By George S. Ansell, John B. Hudson, Stephen A. Koffler

The permeability of hydrogen through the a phase of palladium has been measured by a low pressure permeation technique under conditions such that bulk diffusion was the rate-controlling process. The observed permeability is described by the equation: J = 1.80 x 1O-3 P½exp(-3745)/RT) cc(stp)/sec/cm2/en over a range of hydrogen pressure, P, from 2.9 x 10-5 m Hg to 5.0 x 10-3 cm Hg, and over a temperature range, T, from 300" to 709°K. The fact that the permeability shows a square root dependence on pressure and a reciprocal dependence on thickness was taken as evidence that bulk diffusion, rather than surface reactions, was the rate-controlling process. The permeability data were used in conjunction with the solubility data of Salmon et al., to determine the diffusivity of hydrogen through palludium as: D = 4.94 x 10-3 exp(-5745/RT) cm2/sec There was no influence of sub structural defects observed over the temperature range employed. From the permeability data obtained, coupled with grain size measurements, it was concluded that the ratio of grain boundary diffusivity to bulk diffusivity was less than 105 over the range of temperature investigated. THE diffusive mass transport of hydrogen in the a phase of palladium has been studied previously by numerous investigators.' In spite of the large amount of attention this system has received, there is not good agreement between the results obtained in different investigations.' This is due in part to the fact that the mass transport was surface-limited during some of these studies, rather than being diffusion-controlled3-5 The reason for the disagreement in other cases is not clear. These studies made use of such techniques as rate of absorption from solutions6 and gases,' electrochemical potential,8 time lag,' and permeation10,11 to determine the mass transport behavior. Of these, the gas permeability technique is the only method which allows an easy test to determine if diffusion is the rate-controlling mechanism, thus eliminating the uncertainty regarding the limiting transport processes inherent in the other techniques. The two most recent permeability studies are those of Toda10 and Davis." Toda determined the permeability of hydrogen in the a phase of palladium over the temperature range from 170" to 290°C, and over the pressure range from 36 to 630 mm Hg utilizing a steady-state gas-permeability technique. Toda's result was: J = 1.41 x 10-3 P½ exp(-3220/RT) where J = specific permeability in cc(stp)/sec/cm2/cm, P½ = square root of the inlet pressure in (cm Hg)½, R = Universal gas constant, and T = temperature in deg Kelvin. Davis11 also employed a steady-state gas-permeability technique over the temperature range from 200" to 700°C and over the pressure range from 0.02 to 760 mm Hg. His result for the permeability of hydrogen in the a phase of palladium was: J = 3.15 x 10-3 P½ exp(-A440/RT) In the range of overlapping temperature for these two investigations, the values of the specific permeability calculated from the above two equations differ by a factor of about 1.8. In the present investigation, the permeation of hydrogen in the a phase of palladium was determined over a wide temperature range, 27" to 436oC, and over the pressure range from 2.9 x 10-5 to 5.0 x 10-3 cm Hg. This temperature range overlaps that of the previous investigations of Toda and Davis, but also covers the lower temperature range which has never before been investigated. The lower pressure range used here avoided the interaction between the dissolved hydrogen atoms observed at higher hydrogen concentrations.' MATERIALS The as-received palladium specimens were cold rolled from a casting and were supplied as 5.08 cm discs of 0.508 and 0.762 mm thickness. According to J. Bishop and Company specifications, the composition of the discs was 99.95 pct Pd, the balance being Cu, Ag, Au, and Ir. In order to obtain samples of varying grain size, the as-received discs were then heat treated. Sample 1 was treated for eight minutes in a nitrogen atmosphere at 810°C and then air-cooled. Sample D was heated first to 550°C in helium. The helium atmosphere was then immediately replaced by hydrogen and the temperature was slowly raised to 1220°C and held for 22 hr. The sample was then cooled to 550°C where the hydrogen was replaced by helium and the disc was further furnace-cooled to room temperature. Sample H was given the same heat treatment, only with hydrogen substituted for helium below 550°C. The reason that hydrogen was not used throughout the entire annealing cycle for samples D and H was to prevent the distortion encountered by low-temperature cycling in hydrogen observed by Darling." After these heat treatments were completed, the

Jan 1, 1970

By William C. Aitkenhead, John A. Jaekel

Uranium deposits in the Spokane Indian Reservation, as well as those around Mt. Spokane, are essentially low grade, much of the ore containing less than 0.2 pct U808. The Mining Experiment Station of the Division of Industrial Research, State College of Washington, has been engaged in intensive research on the amenability of these low grade ores to froth flotation. The results: successful flotation of autinite, chief mineral constituent. At the outset of this work the goal was a concentrate of 1 pct U308 with a 90 pct recovery from ores containing less than 0.2 pct U3O8. Most of the work has been done on argillite ore from the Midnight mine on the Spokane Indian Reservation. The goal has not been attained using this ore, but samples of the granite ore from Mt. Spokane yielded successful results. For example, a concentrate containing 11.2 pct U308 was produced from a Mt. Spokane high grade ore containing 1.27 pct U3O8 with a recovery of 97.8 pct. Another Mt. Spokane ore yielded a concentrate of 5.0 pct U3O8 from an ore containing 0.13 pct U3O8, with a recovery of 85 pct. This same ore gave a recovery of 93.5 pct when the grade of concentrate was reduced to 2.0 pct.

Jan 1, 1959

By T. L. Joseph

S. T. Killian (Johnstown, Pa.)—This is one of the finest papers I have read. Tying in stoichiometric calculations with furnace performance and practice is a step which had to be taken sooner or later. The noteworthy difference between Dr. Joseph's type of calculations and regular blast furnace calculations is that the Ib mol system is used as a basis. With the Ib mol system, weights, volumes, and chemical reactions can all be expressed in the same equation. In the paper, wind, ore, flux, and fuel are all expressed as lb or lb mols. Probably Dr. Joseph does not realize it, but the vague word coke appears only twice in the entire paper. Lb of C and Ib mols of C are followed through reactions but the word coke appears only as 1560 lb coke per ton of pig and 1700 lb of coke per ton of iron. Obviously in order to understand furnace reactions, the coke should be expressed as lb or lb mols of C. Furnaces can also be compared more easily. In some respects the paper is too thorough and too complete. The effects of the metalloids reduced into the iron upon the top gases represents a difference of less than 3 pct of the CO formed in the bosh. Due to the completeness of the calculations in relation to the CO/CO2 ratio, this was included and was necessary. However, the exclusion might have enabled more furnace men to follow the lb mol system of calculations through the blast furnace to a better degree. By considering only irons of similar analysis, this part of the calculations might have been omitted. However, if this had been done, total rewriting of the paper later would have been necessary in order to make the work complete as it is now. It also would not have been nearly as authoritative. In the paper, there appears the reaction: H2O + CO ? CO2 + H2 [I] Dr. Joseph states that he did not take this reaction into consideration in any calculations pertaining directly to the paper. The piobable reason- for this is that although it contains all the main reacting top gases except N2, it is rather inflexible since it is monomolecular in relation to each of the reacting gases and does not tie in with the gasification of C. Actually the reactions: H2O + C ? CO + H2 [2] 2H2O + C ? CO2 + H2 [31 and the solution loss reaction: CO2 + c ? 2c0 [41 tend to assume an equilibrium through the reaction: H2O + CO ? CO2 + H2 [I] which should be considered a balancing or equilibrium reaction. Reactions 2, 3 and 4 permit furnace conditions to balance with the CO/CO2 ratio and H2 formation. They tie in with the solution loss. Reaction 1 unites them chemically. Probably the best calculation to make at this time would be to try to find the relative importance of the CO2 from the flux and the H2 in the dilution on an actual furnace gas analysis. For this purpose the Dob-scha-Carnegie-Illinois paper—"Effect of Sized and Sintered Mesabi Iron Ores On Blast Furnace Performance" is chosen. This paper was presented before the blast furnace section of the AIME in 1948. This represents the best large scale furnace operation available to me. Unfortunately the changes were brought about by beneficiation of the burden and not by changes on one burden. In choosing the basis for the calculation in relation to the furnace, 100 mols of dry top sgas is chosen. This leaves something to be desired inasmuch as the nitrogen basis is changing but I believe it will be better understood than any other type and it is the easiest to use.

Jan 1, 1952

By E. A. Gulbransen, K. F. Andrew

In a recent communication14 we have reported on the kinetics of the reactions of zirconium with O2, N2 and H2 as a function of the time, temperature and pressure variables. A systematic study was made and the results correlated with fundamental theories of gas-metal reactions. This paper will present a similar study for titanium. Titanium and zirconium are members of the IV group of the periodic table and possess many similar physical and chemical properties as a result of their similar electronic configuration for the outer electrons. The two metals are relatively inert to both gas and liquid phase corrosion at room temperature. However, at moderate temperatures the metals become active and react readily with the common gases including O2, N2 and H2 which are of interest in this study. A study of the kinetics of these gas-metal reactions is of interest for three reasons: (1) to understand the rate of reaction of titanium and its role in the behavior of high temperature alloys; (2) to understand the practical difficulties of the reduction, refining and working of titanium; and (3) to correlate the data with fundamental theories of gas-metal reactions and crystal structure predictions. Literature Survey Several review papers8 and books4243 exist on the preparation and properties of titanium and its alloys. THE METAL Titanium has, at room temperature, a hexagonal lattice of the zinc type. Hagg19 gives a value of 2.953A for the (a) axis, a value of 4.729 for the (c) axis and a density of 4.427 at 20°C. Burgers and Jacobs6 have observed the transformation of the hexagonal to the body-centered cubic structure at 880°C and have established a value of 3.31 for the cube edge and a density of 4.31. TITANIUM-OXYGEN Carpenter and Reavell6 using a pressure change method have studied the reaction at temperatures of 742° and 1000°C and for a pressure of one-fifth of an atmosphere. The probabilities for reaction are calculated from kinetic theory and they report a value of 10-5 for O2 at 1000°C and 10-6 at 740°C. The titanium-oxygen system has been investigated by Ehrlich.10,11 Five phases are observed. Between (TiO2 and TiO1.90) an alpha-phase, consisting ofarutile lattice, is found. A beta-phase is observed between (TiO1.80 and TiO1.70). A gamma-phase is homogeneous between (TiO1.56 and TiO1.46) and has a structure of the corundum type. The delta-phase exists between TiO1.25 and TiO0.6 and has a sodium chloride structure. From TiO0.42 to Ti the metal structure is observed. The surface oxide films have been studied by Hickman and Gulbransen.20 The rutile structure is observed in the temperature range studied, 300 to 700°C. Three crystalline modifications of TiO2 exist: rutile and anatase which are tetragonal and brookite which has an orthorhombic structure. Anatase is reported36 to exist in two forms: I and II. Anatase II changes to anatase I at 642°C. Anatase I is stable up to 915°C where rutile becomes the stable modification. At 1300°C rutile transforms to brookite which melts at 1900°C. The monoxide, TiO, may be prepared from the dioxide by high temperature reduction with carbon or magnesium. Its melting point is 1750°C. TITANIUM-NITROGEN Carpenter and Reavell6 report that at 1000°C a linear rate law is observed. The probability of reaction is given as 10-8 at 1000°C. Fast12 has studied the solubility of nitrogen and its effect on the mechanical properties of the metal. The crystal structure of TiN has been shown by several workers2'21'44 to follow the sodium chloride structure. However, the calculated density is found to differ from the pycnometric value. This is studied by Brager3,4 in detail. He has suggested that the titanium sites in the lattice are only partially filled at low temperatures. As the temperature of preparation is raised the vacant sites become occupied which expands the lattice and increases the hardness and density. An (a) value of 4.22Å is given for room temperature. TITANIUM-HYDROGEN The solubility and the crystal structures observed in this system have been reviewed in a recent book by Smith.40

Jan 1, 1950

By O. J. C. Runnals

The intermetallic compounds NpAl2, NpAl3, and NpAl have been prepared, and examined by X-ray diffraction methods. The compounds are isostructural with the corresponding U-Al compounds. NpAl3 is face-centered cubic with a = 7.785A and has the MgCu2 structure. NpAl is simple cubic with a = 4.2624 and has the AuCU3 structure. NpAl4 is body-centered orthorhombic with a = 4.428, b = 6.268, and c = 13.71A. The published description for the atomic positions in UAl, applies also to NpAl4 THE U-Al system has been examined by Gordon and Kaufmann.1 They identified the following intermetallic compounds: UAI2, UAl3, and a third, tentatively identified as UAl5. A structure analysis of the latter compound by Borie2 proved that the formula UAl4 was more consistent with the X-ray data. The crystal structures of UAl2 and UA have been reported by Rundle and Wilson.3 UAl2 was found to be isostructural with MgCu. The atomic positions in the simple cubic UA1, cell were found similar to those in the AuCu3 structure. Three analogous compounds exist in the binary system Np-Al. X-ray data for the compounds NpAl2, NpAl3, and NpAl4 are reported below. The neptunium used in the investigation was supplied through the courtesy of the Argonne National Laboratory as neptunium (V) nitrate. It was stated to have a radioactive content of 99.25 pct Np237. The impurity limits had been established by a spectrographic analysis given in Table I. Any titanium, boron, or bismuth impurity should be effectively removed during the fluorination of NpO2 to NpF4, and sodium, lithium, magnesium or strontium during the alloying procedure. The oxalate ignition technique, described by Westrum for the preparation of finely-divided reactive PuO2, was used.The neptunium (V) nitrate solution, containing 100 mg Np, was evaporated to dryness on oxalic acid crystals. The resulting oxalate was calcined to NpO, by heating in platinum at 650°C for 2 hr. An equimolar mixture of anhydrous hydrogen fluoride and purified hydrogen was passed over the NpO2 for 2 hr at 500°C. According to Fried and Davidson" the above fluorination conditions should produce the purple-black fluoride, NpF3 However, the light-green product showed only NpF4 lines on an X-ray diffraction pattern and contained only an estimated 5 pct of finely dispersed black NpF3 particles on microscopic examination. NpAl3: An intimate mixture of 50 mg of neptunium fluoride and aluminum powder (99.99 pct pure, —28 to $60 mesh) was heated to 900°C in a BeO crucible in vacuum by a tungsten coil for 2 hr, to allow the following reaction to proceed: NPF4 + 7Al + NpAl, + 4AlF. [1] The formation and sublimation of aluminum mono-fluoride in this system was verified from an X-ray diffraction analysis of the sublimate. The diffraction pattern was similar to one obtained in the aluminum reduction of UF4 to UF3,6 showing both Al and AlF3 lines. The resulting alloy was sintered at 1100°C for 1 hr. A powdered specimen of the crystalline product was sealed in a thin-walled quartz capillary for X-ray examination. The photograph was taken on a 14.32 cm General Electric powder diffraction camera, using filtered copper radiation. The films were calibrated in terms of a NaCl standard pattern. The wavelengths used in the calculations were 1.5418A for Cu K and 1.5405A for Cu K The powder diffraction pattern showed that NpAl is simple cubic with a = 4.262 % 0.005A, and is isostructural with UA13 where a = 4.27A1 or a =

Jan 1, 1954

By Harry M. Mikami, Harold A. Heiligman

The term chromite is often used to cover all chrome ores and concentrates which are the designations actually employed by most industrial users and producers. Chromite is, of course, the predominant mineral in chrome ores which are aggregates of chromite and gangue minerals, most commonly magnesian silicates. Most chrome ores now used are petrographically chromitites which is a rock, rather than an individual mineral term. The title of this chapter, following past usage, is meant in the broad sense. Chromite is the only primary commercial source of chromium. This book is intended to deal only with nonmetallic minerals and rocks. Chromite uses are both metallic (ferroalloys) and nonmetallic (refractories and chemicals), but any discussion of mineralogy, geology, and mining is common for all types. A number of the major commercial ores are interchangeable, and their uses are determined by economic considerations. Mineralogy COMPOSITION [Chromite is a term embracing a wide range of chromium-bearing spinel*-group minerals the compositions of which can be expressed as (Mg,Fe2+)0.(Cr,AI,Fe3+ )203.t This can be further generalized to R2+O.R23+03 and the molecular RO: R,03 ratio is generally close to one. The exact composition may be arbitrarily expressed as a solid solution of six end-members, MgAI2O4, MgCr2O4, MgFe2O4 FeCr2O4, FeA12O4, and Fe2+.Fe23+04 with the proportions of each stated or plotted in the six-cornered prism of Johnston and Stevens61 or this scheme may be simplified to comprise only three endmembers making up a composition triangle, Fig 1. [ ] FIG 1-Triaxial composition diagram showing molecular compositions of chromites listed in Table 1. The RO.Fe2O3 corner includes Ti02 norms listed in the table. Note that the high-alumina chromites (1, 2, 3, 9), form a cluster well apart from the high-Cr2O3 chromites. There is a tendency for high-iron chromites to be higher in Fe2O3 + TiO2 but it is not a consistent or systematic relationship. The MgO/RO ratio must also be known to characterize the chromite chemically. Simplest and most convenient method is Thayer's' in which a chromite such as (Mg.65Fe.352+)O.(Cr.40Al.50Fe.103+)203 would be written as (Mge,) Cr eAlo. The molecular pro- portions of ferrous and ferric oxides can be seen at a glance as the divalent and trivalent oxides]

Jan 1, 1960

By Craig R. Barrett, Alan J. Ardell, Oleg D. Sherby

It is shown that the apparent activation energy for creep of pure poly crystalline metals increases with increasing temperature in the temperature range 0.5 to 1.0 of the absolute melting temperature. This increase is probably associated with the influence 0-f the elastic modulus on the creep rate. By accounting for the variation of Young&apos;s nodulus with temperature, the true activation energies for creep of pure cadmium and aluminuvl are shown to be equal to the activation energies for self-diffusion in these metals, within experimental error, at all temperatures above 0.5T,. New creep parameters are proposed for cmrelation of steady-state creep rate and time-to-rupture data. These are respectively, where u is the creep stress, E is Young&apos;s rrodulus, i,is the steady-state creep mte, t, is the time -to-rupture, and D is the self-diffusion coefficient [equal to Do exp (-QSd/RT)] . It has been established experimentally1 and theoreticallyZm4 that high-temperature creep of poly-crystalline pure metals is a thermally activated process and may be represented by the general expression where <, is the steady-state creep rate, A is a constant dependent on the internal structure of the material, f is some function of the applied stress (0) and test temperature (T), and D is the self-diffusion coefficient. If D is separated into its temperature-dependent and independent portions, then it is possible to rewrite Eq. [I] as where Qsd is the activation energy for self-diffusion. Assuming a simple Arrhenius-type relationship between creep rate and temperature at a given constant stress, the apparent activation energy for creep, Q,, is given by the expression It is obvious that if is not a function of temperature It has been shown that the steady-state creep rate for pure polycrystalline metals1 can be represented by where S is a constant, L is the grain diameter, E is the isotropic polycrystalline (unrelaxed) elastic modulus, and n is a constant equal to approximately 5 over a wide range of stress. The apparent activation energy for creep calculated from this expression at constant grain size and stress is given by

Jan 1, 1964

By W. R. McMillan, E. A. Gulbransen, K. F. Andrew

Annealed and electrolytically polished pure iron was oxidized between 650° and 850°C at oxygen pressures of 0.1 to 2 microns Hg. Electron optical studies showed that oxidation occurs discontinuously over the surface and orients crystallographically with the substructure of the metal grains. IN previous papers&apos;, " the authors described the formation of oxide films on high purity iron at norrnal pressures and at temperatures below 300°C. Electron optical studies showed that the oxide film consisted of many individual oxide crystallites having nearly random orientation on each metal grain. The size of the oxide crystallites depended upon the temperature and upon the extent of oxidation. In these studies the crystallite size varied from 250 to 1800Å. Recently, Bardolle and Benard3 studied the crystal habit of the oxide crystallites formed on Armco iron between 650" and 850°C in what might be defined as a "poor vacuum" atmosphere in which the pressure could be varied between 10-1 to 10-3 mm of Hg. Their results showed that, at 850°C and a vacuum of l0-2 to 10-3 mm of Hg, a few well oriented nuclei of oxide were formed on the metal grains. At pressures between l0-1 to 10-2 mm of Hg, many oriented nuclei of oxide were formed. At 750°C the metal surface was bright although an oxide was present. Unfortunately, the extent of oxidation, the oxygen pressure, and the influence of carbon in the metal were not determined, and it was, therefore, impossible to give a theoretical interpretation to the very beautiful light micrographs. Bardolle and Benard used the light microscope to determine the crystal habit of the oxide and X-ray diffraction to determine the orientation relationships. It was believed that the use of controlled amounts of oxidation at high temperature is an important method for the study of the initial stages of oxidation of metals at high temperatures. This paper presents the first results of an electron optical study of this problem for iron. Since the electron microscope and electron-diffraction methods using stripped oxide films and surface replicas yielded finer details of the crystal habit and structure of oxide film, these methods were used in this study. Two types of iron having different carbon contents were used: Puron and Armco* iron. A com- parison of the results for these materials made possible a study of the influence of the surface oxide-carbon reaction on the initial stages of oxidation. Before discussing the experimental results, the thermodynamic equilibria of 1—the oxidation reaction, 2—the surface oxide-carbon reaction, and 3—the solubility of oxygen in iron, will be considered. In addition, it is important to consider the kinetic-theory predictions on the rate of collision of oxygen with the iron surface. Thermodynamic and Kinetic-Theory Calculations Only one type of reaction is usually considered in the oxidation of iron at normal pressures at high temperatures: Fe(a) + 1/2O2(g) = FeO(s) 3Fe(a) + 2O2(g) = Fe3O4(s) 2Fe(a) +3/2O2(g) = a-Fe2O3(s). [11 However, two other reactions may occur: FeO(s) + C (solid solution in Fe) + Fe(a) + CO(g) [2] and Fe(a) + O2(g) e Fe(a) (solid solution of 0,). [ 3 ] In addition, iron will react with the higher oxide at certain temperatures to form FeO. For a complete interpretation of the oxidation of iron at low pres-

Jan 1, 1955

By W. H. Ode, W. A. Selvig

By plotting fixed carbon against British thermal units of coals free from mineral matter, and ranging in rank from anthracite to lignite, it is found that the coals of higher rank, from anthracite to the higher rank of the high-volatile bituminous coals, inclusive, can be separated into groups according to their degree of metamorphism by reference to their fixed carbon. Such charts show also that the coals lower in rank can be best separated into groups with respect to B.t.u., especially when plotted on the moist basis, that is, coal containing its natural bed moisture. A tentative scheme for coal classification was presented at the October, 1932, meeting of the Technical Committee on Scientific Classification, of the American Standards Association Sectional Committee on Coal Classification. This scheme was sponsored by Subcommittee IV on Tentative Classification of Coals, under the chairmanship of W. T. Thom, Jr. It proposed the grouping of coals according to rank by reference to fixed carbon and B.t.u., on the basis of coal containing its natural bed moisture but free from mineral matter. This scheme proposed classifying coals into four broad classes: (1) anthracitic, (2) bituminous, (3) subbituminous, (4) lignitic. The anthracitic class was divided into three groups designated as meta-anthracite, normal anthracite, and semianthracite. The bituminous class also was divided into three groups, low volatile, medium volatile, and high volatile. The high-volatile group was further subdivided into four subgroups according to moisture content, as fo1lows: (1) less than 5 per cent, (2) 5 to 10 per cent, (3) 10 to 15 per cent, and (4) 15 per cent and more. The subbituminous class was divided into two groups, group 1 including subbituminous coals having calorific values of 10,500 B.t.u. or more, and group 2 including those with less than 10,500 B.t.u. The lignitic class of coal was divided into two groups both below 8,000 B.t.u., the one group consisting of consolidated and the other of unconsolidated

Jan 1, 1934

By R. J. P. Lyon, A. E. Prelat, H. Lawrence

Introduction In 1977, the US Bureau of Mines awarded a grant to the state of South Carolina to explore the possibility of using Landsat multispectral scanner (MSS) data as an aid in monitoring surface mining activities in selected counties of the state. Work had been done in Aiken County prior to the grant by USBM and state personnel at the EROS Data Center using both the GE Image 100 and ESL IDIMS systems. The initial work on the 1:100 consisted of locating and measuring the areas of various kaolin mines. The results were excellent on location, identification, and accurate area measurements of several mines as compared with aerial photos of each mine. The effort also included locating and measuring the size of all mines (including sand and gravel) within two US Geological Survey (USGS) 7 % - min quadrangle maps. Line printer overlays using the IDIMS equipment and software resulted in the location of all known mines within an estimated error less than zt 91.4 m. Mine acreage was calculated by counting each symbol (which represented one pixel) and multiplying by 1.1 (the number of acres per pixel). [Fig. 1] shows a portion of one quadrangle overlay. [Table 1] gives a comparison of acreage measured for several mines from the 1-100 and IDIMS system vs. aerial photo measurements. The success of the preliminary work resulted in the South Carolina Land Resources Conservation Commission submitting a proposal to USBM for funding to expand the scope of work to other mineral mining operations within the state and determine if Landsat Imagery could be used to accurately locate and measure mining and reclamation activity on a continuing basis. Three separate tasks were proposed for selected kaolin mines in Aiken County: Task 1, to measure changes in active mine developments over the period 1974-77; Task 2, to measure reclamation activity, and, if time permitted, seasonal changes in mine signatures over the same period of time; and Task 3, to classify one complete mining operation (i.e., differentiate between active, spoil, overburden, water, reclaimed portions and surrounding terrain. The major effort was centered around J.M. Hubeis Richardson mine. Mining operations were progressing in a northerly direction and included three areas of reclamation: one prior to 1974; one started during early 1974; and one reclaimed during 1976. A discussion of all work done under the grant is available in the March 1979 Final Report listed under References. Computer compatible tapes (CCTs) containing MSS data from Landsat Path 18, Row 37, were purchased from the National Aeronautics and Space Administration (NASA) covering the period February 1974 through January 1977. The MSS data were processed on the General Electric Image 100 using parallelepiped classification at the EROS Data Center&apos;s Data Analysis Laboratory, Sioux Falls, SD, and at the Stanford Remote Sensing Laboratory, Stanford University, Palo Alto, CA, utilizing both an unsupervised classification (ISOMIX) and a supervised classification (sequential discriminant analysis). Studies at Stanford University Remote Sensing Lab (SRSL). In Feburary 1977, initial work was begun at Stanford using the STANSORT computer program running on a DEC PDP-10 (Honey, Prelat, and Lyon, 1974). This software is fully interactive and designed to study Landsat CCT data at high resolution (small areas) on a pixel-by-pixel basis (Lyon, 1977). Unsupervised Classification. The initial step was to locate the Richardson mine on the positive print of the full Landsat scene from CCT 1644-15252, dated 6/17/74. This was relatively easy due to a large abandoned kaolin mine and a long narrow pond clearly visible in the scene. Two unsupervised classifications of the Richardson mine were run using ISOMIX clustering (Honey, Prelat and Lyon, 1974). (ISOMIX essentially follows the interactive clustering procedures of ISOCLS Kan, Holley, and Parker. 1973). Although the classifications were successfully accomplished, it was apparent from the TV display that the results did not clearly define the mine areas. A supervised classification would have to be made in order to clearly separate each portion of the mine. Supervised Classification. This classification was done using the Stepwise Discriminant Program (BMDO7M) which is part of the BIOMED package (Dixon, 1970) and involved the following steps: Training group populations were selected and the digital

Jan 1, 1982

ALABAMA. Aldrich.-Aldrich, W. F. Anniston.-Noble, A. E., 20th St. and Wilmer Ave. Auburn.-Brown, R. L., Box 0. Bessemer.-Abbott, C. E., T. C., I. & R.R. Co. Ferguson, V., U. S. C. I. Pipe & Fdy. Co. Williams, E. P., Tenn. C., I. & R. R. Co. Birmingham.-Aldricb, T. H. Aldrich, T. H., Jr., 406 Woodward Bldg. Allen, A. W., 1616 S. 14th Ave. Bowron, J., 1401 S, 20th St. Burbidge, T. A., Browu-Marx Bldg. Coxe, E. H., Tenn. C., I. & R. R. Co. Crawford, G. G., Tenn. C., 1. & R. R. Co. Crockard, F. H., Woodward Bldg. Dimmick, F. D., Dimmick Pipe Co. Ellis, E. E., 1515 Brown-Marx Bldg. Fairbairn, C. T., Woodward Bldg. Fies, M. H., 2316 Highland Ave. Hiller, E., 516 Brown-Marx Bldg. Hillman, M. P. G., 707 Empire Bldg. Ludwig, C. P., 12th Ave. and 12th St. McCormack, G. B., Lookout Mt. Iron Co. McCrery, C., Tenn. C., I. & R. R. Co. Moffett, C. A , 909 Brown-Marx Bldg. Peters, R.. Jr., Brown-Marx Bldg.

Jan 1, 1917

By W. A. Tiller, J. D. Harrison

HOT pressing of powder particles has gained importance recently, since it affords a method in which high densities are rapidly attained. In a recent study on hot pressing of alumina powders, Mangsen, Lam-bertson, and Best1 have shown within the limits of their experiment, the validity the rate equation for densification in hot pressing, originally proposed by Murray, Livey, and Williams.2 i.e., where D = fraction of theoretical density, t = time, P = pressure and 77 is the viscosity, all in appropriate units. This equation was derived from earlier work of Shuttleworth and Mackenzie3 which is based on the closing of spherical pores under the action of surface tension. The integrated form of this equation yields a straight-line relation between log (1 - D) and t. Such conditions were found by Felten4 to be true only after extended periods of pressing. In an endeavor to quantitatively evaluate the exactitude of this equation in the initial sintering stage, i.e., prior to sealing of the pores, spherical anti-

Jan 1, 1962

By Y. A. Chang

Phase relationships in the system Cr-Si have been established based on the melting point, X-ray, metallo-graphic, and DTA studies. The three intermediate phases, Cr3Si, Cr5Si,, and CrSi,, melt congruently at 177V ± I@,Cr3Si, 1680"i 20°, and 1490" *20°C, respectively, while the fourth intermediate phase CrSi, melts peritectically at 1413" i 5°C to Cr5Si3 and a melt containing 51 at. pct Si. The temperatures and compositions of the four eutectic isotherms occurring in this system are given below: DTA and metallographic evidences indicate that Cr5Si, undergoes a phase transformation at 1505" i20°C. The high-temperature form of this phase could not be retained by the quenching techniques used in this study. TECHNOLOGICAL interest in the developing of composite systems, consisting of Sic on the one hand as a fiber-reinforced material and metallic substances such as chromium, nickel, or Cr-Ni alloys as a binding agent on the other hand, stimulated the present investigation of phase relationships in the binary system Cr-Si. Earlier works concerning this system have been evaluated and summarized by ansen and Anderko.&apos; Their phase diagram was based mainly on the works of Kieffer, Benesovsky, and schroth2 and Kurnakov.~ According to these authors, the three intermediate phases Cr3Si, CrSi, and CrSi, all melt congruently at approximately 1730°, 1600°, and 1550°C. However, they did not agree on the compositional stability of the fourth intermediate phase between Cr3Si and CrSi. Later Parthe, Nowotny, and schmid4 determined the structure of this phase to be tetragonal T-1 type using the single-crystal method, and concluded that this phase had a formula of Cr5Si3. Since the compilation of Hansen and Anderko,&apos; a new phase diagram for the system Cr-Si has been proposed by Elliott5 based on the works of Goldschmidt and rand,&apos; Guseva and ~vechkin,~ and Trusova, Kuzev, and Ormont8 and the earlier works quoted by Hansen and Anderko.&apos; According to this proposed phase diagram, all four intermediate phases have large ranges of homogeneity and all melt congruently. More recently, Svechnikov, Kocherzhinskii, and yupkog studied the system Cr-Si by the DTA-method. According to their findings, the three intermediate phases, Cr3Si, Cr5Si3, and CrSi,, melt congruently at 1700°, 1720°, and 1475"C, respectively, while the fourth intermediate phase, CrSi, melts peritectically at 1475°C to Cr5Si3 and a melt containing 50 at. pct Si. The temperatures and compositions of the four eutectic isotherms were found to be: In view of the discrepancies existing in the literature concerning the system Cr-Si, it was decided to rein-vestigate the phase relationships in this system. EXPERIMENTAL a) Starting Materials. Chromium disilicide and chromium or silicon powders were used in the present study to prepare the melting point and DTA samples. CrSi, was obtained by directly reacting cold-pressed elemental powders in an atmosphere of Hz at a temperature of about 1250°C. Chromium powder, purchased from Stark Chemical Co., had the following impurities in ppm: Fe, 200; Mg, 1000; and 0, 250; while silicon powder, purchased from the Welded Carbide Co., had the following impurities in ppm: Ca, 700; and Fe, 3500. b) Melting-Point Determination and Differential Thermal Analysis. Cylindrical melting-point samples of approximately 13 mm in diam and 30 mm in length with a rectangular groove in the center were prepared by hot-pressing of well-mixed powder mixtures in graphite dies. Before the melting-point determination, the hot-pressed samples were ground on a sand paper to remove any minute surface contamination of graphite. A small hole of 1 mm in diam, drilled on the center portion of the samples, served as a blackbody cavity for the temperature measurements. DTA samples approximately 13 mm in diam and 15 mm in length were prepared in a manner similar to the melting-point samples. Melting points were determined using the Pirani technique under a helium atmosphere of 40 psi. The design, performance, and operation of this apparatus have been described in detail by Rudy and ~ro~ulski.&apos;~ The temperature measurements were carried out with a calibrated disappearing-filament-type micro-pyrometer. The measured temperature was corrected for losses from the quartz window of the melting-point furnace and for deviations from blackbody conditions of the observation hole. The procedure for temperature correction has also been previously described." The DTA method of Heetderks, Rudy and Eckertl&apos; was also used to check any phase transformations of selected alloys in the system Cr-Si. It was not possible to make remated runs on the same sample once melt-

Jan 1, 1969

By A. M. Gaudin

Jan 1, 1962

By W. A. Backofen, D. L. Holt

Push-pull fatigue tests have been carried out at 4.2°K, 77oK, and room temperature on two poly crystalline materials of widely different stacking-fault energy (?): pure copper (? - 70 ergs per sq cm) and the Cu-8 wt pct A1 alloy (? - 2.8 ergs per sq cm). Constant stress-amplilude was imposed and measurement was made of the plastic-strain amplitude (ep) at saturation. Lives extended from 104 to 106 cycles. Designating lives at the various temperatures by NRT, N77, and N4.2. the ratios N77/NNT and N4.2/N77 ranged from 3.5 to 18 under the condition of common Ep . Metallo-graphic examination revealed different crack morphology in Cu-8 Al fatigued at room temperature, and at 77" and 4.2oK. At room temperature, cracks lay in or near grain and lain boundavies; at 77o and 4.2oK. cvacks were transcrystalline. Tests on single crystals of Cu-8 A1 showed that such a change in the cracking mode in polycrystallitle material accounted for a factor of- about 3.25 in N77/NRT . The longer life at lower tewperatztre (conslant cp) has heels attributed to two deuelopinents: a reduced production of the dislocation tangles and subgrain boundaries which serve as paths of rapid cracking, and suppression of oxygen chetni-sorption at the crack tip It was concluded that in both materials the luller accounted for an extension of the life at 4.2oK beyond that at room temperature by a factor of 15. XV ECENT experiments on the fatigue of Cu-A1 alloys in the so-called high-cycle range (greater than lo4 cycles) have emphasized the importance of stacking-fault energy (y) as a quantity affecting crack propagation rate and fatigue life.1,2 It was found in comparisons at essentially fixed plastic-strain amplitude that crack growth rate decreased by a factor of about 5 over the composition range from copper (? - 70 ergs per sq cm) to Cu-8 wt pct Al (? - 2.8 ergs per sq cm). The argument was made that, when stacking-fault energy is high, cross slip and climb are favored, so that dislocation tangles and/or subgrain boundaries form more readily under cyclic loading. Since the boundaries and tangles act as paths of rapid crack propagation ,3, 4 life is shortened as a result. However, when stacking-fault energy is reduced (as by alloying), cross slip and climb become more difficult, with the result that substructure formation is retarded and growth rate is also reduced. A purpose of the present work was to investigate the substructure effect in relation to temperature. As temperature is lowered, ? is varied only slightly (if at all), but decreased thermal activation can interfere with cross slip and climb. Thus substructure formation could be curtailed and life increased. Fatigue life in the high-cycle range is also known to be strongly influenced by environment. Working with copper, Wadsworth and Hutchings observed that life in a vacuum of 10-8 mm Hg exceeded life in air by a factor of 20.5 They isolated oxygen as the agent that furthered cracking. While the details are still unclear, a requirement in any mechanism of oxygen-accelerated cracking is that there be chemisorption at the crack tip. That could prevent welding on the compression half cycle,= interfere with reversal of slip,1, 6 or aid in breaking metal-metal bonds at the crack tip.5&apos;7 In the work being reported here, temperature was lowered by immersion in liquid nitrogen and helium, which also served to reduce both the oxygen concentration and chemisorption rate. A possible effect upon life, i.e., a lengthening, had to be recognized. Several researchers have determined fatigue lives at low temperatures presenting their results in the form of stress amplitude (S) vs cycles in life (N) curves.8-11 Such curves reflect, primarily, the fact that metal is strengthened by lowering temperature; effects of substructure and changing environment tend to be masked. The difficulty can be overcome by comparisons based on identical plastic-strain amplitudes, and in the present work the dependence of life on both plastic strain and stress amplitude was established. EXPERIMENTAL Materials. The principal materials were polycrystal-line copper (? - 70 ergs per sq cm)" and the Cu-8 wt pct Al alloy (? - 2.8 ergs per sq cm),I3 the latter being near the limit of solubility of aluminum in copper and having, therefore, the lowest stacking-fault energy in the CU-Al system. Specimens were machined from 0.118-in.-diam cold-swaged rods of high-purity (99.999 pct) copper and the Cu-8 Al alloy, the latter produced initially in a graphite boat by induction vacuum melting a mixture of 99.999 pct Cu and 99.99 pct Al. The machined specimens were annealed to produce mean grain diameters of about 0.070 mm in copper and 0.190 mm in the alloy. Specimen dimensions are given in Fig. 1. Values of the tensile yield stress, ultimate strength, uniform strain (determined by the Considgre construction), and reduction of area, for both materials at 4.2oK, 77oK, and room temperature, are listed in Table I. The tensile apparatus in which these results were obtained has already been described.14 Apparatus. Specimens were fatigued in push-pull with a machine that is illustrated schematically in Fig. 2. The specimen is first soldered into the top grip (1) with Woods metal, and the grip is then screwed into the inner tube (2) which is connected to the drive rod of the Goodmans vibration genera-

Jan 1, 1968

By A. E. Powers, J. F. Libsch

THE simultaneous influence of time and temperature upon the tempering process in steel is well known. Hollomon and Jaffe¹ have expressed the effect of time and temperature upon the progress of tempering by a single parameter, T (c + log t); where T is the absolute temperature; t, the tempering time; and c, a constant characteristic of the steel and treatment. It was found that when hardness data for plain carbon and low alloy steels were plotted vs. this parameter, a master tempering curve was obtained which satisfied all the data for a given steel and a given hardening treatment. Roberts, Grobe, and Moersch² successfully applied the tempering parameter to various tool steels, including high speed steel for tempering times ranging from 6 min to 100 hr. The influence of tempering time and temperature upon the physical properties of high speed steel has also been extensively investigated.&apos;" Recently, the use of induction heating for very rapid tempering treatments has received attention. The authors% have shown that tempering treatments of only a few seconds duration may be successfully applied to plain carbon and low alloy steel. However, the influence of such short tempering treatments in high speed steel has not been explored. Since high speed steel is a highly alloyed steel exhibiting physical reactions during tempering that are often relatively slow and large in magnitude, it is an interesting steel for the study of tempering reactions. It was the purpose of the present investigation, therefore, to study the early progress of reactions leading to secondary hardness in high speed steel, type 6-5-4-2, and to determine if induction-tempering treatments of a few seconds duration are able to produce results equal to those of more conventional long-time tempering cycles. Experimental Details The chemical compositions for two different heats of W-Mo high speed steel used in this study are given in Table I. Table II summarizes the heat treatment given various groups of specimens cut 21/2 in. long and centerless ground to ¼ in. diam. Hardening treatments consisted of preheating to 1600°F (870°C) for V2 hr and then oil quenching from 2250°F (1230°C). Heat I was subjected to the high temperature in a salt bath for 3 min, while specimens of heat II were austenitized in a carbon-block muffle furnace for 10 min. Specimens of series E were immediately refrigerated to — 318°F (— 195°C) in liquid nitrogen following the hardening treatment to transform the major portion of the retained aus-tenite. Specimens of series F and G were subzero cooled to — 100°F (-75°C) in a dry ice-alcohol mixture. Induction tempering was performed with a Lepel high frequency converter operating at a frequency of approximately 300,000 cycles per sec. Heating cycles were controlled and recorded for each specimen using a chromel-alumel thermocouple, percussion welded to the surface of the specimen, and a modified high speed instrument with a timer previously used and described.&apos; Temperature oscillation of the specimens, while being held at the tempering temperature, was ± 15°F (8°C). Tempering Treatments: After hardening, specimens were tempered between 900" and 1500°F (480" and 815°C) to study the progress of retained austenite decomposition and secondary hardening. The specimens tempered in salt for 1 hr (series C, G, and I) were considered to represent conventional treatment and are used for comparison with rapid tempering treatments. Several induction-tempering cycles were employed: 1—flash tempering, i.e., induction heating to the tempering temperature and immediately cooling (series A, E, and F); 2—induction heating for 60 sec at temperature (series B); and 3—double-induction tempering by two successive heating and cooling cycles (series D). All specimens tempered by induction were heated at an initial rate of 450°F (250°C) per sec except those of series E, which were heated at an initial rate of 1300 °F

Jan 1, 1952

By Albert Ladd Colby

PAGE I. Introduction,...........577 11. PRocess of Manufacture. 1. American Specifications. 2. Foreign Specifications, . ......... 580 III. Chemical Properties. I. Chemical Composition: (a) American Specifications ; (b) Foreign Specifications. 2. Chemical Analysis: (a) American Specifications ; (b) Foreign Specifications ; (c) Number of Analyses Required ; (d) Sample for Analysis ; (e) Check-Analyses Impracticable ; (f) Rejection Solely on Variation in Com-&apos; position,............581 IV. Physical Properties. 1. Drop-Test and Drop-Testing Hachine: (a) American Specifications ; (b) Foreign Specifications ; (c) Limits in Deflection. 2. Tensile Test: (a) American Specifications; (b) Foreign Specifications ; (c) Test-Pieces are not Representative ; (d) Specified Tensile Strength is Affected by the Section ; (e) BpeciBed Tensile Strength is Often Inconsistent with Specified Chemistry ; (f) Specified Tensile Strength is Often Inconsistent with Specified Elongation ; (g) Amount of Tensile Testing Required is Excessive ; (11) Conclusions. 3. Dead-Weight Test: (a) American Specifications; (b) Foreign Specifications; (c) Number of Tests Specified. 4. Bending-Test: ((1) American Specifications ; (b) Foreign Specifications,..........589 V. Section. 1. American Specifications. 2. Foreign Specifications: (a) Templets ; (b) Sample Piece of Rail; (c) Allowable Variation from Templet,...........601 VI. Weight. 1. American Specifications. 2. Foreign Specifications,. . 603 VII. Length. 1. American Specifications. 2. Foreign Specifications, . . 604 VIII. Drilling. 1. American Specifications. 2. Foreign Specifications, . 604 IX. Finish. 1. American Specifications. 2. Foreign Specifications, . . 50.5 X. Branding. 1. American Specifications. 2. Foreign Specifications : (a) Data to be Rolled in Raised Letters on Web of Rail ; (b) Marking of the Blow-Number on Each Rail; (c) Additional Marking and Painting of Rails,........605 XI. Inspection. 1. American Specifications. 2. Foreign Specifications: (a) Prior Notice of Rolling; (b) Free Access to the Works ; (c) Cost of Inspection, Analyses and Tests to be Borne by the Manufacturer ; (d) Rails after Inspection by Manufacturer to be Sorted into Lots Prior to Inspection by the Engineer ; (e) Disposition of Rejected

Jan 1, 1907

By Irving Cadoff, Kurt Komarek, Edward Miller

Barium can be purified by equilibration with titanium. The melting point of barium was found to be 726.2° i 0.5 °C. The room-temperature lattice parameters of BaTe and Bask are 7.004 * 0.002A and 6.600 * 0.002A. Melting points for BaTe and Base were found to be 1510° * 30°C and 1830° ± 50°C, respectively. HIGH-purity barium and its compounds are difficult to prepare because of the reactivity of barium with the atmosphere and the large heats of formation of the compounds. Purification of barium by vacuum distillation,&apos; and the preparation and properties of barium oxide2 and barium sulfide3 have been reported. However, little has been done on the homologous compounds barium selenide and telluride. PURIFICATION OF BARIUM Distilled barium obtained from King Laboratories was used as the starting material. The analysis supplied with the metal showed the presence of: 0.4 wt pct Sr, 0.001 pct Mg, 0.02 pct F, 0.003 pct Cu, 0.005 pct Na and less than 5 x 10-3 wt pct of any other metallic impurity. Analyses for oxygen and nitrogen were not available. Since there is evidence4 that any barium nitride present in the starting material may decompose on distillation producing nitrogen which can contaminate the distillate, further purification was performed. At elevated temperatures, any nitrogen and oxygen present in barium should be removed by reaction with titanium. Assuming that the solubility of oxygen in liquid barium is negligible near the melting point of barium, any oxygen present will be in the form of BaO. Removal of oxygen from molten barium is expressed by the equation: BaO(S)+ TixOy(S) = Ba(l)+ TixO(y+1)(s) where Ti,Oy and TixO(y+1) are solid solutions of oxygen in titanium. At 1000°C, the change in free energy for this reaction is negative for (y+1)/x +y+1) x (100) 17.5 at. pct O.5 Since reaction with commercially pure titanium (containing 0.07 wt pct oxygen) results in a free energy change for the reaction of -19 kcal per g-atom, slight solubility of oxygen in barium would not hinder the oxygen removal. Since comparable thermodynamic data are not available to permit calculation of the partition of nitrogen between liquid barium and titanium, a similar quantitative relationship cannot be obtained. However, on the basis of work by Kubaschewski and Dench,5 complete removal of nitrogen from liquid barium can be expected. Since the melting point of barium is depressed markedly by small additions of nitrogen,&apos; the change in melting point during reaction of barium with titanium was used to follow the purification reaction. MELTING POINT OF BARIUM A 50-g sample of barium was sealed by arc welding under argon into an all titanium crucible provided with a thermocouple well. The melting point of the sample was determined by thermal analysis, using a Pt/Pt-10 pct Rh thermocouple which was calibrated according to National Bureau of Standards specification6. The crucible was then heated for 48 hr at 950°C in vacuum and the melting point redetermined. This procedure was repeated until three successive thermal analyses agreed within ±0.5oC, the limits of error of the analysis. The melting point increased from an initial value of 720.0°C to a final value of 726.2°C. Analysis on samples quenched from 950°C gave a solubility value of 0.004 wt. pct Ti. Assuming that the titanium-barium phase diagram is similar to those of titanium-magnesium7 and titanium-calcium,8 the solubility of titanium in liquid barium decreases with decreasing temperature. Therefore, the solubility of titanium in liquid barium should be less than 0.004 wt. pctat the melting point (726oC), and the effect of dissolved titanium on the melting point would be negligible. Addition of up to 3 wt pct Sr does not significantly change the melting point of barium,7 so that the effect of the 0.4 wt pct Sr in the starting material will also be negligible. The value of 726.2" ± 0.5C obtained for the melting point of barium can be compared .with a determination carried out by Keller and coworkers in low-carbon steel crucibles,&apos; who obtained a value of 725± 1C, using barium purified by fractional distillation. The higher value obtained in the present investigation is indicative of the effectiveness of titanium in removing traces of nitrogen. PREPARATION OF BaTe AND Base The compounds were prepared by direct reaction

Jan 1, 1961

By M. E. Wadsworth, R. L. Pearson

THE dissolution of UO, in carbonate solutions can occur only il the tetravalent uranium is oxidized to the hexavalent state. The carbonate system is of particular interest because it provides a means whereby the oxidized uranium may be dissolved by forming the complex ion UO,(CO3)3-1. In the presence of oxygen the over-all reaction may be written UO+1/2O,4CO3T+2HCO2UO,(CO4)11+H2O [1] UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. The mineral ulrichite is the natural counterpart of the synthetic UO, used. The kinetics of the leaching of UO, should be similar for any of the uraninite type minerals. A pressurized system was used not with the hope it could be extended to commercial systems as a primary purpose but simply to provide the means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The importance of such pres-

Jan 1, 1959

By C. S. Barrett, C. T. Haller

TWINNING in magnesium is known to occur profusely under certain conditions, and when it occurs in polycrystalline materials it brings about a partial or even a complete change in the preferred orientation. The amount of research on this subject, however, has not been in proportion to its importance as a mechanism of deformation and reorientation. Much of the research has been limited to twinning in single crystals. The present study&apos; concerns polycrystalline sheet, and is an investigation of the twinning produced by plastic deformation as a function of the following variables: I. Direction and type of deformation. 2. Amount of deformation. 3. Speed of deformation. 4. Temperature of deformation. 5. Composition and temper of the sheet. 6. Twins previously produced. 7. Twins previously produced, then annealed. By proper control of these variables it is shown that, on a laboratory scale, samples can be produced that are free from preferred orientations. MATERIALS AND METHODS The materials used were samples of commercial magnesium-alloy sheets with nominal compositions given in Table I. [ ] X-ray diffraction was used in most of this work to detect the twins and to estimate the amount of twinning. Since twinning on {102} planes causes a reorientation of the crystal lattice by 86°, it is very easy to study with X-ray diffraction patterns, particularly if one notices the diffraction ring from the basal plane the 002 reflection. By properly directing the X-ray beam, it is possible to produce 002 reflections from twinned material at, say, the 6 and 12 o&apos;clock positions on the 002 ring, with the untwinned material reflecting to 3 and 9 o&apos;clock positions; and by judging the relative intensity of the arcs on the diffraction ring at these positions, it is possible to judge the amount of twinned material relative to the untwinned. This X-ray method of estimating the amount of twinning is generally superior to metallographic observation, for it was found

Jan 1, 1946