The official Institute reports for the year 1929 were distributed in pamphlet form at the Annual Meeting, February, 1930, and were later included in Section 2 of Mining and Metallurgy, June, 1930, and thus made available to the entire membership. Membership In its report the Admissions Committee set forth the changes in membership during 1929, as follows: Total membership, Jan. 1, 1928, 8582; elected and placed on rolls in 1929, including 59 reinstatements, 509; loss by resignations in 1929, 88; loss by death in 1929, 110; loss by suspension in 1929, 37; membership at end of year not including Student Associates, 8856. Distribution of membership: Honorary Members, 16; Members, 6590; Junior Members, 38; Associates, 1041; Junior Associates, 1033; Rocky Mountain, 138; total membership, Jan. 1, 1930, 8856; Student Associates, 150; total including student associates, 9006. Treasurer's Annual Report, Year of 1929 Statement of Receipts For the year ended December 31, 1929 Dues: Arrears............................................ $ 3,501.75 Current............................................ 97,257.12 New Members...................................... 5,721.50 Advance........................................... 1,970.79 $108,451.16 Initiation Fees.................................................. 7,436.00 Magazine Receipts: Advertising Gross Receipts........................... $40,610.81 Magazine Sales..................................... 3,799.84 44,410.65 Sale of Transactions Current........................... $ 2,985. 15 Sale of Special Editions Current........................ 5,147.82 Sale of Back Transactions and Special Editions........... 4,186.93 Sale of Year Book..................................... 65.50 Sale of Authors' Reprints.............................. 2,585.40 Sale of Pins and Fobs.................................. 14.73 Sale of Technical Publications.......................... 1,451.55 Sale of Bindings...................................... 3,949.13 20,376.21 Net Interest Received: On Bank Balance and Temporary Investments......... $ 2,595.04 On Lie Membership Fund........................... 3,223.43 On James Douglas Library Fund...................... 5,425.61 On General Reserve Fund............................ 2,015.58 13,259.66 Miscellaneous Receipts........................................... 335.80 Total Receipts................................................ $194,269.48

Jan 1, 1930

By Lawrence Adler

MINE hoist ropes have hitherto been selected by successive approximation, a process both tedious and inexact. The proposed expression is a readily solved synthesis of existing data and the following standard equation:1 [ ] For convenience, a glossary of all terms appears on page 564. Since rope weight (Wr) and bending load (B) are functions of unit rope weight (Wo), which in turn is a function of rope strength (T), W, and B can be expressed in terms of T. Wr as a Function of T: A study of the curve in Fig. 1, unit rope weight vs strength, yields Eq. 2:

Jan 5, 1957

University of Alabama University, Alabama Mining and Metallurgical Society WILLIAM R. HIGGS, President ROBERT E. MEAD, Secretary J. R. CUDWORTH, Faculty Sponsor MILTON H. FIBS, Counselor University of Arizona Tucson, Arizona Miners' Society LEE BLESSING, President R. W. CORY, Secretary E. P. MATHEWSON, Faculty Sponsor B. R. HATCHER, Counselor University of California at Los Angeles Los Angeles, California Student Chapter, A.I.M.E. ARCHER WARNE, President ROBERT JOHNSTON, Secretary E. K. SOPER, Faculty Sponsor EMILE HUGUENIN, Counselor Colorado School of Mines Golden, Colorado Student Chapter, A.I.M.E. J. Ross REED, President ANDREW PERRY, JR., Secretary J. BURNS READ, Faculty Sponsor A. W. NEWBERRY, Counselor

Jan 1, 1936

By P. S. Bagga, P. T. Luckie

Liberation (the process of destroying the interlock between unwanted materials, such as mineral matter and pyrite, and coal) is one of the most important precursors to the benefication of raw coal in order to produce high grade marketable coals at economical recovery levels. Liberation is achieved usually by comminuting the raw coal. However, because of the significant interaction between the production of fine particles to achieve liberation and the cost of separating fine particles, the coal industry needs a method projecting the change in washability with size reduction. Such a projection can be combined with size reduction and separation simulators in order to examine completely beneficiation circuitry to produce coals of stringent specification. This paper presents the development of an appropriate liberation model for coal and its solution by Monte Carlo simulation to predict the expected washability of the raw coal as a function of comminution. It includes model validation with a known binary mixture as well as with a known teritary mixture.

Jan 1, 1983

The official Institute reports for the year 1929 were distributed in pamphlet form at the Annual Meeting, February, 1930, and were later included in Section 2 of Mining and Metallurgy, June, 1930, and thus made available to the entire membership. Membership In its report the Admissions Committee set forth the changes in membership during 1929, as follows: Total membership, Jan. 1, 1928, 8582; elected and placed on rolls in 1929, including 59 reinstatements, 509; loss by resignations in 1929, 88; loss by death in 1929, 110; loss by suspension in 1929, 37; membership at end of year not including Student Associates, 8856. Distribution of membership: Honorary Members, 16; Members, 6590; Junior Members, 38; Associates, 1041; Junior Associates, 1033; Rocky Mountain, 138; total membership, Jan. 1, 1930, 8856; Student Associates, 150; total including student associates, 9006. Treasurer's Annual Report, Year of 1929 Statement of Receipts For the year ended December 31, 1929 Dues: Arrears............................................ $ 3,501.75 Current............................................ 97,257.12 New Members...................................... 5,721.50 Advance........................................... 1,970.79 $108,451.16 Initiation Fees.................................................. 7,436.00 Magazine Receipts: Advertising Gross Receipts........................... $40,610.81 Magazine Sales..................................... 3,799.84 44,410.65 Sale of Transactions Current........................... $ 2,985. 15 Sale of Special Editions Current........................ 5,147.82 Sale of Back Transactions and Special Editions........... 4,186.93 Sale of Year Book..................................... 65.50 Sale of Authors' Reprints.............................. 2,585.40 Sale of Pins and Fobs.................................. 14.73 Sale of Technical Publications.......................... 1,451.55 Sale of Bindings...................................... 3,949.13 20,376.21 Net Interest Received: On Bank Balance and Temporary Investments......... $ 2,595.04 On Lie Membership Fund........................... 3,223.43 On James Douglas Library Fund...................... 5,425.61 On General Reserve Fund............................ 2,015.58 13,259.66 Miscellaneous Receipts........................................... 335.80 Total Receipts................................................ $194,269.48

Jan 1, 1930

The official Institute reports for the year 1929 were distributed in pamphlet form at the Annual Meeting, February, 1930, and were later included in Section 2 of Mining and Metallurgy, June, 1930, and thus made available to the entire membership. Membership In its report the Admissions Committee set forth the changes in membership during 1929, as follows: Total membership, Jan. 1, 1928, 8582; elected and placed on rolls in 1929, including 59 reinstatements, 509; loss by resignations in 1929, 88; loss by death in 1929, 110; loss by suspension in 1929, 37; membership at end of year not including Student Associates, 8856. Distribution of membership: Honorary Members, 16; Members, 6590; Junior Members, 38; Associates, 1041; Junior Associates, 1033; Rocky Mountain, 138; total membership, Jan. 1, 1930, 8856; Student Associates, 150; total including student associates, 9006. Treasurer's Annual Report, Year of 1929 Statement of Receipts For the year ended December 31, 1929 Dues: Arrears............................................ $ 3,501.75 Current............................................ 97,257.12 New Members...................................... 5,721.50 Advance........................................... 1,970.79 $108,451.16 Initiation Fees.................................................. 7,436.OO Magazine Receipts: Advertising Gross Receipts........................... $40,610.81 Magazine Sales..................................... 3,799.84 44,410.65 Sale of Transactions Current........................... $ 2,985. 15 Sale of Special Editions Current........................ 5,147.82 Sale of Back Transactions and Special Editions........... 4,186.93 Sale of Year Book..................................... 65.50 Sale of Authors' Reprints.............................. 2,585.40 Sale of Pins and Fobs.................................. 14.73 Sale of Technical Publications.......................... 1,451.55 Sale of Bindings...................................... 3,949.13 20,376.21 Net Interest Received: On Bank Balance and Temporary Investments......... $ 2,595.04 On Lie Membership Fund........................... 3,223.43 On James Douglas Library Fund...................... 5,425.61 On General Reserve Fund............................ 2,015.58 13,259.66 Miscellaneous Receipts........................................... 335.80 Total Receipts................................................ $194,269.48

Jan 1, 1930

Jan 1, 1967

By L. H. Schwartz, S. K. Lahiri, M. E. Fine, D. Chandra

WHILE the yield stress of solution treated Fe-Cu alloys increases rapidly with aging, a precipitate has only been directly observed in overaged samples.'-" This precipitate is essentially pure fcc copper, the E phase. Hornbogen2 suggested that the initial hardening is due to clustering of copper atoms in a bcc iron matrix. Hornbogen was not able to obtain direct confirmation for such bcc clusters by either X-ray diffraction or electron microscopy; however, he did observe analogous clustering in Fe-Au alloys7 where the scattering factor difference between iron and gold is more favorable than that for iron and copper. Fujii, Nemoto, Suto, and Monma4 recently observed diffuse electron diffraction scattering in a 2.5 pct Cu alloy aged at 500°C: for 30 hr. They suggested that part of the diffuse SCattering was due to a modulated structure of 26 to 42 wavelength parallel to the (110) matrix plane. This disappeared with further aging. However, 30 hr at 500°C is well beyond the peak strengthening in this alloy which occurred at less than I hr at 500oc.4 By transmission electron microscopy they could not distinguish between quenched samples and samples aged to maximum strength. The purpose of the present investigation was to try to obtain further confirming evidence for a precipitation stage preceding the formation of the fcc E phase. Change in Young's modulus was selected for study be- EXPERIMENTAL PROCEDURE The Fe-1.67 at. pct Cu alloy was supplied by the U.S. Steel Corporation in the form of a hot forged rectangular bar. The carbon and nitrogen contents of this alloy were 70 ppm and less than 10 ppm, respectively. The samples for Young's modulus measurements were made by cold swaging to & in. diam and cutting to 2 in. lengths. Tensile test samples 1 in. long were prepared by cold rolling to a thickness of 0.012 in. and then machining to gage dimensions of 0.5 by 0.012 in. For Mijssbauer studies, foils 1 mil thick were prepared by cold rolling. During fabrication the alloy was given intermediate anneals at 845OC followed by quenching. The specimens after preparation were solution treated at 1000°C (y field) or 845°C (a field) for 1 to 2 and 5 to 6 hr, respectively, in a dynamic vacuum of about 2 x lom6 torr. The tensile and modulus specimens were drop-quenched into iced brine through an aluminum foil which vacuum-sealed the bottom of the furnace tube. The MOssbauer foils were drop-quenched into helium gas cooled by passing through N2 (liq) in a copper coil. The grain diameter of the modulus and tensile specimens was between 0.025 and 0.035 mm. The samples were aged from 400" to 500°C in a dynamic vacuum of 2 x 10-6 torr and cooled by pulling into a water-cooled portion of the vacuum system. The dynamic Young's modulus was measured at room temperature using electrostatic excitation and detection of longitudinal vibrations.' Neglecting any length change during the aging, (this is expected to be comparatively small), the fractional change of Young's modulus (?Et)/Eav, is equal to twice the fractional change of the resonant frequency (?ft)/fav . ?ft =ft —fo where fo and ft are the resonant frequencies of a specimen before aging and after aging to time t. The measured f's, approximately 51,000 cps, were corrected to 25°C for any variation in the ambient temperature. The tensile tests reported were carried out at room temperature in an Instron with a 1000 lb full scale load cell. The flow stress reported herein corresponds to a strain of 0.002. The Massbauer spectra were taken in a constant acceleration model AM-1 NSEC spectrometer. The

Jan 1, 1970

By A. Simkovich, R. W. Lindsay

The possibility of using sodium sulfide slags to remove copper from ferrous alloys has been investigated by Jordan1 and by Langenberg.2, 3 In these studies, such slags were determined to be capable of removing copper and sulfur from the melt. The present work represents additional effort to clarify the effects of temperature on copper removal. The experiments were performed in a 17-lb induction furnace. Graphite crucibles contained the melts and kept the baths saturated with carbon. Temperatures were measured with a calibrated optical pyrometer and were controlled by manipulation of power input to the furnace. Estimated accuracy of temperatures in this investigation is ± 10°C (18°F) for measurements prior to slag additions, and + 20°C (36°F) after slag formation. The procedure consisted of melting 800 g of electrolytic iron. During this step, powdered graphite covered the exposed iron surface. After a predetermined temperature was reached, copper shot was added. A sample of the molten alloy for chemical analysis was then aspirated into a silica sheath. Next, a slag-forming mixture of sodium sulfite and graphite was added instantaneously to the melt. The sodium sulfite amounted to one-tenth the charge weight of iron; sufficient graphite was added to combine with oxygen in the sodium sulfite, assuming formation of carbon monoxide and reduction of the sulfite to sulfide. Subsequent to the slag addition, the molten alloy was sampled periodically, with the exception of heat A in which no intervening samples were taken between the slag addition and the end of the run. The iron was poured into a graphite mold, and the ingots sectioned and drilled for samples. Results of selected heats are presented in Table I. Analyses of samples drawn from the iron prior to slag addition are listed under zero time. Two samples from heat D were reported with copper contents greater than the initial concentration in the bath. Owing to the gradual but complete disappearance of slag during this heat, it is believed copper momentarily became more concentrated in the upper portion of the bath while reverting from the slag. This is the region from which samples were drawn. It should be noted that analysis of the ingot was equal to the copper content at the time of slag addition. The terminal temperatures of heats D and E, and the initial sulfur content of heat A are also to be noted. Because of the large temperature drop which occurred when slag was formed in heat D, power input to the furnace was increased in heat E after the slag addition, causing a higher terminal temperature. In heat A, the initial sulfur concentration was relatively high as compared to heats B through E owing to contamination by some slag remaining in the crucible from a previous heat. It is evident from Table I that copper was removed at the onset of slag formation. Roughly 30 pct of the copper was taken into the slag, with the exception of heat D, which had approximately 50 pct removed. For a comparatively short time of slag-metal contact, it appears that no gain is to be made in copper removal through use of high or low temperatures. If the slag initially formed remains in contact with the iron for an extended period, temperature has a marked effect upon copper removal, as can be seen by studying results for the two extremes in temperature. At about 1425°C, the copper level remained relatively constant after the initial removal by the slag. However, in the region of 1670°C, a definite reversion of copper occurred. Reversion was incomplete in heat D, and complete in heat E. The final temperatures of heats D and E differed by about 75°C. This temperature difference is thought to be the reason for only partial copper reversion in heat D. It is believed the effects of temperature noted above are related to the evolution of a white fume, which appeared in every run except heat A. (In the case of heat A, the fume was practically indiscernible.) After each slag addition, a yellow flame formed for about 5 sec. When the flame subsided, a white fume appeared. Upon contact with surrounding cooler surfaces, this fume deposited as a white solid. In the experiments made at 1425°C, evolution of fume continued unchanged to the end of the runs. However, heats D and E exhibited a different behavior. A very noticeable decrease in fume evolution from heat D was observed. Furthermore, this heat had much less slag remaining than did runs A through C when the experiments were terminated. No slag remained at the end of heat E; evolution of fume from this heat ceased prior to pouring. Spec-trographic analysis of the white deposit indicated sodium to be the major metallic element, with the maximum concentration of iron and copper as 0.1 and 0.01 pct, respectively. It is supposed the white fume observed in these experiments is principally sodium oxide (Na2O), formed by oxidation of sodium in the slag and subsequent sublimation. (Sodium oxide is a white to gray substance in the solid state; at 1275oC, it sublimes.4) According to this mechanism, elevated temperatures would accelerate removal of sodium from the slag, sulfur pickup by the

Jan 1, 1961

By John F. Lundeberg

CLAUSS1 observed that if isothermal creep data could be approximated as straight lines on a log stress-log time plot, a relationship existed that could be expressed as log t = m log s + b [ l] where t = time,

Jan 1, 1965

By R. F. Decker, J. R. Mihalisin

Phase transformations in a series of relatively pure nickel-titanium-aluminum binary and ternary alloys were studied. The purpose was to clarify age-hardening mechanisms, especially in predominantly titanium-hardened compositions. The micro-structures, as determined on a tirne-temperature-transformation basis by light and electron microscopy and X-ray diffraction, were correlated with room temperature and hot hardnesses. The stability of the ? phase under nonequilibrium conditions was shown to be important in this system. MANY of the alloys designed for service in the temperature range of 1200oF (649°C) to 1800°F (980°C) are austenitic iron-.nickel base alloys hardened by titanium and aluminum. The control of high-temperature properties of these alloys has been advanced by the knowledge of microstructures provided by the equilibrium diagrams of Taylor and Floyd1 and Taylor.2, 3 However, there have been notable instances in the predominantly titanium-hardened alloys where the correlation of properties with microstructure and the equilibrium diagrams has been unsuccessful. Mihalisin and carrol14 have noted in electron microscope studies of commercial alloys of this type that a fee phase precipitates and transforms to 71 (hep Ni3Ti) in stress-rupture tests. Bieber5 found that this fee phase remained in nickel-chromium-titanium alloys even when aluminum was excluded. Age hardening in iron-nickel base alloys has been attributed to 71 by Craver, Aggen, and Dyrkacz,6 ? (fee phase based on Ni3Al) by Beattie and Hagel7 and both phases by Lena,8 Yet, on the basis of the nickel-titanium-aluminum equilibrium diagram of Taylor and Floyd shown in Fig. 1, it has been difficult to understand the presence of ? in low aluminum alloys. Furthermore, the characteristic coarse dispersion of 71 has not been commensurate with the marked aging response. Also there have been anomalous grain boundary transformations in the iron-nickel base alloys which have markedly reduced notched stress rupture properties.9 These have been related to boron content and residual cold work. Recently, Golubtsova and Mashkovich,10 Buckle and Manene11 and Bogaryatskii and Tyapkin12 have noted a transition fee Ni3Ti in titanium-hardened nickel-base alloys. It was apparent from the latter studies that a transition phase was important in the nickel-titanium-aluminum system. The purpose of this study was to identify this phase, measure its transformation characteristics and kinetics, and attempt to correlate these findings with age hardening. It was believed that time-temperature-transformation studies, because of their adaptability to transition phases, would be of most value for this investigation. Accordingly, this method of study was undertaken on relatively pure nickel-titanium-aluminum alloys with controlled variations in boron content and residual cold work. EXPERIMENTAL PROCEDURES Compositions were selected from the nickel-titanium-aluminum isothermal section of Taylor and Floyd.' These compositions are plotted in Fig. 1 and were selected to obtain equal aging potential of approximately 15 pet by volume of the equilibrium precipitate. The materials were vacuum melted from

Jan 1, 1961

By G. E. Karantzavelos

A novel two-stage froth flotation process for the recovery of pure magnesite from low grade ores is described. The process consists of a first-stage, magnesite flotation step where a rougher magnesite concentrate is floated with amine collectors. The first-stage froth concentrate is then repulped in fresh water, and quartenary ammonium salt and fuel oil are added to float the remaining impurities. The results from laboratory batch tests show that a high-grade magnesite concentrate assaying 0.99-0.20% Si02 and 2.84-0.46%a Ca0 can be produced. Regulation of the variables controlling magnesite froth flotation also allows the variation of the ratio % Ca0: % SiO2, between the acceptable limits 0.32 to 5.79. This ratio is important to the quality of dead-burned magnesite.

Jan 1, 1985

By J. E. Stukel, J. Cocubinsky

A CONSIDERABLE amount of information is available on the equilibrium distribution of manganese between slag and metal under oxidizing conditions. These data have increased our knowledge of the manganese reactions in the open hearth, ladle, and ingot mold. In contrast, there is a paucity of data on the slag-metal distribution of manganese under reducing conditions. The purpose of the present investigation was to study the equilibrium distribution of manganese between blast-furnace type slags and iron saturated with carbon. Experimental Method Furnace: The induction furnace used for the experiments is shown in Fig. 1. A 1 in. pipe, attached to the transite cover, was fitted with a window through which the charge could be observed. Material could be introduced into the furnace through a tee and plug without removing the cover. A graph-it cylinder (3 in. ID and 10'/2 in. long), centered within the induction coil, was used as a heating element. During a test, a zircon plug kept the top of the furnace from becoming too hot from heat radiation. At the bottom, a graphite block on the vertical center line of the furnace and extending 1 1/2 in. into the coil, was used as a support for the graphite crucibles containing the melt. The graphite crucibles, machined from regular carbon electrode stock, had a 2% in. OD with 3/16 in. walls and were 5% in. long. The fumes present in the furnace during the early part of a run made optical readings uncertain. A noble metal thermocouple was, therefore, adopted to measure the temperatures. The arrangement used, shown in Fig. 1, allowed the silmanite protection tube to be replaced with a minimum effort. The thermocouple was calibrated against a standard Pt-Pt-Rh thermocouple in a fused quartz protection tube. The latter was inserted in the molten iron by removing the glass window on the cover. The lower couple was found to be very sensitive to temperature changes. To insure accurate temperature readings, the graphite crucibles were made to fit tightly against the silmanite protection tube. Further, to avoid contamination of the thermocouple by carbon, the silmanite tube was changed and the calibration procedure was repeated at frequent intervals. By using this temperature measuring technique, the furnace was easily held within *1O°C of the desired temperature. Because of the small free space in the furnace, no attempt was made to control the atmosphere. It

Jan 1, 1955

Discussion of "The Ordering Transformation in Titanium-Aluminum Alloys Containing up to 25 at. pct Aluminum" by F. A. Crossley, Trans, TMS-AIME, 1968, vol. 242, pp. 726-30. Dr. Blackburn, in his response, pointed out that the c/a ratio of the Ti-26 at. pct A1 alloy quenched from 900°C is 1.6006 and not 1.5965 as plotted in Fig. 19. An error in transcription was made in preparing Table V of Ref. 1 (F. A. Crossley, Trans. TMS-AIME, 1966, vol. 236, p. 1174). The corrected Fig. 19 strengthens rather than weakens the argument that a martensitic transformation occurs in alloys containing from 15 to 18 at. pct Al. A Study of the Factors Which Influence the Rate Minimum Phenomenon During Magnetite Reduction, by P. K. Strangway and H. U. Ross, Trans. TMS-AIME, 1968, vol. 242, pp. 1981-88. Page 1883 Reverse Figs. 5 and 6. Sigma—Its Occurrence, Effect, and Control in Nickel-Base Superalloys, by J. R. Mihalisin, C. G. Bieber, and R. T. Grant, Trans. TMS-AIME, 1968, vol. 242, pp. 2399-2414. Pages 2403, 2407, and 2414 Arrows should appear on Figs. 4 and 9; a sigma is missing from Table IV; line 2, page 2414, change "case" to "cast". These are published correctly in the bound volume. Index, December Issue There were a few omissions in the Author Index. These have been corrected and published properly in the bound volume.

Jan 1, 1970

By L. D. Lamont, W. C. Muehlhof

Throughout the anthracite industry's history, the problem of handling and disposing of refuse material has been one of major importance. In the early days of the industry's activities, only the large sizes of anthracite were satisfactory for market requirements and the smaller sizes were deposited as refuse. As time went by, more efficient coal-burning equipment was developed and a market demand was created for the finer sizes of coal. This demand made it possible to recover marketable coal from banks deposited as refuse in the earlier days of mining. The same condition holds good today and we can see a definite trend toward the objective of utilizing the No. 4 and No. 5 buckwheat sizes. Under present conditions, we know that a limited market exists for No. 4 and 5 buckwheat; we know that the finer sizes of anthracite can be burned as pulverized fuel; we know that these fine sizes can be processed and sold as briquettes, and we also know that the heat content of these fine sizes of coal is comparable with that of the sizes now merchandized. Therefore, it should be the objective of the industry to conserve these fine sizes of coal in such manner that if and when processing facilities are developed, and market demands exist, the material can be salvaged and made available to meet these demands. From the standpoint of economical future reclamation, the ideal method of disposing of refuse containing the finer sizes of coal is to deposit it in banks separate and apart from other breaker refuse. By this procedure, the minimum amount of material will be processed in future salvage operations to recover the No. 4 and No. 5 buckwheat sizes. Many collieries in the anthracite region are operated under leases that have a specific term. These lease agreements provide that, upon expiration of the lease by term, exhaustion or otherwise, the ownership of the refuse material reverts to the lessor. Therefore, a question was raised in the minds of these operators: Why should I assume the expense of such procedure when I have no assurance that I will benefit by the future processing and sale of these fine sizes? Under present conditions, the answer to this question is not one of choice but of necessity, as restrictions imposed by legislation make it mandatory on operators of preparation plants to take necessary steps to properly treat silt-laden waters before permitting them to enter the streams. By reason of these restrictions, the disposal of fine sizes becomes a secondary rather than a primary operating consideration, and the procedure for disposing of this refuse becomes a matter of choice governed principally by topographical and geographical conditions. Methods of Handling Refuse There are three principal methods of handling and disposing of fine-size refuse; namely:

Jan 1, 1947

By W. C. Muehlhof, L. D. Lamont

Throughout the anthracite industry's history, the problem of handling and disposing of refuse material has been one of major importance. In the early days of the industry's activities, only the large sizes of anthracite were satisfactory for market requirements and the smaller sizes were deposited as refuse. As time went by, more efficient coal-burning equipment was developed and a market demand was created for the finer sizes of coal. This demand made it possible to recover marketable coal from banks deposited as refuse in the earlier days of mining. The same condition holds good today and we can see a definite trend toward the objective of utilizing the No. 4 and No. 5 buckwheat sizes. Under present conditions, we know that a limited market exists for No. 4 and 5 buckwheat; we know that the finer sizes of anthracite can be burned as pulverized fuel; we know that these fine sizes can be processed and sold as briquettes, and we also know that the heat content of these fine sizes of coal is comparable with that of the sizes now merchandized. Therefore, it should be the objective of the industry to conserve these fine sizes of coal in such manner that if and when processing facilities are developed, and market demands exist, the material can be salvaged and made available to meet these demands. From the standpoint of economical future reclamation, the ideal method of disposing of refuse containing the finer sizes of coal is to deposit it in banks separate and apart from other breaker refuse. By this procedure, the minimum amount of material will be processed in future salvage operations to recover the No. 4 and No. 5 buckwheat sizes. Many collieries in the anthracite region are operated under leases that have a specific term. These lease agreements provide that, upon expiration of the lease by term, exhaustion or otherwise, the ownership of the refuse material reverts to the lessor. Therefore, a question was raised in the minds of these operators: Why should I assume the expense of such procedure when I have no assurance that I will benefit by the future processing and sale of these fine sizes? Under present conditions, the answer to this question is not one of choice but of necessity, as restrictions imposed by legislation make it mandatory on operators of preparation plants to take necessary steps to properly treat silt-laden waters before permitting them to enter the streams. By reason of these restrictions, the disposal of fine sizes becomes a secondary rather than a primary operating consideration, and the procedure for disposing of this refuse becomes a matter of choice governed principally by topographical and geographical conditions. Methods of Handling Refuse There are three principal methods of handling and disposing of fine-size refuse; namely:

Jan 1, 1947

By G. Sachs, A. W. Dana, C. C. Chow

A great number of the investigations on the plastic flow of metals have been concerned with the establishment of a "universal" stress-strain relation. In such a relation some stress function when plotted against a strain function should yield identical curves for the various stress states. In the first investigation of this type, Ludwik and Scheu1 plotted the maximum shearing stress as a function of the maximum principal strain. Later Ros and Eichinger2 introduced two universal stress-strain relations, the one relating the maximum shearing stress to the maximum shearing strain, and the other relating a stress invariant, suggested by von Mises and Haigh, to the corresponding strain invariant. (In more recent investigations the stress and strain invariants are frequently supplemented with some factor to render their meaning more lucid.) A further suggestion which has not attracted appreciable attention is that by Baranski³ who used stress and strain deviators. The most common means of experimentation to determine the relation between stress and strain consists in subjecting thin walled tubes to combined internal pressure and axial tension.4a,4b,4c This method allows the study of plastic flow under stresses which are variable in two directions. However, the plastic flow which can be obtained in this manner is comparatively small, being limited by either tension failure or instability. For copper,'. only the relation between maximum shearing stress and maximum shearing strain yielded good agreement. On the other hand, tests on a stee14b and on an aluminum alloy4c. resulted in systematic deviations if any of the discussed universal stress-strain relations were used. It would seem, therefore, that the agreement mentioned above for copper is only incidental and explained by its high rate of strain hardening compared to that of other metals. Much larger strains than experienced in the tube tests can be obtained by subjecting a thin membrane of a ductile metal, which is restrained at its periphery, to a uniform hydraulic pressure. The thin sheet forms a deep bulge before it fails. The stresses and strains in such a bulge increase with increasing distance from the edge of the clamping "die," the maximum stresses and strains occurring at the pole (crown) of the bulge. While the stress and strain states are determined by the contour of the bulge, the absolute magnitude of the stresses and strains depends upon the hydraulic pressure. The bulge contour is in turn correlated with the geometry of the die opening. The deformation and fracture characteristics of circular bulges, that is, bulges formed with circular clamping dies, have been the subject of numerous experimental and analytical investi-gations.5,6,7 It has been shown that plastically deformed circular bulges develop large and comparatively uniform strains before failure by instability"6b,6c,6d and closely assume a spherical shape.6d Also the distribution of strains across the contour of the bulge is dependent on the metal being investigated and is correlated with, but cannot be predicted from, the metal's stress-strain characteristics. On the other hand, oblong or elliptical bulges, that is, bulges formed with elliptical clamping dies, are not as susceptible to analytical analysis and have not been investigated to the extent that circular bulges have. The few available data6c,7c indicate that stress states are obtained at the poles of the bulges, varying between plane strain and balanced biaxial tension, depending upon the geometry of the die opening. In this paper, the strain state and curvatures exhibited by three bulge shapes, a circular and two elliptical bulges, Fig 1, are analyzed experimentally using methods described in previous publications.6a,6c An attempt is made to derive the stress-strain relations for these bulges, which represent strain states in which the ratio of the two positive principal strains varied between 1.0 and 0.35. In addition, tension tests yielded data for a value of —0.5 for this strain ratio. Such an analysis should indicate the applicability of the various laws correlating stress with strain to the stress and strain states occurring in bulged shapes. Definitions and Nomenclature The definitions of the major stress and strain quantities used in this paper are as follows: s1, s2, s3 = principal normal stresses Sl > s2 > S3 t = shear stress e = conventional (unit) strain e = In (1 + e) El, E2, E3 = principal natural strains 7 = shear strain The maximum shear stress: , _ S1 — S3 lmax = 2 Frequently, the flow stress, s1 — s3 = 2lmax rather than the maximum shear stress is used.

Jan 1, 1950

By T. A. Rickard

In " The Genesis of Certain Auriferous Lodes "* Dr. Don makes a reference to a curious vein-formation known as the "Indicator," which characterizes a portion of the Ballarat mining district,, in Victoria, Australia. During 1890 and again in 1898 I had an opportunity of making a few notes, which, although somewhat belated,t may be worth adding to the observations recorded in the Transactions of the Institute. The country of the Ballarat gold-field consists of the Lower Silurian slates and sandstones, which also enclose the reefs of Bendigo; but it is noteworthy that the successive anticlinal folds, and accompanying saddles of quartz, which distinguish Bendigo are not characteristic of Ballarat, the geological structure of which presents greater complexity. That part of the district known as Ballarat East became famous early in its history on account of the large nuggets which were found in the alluvium, and subsequently it became further known because of a peculiar persistent black seam, traversing the bed-rock underlying the alluvial deposits, which was found to be associated with rich bunches of gold-ore, not only in the gravel that capped it at the surface but also in the quartz-veins which crossed it underground. The name of " Indicator " was early given. In 1871 Mr. Morgan Llewellyn directed attention to it as influencing the distribution of the gold. In the government quarterly report for December, 1888,

Jan 1, 1901

By L. J. Erck, T. E. Ban

A discussion of laboratory procedures used to determine pellet quality and to simulate handling and firing conditions. Strength-temperature relationships in pelletizing; effect of chemical additives on agglomeration; and crushing, abrasion, and impact resistance of the pelletized products are discussed with respect to five different iron ore concentrates. IN most routine experimental work on products and processes, method:; of operation and product evaluation are established from accurately controlled laboratory tests. With particular emphasis on the pelletization of fine iron ore concentrates, standardized procedures of laboratory production and product testing have been established at Cleveland-Cliffs Iron Co. Research Laboratory at Ishpeming, Mich. A program of this nature was used for investigating the agglomeration characteristics of various iron ore concentrates. The factors which control the process were studied and subsequently controlled for these investigations. Pelletizing as applied to iron ore agglomeration involves the preparation of spheroidal masses from a fine moist concentrate, followed by high-tempera-ture firing to produce a final product. The preparation of moist spherorids is generally designated as balling. This produces the so-called green pellets or balls. After, these have been fired they are called pellets. Balling is accomplished by rolling moist concentrates in a revolving drum until small spheroids form by a snow-balling action. These balls are then heated in a shaft furnace, or a modification of this device, to a temperature high enough to cause agglomeration within the individual balls while they descend countercurrent to hot oxidizing gases. By this process the lour strength balls are converted through various chemical and physical-chemical processes into hard pellets. With correct balling and firing, the pellets are strong, resist abrasive action and handling treatments, and provide a suitable blast furnace and open hearth feed. In 1950 Tigerschiold and Ilmoni developed a working hypothesis to explain the formation and stability of green pellets.' Their work was presented on the basis of geologists' discoveries concerning the soil-water system and C. V. Firth's early postulates of green pellet formation.' Fundamental reactions oc-curing within fired pellets have been described by Cooke and Ban, who showed the microstructure changes caused by different firing temperatures." All these investigators have provided scientific clarifications of agglomeration by the pelletizing process and have opened avenues for greater development. Mineral grain growth and ceramic bond formation are the two basic phenomena imparting coherency to particles within a fired pellet of iron ore. Each of these is established by the transfer of thermal energy to the mineral particles. Grain growth mechanisms are chiefly physical reactions wherein smaller particles consolidate into larger ones, with resulting decrease in surface energy conforming with the second law of thermodynamics. Ceramic bond formation is a chemical reaction usually between basic and acid metallic oxides of the gangue and ore minerals. CaO, MgO, A1203, and FeO of Fe3O4, react in varying proportions with SiO, or Fe2O3, to form a great series of compounds or amorphous solid solutions. These product bond iron mineral particles together by a bridging action or by direct reaction with the surfaces of the particles. The result of the grain growth-ceramic bond formations is a consolidated, coherent compact of gangue and iron minerals formerly held together by much weaker bonds of interstitial water and forces common to dry, unconsolidated particles.4 With respect to iron ore agglomeration, these high temperature bonding reactions have been described by Schwartz, who referred to the bonds in sinters," and by Cooke and Ban, who referred to the bonds in fired pellets." The extent of the bonding phenomena and the consequent strength of fired pellets is governed by

Jan 1, 1954

By R. G. Davies, R. H. Richman

Several techniques, X-ray diffraction, transmission electron microscopy, conventional, metallography, and mechanical property measurements are combined to investigate decomposition in the suPersaturated solid solution Fe-27 at. pct Be. The following sequence of structures for aging temperatures below 400°C is established: massive short-range order, pseudo-FeBe (L2o) order, Fe3Be (DU3) order, sinusoidal modulation of composition, general or continuous precipitation, and discontinuous or cellular precipitation. In addition to this sequence itself, several features of the individual stages are noteworthy; for example, when coherent modulations occur, their development is parallel to (100) everywhere in the specimen apparently without incubation, and both the wavelength and the composition amplitude of the modulations increase with aging time. Two types of discontinuous reaction are observed, depending upon the aging temperature. At low temperatures (<550°C) the boundary-nucleated variety of discontinuous precipitate predominates; but at higher temperatures (>600°C) the crystallographic variety occurs instead. Hardness and flow-stress measurements clearly reflect the quoted structure sequence. Some qualitative aspects of the structure changes and of the relationship between mechanical properties and structure are discussed. BERYLLIUM in solid solution markedly strengthens iron.&apos;" A recent study demonstrated that not only were supersaturated single crystals of Fe-27 at. pct Be very strong, but they deformed primarily by mechanical twinning.3 Such behavior, coupled with the decrease in solid solubility of beryllium in a Fe from about 33 at. pct at 1165°C to about 10 at. pct at 500°C4 as shown in Fig. 1, leads naturally to questions about property changes with aging in this system. In 1929 roll,1 and later Seljesater and Rogers,5 reported that useful increases in strength could be obtained by aging quenched Fe-Be alloys, but it was not until quite recently that any of the details of precipitation in these alloys were studied. Richman6 observed that both an Fe3Be superlattice (with a DO3 crystal structure the same as Fe3A1, illustrated in Fig. 2) and a modulated structure preceded the appearance of a discrete second phase in the 20 at. pct Be composition. Here, a modulated structure refers to a periodic composition fluctuation within one crystal, while its lattice remains coherent. Subsequent work on a Fe-Be alloys by Heubner7 and von Heimendahl and Heubner8 confirmed the existence of the modulated structure, although only an FeBe (L20) ordered structure was detected (also shown in Fig. 2). Both Rich-man and Heubner corroborated the large increases in hardness during aging reported earlier, but other mechanical properties were not examined. Since modulated systems are encountered relatively infrequently, the influence of coherent modulation upon mechanical properties is not well-known. With the accumulation of information about age-hardening systems, it has become clear that many precipitation reactions cannot always be described by the concept of heterogeneous nucleation at some lattice discontinuity followed by diffusional growth. Rather, complex sequences involving prior "preparation" of the matrix are quite common; that is, a transition structure occurs in the parent phase, instead of in some "nucleus" form. Delineation of such subtle sequences appears to be a worthwhile step toward the understanding of solid-state precipitation. Since not many structural progressions of comparable nature have been reported, the objectives of the present survey are to identify and elucidate the various

Jan 1, 1967