Search Documents

By Don B. Shupe, John K. Berry

The handling and disposal of mine water is a much larger problem than is apparent at first glance. Many more tons of water are removed from underground coal mines in the United States each year than tons of coal. In the old anthracite region of Pennsylvania the average was around 32.7 t (36 st) of water for each ton of coal produced, while bituminous mines average about 4.5 or 5.4 t (5 or 6 st). Water encountered in the mines may come from several different sources. In mines with light cover and without a firm solid roof, rain may seep directly into the workings. This is also true of deeper mines where pillar falls have broken the roof to the surface. The top under creek beds is generally faulty and broken and water comes through the roof at this point. Deeper mines are frequently overlain by water-bearing strata and pillar breaks and faulty top can admit water, while places running to the dip often accumulate water which comes up through the bottom. In all cases, except where passing under a year-round stream, the amount of water made is usually pretty closely connected with the weather-more water during the rainy season, less in the dry, although the deeper a nine is, the longer it is before changes in rainfall are felt. Another source of water, not connected with seasonal changes, is old water, accumulated over a period of time in abandoned workings of the mine, or from flooded adjacent mines. Here the water filters through the coal, the parting, or comes up through cracks in the bottom. Similarly, core holes, drilled to prospect the property, can be a source of unexpected water and modern safety requirements for dust-allaying water at the working faces can turn a pleasant working area into a soggy mess over the weekend if the system is not properly maintained and operated. Why water must be disposed of is obvious. If allowed to accumulate, sooner or later the mine will fill up, or at least it will become "roofed" in low places, blocking ventilation and traffic. It must be controlled long before it reaches this stage. Water standing in the working faces is

Jan 1, 1981

By Don B. Shupe, John K. Berry

The handling and disposal of mine water is a much larger problem than is apparent at first glance. Many more tons of water are removed from underground coal mines in the United States each year than tons of coal. In the old anthracite region of Pennsylvania the average was around 32.7 t (36 st) of water for each ton of coal produced, while bituminous mines average about 4.5 or 5.4 t (5 or 6 st). Water encountered in the mines may come from several different sources. In mines with light cover and without a firm solid roof, rain may seep directly into the workings. This is also true of deeper mines where pillar falls have broken the roof to the surface. The top under creek beds is generally faulty and broken and water comes through the roof at this point. Deeper mines are frequently overlain by water-bearing strata and pillar breaks and faulty top can admit water, while places running to the dip often accumulate water which comes up through the bottom. In all cases, except where passing under a year-round stream, the amount of water made is usually pretty closely connected with the weather-more water during the rainy season, less in the dry, although the deeper a mine is, the longer it is before changes in rainfall are felt. Another source of water, not connected with seasonal changes, is old water, accumulated over a period of time in abandoned workings of the mine, or from flooded adjacent mines. Here the water filters through the coal, the parting, or comes up through cracks in the bottom. Similarly, core holes, drilled to prospect the property, can be a source of unexpected water and modern safety requirements for dust-allaying water at the working faces can turn a pleasant working area into a soggy mess over the weekend if the system is not properly maintained and operated. Why water must be disposed of is obvious. If allowed to accumulate, sooner or later the mine will fill up, or at least it will become "roofed" in low places, blocking ventilation and traffic. It must be controlled long before it reaches this stage. Water standing in the working faces is

Jan 1, 1981

By James O. Elton

This paper covers, besides laboratory work, a study of actual operation at the Washoe Smelter over a considerable period of time, together with the results of a visit to the Midvale plant of the United States Smelting & Refining Co., near Salt Lake. For the latter privilege, as well as permission to publish the resulting data herein given, I am indebted to George W. Heintz, General Manager of the Midvale plant, and here take pleasure in expressing my appreciation for the many courtesies extended to me by Mr. Heintz and members of the technical staff at the smelter. Almost all of the world's supply of arsenic is recovered as a byproduct in the smelting of other metals. It is seen 'on the market in various forms, the most common being arsenic trioxide, the " white arsenic " of commerce, which is sold as a heavy white powder, or in white, glassy, translucent masses. The trioxide is used in the manufacture of pigment, glass, and insecticides. About 50 per cent. of the domestic consumption is supplied by imports. Statistics of Arsenic Trioxide in United States.' Production. Consumption. Price Per Pound. Year. Tons. Tons. Cents. 1907..........1.010 5.471 5 1908,.........1,302 6,098 33/4 1909,.........1,007 4,600 2 7/8 1910,.........1,526 5,428 2 1/2 1911,.........3,081 6,539 2 1912,2........ 2,926 Closed at 4 7/8 Arsenic occurs in combitlation with sulphur and the metals in a large number of minerals. It is present in small amounts in many ores. In the roasting and smelting furnaces many of its compounds break down, liberating arsenic trioxide, which is volatilized and carried by the gases into the flue system, where a part is condensed and settles with the flue dust.

Jan 1, 1914

By D. K. Deardorff, H. Kato

THE transformation temperature of hafnium from hcp to bcc is 1750° + 20 °C in contrast to previously published values by Duwez and fast2 which are believed inaccurate. The Bureau of Mines determined this value by measuring the temperatures at which a sudden decrease was observed in the electrical resistance of hafnium alloys containing up to 18 at. pct Zr, and then extrapolating the temperatures to 0 pct Zr. Duwez1 previously reported a transformation temperature of 1310°C, obtained by use of a rapid-cooling thermal-analysis technique. Later, Fast2 published a much higher value of 1950° 100°C based upon: a) his own determination of 1690°C for the beginning of the transformation range for hafnium containing 5.7 at. pct Zr, and b) his belief that lattice parameters reported3 for Duwez' hafnium indicated i contained 19 at. pct Zr and that the 1310°C value should be associated with that composition. Russell4 subsequently stated that Duwez and Fast probably were reporting their lattice parameters in different units and reassigned a value of 6.0 at. pct Zr to Duwez' hafnium. If this assumption were true, Duwez' hafnium was of approximately the same purity as Fast's, but his transformation value was considerably lower. The reason for this divergence is not known. Fast's value for hafnium containing 5.7 at. pct Zr agrees well with our data. McGeary5 determined a transformation value of 1660°C by metallographic examination of heat-treated specimens, but the zirconium content of his hafnium was not definitely established. The specimens used in this investigation were 1/8-in.-diam rods 6 1/2 in. long, fabricated by hot-swaging bars cut from arc-melted buttons. These buttons were melted from crystal bar hafnium and crystal bar zirconium. The chief impurity in the hafnium

Jan 1, 1960

By I. H. Pratt

The results of a study on the preparation of thin-film capacitor structures are discussed. The dietectric source material was quartz which was sputtered and deposited onto aluminum electrodes and counter-electroded to complete the metal-oxide-metal structures. This configuration was utilized to evaluate the dielectric, the device characteristics, and related process parameters. The effect of gas sputtering pressure, magnetic field strength, source-to-substrate distance, and power density on the rate of deposition is shown. Increased film thickness uniformity over a 3 by 3 in. area by optimum substrate positioning is indicated. Dielectric constant, dissipation factor, dielectric breakdown strength, insulation resistance, heat treatment, capacitance, and dissipation over the range 400 Hz to 5 MHz are reported. In the fabrication of silicon-integrated circuits, silicon dioxide has found use as a material suitable as a diffusion mask, for surface passivation of the silicon, and for protection of conductive films used for interconnections. Its use as a dielectric for thin-film capacitors in film hybrid circuits has been limited, to a degree, for lack of a compatible processing technique and because of its relatively low dielectric constant. With the recent advent of practical metal-oxide-semiconductor (MOS) field effect devices, the material is now being used to insulate the gate electrode from the conducting channel in the silicon. In this latter application, more stringent requirements have been imposed on .the oxide. A comprehensive resume of the use of silicon dioxide in integrated silicon device technology has been compiled including oxide film and bulk properties, method of oxide formations, and their applications.' A relatively new process to deposit SiO, and other dieIectrics is by rf sputtering, and the purpose of this paper is to describe the behavior of capacitors fabricated with a dielectric which has been sputtered from a quartz target and to indicate the relative effect of several of the process parameters on the film deposition. Work on rf sputtering of SiO2 and other dielectrics has been reported utilizing a triode type of sputtering system as described herein or a diode self-sustained glow discharge system. 2-8 SPUTTERING The process occurs during an electrical discharge in a gas plasma which provides the ions for acceleration to the target to produce the desired sputtering. The necessary plasma can be generated by a dc glow discharge through application of a high potential between two electrodes at approximately 2 to 10 x 10-2

Jan 1, 1969

By Clarence Zener

THE internal friction of nonferrous metals vibrating at low stress amplitudes has so far always been successfully interpreted in terms of inhomogeneities of one sort or another. Examples are the fluctuation of stress across a specimen vibrating transversely,1,2,3 the stress inhomogeneities due to the elastic anisotropy and partial random orientation of the individual crystallites,4,5 localized weak regions introduced by cold-working,6,7 grain boundaries and possibly twinning planes.8,9 Perfect single crystals are, by definition, homogeneous. Actual single crystals usually, perhaps always, contains some imperfections. The present investigation. was undertaken to determine whether the internal friction of single crystals may likewise be attributed to inhomogeneities. This study was made possible through the gift of a large single crystal of 70-30 alpha brass by H. L. Burghoff, of the Chase Brass and Copper Co. The specimen, ½ in. in diameter and 10 in. long, was similar to samples previously described by Mr. Burghoff.10 EXPERIMENTAL METHOD The experimental method used has previously been described in Institute papers.5,6,9 The measure of internal friction adopted here, 1/Q, is (1/p) X the logarithmic decrement, a measure used by some writers, and is also (1/2p) X the specific damping capacity, a measure used by other writers. In all measurements the stress level was kept so low that the measurements were independent of stress level. In all measurements in which the temperature was varied, observations were made as the specimen slowly cooled from its highest temperature. The specimen was vibrated transversely. Observations were made at the funda¬mental frequency and at the first overtone, of about 620 and 1710 cycles per second, respectively. No attempt was made to avoid acoustical losses. EXPERIMENTAL RESULTS The specimen was annealed for several hours at 450°C. The temperature dependence of the internal friction was then determined from room temperature to 400°C. As shown in Fig. 1, the internal friction increased by only a factor of 2 from room temperature to 300°C., then by a factor of l00 during the next 100° interval. These measurements are consistent with the view that the observed internal friction is the superposition of two distinct parts. One, dominant at room temperature, is nearly independent of temperature. This part may be accounted for by acoustical losses and by transverse thermal currents. It was not further investigated. The second part, when plotted in the manner of Fig. I, lies upon a straight line. Therefore it has a heat of activation H; i.e., it varies with temperature as Internal friction e~H/RT [I]

Jan 1, 1942

By J. M. Smith, G. P. Willhite, J. S. Dranoff

Heat transfer rates were measured in sandstones with flow of gases perpendicular to the direction of energy transfer. Effective thermal conductivities ker ranged from 0.7 to 1.7 Btu/(br)(ft)(°F). The contribution of the solid phase appeared to be the most important in these consolidated materials, although the thermal conductivity of the gas had some effect. The velocity of the gas through the pores of the sandstones had no influence upon ker up to values of 168 lb/(br) (sq ft) in agreement with data obtained for unconsolidated beds of glass beads. The present results indicated that gas mixing, and hence heat transfer by convection in the pores, is less for perpendicular transfer of energy than when fluid flow and energy transfer are in the same direction. HEAT TRANSFER PERPENDICULAR TO FLUID FLOW IN POROUS ROCKS Heat transfer in porous media with pore sizes in the micron range depends upon the fluid in the pores and the geometry of the solid phase. The best characterized system is a bed of solid spherical particles. Heat transfer in this system has been studied extensive1y (Ref. 8 summarizes the literature up to 1959) when the pores contain stagnant fluid. When the fluid is in motion the directions of flow and energy transfer have an effect on the heat transfer rates, as demonstrated by comparing the work of Willhite, et al l3 for perpendicular flow and that of Kunii and Smith9 for parallel flow of energy and fluid. For perpendicular flow, no increase in effective thermal conductivity ke was noted up to mass velocities G of 77 lb/(hr) (sq ft). In contrast, for parallel flow ke, increased with G in the same range of flow rates. These higher values of ke in the direction of flow also have been observed3,4,10 in beds of larger particles, 0.1- to 0.5-in. diameter. For beds of consolidated materials, such as porous rocks, data are not available for these compar- isons, although Adivarahan1 reported results for the parallel case. Hence the primary objective of this work was to measure ke values for perpendicular flow of fluid and energy in porous rocks. Of interest also was the variation in effective conductivity with fluid velocity. APPARATUS AND PROCEDURE In the experimental method, a constant heat flux was applied to the inner surface of an annular section of the porous rock. By cooling the outer wall, a temperature gradient through the annular sample was established and measured with thermocouples placed within the sample at various radial positions, and at three elevations (A,B.C). The location of the 2-in. O.D., 3.75-in. long sample in the apparatus is shown in Fig. 1. Fluid entered the bottom (1) of the 3-in. I.D. (approximate) steel shell, flowed upwards through the sample and out at the top (3). pressure taps (2,4) were used to check the permeability of the sample. The energy flowed radially from the centrally-located electric heater through the sample and was absorbed in the water-cooled jacket. The samples studied were naturally occurring sandstones from different locations with the properties given in Table 1. These materials are identical with those used by Adivarahan 1 for the parallel flow of energy and fluid. Prior to use they were refluxed with toluene to remove hydrocarbons and leached with distilled water to remove soluble salts. Each sample was visually examined and discarded if large nonhomogeneities, such as cracks or stone particles, were noted. Eight copper-constantan thermocouples were inserted in holes drilled radially into the sample with

By Robert A. Rapp, Ronald L. Pastorek

Solid-state electrochemical measurements by three alternative experimental procedures were made with the cell FeO, Fe3O4 |Zro.85Cao.15O1.85 |Cu| Zr0.85CaO.15O1.85 | FeO, Fe304 to establish the solubility and diffusivity of oxygen in solid copper in the temperature range 800" to 1030°C. The solubility of oxygen in solid copper and the diflusivity of oxygen in solid copper Dgu = 1.7 X 10-2 exp(-16,000/RT) Cm2/sec were determined and confirmed in alternative experiments. The enthalpy of solution of oxygen in solid copper equals —10,000 cal per mole; the partial excess entropy of the oxygen atoms in the Cu-O dilute solution is approximately the same as that found for interstitial atoms in other metals. The diffusivity of oxygen in solid copper is consistent with that expected for an interstitial atom. RELIABLE values for the saturation solubility N(s) and diffusivity DO of oxygen in solid copper have not been unambiguously established in the literature. Following three early determinations by others,1"3 Rhines and Mathewson4 reported that the solubility of oxygen in solid copper increased from 0.007 at. pct 0 at 600°C to about 0.015 pct at 1050°C. Phillips and skinner,, using essentiially the same analytical procedure, reported that the solid solubility increases from 0.0018 at. pct 0 at 550°C to about 0.0075 pct at 1050OC. The only previous value for the diffusivity of oxygen in solid copper was reported by Ransley.6 Ransley deoxidized Cu-Cu2O alloys in an atmosphere of carbon monoxide gas to yield a solubility-diffusivity product. He used the solubility data of Rhines and Mathewson to calculate the diffusivity values. Another method for obtaining the solubility-diffusivity product (N(s) DO) is by measuring the widths of internal-oxidation zones in copper alloys as reported by Verfurth and Rapp.7 However, the calculated N(S)Do products depend upon the alloy content of the specimen, so that the internal oxidation of copper alloys does not follow ideal internal oxidation kinetics. As a result, unequivocal values for the N(s) DO product were not obtained by this procedure. A solid-state coulometric titration technique similar to that employed in this work was introduced by C. Wagner8 to study the dependence on silver activity of the Ag/S ratio in silver sulfide in the temperature range of 160" to 300°C. Similar experiments have been carried out by C. Wagner and co-workers9-11 to study the stoichiometry range of silver and copper tellurides, cuprous sulfide, and cuprous selenide. Numerous authors have carried out electrochemical measurements with a solid oxygen-ion-conducting electrolyte to determine the solubility and/or diffusivity of dissolved oxygen in several liquid metals.12-l6 Rickert and Steiner17,18 have used solid-state electrochemical measurements to determine the diffusivity of oxygen in solid silver from 760" to 900°C. Two different cell geometries were used. In the cell of linear geometry Fe, FeO | ZrO2 + (CaO) | Ag + [0 (dissolved)] [1] oxygen diffused from the interior of the silver electrode to the silver/electrolyte interface where the oxygen activity had been lowered from a fixed initial value to practically zero by the application of voltage to the cell. The diffusivity of oxygen in solid silver was determined from the solution of the diffusion equation and the time dependence of the cell current. However, this determination of the diffusion coefficient depended upon a knowledge of the solubility of oxygen in solid silver. A cylindrical geometry was used for the cell Pt, O2(Po2 = 0.21 atm) | ZrO2 + (CaO) | Ag + [0 (dissolved)] [II] which also allowed the diffusivity of oxygen in solid silver to be determined. These values were in agreement with other available data.l9 Recently, Raleigh20,21 used a method involving the measurement of diffusion-limited currents in a cell involving the AgBr solid electrolyte to determine the diffusion coefficient of silver in Ag-Au alloys at 400°C. Diffusivity values on the order of l0-14 sq cm per sec were measured in the alloy composition range 10 to 60 at. pct Ag in a single experiment. From numerous electrical conductivity and galvanic cell measurements,9'22"26 the solid solution Zr0.85 Ca0.15 O1.85 has been established as an electrolyte with predominant oxygen ion conduction over a wide range of intermediate and high oxygen activities. For interrelating the thermodynamics and the kinetics of the dissolution of oxygen in solid copper in this investigation, a galvanic cell was constructed with FeO-Fe3O4 as the reversible reference electrode, the Zr0.85Ca0.15 O1.85 electrolyte, and a pure copper specimen under-saturated in oxygen as the other electrode. THEORETICAL ANALYSIS Three variations of a high-temperature electrochemical technique were used in this study to provide two determinations each of the solubility and diffusivity

Jan 1, 1970

By Glenn C. Waterman, Scott Hazen

3.1-1. Purpose. Development drilling is directed towards determining the grade, volume, and three-dimensional outline of a mineralized zone previously located by exploration. It is distinguished from exploration or reconnaissance drilling, which has as an objective the discovery of new mineralized areas. A development drilling and bulk sampling program should furnish the following information: 1. Geology of the mineralized zone. 2. Quantitative data on grade and tons of material within pertinent cutoff limits. 3. Physical size and shape of the deposit. Areas underlain by waste as well as ore. 4. Mineralogica1 and metallurgical characteristics of the ore. 5. I1hysical characteristics of the ore. 6. Hulk samples for metallurgical testing and grade check. 7. Data on other factors that could affect mining operations, such as ground water, ground conditions, etc. 3.1-2. Procedures. There are numerous methods and techniques that are used to acquire pertinent data on a potential ore deposit. The total cost and accuracy of a development program depends on significant evaluation of the geology, proper selection of a drilling method, thorough analysis of sample data, and accurate evaluation of all the information. Knowledge of the geology of the mineral deposit is important in planning the development testing program and in evaluating the data obtained from such a program. Exploration work usually provides some significant information on the general size, shape, thickness, grade, and geology of the deposit. In some cases no further data are needed; in many cases geological complexities suggested by the preliminary work require further geological study. Of considerable importance may be the following:

Jan 1, 1968

By AIME AIME

TWO weeks ago the writer was lunching in the Engineers` Club in New York with a man who has perhaps the widest acquaintance among engineers of anyone in the country a member of another of the Founder engineering societies. "By the way," lie asked. "who have they nominated for your next president."' "Doctor Becket," I told him- "Oh. that's line," he replied, in a heartfelt tone that rang with sincerity. "I have come in contact with him occasionally and he is just the right type.' And that is the way Dr. Frederick M. Becket impresses everybody. The right type. Most Institute members of the western group of hard-rock minors do not know him, but then they meet him in his swing around the circle next year they will not require a long acquaintance to sense his kindly and outstanding personality, to realize that he is a gentleman in the bet meaning o1 that word, a man of wide sympathies and interests.

Jan 1, 1932

By W. H. Bassett, J. C. Bradley

In considering the effects of reducing gases on hot solid copper the following conclusions have been reached. (I) Depth of deoxidation of copper heated in reducing gas is grealer the smaller the amount of cuprous oxide originally present in the copper, the range studied being from 0.015 to 0.136 per cent. oxygen. It is suggested that the reason for this diflerence in depth of deoxidation is thai, when the copper is low in cuprous oxide, the reducing gas is diluted less by the gas that is formed in the reaction than when the copper is high in cuprous oxide; and the greater the concentration of the reducing gas the deeper the deoxidation. (2) The rate of deoxidation is much more rapid at the beginning of exposure than at the end, a condition especially noticeable at temperatures around 900" C.; that is, deoxidaion is retarded as the depth penetrated by the reducing gas increases. (3) Within the accuracy of the experiments arsenic in copper up to 0.5 per cent. has no tendency to increase or decrease the action of a reducing gas on the cuprous oxide presenx in the copper. In 1912 pieces of 0.365-in. hard copper rod 1/2 in. long were heated in a porcelain tube in an electric furnace, while illuminating gas was passed through. An approximate analysis of this gas is: Hydrogen 38 per cent., carbon monoxide 30 per cent., illuminants 13 per cent., methane 10 per cent., ethane 3 per cent., carbon dioxide 3 per cent., nitrogen 2 per cent., oxygen 0.4 per cent. After heating for various lengths of time at various temperatures, samples were quenched

Jan 1, 1926

By R. B. Adair, J. S. Browning

The laboratory batch and continuous flotation pilot plant tests demonstrated the technical feasibility of recovering high grade mica concentrates from weathered mica pegmatite ores of Alabama and Georgia. The research indicated that combinations of anionic and cationic collectors may be used effectively for flotation of fine size mica from weathered pegmatite ores. In continuous tests, concentrates containing 98.5% mica were obtained from the Georgia pegmatite ore; the Alabama pegmatite ore concentrates contained 98.4% mica. The recoveries were 91 and 89% respectively. INTRODUCTION The principal uses of fine ground mica are as a filler in wallboard joint cement, as a filler and surface coating for roofing, as an ingredient in paints, and in oil well drilling mud. The mineral has other uses in the manufacture of rubber, wallpaper, plastics, welding rods, electric insulation, house insulation, and textiles, and as an annealing agent in metal treatment. In recent years, more than 99% of the domestic mica produced has been scrap and flake mica (mica which does not meet specifications for sheet mica and is used for producing fine ground mica). There has been a continued increase in mica production for several years, the 1963 production of scrap and flake mica totaling 117,251 tons.1 Ground mica is obtained primarily by crushing and milling pegmatites and schists. To a lesser extent, mica is produced as a byproduct of kaolin washing and feldspar and spodumene flotation operations. The processes used in recovering mica by crushing and milling pegmatites are generally simple, consisting of various combinations of alternate roll crushers and trommel screens that separate the mica and gangue at screen sizes coarser than 6-mesh. As these processes are designed to recover only coarse mica, high losses in the plant rejects are common. Large tonnages of tailings from the crushing and screening plants have been accumulated in a number of areas. Methods for treating such products were developed by the Bureau of Mines in 1941,2 but have not been generally applied. More recently, mica flotation research has been completed and published by the Bureau of Mines.3 These methods required complete removal of 150- to 200-mesh materials from the flotation feed with consequent fine mica losses. Later, the Bureau of. Mines investigated methods for-recovering fine size mica from pegmatite ores after desliming sufficiently to remove clay materials, but not so drastically as to remove the fine sands. This report summarizes the results of these studies. The process developed was effective on pegmatite ores from two locations and should be applicable to the commercial treatment of other mica-bearing pegmatite ores and fine rejects that have been accumulated at various mica-milling operations. DESCRIPTION OF ORES The ores used in the investigation were obtained from the Dixie Mines, Inc., Heflin, Alabama, and the Ruberoid Corporation, Hartwell, Georgia. The sample from Alabama contained muscovite and quartz, with a high percentage of clay, and minor amounts of biotite, kaolin, limonite and tourmaline. The mica in the ore was essentially all minus 4-mesh in size and was free of attached mineral grains. The Georgia sample contained muscovite and quartz, with minor amounts of biotite, kaolin, and limonite. The mica in the ore, which was essentially all minus 4-mesh, was liberated. Petrographic analyses of the two samples are given in Table I. THE ANIONIC-CATIONIC MICA FLOTATION METHOD Previous investigators2,3 have reported that complete desliming of mica ores at 150- to 200-mesh was required prior to flotation with cationic collectors to obtain satisfactory selective separation of the mica from the other mineral components. Numerous tests were made at the Tuscaloosa Metallurgy Research Center to determine if some reagent combination could be used to selectively float finer size mica without complete desliming. The investigation led to development of a process using a simple reagent com-

Jan 1, 1967

By Langtry E. Lynd

The predominant tonnage use of titanium is as a white pigment, in the form of rutile or anatase, which are allotropic modifications of titanium dioxide. Because of its whiteness, high refractive index and resulting light scattering ability, titanium dioxide is unequaled as a white pigment for paints, paper, rubber, and a wide variety of other materials. Consumption of titanium dioxide pigments for these uses has been rising steadily for many years, United States consumption in 1956 amounting to about 486,000 tons, worth $250,000,000. Production was off a little in 1957 and 1958. An outstanding development in the titanium field in recent years is the expansion of titanium metal production. Virtually nonexistent before 1948, United States production of pure titanium metal sponge reached a high in 1957 of about 17,200 tons, worth about $77,000,000. United States titanium sponge metal production in 1958 was cut back to about 4,600 tons because of reductions in military requirements. Another major use of titanium, in the form of the mineral, rutile, is for welding rod coatings. United States consumption of rutile for this purpose in 1958 amounted to about 11,000 tons, worth $1,100,000. Titanium-Bearing Minerals Although several minerals contain titanium as a major constituent, only a few of these occur in sufficient quantities and concentrations to be of commercial importance. These are ilmenite (FeTiO3), rutile (TiO2), and alteration products of ilmenite which have been referred to as weathered ilmenite, leucoxene, or arizonite. The other polymorphs of titanium dioxide, brookite and anatase, occur in a few deposits, of which only one has been of even minor importance. Considerable concentrations of titanite or sphene (CaTiSiO5) and perovskite (CaTiO3) are known, but do not compete with ilmenite and rutile deposits in grade or size. Rutile is very widely distributed as an accessory mineral in most rocks, but large deposits of commercial importance are rare. A few rock deposits have been worked for rutile but only one, in Virginia, is in operation (1959). Development of one in Mexico was discontinued recently. At present, the main sources of rutile are the beach and dune sands of Australia and Florida. A major use of rutile is for the manufacture of titanium tetrachloride, which is the intermediate compound universally used in titanium metal manufacture. Another main use of rutile is for welding rod coatings. Although the whiteness and brightness of titanium dioxide pigment is due to the high refractive index of rutile or anatase, natural rutile is too impure to be used directly as a white pigment, is too expensive to use for manufacturing pure oxide pigment, and is too scarce to provide the required tonnages. Instead, the cheaper, more abundant, mixed oxide of iron and titanium, ilmenite, which is readily decomposed by sulfuric acid, is used for manufacture of rutile and anatase pigments. Ilmenite is mined from both rock and sand deposits. Rock deposits contain ilmenite in massive or heavily disseminated form along with magnetite or hematite and are almost invariably associated with anorthositic and gabbroic rocks. Ilmenite also occurs as an accessory mineral in a great many igneous and metamorphic rock types. Concentrations of

Jan 1, 1960

By V 7. 0 / 300 dpi

WHEN the copper smelters were built, in Montana, all of the refractory products which were used in their construction were shipped in from Eastern factories. It was apparent that if a material suitable for the manufacture of these products could be found within the State, a saving of freight could be effected and a new industry built up. Prospecting for such materials was started and experiments were made with samples from numerous deposits. Considerable effort and funds were expended in an attempt to manufacture silica brick from Dillon quartz, a light colored sandstone that is found near Dillon, Mont., on the Oregon Shortline railroad. As a brick material the Dillon quartz was a failure, but it has proved very satisfactory as a silica cement. It is now being used in laying silica brick and for reverberatory furnace bottoms. A bed of quartzite that is particularly suited to the manufacture of high-grade silica brick -was finally discovered at Browns Spur, 6 miles west of Anaconda. The material from this deposit is now being used in the manufacture of the Anaconda silica brick, which have gained a wide reputation for heat-resisting and lasting qualities. The analysis of all average sample of this quartz is: SiO2,, 96.7; Fe203, 0.3; Al203, 2.5; CaO, 0.3 per cent. The very low percentage of fluxing ingredients makes this a most refractory material. All of the Anaconda silica brick are hand molded. Various types of brick machines have been tried, but the hand-mold process proved the best suited to the manufacture of silica brick from this material. The silica is first put through a jaw crusher and is then clumped into wet pans, where 4 per cent. of lime paste is added, to produce a bond. Without the lime the. material would not be plastic enough to mold. After a few minutes' grinding in the wet pans the material is conveyed to the molder, who forces it into the molds by hand. The brick are then dumped on pallets and placed in the drier, where they are left until dry enough to be set in the kilns. Some of the brick are re-pressed before being dried. They are burned about five days, in round down-draft kilns. It is not necessary to have as much heat in the kilns as the brick will be subjected

Jan 9, 1913

By J. E. Flinn, E. R. Gilbert

Recently, Green reported some high-temperature, 0.60 to 0.89 T3, creep results on unalloyed tantalum. From his study he determined an activation energy of 114 kcal per mole for steady-state creep using the T, differential-temperature method25 for testing. He accounted for the difference between this value and 110 kcal per mole for self-diffusion by the temperature dependence of the elastic modulus, 4 kcal per mole. This reported activation energy is in apparent disagreement with that which can be determined from Green's isothermal data, which we have plotted as log creep rate vs 1/T in Fig. 15. From this figure, it appears that there are two activation energies of -185 kcal per mole at the higher temperatures and -75 kcal per mole at the lower temperatures. It is not obvious that the data can be fitted to a straight line corresponding to an activation energy of 114 kcal per mole. One is led to two possible conclusions regarding Green's study: there are two discrete processes controlling the creep rate from 0.60 to 0.89 Tm or the apparent activation energy is not discrete but continuously increases with increasing temperature. The former speculation would be in closer agreement with the high-temperature creep behavior of tungsten.28 The apparent disagreement between the activation energies determined by the AT and isothermal methods certainly suggests that further study on the high-temperature creep of tantalum is needed.

Jan 1, 1967

By Ernst M. Cohn

The demonstrations of the "Silent Sentry" by Union Carbide Corp. in 1957 and of a special tractor-plow by Allis-Chalmers in 1959 ushered in the technology era of fuel cells. The idea for direct conversion of chemical to electrical energy, first published in 1801 by Davy in England and Ritter in Germany, has been kept alive by a few people through 150 years: Grove built the first hydrogen-oxygen fuel cell in 1839; Mond and Langer made electrolyte contributions around 1890 that are still used today; Baur worked on coal-based cells from 1900; Bacon started his work in the '30's, which resulted in the first multi-kilowatt unit in the '50's; Davtyan studied molten-salt electrolytes in the '40's, followed by Ketelaar in the '50's; and Justi developed highly active electrodes in the '50's, to name only some of the pioneers. Despite the tremendous increase in research and development of fuel cells, these direct energy converters are still in their infancy. They will find their functional application in space, where power density must be maximized and product water utilized. These early systems will provide valuable experience in system engineering and reliability.

Jan 9, 1964

By A. Gatti, R. L. Fullman

A very fine dispersion of aluminum oxide is produced by internal oxidation of solid-solution alloy of 0.14 pet A1 in Ag. The particle size of the aluminum oxide is approximntely 50 to 100A in radius. The yield strength of the alloy is increased markedly by internal oxidation. A further increase in strength is produced by cold working the internally oxidized alloy. Recrystallization is retarded by the finely dispessed aluminum oxide particles, so that the strength increase resulting from cold work is retained on annealing at temperatures 14 to about 700°C. MANY workers'-3 in the past have studied various aspects of the internal oxidation of aluminum-silver alloys. This paper is an extension of these studies with emphasis placed on the effect of time and temperature of annealing on the strength of these alloys after oxidation and subsequent cold working. Two general conditions are necessary to internally oxidize an alloy. First, oxygen must diffuse through the base material more rapidly than does the addition; otherwise oxidation will take place as a surface layer. Secondly, the affinity of oxygen for the addition must be greater than for the base material. After internal oxidation of certain alloys takes place, a marked increase in hardness accompanied by higher yield stress and improved creep properties is noted, presumably as a result of the highly dispersed oxide within the base material. Meijering and Druyvesteyn1 also noted that the internally oxidized portion of a partly oxidized alloy failed to recrys-tallize under annealing conditions that led to coinplete recrystallization of the unoxidized part. EXPERIMENTAL-METHODS AND PROCEDURES Few alloys can be made to contain a second phase that is extremely stable at high temperatures. Silver plus aluminum in solid solution was chosen for these internal oxidation studies because of the high rate of oxygen diffusion through silver and the very stable nature of aluminum oxide. Two alloys were vacuum cast. The nominal compositions were: Alloy A—1 pct Al, balance Ag; Alloy B—0.1 pct Al, balance Ag. Chemical analysis, which does not distinguish between aluminum and aluminum oxide, showed the conlposition to be: Alloy A—1.6 pct Al, and Alloy B—0.14 pct Al. The ingots were machined for surface cleaning, swaged and drawn to 0.020-in. diam wire. A sample 20 ft long of the 0.020-in. dianl wire of each composition was annealed 24 hr at 800°C in pure dry hydrogen. Each wire was then cut into two equal pieces. Photomicrographs of the 0.14 pct A1 alloy are shown in Fig. 1, the annealed 0.020-in. wire at the left and the oxidized wire to the right. The oxidation treatment for the first set of data was 1000 hr at 800°C in air. After this treatment the 1 pct A1 proved to be brittle. It is assumed that high alunlinum oxide concentration at the grain boundaries was responsible. The 0.14 pct Al wire remained ductile and all further data were derived using this alloy. One-half of this wire, about 5 ft, plus 5 ft of as-homogenized wire, was then drawn cold to 0.005 in. diam. All tensile tests were conducted with an Instron Engineering Corp. tensile-testing machine, Model TT-B. Unless otherwise indicated, the tests were made at room temperature with a strain rate of 0.1 per min. All metallographic samples were etched with an aqueous solution of 2 pct each of CrO3 and H2SO4 . EXPERIMENTAL RESULTS AND DISCUSSION PARTICLE SIZE DETERMINATION A study was made of the particle size of the aluminum oxide produced in the samples of Ag + 0.14 pct Al, oxidized 1000 hr at 800°C. A cross section of the as-oxidized wire was mounted in bakelite, polished, and etched with an aqueous solution of 2 pct each of CrO3 and H2SO4. The specimen was then thoroughly cleaned by stripping successive coatings made by applying 10 pct nitrocellulose in amyl acetate. The final replica of the cross section was made by applying 2 pct nitrocellulose in amyl acetate. The replica was stripped, transferred to a copper screen, shadow cast with chromium at 10 deg and photographs taken using a Phillips Metallix electron microscope at an accelerating potential of 100 kv. A photograph of an etched sample of the as-oxidized material is shown in Fig. 2. We believe the pits in the photograph are places were A12O3 inclusions were sitting in the matrix. By inspection, it appears that the volume fraction ob-

Jan 1, 1960

By P. B. Leavenworth

Twenty-six fields were found in the Texas Gulf Coast in 1940 as compared to 17 fields in 1939. Of these, 14 were oil fields and 12 were gas and distillate. About 150 wells were drilling at the end of the year. Production for the year 1940 amounted to 104,127,247 bbl. as compared to 100,-253,937 bbl. for 1939. Considerable wildcatting for Wilcox production featured the exploration, but discoveries were few and the type of fields found mainly gas and distillate. On the whole, the program was discouraging. New Fields Alta Lomu. Galveston County.—The Alta Loma field was discovered on May 20, 1940, by the Stanolind Oil and Gas Company's No. I John A. Hulen, which blew out at a depth of 9166 it. and ran wild for several days, with an estimated production of 400 bbl. per hour of 36" gravity oil from a sand in the top of the Frio. Water soon appeared but the well produced more than I3o,ooo bbl. of oil between May 20 and June 10, together with a large amount of salt water. Later the well was killed and recompleted on Nov. 23, for 276 bbl. of 34" gravity oil per day. Probably this was the most sensational discovery of the year, although development to the end of the year was disappointing. The discovery was the result of reflection seismograph work of the Stano-End Oil and Gas Co., the principal leaseholders. Bailey's Prairie, Brazoria County.— Glenn H. McCarthy9s No. I W. B. Munson was completed in a lower Frio sand from perforations 11,345 to II,349 ft. for 8 bbl. of fluid (50 per cent black oil, 27" gravity, and 50 per cent B. S. and W.) on Sept. 24, 1940. It was finally recompleted as a gas well from perforations 11,631 to 11,651 ft., on Oct. 9, 1940. The well had been drilled to a total depth of 11,860 ft. This well produced for only a short time and the area is at present inactive. Blessing, Matagorda County.—The Texas Company's No. I A. B. Pierce was completed from a Frio sand from 8265 to 8300 ft. on July 8, 1940, for an initial production of 29 bbl. of distillate, I 1/2 million cu. ft. of gas. One other gas and distillate well was completed in 1940. Borden, Wharlon County.—J. F. Hutch-ins' No. 2 A. P. Borden Estate was completed on Feb. 11, 1940, for 108 bbl. of 35,6° gravity oil, from a Frio sand at 4758 to 4771 ft. This is the second well drilled in the area by Hutchins. Two other wells in 1940 were failures and there was no activity at the end of the year. Dyersdale, Harris County.-The Dyers-dale field was opened by the completion, on Sept. 15, 1940, of H. C. Cockburn's No. I G. Burkitt from a sand in the top of the Frio, through perforations from 4067-4072 ft., for 240 bbl. of low-gravity oil. By the end of the year the field had been fairly well outlined and did not appear to be a major discovery. Duck Bay, Calhoun County.—Coronado Oil Company's No. I Welder, alter having drilled to 10,002 ft., perforated casing from 5654 1/2 to 5659 it. and was completed for 60 bbl. of 36.8° gravity oil On July 27, 1940, from a Miocene sand.

Jan 1, 1941

By P. B. Leavenworth

Twenty-six fields were found in the Texas Gulf Coast in 1940 as compared to 17 fields in 1939. Of these, 14 were oil fields and 12 were gas and distillate. About 150 wells were drilling at the end of the year. Production for the year 1940 amounted to 104,127,247 bbl. as compared to 100,-253,937 bbl. for 1939. Considerable wildcatting for Wilcox production featured the exploration, but discoveries were few and the type of fields found mainly gas and distillate. On the whole, the program was discouraging. New Fields Alta Lomu. Galveston County.—The Alta Loma field was discovered on May 20, 1940, by the Stanolind Oil and Gas Company's No. I John A. Hulen, which blew out at a depth of 9166 it. and ran wild for several days, with an estimated production of 400 bbl. per hour of 36" gravity oil from a sand in the top of the Frio. Water soon appeared but the well produced more than I3o,ooo bbl. of oil between May 20 and June 10, together with a large amount of salt water. Later the well was killed and recompleted on Nov. 23, for 276 bbl. of 34" gravity oil per day. Probably this was the most sensational discovery of the year, although development to the end of the year was disappointing. The discovery was the result of reflection seismograph work of the Stano-End Oil and Gas Co., the principal leaseholders. Bailey's Prairie, Brazoria County.— Glenn H. McCarthy9s No. I W. B. Munson was completed in a lower Frio sand from perforations 11,345 to II,349 ft. for 8 bbl. of fluid (50 per cent black oil, 27" gravity, and 50 per cent B. S. and W.) on Sept. 24, 1940. It was finally recompleted as a gas well from perforations 11,631 to 11,651 ft., on Oct. 9, 1940. The well had been drilled to a total depth of 11,860 ft. This well produced for only a short time and the area is at present inactive. Blessing, Matagorda County.—The Texas Company's No. I A. B. Pierce was completed from a Frio sand from 8265 to 8300 ft. on July 8, 1940, for an initial production of 29 bbl. of distillate, I 1/2 million cu. ft. of gas. One other gas and distillate well was completed in 1940. Borden, Wharlon County.—J. F. Hutch-ins' No. 2 A. P. Borden Estate was completed on Feb. 11, 1940, for 108 bbl. of 35,6° gravity oil, from a Frio sand at 4758 to 4771 ft. This is the second well drilled in the area by Hutchins. Two other wells in 1940 were failures and there was no activity at the end of the year. Dyersdale, Harris County.-The Dyers-dale field was opened by the completion, on Sept. 15, 1940, of H. C. Cockburn's No. I G. Burkitt from a sand in the top of the Frio, through perforations from 4067-4072 ft., for 240 bbl. of low-gravity oil. By the end of the year the field had been fairly well outlined and did not appear to be a major discovery. Duck Bay, Calhoun County.—Coronado Oil Company's No. I Welder, alter having drilled to 10,002 ft., perforated casing from 5654 1/2 to 5659 it. and was completed for 60 bbl. of 36.8° gravity oil On July 27, 1940, from a Miocene sand.

Jan 1, 1941

By Carl F. Floe, John Chipman

THE system molten copper-oxygen-sulphur is of interest from both the practical and theoretical standpoints; practically, because oxygen and sulphur play an important role in the commercial production of copper, and theoretically because it offers a chance to study the reaction between an oxide gas, SO2, and a molten metal. Reactions of this type, such as that between CO or C02 and molten iron, are important in many metallurgical operations. Again, the determination of any gas-metal equilibrium is of theoretical interest and value insofar as it contributes to the general development of the laws for solution of gases in metals. This problem is being given an increasing amount of attention in modem metallurgy. This paper is the first of a series and presents the results of a determination of the solubility of sulphur dioxide in molten copper at temperatures from 1100° to 1500°C., and pressures from about 20 mm. of mercury to somewhat above atmospheric. REVIEW OF PREVIOUS WORK The solubility of gases in most liquids has been found to obey Henry's law, which states that for a fixed temperature the amount of gas dissolved is directly proportional to the pressure. However this law does not hold for liquid metals. Instead, it appears that for many gases, particularly the simple diatomic ones such as 02, N2 and H2, the amount dissolved in liquid metals is directly proportional to the square root of the pressure. This is known as Sieverts' law. It may be recognized as a special case of Henry's law, which applies when the solute gas is dissociated into atoms or when it reacts with the solvent metal to form solute molecules containing single atoms of the gaseous elements, as, for example: [2M -}-G2 = 2MGK =G) IYf X[I]] which, if the solubility is not too high and the concentration of metal therefore nearly constant, can be simplified to: [MG = Ki Pa,[2]] Following the same reasoning, it would be expected that the solubility of SO2 in copper would be proportional to the cube root of the pressure, the reaction being as follows: [6Cu + S02 = Cu2S + 2Cu20[3] K Cu2S X (Cu20)2(Cu)e(Psm)[4]] or, neglecting the change in metal concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume V of gas absorbed: [K1 =or Vdo,= K2/PBO [5] PsO]

Jan 1, 1941