By Roy McLellan

THE slags derived from the smelting of lead and copper ores are composed essentially of silicates. The problems arising from the smelting of these ores consequently involve the study of silicate fusions. In the absence of specific knowledge concerning the compounds occurring in slags, it has been the practice of metallurgists to treat them in terms of their total chemical composition. Slags have been classified as monosilicates, bisilicates, sesquisilicates, and subsilicates according to the relative amounts of oxygen in the acid and basic radicles of the hypothetical salt produced. While this has been a useful guide to metallurgists in computing the furnace charges, it falls far short of a basis for the scientific investigation of slags. In order to understand the nature of a slag as a whole it is necessary to learn the physical and chemical properties of the mineral compounds which go to make up that slag. The efficiency with which an ore is smelted in a furnace depends primarily on the physical properties of the compounds formed during the operation. When the melting points and fields of stability of each of the mineral compounds in slags have been established, it will be possible to determine the properties of any given slag by examining the nature and amounts of its mineral constituents.

Jan 1, 1930

By F. N. Rhines, A. H. Grobe

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By A. H. Grobe, F. N. Rhines

At elevated temperatures the oxide of silver is unstable in the air at atmospheric pressure, consequently no external oxide scale forms upon pure silver under conditions of high-temperature annealing. When small quantities of certain alloying elements are present in the silver, the formation of a thin external scale is possible1 and in addition there may form a subscale composed of the oxide of the solute element precipitated within the body of the silver. Norbury2 and Leroux and Raub3 have reported internal oxidation (subscaleiormation) in alloys of silver with 2, 7.5, and 30 per cent of copper. The presence of the subscale is believed to be responsible, at least in part, for the objectionable "fire mark" in Sterling silver.4 Several other alloys of silver, after oxidizing heat-treatments, are known to exhibit undesirable polishing characteristics that may be the result of internal oxidation. Except for the absence of an external scale of silver oxide, it is to be anticipated that silver alloys will prove to be very similar in their oxidation behavior to the alloys of copper, the oxidation characteristics of which have been studied in some detai1.5,6 The present research confirms this anticipation. The oxidation of a series of 20 dilute alloys of silver has been studied metallographically; some types of subscale not encountered among the copper alloys have been found. Instances of internal oxidation in alloys of most of the metals of the 1-6 and VIII groups of the periodic system are on record, but evidence of this type of oxidation in alloys of the metals of the intermediate groups is lacking. A number of the metals of the intermediate group, among them cadmium, lead, tin, and zinc, appear to provide the conditions essential to subscale formation; i.e., they form oxides with a relatively low negative free energy of formation, they dissolve other metals that form more stable oxides, and, presumably, oxygen will diffuse through them. In a study of 40 alloys of these white metals only a few cases of internal oxidation have been found. The probable reasons for this difference in behavior will be discussed presently. Experimental Procedure Silver.—The silver alloys employed in the oxidation studies were prepared in heats of 30 grams each from high-purity silver (99.993 per cent Ag)* and the purest avail-

Jan 1, 1942

By Charles White Merrill

Mankind's progress is measured in minerals. Man's emergence from prehistory is marked by passage through a Stone Age and a Bronze Age and into the present era, sometimes called the Iron Age or the Age of Metals. With the evolution of civilization and the development of a modem industrial economy, minerals become more and more important. Structures, roads, and machines are built largely of minerals; the energy to heat the structures and to drive the machines is mostly mineral; agricultural fertility is maintained by mineral fertilizers and water; and military strength is provided by fortresses, armaments, and munitions, largely of mineral origin. Thus in the material world, in the productivity of the economy, access to minerals has paramount importance. Every evidence indicates increasing dependence on minerals in the modem economy, particularly on the mineral fuels as energy sources to provide the power base for advancing industrialization. Both the total and the per capita consumption of almost every mineral is increasing in the industrialized nations. Moreover, nations with predominantly agrarian economies call themselves underdeveloped and universally strive to industrialize. Most mineral consumption trends in the more advanced economies have been greatly exceeding population growth-which itself has been advancing at an accelerating rate--and sometimes have surpassed the growth in real income. Some minerals have only recently been adopted or grown to importance in use. Titanium as a metal appeared as a commercial product only in 1948, and even coal seriously displaced wood as a source of heat less than two centuries ago. On the other hand, minerals have always played an important role in construction. The prehistoric megaliths that form the dolmens of Salisbury Plain are stone; the pyramids are andesite faced with limestone; and many other ancient structures are built of mineral materials. In modem times the whole course of architecture has been redirected by new building materials, mostly mineral. Most conspicuous is the sky-

Jan 1, 1959

By Manuel Valerio Ortega

This Mexican amalgamation-process, invented in 1557, at Pachuca, by Bartolome de Medina, has been widely discussed in America and Europe, but thus far there is no universal agreement as to all the chemical reactions involved. Having been, after many trials, the first to succeed in effecting the amalgamation of silver-ores by the same mechanical means, but doing without one of the chemical substances which had been considered indispensable in the practice of 300 Sears, I am led to offer these notes as a contribution to the discovery of an exact theory concerning the patio process. My treatment for silver- and gold-ores being protected by letters-patent in this country, the United States, France, Peru, Bolivia and Chile, I may speak freely concerning its materials and manipulation. I. Patio-Amalgamation. The ore extracted from the mine is sorted by pepenadores, who break the large pieces with hammers, rejecting those which contain no ore, set aside the very rich to be smelted, and deliver the rest to be crushed and pulverized for direct amalgamation in the patio. The broken lumps, of about fist-size, are first ground in Chilean mills, and then reduced, in arrastras or tahonas, to fine slime. After the lama or slime has acquired a suitable consistency by the evaporation, through the sun's heat, of a part of the water which it contained, it is spread upon the patio or amalgamating-floor, where it is mixed with 5 or 6 per cent. of common salt. The next day a certain amount (depending upon

Jan 1, 1902

By F. A. Crossley

The titanium-rich end of the Ti-A1 system has been investigated up to 35 at. pct A1 (23 wt pet). One conzpound Ti3Al was found to occur between primary a and TiAl. It is ordered hcp with DO19 structure, it has virtually no solid-solubility range, and it has a closed maximum at about 875°C. OIL either side of the compound are a +Ti3Al two-phase fields. The limiting a1uminum solubility in primary a at the titanium-rich end is indicated to be 7.5 at. pct A1 (4.4 wt pet) at 550°C and about 6.8 at. pct Al fl wt pct) at 500°C. Quenching alloys from above the a + Ti3Al two-phase field produces the following structures with respect to alloy composition: Up to 13 at. pct A1 (7.8 wt pet), a solid solution; from 15 to 18 at. pct A1 (9 to 11 wt pct), shear transformation product or martensite; from 19 to approximately 30 at. pct (11 to 19 wt pet), submicro-scopic coherent Ti3Al in an a malvix. The twin hcp phase fields reported in the literature are the result of nonequilibrium corzdztions. Ti-A1 alloys, once partitioned by dwelling- in the a + ß phase field during either hot working or heat treatment, are extremely difjicult to homogenize at temperatures below 1000°C. Such partitioned alloys exhibit the characteristics or symptoms of two-phase materials, and may be said to suffer the "twin-phase syndrome". THE earliest investigations of the Ti-A1 system by Ogden et al.1 and Bumps et al.2 reported wide solubility of the primary solid solutions. Aluminum was reported soluble in the low-temperature allomorph to the extent of 37 at. pct (25 wt pct), and the first intermediate phase was reportedly TiA1. Somewhat later Kornilov et al.3 reported a similar diagram with phase boundaries displaced towards lower aluminum contents and higher temperatures. Beginning about this time (1956) reports in the literature made it very clear that one or more intermediate phases occurred at lower aluminum contents than TiAl.4-17 These reports included five major investigations of the titanium-rich end of the Ti-A1 diagram.4,12,14,16,17 Three of these diagrams show two two-phase fields below 37 at. pct Al, while two of them show a single two-phase field. The existence of the phase Ti3A1 is firmly established and is included in each of the diagrams, except one—that of Sato and Huang.12 The new phases are reportedly hcp and differ from primary a only slightly when disordered, and when ordered the "a" parameter is approximately one,4,12,15 two, 6-10,13,14 or four14 times that for primary a. Beyond this, however, the diagrams are remarkable for their lack of agreement. Two tacit assumptions are usually made in phase-diagram determinations of metal systems. These are: 1) equilibrium anneals bring the alloy to equilibrium or to indistinguishable closeness to it, and 2) equilibrium conditions established at elevated temperatures are either "frozen" by rapid quenching for evaluation at room temperature, or quench-transformation products are recognized as such. In the current investigation evidence was obtained that over substantial composition ranges neither of these two conditions was met in any of the more recent major investigations. I) MATERIALS, METHODS, AND TECHNIQUES The alloys of this investigation were prepared by nonc on sum able electrode arc melting. Materials used in the preparation of the alloys are summarized in Table I. The investigative tools employed were: optical and electron microscopy, differential thermal analysis (DTA), disatometry, X-ray diffraction, electron diffraction, and resistometry. Alloys for microscopic and X-ray investigations were prepared as 15-g melts. Alloys containing from 7 through 11 at. pct A1 were hot-rolled out of a furnace at 900°C, from 12 through 15 at. pct out of a furnace at 1000°C, and from 16 through 18 at. pct out of a furnace at 1125°C. Alloys containing more than 18 at. pct A1 could not be hot-rolled. The ingots were covered with Markal coating prior to hot rolling to minimize atmospheric contamination. After hot rolling, alloys containing up to 15 at. pct A1 were ground and pickled to remove 7 mils from each surface; alloys containing 16 and 18 at. pct A1 were skinned to a

Jan 1, 1967

COMMITTEE IN CHARGE SPENCER PENROSE, Chairman A. E. CARLTON, Chairman Finance Committee GEORGE M. TAYLOR, Vice-Chairman J. DAWSON HAWKINS, Secretary DENVER Arrangement DAVE G. MILLER FRANK BULKLEY GEO. E. COLLINS Entertainment F. H. BOSTWICK F. E. SHEPARD HOWLAND BANCROFT B. P. MORSE J. G. PERRY Finance T. B. STEARNS RICHARD A. PARKER T. B. BURBRIDGE

Jan 7, 1918

By C. R. Wohrman

A MELT of pure electrolytic iron with about 0.4 per cent. sulfur and 7 per cent. manganese was prepared in connection with a study of inclusions in iron. The alloy darkened rapidly when etched with a 10 per cent. alcoholic solution of nitric acid, and microscopic examination revealed the presence of a semimartensitic, semi-Widmanstättian structure (Figs. 1 and 2) closely resembling the structures found by Benedicks in his artificially prepared "meteoric iron." 1 The structures found by Benedicks were readily explained by the presence in his alloy of the two well known iron-nickel solid solutions, taenite and kamacite, and of their eutectoid (?) aggregate, plessite. By analogy, one would infer the existence of similar phases in the iron-manganese alloy just described, such as inference being strengthened by the similarity displayed in many ways by nickel and manganese in their effects on iron. IRON-MANGANESE ALLOTS ARE REGARDED AS HOMOGENEOUS Heterogeneity of iron-manganese alloys has not been recognized heretofore, judging from the data of standard metallographic books and those of original papers. In fact, iron and manganese are quite generally regarded as completely miscible in the solid state. Dr. Rosenhain,2 for example, writes: Alloys of group (a), of which those of gold-silver, iron-manganese, and copper-nickel are examples, when allowed to crystallize sufficiently slowly to attain their condition of final equilibrium, present a microstructure exactly similar to that of a pure metal-the homogeneous character of the molten solution is in that case so completely maintained that the microscope cannot detect the presence of any second constituent.

Jan 1, 1927

By Daniel Hanson

FoR most of their practical applications metals are required to withstand stresses of appreciable magnitude: indeed, it id because they possess the quality of resisting stress without becoming permanently deformed that they find such extensive use in the service of man. Metals and alloys must, in service, usually behave as elastic substances—or nearly so. It is not difficult to satisfy this condition at ordinary temperatures. Iron and its alloys, especially the steels, are at normal temperatures excellent elastic bodies, capable of satisfying most of the mechanical requirements of the engineer: where electrical, chemical or other properties are impor-tant, which cannot be met by steels, it is usually possible to find a non-ferrous alloy such as nickel, copper or aluminum, which will prove satisfactory. When the metals or alloys are not inherently sufficiently elastic, cold-working or heat-treatment may develop elastic properties to a sufficient extent for practical needs. By means of relatively simple, rapid tests we can measure such properties as elastic modulus, limit of proportionality and proof stress, upon which design can be based with confidence. The case of the soft metals, such as lead and tin, is well known to be exceptional. They possess no definite limit of elasticity, and the value of proof stress or tensile strength depends to a great extent on the speed with which the test is carried out. Design here must be based on other considerations than a well-established theory of the proportionality of stress and strain. It is now generally recognized that steels and non-ferrous alloys possess at temperatures not greatly exceeding that of the atmosphere, characteristics quite different from those existing at ordinary temperatures, and that they assume qualities similar to those of the soft metals. Not only have they no limit of elasticity, but the proof stress and the ultimate stress depend on the time of application of the load. Flow under load may persist for long periods of time, possibly indefinitely, and the determination of a true maximum stress becomes a matter of great difficulty.

Jan 1, 1939

By Daniel Hanson

FoR most of their practical applications metals are required to withstand stresses of appreciable magnitude: indeed, it id because they possess the quality of resisting stress without becoming permanently deformed that they find such extensive use in the service of man. Metals and alloys must, in service, usually behave as elastic substances—or nearly so. It is not difficult to satisfy this condition at ordinary temperatures. Iron and its alloys, especially the steels, are at normal temperatures excellent elastic bodies, capable of satisfying most of the mechanical requirements of the engineer: where electrical, chemical or other properties are impor-tant, which cannot be met by steels, it is usually possible to find a non-ferrous alloy such as nickel, copper or aluminum, which will prove satisfactory. When the metals or alloys are not inherently sufficiently elastic, cold-working or heat-treatment may develop elastic properties to a sufficient extent for practical needs. By means of relatively simple, rapid tests we can measure such properties as elastic modulus, limit of proportionality and proof stress, upon which design can be based with confidence. The case of the soft metals, such as lead and tin, is well known to be exceptional. They possess no definite limit of elasticity, and the value of proof stress or tensile strength depends to a great extent on the speed with which the test is carried out. Design here must be based on other considerations than a well-established theory of the proportionality of stress and strain. It is now generally recognized that steels and non-ferrous alloys possess at temperatures not greatly exceeding that of the atmosphere, characteristics quite different from those existing at ordinary temperatures, and that they assume qualities similar to those of the soft metals. Not only have they no limit of elasticity, but the proof stress and the ultimate stress depend on the time of application of the load. Flow under load may persist for long periods of time, possibly indefinitely, and the determination of a true maximum stress becomes a matter of great difficulty.

Jan 1, 1939

By D. A. Dahlstrom

Application of the cyclone to separation of undesirable -200-mesh clay, silt, and high-ash fractions from coal slurries was found to possess many economic and process advantages. Up to 93.3 pct removal was attained at rates of 113 to 155 gpm per sq ft of cross-sectional area.

Jan 2, 1951

By Will Mitchell, T. G. Kirkland, C. L. Sollenberger

R. S. Handy (Santa Rosa, Calif.)—It would be interesting to learn the comparative results of treating the Korean scheelite ore described in this paper according to the following procedure: I—Follow the procedure described in the paper to the recovery of the sulphides by flotation. 2—Dilute the residue from the sulphide flotation strongly with water and disperse the contained colloids by adding a mixture of 75 pct sodium silicate and 25 pct quebracho to dispersion point. 3— Settle the dispersed pulp and decant the supernatant colloids. 4—-Dilute, settle, and decant the pulp until the settled residue is crystalline. Not over 10 pct of the tungsten minerals should follow the colloids. 5—Treat the settled residue by flotation, having established the proper pH. Oleic acid homogenized with cresylic acid or kerosene is more selective for scheelite than is oleic acid alone. (The recovery of the contained tungsten minerals should be practically complete in this operation.) 6—Deflocculate the tungsten concentrate from step 5 with the same dispersion agents as in step 2 and treat the deflocculated pulp by gravity. The minerals that tend to float with scheelite are generally of low specific gravity and the separation is efficient. The heavier contaminants, such as pyrrhotite and magnetite can be removed magnetically, leaving a practically pure scheelite. E. J. Pryor (Imperial College of Science and Technology, London)—It occurred to me that instead of using temperature as a differentiating control, more precision might be obtained with a reagent of a type we developed here for the flotation of high grade fluorspar in cold pulps. This reagent, which is manufactured on a modest scale in England, is based on oleic acid, which has been modified by our patented process to ensure complete stable dispersion at any desired concentration in water. It thus becomes possible to utilise unimolecular layers with good selectivity. In the fluorspar flotation for which we developed it, it is possible to hold a tight control on depressing quebracho for the calcite without substantial loss of flu-orite, and recovery exceeding 99 pct is not uncommon in the mill where it is in use, even under wintry conditions. No attempt has been made yet to extend the use of the reagent, as we have not completely overcome

Jan 1, 1952

By William Hutton Blauvelt

The type of gas producer in which the ashes are fluxed and run off as slag was among the very earliest made. Ebelmen built the first one in 1840 at Audincourt, France, only a year after the installation of the first gas producer of which we have record. Charcoal was used as the fuel, with blast-furnace slag and clay as flux. My interest in this type of producer began when as a boy I saw the fluxing producer at Chester, N. J., which was invented by W. J. Taylor, and described by him in 1881.' This producer was invented independently by Mr. Taylor to meet the difficulties he experienced in making producer gas for roasting sulphurous iron ores. It will be of interest to review briefly his description of his producer. It was built like a small blast furnace, having a hearth 24 in. in diameter and 24 in. high. The bosh angle was 25' from the vertical; the diameter at the bosh 4 ft. and at the top 3 ft.; the total height 12 ft. The producer contained one water-cooled tuyere 12 in. above the bottom, with a 1.5-in. nozzle. Depth of the coal above the tuyere, 6 ft. Mr. Taylor mixed the coal with from 30 to 40 per cent. of basic blast-furnace slag to flux the ash. Occasionally some limestone was also used, but never limestone alone, as the use of the furnace cinder gave a larger volume of slag and made it easier to maintain a proper fluidity. The producer was blown with a small Weimer blowing engine, delivering 300 ft. of air per minute, at from 1 to 1.5 lb. pressure. The slag was tapped every 2 hr. and was black and glassy in appearance. Broken or egg size anthracite was used. The fine sizes of anthracite could not be made to work. Mr. Taylor expressed the belief that bituminous coal could be used if not too fine, but no experiments were made with this coal. Runs were made of four weeks' duration, with no stops or changes. Mr. Taylor reported the following advantages: 1. Excellent gas, very uniform in quality. The high fuel bed permitted no air to pass unconsumed, and the gas was almost entirely free from carbonic acid.

Jan 1, 1914

By Paul Gordon, A. S. Iyer

Apreliminary investigation has been carried out on the annealing behavior of explosively deformed copper as compared to that of conventionally deformed copper, using hardness, stored energy, and the sharpening of X-ray spots on Debye rings as the measures of annealing. Some metallographic observations were also made. Two purities of copper were studied. The first was tough pitch copper obtained as a small piece from the guard ring of a sample explosively deformed to approximately 500 kbars.* The second consisted of mentedand deformed these samples quite badly so that only a few small fragments were available for the annealing experiments. As a result, little in the way of quantitatively significant data was gleaned from the measurements. However, several important qualitative differences between the annealing of explosively deformed and conventionally deformed copper have been observed. It is these effects which are described in this report. Fig. 1 presents the results of hardness and stored energy measurements during the annealing of the high-purity copper after explosive and after conventional deformation. The data for the conventionally deformed copper were taken from the work of Gordon;' in this copper it is evident that most of the stored energy is released concommittantly with the hardness drop. As shown in orddon's' investigation, these effect:: are definitely associated with recrystal-lization. In the case of the explosively deformed copper, on the other hand, a large fraction of the stored energy is released before any appreciable hardness change takes place. At 160°C about 40 pct, and at 170°C about. 80 pct, of the stored energy appears to have been released prior to the onset of softening, i.e., undoubtedly prior to recrystallization. In view of the facts that the hardness and energy measurements were made on separate samples and that there is reason to suspect that the intensity of the explosive deformation from sample to sample may not have been uniform, a check run was carried out in which both energq release and hardness changes were measured cnn the same sample. The results of this run, shown in Fig. 2, confirm the conclusion that much of the stored energy is released before the hardness begins to change appreciably. In an effort to obtain some idea of the activation energy associated with the early release of energy, a single callorimetric sample was annealed in two steps, first at 149.5"C and then at 159.5"C, Fig. 3.

Jan 1, 1962

By Charles T. Malcomson

In the United States, improvements in methods of combustion have made possible the use of the smaller sizes of anthracite. This coal is now being reclaimed from the culm banks accumulated by the miners in the more prodigal years. To-day the freshly mined "slush" is segrega,ted and stored against the time when, through briquetting or some other means, it may be utilized as a commercial fuel. For many years Europe has achieved enviable results in the conservation of her small coal by briquetting. This profitable industry, first placed on a commercial basis in France in 1842, has grown to such magnitude that the production during 1913 exceeded 36,000,000 short tons. Briquets produced in Great Britain are used principally for steam purposes and the greater part of the output is either exported or taken by the Admiralty. On the Continent the briquets are sold in all branches of the coal trade. The French railways consume from 16 to 40 per cent. of their fuel in briquet form, and in Germany the lignite briquets (of which 20,000,000 tons were produced in 1913) are as familiar and interesting to the American traveler as the huge porcelain stoves in which they are burned. It is not strange, therefore, that aggressive and far-sighted promoters heralded this means of converting our ubiquitous coal waste into revenue. To the superficial student the briquetting process seemed so simple as to make success easy. It is for this reason principally that the path of the industry in America has been strewn with failures. The rash enthusiast had either not worked out the mechanical problems involved or had failed to grasp the local conditions under which the briquets must be made and sold. It may be confidently stated, however, that in spite of the many vicissitudes through which it has passed, coal briquetting is now an accomplished economic success in this country, and as a profitable adjunct to the coal industry it has come to stay. Several valuable contributions relating to coal briquetting are found in the Transactions. Charles Dorrance, Jr., has sketched briefly the history of the anthracite briquetting plants from the time of Loiseau's pioneer plant down to that of the Lehigh Coal & Navigation Co. at Lans-ford. Since then this phase of the industry has remained practically at

Jan 1, 1915

By Walter H. Bruckner, George B. Clark

SINCE the end of World War II interest has been increasing in the use of shaped charges in the mining industry and in other industries using explosives for blasting purposes. Shaped charges employ the principle known as the "Munroe effect," which was discovered by Charles E. Munroe more than 50 years ago (in 1888). Details of their design have been explained e1sewhere.l,2,3 Fig I shows the essential features of design of two types of shaped charges (with conical and hemispherical cavities) and a schematic sketch of their action upon detonation. The following discussion deals with the behavior of the metal in the cavity liners when they are subjected to intense pressures exerted when the explosive charge is detonated. Among the conclusions reached in research on shaped explosive charges, the following have been established concerning cavity liners: 1,2 I. The optimum wall thickness of a conical cavity liner is dependent upon the apex angle of the cone as well as on the base diameter of the charge. Acute apex angles require thinner walls for optimum performance and more obtuse angles require thicker walls for the same base diameter. 2. Cones were more effective in forming a penetrating jet when the walls were tapered; i.e., the thickness of the wall of the cone increased from the apex down. 3. The physical and mechanical proper- ties of metals have a marked effect upon their performance as cavity-liner material. Boiling point, ductility, malleability, tensile strength, and hardness are among the properties that influence the effectiveness of a metal used as a cavity liner. Lead, for example, makes a wide, flat crater in steel plates. Aluminum makes a deeper crater than lead, and an aluminum alloy having a high tensile strength makes a deeper hole, but slightly smaller in diameter. Cast iron makes a deep, narrow hole. These findings, together with the following analysis under Metallographic Survey of Slug, offer solutions to many of the problems involved in solving the mechanism of the formation of Munroe jets. It has been fairly well established that cavity liners collapse in a manner similar to that indicated in Fig 2. Conical liners are known to collapse upon themselves while hemispherical liners are believed to turn inside out in the process of jet formation. The first has been definitely proved by recovery of collapsed portions of cones, while liners from partly detonated charges show that hemispheres may turn inside out. Fig 3 shows a sketch of a recovered slug from a 6-in. shaped charge using a 45° cone made of cast iron. (This size of charge drilled holes up to 3 ft in depth in solid granodiorite.)

Jan 1, 1947

By Robert J. De Angelis, James H. Barker

An improved method for solving dynawzical dislocation problems using a digital computer is described in this paper. Interactions between two distinct types of dislocations were studied: attractive screw dislocations; and Lomer lock forming dislocations. One dislocation is positioned in the lattice and is initially at rest, while the other dislocation is moved through the lattice on an intersecting slip plane at a constant velocity in the range 0.5 to 0.999C. (C is the transverse velocity of sound.) The results obtained from these computations indicate that screw dislocations account for a small fraction of the total strain over a wide portion of the range of velocities studied. They further indicate that mixed dislocations mainly repel other dislocations in the neighborhood of the active glide plane. From this a possible explanation for cell formation is put forth. The density of Lomer locks expected to exist after a strain of 0.2 was found to be 1.4 x 106 cm-2 which is in good agreement with indirect experimental estimates. IN the past, predictions of favorable or nonfavorable dislocation reactions were based on the associated changes in elastic strain energy. Such considerations take no account of the probability of the two dislocations coming into contact to react. Venables1 was the first to approach these probabilities by considering the interactions between two moving screw dislocations on perpendicular glide planes. Because of the restrictive types of dislocations and glide plane geometry employed, his results have limited application to metallic crystals. The work to be presented here develops a general approach to solving dynamical dislocation problems; either dislocation-dislocation interactions, presented here in detail, or dislocation interactions with any other suitably defined stress field. Two types of dislocation-dislocation interactions common to face centered cubic (fee) materials are considered: those between pure screw dislocations of opposite sign on intersecting slip planes and those between mixed dislocations on intersecting slip planes, that can react to form a perfect dislocation. This latter reaction, referred to as the Lomer reaction, produces a locked product dislocation that finds it energitical favorable to disassociate into two Shockley partials and a stair-rod dislocation. This partial configuration known as a Lomer-Cottrell (L-C) lock plays a major role in work hardening of fee crystals. seeger2 names the L-C lock as the prime contributor to Stage II hardening while Kuhlmann-wilsdorf3 and Meakin and Wils- dorf4 also state that it is a significant contributor to work hardening. However, with a few notable exceptions,5-7 direct observations of the Lomer lock and the L-C lock by electron transmission microscopy are scanty, and even these are subject to other interpretations.5,6 In a study of partial dislocations present in austenitic stainless steel, whelan8 did not observe any L-C locks at the head of pile-up groups. This result contradicted existing work hardening theories and led him to postulate an alternate theory based on the stress required to break away dislocations intersecting a pile-up group, from their stacking fault nodes. Due to the importance of the Lomer reaction in producing L-C locks which are an essential feature in current work hardening theories and because there exist no data giving direct quantitative values for the density of locks, and because there has even been some doubt expressed as to whether this important reaction occurs at all, a study of the dynamic behavior of the mixed dislocations which form the Lomer lock was undertaken. Due to their ability to cross-slip with relative ease, screw dislocations play an important role in the deformation of fee crystals. For this reason, the second type of reaction considered here is between screw dislocations of opposite sign. In addition, computations in volving screw dislocation interactions are relatively simple, thus providing a convenient check on the cornputational scheme employed. DEFINITION OF PROBLEM The force exerted on a dislocation due to a generalized stress field is given by the Peach and Koehler9 equation: Here t2 and b2 are respectively the tangent and Burgers vectors of the dislocation, and T1 is the stress dyadic defining the local stress field. The stress field may be externally applied or generated internally by the presence of a lattice defect, such as a second dislocation, as is the case in this work. Frank10 has shown that an equivalent momentum, P, of a screw dislocation can be defined by: Here, EST is the total energy of a screw dislocation and ESo is its rest energy. The left side of Eq. [2] is the time derivative of momentum and the right side is the position derivative of the energy due to the dynamical nature of the dislocation. The total energy of a dislocation is the sum of the potential and kinetic energies. Weertman11 has developed the expressions which were used here; these give the potential and kinetic energies of uniformly moving edge and screw dislocations in an isotropic medium.

Jan 1, 1969

By K. B. Nowels

Data pertaining to pipe line flow for both oil and gas in horizontal or nearly horizontal pipe lines are both extensive and accurate. However, the pipe formulas used to determine pressure drop for flowing fluids (liquids and gases) under conditions of horizontal flow are not generally applicable to flowing oil and/or gas wells. Except for some data developed in small laboratory set-ups, little or no information was available concerning flow of oil and gas mixtures in vertical pipes, when, in 1928, the writer began the development of a method for computing pressure drops in the pipes of flowing oil wells, as outlined in this paper. In 1929, Urenl presented some findings based on laboratory experiments in which vertical flow of an extremely heavy crude oil was induced by means of air through a 2-in. pipe, 41 ft. long. The friction factors derived from the experiment, as well as values for pressure drop per 100 ft., are not believed satisfactory in their application to flow problems in the field. Versluys,2 also in 1929, presented a mathematical development of the theory of flowing oil wells, and in 1930, gave a companion paper3 setting forth some principles governing the choice of length and diameter of tubing in oil wells. Since the termination of the study presented in this paper, another valuable contribution pertaining to the problem of vertical flow was made by Moore and Wilde.4 Although there were writings dealing with the principles of the gas-lift, a search of the available literature indicated that specific information on vertical flow was lacking with the exception of the writings of Uren, Versluys, and Moore and Wilde, to which reference has been made.

Jan 1, 1932

[¦Abad, Leopoldo F., College of Min., Univ. of California Berkeley, Cal. '23 ¦Abarquez, Ramon F., Met., Bureau of Science Manila, P. 1. '24 ¦Abbey, Robert Graham, Student, Case School of Applied Science Cleveland, Ohio. '21 Abbott, A. N., Mines Supt., Mazapil Copper Co., Ltd ...Concepcion del Oro, Zacatecas, Mexico. '23 Abbott, Clarence B., Gen'l Supt., Iron Mines Div., Tenn. Coal, Iron & R. R. Co., 1405 Minnesota Ave., Bessemer, Ala.' '04] [ ]

Jan 1, 1925

By G. F. Comstock

THE subject of transverse fissures in steel rails has been discussed very thoroughly in recent years from various points of view and the final opinions expressed may be roughly classified into two groups: (1) That these fissures are the result merely of fatigue of the steel and are independent of the quality of the metal. (2) That the quality of the metal and the mill practice must have something to do with them. The first point of view was most-ably and logically presented by J. E. Howard,1 and in the discussion of this paper, as well as in several other preceding publications, Dr. P. H. Dudley, Consulting Engineer of the New York Central Lines, has strongly defended the other opinion.2 The steel makers of the country have naturally rallied under Mr. Howard's banner, hoping to place the entire blame for these. failures upon the railroads with their high wheel-loads, hard steel, heavy traffic, and sometimes inferior roach-bed; while the railroad men,, on the other hand, have been busy accumulating statistics and records in the effort to find an actual reason in the rails themselves that would account for the seemingly haphazard occurrence of transverse fissures under varying conditions and at widely separated points. The view that these fissures were due merely to normal fatigue under alternating stresses seemed most reasonable to the writer until quite recently, because from work clone in this laboratory, as well as the work of other investigators of the problem, no structural differences, in the vast majority of cases, were found between metal at the nuclei of transverse fissures and metal at similar positions in the same rails or in other rails that had not developed fissures. . Within the last year or two, however, since the method of etching polished sections for the microscope with a cupric chloride solution has been tried systematically. on lengthwise sections, passing through the nuclei of transverse fissures, evidence

Jan 11, 1918