Electrochemical Reduction Of Cobalt Tetrafluoroborate In 1-Butyl-3-Methylimidazolium Tetrafluoroborate Ionic Liquid

Electrodeposition of cobalt from cobalt tetrafluoroborate (Co(BF4)2) was investigated using 1- butyl-3-methylimidazolium tetrafluoroborate (BMIMBF4) ionic liquid. The experiments were conducted at 353 K. Chronoamperometry experiments confirm that the electrodeposition of cobalt on tungsten electrode proceeds via three-dimensional instantaneous nucleation with diffusion-controlled growth process. The average diffusion coefficient of Co(II) was found to be 7.5 × 10-8 cm2s-1 at 353 K, which is in good agreement with the estimated value from cyclic voltammetry. The electrochemical deposit was characterized using SEM-EDS and XRD methods. The SEM image shows formation of a dense and compact deposit at - 0.75 V. The EDS and XRD analysis confirm that the obtained deposit is pure cobalt metal.