This paper describes the unusual hazardous conditions encountered in mining thick, inclined coal beds under heavy cover in Carbon County, Utah. This description includes heavy roof conditions, sloughing ribs, steep pitches, and severe bouncing experience. Emphasis is placed on the top bench system of mining and development in the top half of a 16-ft seam, under the roof rock, which is bolted, and the recovery of the bottom coal on retreat; success of bolted roof and ribs; and shuttle car haulage on pitches up to 25%. The use of protective cages for operators of face equipment, the guarding of belt conveyor systems to prevent injury associated with deliberate entry, and the positive lockout of electrical equipment is described and illustrated. Most coal mining areas of the Western United States are characterized either by thick beds, steep pitches or heavy cover. Individually, each of these may present inherent safety hazards that in- fluence mining. When all are met at one location, the combined effect is to make the safe operation of the mining property a challenge to management. These combined conditions are met in the coal mines of the Columbia-Geneva Steel Div. of the United States Steel Corp., in southeastern Utah. This coal bed measures up to 16 ft in thickness, the pitch is as much as 25% and mining is under a cover approaching 3000 ft. The Sunnyside coal bed is found in the Book Cliff Mountains, a great escarpment extending from west of Castle Gate, Utah, some 180 miles to Grand Junction, Colo. West of Green River, Utah, the Book Cliffs swing sharply to the north because of the domelike uplift of the San Rafael Swell to the southwest. It is in this northerly extension of the Book Cliffs that the Sunnyside coal in the Blackhawk Formation of the Mesa Verde Group, Upper Cretaceous Age is found. The strata are transected by numerous faults with from a few inches to as much as a hundred feet of displacement. All of these faults have had some effect on the mining operation, either in roof control or, in the case of major faulting, the pattern of mine development. MINING PRACTICES Mining has generally been confined to the Lower Sunnyside Seam which measures from 7 to 16 ft in

Jan 1, 1963

By E. F. Koch, J. L. Walter

oriented crystals of iron and iron with 3, 5, and 6.25 pct Si were rolled to reductions of 10 and 70 to 97 pct at room temperature. Similarly oriented crystals were deformed in tension. Dislocation substructures of the deformed crystals were observed by transmission electron microscopy to determine the effect of silicon on the formation of substructures. Pole figures were obtained to relate orientation changes to substructure. When rolled 10 pct, the iron crystals and the 3 pct Si-Fe crystals formed cells, 1 and 0.2 u in diameter, respecliuely. Cells were absent in the higher-silicon crystals. Extended dislocations and possible stacking faults were observed in the 6.25 pct Si-Fe crystal rolled 10 pct and annealed at 650°C. The stacking-fault energy was estimated to be 20 ergs per sq cm. Rolling to 70 pct resulted in the formation of sub-bands (0.9 µ wide) ill the iron crystals and transition bands (containing 0.2-µ-wide subbands) in the 3 pct Si crystals. No subbands formed in the 5 pct Si-Fe crystal until it was ankzealed. SliP occurred on (112) planes ill tension. The slip traces on the 3 pct Si crystal were wary while those on the 5 pct Si crystal wvere straight. The strain-hardening coefficient for the 5 pct Si crystal was nearly zero. Cells did not form, at least at elongations up to 10 pet. The results suggest that cross slip of iron is restricted by additions of silicon beyond about 3 pct possibly by formation of immobile extended dislocations. IN a previous paper' the authors described the substructures developed in (100)[001]-oriented crystals of 3 pct Si-Fe which were rolled to reductions of 10 to 90 pct at room temperature. At low reductions (10 to 20 pct) cells, approximately 0.2 to 0.3 ja in diameter, were formed. The cell walls consisted mainly of edge dislocations. With increasing reduction (up to 50 pct) the cells were seen to elongate in the rolling direction. In certain regions of the crystal there were significant reorientations which were characterized as rotations about an axis normal to the (100) or rolling plane. These regions were called "transition bands". The regions in which there were no reorientations were called ('deformation bands". At reductions of 60 to 70 pct the elongated cells in the transition bands became sub-bands separated by low-angle tilt boundaries with angles of disorientation of about 2 deg. The elongated cell structure in the deformation band was replaced by a general distribution of dislocations. It was noted that the width of the subbands in the transition bands remained 0.2 to 0.3 µ; i .e., the width of the subbands was the same as the initial cell diameter for reductions up to at least 70 pct. From this, and from considerations of the mechanism of formation of the transition bands,' it was concluded that the subbands evolved directly from the initial cells. In order to check this conclusion, it was decided to examine the relationship between initial cell diameter and width of subbands produced by large rolling reductions. Cell size is known to be dependent upon the temperature of deformation.2,3 However, preliminary experiments with 3 pct Si-Fe crystals indicated that the change in cell size with increasing temperature of deform,ation was not sufficient for the present purpose. On the other hand, cell diameters generally reported for iron deformed at room temperature2'3 range from 1 to 2 p, a factor of 3 to 10 larger than the cells in 3 pct Si-Fe rolled to 10 pct reduction,' indicating the possibility of a marked dependence of substructure (at least in terms of cell size) on the amount of silicon in iron. Thus, the investigation was enlarged to include the study of the effects of varying silicon content on substructure in lightly rolled as well as in heavily rolled crystals of iron and iron with 3, 5, and 6.25 pct Si. The crystals used in this study all had the same orientation, (100)[001], with respect to rolling plane and rolling direction. These were rolled to reductions of from 10 to 97 pct and the substructures determined by electron transmission microscopy in both the rolled state and after annealing. In addition, stress-strain curves were obtained from (100)[001]-oriented crystals of iron and 3 and 5 pct Si-Fe to determine the effect of silicon on tensile properties. The dislocation substructure of the tensile specimens was also determined for Samples pulled to 2 and 10 pct elongation at room temperature for comparison with the substructures produced by rolling. 1) EXPERIMENTAL PROCEDURE Crystals with 3, 5, and 6.25 pct Si were prepared by annealing 0.012-in.-thick sheets of high-purity Si-Fe in purified argon at 1200°C to effect growth

Jan 1, 1965

By S. Ramachandran, N. J. Grant, T. B. King

MANY investigations of the rate of the sulfur transfer reaction between carbon-saturated iron and blast furnace type slags have been made." It is evident that the reaction is complex, the rate being affected by the presence of elements dissolved in the metal that are readily oxidized and therefore capable of existing in the slag phase. Thus Goldman, Derge, and Philbrook- have shown that carbon, silicon, manganese, and aluminum, in order of increasing effectiveness, accelerate sulfur transfer from iron containing these elements to blast furnace type slags. Quantitative information is still, however, not available on the relation between what have been termed side reactions, such as silicon transfer and CO evolution, and the sulfur transfer reaction itself. In other words, the stoichiometry of the reaction has not been investigated. In the present investigation, the transfer of all reacting elements and the evolution of CO have been measured simultaneously in order to establish the mechanism of the reaction which occurs in practice. Information of this nature cannot be deduced from equilibrium studies. It should be pointed out that in kinetic studies of this type quantitative conclusions are applicable only to the system studied. This restriction should be borne in mind when attempts are made to compare results from different investigations. Apparatus The apparatus used enables slag and metal samples to be taken at frequent intervals and also provides a continuous record of the amount of gas evolved. A sketch of the apparatus is given in Fig. 1. It may be considered in three sections: 1) furnace section, 2) blank volume section, and 3) pressure measuring section. The furnace section is shown in detail in Fig. 2. It consists of two graphite crucibles, C and D, super-

Jan 1, 1957

By R. H. Winn

A method for the selection of the most suitable corrosion inhibitor for a particular system is given. The method involves the evaluation of surface passivity by means of copper ion displacement after the metal surface has been subjected to the corrosive atmosphere. The application of the method to the selection of suitable inhibitors for use in producing wells is described. Correlation with recognized laboratory tests has beet1 found to be good within the limitations of the test. The use of the test to evaluate inhibitor persistencc is described. INTRODUCTION Corrosion as it is associated with the industry shows wide variations in its qualitative as well as its quantitative aspects. This complicates the work of the corrosion engineer. In the past few years the efforts of the corrosion engineer have been further taxed by the large numbers of products being marketed as corrosion inhibitors by various manufacturers. These products are submitted to him together with a limited amount of data to support their use as inhibitors. The data are usually authentic and reliable yet all too often when these products are applied to an actual corrosive system the results are disappointing due to the ineffectiveness of the inhibitor and the corrosive system. The corrosion engineer must select a comparatively limited number of inhibitors for field trial from the large number available. The selection is usually made on the basis of a standardized laboratory test such as that adopted by the National Association of Corrosion Engineers or by field experience in an area; however, testing of this type is discouraging on large numbers of compounds, particularly in view of the specificity of environment. It has been an object of this work to devise a method which will allow the corrosion engineer to select the best inhibitor for a specific environment under field conditions. The test would of necessity be rapid and inexpensive. It would preferably eliminate the need for expensive and delicate instruments. STATEMENT OF THEORY The test as developed makes use of the fact that metal ions will be displaced from solution by metals having a more positive electrode potential. Thus, if an active iron surface is exposed to a solution of a copper salt, free copper will plate spontaneously on the iron surface as it is displaced from the salt solution by iron ions. If the iron surface is passified, as by coating with an insulating-type organic corrosion inhibitor, it is no longer capable of displacing the copper ions due to its own limited ionization. The result will be a change in the amount of copper plated upon exposure to a neutral copper salt solution. In practice it has been found possible to measure the magnitude of the alteration of the cell potential by determining the copper deposited on a standard iron surface under controlled conditions. This means that, as the film builds up, the resulting shift in the electrode potential tends to cause the iron surface to act more like a noble metal, resulting in a reduction in the cell potential to a point that copper will no longer plate spontaneously. Obviously, the salts of other metals such as silver, gold or platinum might be used for this operation; however, copper was selected because of the color difference of the plate, the comparatively low cost of copper salts and the ease of evaluation of the plated copper. Furthermore, its high cell potential provides a substantial driving energy. The determination of the copper is readily done colorimetrically by dissolving it in 5 per cent ammonium hydroxide solution containing 2 per cent potassium per-sulfate. The blue color of the copper ammonic complex ion so developed may be compared with standards prepared by dissolving known quantities of copper powder in the same reagent. In routine screening it is seldom desirable to determine the amount of copper plated. It is usually more important to determine the concentration of inhibitor required to prevent the plating of copper.

By D. J. Coolidge, H. L. Sheakley

THIS paper does not deal with all sands used in the glass industry in Missouri; it covers only that used in the plate-glass factory at Crystal City. However, it is probably safe to say that other sands, pro- [ ] duced throughout the state for this purpose, are of identical nature. The glass sand used in Missouri is commonly called the St. Peter deposit, which is ascribed to the Ordovician Rock series in the form of sandstone. This St. Peter deposit, aside from a few small outliers, covers a large area of eastern Missouri. It forms, through a broad curve, the northeast margin of the typical Ozark region between Cape Girardeau on the southeast and Mineola, Montgomery County, on the northwest. The belt is extremely irregular, varying from one to ten miles in width; its length is 150 miles in a straight line. [ ] The outcrop near the entrance to the Crystal City mine appears in the form of a sandstone bluff approximately 30 ft. high, running along Plattin Creek (Fig. , I). Above the sand rock an overburden of Joachim limestone appears, which, thickens to nearly 300 ft. and forms the hill commonly called Buck Knob. Test holes, where drilled at various points and the drillers' log indicate that the St. Peter deposit ranges in thickness from 63 to 71 feet. PROPERTIES OT THE ST. PETER SAND From an analysis of the glass sands of the St. Peter formation in Missouri, the follow-

Jan 1, 1942

By H. P. Stüwe

HE recent papers of Aust and Rutter112 have again brought to mind the importance of certain "special" orientation relationships between the lattices of two fcc crystals on the mobility of the grain boundary separating them. No theoretical treatment of this problem has been offered till now. The only principle published so far that has given an indication why certain orientation relationships should be "special" is the counting of "coincidence sites" according to the suggestions by Kronberg and Wilson.3 The "coincidence plots" published by these authors show, for instance, that two fcc lattices rotated by 38 deg around a common (111)-axis have 1/7 of their lattice sites in common. Such an orientation relationship is also characteristic for high boundary mobility. The accuracy of the orientation relationship needed for high mobility is not too rigid. Deviations up to 10 deg from the ideal orientation seem to be tolerable as can be gathered from the experimental data.'j4 The auestion arises, then. how the density of coincidence sites will be affected by a deviatioi from mathematical accuracy. This can be checked by a simple model. Two sieves are prepared, the arrangement of the holes corresponding to lattice sites on a (111)-plane in a fcc crystal. They are placed upon each other, Fig. 1. One is kept fixed, the other is rotated around an axis pushed through one hole in common to both. The light falling through holes of both sieves is then a measure for the density of coincidence sites. If the diameter of the holes is very small, light intensity is contributed only by holes the centers of which coincide "exactly." If the diameter of the holes is rather large, some intensity will be contributed by

Jan 1, 1962

By G. F. Bolling

STUDIES of grain boundary migration in zone-refined metals have all shown that the rate of migration is greatly reduced by small added solute concentrations. However, it is apparent that a difference exists between boundary migration during normal grain growth and single boundaries migrating in a bicrystal to consume a substructure. To effect the same reduction in velocity in the two cases, much more solute is required for grain growth than for the single boundary experiments. One case is available for direct comparison; both Bolling and winegardl and Aust and utter' added silver and gold to zone-refined lead to study grain growth and single boundary migration, respectively. For comparable reductions in migration rates, about 500 times more solute was required to retard grain growth than to retard the single boundaries. A reason for this difference is suggested here. The rate of grain boundary migration is dependent on solute concentration and must therefore also depend on the solute distribution; i.e., regions of higher solute concentration encountered by a moving boundary must produce greater retardation and thus could determine any observed rate. A dislocation substructure can be the source of a nonuniform solute distribution since it can attract an excess concentration of certain solutes. In fact, it is probable that the solutes which impede grain boundary migration most would segregate most severely to a substructure for the same reasons. Thus a dislocation substructure present in a crystal being consumed could locally magnify the concentration of solute confronting an advancing grain boundary. In the single boundary experiments a low-angle substructure, within single crystals obtained by growth from the melt, was used to provide the driving force to move a grain boundary; in grain growth, no substructure of this magnitude was present. The increased solute concentration at subboundaries should be given approximately by C, = G e c,/kT, where t, is a binding energy and CO the bulk concentration. To account for the difference between the two experiments in the Pb-Ag and Pb-Au cases, C, must be the concentration impeding the single boundary migration, and a value of t, = 0.25 ev is necessary. This is reasonable, even though calculation on a purely elastic basis gives t, = 0.12 ev. because electronic effects must enter for silver and gold in lead. The compound AuPbz forms3 and the metastable compound AgrPb has been reported to nucleate at dislocations prior to the formation of the stable, silver-rich phase.4 Other observations support the hypothesis that a magnified solute concentration impedes the single boundary migration. For example, some crystals were grown by Aust and Rutter at concentrations of ~ 0.1 wt pct Sn and 2 x X at. pct Ag or Au which exhibited a cellular substructure, and in these crystals no boundary migration was observed. It is therefore evident that the higher concentrations at cell boundaries drastically inhibited migration. Inclusions would not have been responsible for this inhibition since according to recent work on cellular segregation,5 no second phase should have occurred in the segregated regions at the cell boundaries for the conditions of growth used, at least in the Pb-Sn system. In the purest lead, only the "special" boundaries observed by Aust and Rutter gave rise to the same activation energy as that obtained in grain growth. It is reasonable to suppose that the structure of special boundaries does not favor segregation at low concentrations and thus solute, or an inhomogeneity in its distribution, would have no effect. Random boundaries, on the other hand, are affected by solute and the substructure would enhance residual concentrations in the zone-refined lead, leading to a higher activation energy. It is clear, even without a detailed theory, that the apparent activation energies and exact solute dependence in the two experiments must be different as long as the non-uniform solute distribution produced by the substructure is important. Recrystallization experiments should also be susceptible to the same kind of local segregation at subboundaries or disloca tion cell walls; a suggestion similar to this has been made by Leslie et al.' Following the arguments presented here, the effects of a given solute concentration would be like those observed by Aust and Rutter if segregation occurred, and like those of grain growth otherwise. This work was partially supported by the Air Force Office of Scientific Research; Contract AF-49(638)-1029.

Jan 1, 1962

By Willard L. Hunter

Four solvent extraction systems were studied to determine their efficiency jor extraction and separation of tantalum and columbium. Aqueous feed solutions of varying HF-HCl concentrations and metal content were contacted with equal volumes of cyclohexanone, 3-methyl-2-butanone, and 2-pentanone and solutions of varying HF-H2S04 concentrations were contacted with equal volumes of 2-pentanone. One multistage continuous test was made in a polyethylene pulse column using cy clohexanone as the organic phase. In each system studied, columbium and tantalum purities in excess of 95 pct with respect to each other were obtained in single-stage tests at low acidities in the feed solution. Separation factors ranging from 1700 to 2400 were obtained when rising HF-HCl mixtures in the aqueous phase. Best results were obtained when a solution of HF-H2S04 was used as the aqueous phase and 2-pentanone as the organic phase. A separation factor in excess of 6000 was obtained in one stage with aqueous solution concentrations of 2 _N HF and 2N H2S0,. When acid concentrations were increaszd to 52 HF and 10 _N H2S0,, 99.9 pct of the tantalum and 98.2 pct of the columbium initially present in the feed solution were transferred to the organic phase. The separation of columnbium and tantalum obtainable by means of the solvent extraction systems presented in this paper was found to corn -pare favorably with other systems, including the HF-H2SO4-methyl isobutyl ketone system currently used by most producers for the extraction and separation of these metals. TANTALUM and columbium are always found together in minerals of commercial significance, although the proportion of the two metals in ores varies within broad limits. Columbium is estimated to be 13 times more abundant than tantalum. Five methods generally employed for the separat:ion of these metals are: 1) fractional crystallization (the Marignac process),2 2) solvent separation, 3) fractional distillation of their chlorides, 4) ion exchange, and 5) selective reduction. Of these methods, the one currently used by industry to the greatest extent is that of solvent separation. One of the early technical developments in solvent separation of tantalum from columbium was reported by the Bureau of Mines: the HF-HC1-methyl isobutyl ketone system; data were presented for both laboratory and pilot-plant experimentation.3 Of twenty-eight organic solvents tested for their ability to extract tantalum from an HF-HC1 solution of columbium and tantalum, 3-pentanone (diethyl ke-tone), cyclohexanone, 2-pentanone, and 3-methyl-2-butanone were chosen for further study. Data on the HF-HC1-diethyl ketone system has been published4 and data describing the use of cy clohexanone, 2-pentanone, and 3-methyl-2-butanone as the organic phase are included in this report. RAW MATERIAL The source of tantalum and columbium oxides for this study was ('Geomines" tin slag from the Manono Smelter, Cie Geomines, Gelges, S.A., Congo. In order to extract the valuable Ta-Cb content, the slags were carbided, chlorinated, and the sublimate from chlo-rination was hydrolized and washed free of chloride with water. The washed material was air-dried and stored in a stoppered container. Throughout the paper, "feed material" refers to this mixture of hydrated oxides which was employed because of its high solubility in aqueous solutions. Typical analysis of the hydrated oxides is shown in Table I. I) HF-HC1-CYCLOHEXANONE SYSTEM Batch Separation. Effect of Acid Concentration. To determine the effect of varying the acid concentration upon the transfer of tantalum and columbium, a series of tests was made in which approximately 2.5 g of feed material was added to 25 ml solutions of 2, 4, 6, 8, and 10 N HF and 0 through 5 N HC1. Tantalum pentoxide concentration of the solu%ons was approximately 21 g per liter and columbium pentoxide was 14 g per liter. These starting solutions were shaken with equal volumes of cyclohexanone in 100 ml polyethylene bottles for 30 min. The phases were carefully separated in 125 ml glass separatory funnels. The time of contact of the solutions with the separatory funnels was kept at a minimum to reduce silica contamination. The measured phases were separated into 400 ml polyethylene beakers and the metal contents of each were precipitated by addition of an excess of ammonium hydroxide. Precipitate from each phase was filtered on ashless filter paper, ignited at 800" to 1000°C for 45 min, weighed, and analyzed by X-ray fluorescence.5 Data tabulated in Table I1 and illustrated in Fig. 1, show that maximum separation of tantalum from columbium for each HF concentration was obtained with no HCl present. The purest tantalum product was obtained with some HCl present. The highest separation factor was obtained at 2 N HF and

Jan 1, 1970

By R. F. Hinds

A pressurizing system was designed and built to apply a radial pressure of 5.000 psi to rock samples. Samples of the Bradford, Weir and Kirkwood sandstones were subjected to radial pressures parallel and perpendicular to the bedding in the system and the changes in conductivity, porosity and permeability were deter-mined. Asymptotic decreases in conductivity, porosity and Klinkenberg permeability were observed over the 0- to 3,500-psi range. From these data, the increase of formation factor over the same range was calculated. The cementation exponent expressed in the Archie equation was found to increase with pressu,re. The rate of change varied from formation to formation. Only small differences were observed for samples taken parallel to the bedding as comnared to those taken perpendicular to it except for the Bradford sand. Above 3,500 psi the data are not good enough to tell if the properties continue to fall-off asymptotically or in a different manner. A possible explanation for the probable litnit of the asymptotic rate around 3,500 to 4,500 psi is that this represents the maximum pressure which the formations have unrdergone during their geological life as a result of burial. INTRODUCTION For many years measurements have been made in the laboratory of the properties of oil-bearing sandstones with little consideration being given to whether these properties had been changed when the samples were moved from their original position in the ground to the laboratory. Relatively little has been reported in the literature on the effect of pressure on the properties of sandstones. The changes in permeability for eight typical consolidated oil-bearing sandstone samples with overburden pressure (0- to 15,000-psi range) was presented by Fatt and Davis' in graphical form. In 1953 Fatt' also reported the relationship between porosity and overburden pressure for four typical consolidated oil-bearing sandstone samples (0- to 5,000-psi range). Fatt later described the changes of formation factor and porosity of 20 typical oil-bearing sandstone samples with overburden pressure changes (0- to 5,000-psi range) giving the values of the coefficients and exponents in the Archie' equation, and the more general Winsauer equation', where C, k and m are empirical constants, F is the formation factor, and + is the porosity. During the experiments of this investigation the core was contained in a neoprene rubber sleeve as shown in Fig. 1. It was held between two steel end members which were mounted in a steel cylinder. The unassembled pressure cylinder with its component parts is shown in Fig. 2. The core was insulated from the two steel end members by a Teflon sleeve with a small hole in the

By H. Larson, J. Chipman

The ferrous and ferric oxide concentrations of slags, expressed as j = Fe+++/(Fe+++ + Fe++), have been established through gas-slag equilibrium at 1550°C in a range of oxygen pressure of 10-I to 10-9 equilibriumatm. The value of j is increased by basic additions (BaO, CaO, MgO, MnO) and decreased by acidic oxides (SiO2 and TiO2). Oxygen pressure is shown graphically as a function of composition for slags which are analogous to those at the slag-gas interface of the open hearth furnace. THE progress which has been made in recent years in understanding the chemistry of metallurgical slags has been based largely on studies of slag-metal and slag-gas equilibria. There is a considerable body of knowledge which is applicable to reactions occurring at the slag-metal interface in open hearth steelmaking. There is little information concerning reactions of the slag with the furnace atmosphere and hence little basis for an understanding of the transfer of oxygen, sulphur, or hydrogen between gas and slag. The oxygen pressure of the open hearth atmosphere is normally of the order of 10-1 to 10-3 atm which differs by several orders of magnitude from that of about 10" atm at the slag-metal interface. The chemical properties of the slag, for example, the ratio of ferric to ferrous iron and the ability of the slag to hold sulphur in solution, are greatly affected by changes in oxygen pressure. This investigation was undertaken to enlarge our knowledge of the effect of oxygen Pressure on steel-making slags. Using air or controlled mixtures of CO a CO2 a range of oxygen Pressures from 10.' to 10.' was covered. Review of the Literature There are only a few references in the literature which pertain directly to this investigation. The most important is that of Darken and Gurry1,2 on the system iron-oxygen. This work included the determination of the phase diagram of the system and also a study of the field of homogeneous melts and their oxygen pressures. Their apparatus and procedure were very similar to that used in this study. Iron oxide was melted in a platinum crucible under an atmosphere of CO2:CO, CO2:H2, H2O, CO2, air or O2 depending upon the partial pressure of oxygen desired. After equilibrium was reached, the sample was quenched and analyzed for ferrous and ferric oxide. By appropriate calculations these authors were able to determine the oxygen and iron activities in the various slags, heats of formation of the oxides of iron, and heats of solution of iron and oxygen in the liquid slags. In a subsequent paper' the same authors made a less thorough investigation of the effects of additions of lime and manganese oxide on the composition of iron oxide melts. Only a few experiments were made and those in a narrower range of temperature and oxygen pressure. Darken' has investigated the fusion temperature of iron oxide in contact with silica under various atmospheres. He found that the temperature changes from 1120° to 1447°C as the gas composition changes from CO2/CO equal to 20.8 to pure oxygen. A comprehensive paper by White" predates the work of Darken and Gurry. The decomposition of ferric oxide into oxygen and lower oxides of iron was studied from 1000° to 1650°C and under oxygen pressures from 2 to 76 cm of mercury. The effect of

Jan 1, 1954

[Aalde, Kaare, ('40) New Mexico School of Mines, Socorro, N. M. Abadesco, Enrique A., ('39) Univ. of the Philippines, Manila, P. I. Abdul-Ahad, A., ('39) Montana School of Mines, Residence Hall, Butte, Mont. Abreu, Ovidio M., ('38) Univ. of Nevada, Reno, Nev. Acker, Voscoe, . ('39) Agricultural & Mech. College of Texas, College Station, Tex. Acosta S., Gonzalo, ('40) Univ. of Texas, Univ. Sta., Box 1785, Austin, Tex. Adams, Albert, ('38) New Mexico School of Mines, Socorro, N. M. Adams, Charles W.,' ('39) Michigan College of Min. & Tech., Houghton, Mich. Adams, Hugh T., Jr., ('39) Univ. of Oklahoma, Norman, Okla. Adams, Jack L., ('39) Univ. of Oklahoma, Norman Okla.]

Jan 1, 1940

By O. Chanute

In discussion of Mr. Macdonald's paper, I can say little more thau to add t~ the general acknowledgments of iguorae, and like several of the gentlemen who have preceded me, make one of those confessions which are thought to be good for the soul. Having had some experience in the erection of bridges during past years, I am aware that We yet need much information in order to proportion them to the best advantage. I would more especially like to emphasize three of the points mentioned by Mr. Macdonald, as among those upon which we lack knowledge; these are: first, the behavior of steel; second, the proportions of compression members; and, third, the influence of the size of a bar upon its strength per square inch. First, as to steel. While we all acknowledge this as the material of the future, our position map be said to be still one of expectaucy. Feu? engineers are bold enough to employ it largely in bridges, and those who do, find such serious difficulties in obtaining uniform grades of it, are so puzzled by apparent anomalies and unexpected phenomena, that it requires considerable faith and courage to apply it in large structural masses. A series of systematic experiments,

Jan 1, 1882

By Y. L. Yao

THE NaT1-type compound may be considered as the penetration of two diamond lattices in such a way that a superstructure of the bcc lattice is formed. Examples of the NaT1-type compound of lithium are LiZn, LiCd, LiA1, LiIn, and LiGa. Except for LiZn and LiCd, each molecule of these equiatomic compounds contains a total of four valence electrons. In LiZn and LiCd it was suspected (for example, see Ref. 1) that the fourth electron was withdrawn from the 18-shell of zinc or cadmium. An incomplete 18-shell would have to show strong paramagnetism. In 1955 Klemm and Fricke2 determined the magnetic susceptibility of LiZn, LiCd, LiA1, and LiIn (also NaTl and NaIn). The molar susceptibility of the outer electrons of LiZn and LiCd was found to be not strongly but weakly positive; that of LiAl and LiIn not negative but weakly positive. Thus they questioned the hypothesis about LiZn and LiCd in particular and the description of the NaT1-type structure in general. However, they did not determine the magnetic susceptibility of LiGa. This note is to report results for all five compounds of lithium. The starting materials are 99.9 pct pure lithium sticks containing less than 0.005 pct Na. 99.9 pct Zn, 99.9 pct Cd, 99.99 pct Al, 99.999 pct In, and 99.999 pct Ga. Weighed amounts of two components were wrapped in tantalum foil and placed in a graphite crucible. It was found that the tantalum sheath minimized the vaporization losses of lithium during melting. The sheath was easily stripped from the alloy rod and the tantalum in the alloy was barely detectable (less than 0.01 wt pct). The melting was performed in a resistance furnace under an argon atmosphere. Alloy specimens were annealed for 1 hr at 400°C in vacuum. The magnetic susceptibility at room temperature was determined by the Faraday Method, using the procedures previously described.' The results are shown in Table I. The interpolated values at 50 at. pct of Li and the average values at 48 to 52 at. pct of Li at 20°C determined by Klemm and Fricke2 are also shown. It is seen that the present value for LiZn and LiCd is slightly more positive but the present value for LiAl and LiIn is slightly less positive than their corresponding values. Also, it is noted there is an abrupt decrease of susceptibility of LiAl from 51.2 to 52.5 at. pct of Li. Klemm and Fricke2 found that the total susceptibility of LiZn, LiCd, LiA1, and LiIn is almost independent of temperature. slater4 gave a working expression for the diamagnetism of the atomic core as follows:

Jan 1, 1964

By C. A. Heberlein

C. A. HEBERLEIN,* New York, N. Y.-The results stated by Rey and Brevers are so startling that they are of great interest, as the concentration of a low percentage of cinnabar by differential flotation yields a high-grade concentrate in the presence of either arsenical or iron pyrite. The authors say: "Cyanide can thus be used to depress arsenopyrite and make a good cinnabar-arsenopyrite separation. A cinnabarpyrite separation could probably be effected in the same way." Corrosive sublimate at the present price of mercury would be a very expensive reagent but the expense would be justifiable if a high rate of concentration could be obtained with a high extraction. On my request, special tests were made in the Punitaqui mill in Chile along the line suggested by the authors, without any improvement of either grade or extraction. As the recovery of the cinnabar in a complex sulphide of chalcopyrite and pyrite gave unsatisfactory results, I had tests made at the testing laboratory of the American Cyanamid Co. at Stamford, Conn. As these tests turned out to be highly satisfactory, not only at Stamford but later at the mine, they are presented here. [AMERICAN CYANAMID TEST FEED PER CENT Si02 66.54 A12032.08 CaO0.70 MgO 0.00 Alkalis1.78 Fe15.63 Cu0.44 S9.42 Hg0.45 OZ. PER TON Ag0.95 Au0.151 Screen Analysis of Tailings, Per Cent Plus650.0 Plus 1001.32 Plus 15020.75 Plus 20019.85 Minus 20058.08] The pulp had a density of 22 and a pH of 7.8. Total time of conditioning was one minute. The reagent added was Texas fuel oil, 0.116lb. Of 33.7 Bé. gravity containing 0.9 per cent sulphur. Frother, 0.062 lb. of No. 5 pine oil. Rate of concentration of mercury was 25.7: 1 [ ]

Jan 1, 1941

THE 125th meeting of the Institute was held in New York, Feb. 20-23, 1922, inclusive, and was the most successful annual meeting of the Institute ever held; there was a larger registration, there were more sessions of importance, and a greater number of sessions, than in any previous year. The total registration was 1331, comprising 351 New York members, 393 visiting members and 587 guests. At the annual business meeting of the Institute, held on Tuesday, Feb. 21, with President Ludlow presiding, there was a much larger attendance than usual. The report of the tellers was read and the following officers were declared elected: Arthur S. Dwight, Director and President-District 0 J. V. W. Reynders, Director and Vice-president-District 0 A. R. Ledoux, Director and Vice-president-District 0 Charles F. Rand. Director-District 0 George D. Barron, Director-District 0 William H. Bassett, Director-District 1 Thomas B. Stearns, Director-District 8 William Kelly, Director-District 5

Jan 3, 1922

By E. H. Jr. Dix

THE use of magnesium as an alloying element in aluminum alloys has been limited, in general, to comparatively small quantities. In duralumin-type, strong-aluminum alloys, magnesium is present to the extent of ½ to ¾ per cent. and various grades of Magnalite and the "Y" alloy of the National Physical Laboratory of England contain up to 1 1/2 per cent. In this country small quantities of aluminum alloy sheet containing 4 per cent. magnesium are produced commercially. All commercial aluminum contains sufficient silicon to convert a portion of the magnesium added to the compound Mg2Si. It is well known that the solubility of both magnesium and magnesium-silicide decrease with decrease in temperature. It is, therefore, impossible to separate the age-hardening effect of the magnesium-silicide from that of magnesium, except by the use of aluminum of such high purity that the silicon content is negligible. The present paper is the fifth1, 2,3,4 of a series from the laboratories of the Aluminum Co. of America reporting the results of investigations of the equilibrium relations in aluminum-rich alloys made from the high purity aluminum manufactured by this company .5

Jan 1, 1929

By M. Gell, G. R. Leveran

The high- and low-cycle fatigue properties of the nickel-base superalloy, Mar-MBOO, in columnar-grained and single-crystal forms were determined at room temperature. It was found that the fatigue lives of these materials were greatly affected by the size of preexisting cracks in MC-type carbides contained in the micro structure. Most of the data falls on two curves given by: (zN)'/A€= K, where Nf is the number of cycles to failure, Af is the total strain range, and K is a function of carbide size. No difference was observed in the fatigue behavior of the columnar-grained and single-crystal materials for the same MC carbide size. Matrix slip and crack initiation occurred at precracked MC carbides and, to a lesser extent, at micropores. Fatigue crack propagation was mainly in the Stage I mode, i.e., on cry stallo graPhic slip planes. The Stage I fracture in these materials was unusual in that distinct features were observed on the fracture surfaces. In high-cycle fatigue, these features resembled those commonly observed on the cleavage fracture surfaces of bcc and hcp materials. Yet, in this study, the cracks propagated slowly in a cyclic manner. In low-cycle fatigue, the Stage I facets contained equiaxed dimples, similar to those observed on the tensile fracture surfaces of ductile materials. These observations indicate that both local normal and shear stresses are involved in these Stage I fractures. A model is proposed to explain these results based on the weakening of the cohesive energy of the active slip planes by reversed shear deformation and the fracture of the bonds across the weakened planes by the local normal stress. RECENT developments in casting technology have produced cast nickel-base superalloys in columnar -grained and single-crystal forms.1'2 The tensile and creep properties of the nickel-base superalloy, Mar-M200, cast in these forms have been shown to be superior to the corresponding properties of the conventionally cast polycrystalline material.lp2 This improvement in properties results, in part, from the elimination of grain boundaries in the single crystals and the alignment of the grain boundaries parallel to the stress axis in the columnar-grained castings. As part of a program to evaluate the fatigue properties of nickel-base superalloys cast in single-crystal and columnar-grained forms, a study has been made of the cyclic deformation and fracture of Mar-M2OO at room temperature. M. fiFl I .hininr Mpmher AIMF ic ^pninr Rocoarrh Accn^iata anH I) EXPERIMENTAL PROCEDURE The composition range of Mar-Ma00 in weight percent is: 8 to 10 Cr, 9 to 11 Co, 11.5 to 13.5 W, 0.75 to 1.25 Cb, 1.75 to 2.25 Ti, 4.75 to 5.25 Al, 0.01 to 0.02 B, 0.03 to 0.08 Zr, 0.07 to 0.12 C, bal. Ni. All of the castings met the above specifications. The castings were solutionized for 1 to 4 hr at 2250°F followed by aging at 1600°F for 32 hr which resulted in a 0.2 pct offset yield stress of 150,000 psi at room temperature. The microstructure of the material consisted of cuboidal, coherent particles of ordered, fcc Ni3(A1,Ti) (commonly designated y'), approximately 0.3 p on edge, distributed in an fcc y solid-solution matrix. MC carbides together with shrinkage and gas micropores were also distributed throughout the materials. The MC carbides and micropores were located preferentially in the interdendritic interstices, as well as in the grain boundaries in the columnar-grained castings. The (100) direction of all the single crystals and the common (100) axis of the grains in the columnar materials were aligned within about 5 deg of the specimen axis. Fatigue testing was carried out in the high-cycle (HCF) and low-cycle (LCF) fatigue regions, with the major difference being gross yielding of the specimen occurred during the first cycle in the LCF region. This division also corresponded with the more usual one in which the life of a specimen in LCF is less than lo4 cycles and that in HCF is greater than lo4 cycles. The designs of the high-cycle fatigue and low-cycle fatigue specimens are shown in Figs. l(a) and (c), respectively. The gage sections of both HCF and LCF specimens were electropolished prior to testing. The HCF specimens were tested in an MTS, closed-loop, hydraulic fatigue machine at 10 cps in air. The specimens were cycled between a tensile stress of 5000 psi and a maximum tensile stress which ranged from 35,000 to 125,000 psi, Fig. l(b). The LCF specimens were cycled under strain control from zero to a maximum tensile strain, Fig. l(d), in a Wiedemann-Baldwin testing machine. The experimental procedure has been described elsewhere.3'4 Both HCF and LCF tests were interrupted periodically in order to replicate the development of slip and cracking at the specimen surface. This was accomplished by placing plastic replicating tape around the gage section of the specimen while the specimen was in the mahine. The size of the MC carbides for all specimens was measured on a polished longitudinal section through the gage section after fatigue testing. The method of measurement consisted of carefully scanning the entire polished section in order to locate the largest MC carbides. Photographs were then taken of the six longest carbides oriented approximately normal to the

Jan 1, 1969

By S. Saito, P. A. Beck

The crystal structure of MoNi3 was determined by means of X-ray diffraction. This structure is isotype with that of ovgered TiCu3. The lattice parameters are: a. = 5.064A, bo = 4.224A, co = 4.448A, and zf 0.157. If the orthorhombic distortion (slight relative to the corresponding orthohexagonal unit cell) is disregarded, the structure may be described in terms of a close-packed ordered atomic layer, stacked in the sequence: abab. The structztres of ordered TiCu3 and TiAl3 are homotectic. The three types of ordered hexagonal phases, iso-structural with TiNi3, MgCd3, and VCo3, are known to occur in AB3 alloys of transition elements of the first, second, ad third long periods. It was noted1 that phases with the TiNi3 structure occur selectively in alloys of Ti-group elements with Ni-group elements. In AB3 alloys of Ti-group and V-group elements with Co-group elements the AuCu3-type structure predominates.' The vCO3 structure, which was determined very recently,' has hexagonal symmetry, but the actual atomic arrangement here, too, is rather closely related to the ordered cubic structure of AuCu3-type. However, an ordered hexagonal close-packed structure of the MgCd3-type occurs in MOCO33 and WCO3.4 Consequently, the question arises as to whether or not the crystal structure of MoNi3 is also of the MgCd3-type. Grube and winkler5 found that MoNi3 has a hexagonal close-packed structure with a = 2.54A and c/a = 1.65. They pointed out that some additional weak diffraction lines could be observed in the powder pattern, which may have been due to an ordered atomic arrangement in this phase. However, no detailed information was obtained by them and the structure was apparently not further investigated by others. The present work was, therefore, undertaken in an attempt to determine in detail the structure of MoNi3, and to investigate the possibility of ordering. EXPERIMENTAL METHODS Alloys used in the present work were arc-melted in a water-cooled copper crucible under helium atmosphere. Electrolytic nickel and molybdenum, both 99.9 pct pure, were used. Chemical analyses were not made, but the melting loss was not higher than 2 pct for any alloy. Ingots were first homogenized at 1200°C for 48hr, quenched, heavily cold worked, and then annealed at 820" or 860°C for 1 week, followed by quenching in cold water. Powder specimens for X-ray work were prepared by crushing the heat-treated solid specimens. In order to remove strains, the powders were reannealed in evacuated scaled fused silica capsules for 6 hr at the same temperature at which the corresponding solid specimens were annealed. X-ray photographs were taken with an asymmetric focussing camera, using unfiltered CrK or CuK radiation. EXPERIMENTAL RESULTS The X-ray diffraction patterns of alloys containing 20.8, 25, and 26.4 at. pct Mo, homogenized at 1200°C, showed the face-centered-cubic structure of the Ni-base a-solid solution. It was revealed, however, by micrographic examination that the 26.4 at. pct Mo alloy contained in addition very small amounts of a second phase, in accordance with the phase diagram.6 On the other hand, the 20.8 at. pct Mo alloy after annealing at 820°C gave the X-ray diffraction pattern of the ordered face-centered-tetragonal MONi4.7 In this pattern several additional weak diffraction lines were also observed, corresponding to the strongest diffraction lines of MoNi3. The alloys containing 25 and 26.4 at. pct Mo after annealing at 820" or 860°C gave X-ray diffraction patterns, as shown in Tables I and 11, corresponding to MoNi3. Each one of the reflections which could be tentatively indexed on the hexagonal close-packed cell of Grube and Winkler,5 with the exception of the basal plane reflections, was split into a doublet, as seen in Table I. Since microscopically the alloy consisted of a single phase, it seemed probable that the lattice of MoNi3 is actually slightly deformed, as compared with the tentative hexagonal unit cell. In addition to these diffraction lines, several weak lines were also present, as shown in Table 11, which could not be indexed at all on the hexagonal close-packed cell considered. Satisfactory indexing of all diffraction lines observed was found to be possible by using an orthorhombic unit cell with ao = 5.064A, ft = 4.224A, and c = 4.448A. These values, whose accuracy is estimated to approximately ± 0.008A, correspond to 95.14A3 for the volume of the unit cell, and to an X-ray density of 9.50 g per cm3. If no attention were paid to the weak reflections listed in Table II, a reduced -unit cell of half the volume (a = 2.532A, b = 4.448A, and c = 4.224A), closely related to the orthohexagonal cell, might be used. The dimensions of the orthohexagonal cell of the same volume as the reduced cell are: a = 2.562A, b = 4.437 A, and c = 4.183A. It may be seen that in the reduced cell the a axis is slightly shorter, while the b and c axes are slightly longer than those corresponding to the orthohexagonal cell of the same volume. This slight orthorhombic distortion is re-

Jan 1, 1960

By J. W. MacDonald

Review of equipment, performance, and shaft design plans including head-frames for sinking and forms for lining are given. Also included are comparative data for shafts of 11 x20 ft and 193/4 x 30 ft with 756 and 666-ft depths, respectively. Advantage from curtain wall installation with "slip forms" which warrant consideration for normal lining are outlined. A preliminary review is also made of "chemical grouting" to stop water inflow leakage with Halliburton equipment and service. Two coal mine shafts recently completed in Franklin County, Ill., afford experience and accomplishment to warrant review. These shafts provide access to a tract with a potential recovery of one hundred million tons. This work provided the initial sinking by other than a contractor's organization since 1918. Four additional shafts required during the interim were sunk under contract arrangement with others. Supervisory contact and inspection afforded experience to govern planning and conduct of the recent work. TEST DRILLING Core test holes were drilled within each of the two shaft locations. Four additional cable tool holes were drilled on a radius of 700 ft from the shaft bottom to determine the coal seam elevations and govern the underground layout plans for each shaft. A graphic log of the hoist shaft test drillhole is shown by Fig. 1. A very soft sandstone was found at a depth of 16 ft. Cored recovery of the sandstone proved much weaker than the overlying compacted sand secured with coring facilities for soil recovery. Gradation from the very soft sandstone to fairly hard material occurred with the next 14 ft, extending to a depth of 30 ft. The weak character within the upper portion entailed need of adequate protection when sinking as described later. A part of the sandstone provided sufficient porosity and permeability to warrant further investigation. Adjacent cable tool drilling for temporary water supply disclosed inflow was limited to 2 gpm with a depth of 40 ft. It was increased to 12 gpm during the next 50 ft of drilling and occasioned subsequent precaution when sinking. General arrangement of facilities for sinking the hoist shaft is shown by Fig. 2. An available steel frame building was used to accommodate the hoist, compressor, shop, and shower or change room. The stiff leg derrick with 90-ft length of boom permitted removal of forms from the wood shop to the storage area or delivery within the shaft. Reinforcing steel and other needs were similarly handled, in addition to headframe erection. The headframe was placed over one end of the shaft to enable passage of forms for lining through the adjacent half next to the stiff leg derrick. The steel headframe as shown by Fig. 3 was fabricated locally. Side anchored cables from the

Jan 1, 1961

By G. Thodos, W. F. Stevens

The point-source function introduced by Horner' us a solution to the general unsteady-state equation for the flow of fluids through porous media has been utilized to calculate pressure profiles for adjacent wells as a function of time. By trial and error, the time at which the pressure waves meet to cause interference can then be calculated. For this calculation, the time of interference is arbitrarily defined as that time when both pressure waves exhibit a pressure decrease of 25 psi ar the same point within the formation. To illustrate the method, an example involving two adjacent wells producing at different rates has been worked out and is presented in detail. INTRODUCTION The initiation of production of a new well is usually accompanied by pressure drawdown measurements in order to establish the extent and characteristics of the formation. The interpretation of such pressure drawdown data is based on mathematical developments involving a single well in an infinite reservoir. If more than one well is present in a reservoir, the possibility of interaction between wells exists. Therefore, care must be taken in interpreting the pressure drawdown data. It becomes important to be able to determine when this interaction, or interference, becomes significant. This paper presents a method for the prediction of the approximate time of interference between two such adjacent wells. The basic differential equation describing the pressure distribution existing during unsteady-state flow of a slightly compressible fluid has been solved by Hor-ner.' for a constant production rate from a circular homogeneous reservoir of infinite extent. The solution utilizes the point-source function to define the pressure at various points within the formation as a function of time. The resulting expression is: q = production rate, STB/D ,;= formation volume factor, dimension-less µ = fluid viscosity, cp k = formation permeability. md H = formation thickness, ft C - fluid compressibility, psi' F = formation porosity, dimensionless R = distance from centerline of well, ft T = production time, hours Ei(—u) = Ei-function of U Eq. 1 may be used to calculate the pressure profiles generated during production from a single well in an infinite reservoir.