Jan 1, 1970

By Eleanor Haslem, Carl A. Zapffe

THE present investigation has three principal purposes: I. To develop a method for measuring hydrogen embrittlement that avoids certain errors complicating previously used methods. 2. To explore in a preliminary way some of the fundamental factors controlling embrittlement. 3. To apply the measurements specifically to stainless grades of steel, whose sensitivity or insensitivity to hydrogen embrittlement has never been clearly defined. SELECTING A TEST METHOD Hydrogen embrittlement is a condition of low ductility resulting from excessive absorption of hydrogen by the steel at some period in its history, and may be revealed by almost any test involving cold deformation. Tensile tests, impact tests, and bend tests are commonly used for detecting hydrogen embrittlement; although numerous other tests, such as cold-upsetting or extrusion, could be used. The simplicity of using a wire specimen for cathodic and acid pickling tests, and the especial adaptability of the bend test to wire specimens, led to selection of the bend test for the present research. Bend tests usually have been of three general types: (I) fatigue, (2) reversed bend, and (3) single bend. The first two types, though widely used, are inaccurate because their measurements are counteracted by an aging effect; and the third type has not been developed to its fullest utility. The effect of cold-working in removing hydrogen is well known. During a bend test hydrogen can be observed escaping from the convex side simply by coating the specimen with oil; and any technique employing flexing or reverse bending may therefore have its measurements masked because the mechanical action reduces the embrittlement during the test. This factor is so important that even elastic flexing of a hydrogen-charged wire specimen should be avoided before testing if accurate measurements are desired. DEVELOPING A MACHINE FOR MEASURING HYDROGEN EMBRITTLEMENT As for the single-bend test, its theory is good, and recovery caused by mechanical work is kept to a minimum. With a given degree of hydrogen embrittlement, a specimen will break at a given angle if the bending is applied unidirectionally and uniformly. The radius of the bend must be kept constant; and the rate of bending should be a constant, slow enough to allow reading of the breaking angle, and yet rapid enough to prevent significant recovery from the escape of hydrogen during bending. A simple apparatus (Fig. I) was constructed using a type H Foxboro drive unit A, which is a synchronous motor with a gear-reduction ratio of 600 to I. A cord, fixed at one end to a wooden pulley B on the drive shaft of the motor, follows the pe-

Jan 1, 1946

By F. W. Steadman, Charles S. Barrett

Deformation bands of surprising regularity are found in large-grained poly-crystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron1 and brass.2,3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,6 and Brick and Williamson,8 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others," although the orientation (110) [II2]—that is, (110) parallel to the rolling plane and [TIP] parallel to the rolling direction—is generally recognized as the most prominent orientation and (112) [III] one of the lesser orientations. Other orientations have been given by some observers as (236) [535], (100) [00I], and (110) [00I]. The texture of copper has also been described as (I35) [533].6,7 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,' and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [II3] and (110) [II7] are about equally stable. Materials and Methods The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slicec 1/2 in. thick and 21/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By Charles S. Barrett, F. W. Steadman

Deformation bands of surprising regularity are found in large-grained poly-crystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron1 and brass.2,3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,6 and Brick and Williamson,8 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others," although the orientation (110) [II2]—that is, (110) parallel to the rolling plane and [TIP] parallel to the rolling direction—is generally recognized as the most prominent orientation and (112) [III] one of the lesser orientations. Other orientations have been given by some observers as (236) [535], (100) [00I], and (110) [00I]. The texture of copper has also been described as (I35) [533].6,7 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,' and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [II3] and (110) [II7] are about equally stable. Materials and Methods The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slicec 1/2 in. thick and 21/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By R. E. Reed-Hill

Recently Levine applied the Conrad-Wiedersich17 equation where H is the activation enthalpy, v the activation volume, T* the effective shear flow stress, T the absolute temperature, and ? the strain rate, to an analysis of titanium single-crystal data. The activation energy as a function of testing temperaturs obtained from specimens oriented for single (1010) prismatic slip is shown in Fig. 12. This diagram indicates a different linear dependence of H on T in the temperature interval from 220° to 300°K than from 0° to 220°K. Levine interpreted the break in this curve as indicating a change in the thermally activated mechanism controlling the flow stress. The purpose of this communication is to point out that the data in Fig. 1 is not consistent with the concept of a flow stress controlled by a simple thermally activated mechanism between 220° and 300°K. The Conrad-Wiedersich relation assumed that the strain rate can be expressed by:

Jan 1, 1968

By A. Gatti

A dispersion of AI2O3 was produced within chromium by the hydrogen reduction of a solid solution of Cr2U3-A1203. The yesulting powder. was compacted, extruded, and the material tested in tension at various temperatures and in creep at 1800°F. The material is ductile above 1200°F and is at least twice as strong as electrolytic chvomium at all temperatures. Its creep resistance, rupture strength, and ductility at 1800°F warrant further work to improve its Low -temperatutre properties. BECAUSE of its high melting point and excellent corrosion resistance, chromium has long been considered as a base for high-temperature alloys. Most chromium base alloys, however, are extremely brittle at low temperatures. Elements such as nickel and iron lower the melting point of chromium and thereby limit its high-temperature usefulness. Chromium-alumina materials made by othersl, 2 have shown good high-temperature creep resistance but poor ductility and thermal shock resistance. Pure ductile chromium3 is weak at high temperatures and reverts to a brittle state if exposed to nitrogenous atmospheres. In sintered aluminum powder (SAP)4 and internally oxidized alloys of silver, copper, and nickel, fine dispersions of oxide phases can control hardness, recrystallization, and yield stress. The possibility of formation of a ductile, high-strength material by precipitating dispersions of alumina in a chromium matrix appears worthy of investigation. MATERIAL Powder Production—Chromium oxide and alumina in amounts to produce a final alloy of Cr + 16 pct AI2O3 by weight were colloid milled, filtered, dried and high fired for 16 hr at 1600°C in air. The resulting solid solution of oxides was ball-milled to a fine powder and the chromium oxide reduced to chromium by heating in pure dry hydrogen for 64 hr at 1400°C. Final Materials Produced by Powder Metallurgy Techniques—-Chromium powder, containing a disper-sion of alumina, was pressed into 1 1/8-in. diam slugs at 25 tons per sq in. and sintered 16 hr at 1400° C in pure dry hydrogen. The sintered slugs were encased in a stainless steel can, 2 in. in diam, and extruded at 1200° C through a 1/2-in. die. The 16 to 1 extrusion ratio produced a final chromium-alumina rod 1/4 in. in diam about 30 in. long. Samples of the rod were plunge-ground to small rupture bars of 0.82-in. gage length with a 0.01-sq-in. cross section. RESULTS Microstructure Studies—Fig. 1 is the microstruc-ture of the material in the as-sintered condition while Fig. 2 is the microstructure of the material as-extruded. Comparison of the as-sintered and as-extruded micrographs show the redistribution and realignment of the alumina inclusions by the extrusion

Jan 1, 1961

By Arthur B. Cummins, Henry Mulryan

DIATOMITE is a hydrous or opaline form of silica, commonly known as diatomaceous earth, diatomaceous silica or kieselguhr. The term "infusorial earth" has lost its original meaning and today is incorrect in view of the distinctions between diatoms and infusoria. Various locality and variety names are obsolete but some retain local significance. Moler and Celite are trade names that have become associated with diatomite products from certain deposits in Denmark and near Lompoc, California. COMPOSITION Diatomite is essentially silica with some combined water (2 to 10 pct). Frequently it contains organic matter (from traces up to over 30 pct) and varying amounts of inorganic impurities such as sand, cryptocrystalline silica, clay, volcanic ash, calcium carbonate, magnesia and soluble salts. In the natural or crude state, diatomite contains from 10 to 65 pct or more of free water. Table I gives analyses of several diatomites from deposits of different types. PROPERTIES Pure varieties, either massive or stratified, are friable and porous, of low apparent density, and somewhat chalklike in appearance. Varieties containing organic matter vary from sedimentary oozes to peatlike materials. Impure varieties may be more or less claylike, sandy, calcareous or cherty. Compacted types approach porcellanite and silicified shales. COLOR-white, cream, gray, tan, brown, greenish to nearly black. HARDNES-light-weight varieties appear 1 to 1.5 because of porosity, but microscopic particles are 4.5 to 6.5. SPECIFIC GRAVITY-1.9 to 2.35. APPARENT DENSITY---dry block form, 20 to 40 lb per cu ft; dry powder, 5 to 16 lb per cu ft. CRYSTAL SYSTEM-generally amorphous (isotropic by X-ray diffraction) but frequently showing faint cristobalite pattern.67.68,70 MELTING POINT-1400° to 1650°C. STREAK-white. LUSTER

Jan 1, 1949

By W. R. Ingalls

IF, in this study of the outlook for the copper industry of the United states, I find myself assuming to be prophetic in some respects I shall express myself with hesitation and with the foresight that after the end of the war with Germany the war with Japan may continue; anyway there is sure to be an uneasy period before copper and the other metals begin to flow smoothly through the natural channels of consumption. It is mainly my purpose to survey conditions and suggest some probabilities, or possibilities, rather than to prophesy. In interpreting them it will be necessary to make certain aasurnptions, among which will be (1) expectation of a rise in the general price level,, which so far has been one-sided; (2) continuance of the k. tariff on copper imports; and (3) lock-up of government-owned copper as a military re- serve. Of these assumptions the first is indicated by the lessons from economic history, and by current symptoms. The second and third depend upon political action by Congress.

Jan 1, 1944

By Frank M. Monroe, James R. Cost

The solubility of nitrogen in vanadium is determined from 275" to 575°C by measuring the height of the nitrogen internal friction peak of equilibrated V-N alloys. The proportionality constant at 275°C between the internal friction peak height (Q- 1) and the atom percent nitrogen in solution is found to be 0.095 per at. pct for nitrogen concentrations up to 0.8 at. pct. The heat of solution of the nitride in vanadium is 5500 cal per mole. The solubility of nitrogen in the Group V metals is discussed. LITTLE work has been performed on the vanadium-nitrogen terminal solid solution. Hahn1 found the solubility for nitrogen to be very small and reported the existence of a hexagonal phase of composition near that of V2N at the solubility limit. Rostoker and Yamarnoto2 reported the solubility to be at least 3.5 at. pct at the melting point and to be less than this value at 900°C. In addition, they reported from X-ray diffraction studies that nitrogen in solution produces tetragonality in the vanadium lattice. An X-ray study by Schonberg3 has confirmed the results of Hahn but indicated that the tetragonality observed by Rostoker and Yamamoto was due to the presence of oxygen in their specimens. Beatty4 has performed lattice parameter and hardness measurements on terminal solid solutions and found the upper limit of the solubility to be at least 0.66 at. pct N. No measurements have been made of the pressure-temperature-composition relationships (P-T-X) for the terminal solid solution. As a part of a research program on gas-metal equilibrium, an attempt was made to study the P-T-X relationships in the V-N system using both the internal friction and the gas equilibration methods which have been successful with the Nb(Cb)-N and Ta-N systems (see Ref. 5 for a review of this work). Extensive investigation, using the gas equilibration methods, showed this method not to be applicable with vanadium This was presumably due to the gettering action of vanadium sublimed on the walls of the Sieverts apparatus. Thus, the nitrogen pressure relationships with temperature and composition were not obtained. The internal friction methods were, however, found to be applicable, and the temperature-composition relationships are reported in this paper and compared with similar results for the Nb-N6 and Ta-N7 systems. The existence of a Snoek internal friction peak due to nitrogen in solution in vanadium has been clearly demonstrated. 8-10 Powers and Doyle found the peak to be at approximately 275°C for frequencies near 1 cps.8 In a subsequent paper10 they reported the proportionality constant at 275°C between the internal friction peak height (Q-1) and the concentration of ni- trogen in solution (in atom percent) as 0.06 per at. pct. The studies of Stanley and wert9 indicated qualitatively that the height of the Snoek peak decreased with aging at the peak temperature and thus suggested that internal friction methods were suitable for study of the solubility. EXPERIMENTAL METHOD The vanadium for this investigation was of particularly high purity. It was obtained from the Ames Laboratory of the U.S. Atomic Energy Commission, Ames, Iowa in the form of a 1/2-in. diam, three pass zone-refined ingot. The electrical resistivity ratio (p300ºk/p4ºk) was 160. The initial composition was determined as follows: Carbon 200 ppm Oxygen 150 ppm Chromium <50 pprn Iron 125 ppm Silicon <50 ppm Other metallic 100 pprn The initial vanadium ingot was fabricated to 30-mil wire by swaging and wire drawing without the need of intermediate annealing. Lengths of this wire were then further purified (particularly for oxygen) by outgassing at 10-6 torr at 1400°C for 4 hr. The outgassing treatment resulted in specimens with a bamboo grain structure and a lustrous appearance. Desired amounts of nitrogen were added to the outgassed wires in a Sieverts apparatus in which known amounts of nitrogen were equilibrated with the wire at 1300°C. Nitrogen concentrations were produced in the desired range from less than 1 to 10 at. pct N. Monitoring of the partial pressure of nitrogen in the Sieverts apparatus indicated that at 1300°C equilibrium between the nitrogen gas and the vanadium was obtained within 10 min. Relatively rapid cooling from the nitrogen addition temperature was obtained simply by turning off the specimen heating current and cooling to room temperature in the partial pressure of nitrogen. Internal friction measurements of wire specimens were made under forepump vacuum in a torsional pendulum at frequencies near 1 cps. The torsional pendulum was of low thermal inertia and was designed so that specimens could be heated both by a conventional tube furnace and by the joule heating of a separate current through the wire specimen." Use of a static atmosphere of helium gas as a quenching medium made it possible to cut the specimen current, rapidly cool the specimen to the measurement temperature, and make a measurement of the internal friction in less than 1 min. Because of the large solubility of vanadium for nitrogen, the internal friction peak heights were in some cases greater than Q-1 = 0.1. This high damping resulted in an estimated relative uncertainty in the damping measurements of approximately 10 pct. X-ray analyses made to identify the precipitated ni-

Jan 1, 1970

By Appendix by A. S. Goldoni, R. E. Tate, E. M. Cramer

The diffision coefficient for self-diffision of plutonium in the temperature range 350" to 440°C has been measured by using puZ3 as the tracer isotope. Autoradiopaphic techniques were used to inzlestigate the possibility of grain boundary diffusion, hut only evidence for volume diffusion was found. The least-squares fit of the data gives the .following equation for the diffision coefficient: The computer least-squares technique for fitting the nonlinear equations is outlined. DETERMINATION of the self-diffusion coefficient of the fcc 6 phase of plutonium is in principle a straightforward experimental task. However, the chemical reactivity, the intense @ activity, and the toxicity of plutonium put limitations on the experimental techniques. The technique selected included roll bonding for preparation of the diffusion couples and pulse-height analysis of the @-particle activity to determine the distribution of the PU tracer in the diffusion couples. EXPERIMENTAL PROCEDURE Couple Preparation. Cylinders about 0.5 in. in diam were cast from two special stocks of plutonium, one of which had been enriched in puZ3&apos;, as shown in the isotopic analyses listed in Table I. For each roll-bonded composite sheet, a cylinder 0.437 in. in diam and 0.190 in. thick was turned from each kind of plutonium on a lathe in a 98 pct He atmosphere. The two freshly machined cylinders were positioned face to face in a tube of commercially pure aluminum which had been sealed at one end by welding and the assembly was evacuated on a vacuum manifold overnight. The elapsed time between machining the faces of the plutonium cylinders and evacuating the loaded tube was about 15 min. After overnight evacuation of the assembly the indicated vacuum was 1 X 10"5 torr or better. The aluminum tube was then warmed and pinched off with a cold-welding tool. The pinched-off weld was also fusion-welded as an additional precaution against leakage of air into the evacuated assembly. The assembly was immediately heated for 30 min in a 250°C furnace and reduced in thickness by being passed through a rolling mill with rolls heated to 200°C. The rolling schedule (four passes of 100 mils each with a 10-min reheat after two passes) reduced the thickness of the assembly to 100 mils. The rolled assembly was allowed to cool normally in air. The rolled assembly was sheared at the edges and the aluminum peeled from the composite plutonium sheet. The elliptical sheet was about 0.060 in. thick and usually three 0.383-in.-diam disks could be punched from its central portion. The sheet was heated on a hot plate to the ductile low 0 range (140°C as measured by temperature-indicating pellets) before each disk was quickly punched. The quality of the bond in the disks was evaluated by metallographic examination of the scrap sheet adjoining the hole left by the punch. Only well-bonded specimens without oxide in the interface (as indicated by metallography) were considered satisfactory for further use. More than half of the specimens so examined contained sufficient oxide in the interface to be rejected. Diffusion Anneal. Each disk to be diffusion-annealed was wrapped in 1-mil-thick tantalum foil and sealed within a Pyrex capsule evacuated to 1 x 10~5 torr or better. This capsule was then sealed within another Pyrex capsule at a similar pressure. The diffusion anneals were carried out at temperatures between 350" and 440°C in Marshall furnaces adjusted to have a temperature gradient of not more than *1/2"C over a 5-in. length. This gradient was then further smoothed by using a nickel tube as a liner in the furnace. The liner was divided into three longitudinal cavities by a septum of nickel sheet to which two calibrated Chromel-Alumel thermocouples were attached. One thermocouple was used for controlling the furnace temperature by means of a Brown Pyrovane controller equipped with a Capaciline anticipation circuit; the second thermocouple was monitored twice daily with a Leeds and Northrup K-2 precision potentiometer.

Jan 1, 1964

By W. P. Lass

(San Francisco Meeting, October, 1911.) TEE purpose of this article is not only to describe the plant and method of cyaniding the Treadwell concentrates, but to present some of the results of the experimental work obtained in the past three years for the Alaska-Treadwell Gold Mining Co., at Douglas Island, Alaska., under the direction of F. W. Bradley, Consulting Engineer, and Robert A. Kinzie, General Superintendent, of the affiliated companies. At the time the experimental work was undertaken the concentrates were being shipped to the smeltery at Tacoma, Wash., and the cost for treatment of 3-oz. (gold) concentrates was $11.95 per ton, divided as follows: Smelting-charges, . $4.00 Loading, freight, insurance, etc., 2.89 Interest due to time lost in transit and in settlement, . 0.05 Loss due to settlement for 95 per cent. of the gold at $20 per ounce, 5.01 Total, . . $11.95 From the experimental work described later, it was estimated that 96 per cent. extraction could be made by treatment on the ground, and that the cost, when treating 80 tons per day, would be $3.25 per ton, divided as follows; Per Day. Per Ton. Labor, . $66.16 $0.827 Chemicals, . 76.60 0.960 Power and steam-heat, 67.60 0.845 Marketing-, refining- and other charges, 49.36 0.617 Totals, . . $259.72 $3.250 Adding to this total the 4 per cent treatment-loss, which on 3-oz. concentrates amounts to $2.48, gives a total cost of $5.73 per ton. Comparing this with $11.95, the cost when shipping to the smelter, leaves a net gain of $6.22 per ton by the local

Feb 1, 1912

By B. C. Allen

Surface free energy and surface self-diffusion of solid molybdenum were studied in the temperature range 1600" to 2400°C using pressure-sintered bi-crystals. Comparison of groove angles formed in various surfaces perpendicular to the grain boundary indicate a maximum of 1 pct variation in surface free energy with crystallographic mientation. This anisotropy tends to decrease with increasing temperature. The surface diffusion of the bicrystals is equivalent to that of sheet with a mild (100) Preferred orientation. Anomalously low values found for bi-crystals with surface orientations of (OOl), (012), and (011) are rationalized in terms of anisotropy in surface free energy. THE effect of crystallographic orientation on surface free energy1,&apos; and surface self-diffusion3,4 has been primarily studied in fcc metals. The object of this work was to study the effect of orientation on surface diffusion and surface free energy of bcc molybdenum using pressure-sintered bicrystals. EXPERIMENTAL WORK Materials and Crystal Preparation. Arc-melted molybdenum rod was obtained commercially and electron beam zone refined at 50 cm per hr at 10- 5 torr to form single crystals about 8 cm long and 0.65 cm diam. Three crystals were prepared with axial orientations about 1 deg from [001.], [011], and. [111]. To reduce the carbon content, the crystals were annealed 2 hr in 1.4 atm flowing wet hydrogen at 2050°C. Then the oxygen content was reduced by annealing for 2 hr in -30°C dewpoint hydrogen at 2020°C. The resulting impurity analysis is given in Table I. Bicrystal Preparation. The single crystal rods were cut into transverse slices with a thin silicon carbide abrasive wheel to produce specimens about 0.6 cm long. They were mounted in epoxy and surrounded by stainless steel washers. Cutting in half was done longitudinally at various angles to known crystallographic planes containing the cylinder axis according to Fig. 1. To reduce surface deformation resulting from the cutoff wheel and thus reduce parasitic grain boundary formation on subsequent annealing, about 0.003 cm was manually ground off each cut surface with 600 grit paper. Care was taken to keep the surface flat. After removal from the mounts, one half was generally ro-tated 180 deg with respect to the other to give a po- tential symmetrical tilt grain boundary between the two halves. In the other cases when low misorienta-tion angles were desired, the crystals were not rotated. On the basis of symmetry, sufficient bicrystals were prepared to cover the entire range of misorientations for symmetrical tilt boundaries. The misorientations, +, ranged from 0 to 45, 0 to 90, and 0 to 60 deg for [001], [011], and [111] bicrystals, respectively. One [Ill] twist bicrystal was prepared from 2 single crystal discs rotated 17 deg relative to each other. Each specimen consisted of two pieces which were placed in a cylindrical tantalum can. Sharp edges were rounded and the fit was made as snug as possible to reduce subsequent deformation during bonding. The assembly and crystals generally were vicuum outgassed at 900" or 1700°C and then electron beam welded in the can at l x 10-4 torr. After being leak checked, the samples were placed in an autoclave and hydrostatically gas-pressure bonded5 in four batches under helium at 10,000 to 18,000 psi at 1650°C for 3 hr. Satisfactory bonds were obtained in many cases, and most of the crystals bonded after two exposures. The results did not appear to be affected by the various pressures used, preannealing conditions, crystal orientation, or time-pressure-temperature route taken to the final bonding condition. After bonding, the tantalum cans were selectively removed in cold concentrated HF. Measurements indicated overall deformation was under 1 pct. The bicrystals were metallographically ground and polished flat and perpendicular to the axis. Examination showed the boundaries were straight and almost free of parasitic grains caused by extraneous local deformation. Annealing. In preparation for thermal grooving, the bicrystals were cleaned and annealed by outgassing at 10-5 torr at 1900°C and heating at 2300°C under 1 atm 99.996 Ar for 0.5 hr. The crystals were held in a closed 4-deck box made of molybdenum sheet, and were heated in a Ta-1OW resistance furnace. The ar-

Jan 1, 1970

By B. A. Kulp, R. R. Reeber

Lattice parameters for the wurtzite form of&apos; CdS mere measured by powder X-ray diffraction techniques over the temperature range 26° to 1000 K&apos;. A negative thermal -expansion coefficient was determined parallel and perpendicular to the c axis below 13.5°K. Near 808°K, the curves of the a, parameter, the differential thermal expansion, and the resistivitv vs absolute temperature exhibited a reversible discontinuity. j\. direct determination of the lattice parameters of CdS over an extended temperature range is of particular use in interpretation of the effects of high pressure on the band structure of semiconductor materials. For example, Langer&apos; has studied the effects of pressure on the absorption edge of CdS from 77°K to room temperature. In order to properly interpret his results it is necessary to know the change in lattice constants as a function of temperature for the wurtzite, zincblende, and rocksalt2 modifications of this material. Thermal-expansion measurements for CdS, wurtzite phase, have previously been determined over a limited temperature range.s74&apos;5 The zincblende phases, of other compounds with similar bonding, have been investigated by Novikova et a! .&apos;&apos; Previous thermal-expansion measurements for metals with hexagonal symmetry have for the most part used bulk sample techniques for low-temperature result. Most X-ray measurements at low temperature have been on materials with cubic symmetry.&apos;jQ The use of X-ray powder-diffraction techniques offers a convenient and accurate method of measurement over a wide temperature range. The X-ray method, besides measuring unit cell size, also provides information about change in structure type and the nature of some of the stacking defects present. I) EXPERIMENTAL PROCEDURE The thermal expansion was measured by X-ray powder-diffraction techniques. Lattice parameters for the range 300" to 1000°K were determined in a 19-cm Unicam camera. From 26" to 300°K a 34-cm back-reflection camera with the Van Arkel" film arrangement was used. The sample was bonded to a copper cold finger below a helium, hydrogen, nitrogen, oxygen, dry ice, or ice brine bath in a metal cryistat. che inner bath was surrounded by another one for radiation shielding. Nitrogen was used in this outer bath for the very low-temperature runs while dry ice and acetone was used for the 195°K point. CuKa X-rays, filtered with a nickel foil, entered the cryostat through a 0.001-in.-thick aluminum window. During a typical 9-hr exposure the sample was continuously rotated through a 30-deg arc. Heat losses from the sample holder limited the minimum temperature attained to 26°K with helium in the inner dewar. Temperature calibration between 25" and 125°K was determined with an Allen Bradley 300-ohm carbon resistor. The resistor was attached to the back of the copper finger with a thin layer of silicone grease. Liquid He, HZ, N2, and O2 baths were used to calibrate the resistor. Temperature variation is estimated to be *2"K with a slightly higher uncertainty at room temperature and 264°K. The thermal expansion of high-purity germanium from 373" to 900°K was measured as a calibration for the Unicam camera. This value was compared with the known value1&apos; for the thermal expansion. A discontinuity in the thermal-expansion coefficient of the CdS a, parameter was observed. Similar discontinuities in the resistivity and differential thermal analysis at the same absolute temperature indicate that the temperature error is *5°K in the temperature range above 500°K. Temperature errors in the Unicam camera below 500°K are appreciably higher due to large gradients in the resistance furnace. II) SAMPLE PREPARATION The CdS was Eagle Picher ultrapure grade. The crystallite size range of the as-received powder

Jan 1, 1965

By C. E. McCarthy, A. George Stern, Stanley J. Green

THE national interest prompts consideration of any new source of mineral wealth even though the immediate need may be of minor importance. A critical shortage of potash in the United States during the World War of I9I4-I8 stimulated broad development, which established an American potash industry on a basis so sound that this commodity is not even listed as urgent in the present war program. However, this should not minimize its importance, and the need remains, not only for adequate supplies of the usual potash salts (the chloride and the sulphate) but of all potash chemicals. Potassium carbonate (known commercially as pearl ash) has been a high-cost commodity; in consequence, the quantity used by industry has been relatively small. By a combination of fortuitous geographical circumstances, there is opportunity to produce a low-cost potassium carbonate with the possibility that this might become an important source of chemical potash. The following paper considers a recently developed process1 taking advantage of these conditions. WYOMINGITE DEPOSIT For many years it has been known that a deposit of potash-bearing igneous rock known as wyomingite occurs in the southwestern part of Wyoming at Zirkel Mesa, which is 44 miles northeast of the town of Green River (Fig. I). The western escarpment of this deposit is about 3 miles east of the Superior Branch of the Union Pacific Railroad. This mesa alone covers approximately 3300 acres, and the average thickness of the wyomingite flow is 75 ft. It has been estimated2 that about one billion tons of wyomingite occur in this one deposit, all of which can be mined by open quarrying without overburden. In addition, there are several smaller deposits within 10 miles, so that the aggregate wyomingite in the area approaches two billion tons. This is one of the world&apos;s largest sources of leucite, and the only known deposit of its kind in the United States. The wyomingite (which is in the form of a lava flow and numerous small craters), with the mineral leucite as its most important component, has a mineral composition3 of: leucite, 50 per cent; phlogopite, 15; diopside, I2; kataphorite, 15; glass and apatite, 8. The phlogopite is present in visible phenocrysts 1/8 to 1/2 in. in diameter, but the leucite usually is almost microcrystalline and not capable of liberation by grinding. Chemically, the wyomingite has a potash content averaging slightly higher than eleven per cent K20. The potash is mainly in the leucite, but part of it is in the phlogopite and a small amount is in the feldspars that are occasionally seen as undigested occlusions of the granite country rock, through which the leucite-bearing lava intruded, and as sanidine feldspar both in the crystalline and glassy phases of the rock. A typical analysis of the wyomingite from Zirkel Mesa is as follows:

Jan 1, 1944

NEW YORK LOCAL SECTION Executive Committee Louis D. HUNTOON, Chairman ARTHUR S. DWIGHT, Vice-Chairman THOMAS T. READ, Secretary, Woolworth Bldg., New York, N. Y. E. MALTBY SHIPP, Treasurer GEORGE F. KUNZ W. DE L. BENEDICT Meeting, Jan. 16, .1914 A meeting of the New York Local Section of the American Institute of Mining Engineers was held at the Engineering Societies Building, 29 West 39th Street, New York City, Jan 16 1914 the Chairman, -L. D. Huntoon, presiding. Forty members weld present. In the absence of the Secretary, C. A. Bohn was appointed Secretary pro teen. N. H. Darton, Geologist of the U. S. Geological Survey, delivered an address on. The Occurrence of Gas in Coal, illustrated by lantern slides of charts, curves, and tables showing various features of gas occurrences. J. W. Richards, J. T. Beard, W. L. Saunders, L. D. Huntoon, and Mr. Darton participated in the discussion which followed the address. THOMAS T. READ; Secretary.

Jan 3, 1914

[Officers and Committees of the Society of Petroleum Engineers 1 Officers and Staff of the AIME 2 . Officers of AIME Sections Predominantly Petroleum in Membership 3 AIME Local Sections and SPE Regional Organization Maps 5 Alphabetical List of Members 7 Geographical List of Members 102 Advertisers&apos; Index 133]

Jan 1, 1961

By Thomas A. Read

The internal friction of single crystals of metals is affected markedly by a variety of factors, which, according to the literature, are without influence on the internal friction of polycrystalline metals at strain amplitudes less than 10-5. For example, the internal friction of a suitably oriented zinc single crystal is multiplied by a factor of ioo when the vibration amplitude is slightly increased, and the internal friction of a copper crystal is markedly increased by the application of a stress of 30 lb. per sq. in. for one minute. In this paper it will be shown that these, together with the other phenomena associated with the damping of mechanical vibrations in metal single crystals, can be satisfactorily explained, at least qualitatively, in terms of an atomic mechanism that has been proposed for quite another purpose—that of accounting for slip in metals. The extraordinary agreement between the observed behavior of the metal single crystals and the behavior that could be predicted on the basis of this atomic mechanism leads to the belief that the latter is probably essentially correct. If this is so, it follows that valuable information about the slip process in metals may be gained from measurements of internal friction on single crystals. In this paper the results of the only study to date on the damping of mechanical vibrations in single crystals of metals mill be presented. Experimental Procedure The internal friction of a material is a measure of the rate at which the energy of mechanical vibrations is converted into heat. The measure of internal friction used in the present paper is the decrcment A, which is defined as the fraction of the energy of vibration lost per half cycle. The measurements described here were made for longitudinal oscillations at a frequency of 33.5 kc. for the copper crystals, and at a frequency of 39 kc. for the zinc crystals. The method used is that of the composite piezoelectric oscillator. The single-crystal specimens are in the form of circular cylinders M in. in diameter and I 1/2 to 21/2 in. long. The crystal rods are waxed in a V-block and sawed to the proper length with a fine jeweler&apos;s saw. The ends of the specimen are ground flat, and one end is cemented with a very thin film of beeswax and rosin to the end of an x-cut quartz rod which is 1/4 in. in diameter and 3 in. long. The length of the specimen rod is determined by the condition that its natural frequency for longitudinal vibration be the same as that of the quartz rod, within 0.5 per cent. The lengths of the specimens are thus different for different orientations of the cylinder axis with respect to the crystallographic axes. When the specimen and quartz rods are thus matched in frequency the adhesive is at a node of stress, and it has been shown experimentally that under these circumstances

Jan 1, 1941

By Thomas A. Read

The internal friction of single crystals of metals is affected markedly by a variety of factors, which, according to the literature, are without influence on the internal friction of polycrystalline metals at strain amplitudes less than 10-5. For example, the internal friction of a suitably oriented zinc single crystal is multiplied by a factor of ioo when the vibration amplitude is slightly increased, and the internal friction of a copper crystal is markedly increased by the application of a stress of 30 lb. per sq. in. for one minute. In this paper it will be shown that these, together with the other phenomena associated with the damping of mechanical vibrations in metal single crystals, can be satisfactorily explained, at least qualitatively, in terms of an atomic mechanism that has been proposed for quite another purpose—that of accounting for slip in metals. The extraordinary agreement between the observed behavior of the metal single crystals and the behavior that could be predicted on the basis of this atomic mechanism leads to the belief that the latter is probably essentially correct. If this is so, it follows that valuable information about the slip process in metals may be gained from measurements of internal friction on single crystals. In this paper the results of the only study to date on the damping of mechanical vibrations in single crystals of metals mill be presented. Experimental Procedure The internal friction of a material is a measure of the rate at which the energy of mechanical vibrations is converted into heat. The measure of internal friction used in the present paper is the decrcment A, which is defined as the fraction of the energy of vibration lost per half cycle. The measurements described here were made for longitudinal oscillations at a frequency of 33.5 kc. for the copper crystals, and at a frequency of 39 kc. for the zinc crystals. The method used is that of the composite piezoelectric oscillator. The single-crystal specimens are in the form of circular cylinders M in. in diameter and I 1/2 to 21/2 in. long. The crystal rods are waxed in a V-block and sawed to the proper length with a fine jeweler&apos;s saw. The ends of the specimen are ground flat, and one end is cemented with a very thin film of beeswax and rosin to the end of an x-cut quartz rod which is 1/4 in. in diameter and 3 in. long. The length of the specimen rod is determined by the condition that its natural frequency for longitudinal vibration be the same as that of the quartz rod, within 0.5 per cent. The lengths of the specimens are thus different for different orientations of the cylinder axis with respect to the crystallographic axes. When the specimen and quartz rods are thus matched in frequency the adhesive is at a node of stress, and it has been shown experimentally that under these circumstances

Jan 1, 1941

By W. Weissberger, Frankiewicz, L. Pommier

Introduction In the U.S., about one-quarter of the fuel oil and natural gas consumption is associated with power production in utility and industrial boilers and process heat needs in industrial furnaces. Coal has been an attractive candidate for replacing these premium fuels because of its low cost, but there are penalties associated with the solid fuel form. In many cases pulverized coal in unacceptable as a premium fuel replacement because of the extensive cost of retrofitting an existing boiler designed to burn oil or gas. In the cases of synthetic fuels from coal, research and development still have a long way to go and costs are very high. Another option, which appears very attractive, is the use of solid coal in a liquid fuel form - coal slurry fuels. Occidental Research Corp. has been developing coal slurry fuels in conjunction with Island Creek Coal (ICC), a wholly-owned subsidiary. Both coal-oil mixtures and coalwater mixtures are under development. ICC is a large eastern coal producer, engaged in the production and marketing of bituminous coal, both utility steam and high quality metallurgical coals. There are a number of incentives for potential users of coal slurry fuels and in particular for coal-water mixtures (CWMs). First, CWM represents an assured supply of fuel at a price predictable into future years. Second, CWM is available in the near term; there are no substantial advances in technology needed to provide coal slurry fuels commercially. Third, there is minimal new equipment required to accommodate CWM in the end-user&apos;s facility. Fourth, CWM is nearly as convenient to handle, store, and combust as is fuel oil. Several variants of CWM technology could be developed for different end-users in the future. One concept is to formulate slurry at the mine mouth in association with an integrated beneficiation process. This slurry fuel may be delivered to the end-user by any number of known conveyances such as barge, tank truck, and rail. Slurry fuel would then be stored on-site and used on demand in utility boilers, industrial boilers, and potentially for process heat needs or residential and commercial heating. An alternative approach is to formulate a low viscosity pre-slurry at the mine mouth and to pipeline it for a considerable distance, finishing up slurry formulation near the end-user&apos;s plant. Finally, at the other extreme of manufacturing alternatives, washed coal would be shipped to a CWM manufacturing plant just outside the end-user&apos;s gate. Depending on fuel specifications and locations of the mine and end-user facility, any of these alternatives may make economic sense. They are all achievable in the near term using existing technology or variants thereof. The Coal-Water Mixture CWMs contain a nominal 70 wt. % coal ground somewhat finer than the standard pulverized ("utility grind") coal grind suspended in water; a complex chemical additive system gives the desired CWM properties, making the suspension pumpable and preventing sedimentation and hardening over time. Figure 1 shows the difference between a sample of pulverized coal containing 30 wt. % moisture and a CWM of identical coal/water ratio. The coal sample behaves like sticky coal, while the CWM flows readily. The combustion energy of a CWM is 96-97% of that associated with the coal present, due to the penalty for vaporizing water in the CWM. Potentially any coal can be incorporated in the CWM, depending on the combustion performance required and the allowable cost. CWMs are usually formulated using high quality steam coals containing around 6% ash, 34% volatile matter, 0.8% sulfur, 1500°C (2730°F) initial deformation temperatures, and energy content of 25 GJ/t (21.5 million Btu per st). Additional beneficiation to the 3% ash level can be accomplished in an integrated process. There are a number of minimum requirements which a satisfactory CWM must meet: pumpability, stability, combustibility, and affordability. In addition, a CWM should be: resistant to extended shear, generally applicable to a wide variety of coals, forgiving/flexible, and compatible with the least expensive processing. It was found that a complex chemical additive package and control of particle size distribution are necessary to achieve these attributes simultaneously, while maximizing coal content in the slurry fuel. Formulation of Coal-Water Mixtures A major consideration in the manufacture, transportation, and utilization of a slurry fuel is its pumpability, or effective viscosity. Most CWM formulations are nonNewtonian, i.e., viscosity depends on the rate and/or duration of shear applied. Viscosities reported in this paper were obtained using a Brookfield viscometer fitted with a T-spindel and rotated at 30 rev/min, thus they are apparent viscosities measured at a shear rate of approximately 10 sec-1. The instrument does reproducibly generate a shear field if spindle size and rotation rate are held fixed. By observing the apparent viscosities of several slurries at fixed conditions it is possible to obtain a relative measure of their viscosities for comparison purposes. A true shear stress-shear rate relationship at the shear rates at which the CWM will be subjected in industry may be obtained using the Haake type and a capillary viscometer. These viscometers are used for specific applications. However, for comparison purposes, apparent viscosities are reported.

Jan 1, 1985

By B. Blumenthal

THE present investigation was planned as a survey of the lead-rich portion of the ternary lead-antimony-silver system by thermal analysis. Since, however, a rigorous application of the conventional thermal analytical method is time consuming, an attempt was made to speed up the investigation by reducing the time required for a single thermal analysis. This was done by increasing the rate of cooling to 12° to 18°C. per minute, since such a rate does not permit even an approach to equilibrium conditions, the melt was stirred vigorously by a stirrer operating at the high rate of 665 r.p.m. This proved to be effective in obtaining cooling curves with distinct points of arrest and of excellent reproducibility, which satisfactorily compare with those obtained at a rate of 1" to 2°C. per min. with or without slow stirring (Fig. I). By this method the lead-rich end of the lead-alltimony system and a series of ternary alloys in sections parallel to the lead-antimony side of the ternary system were investigated and it was observed that the two branches of the liquidus curve of the binary alloys did not intersect at the euteotic temperature. An equivalent effect mas observed in the ternary system. The eutectic temperature of the binary lead-antimony system was found to be 252.0°C., which confirms the recent in- vestigation by Pellini and Rhines,1 who determined the eutectic temperature to be 2 51.5°C. The observation that the curves of primarY crystallization of the lead-antimony system do not intersect at the eutectic temperature was previously made by Dean.2 Dean explains the phenomeilon by assuming the existence of a compound Sb4pb. He felt that supercooling was not the cause of the phenomena because he was unable to influence them by inoculation. The X-ray investigation by Solomon and Morris-Jones,3 the metallographic investigations by Stead,4 Charpy,5 Gontermann,6 and Dean, Zickrick and Nix,7 and the numerous investigations of physical properties, definitely disprove the occurrence of any compound. The work of Dean was not confirmed by Broniewski and Sliwoski,8 whose experiments did not show any irregularity and who report a eutectic composition of 13 per cent antimony and a eutectic temperature Of 2500 to 252°C. at a rate Of coo1ing of about 6°C. Per min. Abell Redlich and Adler9 then report a eutectic composition of 12.1 per cent upon reviewing the previous publications and adding a few of their own cooling curves. In 1934 Quadrat and Jiriste10 found from careful analyses of the bottom portion of slowly cooled hypereutectic melts that the eutectic only 11 .4 to 11.5 per cent antimany. (Previous analyses by Stead4 .in 1891 gave 13 per cent.) Weaver,ll however, reported in 1935 that cooling cunres indi-

Jan 1, 1944