Aamot, Olav Crone, Research Engr., Norsk Elektrokemisk Kongensgt, 18, Oslo, Norway ?29 Abbott, Clarence E., V.P., Charge of Raw Materials, Tenn. Coal, Iron & R. R. Co., 1242 Brown-Marx Bldg., Birmingham, Ala. '04 Abbott, Louis Benjamin, Chief Engr., Consolidation Coal Co., Watson Bldg., Fairmont, W. Va. '15 Abel, Raymond L., Asst. Prof., Dept. of Pet. Refin., Univ. of Pittsburgh Pittsburgh, Pa. '28 Abel, Walter D., Cons. Engr 364 S. Cloverdale Ave., Los Angeles, Calif. '32 Abele, Louis T 1457 Euclid Ave., Zanesville, Ohio. '31 Abell, Leo M Sullivan Concentrator, Chapman Camp, B. C., Canada. '31 Aborn, Robert H., Asst. Met., Research Lab., U. S. Steel Corp., Lincoln Highway, Kearny, N. J. '19 Abraham, W. E. V., East India United Service Club, 16 St. James' Sq., London, S. W. 1, England. '28

Jan 1, 1936

By P. R. Sperry, M. L. Holzworth, P. A. Beck

The basic work of Z. Jeffries 1,2,3 has long ago established the main features of grain growth in the presence of a dispersed second phase. Working with sintered specimens of initially fine grained tungsten, to which various amounts of thoria had been added, Jeffries found that grain growth was inhibited, that is, practically prevented, up to a certain annealing temperature. When this temperature, which increased with the thoria content, was exceeded, extremely large grains developed abruptly from the fine grained matrix. such a a temperature" was later found by Gross-mann~3,14 in certain types of steel, while ~~i~ showed15 that in other steels grain growth was gradual, without inhibition and abrupt coarsening. Later work demonstrated the connection between coarsening and aluminum additions. The viewpoint that the direct cause of inhibition and coarsening in aluminum killed steels is a fine dispersion of aluminum oxide21 appears to be held quite generally, although some doubts have been voiced even very recently, 20 In steels with Ti additions the titanium carbide phase is considered responsible for the inhibition effects found.20 The coarsening temperature increases with the titanium content. That coarsening may occur, as a result of, certain heat treatments, even in low carboil rimmed sheet steel, was shown by Samuels. He also detected coarsening in a steel ingot of similar composition, after giving it the same heat treatment as that used by him for the sheet material. In this instance the identity of the inhibiting phase has not been determined. However, Tangerding found23 that even the few small carbide particles, which occur in carbonyl iron, have a very marked inhibitive effect. As a result of an oxidizing anneal at 850°C, large grains begin to form at the surface of the carbonyl iron specimen, and gradually grow inward as the subsurface oxidation of the carbide particles progresses and eliminates the obstruction. The carbide particles Can be removed also by annealing in hydrogen, with similar results. But if the oxidizing anneal of 10 hr at 850°C in air is followed between in hydrogen for 75 hr at the Same temperature, grain growth is more hibition usually the whole specimen is transformed into a single crystal (approx. 1.5 cm X 5 cm). The reversed procedure, that is, hydrogen annealing followed by oxidizing annealing leads to smaller grains. Tangerding arrived at the logical conclusion that there must have been in his specimens some additional obstruction to grain growth hibition from a minor impurity, other than carbon. It seems likely that this obstruction was caused by an oxide formed during the oxidizing anneal and gradually reduced rtain the subsequent hydrogen-annealing. Other instances of grain growth inhibition of varying severity, associated with a dispersed second phase, have been described by several authors. Notable examples: lead with 0.06 pet Cu or Ni,24 cartridge brass with 0.12 pct Cr,25 or with up to 0.15

Jan 1, 1949

By Enid C. Plante, K. L. Sutherland

Practical metallurgists are unanimous in stating that oxidation of mined sulphide ore adversely affects separation of the constituent minerals under standard conditions in a mill. Frequently, the need for different operating conditions in different plants is attributed either to the extent of oxidation of the mineral surfaces or to soluble oxidation products. The investigations reported in this paper study the effect of oxidation on the primary condition necessary for flotation, namely that of adhesion of an air bubble to the mineral. Oxidation Products from Sulphide Minerals Weinig and Carpenter1 state that the relative rates of oxidation of some sulphides are: FeAsS > FeS2 > CuFeS2 > ZnS > pbS > Cu2S tetrahedrite. They also show that oxidation is rapid at first, that sulphides of older geological formations are more stable than those of recent date and that mixtures oxidize more rapidly than any one mineral alone. The more rapid oxidation of mixtures is borne out by results of Gottschalk and Buehler2 who found that PbS, zns and cus oxidized 8 to 20 times faster when pyrite was present. Only the end products of oxidation, sulphate and the metal ion, were identified in these tests. Gaudin3 states that pyrite is difficult to oxidize in the laboratory. Winchell,4 using pyrite containing 99.98 pct FeS2, allowed water to percolate through a bed of this ground material. At the end of three months only a trace of Fe+++and So4- were found. Even after 10 months the quantity of Fe+++ was only 7.8 mg and SO4- 25.5 mg per liter of percolating solution. Car-michael5 confirmed Winchell's results on the slow oxidation of pyrite. Usually the oxidation of sulphide surfaces has been conducted in neutral or acid solutions, the acidity being caused by the oxidation products. Eliseev and Nagir-nyaka found that treatment of pure pyrite with lime gave only thiosulphate, but considered it possible that thiosulphate was obtained not by oxidation of the pyrite itself, but by oxidation of calcium disul-hide. Mitrofanov7 suggested that thiO~ulphate was formed by the following process: oxidation of sulphide to give free sulphur (this frequently happens with marcasite), followed by oxidation of the sulphur to sulphur dioxide and reaction of the sulphur dioxide with sulphur to give thiosulphate. Ferric and ferrous hydroxides, or similar compounds, were shown to be present. The Research Staff of the United Verde Copper Co.8 treated ore from the United verde mine with lime. Thiosulphate, sulphide and polysulphides were stated to be

Jan 1, 1949

By E. C. Skinner

Cardox, which consists essentially of a steel tube containing carbon dioxide compressed to the liquid state, is a trade name designating a device used principally in coal mines to break down coal. The use of Cardox to break down coal was developed in the Middle Western coal fields around 1927 or 1928. At first, a large, heavy tube was used, requiring many parts. Through experimentation and technologic improvement, the weight of the tube has been brought down from 88 lb. to 20 lb. and the new, light tube makes use of larger volumes of CO2 at lower pressures than formerly was thought possible. This blasting method is extensively used today in coal mines and probably one tenth of the bituminous coal produced in the United States is prepared with Cardox. Construction and Application As used in the coal mine, Cardox looks like a piece of steel pipe 2 to 3 in. in diameter and 3 to 5 ft. long. When it is necessary to fire a shot, the tube is wired with two leg wires that are long enough so that when the tube is pushed the desired distance into the hole the wires will protrude 5 to 6 in. It has been found that No. 18 insulated copper annunciator wire is the best material for leg wires. A two-conductor rubber-covered shot-firing cable of sufficient length is then attached to the leg wires. A 2 to 6-volt current is applied, either by means of shot-firing batteries or the standard type of shot-firing generator. Upon the application of the current, the charge in the cartridge is set off. Because the breaking action upon the coal is supplied by the relatively slow physical expansion of the carbon dioxide gas rather than by the rapid chemical formation of gases as in more familiar explosives, the result is a slow heaving action, somewhat similar to that produced by black powder, rather than a shap detonating effect. Permissible powder does its work at roughly ten times the pressures in use with Cardox. The escaped gas from a Cardox shot apparently works along the planes of weakness in the coal face, such as the coal cleats, the edges of the cut, and along the top of the seam, breaking off the coal toward the free faces and heaving the mass of coal outward. Cardox tubes are manufactured in various sizes to take care of variable conditions of seam size, undercut depth, cleatage, coal hardness, and so forth. The tubes range in diameter from 2 to 3 in. (Table I) and the normal CO2 charge is from 24 to 96 oz. For any one tube size, several sizes of shear disks are available, thus excellent control of the type of shooting desired is possible. In general, local experience and experimentation dictate the size of tube chosen for any particular job. For high coal, and deeper or wider cuts, a larger size is chosen to start with, and the opposite is true for low coal, softer coal, or small cuts. After the tube size has been experimentally selected, tests are run in the mine to determine how many shot holes are needed and where the holes should be placed. The size of the disk,

Jan 1, 1944

By E. C. Skinner

Cardox, which consists essentially of a steel tube containing carbon dioxide compressed to the liquid state, is a trade name designating a device used principally in coal mines to break down coal. The use of Cardox to break down coal was developed in the Middle Western coal fields around 1927 or 1928. At first, a large, heavy tube was used, requiring many parts. Through experimentation and technologic improvement, the weight of the tube has been brought down from 88 lb. to 20 lb. and the new, light tube makes use of larger volumes of CO2 at lower pressures than formerly was thought possible. This blasting method is extensively used today in coal mines and probably one tenth of the bituminous coal produced in the United States is prepared with Cardox. Construction and Application As used in the coal mine, Cardox looks like a piece of steel pipe 2 to 3 in. in diameter and 3 to 5 ft. long. When it is necessary to fire a shot, the tube is wired with two leg wires that are long enough so that when the tube is pushed the desired distance into the hole the wires will protrude 5 to 6 in. It has been found that No. 18 insulated copper annunciator wire is the best material for leg wires. A two-conductor rubber-covered shot-firing cable of sufficient length is then attached to the leg wires. A 2 to 6-volt current is applied, either by means of shot-firing batteries or the standard type of shot-firing generator. Upon the application of the current, the charge in the cartridge is set off. Because the breaking action upon the coal is supplied by the relatively slow physical expansion of the carbon dioxide gas rather than by the rapid chemical formation of gases as in more familiar explosives, the result is a slow heaving action, somewhat similar to that produced by black powder, rather than a shap detonating effect. Permissible powder does its work at roughly ten times the pressures in use with Cardox. The escaped gas from a Cardox shot apparently works along the planes of weakness in the coal face, such as the coal cleats, the edges of the cut, and along the top of the seam, breaking off the coal toward the free faces and heaving the mass of coal outward. Cardox tubes are manufactured in various sizes to take care of variable conditions of seam size, undercut depth, cleatage, coal hardness, and so forth. The tubes range in diameter from 2 to 3 in. (Table I) and the normal CO2 charge is from 24 to 96 oz. For any one tube size, several sizes of shear disks are available, thus excellent control of the type of shooting desired is possible. In general, local experience and experimentation dictate the size of tube chosen for any particular job. For high coal, and deeper or wider cuts, a larger size is chosen to start with, and the opposite is true for low coal, softer coal, or small cuts. After the tube size has been experimentally selected, tests are run in the mine to determine how many shot holes are needed and where the holes should be placed. The size of the disk,

Jan 1, 1944

By Orlando Romig

PART I-PREPARATION OP METALLIC SINGLE CRYSTALS WITH ESPECIAL REFERENCE TO SINGLE CRYSTALS OP ZINC? As metals and alloys are composed, of, an aggregate of allotriomorphic crystals or grains, each possessing an individual orientation, the physical characteristics of a metal or an alloy are closely related to the properties of the individual crystals. The preparation and study of single metallic crystals are, therefore, matters of considerable importance. The advent of the X-ray spectrograph as a valuable metallurgical tool has magnified the importance of this subject, because the interpretation of some X-ray spectrographs is difficult unless single crystals are used in these studies. PREVIOUS WORK The first paper, as far as the writer knows, on the behavior or preparation of single crystals of metals is by Baker.1 He describes the behavior of extruded wires of sodium and potassium. These wires, when pulled in tension, instead of I showing the usual conical fracture common to most metals, had a chisel-shaped fracture when they were broken. I and II, Fig. 1, have a similar fracture. Baker checked his results by preparing single crystal wires from molten sodium and potassium and observing their properties. He prepared the wires by filling glass tubes, under oil, with the molten metal. The surfaces of the strained wires showed slip bands of remarkable clearness of which photographs are shown in his paper. He concluded that these wires were single crystals and "that the portions of the metal brought into play are cubes. Such cubes, when placed so that a plane through 'two opposite edges was parallel to the axis of the wire, would allow of lateral contraction by faces gliding over one another in one direction only and not in the direction at right angles."

Jan 1, 1927

By William L. Fink, Dana W. Smith

In parts I1 and II2 of this series, there were presented results of investigations on the age-hardening of an aluminum-copper and an aluminum-magnesium alloy. It was shown that the simple precipitation theory of hardening3 adequately explained the aging phenomena, including certain so-called "anomalous" behaviors which had caused other investigators to reject or modify the precipitation theory. However, these papers did not discuss the double aging peaks, which have been stressed in recent articles by Dr. M. Cohen4 and Dr. M. L. V. Gayler.6 The present paper is devoted to an explanation of this "anomaly." Fig. 1 is a generalized schematic representation of aging curves at different temperatures. Curve A corresponds to the aging at the lowest temperature, and D at the highest temperature. Certain previous investigators have explained curve A and the initial peaks

Jan 1, 1938

By William L. Fink, Dana W. Smith

In parts I1 and II2 of this series, there were presented results of investigations on the age-hardening of an aluminum-copper and an aluminum-magnesium alloy. It was shown that the simple precipitation theory of hardening3 adequately explained the aging phenomena, including certain so-called "anomalous" behaviors which had caused other investigators to reject or modify the precipitation theory. However, these papers did not discuss the double aging peaks, which have been stressed in recent articles by Dr. M. Cohen4 and Dr. M. L. V. Gayler.6 The present paper is devoted to an explanation of this "anomaly." Fig. 1 is a generalized schematic representation of aging curves at different temperatures. Curve A corresponds to the aging at the lowest temperature, and D at the highest temperature. Certain previous investigators have explained curve A and the initial peaks

Jan 1, 1938

W. 0. HOTCHKISS,* Madison, Wis.-When we began to do geological field work in the Lake Superior region, we found a correlation in existence, and, as youngsters, accepted all that as settled. Both Mr. Allen and I, since that time, have seen a great many things that were not apparent nor visible to Van Hise, and those who worked with him; we realize now that the correlation was not final and that much remains to be determined concerning geology of the Lake Superior region. My attitude on this matter is that we should not publish an amended correlation as a final thing. We should avoid, in every way possible, foreclosing the minds of those who follow us in working in the geology of this region. As a matter of fact, no correlation can be final at present, because facts and data are accumulating so rapidly that every classification must be immediately modified to fit further observation. Consequently, my attitude in this matter would be, instead of saying that the iron formations of the Lake Superior region are all Middle Huronian, to say that there may be three Huronians-or four or five- we do not know. I believe it is better policy to hold to our present correlation. I do not believe there is any economic benefit to the mining man or the geologist working on problems relating to explorations for iron ore, that cannot be just as well solved by maintaining our present correlation, with a. wholesome idea of our lack of knowledge and the necessity for further detailed work. Then, if any new horizons are discovered in any particular range, the minds of the investigators will not be foreclosed because some one has said that all the iron formation is in the Middle so that there is no use looking elsewhere for it. There is use looking elsewhere, in many cases, as the ore deposits become exhausted.

Jan 1, 1920

By C. W. MacGregor

THE observation of the flow layers, or Lüders' lines, produced in mild steel when it is stressed into the plastic range often provides considerable useful information for the study of the fundamental mechanism of the plastic flow of metals. It is a commonly observed fact that as soon as the upper yield point in a mild-steel tensile-test bar is passed, an unstable condition develops in the equilibrium, the load on the testing machine drops and if the surface of the bar contains a thin mill scale, the latter begins to flake off rapidly along certain "lines." These "lines" are in reality traces of wedge-shaped flow layers and are formed by the intersection of the surface of slip and the surface of the bar. The average plane of the flow layer itself has been found by various experimenters to be inclined at an angle of approximately 45° to the axis of the test bar. In a body of more complicated shape stressed in possibly a different man-ner, the tangent planes to the flow layers at each point seem in many cases to be inclined at an angle of about 45° to the principal stress direc-tions at the point. As examples of the latter may be mentioned the logarithmic spirals obtained when a rivet hole is punched in a thin plate, or when a tube is subjected to internal pressure only, etc. Hence if the flow layers are observed from an experiment, the shear-stress trajectories -the curves indicating the directions of the maximum shearing stresses in the body-may then be approximately determined. Since the latter curves form an orthogonal family inclined at 45° to the principal stress directions, the family of principal stress trajectories, or the curves indicating the directions of the principal stresses, may be thus obtained. Although the discontinuous type of stress-strain curve at the yield point is commonly observed with test bars of mild steel, more recent experiments have shown that this is by no means the only material exhibiting this interesting phenomenon. A similar effect has been observed in zinc and cadmium crystals, by Becker and Orowan;1 in duralumin and other aluminum alloys, by Dawidenkow,2 Elam,3 Fell, and others; in copper and copper-alloy crystals, by Elam;5 in brass by Elam;5 in brass wires by deForest;6 in higher carbon steels, tungsten steel, and

Jan 1, 1939

By R. H. Hadfield

Professor ArnolD, of the Sheffield Technical School, who has done so much excellent work in metallurgical research, recently produced, with the aid of aluminum, a sound ingot and bar from the purest known Swedish brand containing 99.8 per cent. of pure iron. Table 1. shows the physical quantities of this metal. TABLE I.— Tests of a Sample of Almost Pure Iron Prepared by Professor Arnold from D. v Ewedish Bar, Containing Before Fusion 0.04 Per Cent. of Carbon. I. II.+ III. Series mark,.. 136 1.371F ...... C, 0.07 0.07 Si, 0.04 0.04 8, 0.02 0.03 ...... Analysis, per cent,. .. P, 0.02 0.015 ...... Mn, 0.06 0.07 Al, 003 ............ Fe, 99.76 99.81 ...... Specific gravity,........... 7.863 ...... Original diameter, inches,. .. 0.564 0.798 0.798 Original area, square inches,. . 0.25 0.50 0.50 Limit of elasticity, tons per square inch,...... 18. 3.8 Breaking-load, tons per square inch,. 21. 23. 14.75 Total elongation, per cent., measured on 2 in.,...... 50. 49.25 61. Total reduction of area, per cent.,. 80. 69.60 61.20 Extension at permanent set, per cent.,...... 0.007 ...... silky and Appearance of fracture,. .. . silky i granular in parts.

Jan 1, 1894

By M. J. Hordon

Measurements of the 103 yield stress of ordered and disordered poly crystalline Cu ,Au were related to the ordered antiphase domain size determined by resistivity measurements. For undeformed material, a yield stress maximum wa obtained at a critical domain diameter of about 40A. Plastic deformation resulted in a marked increase in the yield stress and electrical resistivity of the ordered alloy compared to the disordered, the strain hardening rate increasing regularly with initial antiphase domain size. Order hardening was accompanied by a sharp reduction in size of the initially large domains. It has been observed that the yield stress of ordered and partially ordered Cu3Au alloy varies sensitively with antiphase domain size aid degree of order.ly2 In addition, ordering of the lattice leads to a marked increase in the strain hardening rate (order hardening) as compared to the rate for the disordered alloy. In the present investigation, changes in the electrical resistivity and yield stress of ordered polycrystalline Cudu with varying initial domain diameters were measured after tensile plastic deformation in order to examine the effect of cold work on the antiphase domain size. EXPERIMENTAL PROCEDURE Au-Cu alloy of 99.99 pct purity analyzing 50.85 wt pct Au-balance copper was obtained from the Handy-Harmon Co., N. Y., in the form of 0.061 in. diam drawn wire. Wire specimens 3 in. in length were given the following annealing treatment in nitrogen: 500" for 72 hr, 820" for 15 hr, and 450" for 5 hr, followed by a water quench. The annealing sequence resulted in a completely disordered structure with a grain size of about 0.2 mm. The disordered specimens were then reannealed at 360' in nitrogen for periods varying from 10 min to 150 hr followed by quenching to produce ordered structures with varying domain sizes. The degree of ordering and variation of domain size was followed by electrical resistivity measurements made at room temperature using a low resistance precision Kelvin double bridge apparatus. The specimen resistance was determined over a length of 4.0 cm between two brass knife-edge contacts while the specimen was immersed in an oil bath to minimize temperature variations. In addition, the current flow in the circuit was minimized by a current pulse technique in balancing the bridge in order to avoid heating the specimen. Using a sensitive galvanometer to detect the bridge null, the accuracy of the resistance measurement Wire specimens were plastically strained in tension with an Instron tensile unit at strain rates in the range 5 x 10"5 sec-' to 2 x 10"4 sec-'. Stress and extension data were fed into the Instron chart drive amplifier to obtain the actual stress-elongation curve from which the yield stress at 10"3 strain was determined. The maximum resolution of the apparatus was approximately 50 psi stress and 3 x 104 strain. At various plastic strain levels, deformation was interrupted and the electrical resistivity determined after removing the stress. RESULTS AND DISCUSSION 1) Yield Strength of Ordered Cudu. In order to determine the effect of the ordered antiphase domains on the initial yield stress, specimens were prepared with varying domain sizes ranging from zero for 5 completely disordered structure to about lo5A for a completely ordered structure by suitable annealing treatment. Domain sizes were estimated by comparing room temperature electrical resistivity data with the original data of Jones and sykes3 as modified by rdle.' In agreement with previous work, the resistivity varied sensitively with domain diameter and degree of order, decreasing from approximately 11.6 x l0- ohm-cm for the disordered structure to about 5.9 x l0- ohm-cm for ordered domains above 10"3 cm in diameter. Fig. 1 shows the change of the 103 yield stress with ordered domain size. It is evident that the maximum

Jan 1, 1963

By L. D. Jaffe

IN previous metallographic work on titanium and its alloys, difficulty has been encountered in distinguishing spheroidal particles of titanium hydride, dispersed in a-titanium, from other phases that may be present, such as p-titanium. This problem is common in examination of commercial unalloyed titanium.' In the course of an investigation of the Ti-H phase diagram, it was noted that titanium hydride, dispersed in a matrix of a-titanium, showed strong optical anisotropy when examined under polarized light. With sensitive tint illumination, particles of the hydride, when the stage is rotated, changed from bright yellow to bright blue in color. Since P-titanium is cubic, it showed no color change on rotation, remaining dark gray or blue-gray. Although a-titanium is hexagonal, it showed only a minor color change, going from pale pinkish-blue to pale purplish-blue. These colors could be modified somewhat by adjustment of the illumination. They were observed in specimens mechanically polished, both without etching and after etching with hydrofluoric acid-nitric acid mixtures in either water or glycerine. The strong color change of the hydride seems to offer a simple method for its metallographic identification. Optical anisotropy of titanium hydride is inconsistent with its accepted face-centered-cubic structure.' Samples of iodide titanium containing 6 to 40 atomic pct deuterium were prepared for diffraction studies. After deuterating and slow cooling' the samples were held 21 % hr at 400 °C, water quenched, held 61 hr at 100°C and quenched, then held 64% hr at 255 C and quenched. Debye ex-posures with MoKa X-rays and 1.111A neutrons were made at room temperature of samples as-deuterated and after the 100" and 255°C treatments. Table I shows the lines observed, in addition to those attributable to a-titanium. These data show that the hydride phase was not cubic, but probably tetragonal. The titanium atoms appeared to form a body-centered-tetragonal lattice complex, two titanium atoms per cell, with approximate dimensions: a = 3.12A, c = 4.18A, and c/a =1.34A. This is equivalent to a face-centered-tetragonal complex, four titanium atoms per cell, with approximate dimensions: a = 4.42A, c = 4.18A, and c/a - 0.946A. The presence of the 2.98 and 1.81A neutron lines indicates that the true Bravais lattice is not identical with this lattice complex, but may be primitive tetragonal with dimensions some multiple of those of the complex. The relative intensities of the hydride and a-titanium X-ray lines as functions of overall composition indicated that the hydride, presumably in equilibrium with the a at 100" to 255"C, contained more than 62 atomic pct H. Acknowledgments The experimental work covered in this report was done at Brookhaven National Laboratory, through the courtesy of D. Gurinsky. The cooperation of J. Sadofsky, 0. Kammerer, A. McReynolds, and A. Cendrowski is gratefully acknowledged.

Jan 1, 1957

By C. E. Berner

Since 1933, the Coal Mine Rating Schedule in Pennsylvania has provided credits in the Workmen's Compensation insurance premium rates for the use of safety hats, goggles and shoes. In that year, the worth of such protective clothing had just been well established and satisfactory articles were being made by a number of manufacturers. Standards for these three items of safety clothing' were written in the Rating Schedule and have been little changed through the years. The credit in the premium rate for a bituminous mine is $0.14 for hats, $o.08 for goggles, $o.08 for shoes. In order to earn such credit, it is necessary that all the employees in the particular mine be equipped with safety hats, goggles or shoes, as the case may be. In fact, it is not unusual for mines to qualify in all three categories, thus earning a rate reduction of $o.30 per $100 of payroll. These credits have been a decided stimulus to the use of safety clothing, and at present insured bituminous mines are credited as follows: Hats........ 63 per cent, or 22,600 employees Goggles..... 28 per cent, or 10,000 employees Shoes....... 44 per cent, or 15,800 employees Of course, many other employees wear these protective articles but they are in mines that are not fully equipped and so are not given the rate credit. The growth in use of this equipment has not been spectacular but it has been steady, as shown in Table I. An interesting thing about this is that it covers virtually all of the small and medium-sized bitumi- nous mine operations in Pennsylvania. A number of large operations are included, but many large mines are self-insured. It is difficult to keep alive interest in safety work in the smaller mines: first, because employment of safety engineers is out of the question and the one or several mine officials employed are often concerned only with production; second, because the life of many small mines is brief, so that safe conditions although established do not last long. Conditions as to safety in mines of this class rest chiefly with inspectors of state mine departments and of casualty insurance companies. Many millions of tons of production come from these mines, so that

Jan 1, 1944

By C. E. Berner

Since 1933, the Coal Mine Rating Schedule in Pennsylvania has provided credits in the Workmen's Compensation insurance premium rates for the use of safety hats, goggles and shoes. In that year, the worth of such protective clothing had just been well established and satisfactory articles were being made by a number of manufacturers. Standards for these three items of safety clothing' were written in the Rating Schedule and have been little changed through the years. The credit in the premium rate for a bituminous mine is $0.14 for hats, $o.08 for goggles, $o.08 for shoes. In order to earn such credit, it is necessary that all the employees in the particular mine be equipped with safety hats, goggles or shoes, as the case may be. In fact, it is not unusual for mines to qualify in all three categories, thus earning a rate reduction of $o.30 per $100 of payroll. These credits have been a decided stimulus to the use of safety clothing, and at present insured bituminous mines are credited as follows: Hats........ 63 per cent, or 22,600 employees Goggles..... 28 per cent, or 10,000 employees Shoes....... 44 per cent, or 15,800 employees Of course, many other employees wear these protective articles but they are in mines that are not fully equipped and so are not given the rate credit. The growth in use of this equipment has not been spectacular but it has been steady, as shown in Table I. An interesting thing about this is that it covers virtually all of the small and medium-sized bitumi- nous mine operations in Pennsylvania. A number of large operations are included, but many large mines are self-insured. It is difficult to keep alive interest in safety work in the smaller mines: first, because employment of safety engineers is out of the question and the one or several mine officials employed are often concerned only with production; second, because the life of many small mines is brief, so that safe conditions although established do not last long. Conditions as to safety in mines of this class rest chiefly with inspectors of state mine departments and of casualty insurance companies. Many millions of tons of production come from these mines, so that

Jan 1, 1944

By A. R. Krause, C. Laird

In order to establish whether or not there is a real temperature effect in fatigue (independent of environment) , poly crystalline copper and Cu- 7.9 A1 alloy have been cycled at 298° and 7° K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen. The lives of both copper and the alloy were found to be highly temperature-dependent in the absence of environment. This result casts serious doubt on the validity of the cell structure hypothesis for stage I crack propagation as presently formulated, because it predicts that there should be no such tempevnture dependence. On the other hand, the plastic blunling process is consistent with the result. Effects of environment aside, the homogenization of slip which accompanies testing at low temperature, and at low strains, seems to be the main cause for increased fatigue life. At high strain amplitudes, the fatigue lives of wavy slip materials, typically copper, are independent of temperature.' It is well-known, however, that low-strain lives greatly as as the temperature of testing is decreased. By contrast, the lives of planar slip materials, such as Cu-7.9 pct A1 alloy, increase to an even greater extent with decreasing temperature throughout both the high and low strain ranges.1'2'5 The mechanism of this temperature effect is associated with the earliest stages of fatigue failure,'" crack nucleation, and stage I growth,"' which is slow propagation along slip bands to the depth of a few grain diameters. Such life behavior has been interpreted on at least two different bases. On the one hand, those interested in the temperature effect at high strain amplitudes1 believe that stage I growth occurs by the plastic blunting process of crack propagation.7'9 They explain the effect in planar slip materials by the homogenization of slip* which accompanies fatigue testing at low temper- atures and serves both to delay crack nucleation and to decrease the rate of stage I propagation. On the other hand, Holt and Backofen,2 who have studied the effect in low strain fatigue, believe that stage I growth can be interpreted by a cell structure hypothesis.10-12 They have challenged2 the conclusion that there is a real temperature effect in this regime of fatigue testing and have interpreted the increased fatigue lives almost entirely in terms of the "environmental-protective'' effect of the liquid nitrogen and helium baths used to obtain low temperatures. This interpretation by Holt and Backofen2 may offer a means of discriminating between these two mechanisms as currently formulated and used to explain stage I growth. On the basis of the plastic blunting process applied to stage I crack propagation,7* the low strain fatigue lives of both wavy and planar slip materials should be increased with decreasing temperature. This follows because both materials show increased slip homogenization in this strain regime."13 Consequently, crack nucleation in intensified bands will be delayed and the linking of such small cracks into larger stage I cracks will be difficult. In addition, the blunting process required to lengthen a stage I crack from the order of 2 to 10 (where the strain concentration of the crack begins to overcome the slip homogenization property of the material) will also be retarded. These delays will give rise to longer lives in both kinds of material. In contrast to the blunting hypothesis, no temperature dependence has been predicted on the basis of the cell structure hypothesis, because it is well-known that materials cycled at low temperature show no differences in type of dislocation structure for a given strain amplitude.18"20 If the lives of wavy and planar slip materials do show a temperature dependence when the environment is eliminated as a variable, then it is questionable whether cell structures per se have a fundamental role in fatigue fracture. Accordingly, specimens of copper and Cu-7.9 wt pct A1 have been cycled at 298° and 77°K in vacuo and the fatigue lives compared with those in air and in liquid nitrogen, in order to establish whether or not there is a real temperature effect in low strain fatigue. Since it is difficult to measure the strains in specimens when cycled in vacuo, S-N curves have been used as the basis of comparison. In studying the influence of temperature on fatigue life in ordinary environment, Holt and Backofen2 used the superior basis of E-N curves. However, they also published S-N curves and thus established the relationship between E-N and S-N curves. This relationship is used to support the S-N comparison reported in the present investigation. EXPERIMENTAL Materials. The copper employed in this investigation was of 99.99 pct purity and the cu-7.9 pct A1 was prepared from metals of the same purity. The stock, of 3 in. initial diam, was reduced in size by rolling

Jan 1, 1969

By E. Northcott, I. M. LeBaron

Before describing the electrostatic processing of feldspar, it might be well to review some of the basic definitions and terminology of feldspars. The feldspar minerals constitute a group of alumino-silicates of potassium, sodium, and calcium. Barium feldspar sometimes occurs naturally but is very rare. Hardness varies between 6 and 6.5 and specific gravity between 2.5 and 2.8. Color is generally white or pale shades of red, yellow, or green. The approximate chemical composition of the principal feldspars is given in Table I. The albite (sodium aluminum silicate) and an orthite (calcium aluminum silicate) feldspars are the end members of a series called plagioclase. These two molecules form a complete solid solution series ranging from pure soda feldspar at one end to the pure lime feldspar at the other end. Intermediate solid solutions are known as oligoclase, andesine, labradorite, and bytoconite. The general structure throughout this series is the same. Sodium and calcium may replace each other and silicon and aluminum may replace each other in the structure.

Jan 10, 1958

By G. Y. Chin, A. R. Von Neida

The relationship between crystalline texture and magnetic anisotropy in a Co-10 pct Fe alloy has been investigated by means of X-ray pole .figures, hysteresis-loop tracings, and magnetic-torque measurements. The cold-rolled texture of a sample after 95 pct thickness reduction is of the "brass-type", that is, (110)[112/. At 500°C the cold-rolled material recrystallizes fo a (311)[112] orientation, plus a minor (210) [001] component. This texture persists up to 1400°C, at which point it is replaced by a secondary recrystallization texture, (111)[112]. Magnetic-torque measurements show that the easy axis of magnetization lies along the transverse direction in the cold-rolled material and changes to the rolling direction after primary recrystallization. This change is also reflected in the hysteresis characteristic; whereas the B-H loop along the rolling direction is nonsqunre with a low value of residual induction (750 vs 19,000 gauss at saturation) for the cold-rolled material, the annealed sample exhibits a very square loop with a large value of residual induction (16,000 gauss). Theoretical torque curves calculated from the texture data on the basis of magnetocystalline anisotropy energy compare favorably with the observed torque curves. Values of the crystal anisotropy constant, K1, obbained from these comparisons are in good quantitative agreement with single-crystal data. Furthermore, both the torque amplitude of the poly crystalline material and the magnitude of K1 obtained with a single crystal show an identical temperature dependence over the range from —195° 10 +220°C. It is thus conclzided that the magnetocrystalline anisotrpopy erlergy is chiefly I-esponsible. for the nzagnetic allisotropy of textured Co-10 pct Fe alloy. THE results of a study on the relationship between crystalline texture and magnetic anisotropy of an alloy containing 90 pct Co and 10 pct Fe by weight are reported in this paper. The alloy has an fcc structure: a saturation magnetization of about 19,000 gauss,2 and a nearly zero value of magnetoatriction.3 puzey4 has reported a large crystalline anisotropy constant of -7.4 X 105 ergs per cu cm, indicating the (111) directions as the easy axes of magnetization. Hence, texture variations resulting from cold work and annealing are expected to introduce a magnetic anisotropy in the polycrystalline material through the alignment of these (111) easy directions. In the present study, magnetic anisotropy of both rolled and annealed strips was determined by magnetic-torque measurements and hysteresis-loop tracings The results were correlated quantitatively with calculations based on texture data obtained by the X-ray pole-figure technique. It is established that the magnetocrystalline anisotropy energy is indeed chiefly responsible for the magnetic anisotropy of textured Co-10 pct Fe alloy. EXPERIMENTAL Material Preparation. The alloy nominally contained 90 pct Co, 9.5 pct Fe, and 0.5 pct Mn by weight, the chief impurities being nickel, carbon, and silicon (less than 0.5 pct total). The cast ingot was rolled to strips 10 mils thick and slit to 1 in. in width. After strand annealing at 900°C in a hydrogen atmosphere, these strips were further cold-rolled to various thicknesses down to 0.25 mil (97.5 pct reduction), with samples collected for study of the development of texture and magnetic anisotropy as a function of thickness reduction. subsequently, samples cold-rolled from 100 mils to 0.25 mil were obtained, thus extending the thickness reduction range to 99.75 pct. In addition, 0.5-mil samples cold-rolled from 10 mils were selected

Jan 1, 1965

By W. M. Wojcik, R. F. Kowal

Oxygen and sulfur distributions in commercial, 5-ton ingots of killed, medium carbon steel are described. Oxygen distribution is found to vary with deoxidation practice. Irregular distribution of oxygen within ingots makes necessary special precautions in sampling of rolled products for analysis of oxygen. Oxygen distribution is discussed in terms of recently published solidification concepts which had been successfully applied to simpler cases of segregation. These concepts have been found inadequate to explain observed oxygen distributions. Convective movements of the liquid metal, as determined by tracer elements, are shown to be capable of accounting for the observed distributions of oxygen. IN an effort to explore the origin of surface and subsurface imperfections in pierced steel products, a study of oxygen and sulfur segregation was made on ingots cast in open-top and hot-top molds. The results of our previous investigations1"3 have indicated the importance of the location and amount of oxide inclusions in an ingot. Inclusions close to the surface of the ingot have been found to contribute greatly to the formation of imperfections in the surface of finished products. This study of the effects of deoxidation and casting practice on segregation and the resulting oxygen distribution in ingots was initiated to determine the parameters controlling the location of inclusions in an ingot. Segregation of solute elements during solidification of low-melting binary alloys has been studied in the past.1, 5 Formation and growth of inclusions in iron melts have been studied under specific conditions."- In spite of these and other recent studies,10-12 segregation during solidification of commercial, killed steel ingots is not well understood. Consideration of solidification rates, of segregation during solidification of the chill, dendritic, and central zones, and of material balances for the segregated elements has indicated that a simplified theoretical solidification model is not adequate. However, the observed high oxygen contents in localized volumes of the dendritic zone can be rationalized if additional effects of convection currents in the ingots, precipitation, and rapid growth of new phases are considered. EXPERIMENTAL PROCEDURE Steelmaking and Processing. A group of nine killed. medium carbon steel heats having compositions listed in Table I have been studied. The deoxidation and mold practices used were varied to give a wide range of steel oxygen contents. The amounts of aluminum added to the ladle and the ingot casting practices (hot top and open top) were the main variables. The steel was made by a duplex practice in 160-ton tilting basic open-hearth furnaces. All nine heats were top-cast into 24 by 24 in. big end down, fluted molds, to a height between 60 and 76 in., using both open tops and exothermic hot tops. The deoxidation practice and the tapping and teeming details for each heat and ingot studied are given in Tables II and III, respectively. Hot-top practice is indicated by the letter H following the heat designation. Furnace and ladle temperatures were measured by standard disposable-tip, Pt/10 pet PtRh thermocouples. Teeming-stream temperatures were obtained as described by Samways et al.,13 by immersing a Pt/10 pet PtRh thermocouple, covered by a silica sheath, into the teeming stream under the nozzle. The output of this thermocouple was recorded with Leeds & Northrup Speedomax potentiometer. Calibration of the latter thermocouples was based on the freezing point of a pure iron/oxygen alloy (2795°F). The accumulated errors of measurements were within ±10°F. The thermocouple measurements were supplemented in this investigation by continuous recording of a ratioing, two-color pyrometer (Shawmeter), protected from smoke by a blast of clean air within the sighting tube, and calibrated to read with better than ±10°F accuracy. Following teeming of three heats, P, R, and T, tracer elements were added to the steel in the molds to obtain a record of the progress of solidification. As soon as the teeming stream was shut off, a 0.010-in.-thick steel can containing a mixture of crushed standard ferro-titanium and ferro-vanadium (0.05 pet of each alloy element) was plunged into the middle of the steel pool to a depth of 6 in. In about 30 sec no indication of the can or its contents remained. The surface of the open-top ingots solidified in 20 to 30 sec. A study of liquid metal movement and the precipitation of oxides was facilitated materially by use of the tracer technique as titanium has a low distribution coefficient between solid and liquid steel while vanadium has a high distribution coefficient.

Jan 1, 1965

Jan 1, 1963