By Otto H. Henry, Edward L. Badwick

Up to the present time, according to Hansenl and Haughton,² the constitution of the bismuth-indium system has not yet been published. The generally accepted value for the melting point of indium, as listed in most scientific journals and textbooks, is 155°C. Recently, however, H. M. Davis3 has determined a new melting point for indium of 157.3²C O.l°C. Since bismuth has been used in preponderance as an alloying element in the majority of low-melting alloys, and indium has been used with considerable success in lowering the melting points of low-melting alloys, 4,6 an interest has been developed in the application of these two metals, making a complete knowledge of the constitution of its alloys desirable. In this investigation, the melting point of indium reported by H. M. Davis has been found to be substantially correct. A value of 157. ²°C ± O.5°C was determined. The two eutectic compositions have been placed at 34 and 50 pct bismuth with their respective eutectic temperatures as 72.4°C ± 0.5°C and 90°C ± 0.5°C. The bismuth-indium phase diagram has been determined by thermal and microscopic analysis and is shown in Fig I. Thermal Analysis Granulated bismuth and indium shot, having a guaranteed purity of 99.99 and 99.95 pct, respectively, were melted in a carbon crucible by means of a laboratory heater. To minimize oxidation of the alloys, a heavy mineral oil (Nujol) having a high- flash point was used. A platinum-platinum rhodium thermocouple of fine wire encased in a thin-walled Pyrex glass tube, about 1/8 in. in diameter, was connected to a type K potentiometer for temperature measurements. The thermocouple was calibrated against the melting points of tin, bismuth, and the silver-copper eutectic and the boiling point of water. Since the temperature readings could be reproduced to 0.²°Cl and the accuracy of the temperature standards in this range is slightly better than 0.5°C, it scems reasonable to assume that the temperature readings are reliable to approximately 0.5°C. The cooling rate could be controlled by varying the amount of insulation surrounding the crucible. Three or four layers of asbestos paper, 1/16 in. thick, sufficed to give a cooling rate of from I° to ²°C per minute. Undercooling was slightly noticeable. This condition was minimized by vigorous stirring, since the advantage of using slower rates was too small to justify the greater expenditure

Jan 1, 1947

By A. K. Mukherjee, J. E. Dorn, J. D. Mole

Investigations were carried out on the effect of polyslip on the strain hardening of aluminum single crystals. The orientations investigated were those lor which the tensile axis was in the [001], [111], [112], and [012] directions plus another for which the Schmid angles for {111}(110) slip were 1 deg. The experimental data were analyzed on a model based on the intersection of dislocations with particular emphasis on the effect of polyslip on the activation volume for inter-section. It is shown that the rate of strain hardening inreases for those orientations wherein attractive dislocation intersections occur and that those orientations which produce the greater number of such intersections exhibit the greater strain hardening. Good correlation of the data is obtained with the concept that attractive junctions, as proposed by Saada, Play an important role in accounting for the rate of strain hardening. EXISTING concepts on the nature and cause of strain hardening in fcc metals have been deduced principally from experiments on the deformation of single crystals under single slip. The effect of crystal orientation on the shapes of the stress-strain curves for single slip have been summarized by seegerl and more recently by Clarebrough and Hargreaves.2 Tensile specimens whose axes fall near the center of the [001]-[011] line of the standard triangle of the stereographic projection exhibit the longest range of easy glide (Stage I) and the lowest rates of linear hardening (Stage 11) whereas specimens whose axes lie near fie [001]-[111] line of the standard triangle have limited or no easy-glide range and exhibit somewhat higher linear strain-hardening rates. Specimens whose axes lie near the [001] or the [ill] poles do not exhibit easy glide and have the highest rates of linear hardening. Kocks3 has shown that the highest rates of linear hardening Occur under Polyslip when the tensile axis coincides with the [111] or the [ 001] pole. Since the rate of strain hardening is sensitive to specimen orientation and the incidence of polyslip, these relationships might help to discriminate between various dislocation models for strain hardening in fcc metals. Previous attempts to analyze the effect of orientation on strain hardening,1"3 however, did not provide a unique answer to this problem. Consequently the present investigation was undertaken wherein additional data, particularly that for the effect of polyslip on the activation volume for intersection, was also determined in order to provide more complete information on the details of strain hardening. Whereas analyses of these data reveal that several recommended models for strain hardening are at variance with the facts, good correlation of the data is obtained with the concept that attractive junctions4 play an important role in accounting for the rate of strain hardening. I) EXPERIMENTAL APPROACH seegerl demonstrated that slip in fcc crystals at low temperatures is dependent on thermally activated intersection of glide dislocations with forest dislocations. This has been confirmed by tests on single crystals of aluminum by Mitra, Osborne and Dorn5 and on polycrystalline aluminum by Mitra and Darn.' Thus in accord with Seeger's theory, the shear strain rate, ?, below a critical temperature, T, is where .V is the number of points of contact per unit volume between forest dislocations and glide dislocations, A is the area swept out per successful intersection, b is the Burgers vector, v is the frequency of vibration of the segment of the glide dislocation undertaking intersection, U is the activation energy for intersection, k is Boltzmann's constant, and T is the absolute temperature. For aluminum, which has an extremely high staeking-fault energy, the constriction energy is negligibly small and therefore the activation energy decreases practically linearly with the stress according to as will be recomfirmed later, where Uo is jog energy at the absolute zero, G and Go are the shear moduli at the test temperature T and O°K, respectively, L is the spacing of the forest dislocations, t is the applied shear stress for slip, and tGo is the stress field that must be surmounted athermally.

Jan 1, 1965

By M. J. Mullikin, J. B. Conway

for use in describing combined first- and second-stage creep data. In the above ?o represents the instantaneous strain on loading, ?t the limit of transient creep, ?S the steady-state creep rate, t the time, and ? a constant leading to the exhaustion rate of transient creep. It was noted that this equation was similar in form to that proposed originally2 by McVetty. This type of equation was also suggested by Andrade and Aboav3 in studies of the shear strain of cadmium. Calculation of the constants ?o, ?t, ?, and ?s, in Eq. [ l] is somewhat involved due to the slight complexity of this relationship. In the paper by Garofalo a computer approach based on a least-squares analysis was recommended. Such an approach involves a trial and error solution but when a computer facility is available the difficulties in this calculation are of little consequence. It does mean however that the evaluation of this type of equation would become quite tedious if computer facilities were not available. Some recent studies have identified a fairly straightforward method for calculating the constants in the Garofalo equation. While not leading to a least-squares evaluation the approach is accurate and is recom-

Jan 1, 1967

By Edna A. Dancy, Gerhard J. Derge

The specific conductance of FeOx,-CaO melts in contact with iron was found to decrease from 200 ohm-1 cm-1 for FeO, to 40 ohm-1 cm-1 for a melt containing 26.3 pct CaO at 1400°C. The temperature coefficient was positive at all compositions, but became smaller at high CaO contents. Current efficiencies for electrolysis increased from 2.5 pct in FeOx to 17.3 pct at the high CaO composition, indicating a change from predominantly electronic conduction to conduction with a substantial ionic contribution. It was shown that Ca++ ions as well as Fe++ ions carry the ionic current. A subsidiary investigation on the apparent effect of atmospheres of argon, helium, and nitrogen on the electrical conductivity showed that this could be correlated with surface temperature losses, which varied with the thermal conductivities of the gases and resulted in precipitation of metal by the reaction 3 Fe++ = 2 Fe+++ + Fe. The work described in this paper is offered as a contribution to the general fund of knowledge concerning metallurgical slags. Measurement of electrical conductivity and electrolysis are comparatively trouble -free methods for investigating molten materials, but, although these methods had been used for complex slags, it was not until the work of Bockris et al.1 that the approach of examining simple binary slag systems was employed, and CaO-SiO2, MnO-SiO2, and Al2O3-Si9 were studied. Two groups have performed work of particular relevance to the present investigation. Inouye, Tomlinson, and chipman2 studied the conductivity of wustite as a function of temperature and of the addition of 5 mol pct of a number of oxides, including CaO. They concluded that molten FeOx in equilibrium with iron is a semiconductor. Simnad, Derge, and ceorge3 demonstrated the ionic nature of liquid iron silicate slags and also concluded that, although the conductivity of FeOx in equilibrium with iron is predominantly electronic in nature, there is a small ionic contribution. The work reported here on FeOx,-CaO slags consists of three main parts, namely, the determination of the specific conductance over a wide composition range, an investigation into the nature of the conductivity through current-efficiency measurements over the same composition range, and an attempt to identify the current-carrying ions, as well as a subsidiary investigation on the apparent effect of the nature of the inert atmosphere on the conductivity. EXPERIMENTAL Materials. The slags, varying in composition from FeOx to 27 pct CaO, were prepared by heating reagent- grade Fe2O3 in an ingot iron crucible with a suitable amount of CaCO3 and, in some cases, powdered iron, in air. This prefused material was then used for the runs. At the end of each run the cell was removed from the furnace and quenched by immersing the bottom half in water. After crushing, the slags were analyzed for calcium and total iron by the usual wet methods. The oxygen content was obtained by difference. Specific Conductance: Apparatus and Method. Fig. shows the experimental setup, with the conductivity cell and leads of ingot iron. The standard four-probe method for measuring high conductivities was used. In this, the potential drop across the unknown resistance is compared with the potential drop across a known resistance connected in series, i .e., same current through both resistances. Thus there are both current and potential leads to the center electrode and to the crucible, which acts as th other electrode. Both ac and dc circuits were available for the measurements; they have been described in earlier work performed in this laboratory.4,5 The geometry of the cell was such that the center electrode was equidistant from the bottom and sides of the crucible. This ensured that the current path was the same irrespective of the magnitude of the conductivity of the material in the cell. Cell constant were measured with KC1 or NaCl solutions, which have considerably lower conductivities (0.0013 to 0.25 ohm-' cm) than the slags, and this precaution in design made sure that the determined cell constants applied to the cells with contents of any conductivity. The cell-constant determinations were made with the ac measuring circuit to prevent polarization. The four-probe method eliminates lead resistance but not the resistance of those parts of the center

Jan 1, 1967

By C. Atkinson

A method is described for the numerical solution of the diffusion equation with a composition-dependent diffusion coefficient and applied to the radial growth of a cylinder; the radial growth of a sphere, and the symmetric growth of an ellipsoid. Sample applications of the method are made to the growth of particles of proeutectoid ferrite into austenite. RECENTLY&apos; we described a method for numerical solution of the diffusion equation with a composition-dependent diffusion coefficient for the case of the growth of a planar interface. In this paper we extend this method to describe the radial growth of a cylinder, the radial growth of a sphere, and the symmetric growth of an ellipsoid. In the latter case, limiting values of the axial ratios of the ellipsoid reduces the problem to one of a cylinder, a sphere, or a plane depending on the axial ratio. A check on these limiting values is made in the results section. In all of these cases we consider growth from zero size. A natural consequence of this assumption as applied to the sphere, for example, is that the radius of the sphere is proportional to the square root of the time. This is consistent with the condition that the radius is zero initially, i.e., grows from zero size. It may be argued that it is more realistic to consider particles which grow from a nucleus of finite initial size; even in this case the analysis of this paper is likely to be applicable. This can be seen if a comparison is made of the work of Cable and Evans,2 who consider a sphere of initially finite size growing by diffusion in a matrix with a constant diffusion coefficient, with the results of Scriven3 for growth from zero size. This comparison shows that the rates of growth in each case differ trivially by the time the particle has grown to about five times its initial size." This investigation is a generalization of those of Zener,4 Ham,5 and Horvay and cahn6 to the situation often encountered experimentally, in which the diffusion coefficient varies with concentration. First let us consider each of the cases separately. I) GROWTH OF SPHERICAL PARTICLES FROM ZERO SIZE In this case the differential equation in the matrix depends only on R, the radius in spherical coordinates, and can be written: ? 1 <^\ ^13D . , dt U\dRz + R 3Rj + dR dR [ J where C is the composition, t is the time, and D is the diffusion coefficient which depends on c. The boundary conditions will be: c = c, at the moving interface in the matrix, c = c, at infinity in the matrix (and at t = 0, everywhere in the matrix), c = X, is the composition in the spherical particle. Each of the above compositions is assumed constant. In addition there is the flu condition at the moving interface which can be written: , dR0 ~/3c dt \dR/H =Ra where R,, which is a function of t, is the position of the moving interface. We make the substitution q = RI~ in [I] reducing this equation to: & - m - *ws) »i where we have written D = D,F(c) or simply D,F, and Do = D(c,). Thus F[c(q0)] = 1 where q, = ~,/a is the value of the dimensionless parameter q evaluated at the interface. Multiplying Eq. [2] by dq/dc and integrating, we find: where the lower limit of the integral has been chosen so that dc/dq — 0 as c — c,, thereby satisfying the boundary condition at infinity. We require, then, to solve Eq. [3] subject to the condition c = c, when q = q, (this follows from putting R = R, at the interface) together with the flux condition which can be rewritten in terms of q as: Eqs. [3] and [4] together with the condition c = c, at q = q0 enable us to find 77, and the concentration profile c = c(q). Numerical Method. We treat Eq. [3] in the same way as we did the corresponding equation for the planar interface problem&apos; i.e., by dividing the interval c, to c, into n equal steps so that: cr = ca -rbc [5] where r takes the values 0, 1, ... n and we call no,, q1, ... nn the values of n corresponding to the compositions c,, c,, ... c,.

Jan 1, 1970

By A. Mitchell, M. Etienne

VARIOUS&apos;-3 reports on the electroslag remelting process refer to the "thin skin of slag" existing around the slag pool and the solidifying ingot, but none considers the various mechanisms by which this layer forms and thus influences the surface quality of the ingot. A vertical section4,5 of the Cao-CaF2-Al2O3 diagram is shown in Fig. 1 between CaF2 and 6Al2.CaO3 From this, it is seen that a typical "70:30" CaF2:A1a3 slag will solidify to produce 6Al2O3.CaO primary phase in a eutectic matrix. The commercial slags contain sufficient CaO to produce* this composition by both the

Jan 1, 1969

CARL HENRICH (communication to the Secretary*).-I have read with much interest the discussions of my paper by Messrs. A. S. Dwight, E. P. Mathewson, Win. B. Boggs, Jos. W. Richards, and W. C. Smith. Mr. Dwight&apos;s acknowledgment that he always-in lead smelting¬obtained better results by figuring A1203 as an acid in his slags, I may take as a confirmation of my views, notwithstanding his later conversion by, the late T. S. Austin to the latter&apos;s empirical view and way of neglecting the consideration of A1203 altogether in the composition of slags-letting the slags "dissolve" in Al203. I have a strong suspicion that Mr. Austin, in a large custom smelting plant at El Paso, has been able to keep the alumina percentage of his slags sufficiently low, not to give him much trouble, although I have also a suspicion that his furnace foreman may have had a somewhat differing opinion of the practical working of the "dissolving" theory,, whenever its applicability was tested to its limits. That Austin should have conceived the notion that the Ca of CaF2 would enter into a slag as CaO, seems hardly in accord with the recognized ability of that late metallurgist. It is a well-recognized fact that even small amounts of CaF2 will reduce the viscosity of a slag; but I did not think anyone ever had an idea that CaF2, in some mysterious way, parted with its F and coupled itself with 0 to satisfy a craving for CaO on the part of 802-least of all in a lead furnace. The "dissolving" theory for CaF2 was doubtless appropriate, and an improvement on figuring the Ca of CaF2 as CaO to satisfy the demand of Si02 for RO bases. However, I cannot understand the rationality of extending this "dissolving" theory to A1203 and to ZnO. It would be interesting to have more specific data from Mr. Mathewson in regard to the actual composition-analyses-of the slags made, when he had these unusually high alumina slags in Colorado. We "old" smelters all know that within certain limits, usually found out by rather tough experience, we could safely "disregard" A1203. In fact, I believe, we never really analyzed for alumina, except in slag analyses, when we

Jan 6, 1917

By H. D. Merchant

NUMEROUS publications have examined hot hardness of metals and alloys. Some have studied creep in long-time hardness tests, few of which, however, were tested under a spherical indentor. 1-3 The results of Mulhearn and Tabor&apos; indicate a parabolic-type creep for indium and lead, whereas Moore and Tabor2 how a logarithmic-type creep for indium. Similar semilog relationships between hardness and time have been found by Goffard and wheeler3 for magnesium, aluminum, and their alloys. In this note, the elevated-temperature hardness of some complex alloys, shown in Table I, was examined to discover whether any basic information about the deformation behavior of the alloys could be obtained. One of the alloys, H-13 alloy steel, was tested for short-time creep tests to examine the hardness-time relationship at various temperatures. A standard Brinell Hardness Tester, mounted with an appropriate furnace and 99 pct A12O3 poly-crystalline indentor, was employed for the purpose. The alloys were tested at temperatures from room to 1400°F for 30 sec under 1500-kg load. The creep studies were conducted for about 8500 sec at 7l°, 500°, 1000°, and 1200°F. For constants A and B, a relationship of the type H = Aexp(-BT) [ll was obtained for all alloys between hardness, H, and temperature, T. In the semilogarithmic plot, the data points for each alloy were arranged into two groups, each group on a straight line with a specific set of A and B values. These results are in agreement with many such observations on hot hardness, notably those of Westbrook for pure metals,4 The thermal softening coefficient, B, and transition temperature, Tt, for various alloys are shown in Table I. The change in slope around the transition temperature suggests an apparent change in the mechanism of deformation, probably from the shear (below Tt) to the diffusion type of mechanism. At the temperatures above Tt, for constants A&apos; and B, a relationship of the type was obtained between H and T, Fig. 1. The nature of the equation, where R is gas constant, suggests the possibility of a thermally activated mechanism of deformation above Tt. The constant B&apos; may hence be defined as the apparent activation energy of indentation. The B&apos; values of various alloys are shown in Table I. A plot of B vs B&apos; gives a curvilinear relation shown in Fig. 2. The indentation-creep data for H-13 alloy steel is shown in Fig. 3. At 71" and 500°F, the creep initially follows the logarithmic time law. However, the indentation size stabilizes after 7 sec at 71°F, and after 10 sec at 500°F. Further increase in loading time has no effect on indentation size. The creep of 1000° and 1200°F follows the logarithmic time law for the first 1000 sec, after which the

Jan 1, 1964

By F. Seitz

STAFF: Editor, Gerhard Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Managing Editor, James J. Burke THE METALLURGICAL SOCIETY: John Chipman, President; W. R. Hibbard, Jr., Post-President; C. C. Long, Vice-President; T. D. Jones, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: R. Maddin, Chairman; Dennis Carney, J. C. Fulton, J. H. Hollomon, T. B. King, C. C. Long, W. 0. Philbrook, J. D. Sullivan, David Swan, and F.L. Vogel. Review and selection of manuscripts is under the supervisian of the following Publications Committees: Extractive Metallurgy D ivis ion: T. 0. King, Chairman; S. J. Dick inson, R. P. Hermsdorf, R. Schuhmann, Jr., and H. H. Kel logg. Institute of Metals Division: F. L. Vogel, Choirmon; R. L. Smith, Vice Chairman; R.W. Balluffi, J. H. Bachtold, A Servi, C.D.Graham, Jr., C. G. Goetzel, F. E. Joumot, Jr., G. E. Pellissier, Paul Gordon, Jock Washburn, Harold Margol in, A. U. Seybolt, I. R. Kromer, R. A. Meussner, R. W. Guard, M. Harmon, J. N. Hobstetter, Dean Starr, P. Shewmon, R. Gordon, J. 0. Betterton, and E. Morgan. Iron and Steel Division: W. 0. Philbrook, Chairman; F. C. Langenberg, C. W. Sherman, J. Wagstaff, and E. J. Whittenberger. Published bimonthly by the American lnstitute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AlME members. Single copies, $4.00, single copies foreign, $5.00. The AlME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1959 by the Americon Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York ... Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . .Second class postage paid at New York, N. Y. , ond Ann Arbor, Mich. Volume 215, Number 3

Jan 1, 1960

By J. Chipman, G. G. Hatch

One of the important functions of the iron blast furnace is the desulphur-ization of pig iron before it enters the steelmaking furnaces. However, the increasing concentrations of sulphur in the metallurgical coke, source of approximately 90 pct of the sulphur present in the blast furnace charge, and demands for higher rates of production within recent years have increased the need for greater desulphurization within the iron blast furnace. Furnace operators are beginning to look for desulphurizing agents other than blast furnace slag to accomplish the desired degree of desulphurization. A considerable amount of work has been done on desulphurization outside the furnace with soda ash, calcium carbide and various synthetic slags. Whether the desulphurization of pig iron is accomplished wholly inside the furnace or partly inside and the remainder outside, will be determined by the economics involved. Regardless of which is the case, it is believed that it is necessary to have a better understanding of the physical chemistry of desulphurization by blast furnace slags. To this end, it is the object of the present investigation to attempt what is believed to be the first equilibrium study of the distribution of sulphur between liquid pig iron and a wide range of blast furnace slag compositions. Review of Literature There is a considerable amount of information in the literature concerning the desulphurizing power of iron blast furnace slags, the solubility of various sulphides in the slags, and the effect on desulphurization of temperature, of elements dissolved in the liquid iron, and of viscosity. However, there is nothing to indicate that the equilibrium distribution of sulphur between liquid iron saturated with carbon and iron blast furnace slags has been studied experimentally. Wentrupl has made probably the most detailed study of the desulphurization of pig iron to date. He considered that there are three distinct aspects involved, namely: 1. Desulphurization within the blast furnace (by lime and manganese). 2. Subsequent desulphurization by manganese. 3. The effect of subsidiary reactions on the desulphurization by manganese. The experimental work carried out by Wentrup was devoted mainly to obtaining a better understanding of how desulphurization by manganese was accomplished in the mixer and the ladle. Particular attention was given to the part played by carbon, silicon, and phosphorus associated with manganese in the iron, and the effect of temperature on desulphurization. The experimental results indicated that desulphurization by manganese is purely a process of crystallization of manganese sulphide. The addition of silicon to iron melts containing 3.5 pct carbon and less than 0.5 pct manganese had no noticeable effect on desulphurization, but with 1-2 pct manganese the silicon additions improved the desulphurization. Additions of phosphorus also resulted in improved desulphurizati011 by manganese, but the effect was not as marked as in the case of silicon. It was also found that desulphurization by manganese was further improved by lowering the temperature. In order to explain desulphurization inside the blast furnace, Wentrup considered the system iron, sulphur, calcium, oxygen, manganese. (silicon). The distribution of sulphur between the metal and slag was represented by the following equation: (SS) _ (S)Fe + (S)Ca + (S)Mn .... [S] = [s] [1] The parentheses and the brackets represent the equilibrium concentrations in weight per cent of the slag and metal constituents, respectively. Since FeS D (FeS) _ (FeS) (S)Fe LfeS - [FeS] [S] [2] (CaO) + S e (FeO) + (S)Ca _ (FeO)(S)Ca. (S)Ca _ (CaO) Kl = (CaO)[S] [S] ~K1(FeO) [3] Mn + S D (S)Mn (S)Mn (S)Mn K&apos; = [MnpT "1ST = *lIMnJ !4) Substitution of Eq 2, 3, and 4 into Eq 1 resulted in if = L- + *> (Sol + K^ (S) [51 Eq 5 was used to calcu1;lte -f^j and [S] at 1480°C for slags containing 30-50 pct lime, 0.1-2.5 pct iron oxide, 0-26 pct silica, 2 pct sulphur and iron analyzing 1.5 pct manganese. The value for LFaB at 1480°C was found to be equal to 4.5, based on the experimental work of Bardenheuer and Geller.2 The results of the calculations are shown in Table 1. Although the slags are hypothetical and do not represent the range of compositions found in ordinary blast furnace practice, the calculations indicate that lime is effective in controlling desulphurization only if the iron oxide and silica contents of the slag are kept low. Schenck3 did not claim K1 to be a true equilibrium constant, but an empirical value which varied with the silica content of the slag.

Jan 1, 1950

By B. C. Allen

Grain boundary grooving has been studied in chromium, molybdenum, and tungsten under a variety of conditions using high vacuum techniques and tantalum -gettered argon. The average surface free energy of solid chromium, and the chromium-liquid silver interface free energy were respectively found to be 2200 ± 250 and 500 i 130 ergs per sq cm from groove formation kinetics and estimates of pertinent volume difffusion coefficients. The results for chromium were unffected by variations in interstitial content ranging from 0.003 to 0.09 pct C, or 0.003 to 0.03 pct O. Surface diffusion is the primary mechanism of groove formation in chromium under 1 atm argon at 1200" to 140O°C, and is essentially unaffected by 0.003 to 0.09 pct C, 0.003 to 0.03 pct O , metastable nitrogen contents up to -0.01 pct, and up to 2 torr Ag vapor. At higher temperatures, the major mechanism is volume diffusion in argon or evaporation-condensation in stutic vacuum. Surface diffusion occurs in molybdenum at 0.5 to 0.96 and in tungsten at 0.5 to 0.9 of the absolute melting tempera -ture by a single mechanism, possibly by the migration of single adatoms or vacancies. Results were slightly affected by up to 23 tory Sn vapor, and in molybdenum were essentially unaffected by 0.5 Ti or carbon in the range 0.002 to 0.02 pct. Volume difffusion through the liquid is the mechanism of groove formation in chromium-liquid silver at 1200" to 1400°C and in molybdenum-, Mo-0.5Ti-, and tungsten-liquid tin at 1200" to 2000°C. The solid-liquid interface free energies involved were estimated from grooving kanetics. WHEN a grain boundary intersects a solid surface, a groove tends to form along the line of intersection at temperatures above about half the absolute melting point (0.5 TM). The groove progressively grows by preferential atomic migration either by diffusion or evaporation. Establishment of a groove angle occurs in accordance with the grain boundary and surface free energies involved. The motivation for groove formation is a reduction in the total surface free energy of the system. This study is a continuation of previous work on thermal grooving of chromium, molybdenum, and tungsten.&apos; The temperature ranges were extended, and the effect of metallic and interstitial impurities was evaluated. The results were such that certain interface free energies and surface self-diffusion coefficients were deduced from the grooving kinetics. EXPERIMENTAL WORK Materials and Preparation. As indicated in Table I, the 0.05-0.08-cm-thick chromium, molybdenum, and tungsten sheet used was nominally 99.99 pct after recrystallization. Two lots of molybdenum with about the same analysis, Mo-0.5Ti,* and tungsten were ob- *Alloy compsitions are expressed in weight percent . tained commercially. Extruded chromium rod,&apos; prepared from iodide process crystals, was warm rolled to sheet at 700°C. Sheet of three Cr-0 impurity alloys containing up to 0.03 pct 0 was prepared by warm rolling arc melted, extruded, and swaged rod. Two Cr-C impurity alloys containing up to 0.09 pct C were made by equilibrating unalloyed chromium with a known amount of CH4 for 24 hr at 1150°C in previously evacuated quartz capsules. Chromium containing nominally 0.015 and 0.06 pct N was similarly prepared by equilibration with NH3. The sheet was recrystallized to give a stable grain size about equal to the sheet thickness. Molybdenum and Mo-O.5Ti were recrystallized in a tantalum resistance furnace 1 hr at 1 x lo-5 torr at 2300" and 220O°C, respectively. Tungsten was similarly annealed for 1 hr at 2500°C. Chromium and its impurity alloys were outgassed at 1100°C and recrystallized 1 hr at 1700°C under 1 atm Ar. Except for nitrogen, the impurity content stayed roughly constant. Nitrogen in both alloys was reduced to <0.001 pct. In fact, over 80 pct of the added nitrogen was lost after outgassing at llOO°C and annealing sheet 1 hr at 1300°C in argon in the presence of tantalum. Such a rapid loss can be rationalized since -2 torr N are required for equilibrium with 0.04 pct N in solution,3 while the equilibrium pressure is ~10-5 torr over tantalum at 1300°C.4 The recrystallized sheet was cut into small coupons which were metallographically ground and polished on one side with a minimum of grain boundary relief. The surface roughness was on the order of 0.01 µ. The tin and silver used were nominally 99.999 spec-trographically pure. After being outgassed at 1100°C and equilibrated in a molybdenum crucible for 0.5 hr at 1800°C in argon, the tin contained 3 ppm 0, <0.3 ppm N, and 0.1 ppm H. Following outgassing at 900°C and equilibration in a chromium crucible 1 hr at 1400°C in argon, the gas content of the silver was 1 ppm O, <0.5 ppm N, and 0.3 ppm H. Grooving Under Argon or Vacuum. All specimens were placed in unsealed containers made from rod or sheet of the same alloy, thereby enabling the polished surface to achieve gas-solid equilibrium. The annealing fixtures are shown in Fig. 1. The specimen was placed in a resistance furnace with a tantalum or Ta-10W heating element plus tantalum fixtures or radiation shields. Chromium was outgassed at 1100°C, and molybdenum and tungsten were outgassed at 1900°C to 1 x l0-5 torr or at the grooving temperature, whichever was lower. In vacuum anneals, the specimen was then heated directly to the intended grooving temperature. In argon anneals, 99.996 Ar was admitted

Jan 1, 1970

THOSE NOT MARKED ARE MEMBERS; MARKED THUS t ARE ASSOCIATES. HEAVY-FACED TYPE SIGNIFIES HONORARY MEMBERSHIP. JUNIOR MEMBERS ARE MARKED II. THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION. AARONS, J. BOYD, Genl. Mgr., Chaffers G. M. Co., Boulder City, West. Australia. &apos;05 ABADIE, EMILE R., Min. Engr Box 291, Porterville, Tulare Co., Cal. &apos;76 ABBOTT, CLARENCE E., Genl. Supt., Iron Mines Div., 1405 Minnesota Ave., Bessemer, Ala. &apos;04 ABBOTT, J. W., Min. Engr., "St. Omer," 123 N. Grand Ave., Los Angeles, Cal. &apos;94 ABBOTT, Louis BENJAMIN, Chief Engr., Consolidation Coal Co., Elkhorn Div., Jenkins, Ky. &apos;15 ABBOTT, ROBERT R., Met. Engr., Peerless Motor Car Co., Cleveland, Ohio. &apos;12 ABE, ASAKA Yamagano G. M., Satsuma-Gori, Satsuma, Japan. &apos;14 || ABRAHAMS, A. I., Student 1391 Madison Ave., New York, N. Y. &apos;14 tACKER, E. O&apos;C., Met Bethlehem Steel Co., Bethlehem, Pa. &apos;86 ACKER, LOUIS K., JR., Min. Engr 565 Highland Place, Bellevue, Pa. &apos;08

Jan 1, 1917

By B. W. Dyer

IN 1924, the Crescent Eagle Oil Co., while drilling the salt section of the Paradox formation in Grand County, Utah, encountered a salt that did not appear to be sodium chloride. This salt was analyzed and showed the presence of potash minerals, both sylvite (KC1) and carnallite (KMgC12.6H20). Because of the high potash content of the sample, there was considerable speculation: (I) as to whether the hole had been salted, and (2), if not, the extent, richness, and the depth at which the deposit occurred. The discovery caused a large amount of activity in the area. During the next few years, 68 potash prospecting permits were issued by the Government, 24 under the Act of 1917 and 44 under the Act of Feb. 7, 1927, each including about four sections of land. Several holes, all shallow, were drilled for potash. A number of holes were drilled for oil into the salt horizon and the cuttings collected at the oil wells were examined petrographically and chemically. The shallow test holes were not sufficiently deep to reach the potash horizon and revealed nothing of value, but several of the oil test holes gave some indication of where potash might be found. LOCATION AND GEOLOGY OF DEPOSITS The potassium and magnesium salts have been found in various places from the Denver and Rio Grande Western Railroad tracks about seven miles west of Thompsons, in eastern Utah, to Cane Creek, a tributary of the Colorado Rivera distance north and south of about 35 miles. In this locality, there appear to be five separate deposits: the Crescent Eagle area, which is in T. 22 S., R. 19 E.; the Salt Valley area, in the vicinity of the north-south line of T. 23 S., between R. 20 E. and R. 21 E.; the Seven Mile area, in the eastern part of T. 25 S., R. 2o E.; the Cane Creek area, on the Colorado River, in T. 26 S. and T. 27 S., R. 2o E. and R. 21 E.; and the Salt Wash area, in T. 22 S. and T. 23 S., R. 16 E. and R. 17 E. (Fig. I.) The Crescent Eagle and Salt Valley areas are in the Salt Valley anticline, some of the wells being in the fault graben and others outside. Structurally, the Salt Valley anticline is very complex, and can be described in general terms as a northwesterly plunging collapsed anticline about 15 miles long. In the Crescent Eagle area, the valley graben is about 1 mile wide and the salt probably forms a plug, the apex of which is in the vicinity of the Crescent Eagle well. Owing to the complex structure, there has been every opportunity for flowage in the salt to cause local thinning or thickening of beds. The regular succession of formations in the general area* is: [Cretaceous Mancos Dakota Jurassic Morrison Summerville Entrada Carmel]

Jan 1, 1945

H. H. Kellogg (Columbia University)—The accurate measurements of the equilibrium gas ratios for the reaction: Pb(1) + H2S = PbS(c) + H2 [I] reported in this paper are a distinct contribution to the literature, and the authors are to be congratulated. I wish to comment, however, on the correlation of the data which is presented. The authors show a straight line correlation of log H2S/H2 vs 1/T, Fig. 1, and are satisfied with this for calculation of ?Fo even when extrapolated to low temperature (427 °C). Heat capacity data for the constituents of this reaction are available (at least to 900°K), however, and ACP for reaction [I] is finite and positive in the temperature range studied. Simplification of the heat capacity equations yields: ?CP= 2.71 + 1.65 x 10-3T (298°-900°K) This positive value of ?CP should result in a small but noticeable curvature of a plot of log K vs 1/T. That the experimental data fail to show such a curvature may be traced to another oversimplification of the author&apos;s treatment of their data. They assume that the activity of liquid lead is unity for all temperatures, so that

Jan 1, 1961

By S. E. Haszko

SEVERAL new XGa2 intermetallic compounds, Table 1, where X is a rare earth, having the AlB, structure were prepared as part of a continuing study of the magnetic and structural properties of rare-earth alloys.&apos; In this note, the crystallographic results of these compounds are presented. Chart, Eq. 121 for the data in Fig. 1 can be adequately represented by The corresponding standard free-energy change is AF; = -4.576 T log K = -20,900 + 10.20T [5I At low nitrogen concentrations the ratio of mole fraction to weight percentage is a constant so that the mole fraction X of nitrogen is given by X = 0.0392 [%NJ. At low values of X, the activity and the concearation approach each other, hence K, = 0.0392 K,, where K, is expressed in terms of the mole fraction of nitrogen. Hence Eqs. [4]. and [5] become

Jan 1, 1962

By P. Chiotti, J. T. Mason

Metallographic, thermal, X-ray, and vapor-pressure data were employed in establishing the Ce-Zn phase diagram. Nine compounds and three eutectics were observed. The eutectic compositions in weight percent zinc and temperatures are 10 pct and 495"C, 37 pct and 795°C, and 56 pct and 810°C. Three of the compounds, CeZn, CeZnn, and CeZne.5, melt congru-ently at 825°, 87.505°, and 980°C, respectively; the other six compounds, CeZns, CeZns.67, CeZn4.5, CeZn5.25, CeZn,, and CeZnll, decompose peritectically at 820°, 840°, 870°, 885", 960°, and 795"C, respectively. The compound CeZn5.25 is an AB5 type with a small range of composition which lies on the zinc-rich side of the 1 to 5 stoichiometry. Zinc vapor-pressure data obtained by the dewpoint method were employed in calczilating the thermodynamic properties of both the liquid alloys and solid compounds. The data for the A critical review of the information available on the Ce-Zn system up to 1960 has been given by K. Gschneidner, Jr.&apos; Of particular interest is the work by J. schramm2 who investigated the region between 55 and 100 wt pct Zn and reported a CeZn,, compound which decomposes peritectically at 785"C, a CeZn, compound which melts congruently at 972"C, and five temperature horizontals at 79@, 817", 840", liquid alloys were fitted to the relation from which the relation was obtained by integration. In these relations F XS is the excess partial molal free energy, N is atom fraction, and the constants c and d have the values c = (-22,000 + 7.0T) and d = 6171,000 + 74.0T). Relations for the standard free energy of formation for the solid compounds were derived from the data. At 973°K the enthalpy in kilocalories per gram-atom z)aries from —11.3 for CeZnz to —8.21 for CeZn~l and the free energy in the same units varies from —7.1 joy CeZn, to -3.82 for CeZn11. and 942°C in the region between 55 and 75 wt pct Zn. No attempt was made to identify other features of the system. I. Johnson and R. yonko3 used a fused-salt cell to measure the electromotive force between pure cerium and an alloy consisting of zinc-rich liquid in equilibrium with CeZnll. Solubility data for cerium in zinc has been reported by J. Knighton et u1 .4 Johnson and Yonko give the following equa-. tions for the mole fraction of cerium in zinc and the standard free energy of formation of CeZnll:

Jan 1, 1965

By L. F. Tedsen, A. E. Flanigan, J. E. Dorn

SINCE aluminum-alloy sheet may be used occasionally at moderately elevated temperatures, the effects of temperature en the mechanical properties are of interest. Recently the short-time tensile properties of several high-strength materials have been studied at temperatures up to 375°F. This paper deals with stress-rupture and [ ] creep properties at the same temperatures. The work was done at the University of California as a portion of the project NRC-548. It was financed by the War Production Board and was supervised by the Office of Production Research and Development. This paper has been released for publication by the latter agency. The following materials were studied, all in the form of 0.040-in. sheet: Alclad 24S-T Alclad 24S-T8I Alclad 24S-T86 Alclad 75S-T R301-T (clad) [ ] Specimens were loaded in tension in the cross-grain direction. Testing temperatures included 94°F., 211°F., 300°F., and 375°F. Stress levels were selected to cause rupture in times ranging from several minutes to boo hr. In each test the following data were obtained: (I) fracture time, (2) elongation at fracture, (3) the complete strain-versus-time curve (creep curve), (4) creep rate (defined in a later section). MATERIALS Materials for specimens were obtained from the manufacturers&apos; commercial

Jan 1, 1946

By Frank Foote, Eric R. Jette

In a recent article,1 the authors reported the results of an X-ray investigation on the range of solid solutions that occurs in the iron-oxygen system in the vicinity of the compound FeO, which frequently is called "wüstite." The object of that investigation was primarily to study the unusual type of solid solution phenomena involved in this range. Briefly summarized the results were: 1. The NaCl type of lattice found by earlier workers was confirmed. 2. The lattice dimensions decrease rapidly with decrease in iron content. 3. No alloy that was a homogeneous single phase was ever found at compositions beyond 76.80 per cent Fe, while the theoretical iron content of FeO is 77.73 per cent Fe. 4. Measurements of the densities and lattice constants led to the conclusion that the form of substitution was complex, an FeO group being replaced by oxygen. Such a substitution, of course, is equivalent to removing an iron atom (or ion). The ideal unit cell of FeO can be considered as containing four groups of FeO and, thus, when this type of substitution takes place, there remain in the unit cell three FeO groups and an oxygen, or a total of seven atoms with a gross formula of Fe3O4 instead of the original Fe4O4. 5. This was the only interpretation that would fit the experimental results and at the same time be consistent with (a) the previously determined fact that the FeO lattice is ionic (i, e., consists of Fe++ and O? ions) and (b) the chemical fact that as the oxygen content of the substance increases, ferrous iron becomes oxidized to ferric iron. The experimental results of this investigation are included in Fig. 1. The purpose of the present investigation was to determine the limits of this homogeneity range by means of the X-ray structure analysis. This method has been applied frequently to the study of solid solutions by Westgren and his coworkers as well as by other investigators. The principle is simple: if the change in lattice constant with composition is

Jan 1, 1933

By N. A. Gokcen, John Chipman

SILICON is the most commonly used deoxidizer and an important alloying element in steelmak-ing; hence a detailed study of this element in liquid iron containing oxygen is of considerable interest. The equilibrium between silicon and oxygen in liquid iron has been studied by a number of investigators but generally with inconclusive or incomplete results. The variation of the activity coefficients of silicon and oxygen with composition is entirely unknown. Published investigations deal with the reaction of dissolved oxygen with silicon in liquid iron and the results are expressed in terms of a deoxidation product. For consistency and convenience in comparison of the published information, the deoxidation product as referred to the following reaction is expressed in terms of the percentage by weight of silicon and oxygen in the melt in equilibrium with solid silica: SiO (s) = Si + 2 O; K&apos;l = [% Si] [% 012 [I] Theoretical attempts to calculate the deoxidation constant for silicon in liquid iron from the free energies of various reactions yielded results which were invariably lower than the experimental values. Thus, the deoxidation "constants" calculated by McCance,1,2 Feild,3 Schenck, and Chipman were of the order of 10, which is below the experimental values by a factor of more than 10. Experiments of Herty and coworkers" in the laboratory and steel plant resulted in an average deoxidation constant of 0.82x10 &apos; at about 1600°C. The technique employed in their investigation was crude and the reported temperature was quite uncertain. The concentration of silicon was obtained by subtracting silicon in the inclusions from the total. Since at least some of the inclusions resulting from chilling must represent a fraction of the silicon in solution at high temperatures, such a subtraction is not justifiable. Results of Schenck4 for K&apos;1 from acid open-hearth plant data yielded a value of 2.8x10-5, which was later revised as 1.24x10 at 1600°C. Similarly Schenck and Bruggemann7 obtained 1.76x10-5 at 1600OC. The discrepancies and errors involved in the acid open-hearth plant data as compared with the results of more reliable laboratory techniques were attributed by these authors to the lack of equilibrium and the impurities in liquid metal and slag, and are sufficiently discussed elsewhere." Korber and Oelsen" investigated the relation between dissolved oxygen and silicon in liquid iron covered with silica-saturated slags containing varying concentrations of MnO and FeO. The deoxidation products obtained by their method scatter considerably, and their chosen average values of 1.34x10, 3.6x10-5, and 10.6x10-5 1550°, 1600°, and 1650°C, respectively, represent the best experimental results which were available until quite recently. Darken&apos;s10 plant data from a steel bath agree approximately with their data at 1575° to 1625°C. Zapffe and Sims" investigated the reaction of H2O and H2 with liquid iron containing less than 1 pct Si and obtained deoxidation products varying by a factor of more than 20. Inadequate gas-metal contact and lack of stirring in the metal bath should require a longer period of time than the 1 to 5.5 hr which they allowed for the attainment of equilibrium. Furthermore, their oxygen analyses were incomplete and irregular and confined to a few unsatisfactory preliminary samples. Their results did indeed indicate that the activity coefficient of oxygen is decreased by the presence of silicon, although they made no such simple statement. They chose to attempt to account for their anomalous data by the unlikely hypothesis that SiO is dissolved in the melt. Hilty and Crafts" investigated the reaction of liquid iron with acid slags under an atmosphere of argon, making careful determinations of silicon and oxygen contents at several temperatures. Despite erroneous interpretation of the data at very low silicon concentrations, their data represent the most dependable information on this equilibrium that has been published. In the range 0.1 to 1.0 pct Si, their data yield the following values for the deoxidation product: 1.6x10-5, 3.0x10- &apos;, and 5.3x10 at 1550°, 1600°, and 1650°C, respectively. The purpose of the work described herein was to study the equilibrium represented by eq 1 as well as the following reactions, all in the presence of solid silica: SiO2 (s) + 2H2 (g) = Si + 2H2O (g);

Jan 1, 1953

By C. A. Stewart

PAGE. I. Introduction............ 241 II. Location. TopoGRaphy. and History....... 243 III. DescRiption of the Rocks......... 245 1. Altered Sediments.......... 245 2. Alaskite........... 246 3. Alaskite.Porphyry.....255 4. Quartz Dikes........... 257 5. Biotite.Granite.......... 256 6. Quartz.Porphyryl......... 260 7. Andesite........... 262 8. Miscellaneous Dikes......... 263 IV. Age oF the Rocks and Comparison with other Localities.. 263 V. AlteRation............ 265 1. Sericitization........... 265 2. Silicification........... 266 VI. StRuctuRes........267 1. Dip of the Limestone......... 267 2. Faulting........... 267 VII. Contact - metamorhism,.......... 269 1. Endomorphism.......... 269 2. Exomorphism......... 271 Recrystallization and Loss of Color...... 271 New ,Minerals.......... 272 Addition of Material........ 274 Volume.Changes.... 276 Locus of Metamorhism........ 277 Method of Precipitation.........278 VIII. ORe-Deposits............ 278 1. Contact-Metamorphic Copper.Ores,..... 279 General..........279 Shape and Distribution........ 279 Minerals........... 281 Secondary Enrichment........ 282 2. Disseminated Copper.Ores........ 283 3. Origin of the Copper.Orcs........ 284 4. Lead-Silver Ores.......... 287 IX. Bibliography............ 288

Jan 1, 1913