domestic, $1.35 foreign countries. TECHNICAL PUBLICATIONS (separate pamphlet form), $2 per annum domestic, $2.50 foreign. METALS TECHNOLOGY, $7 per annum domestic, $7.80 foreign (Iron and Steel Division and Institute of Metals Division ferrous and nonferrous papers). MINING TECHNOLOGY, $6 per annum domestic, $6.60 foreign (metal mining, milling and concentration, Industrial Minerals Divi-sion, and mining geology papers.) PETROLEUM TECHNOLOGY, $6 per annum domestic, $6.60 foreign. Bound volumes have been mailed to members that have requested them, and MINING and METALLURGY is mailed each month. A member is entitled to one volume a year on his membership and he may purchase for $2.50 one copy of a volume not already received; additional copies of the same volume, $5. Nonmembers may pur-chase the volumes listed, at $5 each, plus 60 cents for Canadian or foreign postage. Extra single copies of MINING AND METALLURGY, 25¢ current issue, back numbers 50¢ each to members; to nonmembers 506 current issue and $1 each, back issues. Subscription price to nonmembers and to members for extra copies, $3 per annum domestic, $4.00 foreign.

Jan 1, 1940

By Willis Burns

I. INTRODUCTION. These notes are submitted, not as a discussion of the modern practice of electrolytic-copper refining, but as the record of a refinery that was among the pioneers in the field and that is to-day, and has been for 17 years, operating under conditions not to be found in any similar plant in the country. I refer to the current density, which is at least 60 per cent. higher than that regularly employed elsewhere, and to the fact that the anodes treated are the direct product of the converter rather than of the reverberatory furnace. The writer has no knowledge of any other refinery treating anodes of this character.

Jan 8, 1913

By Arthur Knapp

Oil-well depletion curves, to be of value, should show when a well or lease may no longer be operated at a profit. The difference, at any time, between the total expenditures and the total income of a lease or well may be called the lease status. Plotting this lease status against time will give a curve subject to more accurate and different interpretations than the barrels-time curves. According to the hypothetical barrels-time curves shown in Fig. 1, well A, at the end of 16 mo., is producing twice as much oil as well B and will continue to produce for another year whereas well B will cease producing in about 6 months. Data fob Lease Status-time or Dollars-timb Curve Time Lease Months Status Lease purchased for $3000.............................. 0 — $ 3,000 No expenses chargeable to lease for 3 mo................. 2 — 3,000 Well A is started; cost of drilling for month is $16,000..... 3 — 19,000 Well is completed at additional cost of $10,000............ 4 - 29,000 Well A is brought in and flows 10,000 bbl. first month (we Fig. 1). Necessary to invest in tanks, boilers, pipe lines, etc.; difference between expenditures and receipts gives profit for month of $5,000............................ 5 — 24,000 Investment is small, cost of operating well A is small, so profits are $15,000................................... 6 — 9,000 Well ceases to flow so there is additional investment for pumping equipment and additional operating expense; net earnings from 6,000 bbl. of oil produced is $4,000. 7 ... Lease operation nor becomes normal and curve becomes smooth........................................... 8 — 500 9 2,000 10 4,500 11 6,000 12 7,700 13 8,700 14 9,000 15 9,500 16 10,000 A hypothetical lease status-time, or dollars-time, curve of this lease is shown in Fig. 2. At zero time, the lease is purchased for $3000, which is plotted below the zero dollar line, All subsequent entries are plotted

Jan 1, 1921

By F. L. Grammer

In these day, when anthracite is less extensively used as a blastifurnace fuel than it was a generation ago, and managers endeavor to maintain regular and known ore-mixtures, the " freezing " of tuyeres, cinder-notch or iron-notch is infrequeut; and, consequently, the oil-burner or " kerosene blowpipe "* is seldom employed; and furnace-foremen have, to a considerable degree, forgotten their former cunning and persistency in the use of the drill and sledge. Still, in starting new or abandoned plants with untrained labor, and in running some of our large 100-ft. furnaces, slips, resulting in very cold furnaces, may occur, even under experienced managers. During my superintendence of the Cleveland, O., blast-furnaces, such a misfortune, owing to a dearth of trustworthy foremen, was experienced; and our electrician, Mr. Thomas Martin, proposed to open the tuyeres and cinder-notch by means of the heat of the electric arc. We have heard that the surface-cracks or marks developed in rolling heavy plates have been closed by electric welding, as by a soldering-iron, and also that an electric burner has been employed at some German blast-furnaces; but the experiment was quite novel to us; and I think it constituted one of the first, if not the very first, successful application of this device, for the purpose named, in the United States. †

Jan 1, 1902

Gentlemen of the American Institute of Mining Engineers.—As you well know an application is about to be made to Congress, by the American Society of Civil Engineers, for the appointment of a cornmission composed of persons skilled in the production and use of iron, steel, and other structural materials, whose duty it shall be to test the strength, elasticity, and other quatities of such materials ; not simply the substances used as such, but the members of large structures composed of such materials, of the forms and sizes in which they are actually used. As I understand, the papers that will be read here to-night will have for their object to show the necessity for such tests, and therefore the necessity for the commission asked for. As the representative of the Society of Civil Engineers, I have to thank you, gentlemen of the Mining Engineers, for the great zeal with which yon have taken up this subject, and seconded the efforts of the Civil Engineers; or, perhaps I ought rather to say, initiated the efforts to get a suitable commission appointed to obtain most vitally important information which it is admitted on all hands we do not now possess. In drawing up the memorial to Congress, in connection with some of the ablest and best informed of our Society, and in all the discossions on the subject, I have been struck with the emphasis with which the confession is made, that so little is known of the strength of the larger-sized members constantly used in building structures of the magnitude which the present requirements of the country now demand. I presume the remarks made to-night will bring this out very prominently. This is no disgrace, for with the means here-

Jan 1, 1882

By J. E. Johnson

At the Cleveland meeting of the Institute in October, 1912, I had the honor to present a paper outlining the conditions surrounding the charcoal iron industry…

Jan 1, 1915

By Waldemar Lingren

CONTENTS. PART I.-GENERAL FEATURES. [ ]

Jan 1, 1902

By R. F. Mehl, C. S. Barrett, A. H. Geisler

THE studies of the mechanism of precipitation and of the resulting property changes in aluminum-silver alloys1-3 have presented some new concepts of the aging reaction-concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.1,4 These platelets grow in lateral dimensions and in thickness with aging time until they are thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstätten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuous precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 EXPERIMENTAL PROCEDURE The alloys were made using 99.97 per cent Al or distilled magnesium, with

Jan 1, 1943

By Howard Scott, Henry S. Rawdon

The method of demonstrating the structure existing in a metal or alloy at high temperatures, by etching a polished sample after it has been heated to the desired temperature, is quite familiar to metallog-raphists. The usual procedure1 2 is to heat the specimen, previously polished for microscopic examination, to the desired temperature, in a neutral atmosphere (hydrogen or nitrogen), then admit the etching gas (chlorine, hydrochloric acid or similar gas) for a few seconds, and finally, after flushing out the etching gas with the neutral one, cool the specimen in the neutral atmosphere. The pattern produced by etching at a definite temperature is usually taken as a record of the microstructure prevailing at that temperature. It has frequently been pointed out that changes in composition of the surface metal occur during the preliminary heating in the neutral atmosphere, so that the appearance produced by the etching at high temperature may not exactly represent the condition of the interior of the specimen. To overcome this uncertainty, the heating has sometimes been done in vacuo,3 the etching gas being admitted when the desired temperature was reached, then pumped out and the specimen cooled in vacuo. The studies of Rosenhain, Humfrey, and other workers 4, 5, 6, 7, 8 dem-

Jan 1, 1922

By Howard Scott, Henry S. Rawdon

The method of demonstrating the structure existing in a metal or alloy at high temperatures, by etching a polished sample after it has been heated to the desired temperature, is quite familiar to metallog-raphists. The usual procedure1 2 is to heat the specimen, previously polished for microscopic examination, to the desired temperature, in a neutral atmosphere (hydrogen or nitrogen), then admit the etching gas (chlorine, hydrochloric acid or similar gas) for a few seconds, and finally, after flushing out the etching gas with the neutral one, cool the specimen in the neutral atmosphere. The pattern produced by etching at a definite temperature is usually taken as a record of the microstructure prevailing at that temperature. It has frequently been pointed out that changes in composition of the surface metal occur during the preliminary heating in the neutral atmosphere, so that the appearance produced by the etching at high temperature may not exactly represent the condition of the interior of the specimen. To overcome this uncertainty, the heating has sometimes been done in vacuo,3 the etching gas being admitted when the desired temperature was reached, then pumped out and the specimen cooled in vacuo. The studies of Rosenhain, Humfrey, and other workers 4, 5, 6, 7, 8 dem-

Jan 1, 1922